WO2006054470A1 - 積層体の製造方法 - Google Patents

積層体の製造方法 Download PDF

Info

Publication number
WO2006054470A1
WO2006054470A1 PCT/JP2005/020568 JP2005020568W WO2006054470A1 WO 2006054470 A1 WO2006054470 A1 WO 2006054470A1 JP 2005020568 W JP2005020568 W JP 2005020568W WO 2006054470 A1 WO2006054470 A1 WO 2006054470A1
Authority
WO
WIPO (PCT)
Prior art keywords
group
refractive index
layer
producing
laminate
Prior art date
Application number
PCT/JP2005/020568
Other languages
English (en)
French (fr)
Inventor
Hiroomi Shimomura
Mitsunobu Doimoto
Ryosuke Iinuma
Hideaki Takase
Original Assignee
Jsr Corporation
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from JP2005197598A external-priority patent/JP2006231900A/ja
Application filed by Jsr Corporation filed Critical Jsr Corporation
Publication of WO2006054470A1 publication Critical patent/WO2006054470A1/ja

Abstract

　基材（３０）と、その上に導電層（２０）及び多層構造（４０），（５０）を有する積層体の製造方法であって、ピロール、チオフェン、フラン、セレノフェン、３，４－エチレンジオキシチオフェン及びこれらの誘導体からなる群から選択される少なくとも一種の単量体を気相重合することにより導電層（２０）を形成し、（Ａ）重合性不飽和基を有する有機化合物（Ａｂ）を結合させてなる金属酸化物粒子、（Ｂ）エチレン性不飽和基含有含フッ素重合体、（Ｃ）速揮発溶剤及び（Ｄ）遅揮発溶剤を含む紫外線硬化性樹脂組成物を塗布して塗膜を形成し、この１の塗膜から溶媒を蒸発させることにより、２以上の層（４０），（５０）を形成することを特徴とする積層体の製造方法。

Description

明 細 書
積層体の製造方法
技術分野
[0001] 本発明は、積層体の製造方法及びそれにより得られる積層体に関し、特に、 2以上 の層を 1の塗膜から形成することができる積層体の製造方法に関する。
背景技術
[0002] 現在、マルチメディアの発達に伴い、各種の表示装置（ディスプレイ装置）において 種々の発展が見られている。そして、各種の表示装置のうち、特に、携帯用を中心に 屋外で使用されるものでは、その視認性の向上がますます重要となってきており、大 型表示装置においても、より見易くすることが需要者に要求されており、この事項がそ のまま技術課題となっている。
[0003] 従来、表示装置の視認性を向上させるための一手段として、低屈折率材料から構 成される反射防止膜を、表示装置の基板に被覆することが行われており、反射防止 膜を形成する方法としては、例えば、フッ素化合物の薄膜を蒸着法により形成する方 法が知られている。然るに、近年では、液晶表示装置を中心として、低いコストで、し 力、も大型の表示装置に対しても、反射防止膜を形成することのできる技術が求められ ている。し力 ながら、蒸着法による場合には、大面積の基板に対して、高い効率で 均一な反射防止膜を形成することが困難であり、しかも真空装置を必要とするために 、コストを低くすることが困難である。
[0004] このような事情から、屈折率の低いフッ素系重合体を有機溶剤に溶解して液状の組 成物を調製し、これを基板の表面に塗布することによって反射防止膜を形成する方 法が検討されている。例えば、基板の表面にフッ素化アルキルシランを塗布すること が提案されている（例えば、特許文献 1及び特許文献 2参照）。また、特定の構造を 有するフッ素系重合体を塗布する方法が提案されている（例えば、特許文献 3参照） 一方、反射防止膜として、帯電防止層に導電性高分子を用いた積層体も知られて いる (例えば、特許文献 4参照)。 [0005] 特許文献 1 :特開昭 61 40845号公報
特許文献 2：特開平 1 1527号公報
特許文献 3：特開平 6— 115023号公報
特許文献 4 :特開 2003— 300267号公報
[0006] これら従来の反射防止膜は、基材上に、導電層（帯電防止層）、異なった屈折率の 層、ハードコート層等が形成された積層体であることが多い。従来の製造方法では、 基材上に、各層をそれぞれ塗布する工程を繰り返してレ、た。
本発明は、以上のような状況を背景としてなされたものであって、その目的は、一回 の塗布工程により 2以上の層を形成できる積層体の製造方法及びそれにより得られ る積層体を提供することにある。また、本発明の他の目的は、導電層を効率よく形成 する積層体の製造方法及びそれにより得られる積層体を提供することにある。さらに 、本発明の他の目的は、基材に対する密着性に優れ、耐擦傷性が高ぐ良好な反射 防止効果を有する積層体の製造方法及びそれにより得られる積層体を提供すること にある。
発明の開示
[0007] 本発明によれば、以下の積層体の製造方法及びそれにより得られる積層体を提供 できる。
1.基材と、その上に導電層及び多層構造を有する積層体の製造方法であって、 ピロ一ノレ、チォフェン、フラン、セレノフェン、 3, 4 _エチレンジォキシチォフェン及 びこれらの誘導体からなる群から選択される少なくとも一種の単量体を気相重合する ことにより導電層を形成し、
前記基材上又は基材上に形成された層の上に、下記成分 (A)〜（D)を含む紫外 線硬化性樹脂組成物を塗布して塗膜を形成し、
この 1の塗膜から溶媒を蒸発させることにより、 2以上の層を形成することを特徴とす る積層体の製造方法。
[紫外線硬化性樹脂組成物]
(A)重合性不飽和基を有する有機化合物 (Ab)を結合させてなる金属酸化物粒子
(B)エチレン性不飽和基含有含フッ素重合体 (C) (B)エチレン性不飽和基含有含フッ素重合体の溶解性が高い、 1種又は 2種 以上の溶剤（以下、「（C)速揮発溶剤」という）
(D) (A)重合性不飽和基を有する有機化合物 (Ab)を結合させてなる金属酸化物 粒子の分散安定性が高ぐかつ、（C)速揮発溶剤と相溶性である、 1種又は 2種以上 の溶剤（以下、「（D)遅揮発溶剤」という）
かつ、（C)速揮発溶剤の相対蒸発速度が、（D)遅揮発溶剤の相対蒸発速度よりも大 きい
紫外線硬化性樹脂組成物 2.前記 2以上の層の各層が、金属酸化物粒子が高密度 に存在する層又は金属酸化物粒子が実質的に存在しない層であって、少なくとも 1 層は金属酸化物粒子が高密度に存在する層であることを特徴とする 1に記載の積層 体の製造方法。
3.前記 2以上の層が、 2層であることを特徴とする 2に記載の積層体の製造方法。
4.さらに、前記 2以上の層を放射線照射することにより硬化させることを特徴とする 1 〜3のいずれかに記載の積層体の製造方法。
5.積層体が光学用部品であることを特徴とする 1〜4のいずれかに記載の積層体の 製造方法。
6.積層体が反射防止膜であることを特徴とする 1〜4のいずれかに記載の積層体の 製造方法。
7.前記積層体が、基材上に、少なくとも帯電防止層、高屈折率層及び低屈折率層 力 基材に近い側からこの順に積層されている反射防止膜であって、
前記導電層が、帯電防止層であり、
3に記載の 2層が、高屈折率層及び低屈折率層からなる
ことを特徴とする 3に記載の積層体の製造方法。
8.低屈折率層の 589nmにおける屈折率が 1. 20〜： 1. 55であり、
高屈折率層の 589nmにおける屈折率が 1. 50-2. 20であって、低屈折率の屈折 率より高いことを特徴とする 7に記載の積層体の製造方法。
9.前記積層体が、基材上に、少なくとも、帯電防止層、中屈折率層、高屈折率層及 び低屈折率層が、基材に近い側からこの順に積層されている反射防止膜であって、 前記導電層が、帯電防止層であり、
3に記載の 2層が、高屈折率層及び低屈折率層からなる
ことを特徴とする 3に記載の積層体の製造方法。
10.低屈折率層の 589nmにおける屈折率が 1. 20〜： 1. 55であり、
中屈折率層の 589nmにおける屈折率が 1. 50〜： 1. 90であって、低屈折率の屈折 率より高ぐ
高屈折率層の 589nmにおける屈折率が 1. 51-2. 20であって、中屈折率の屈折 率より高いことを特徴とする 9に記載の積層体の製造方法。
11.さらに、基材上に、ハードコート層を形成することを特徴とする 7〜： 10のいずれか に記載の積層体の製造方法。
12.紫外線硬化性樹脂組成物において、前記 (Ab)重合性不飽和基を有する有機 化合物が、重合性不飽和基に加えて、下記式 (A— 1)に示す基を有することを特徴 とする 1〜： 11のレ、ずれかに記載の積層体の製造方法。
[化 1]
Figure imgf000005_0001
[式中、 Uは、 NH、 O (酸素原子）又は S (ィォゥ原子）を示し、 Vは、〇又は Sを示す。
]
13.紫外線硬化性樹脂組成物において、前記 (Ab)重合性不飽和基を有する有機 化合物が、分子内にシラノール基を有する化合物又は加水分解によってシラノール 基を生成する化合物であることを特徴とする 1〜： 12のいずれかに記載の積層体の製 造方法。
14.前記（B)エチレン性不飽和基含有含フッ素重合体が、 1個のイソシァネート基と
、少なくとも 1個のエチレン性不飽和基とを含有する化合物 (B— 1)と、水酸基含有含 フッ素重合体 (B_ 2)と、を反応させて得られることを特徴とする 1〜： 13のいずれかに 記載の積層体の製造方法。
15.前記水酸基含有含フッ素重合体 (B— 2)が、下記構造単位（a) 20〜70モル％ 、（ ）10〜70モル％及び（0) 5〜70モル％を含んでなり、かつ、ゲルパーミエーショ ンクロマトグラフィーで測定したポリスチレン換算数平均分子量が 5, 000〜500, 00 0である 14に記載の積層体の製造方法。
(a)下記一般式（1)で表される構造単位。
(b)下記一般式 (2)で表される構造単位。
(c)下記一般式 (3)で表される構造単位。
[化 2]
F R1
— C-C― (つ
[式中、 R1はフッ素原子、フルォロアルキル基、又は— OR2で表される基（R2はアルキ ル基、又はフルォロアルキル基を示す）を示す]
[化 3]
H R3
— C-C— (2)
H R4
[式中、 R3は水素原子又はメチル基を、 R4はアルキル基、 _(CH ) _〇R5若しくは—
2
OC〇R5で表される基（R5はアルキル基、又はグリシジル基を、 Xは 0又は 1の数を示 す）、カルボキシル基、又はアルコキシカルボ二ル基を示す]
[化 4]
H R6
— C-C—— (3)
H (CH2)vOR7
[式中、 R6は水素原子、又はメチル基を、 R7は水素原子、又はヒドロキシアルキル基 を、 Vは 0又は 1の数を示す]
16.さらに、前記水酸基含有含フッ素重合体 (B— 2)が、ァゾ基含有ポリシロキサン 化合物に由来する下記構造単位（d) 0. 1〜： 10モル％を含む 14又は 15に記載の積 層体の製造方法。 (d)下記一般式 (4)で表される構造単位。
[化 5]
Figure imgf000007_0001
[式中、 R8及び R9は、同一でも異なっていてもよぐ水素原子、アルキル基、ハロゲン 化アルキル基、又はァリール基を示す]
17.前記水酸基含有含フッ素重合体 (B— 2)が、前記構造単位 (d)を下記構造単位
(e)の一部として含むことを特徴とする 16に記載の積層体の製造方法。
(e)下記一般式 (5)で表される構造単位。
[化 6]
Figure imgf000007_0002
[式中、 R1Q〜R13は水素原子、アルキル基、又はシァノ基を示し、 R14〜R17は水素原 子又はアルキル基を示し、 p、 qは:!〜 6の数、 s、 tは 0〜6の数、 yは:!〜 200の数を示 す。 ]
18.さらに、前記水酸基含有含フッ素重合体 (B— 2)が、下記構造単位 (f) 0. ：!〜 5 モル％を含む 14〜： 17のいずれかに記載の積層体の製造方法。
(f )下記一般式 (6)で表される構造単位。
[化 7]
H R18
— C一 C (6)
H H
[式中、 R18は乳化作用を有する基を示す]
19.前記化合物（B— 1)が、 2—（メタ）アタリロイルォキシェチルイソシァネートである 14〜： 18のいずれかに記載の積層体の製造方法。 20.紫外線硬化性樹脂組成物の（C)速揮発溶剤は、（A)重合性不飽和基を有する 有機化合物 (Ab)を結合させてなる金属酸化物粒子の分散安定性が低い、 1種又は 2種以上の溶剤であり、（D)遅揮発溶剤は、 （B)エチレン性不飽和基含有含フッ素 重合体の溶解性が低レ、、 1種又は 2種以上の溶剤であることを特徴とする 1〜： 19のい ずれかに記載の積層体の製造方法。
21.紫外線硬化性樹脂組成物が、さらに、成分 (E)少なくとも 2個以上の（メタ）アタリ ロイル基を含有する多官能 (メタ）アタリレートイ匕合物及び Z又は少なくとも 1個以上の (メタ）アタリロイル基を含有する含フッ素 (メタ）アタリレート化合物を含有することを特 徴とする 1〜20のいずれかに記載の積層体の製造方法。
22.紫外線硬化性樹脂組成物が、さらに、成分 (F)光ラジカル重合開始剤を含むこ とを特徴とする 1〜21のいずれかに記載の積層体の製造方法。
23.：!〜 22のいずれかに記載された積層体の製造方法により、製造された積層体。
[0008] 本発明の積層体の製造方法は、組成物を塗布して得られる 1の塗膜から、 2以上の 層を形成することができるため、多層構造を有する積層体の製造工程を簡略化でき る。また、本発明の積層体の製造方法は、導電層を効率よく形成できる。従って、本 発明の積層体の製造方法は、特に、反射防止膜、レンズ、選択透過膜フィルタ等の 光学材料の形成に有利に用いることができる。さらに、本発明の積層体は、フッ素含 量が高いことを利用して、耐候性が要求される基材に対する塗料、耐候フィルム、コ 一ティング、その他として好適に使用することができる。しかも、当該積層体は、最外 層（基材から最も遠い層）に低屈折率層を設けることにより良好な反射防止効果を付 与する。また、本発明によれば、基材に対する密着性に優れ、耐擦傷性が高い積層 体が得られる。これらのこと力、ら、本発明の積層体は反射防止膜として極めて有用で あり、各種の表示装置に適用することにより、その視認性を向上させることができる。 あり、各種の表示装置に適用することにより、その視認性を向上させることができる。 図面の簡単な説明
[0009] [図 1A]「1の塗膜から形成される 2以上の層」を説明するための図である。
[図 1B]「1の塗膜から形成される 2以上の層」を説明するための図である。
[図 1C]「1の塗膜から形成される 2以上の層」を説明するための図である。 [図 ID]「1の塗膜から形成される 2以上の層」を説明するための図である。
[図 1E]「1の塗膜から形成される 2以上の層」を説明するための図である。
[図 2]本発明に係る一実施形態である反射防止膜の断面図である。
[図 3]本発明に係る他の実施形態である反射防止膜の断面図である。
[図 4]本発明に係る他の実施形態である反射防止膜の断面図である。
[図 5]本発明に係る他の実施形態である反射防止膜の断面図である。
[図 6]本発明に係る他の実施形態である反射防止膜の断面図である。
[図 7]本発明に係る他の実施形態である反射防止膜の断面図である。
[図 8]二層分離、分離せず (一部凝集)及び均一構造の各状態の概念を示す電子顕 微鏡写真である。
発明を実施するための最良の形態
[0010] 本発明は、基材と、その上に導電層及び 2層以上の多層構造を有する積層体の製 造方法及びそれにより得られる積層体である。具体的には、本発明の製造方法では 、基材又は基材上に形成された層（以下、ベース層という）の上に、単量体を気相重 合して、導電層を形成する。また、後述する所定の紫外線硬化性樹脂組成物を塗布 し、この塗布した組成物より溶媒を蒸発（以下、「乾燥」と称することもある）させること により、 2以上の層を形成する。なお、乾燥後は溶媒が完全に無くなった状態でなく てもよく、硬化膜としての特性が得られる範囲で溶媒が残存していてもよい。好ましく は、ベース層の上に導電層を形成した後に、その上方に 2以上の層を形成する。また 、本発明では、 1の塗膜から 2以上の層の形成を、 2回以上実施することができる。
[0011] 初めに、導電層の気相重合について説明する。
気相重合により形成される導電層は、例えば特開 2003— 82105号公報に記載さ れた方法等によって製造することができ、具体的には導電性ポリマーから形成するこ とができる。即ち、ベース層に酸化剤を数 x m単位で塗布し、単量体（モノマー）を気 体状態で酸化剤塗膜と接触させることで、重合を進行させ、導電性ポリマー膜を基材 上に形成する。この際、接着力を向上させる意味で、有機溶剤とともにポリウレタン、 ポリ塩ィ匕ビニール、ポリビエルアルコール、メチルセルロース、キトサン等の高分子を 併用することも可能である。 本発明では、酸化剤が塗布されたベース層上で、単量体を気相重合させて導電性 ポリマーからなる導電層を形成するが、この際の反応温度は、 0〜140°Cであることが 好ましレ、。以下、より詳細に重合方法を説明するが、本発明はこれに限定されない。
[0012] 具体的には、まず第 1段階として、ベース層の表面に 0. 5〜： 10重量％の酸化剤を 数 z m単位で塗布する。酸化剤として例えば CuCl、トルエンスルホン酸鉄（ΠΙ)
2 、 過塩素酸鉄 (ΠΙ)、 FeCl及び Cu (C10 ) · 6Η〇から構成される群から選択された化
2 4 2 2
合物が単独又は組合せが使用できる。この際の溶剤条件は使用ベース層の種類に よって異なるが、例えば、メチルアルコール、 2_ブチルアルコール、ェチルセ口ソル ブ、エチルアルコール、シクロへキサン、アセトン、ェチルアセテート、トルエン及びメ チルェチルケトンから選択される有機溶剤を用いることができる。これらは、単独又は 2種以上混合して用いることができ、例えば、メチルアルコール、 2_ブチルアルコー ル及びェチルセ口ソルブから構成される有機溶剤を 7 : 2 : 1、 6 : 2 : 2、 6 : 3 : 1、 5 : 3 : 2 等の割合で混合して用いる。酸化剤が塗布されたベース層は、酸化剤の分解を考慮 し、 80°C以下の熱風乾燥機で乾燥させる。
[0013] 次に第 2段階として、酸化剤で塗布されたベース層に、ピロール、チォフェン、フラ ン、セレノフェン、 3, 4—エチレンジォキシチォフェン及びこれらの誘導体力 なる群 から選択される単量体を、気化して接触させ、ベース層の表面で重合反応を行う。こ の際、単量体を気化させる方法としては、密閉されたチャンバ一内で単量体を 0〜： 14 0°Cで蒸留させる方法と、 CVD (Chemical Vapor Deposition)による方法等が挙げ られる。
このとき、温度条件と反応時間を調整することが好ましぐ重合反応は、 10秒〜 40分 程度行なわれ、一般的には、単量体の種類に応じて変化するが、膜厚及び表面抵 抗値等が目標値に達するまで行なう。
[0014] 次に第 3段階として、重合が完了した後、未反応の単量体及び酸化剤を除去する ための洗浄工程を行う。この際の使用溶剤としては、通常メタノール等のアルコール 類を用レ、、場合によっては水で洗浄することもできる。
[0015] 上記のような一連の工程は、段階的又は連続的に行うことができ、単量体の重合か ら導電膜の形成までは、一連の作業工程で処理することができる。得られた導電性 ポリマーフィルムは、ベース層に対する密着性は良好であり、アルコール溶剤に対す る耐性も十分である。
[0016] 導電層の膜厚は、：!〜 2000nmであること力 S好ましレヽ。 lnm未満の膜厚では、ピン ホール等が発生しやすぐ膜形成が困難であり、また、表面抵抗も大きくなり、帯電防 止性に劣る恐れがある。また、 2000nmを超える膜厚では、表面抵抗は良好である 、透明性、色調が著しく劣り、反射防止膜としては使用困難な場合がある。特に好 ましい膜厚は、透明性、色調、表面抵抗のバランスの観点から、 5〜300nmである。 また、導電層の表面抵抗は通常 102 Ω Ζ口〜 108 Ω /口である。
[0017] 次に、 2以上の層の形成方法について説明する。
ここで、 2以上の層とは、「金属酸化物粒子が高密度に存在する層」と、「金属酸化 物粒子が実質的に存在しない層」を共に含む 2以上の層である場合もあり、また、「金 属酸化物粒子が高密度に存在する層」だけからなる 2以上の層である場合もある。 以下、図面を用いて「2以上の層の各層が、金属酸化物粒子が高密度に存在する 層又は金属酸化物粒子が実質的に存在しない層であって、少なくとも 1層は金属酸 化物粒子が高密度に存在する層」について説明する。図 1Aは、 2以上の層が、「金 属酸化物粒子が高密度に存在する層 1」と、「金属酸化物粒子が実質的に存在しな い層 3」の 2層である場合を示す。図 1Bは、 2以上の層が、「金属酸化物粒子が高密 度に存在する層 1 , la」の 2層である場合を示す。図 1Cは、 2以上の層が、「金属酸 化物粒子が高密度に存在する層 1， la」と、「金属酸化物粒子が実質的に存在しな い層 3」の 3層である場合を示す。図 1Dは、 2以上の層が、「金属酸化物粒子が高密 度に存在する層 1 , la」と、「金属酸化物粒子が実質的に存在しない層 3」の 3層であ る場合を示す。図 1Eは、 2以上の層が、「金属酸化物粒子が高密度に存在する層 lb 」と、「金属酸化物粒子が実質的に存在しない層 3」の 2層である場合を示す。
紫外線硬化性樹脂組成物が 2種以上の金属酸化物粒子を含むときは、図 IB, 1C , 1Dに示すように、「金属酸化物粒子が高密度に存在する層」が 2種類以上形成さ れ得る。
[0018] さらに、「金属酸化物粒子が高密度に存在する層」の「金属酸化物粒子」は、少なく とも 1種、即ち、 1種又は 2種以上の「金属酸化物粒子」を意味する。紫外線硬化性樹 脂組成物が 2種以上の金属酸化物粒子を含む場合、「金属酸化物粒子が高密度に 存在する層」が、 2種以上の金属酸化物粒子から構成されていてよい（例えば、図 1E )。図 1Eでは、「金属酸化物粒子が高密度に存在する層 lb」が、粒子 Xと粒子 Yから 構成されている。粒子 Yが、「金属酸化物粒子が高密度に存在する層 lb」の厚さより 大きいため、「金属酸化物粒子が実質的に存在しない層 3」に突出しているが、この 突出部分も「金属酸化物粒子が高密度に存在する層 lb」に含まれる。
[0019] 尚、図 1A〜1Eでは、「金属酸化物粒子が実質的に存在しない層 3」には通常金属 酸化物粒子が存在していないが、本発明の効果を損なわない範囲で若干含まれて いてもよい。また、「金属酸化物粒子が高密度に存在する層 1 , la, lb」も同様に金 属酸化物粒子以外の他の物質が含まれてレ、てもよレ、。
[0020] 紫外線硬化性樹脂組成物の塗布法としては、公知の塗布方法を使用することがで き、特に、ディップ法、コーター法、印刷法等各種の方法を適用することができる。 乾燥は、通常、室温から 150°C程度の加熱で、 1〜60分程度実施される。 具体的な硬化条件は後述する。
[0021] 本発明では、単量体を気相重合し、さらに、紫外線硬化性樹脂組成物を溶液状で 各種の基材に塗布し、得られた塗膜を乾燥/硬化させて積層体を得ることができる。 例えば、基材が透明基材の場合には、最外層に低屈折率層を設けることにより優れ た反射防止膜が形成される。
反射防止膜の具体的構造は、通常、基材及び低屈折率膜、又は基材、高屈折率 膜及び低屈折率膜をこの順に積層したものであり、さらに本発明では、基材、高屈折 率層及び低屈折率層の間に、導電層からなる帯電防止層を設けている。この他、基 材、高屈折率膜及び低屈折率膜の間に、他の層を介在させてもよぐ例えば、帯電 防止層、ハードコート層、中屈折率層、高屈折率層、低屈折率層の組み合わせ等の 層を設けることができる。
[0022] 図 2は、基材 10上に、帯電防止層 20、高屈折率層 40及び低屈折率層 50が、この 順に積層されてレ、る反射防止膜を示す。
この反射防止膜において、高屈折率層 40が金属酸化物粒子が高密度に存在する 層に、低屈折率層 50が金属酸化物粒子が実質的に存在しなレ、層に相当する。 本発明によれば、帯電防止層 20を気相重合により形成し、高屈折率層 40と低屈折 率層 50を、 1の塗膜から形成できる。
[0023] 図 3は、基材 10上に、ハードコート層 30、帯電防止層 20、高屈折率層 40及び低屈 折率層 50が、この順に積層されている反射防止膜を示す。
この反射防止膜において、高屈折率層 40が金属酸化物粒子が高密度に存在する 層に、低屈折率層 50が金属酸化物粒子が実質的に存在しなレ、層に相当する。 本発明によれば、帯電防止層 20を気相重合により形成し、高屈折率層 40と低屈折 率層 50を、 1の塗膜から形成できる。
[0024] 図 4は、基材 10上に、帯電防止層 20、ハードコート層 30、高屈折率層 40及び低屈 折率層 50が、この順に積層されている反射防止膜を示す。
この反射防止膜において、高屈折率層 40が金属酸化物粒子が高密度に存在する 層に、低屈折率層 50が金属酸化物粒子が実質的に存在しなレ、層に相当する。 本発明によれば、帯電防止層 20を気相重合により形成し、高屈折率層 40と低屈折 率層 50を、 1の塗膜から形成できる。
[0025] 図 5は、基材 10上に、ハードコート層 30、帯電防止層 20、中屈折率層 60、高屈折 率層 40及び低屈折率層 50が、この順に積層されている反射防止膜を示す。
この反射防止膜において、高屈折率層 40が金属酸化物粒子が高密度に存在する 層に、低屈折率層 50が金属酸化物粒子が実質的に存在しない層に相当する。或い は、中屈折率層 40、及び高屈折率層 40が何れも金属酸化物粒子が高密度に存在 する層に相当する力 \又は、中屈折率層 40が金属酸化物粒子が高密度に存在する 層に、高屈折率層 40が金属酸化物粒子が実質的に存在しなレヽ層に相当する。 本発明によれば、帯電防止層 20を気相重合により形成し、中屈折率層 60と高屈折 率層 40、又は、高屈折率層 40と低屈折率層 50を、 1の塗膜から形成できる。好ましく は、高屈折率層 40と低屈折率層 50を 1の塗膜力も形成する。
[0026] 図 6は、基材 10上に、帯電防止層 20、ハードコート層 30、中屈折率層 60、高屈折 率層 40及び低屈折率層 50が、この順に積層されている反射防止膜を示す。
この反射防止膜において、高屈折率層 40が金属酸化物粒子が高密度に存在する 層に、低屈折率層 50が金属酸化物粒子が実質的に存在しない層に相当する。或い は、中屈折率層 40、及び高屈折率層 40が何れも金属酸化物粒子が高密度に存在 する層に相当する力 \又は、中屈折率層 40が金属酸化物粒子が高密度に存在する 層に、高屈折率層 40が金属酸化物粒子が実質的に存在しなレヽ層に相当する。 本発明によれば、帯電防止層 20を気相重合により形成し、中屈折率層 60と高屈折 率層 40、又は、高屈折率層 40と低屈折率層 50を、 1の塗膜から形成できる。好ましく は、高屈折率層 40と低屈折率層 50を 1の塗膜力も形成する。
[0027] 図 7は、基材 10上に、帯電防止層 20、中屈折率層 60、高屈折率層 40及び低屈折 率層 50が、この順に積層されている反射防止膜を示す。
この反射防止膜において、高屈折率層 40が金属酸化物粒子が高密度に存在する 層に、低屈折率層 50が金属酸化物粒子が実質的に存在しない層に相当する。或い は、中屈折率層 40が金属酸化物粒子が高密度に存在する層に、高屈折率層 40が 金属酸化物粒子が実質的に存在しなレ、層に相当する。
本発明によれば、帯電防止層 20を気相重合により形成し、中屈折率層 60と高屈折 率層 40、又は、高屈折率層 40と低屈折率層 50を、 1の塗膜から形成できる。好ましく は、高屈折率層 40と低屈折率層 50を 1の塗膜から形成する。
[0028] 次に、上記の反射防止膜の各層について説明する。
(1)基材
透明基材の具体例としては、例えば、トリァセチルセルロース、ポリエチレンテレフタ レート樹脂 (東レ (株)製ルミラー等）、ガラス、ポリカーボネート樹脂、アクリル樹脂、ス チリル樹脂、ァリレート樹脂、ノルボルネン系樹脂 CJSR (株)製アートン、 日本ゼオン（ 株)製ゼォネックス等）、メチルメタタリレート/スチレン共重合体樹脂、ポリオレフイン 樹脂等の各種透明プラスチック板、フィルム等を挙げることができる。好ましくは、トリ ァセチルセルロース、ポリエチレンテレフタレート樹脂（東レ（株）製ルミラー等）、ノノレ ボルネン系樹脂 CFSR (株)製アートン等）である。
[0029] (2)低屈折率層
低屈折率層とは、波長 589nmの光の屈折率が 1. 20-1. 55である層を表す。 低屈折率層に使用される材料としては、 目的とする特性が得られれば特に限定さ れるものではないが、例えば、含フッ素重合体を含有する硬化性組成物、アクリルモ ノマー、含フッ素アクリルモノマー、エポキシ基含有化合物、含フッ素エポキシ基含有 化合物等の硬化物を挙げることがでる。また、低屈折率層の強度を上げるために、シ リカ微粒子等を配合することもできる。
[0030] (3)高屈折率層
高屈折率層とは、波長 589nmの光の屈折率が 1. 50〜2. 20である層を表す。 高屈折率層を形成するために高屈折率の無機粒子、例えば金属酸化物粒子を配 合すること力 Sできる。
[0031] 金属酸化物粒子の具体例としては、アンチモンドープ酸化錫 (ATO)粒子、錫ドー プ酸化インジウム（ITO)粒子、リンドープ酸化錫（PTO)粒子、酸化亜鉛 (ZnO)粒子 、アンチモンドープ ZnO、 Alドープ ZnO粒子 ZrO粒子、 Ti〇粒子、シリカ被覆 TiO
2 2 2 粒子、 Al O /ZrO被覆 Ti〇粒子、 Ce〇粒子等を挙げることができる。好ましくは、
2 3 2 2 2
アンチモンドープ酸化錫 (AT〇）粒子、錫ドープ酸化インジウム（ITO)粒子、リンド一 プ酸化錫（PTO)粒子、 A1ドープ ZnO粒子 Al O /ZrO被覆 TiO粒子である。これ
2 3 2 2
らの金属酸化物粒子は、一種単独又は二種以上の組み合わせで使用することがで きる。
また、高屈折率層にハードコート層や帯電防止層の機能を持たせることもできる。
[0032] (4)中屈折率層
3種以上の屈折率を有する層を組み合わせる場合に、通常、波長 589nmの光の 屈折率が 1. 50〜： 1. 90であって、低屈折率層より高ぐ高屈折率層より低い屈折率 を有する層を中屈折率層と表す。中屈折率層の屈折率は、好ましくは、 1. 50〜： 1. 8 0、より好ましくは、 1. 50〜： 1. 75である。
中屈折率層を形成するために、高屈折率の無機粒子、例えば金属酸化物粒子を 酉己合すること力 Sできる。
[0033] 金属酸化物粒子の具体例としては、アンチモンドープ酸化錫 (ATO)粒子、錫ドー プ酸化インジウム（ITO)粒子、リンドープ酸化錫（PTO)粒子、 Zn〇粒子、アンチモ ンドープ ZnO、 Alドープ Zn〇粒子、 ZrO粒子、 Ti〇粒子、シリカ被覆 TiO粒子、 A1
2 2 2
O /ZrO被覆 Ti〇粒子、 Ce〇粒子等を挙げることができる。好ましくは、アンチモ
2 3 2 2 2
ンドープ酸化錫 (AT〇）粒子、錫ドープ酸化インジウム（ITO)粒子、リンドープ酸化 錫（PTO)粒子、 Α1ドープ Ζη〇粒子、 Zr〇粒子である。これらの金属酸化物粒子は
2
、一種単独又は二種以上の組み合わせで使用することができる。
また、中屈折率層にハードコート層や帯電防止層の機能を持たせることもできる。 低屈折率層と高屈折率層を組み合わせることにより反射率を低くすることができ、さ らに、低屈折率層、高屈折率層、中屈折率層を組み合わせることにより、反射率を低 くすることができるとともに色目を減らすことができる。
[0034] (5)ハードコート層
ハードコート層の具体例としては、 Si0、エポキシ系樹脂、アクリル系樹脂、メラミン
2
系樹脂等の材料力も構成するのが好ましい。また、これらの樹脂にシリカ粒子を配合 してもよい。
ハードコート層は積層体の機械的強度を高める効果がある。
[0035] (6)帯電防止層
帯電防止層は、導電層の気相重合について上述した通りである。
帯電防止層は、積層体に導電性を付与し、静電気が生じて埃等が付着するのを防 止する。
[0036] これらの層は一層のみ形成してもよぐまた、異なる層を二層以上形成してもよい。
また、低、中、高屈折率層の膜厚は、それぞれ通常 60〜150nm、ハードコート層 の膜厚は通常 1〜20 μ m、帯電防止層の膜厚は通常 5〜30nmである。
本発明では、積層体の導電層及びその他の任意の連続する 2以上の層を本発明 の製造方法で形成できるが、本発明の製造方法によらない、層の製造方法は、公知 の塗布と硬化、蒸着、スパッタリング等の方法により製造できる。
[0037] また、本発明による紫外線硬化性樹脂組成物からなる層は、硬化させて優れた光 学特性と耐久性を有する硬化膜を形成させるために、特に、加熱による熱履歴を与 えることが好ましい。もちろん、常温で放置した場合にも、時間の経過と共に硬化反 応が進み、 目的とする硬化膜が形成されるが、実際上は、加熱して硬化させることが 、所要時間を短縮する上で効果的である。また、熱酸発生剤を硬化触媒として添加し ておくことにより、さらに硬化反応を促進させることができる。この硬化触媒としては特 に制限は無ぐ一般のゥレア樹脂、メラミン樹脂等のための硬化剤として使用されて レ、る各種酸類やその塩類を利用することができ、特に、アンモニゥム塩を好ましく用 レ、ること力 Sできる。硬化反応のための加熱条件は適宜選択することができる力 S、加熱 温度は、塗布の対象である基材の耐熱限界温度以下であることが必要である。
[0038] 本発明によれば、導電層を気相重合で形成できるため、均一な導電層を製造でき る。また、 1の塗膜から、 2以上の層を形成することができるため、積層体の製造工程 が簡略化できる。
また、金属酸化物粒子を偏在化させることによって、積層体の耐擦傷性を向上する こと力 Sできる。
本発明の積層体は、反射防止膜の他にも、例えば、レンズ、選択透過膜フィルタ等 の光学用部品に使用できる。
[0039] 次に、本発明で使用する紫外線硬化性樹脂組成物について説明する。
紫外線硬化性樹脂組成物は、 (A)重合性不飽和基を有する有機化合物 (Ab)を 結合させてなる金属酸化物粒子、（B)エチレン性不飽和基含有含フッ素重合体と、 ( C)速揮発溶剤と、 (D)遅揮発溶剤とを含有することを特徴とする。
[0040] 1.紫外線硬化性樹脂組成物の各構成成分について具体的に説明する。
(A)重合性不飽和基を有する有機化合物 (Ab)を結合させてなる金属酸化物粒子 本発明に用いられる (A)成分は、金属酸化物粒子 (Aa)と、重合性不飽和基を含 む有機化合物 (Ab)とを結合させてなる粒子である（以下、「反応性粒子」、「(A)成 分」又は「(A)成分の粒子」ということがある）。ここで、結合とは、共有結合であっても よいし、物理吸着等の非共有結合であってもよい。
[0041] これらの金属酸化物粒子 (Aa)としては、例えば、酸化チタン、シリカ、アルミナ、ジ ノレコユア、酸化亜鉛、酸化ゲルマニウム、酸化インジウム、酸化スズ、アンチモン含有 酸化スズ (ATO)、スズ含有酸化インジウム（ITO)、リンドープ酸化錫（PTO)粒子、 酸化アンチモン、酸化セリウム等の粒子を挙げることができる。中でも、高硬度の観点 から、シリカ、ァノレミナ、ジルコユア及び酸化アンチモンの粒子が好ましぐ特にジル コニァ粒子が好ましい。また、ジルコニウムやチタニウム等の酸化物粒子を用いること により高屈折率の硬化被膜を得ることができるし、 ATO粒子等を用いることにより、硬 化被膜に導電性を付与することもできる。高屈折率の硬化被膜を得るためには、波 長 598nmにおける屈折率が 1. 5以上の金属酸化物粒子（Aa)が好ましい。このため 、このような目的のためには、シリカ（屈折率約 1. 45)粒子は好ましくない。
[0042] これらの金属酸化物粒子 (Aa)は 1種単独で又は 2種以上を組み合わせて用いるこ とができる。さらには、金属酸化物粒子 (Aa)は、粉体状又は分散液であることが好ま しい。分散液である場合、他の成分との相溶性、分散性の観点から、分散媒は、有機 溶剤が好ましい。このような有機溶剤としては、例えば、メタノーノレ、エタノール、イソ プロパノール、ブタノール、ォクタノール等のアルコール類；アセトン、メチルェチルケ トン、メチルイソブチルケトン、シクロへキサノン等のケトン類；酢酸ェチル、酢酸ブチ ノレ、乳酸ェチル、 Ύ—ブチ口ラタトン、プロピレングリコールモノメチルエーテルァセテ ート、プロピレングリコーノレモノェチノレエーテノレアセテート等のエステノレ類；エチレン グリコーノレモノメチノレエーテノレ、ジエチレングリコーノレモノブチノレエーテノレ等のエーテ ル類；ベンゼン、トルエン、キシレン等の芳香族炭化水素類；ジメチルフオルムアミド、 ジメチルァセトアミド、 N—メチルピロリドン等のアミド類を挙げることができる。中でも、 メタノーノレ、イソプロパノール、ブタノール、メチルェチルケトン、メチルイソブチルケト ン、酢酸ェチル、酢酸ブチル、トルエン、キシレンが好ましい。
[0043] 金属酸化物粒子 (Aa)の数平均粒子径は、電子顕微鏡法による測定で、 0. 001 μ m〜2 μ m力 S好ましく、 0. 001 μ m〜0. 2 μ m力 Sさらに好ましく、 0. 001 μ m〜0. 1 μ mが特に好ましい。数平均粒子径が 2 μ mを越えると、硬化物としたときの透明性 が低下したり、被膜としたときの表面状態が悪化したりする傾向がある。また、粒子の 分散性を改良するために各種の界面活性剤やアミン類を添加してもよい。粒子形状 が棒状（アスペクト比が 1を超えて 10以下の形状を言う）の場合には、短径を粒子径 とした。
[0044] シリカ粒子の市販品としては、例えば、コロイダルシリカとして、 日産化学工業（株） 製 商品名：メタノールシリカゾル、 IPA_ST、 MEK_ ST、 NBA- ST, XBA—ST 、 DMAC— ST、 ST— UP、 ST— OUP、 ST— 20、 ST— 40、 ST_C、 ST_N、 ST — 0、 ST— 50、 ST—〇L等を挙げることができる。また粉体シリカとしては、 日本ァェ ロジル（株）製 商品名：ァエロジル 130、ァェロジノレ 300、ァエロジノレ 380、ァエロジ ノレ TT600、ァェロジノレ 0X50、旭硝子（株）製 商品名：シルデックス Η31、 Η32、 Η 51、 H52、 H121、 H122、 曰本シリカ工業（株）製 商品名： E220A、 E220、富士 シリシァ (株)製 商品名： SYLYSIA470、 日本板硝子 (株)製 商品名： SGフレーク 等を挙げることができる。
[0045] また、アルミナの水分散品としては、 日産化学工業 (株)製 商品名：アルミナゾル—
100、一 200、一520 ;アルミナのイソプロパノール分散品としては、住友大阪セメント (株)製 商品名： AS— 150I ;アルミナのトノレェン分散品としては、住友大阪セメント（ 株)製 商品名： AS— 150T;ジノレコユアのトノレエン分散品としては、住友大阪セメン ト (株)製 商品名： HXU_ 110JC；アンチモン酸亜鉛粉末の水分散品としては、 日 産化学工業 (株)製 商品名：セルナックス;アルミナ、酸化チタン、酸化スズ、酸化ィ ンジゥム、酸化亜鉛等の粉末及び溶剤分散品としては、シーアィ化成 (株)製 商品 名：ナノテック；アンチモンドープ酸化スズの水分散ゾルとしては、石原産業 (株)製 商品名： SN_ 100D ; IT〇粉末としては、三菱マテリアル (株)製の製品；酸化セリウ ム水分散液としては、多木化学 (株)製 商品名：ニードラール等を挙げることができる
[0046] 金属酸化物粒子 (Aa)の形状は球状、中空状、多孔質状、棒状 (アスペクト比が 1を 超えて 10以下の形状を言う）、板状、繊維状、又は不定形状であり、好ましくは、棒状 である。金属酸化物粒子 (Aa)の比表面積（窒素を用いた BET比表面積測定法によ る）は、好ましくは、 10〜： 1000m2/gであり、さらに好ましくは、 100〜500m2/gで ある。これら金属酸化物粒子 (Aa)の使用形態は、乾燥状態の粉末、又は水もしくは 有機溶剤で分散した状態で用いることができる。例えば、分散液として当業界に知ら れている微粒子状の金属酸化物粒子の分散液を直接用いることができる。特に、硬 化物に優れた透明性を要求する用途においては金属酸化物粒子の分散液の利用 が好ましい。
[0047] 重合性不飽和基を有する有機化合物 (Ab)
本発明に用いられる有機化合物 (Ab)は、重合性不飽和基を有する化合物であり、 さらに、下記式 (A—1)に示す基を含む有機化合物であることが好ましい。また、 [ - 0_C ( =〇） _NH_]基を含み、さらに、 [ _〇_C ( = S) _NH_]基及び [_ S _ C ( = 0) _NH_]基の少なくとも 1を含むものであることが好ましレ、。また、この有機 化合物 (Ab)は、分子内にシラノール基を有する化合物又は加水分解によってシラノ 一ル基を生成する化合物であることが好ましレ、。
[0048] [化 8]
|_|
— U-C— N—— （A— 1)
I！
V
[式中、 Uは、 NH、〇（酸素原子）又は S (ィォゥ原子）を示し、 Vは、〇又は Sを示す。
]
[0049] (i)重合性不飽和基
有機化合物 (Ab)に含まれる重合性不飽和基としては特に制限はないが、例えば、 アタリロイル基、メタクリロイル基、ビュル基、プロぺニル基、ブタジェニル基、スチリル 基、ェチュル基、シンナモイル基、マレエート基、アクリルアミド基を好適例として挙げ ること力 Sできる。
この重合性不飽和基は、活性ラジカル種により付加重合をする構成単位である。
[0050] (ii)前記式 (A— 1)に示す基
有機化合物に含まれる前記式 (A— 1)に示す基 [― U— C (=V)— NH ]は、具 体的には、 [— 0— C ( =〇）一NH— ]、 [ 0— C ( = S)—NH— ]、 [- S-C ( = 0) 一 NH ]、 [一 NH— C ( =〇）一 NH ]、 [一 NH— C ( = S)— NH ]、及び [一 S C ( = S)—NH ]の 6種である。これらの基は、 1種単独で又は 2種以上を組合わ せて用いることができる。中でも、熱安定性の観点から、 [― O— C ( = 0)— NH— ] 基と、 [ー0— C ( = S)—NH ]基及び [ S— C ( =〇）一 NH ]基の少なくとも 1つ とを併用することが好ましい。
前記式 (A— 1 )に示す基 [ U— C ( = V)— NH ]は、分子間におレ、て水素結合 による適度の凝集力を発生させ、硬化物にした場合、優れた機械的強度、基材ゃ高 屈折率層等の隣接層との密着性及び耐熱性等の特性を付与せしめるものと考えら れる。
[0051] (iii)シラノール基又は加水分解によってシラノール基を生成する基
有機化合物 (Ab)は、分子内にシラノール基を有する化合物又は加水分解によつ てシラノール基を生成する化合物であることが好ましレ、。このようなシラノール基を生 成する化合物としては、ケィ素原子にアルコキシ基、ァリールォキシ基、ァセトキシ基 、アミノ基、ハロゲン原子等が結合した化合物を挙げることができるが、ケィ素原子に アルコキシ基又はァリールォキシ基が結合した化合物、即ち、アルコキシシリル基含 有化合物又はァリールォキシシリル基含有化合物が好ましい。
シラノール基又はシラノール基を生成する化合物のシラノール基生成部位は、縮合 反応又は加水分解に続いて生じる縮合反応によって、金属酸化物粒子 (Aa)と結合 する構成単位である。
[0052] (iv)好ましい態様
有機化合物 (Ab)の好ましレ、具体例としては、例えば、下記式 (A_ 2)に示す化合 物を挙げることができる。
[0053] [化 9]
Figure imgf000021_0001
[0054] 式中、 R24、 R25は、同一でも異なっていてもよぐ水素原子又は炭素数:!〜 8のアル キル基若しくはァリール基であり、例えば、メチノレ、ェチル、プロピル、ブチル、ォクチ ノレ、フエニル、キシリル基等を挙げることができる。ここで、 jは、：!〜 3の整数である。
[0055] [ (R240) R25 Si— ]で示される基としては、例えば、トリメトキシシリル基、トリェトキ
j 3-j
シシリル基、トリフエノキシシリル基、メチルジメトキシシリル基、ジメチルメトキシシリル 基等を挙げることができる。このような基のうち、トリメトキシシリル基又はトリエトキシシ リル基等が好ましい。
R26は、炭素数 1〜： 12の脂肪族又は芳香族構造を有する 2価の有機基であり、鎖状 、分岐状又は環状の構造を含んでいてもよい。具体例として、メチレン、エチレン、プ ロピレン、ブチレン、へキサメチレン、シクロへキシレン、フエ二レン、キシリレン、ドデカ メチレン等を挙げることができる。
R27は、 2価の有機基であり、通常、分子量 14から 1万、好ましくは、分子量 76から 5 00の 2価の有機基の中から選ばれる。具体例として、へキサメチレン、オタタメチレン 、ドデカメチレン等の鎖状ポリアルキレン基；シクロへキシレン、ノルボル二レン等の脂 環式又は多環式の 2価の有機基；フエ二レン、ナフチレン、ビフエ二レン、ポリフエニレ ン等の 2価の芳香族基;及びこれらのアルキル基置換体、ァリール基置換体を挙げる こと力 Sできる。また、これら 2価の有機基は炭素及び水素原子以外の元素を含む原子 団を含んでいてもよぐポリエーテル結合、ポリエステル結合、ポリアミド結合、ポリ力 ーボネート結合を含むこともできる。
R28は、（k+ 1)価の有機基であり、好ましくは、鎖状、分岐状又は環状の飽和炭化 水素基、不飽和炭化水素基の中から選ばれる。
Zは、活性ラジカル種の存在下、分子間架橋反応をする重合性不飽和基を分子中 に有する 1価の有機基を示す。また、 kは、好ましくは、：!〜 20の整数であり、さらに好 ましくは、 1〜10の整数、特に好ましくは、：!〜 5の整数である。
[0056] 式 (A— 2)で示される化合物の具体例として、下記式 (A— 4)及び (A— 5)で示さ れる化合物が挙げられる。
[0057] [化 10]
Figure imgf000022_0001
[式中、「Acryl」は、アタリロイル基を示す。 「Me」は、メチル基を示す。 ]
本発明で用いられる有機化合物 (Ab)の合成は、例えば、特開平 9— 100111号 公報に記載された方法を用いることができる。好ましくは、メルカプトプロピルトリメトキ シシランとイソホロンジイソシァネートをジブチルスズジラウレート存在下で混合し、 60 〜70°C数時間程度反応させた後に、ペンタエリスリトールトリアタリレートを添加して、 さらに 60〜70°C数時間程度反応させることにより製造される。 [0059] 反応性粒子（(A)成分）
シラノール基又は加水分解によってシラノール基を生成する基を有する有機化合 物 (Ab)を金属酸化物粒子 (Aa)と混合し、加水分解させ、両者を結合させる。得られ る反応性粒子（ (A)成分）中の有機重合体成分即ち加水分解性シランの加水分解物 及び縮合物の割合は、通常、乾燥粉体を空気中で完全に燃焼させた場合の質量減 少％の恒量値として、例えば空気中で室温から通常 800°Cまでの熱質量分析により 求めること力 Sできる。
[0060] 金属酸化物粒子 (Aa)への有機化合物 (Ab)の結合量は、反応性粒子（ (A)成分）
(金属酸化物粒子 (Aa)及び有機化合物 (Ab)の合計）を 100質量％として、好ましく は、 0. 01質量％以上であり、さらに好ましくは、 0. 1質量％以上、特に好ましくは、 1 質量％以上である。金属酸化物粒子 (Aa)に結合した有機化合物 (Ab)の結合量が 0. 01質量％未満であると、組成物中における反応性粒子（(A)成分）の分散性が十 分でなぐ得られる硬化物の透明性、耐擦傷性が十分でなくなる場合がある。また、 反応性粒子（ (A)成分)製造時の原料中の金属酸化物粒子 (Aa)の配合割合は、好 ましくは、 5〜99質量0 /0であり、さらに好ましくは、 10〜98質量0 /0である。
[0061] 反応性粒子（ (A)成分)の紫外線硬化性樹脂組成物中における配合 (含有)量は、 有機溶剤を除く組成物全量を 100質量％として、 10〜90質量％の範囲内であること が好ましぐ 20〜80質量％の範囲であることがより好ましぐ 40〜80質量％の範囲 であることがより好ましい。 10質量％未満であると、硬化膜の硬度が不十分であるか 、又は高屈折率のものが得られないことがある。 90質量％を超えると、成膜性が不十 分となることがある。この場合、反応性粒子（(A)成分)を構成する金属酸化物粒子（ Aa)の含有量は、反応性粒子（(A)成分）の 65〜95質量％であることが好ましい。尚 、反応性粒子（ (A)成分)の量は、固形分を意味し、反応性粒子（ (A)成分)が分散 液の形態で用いられるときは、その配合量には分散媒の量を含まない。
[0062] (B)エチレン性不飽和基含有含フッ素重合体
本発明で用いるエチレン性不飽和基含有含フッ素重合体は、 1個のイソシァネート 基と、少なくとも 1個のエチレン性不飽和基とを含有する化合物 (B— 1)と、水酸基含 有含フッ素重合体 (B— 2)とを反応させて得られ、イソシァネート基 Z水酸基のモル 比が 1. 1〜： 1. 9の割合で反応させて得られるものが好ましい。
[0063] (B- 1) 1個のイソシァネート基と、少なくとも 1個のエチレン性不飽和基とを含有する 化合物
化合物（B— 1)としては、分子内に、 1個のイソシァネート基と、少なくとも 1個のェチ レン性不飽和基を含有している化合物であれば特に制限されるものではなレ、。尚、ィ ソシァネート基を 2個以上含有すると、水酸基含有含フッ素重合体と反応させる際に ゲルィ匕を起こす可能性がある。また、上記エチレン性不飽和基としては、紫外線硬化 性樹脂組成物をより容易に硬化させることができることから、（メタ）アタリロイル基がよ り好ましレ、。このような化合物としては、 2- (メタ）アタリロイルォキシェチルイソシァネ ート、 2_ (メタ）アタリロイルォキシプロピルイソシァネート、 1，1 _ビス [(メタ)アタリロイ ルォキシメチル]ェチルイソシァネートの一種単独又は二種以上の組み合わせが挙 げられる。
[0064] 尚、このような化合物は、ジイソシァネート及び水酸基含有 (メタ）アタリレートを反応 させて合成することもできる。この場合、ジイソシァネートの例としては、 2,4 トリレン ジイソシァネート、 2,6 トリレンジイソシァネート、 1,3—キシリレンジイソシァネート、 1 イソシァネート、 p—フエ二レンジイソシァネート、 3,3' ジメチルー 4,4'ージフエニル メタンジイソシァネート、 4,4'ージフエニルメタンジイソシァネート、 3,3 'ージメチルフ ェニレンジイソシァネート、 4,4'ービフエ二レンジイソシァネート、 1, 6—へキサンジィ ソシァネート、イソホロンジイソシァネート、メチレンビス（4ーシクロへキシルイソシァネ アート）、 2,2,4 トリメチルへキサメチレンジイソシァネート、ビス（2—イソシァネート ェチノレ）フマレート、 6 _イソプロピノレ一 1，3 _フエニノレジイソシァネート、 4—ジフエ二 ルプロパンジイソシァネート、リジンジイソシァネート、水添ジフヱニルメタンジイソシァ ネ一ト、 1， 3 _ビス（イソシァネートメチル）シクロへキサン、テトラメチルキシリレンジィ ソシァネ一ト、 2, 5 (又は 6) _ビス（イソシァネートメチル）一ビシクロ [2. 2. 1]ヘプタ ン等の一種単独又は二種以上の組み合わせが挙げられる。これらの中では、 2，4_ トリレンジイソシァネート、イソホロンジイソシァネート、キシリレンジイソシァネート、メチ レンビス（4—シクロへキシルイソシァネア一ト）、 1， 3 _ビス（イソシァネートメチル）シ クロへキサンが特に好ましレ、。
[0065] また、水酸基含有 (メタ）アタリレートの例としては、 2—ヒドロキシェチル (メタ）アタリ ート、力プロラタトン（メタ）アタリレート、ポリプロピレングリコール（メタ）アタリレート、ジ ペンタエリスリトールペンタ（メタ）アタリレート、ペンタエリスリトーノレトリ（メタ）アタリレー ト、ペンタエリスリトールジ（メタ）アタリレートモノステアレート、イソシァヌル酸 E〇変性 ジ (メタ）アタリレート等一種単独又は二種以上の組み合わせが挙げられる。これらの 中では、 2—ヒドロキシェチル（メタ）アタリレート、ペンタエリスリトールトリ（メタ）アタリレ ートが特に好ましい。尚、水酸基含有多官能 (メタ）アタリレートの市販品としては、例 えば、大阪有機化学 (株)製商品名 HEA、 日本化薬 (株)製 商品名 KAYARAD DPHA、 PET_ 30、東亞合成（株）製 商品名 ァロニックス M_ 215、M_ 233 、 M— 305、 M— 400等として人手すること力でさる。
[0066] ジイソシァネート及び水酸基含有多官能 (メタ）アタリレートから合成する場合には、 ジイソシァネート 1モルに対し、水酸基含有多官能 (メタ）アタリレートの添加量を 1〜1 . 2モルとするのが好ましい。
[0067] このような化合物の合成方法としては、ジイソシァネート及び水酸基含有 (メタ）ァク リレートを一括で仕込んで反応させる方法、水酸基含有 (メタ）アタリレート中にジイソ シァネートを滴下して反応させる方法等を挙げることができる。
[0068] (B— 2)水酸基含有含フッ素重合体
水酸基含有含フッ素重合体 (B— 2)は、下記構造単位 (a)、（b)、 （c)から構成され ていることが好ましぐさらに構造単位 (d)、（e)、（f)を含むことがより好ましい。
[0069] 構造単位（a)
構造単位 (a)は、下記一般式（1)で表される。
[化 11]
F R1
— c-c—— （
[式中、 R1はフッ素原子、フルォロアルキル基、又は— OR2で表される基（R2はアルキ ル基、又はフルォロアルキル基を示す）を示す]
[0070] 上記一般式（1)において、 R1及び R2のフルォロアルキル基としては、トリフルォロメ チル基、パーフルォロェチル基、パーフルォロプロピル基、パーフルォロブチル基、 パーフルォ口へキシル基、パーフルォロシクロへキシル基等の炭素数 1〜6のフルォ 口アルキル基が挙げられる。また、 R2のアルキル基としては、メチノレ基、ェチル基、プ 口ピル基、ブチル基、へキシル基、シクロへキシル基等の炭素数 1〜6のアルキル基 が挙げられる。
[0071] 構造単位（a)は、含フッ素ビニル単量体を重合成分として用いることにより導入する こと力 Sできる。このような含フッ素ビュル単量体としては、少なくとも 1個の重合性不飽 和二重結合と、少なくとも 1個のフッ素原子とを有する化合物であれば特に制限され るものではない。このような例としてはテトラフルォロエチレン、へキサフルォロプロピ レン、 3, 3, 3 _トリフルォロプロピレン等のフルォロレフィン類；アルキルパーフルォ ロビニルエーテル又はアルコキシアルキルパーフルォロビニルエーテル類；パーフル ォロ（メチルビニルエーテル）、パーフルォロ（ェチルビニルエーテノレ）、（プロピルビ ニルエーテル）、パーフルォロ（ブチルビニルエーテル）、パーフルォロ（イソブチルビ ニルエーテル）等のパーフルォロ（アルキルビュルエーテノレ）類；パーフルォロ（プロ ポキシプロピルビエルエーテノレ）等のパーフルォロ（アルコキシアルキルビエルエー テル）類の一種単独又は二種以上の組み合わせが挙げられる。これらの中でも、へ キサフルォロプロピレンとパーフルォロ（アルキルビュルエーテノレ）又はパーフルォロ (アルコキシアルキルビエルエーテル）がより好ましぐこれらを組み合わせて用いるこ とがさらに好ましい。
[0072] 尚、構造単位 (a)の含有率は、水酸基含有含フッ素重合体 (B— 2)の全体量を 10 0モノレ0 /0としたときに、 20〜70モノレ0 /0である。この理由は、含有率が 20モル0 /0未満 になると、本願が意図するところのフッ素含有材料の光学的特徴である、低屈折率の 発現が困難となる場合があるためであり、一方、含有率が 70モル％を超えると、水酸 基含有含フッ素重合体 (B— 2)の有機溶剤への溶解性、透明性、又は基材への密 着性が低下する場合があるためである。また、このような理由により、構造単位（a)の 含有率を、水酸基含有含フッ素重合体 (B— 2)の全体量に対して、 25〜65モル％と するのがより好ましぐ 30〜60モル0 /0とするのがさらに好ましレ、。
[0073] 構造単位 (b)
c H H I I
構造単位 (b)は、下記一般式 (2)で表される。
RCRII
[化 12]
(2)
[式中、 R3は水素原子又はメチル基を、 R4はアルキル基、—(CH ) OR5若しく
2
は— OCOR5で表される基（R5はアルキル基、又はグリシジル基を、 Xは 0又は 1の数 を示す）、カルボキシル基、又はアルコキシカルボ二ル基を示す]
[0074] 一般式（2)におレ、て、 R4又は R5のアルキル基としては、メチノレ基、ェチル基、プロ ピノレ基、へキシル基、シクロへキシル基、ラウリル基等の炭素数 1〜 12のアルキル基 が挙げられ、アルコキシカルボニル基としては、メトキシカルボニル基、エトキシカルボ ニル基等が挙げられる。
[0075] 構造単位 (b)は、上述の置換基を有するビニル単量体を重合成分として用いること により導入すること力 Sできる。このようなビュル単量体の例としては、メチルビュルエー テノレ、ェチノレビニノレエーテノレ、 n—プロピノレビニノレエーテノレ、イソプロピノレビニノレエ一 テル、 n—ブチルビニルエーテル、イソブチルビュルエーテル、 tert ブチルビュル エーテノレ、 n—ペンチノレビニノレエーテノレ、 n—へキシノレビニノレエーテノレ、 n—ォクチ ノレビエルエーテル、 n—ドデシルビニルエーテル、 2—ェチルへキシルビニルエーテ ノレ、シクロへキシルビニルエーテル等のアルキルビニルエーテルもしくはシクロアル キルビュルエーテル類；ェチルァリルエーテル、ブチルァリルエーテル等のァリルェ 一テル類；酢酸ビュル、プロピオン酸ビュル、酪酸ビニル、ビバリン酸ビュル、力プロ ン酸ビエル、バーサチック酸ビエル、ステアリン酸ビニル等のカルボン酸ビエルエステ ル類；メチル (メタ）アタリレート、ェチル (メタ）アタリレート、 n ブチル (メタ）アタリレー ト、イソブチル (メタ）アタリレート、 2—メトキシェチル (メタ）アタリレート、 2—エトキシェ チル (メタ）アタリレート、 2- (n—プロボキシ）ェチル (メタ）アタリレート等の（メタ）ァク リル酸エステル類；（メタ）アクリル酸、クロトン酸、マレイン酸、フマル酸、ィタコン酸等 の不飽和カルボン酸類等の一種単独又は二種以上の組み合わせが挙げられる。
[0076] 尚、構造単位 (b)の含有率は、水酸基含有含フッ素重合体 (B— 2)の全体量を 10 0モノレ0 /0としたときに、 10〜70モル0 /0である。この理由は、含有率が 10モル0 /0未満 になると、水酸基含有含フッ素重合体 (B— 2)の有機溶剤への溶解性が低下する場 合があるためであり、一方、含有率が 70モル％を超えると、水酸基含有含フッ素重合 体 (B— 2)の透明性、及び低反射率性等の光学特性が低下する場合があるためであ る。また、このような理由により、構造単位 (b)の含有率を、水酸基含有含フッ素重合 体（B— 2)の全体量に対して、 20〜60モノレ0 /0とするの力より好ましく、 30〜60モノレ %とするのがさらに好ましい。
[0077] 構造単位 (c)
構造単位 (c)は、下記一般式 (3)で表される。
[化 13] （3)
Figure imgf000028_0001
[式中、 R6は水素原子、又はメチル基を、 R7は水素原子、又はヒドロキシアルキル基 を、 Vは 0又は 1の数を示す]
[0078] 一般式（3)において、 R7のヒドロキシアルキル基としては、 2—ヒドロキシェチル基、 2—ヒドロキシプロピル基、 3—ヒドロキシプロピル基、 4ーヒドロキシブチル基、 3—ヒド ロキシブチル基、 5—ヒドロキシペンチル基、 6—ヒドロキシへキシル基が挙げられる。
[0079] 構造単位 (c)は、水酸基含有ビニル単量体を重合成分として用いることにより導入 すること力 Sできる。このような水酸基含有ビニル単量体の例としては、 2—ヒドロキシェ チルビュルエーテル、 3—ヒドロキシプロピルビュルエーテル、 2—ヒドロキシプロピル ビュルエーテル、 4ーヒドロキシブチルビニルエーテル、 3—ヒドロキシブチルビュル エーテル、 5—ヒドロキシペンチルビニルエーテル、 6—ヒドロキシへキシルビニルェ 一テル等の水酸基含有ビュルエーテル類、 2—ヒドロキシェチルァリルエーテル、 4 —ヒドロキシブチルァリルエーテル、グリセロールモノアリルエーテル等の水酸基含有 ァリルエーテル類、ァリルアルコール等が挙げられる。また、水酸基含有ビュル単量 体としては、上記以外にも、 2—ヒドロキシェチル (メタ）アタリレート、 2—ヒドロキシブ チル (メタ）アタリレート、 2—ヒドロキシプロピル (メタ）アタリレート、力プロラタトン (メタ） アタリレート、ポリプロピレングリコール (メタ）アタリレート等を用いることができる。
[0080] 尚、構造単位（c)の含有率を、水酸基含有含フッ素重合体 (B— 2)の全体量を 100 モル％としたときに、 5〜70モル％とすることが好ましレ、。この理由は、含有率が 5モ ル％未満になると、水酸基含有含フッ素重合体 (B— 2)の有機溶剤への溶解性が低 下する場合があるためであり、一方、含有率が 70モル％を超えると、水酸基含有含フ ッ素重合体 (B— 2)の透明性、及び低反射率性等の光学特性が低下する場合があ るためである。また、このような理由により、構造単位（c)の含有率を、水酸基含有含 フッ素重合体（B— 2)の全体量に対して、 5〜40モノレ％とするの力より好ましく、 5〜3 0モル％とするのがさらに好ましい。
[0081] 構造単位 (d)及び構造単位 (e)
また、水酸基含有含フッ素重合体 (B— 2)は、さらに下記構造単位 (d)を含んで構 成することも好ましい。以下、構造単位 (d)について説明する。
構造単位 (d)は、下記一般式 (4)で表される。
[化 14]
R8 R9
[式中、 R8及び R9は、同一でも異なっていてもよぐ水素原子、アルキル基、ハロゲン 化アルキル基、又はァリール基を示す]
[0082] 一般式（4)におレ、て、 又は R9のアルキル基としては、メチル基、ェチル基、プロ ピル基等の炭素数 1〜3のアルキル基力 S、ハロゲン化アルキル基としてはトリフルォロ メチル基、パーフルォロェチル基、パーフルォロプロピル基、パーフルォロブチル基 等の炭素数 1〜4のフルォロアルキル基等力 S、ァリール基としてはフエニル基、ベンジ ル基、ナフチル基等がそれぞれ挙げられる。
[0083] 構造単位（d)は、前記一般式 (4)で表されるポリシロキサンセグメントを有するァゾ 基含有ポリシロキサン化合物を用いることにより導入することができる。このようなァゾ 基含有ポリシロキサン化合物の例としては、下記一般式（7)で表される化合物が挙げ られる。
[0084] [化 15]
Figure imgf000030_0001
(7)
[式中、 R1Q〜R13、 R"〜R17、 p、 q、 s、 t、及び yは、下記一般式（5)と同じであり、 zは ：!〜 20の数である。 ]
[0085] 一般式（7)で表される化合物を用いた場合には、構造単位（d)は、下記構造単位（ e)の一部として水酸基含有含フッ素重合体に含まれる。
構造単位 (e)は、下記一般式（5)で表される。
[化 16]
R11 R14 R15 R10
— C— (CH2)qCONH(CH2)s— Si— {OSi)y(CH2)tNHCO(CH2)p-C— (5) R13 R16 R17 R12
[式中、 R1Q〜R13は水素原子、アルキル基、又はシァノ基を示し、 R14〜R17は水素原 子又はアルキル基を示し、 p、 qは:!〜 6の数、 s、 tは 0〜6の数、 yは:!〜 200の数を示 す。 ]
[0086] 一般式（5)におレ、て、 R1Q〜R13のアルキル基としては、メチル基、ェチル基、プロピ ル基、へキシル基、シクロへキシル基等の炭素数 1〜 12のアルキル基が挙げられ、 R M〜R17のアルキル基としてはメチル基、ェチル基、プロピル基等の炭素数 1〜3のァ ルキル基が挙げられる。
[0087] 本発明において、上記一般式（7)で表されるァゾ基含有ポリシロキサン化合物とし ては、下記一般式 (8)で表される化合物が特に好ましレ、。
[0088] [化 17]
Figure imgf000031_0001
(8)
[式中、 y及び zは、上記一般式（7)と同じである。 ]
[0089] 尚、構造単位（d)の含有率を、水酸基含有含フッ素重合体 (B— 2)の全体量を 100 モル％としたときに、 0. 1〜： 10モル％とすることが好ましレ、。この理由は、含有率が 0 . 1モル％未満になると、硬化後の塗膜の表面滑り性が低下し、塗膜の耐擦傷性が 低下する場合があるためであり、一方、含有率が 10モル％を超えると、水酸基含有 含フッ素重合体 (B— 2)の透明性に劣り、コート材として使用する際に、塗布時にハ ジキ等が発生し易くなる場合があるためである。また、このような理由により、構造単 位（d)の含有率を、水酸基含有含フッ素重合体 (B— 2)の全体量に対して、 0.：!〜 5 モル％とするのがより好ましぐ 0·：!〜 3モル％とするのがさらに好ましい。同じ理由に より、構造単位 (e)の含有率は、その中に含まれる構造単位 (d)の含有率を上記範 囲にするよう決定することが望ましい。
[0090] 構造単位 (f)
また、水酸基含有含フッ素重合体 (B— 2)は、さらに上記構造単位 (f)を含んで構 成することも好ましい。以下、構造単位 (f)について説明する。
[0091] 構造単位 (f )は、下記一般式（6)で表される。
[化 18]
H R18
— C-C— (6)
H H
[式中、 R18は乳化作用を有する基を示す]
[0092] 一般式 (6)において、 R18の乳化作用を有する基としては、疎水性基及び親水性基 の双方を有し、かつ、親水性基がポリエチレンオキサイド、ポリプロピレンオキサイド等 のポリエーテル構造である基が好ましい。
[0093] このような乳化作用を有する基の例としては下記一般式 (9)で表される基が挙げら れる。
[0094] [化 19]
Figure imgf000032_0001
[式中、 nは 1〜20の数、 mは 0〜4の数、 uは 3〜50の数を示す]
[0095] 構造単位 (f)は、反応性乳化剤を重合成分として用いることにより導入することがで きる。このような反応性乳化剤としては、下記一般式（10)で表される化合物が挙げら れる。
[0096] [化 20]
Figure imgf000032_0002
[式中、 n、 m、及び uは、上記一般式（9)と同様である]
[0097] 尚、構造単位 (f)の含有率を、水酸基含有含フッ素重合体 (B— 2)の全体量を 100 モル％としたときに、 0. ：!〜 5モル％とすることが好ましレ、。この理由は、含有率が 0. 1モル％以上になると、水酸基含有含フッ素重合体 (B— 2)の溶剤への溶解性が向 上し、一方、含有率力 ¾モル％以内であれば、紫外線硬化性樹脂組成物の粘着性 が過度に増加せず、取り扱いが容易になり、コート材等に用いても耐湿性が低下しな いためである。また、このような理由により、構造単位 (f)の含有率を、水酸基含有含 フッ素重合体（B— 2)の全体量に対して、 0· ：!〜 3モル％とするのがより好ましぐ 0. 2〜3モル0 /0とするのがさらに好ましい。
[0098] 水酸基含有含フッ素重合体 (B— 2)の分子量
水酸基含有含フッ素重合体 (B— 2)は、ゲルパーミエーシヨンクロマトグラフィー（以 下「GPC」という。）で、テトラヒドロフラン（以下「THF」という。）を溶剤として測定した ポリスチレン換算数平均分子量が 5, 000〜500, 000であることが好ましい。この理 由は、数平均分子量が 5, 000未満になると、水酸基含有含フッ素重合体 (B— 2)の 機械的強度が低下する場合があるためであり、一方、数平均分子量が 500, 000を 超えると、紫外線硬化性樹脂組成物の粘度が高くなり、薄膜コーティングが困難とな る場合がるためである。また、このような理由により、水酸基含有含フッ素重合体 (B— 2)のポリスチレン換算数平均分子量を 10, 000〜300, 000とするの力 Sより好ましく、 10, 000〜100， 000とするのカさらに好ましレ、。
[0099] 化合物（B— 1)と水酸基含有フッ素重合体 (B— 2)との反応モル比
本発明で用いるエチレン性不飽和基含有含フッ素重合体 (B)は、上述した、 1個の イソシァネート基と、少なくとも 1個のエチレン性不飽和基とを含有する化合物（B_ 1 )と、水酸基含有含フッ素重合体 (B— 2)とを、イソシァネート基 Z水酸基のモル比が 1.：!〜 1. 9の割合で反応させて得られることが好ましい。この理由は、モル比が 1. 1 未満になると耐擦傷性及び耐久性が低下する場合があるためであり、一方、モル比 が 1. 9を超えると、紫外線硬化性樹脂組成物の塗膜のアルカリ水溶液浸漬後の耐 擦傷性が低下する場合があるためである。また、このような理由により、イソシァネート 基/水酸基のモル比を、 1. 1〜： ! · 5とするのがより好ましぐ 1. 2〜： L5とするのがさ らに好ましい。
[0100] 紫外線硬化性樹脂組成物中における（B)エチレン性不飽和基含有含フッ素重合 体の含有量は、有機溶剤を除く組成物全量 100質量％に対して、通常 5〜70質量 %である。この理由は、含有量が 5質量％未満となると、紫外線硬化性樹脂組成物の 硬化塗膜の屈折率が高くなり、十分な反射防止効果が得られない場合があるためで あり、一方、添加量が 70質量％を超えると、硬化性樹脂組成物の硬化塗膜の耐擦傷 性が得られない場合があるためである。また、このような理由から、（B)成分の添加量 を 10〜50質量％とするのがより好ましぐ 25〜50質量％の範囲内の値とするのがさ らに好ましい。
[0101] (C)速揮発溶剤
紫外線硬化性樹脂組成物に含まれる（C)速揮発溶剤は、上記 (B)エチレン性不飽 和基含有含フッ素重合体の溶解性が高レ、 1種又は 2種以上の溶剤である。ここで、ェ チレン性不飽和基含有含フッ素重合体の溶解性が高いとは、 (B)エチレン性不飽和 基含有含フッ素重合体を 50質量％となるよう各溶剤に添加して、室温 8時間攪拌し たときに、 目視で均一な溶液となることをいう。そして、（C)速揮発溶剤の相対蒸発速 度は、後述の（D)遅揮発溶剤の相対蒸発速度よりも大きいことが必要である。ここで 、「相対蒸発速度」とは、酢酸ブチルが 90重量％蒸発するのに要する時間を基準と する蒸発速度の相対値をいい、詳細は、 TECHNIQUES OF CHEMISTRY VOL.2 ORGANIC SOLVENTS Physical Properties and methods of purification 4th ed. (Interscience Publishers, Inc. 1986 page62)に記載されているとおりである。 また、（C)速揮発溶剤は、上記 (A)重合性不飽和基を有する有機化合物 (Ab)を結 合させてなる金属酸化物粒子（ (A)成分の粒子）の分散安定性が低レ、ことが好ましレ、 。 （C)速揮発溶剤は、相対蒸発速度が (D)よりも大きぐ （B)エチレン性不飽和基含 有含フッ素重合体の溶解性が高いことにより、紫外線硬化性樹脂組成物を、基材に 塗布し、溶剤 (C)及び (D)を蒸発させる過程で、 (A)成分の粒子を偏在化させること ができる。
[0102] 本発明で (C)速揮発溶剤として用レ、ることができる溶剤としては、相対蒸発速度が 概ね 1. 7以上の溶剤であり、具体的には、メチルェチルケトン (MEK ;相対蒸発速度 3. 8)、イソプロパノール (IPA; 1. 7)、メチルイソプチルケトン（MIBK ;相対蒸発速 度 1. 6)、メチルアミルケトン（ΜΑΚ ; 0· 3)、アセトン、メチルプロピルケトン等が挙げ られる。
[0103] (D)遅揮発溶剤
紫外線硬化性樹脂組成物に含まれる (D)遅揮発溶剤は、上記 (Α)重合性不飽和 基を有する有機化合物 (Ab)を結合させてなる金属酸化物粒子（ (A)成分の粒子)の 分散安定性が高い、 1種又は 2種以上の溶剤である。ここで、 （A)成分の粒子の分散 安定性が高いとは、（A)成分の粒子のイソプロパノール分散液にガラス板を浸漬して (A)成分の粒子をガラス壁に付着させ、その (A)成分の粒子が付着したガラス板を 各溶剤に浸漬した場合に、（A)成分の粒子が該溶剤中に目視で均一に分散するこ とをいう。また、（D)遅揮発溶剤は、上記 (B)エチレン性不飽和基含有含フッ素重合 体の溶解性が低レ、ことが好ましレ、。
[0104] 本発明で（D)遅揮発溶剤として用いることができる溶剤としては、メタノール (相対 蒸発速度 2. 1)、イソプロパノール（IPA; 1. 7)、 n—ブタノール（n_Bu〇H ; 0. 5)、 tert—ブタノ一ノレ、プロピレングリコーノレモノメチノレエーテノレ、プロピレングリコーノレモ ノエチルエーテル、プロピレングリコールモノプロピルエーテル、ェチルセ口ソルブ、 プロピルセロソルブ、ブチルセ口ソルブ等が挙げられる。
[0105] 本発明で用いる（C)速揮発溶剤及び/又は (D)遅揮発溶剤は、通常、上記 (B)ェ チレン性不飽和基含有含フッ素重合体の製造に用いた溶剤をそのまま用いることが できる。
本発明で用いる（C)速揮発溶剤と（D)遅揮発溶剤は、相溶性であることが必要で ある。相溶性は、組成物の具体的構成において、（C)速揮発溶剤と（D)遅揮発溶剤 が分離しない程度の相溶性があれば足りる。
ここで、選択された溶剤が、本発明で用いる（C)速揮発溶剤又は (D)遅揮発溶剤 のいずれに該当するかは、選択された複数の溶剤種の間で相対的に決まるものであ り、それ故、相対蒸発速度が 1. 7のイソプロパノールは、（C)速揮発溶剤として用い られることもあれば、（D)遅揮発溶剤として用いられることもある。
[0106] 紫外線硬化性樹脂組成物中の溶剤（C)及び (D)以外の成分総量 100質量部に対 し、溶剤（C)及び溶剤（D)の合計量は、通常 300〜5000質量部、好ましくは 300〜 4000質量部、より好ましくは 300〜3000質量部を用いる。溶剤（C)と溶剤（D)の配 合比は、 1 : 99〜99 : 1の範囲で任意に選択することができる。
[0107] (E)少なくとも 2個以上の（メタ）アタリロイル基を含有する多官能 (メタ）アタリレートイ匕 合物、及び/又は、少なくとも 1個以上の（メタ）アタリロイル基を含有する含フッ素 (メ タ）アタリレートイ匕合物
少なくとも 2個以上の (メタ）アタリロイル基を含有する多官能 (メタ）アタリレートイ匕合 物（E— 1)は、紫外線硬化性樹脂組成物を硬化して得られる硬化物及びそれを用い た反射防止膜の耐擦傷性を高めるために用いられる。
少なくとも 1個以上の（メタ）アタリロイル基を含有する含フッ素 (メタ）アタリレートイ匕合 物（E— 2)は、紫外線硬化性樹脂組成物の屈折率を低下させるために用いられる。
[0108] 化合物（E—1)については、分子内に少なくとも 2個以上の（メタ）アタリロイル基を 含有する化合物であれば特に制限されるものではなレ、。このような例としては、ネオ ペンチルグリコールジ（メタ）アタリレート、トリメチロールプロパントリ（メタ）アタリレート、 ペンタエリスリトーノレトリ（メタ）アタリレート、トリメチロールェタントリ（メタ）アタリレート、 ペンタエリスリトールテトラ（メタ）アタリレート、ジペンタエリスリトールテトラ（メタ）アタリ レート、アルキル変性ジペンタエリスリトールテトラ（メタ）アタリレート、ジペンタエリスリ トールペンタ（メタ）アタリレート、アルキル変性ジペンタエリスリトールペンタ（メタ）ァク リレート、ジペンタエリスリトールへキサ（メタ）アタリレート、力プロラタトン変性ジペンタ エリスリトールへキサ（メタ）アタリレート、ジトリメチロールプロパンテトラ（メタ）アタリレ ート、「U_ 15HA」（商品名、新中村化学社製)等の一種単独又は二種以上の組み 合わせの他、下記式（11)で示される化合物が挙げられる。尚、これらのうち、ネオペ ンチルダリコールジ（メタ）アタリレート、ジペンタエリスリトールへキサ（メタ）アタリレート 、ペンタエリスリトールテトラ（メタ）アタリレート、ジペンタエリスリトールペンタ（メタ）ァク リレート及び力プロラタトン変性ジペンタエリスリトールへキサ（メタ）アタリレート、下記 式（11)で示される化合物が特に好ましレ、。
[0109] [化 21]
Figure imgf000036_0001
つ
[式中、「Acryl」は、アタリロイル基である。 ]
[0110] 化合物（E— 2)については、少なくとも 1個以上の（メタ）アタリロイル基を含有する含 フッ素 (メタ）アタリレートイ匕合物であれば特に制限されるものではなレ、。このような例と して、パーフルォロォクチルェチル（メタ）アタリレート、ォクタフルォロペンチル（メタ） アタリレート、トリフルォロェチル (メタ）アタリレート、等の一種単独又は二種以上の組 み合わせが挙げられる。
[0111] 紫外線硬化性樹脂組成物中における成分 (E)の含有量については、特に制限さ れるものではないが、有機溶剤を除く組成物全量 100質量％に対して、通常 5〜80 質量％である。この理由は、添加量が 5質量％未満となると、硬化性樹脂組成物の硬 化塗膜の耐擦傷性が得られない場合があるためであり、一方、添加量が 80質量％を 超えると、硬化性樹脂組成物の硬化塗膜の屈折率が高くなり、十分な反射防止効果 が得られない場合があるためである。また、このような理由から、成分 (E)の添加量を 5〜70質量％とするのがより好ましぐ 5〜50質量％の範囲内の値とするのがさらに 好ましい。
[0112] (F)光ラジカル重合開始剤
紫外線硬化性樹脂組成物においては、必要に応じて、放射線（光）照射により活性 ラジカル種を発生させる (F)光ラジカル重合開始剤 (放射線 (光)重合開始剤）を配 合すること力 Sできる。
[0113] 放射線 (光）重合開始剤としては、光照射により分解してラジカルを発生して重合を 開始せしめるものであれば特に制限はなぐ例えば、ァセトフヱノン、ァセトフヱノンべ ンジルケタール、 1—ヒドロキシシクロへキシルフェニルケトン、 2， 2—ジメトキシ一 1， 2—ジフエニルェタン一 1 _オン、キサントン、フルォレノン、ベンズアルデヒド、フルォ レン、アントラキノン、トリフエニルァミン、カルバゾール、 3 _メチルァセトフエノン、 4_ クロ口べンゾフエノン、 4, 4'ージメトキシベンゾフエノン、 4, 4'ージァミノべンゾフエノ ン、ベンゾインプロピルエーテル、ベンゾインェチルエーテル、ベンジルジメチルケタ ール、 1— (4—イソプロピルフエ二ル）一 2—ヒドロキシ一 2—メチルプロパン一 1—ォ ン、 2—ヒドロキシー2—メチルー 1 フエニルプロパンー1 オン、チォキサントン、ジ ェチルチオキサントン、 2—イソプロピルチォキサントン、 2—クロ口チォキサントン、 2 —メチノレ一 1 [4— (メチルチオ）フエニル]— 2—モルホリノ一プロパン一 1—オン、 2 —ベンジル 2—ジメチルァミノ一 1 (4—モルフォリノフエ二ル）一ブタノン一 1 , 4— (2 ヒドロキシエトキシ）フエニル一（2 ヒドロキシ一 2 プロピル）ケトン、 2, 4, 6 ト リメチルベンゾィルジフエニルフォスフィンオキサイド、ビス一（2, 6 ジメトキシベンゾ ィノレ）一 2, 4, 4 トリメチルペンチルフォスフィンォキシド、オリゴ（2 ヒドロキシ一 2 —メチル一 1 _ (4— (1 _メチルビュル）フエニル）プロパノン）等を挙げることができる
[0114] 放射線 (光）重合開始剤の市販品としては、例えば、チバ'スペシャルティ'ケミカル ズ（株）製 商品名：イノレガキュア 184, 369, 651, 500、 819, 907, 784, 2959, CGI1700, CGI1750, CGI1850, CG24— 61、ダロキュア 1116、 1173、 BAS F社製 商品名：ルシリン TPO、UCB社製 商品名：ュべクリル P36、フラテツリ' ランべルティ社製 商品名：ェザキュア一 KIP150、 KIP65LT、 KIP100F、 KT37 、 KT55、 ΚΤ〇46、 ΚΙΡ75/Β等を挙げることができる。
[0115] 本発明において必要に応じて用いられる光ラジカル重合開始剤（F)の配合量は、 有機溶剤を除く組成物全量を 100質量％として、 0. 01〜： 10質量％配合することが 好ましぐ 0. 1〜： 10質量％が、さらに好ましい。 0. 01質量％未満であると、硬化物と したときの硬度が不十分となることがあり、 10質量％を超えると、硬化物としたときに 内部（下層）まで硬化しないことがある。
[0116] (G)その他の成分
硬化性組成物には、本発明の効果を損なわない限り、必要に応じて、光増感剤、 重合禁止剤、重合開始助剤、レべリング剤、濡れ性改良剤、界面活性剤、可塑剤、 紫外線吸収剤、酸化防止剤、帯電防止剤、無機充填剤、顔料、染料、溶剤 (C)及び (D)以外の溶剤等を適宜配合できる。
[0117] 2.紫外線硬化性樹脂組成物の製造方法
組成物は、次のようにして製造できる。
反応性粒子分散液（ (Α)成分)及びエチレン性不飽和基含有フッ素重合体（ (Β)成 分)、必要に応じて、多官能 (メタ)アタリレート（(E)成分)、放射線 (光)重合開始剤（（ F)成分)等を攪拌機付きの反応容器に入れ 35°C〜45°Cで 2時間攪拌し紫外線硬 化性樹脂組成物とする。
溶剤を最初の反応性粒子分散液に使用した溶剤 ( a )と異なる種類の溶剤 ( β )に置 換する場合は、反応性粒子分散液の溶剤（ a )の質量に対して 1. 0倍の溶剤（ β )も 加え同様の条件で攪拌する。次にこの組成液を、ロータリーエバポレーターを用いて 固形分濃度 50%となる質量まで減圧濃縮し組成物とする。
[0118] 3.紫外線硬化性樹脂組成物の塗布（コーティング)方法
紫外線硬化性樹脂組成物は反射防止膜や被覆材の用途に好適であり、反射防止 や被覆の対象となる基材としては、例えば、プラスチック（ポリカーボネート、ポリメタク リレート、ポリスチレン、ポリエステル、ポリオレフイン、エポキシ、メラミン、トリァセチル セルロース、 ABS、 AS、ノルボルネン系樹脂等）、金属、木材、紙、ガラス、スレート 等を挙げることができる。これら基材の形状は板状、フィルム状又は 3次元成形体でも よぐコーティング方法は、通常のコーティング方法、例えばデイツビングコート、スプ レーコート、フローコート、シャワーコート、ロールコート、スピンコート、刷毛塗り等を 挙げること力 Sできる。これらのコーティングによる塗膜の厚さは、乾燥、硬化後、通常 0 .：!〜 400 x mであり、好ましくは、：!〜 200 μ πιである。
[0119] 4.紫外線硬化性樹脂組成物の硬化方法
紫外線硬化性樹脂組成物は、放射線（光）によって硬化させることができる。その線 源としては、組成物をコーティング後短時間で硬化させることができるものである限り 特に制限はないが、例えば、赤外線の線源として、ランプ、抵抗加熱板、レーザー等 を、また可視光線の線源として、 日光、ランプ、蛍光灯、レーザー等を、また紫外線の 線源として、水銀ランプ、ハライドランプ、レーザー等を、また電子線の線源として、巿 販されているタングステンフィラメントから発生する熱電子を利用する方式、金属に高 電圧パルスを通じて発生させる冷陰極方式及びイオン化したガス状分子と金属電極 との衝突により発生する 2次電子を利用する 2次電子方式を挙げることができる。また 、アルファ線、ベータ線及びガンマ線の線源として、例えば、 6°Co等の核分裂物質を 挙げること力 Sでき、ガンマ線については加速電子を陽極へ衝突させる真空管等を利 用すること力 Sできる。これら放射線は 1種単独で又は 2種以上を同時に又は一定期間 をおレ、て照射することができる。
[0120] 活性エネルギー線を用いた場合、露光量を 0. 01〜10j/cm2の範囲内の値とする のが好ましい。この理由は、露光量が 0. 01j/cm2未満となると、硬化不良が生じる 場合があるためであり、一方、露光量力 SlOj/cm2を超えると、硬化時間が過度に長 くなる場合があるためである。また、このような理由により、露光量を 0.：!〜 5j/cm2の 範囲内の値とするのがより好ましぐ 0. 3〜3j/cm2の範囲内の値とするのがより好ま しい。
[0121] 紫外線硬化性樹脂組成物の硬化反応は、窒素等の嫌気的条件下において行う必 要がある。その理由は酸素によりラジカル重合が阻害される結果、硬化反応が不十 分となるからである。
[0122] 硬化膜は、上記紫外線硬化性樹脂組成物を硬化させて得られ、 2層以上の多層構 造を有することを特徴とする。特に、上記 (A)重合性不飽和基を有する有機化合物（ Ab)を結合させてなる金属酸化物粒子（ (A)成分の粒子）が高密度に存在する 1以 上の層と、上記 (A)成分の粒子が実質的に存在しない 1以下の層からなる二層以上 の層構造を有してレ、ることが好ましレ、。
[0123] 硬化膜は、前記紫外線硬化性樹脂組成物を種々の基材、例えば、プラスチック基 材にコーティングして硬化させることにより得ることができる。具体的には、組成物をコ 一ティングし、好ましくは、 0〜200°Cで揮発成分を乾燥させた後、上述の、放射線で 硬化処理を行うことにより被覆成形体として得ることができる。そのような場合、好まし い紫外線の照射光量は 0. 01〜10j/cm2であり、より好ましくは、 0.：!〜 2j/cm2で ある。また、好ましい電子線の照射条件は、加圧電圧は 10〜300KV、電子密度は 0 . 02〜0. 30mAZcm2であり、電子線照射量は:!〜 lOMradである。
[0124] 紫外線硬化性樹脂組成物を塗布後、組成物中の溶剤（C)及び溶剤（D)が蒸発し て乾燥する過程において、（A)成分の粒子が塗布下地側（隣接層との境界付近)又 はその反対側に偏在化する。そのため、硬化膜の一方の界面付近では、（(A)成分 の粒子が高密度で存在し、硬化膜の他方の界面付近では、（A)成分の粒子が実質 的に存在しないため、低屈折率の樹脂層が形成される。従って、紫外線硬化性樹脂 組成物からなる一の塗膜を硬化させることにより、実質的に二層以上の層構造を有 する硬化膜が得られる。これらの分離して形成される各層は、例えば、得られた膜の 断面を電子顕微鏡で観察することにより確認することができる。 （A)成分の粒子が高 密度に存在する層とは、（A)成分の粒子が集合している部分を指す概念であり、実 質的に (A)成分の粒子を主成分として構成された層であるが、層内部に (B)成分等 が共存する場合がある。他方、（A)成分の粒子が実質的に存在しない層とは、 (A) 成分の粒子が存在しない部分を指す概念であるが、本発明の効果を損なわない範 囲で (A)成分の粒子が若干含まれていてもよい。この層は、実質的に (B)成分と (E) 成分の硬化物等の (A)成分の粒子以外の成分から構成された層である。硬化膜は、 多くの場合、（A)成分の粒子が高密度に存在する層と (A)成分の粒子が実質的に 存在しない層がそれぞれ連続した層を形成した二層構造を有する。基材に PET樹 脂 (易接着層を有する PET樹脂を含む)等を用いた場合、通常は、基材である層、（ A)成分の粒子が高密度に存在する層、（A)成分の粒子が実質的に存在しない層が 、この順番に隣接して形成される。
[0125] ここで、二層以上の層構造とは、「(A)成分の粒子が高密度に存在する層」と、「(A )成分の粒子が実質的に存在しない層」の両者を共に含む 2以上の層からなる場合 もあり、また、二以上の「金属酸化物粒子が高密度に存在する層」のみからなる場合 力 Sある。
[0126] 紫外線硬化性樹脂組成物が 2種以上の (A)成分の粒子を含むときは、「 (A)成分 の粒子が高密度に存在する層」が 2以上形成され得る。さらに、「(A)成分の粒子が 高密度に存在する層」の「(A)成分の粒子」は、少なくとも 1種、即ち、 1種又は 2種以 上の「 (A)成分の粒子」を意味する。紫外線硬化性樹脂組成物が 2種以上の (A)成 分の粒子を含む場合、一つの「(A)成分の粒子が高密度に存在する層」が、 2種類 以上の（A)成分の粒子から構成されてレ、てもよレ、。
[0127] 紫外線硬化性樹脂組成物中の（B)エチレン性不飽和基含有含フッ素重合体は、 熱硬化性樹脂 (例えば、メラミンィ匕合物）に比べて屈折率が低ぐ反射防止膜の低屈 折率層として好ましい光学的特性を有している。そして、（A)反応性粒子の構成材料 として、屈折率の高い金属酸化物粒子を用いることにより、さらに良好な反射防止膜 を形成すること力 Sできる。
[0128] 硬化膜は、高硬度であるとともに、耐擦傷性並びに基材及び基材ゃ低屈折率層等 の隣接層との密着性に優れた塗膜 (被膜)を形成し得る特徴を有している。また、硬 化反応に熱を用いないため、熱硬化反応で生じる加水分解反応を伴わないので、得 られる硬化膜の耐湿熱性に優れている。従って、硬化膜は、フィルム型液晶素子、タ ツチパネル、プラスチック光学部品等の反射防止膜等に特に好適に用いられる。
[0129] 屈折率の変化の程度は、（A)成分の含有量、種類、（B)エチレン性不飽和基含有 含フッ素重合体の含有量、組成、及び (E)成分 (硬化性化合物)の含有量、種類等 により調整できる。
また、硬化膜の低屈折率部分における屈折率は、例えば、 1. 20〜： 1. 55であり、 高屈折率部分における屈折率は、 1. 50-2. 20である。
[実施例]
[0130] 以下の説明におレ、て「部」又は「％」は特記されてレ、ない限り「質量部」又は「質量％ 」を示す。
製造例 1
[重合性不飽和基を有する有機化合物 (Ab)の合成]
攪拌機付きの容器内のメルカプトプロピルトリメトキシシラン 221部及びジブチルス ズジラウレート 1部の混合溶液に、イソホロンジイソシァネート 222部を、乾燥空気中、 50°Cで 1時間かけて滴下した後、さらに 70°Cで 3時間攪拌した。
続いて、この反応溶液中に新中村ィ匕学製 NKエステル A _TMM_ 3LM_N (ぺ ンタエリスリトールトリアタリレート 60質量0 /0とペンタエリスリトールテトラアタリレート 40 質量％からなる。このうち、反応に関与するのは、水酸基を有するペンタエリスリトー ルトリアタリレートのみである。） 549部を 30°Cで 1時間かけて滴下した後、さらに 60°C で 10時間攪拌して反応液を得た。
この反応液中の生成物、すなわち、重合性不飽和基を有する有機化合物における 残存イソシァネート量を FT— IRで測定したところ、 0. 1質量％以下であり、各反応が ほぼ定量的に行われたことを確認した。生成物の赤外吸収スペクトルは原料中のメ ルカプト基に特徴的な 2550カイザ—の吸収ピ―ク及び原料イソシァネ—ト化合物に 特徴的な 2260カイザ—の吸収ピ―クが消失し、新たにウレタン結合及び S (C =〇） NH—基に特徴的な 1660カイザ—のピ―ク及びアタリロキシ基に特徴的な 1720力 ィザ一のピ一クが観察され、重合性不飽和基としてのアタリロキシ基と一 S (C =〇）N H—、ウレタン結合を共に有するアタリ口キシ基修飾アルコキシシランが生成している ことを示した。以上により、チォウレタン結合と、ウレタン結合と、アルコキシシリル基と 、重合性不飽和基とを有する化合物（前記式 (A— 4)及び (A— 5)で示される化合物 (Ab) ) 773部と反応に関与しなかったペンタエリスリトールテトラアタリレート 220部の 組成物 (A # l) (以下、この組成物を、「アルコキシシラン（1)」ということがある。）を得 た。
製造例 2
[ウレタンアタリレート（式（11)で示される化合物）の合成]
攪拌機付きの容器内のイソホロンジイソシァネート 18. 8部と、ジブチル錫ジラウレ ート 0. 2部とからなる溶液に対し、新中村ィ匕学製 NKエステル A—TMM— 3LM— N (反応に関与するのは、水酸基を有するペンタエリスリトールトリアタリレートのみであ る。） 93部を、 10°C、 1時間の条件で滴下した後、 60°C、 6時間の条件で攪拌し、反 応液とした。
この反応液中の生成物、即ち、製造例 1と同様にして残存イソシァネート量を FT—I Rで測定したところ、 0. 1質量％以下であり、反応がほぼ定量的に行われたことを確 認した。また、分子内に、ウレタン結合、及びアタリロイル基（重合性不飽和基）とを含 むことを確認した。
以上により、ウレタンへキサアタリレートイヒ合物（前記式（11)で示される化合物）が 7 5部得られたほか、反応に関与しな力、つたペンタエリスリトールテトラアタリレート 37部 が混在してレ、る組成物 (A # 2)を得た。
[0132] 製造例 3
[シリカ粒子含有ハードコート層用組成物の調製]
製造例 1で製造した重合性不飽和基を含む組成物 (A # 1) 2. 32部、シリカ粒子ゾ ル (メチルェチルケトンシリカゾル、 日産化学工業 (株)製 MEK— ST、数平均粒子径 0. 022 μ ΐη、シリカ濃度 30%) 91. 3部（シリカ粒子として 27部）、イオン交換水 0· 1 2部、及び ρ—ヒドロキシフエニルモノメチルエーテル 0. 01部の混合液を、 60°C、 4時 間攪拌後、オルト蟻酸メチルエステル 1. 36部を添加し、さらに 1時間同一温度で加 熱攪拌することで反応性粒子 (分散液 (A # 3) )を得た。この分散液 (A # 3)をアルミ 皿に 2g秤量後、 175°Cのホットプレート上で 1時間乾燥、秤量して固形分含量を求め たところ、 30. 7%であった。また、分散液 (A # 3)を磁性るつぼに 2g秤量後、 80°C のホットプレート上で 30分予備乾燥し、 750°Cのマツフル炉中で 1時間焼成した後の 無機残渣より、固形分中の無機含量を求めたところ、 90%であった。
この分散液（A # 3) 98. 6g、組成物（A # 2) 3. 4g、 1—ヒドロキシシクロへキシルフ ェニルケトン 2. lg、 11^^八〇111 £907 (2 _メチル_ 1 _ [4_ (メチルチォ）フヱニル] —2—モルホリノプロパン一 1—オン、チノく'スペシャルティ'ケミカルズ製） 1. 2g、ジ ペンタエリスリトールへキサアタリレート（DPHA) 33. 2g、シクロへキサノン 7gを混合 攪拌し、シリカ粒子含有ハードコート層用組成物（固形分濃度 50%)を 145g得た。
[0133] 製造例 4 [ジルコニァ粒子含有組成物の調製]
第一稀元素化学工業 (株)製、 UEP— 100 (—次粒径 10〜30nm) 300部をメチル ェチルケトン（MEK) 700部に添加し、ガラスビーズにて 168時間分散を行レ、、ガラス ビーズを除去してジルコユア分散ゾル 950部を得た。ジルコユア分散ゾルをアルミ皿 に 2g秤量後、 120°Cのホットプレート上で 1時間乾燥、秤量して固形分含量を求めた ところ 30%であった。このジルコユア分散ゾル 100gに、製造例 1で合成した組成物（ A # 1) 0. 86g、ジペンタエリスリトーノレへキサアタリレート（DPHA) 13. 4g、 p メトキ シフエノーノレ 0. 016g、ィ才ン交換水 0. 033gの？昆合 f夜を 60°C、 3日寺 撹拌後、才ノレ ト蟻酸メチルエステル 0. 332gを添加してさらに 1時間同一温度で加熱撹拌すること で、表面変性ジノレコニァ粒子の分散液を 116g得た。この分散液 116g、製造例 2で 合成した組成物（A # 2) 1. 34g、 1—ヒドロキシシクロへキシルフヱ二ルケトン 1. 26g 、 IRGACURE907 (2 -メチル _ 1 _ [4 _ (メチルチオ）フエニル]—2—モノレホリノ プロパン一 1—オン、チバ'スペシャルティ'ケミカルズ製） 0· 76g、 MEK2846gを混 合攪拌し、ジルコユア粒子含有組成物（固形分濃度 4%)を 2964g得た。
[0134] 製造例 5
[錫ドープ酸化インジウム (ITO)粒子含有組成物の調製]
富士化学株式会社製 ITOゾル（10wt% IPAゾル） 700g、 DPHA29. 5g、 2 メ チルー 1 [4 （メチルチオ）フエニル] 2—モルホリノプロパン 1 オン lg、イソ プロピルアルコール (IP A) 1769. 5gを混合し固形分濃度 4%の ITO粒子含有組成 物を得た。
[0135] 製造例 6
[アンチモンドープ酸化錫 (AT〇)粒子含有組成物の調製]
ATO粒子（石原テクノ (株）製、 SN— 100P、一次粒径 10〜30nm)、分散剤（旭電 化工業（株）製、アデカプル口ニック TR— 701)、及びメタノールを、 90/2. 78/21 1 (重量比）の配合量で混合した (全固形分含量 31 %、全無機含量 29. 6%)。ペイン トシエ一力の 50mlポリ瓶に、ガラスビーズ 40g (T〇SHINRIK〇製、 BZ— 01) (ビー ズ径 0. lmm) (体積約 16ml)と上記混合液（30g)を入れて、 3時間分散しメジアン 径 80nmの分散ゾルを得た。このゾル 304gに組成物（A # l) 5. 6g、 p—メトキシフエ ノール 0. 01g、イオン交換水 0. 12gの混合液を 60°C、 3時間撹拌後、オルト蟻酸メ チルエステル 1. 3gを添加してさらに 1時間同一温度で加熱撹拌することで、表面変 性 ATO粒子の分散液を 311g得た。この分散液 278. 3g、組成物 (A # 2) 1. 7g、ぺ ンタエリスリトーノレトリアタリレート 8. 59g、 2_メチル _ 1 _ [4_ (メチルチオ）フヱニル ]— 2 モルホリノプロパン一 1—オン 0. 88g、メタノーノレ 33g、プロピレングリコーノレ モノメチルエーテル 1675を混合攪拌し、 ATO粒子含有組成物（固形分濃度 5%)を 2000g得た。
[0136] 製造例 7
[A1ドープ Zn〇粒子含有組成物の調製]
酸化亜鉛粒子 (堺化学製 A1ドープ ZnO粒子、一次粒径 10〜20nm)、分散剤 (楠 本化成（株）製、ハイブラッド ED151)及びプロピレングリコールモノメチルエーテルを 、 27. 6/4. 8/67. 6 (重量比）の配合量で混合した (全固形分含量 30%、全無機 含量 27. 6%)。ペイントシエ一力の 50mlポリ瓶に、ジルコニァビーズ 40g (ビーズ径 0 . 1mm)と上記混合液（30g)を入れて、 8時間分散しメジアン径 40nmの分散ゾノレを 得た。このゾノレ 290gにペンタエリスリトーノレトリアタリレート 10g、 2—メチノレー 1 [4 - (メチルチオ）フエ二ル]— 2—モルホリノプロパン一 1—オン 0· 5g、プロピレングリ コールモノメチルエーテル 2138gをカ卩ぇ混合攪拌し、酸化亜鉛粒子含有組成物（固 形分濃度 4%)を 2438g得た。
[0137] 製造例 8
[重合性不飽和基を有する有機化合物 (Ab)が結合した反応性アルミナ、ジルコニァ 被覆 Ti〇粒子ゾル (A)の製造]
2
アルミナ、ジノレコニァ被覆 TiO粒子分散液 (ティカ株式会社製 全固形分濃度 28
2
%、粒子濃度 24%) 333. 7部、製造例 1で製造したアルコキシシラン（1)の溶液 5. 4 咅 ^蒸留水 0. 20咅 ^ p ヒドロキノンモノメチノレエーテノレ 0. 03咅を？昆合し、 65°Cで 加熱攪拌した。 4時間後、オルト蟻酸メチルエステル 2. 2部添カ卩し、さらに 1時間加熱 することで、固形分 32%の反応性アルミナ、ジノレコニァ被覆 TiO粒子ゾル (A)を得
2
た。
[0138] 製造例 9 [水酸基含有含フッ素重合体 (B— 2)の製造]
内容積 1. 5Lの電磁攪拌機付きステンレス製オートクレープを窒素ガスで十分置換 した後、酢酸ェチル 500g、パーフルォロ（プロピルビニルエーテノレ） 43. 2g、ェチル ビニノレエーテノレ 41. 2g、ヒドロキシェチルビニルエーテル 21. 5g、ノニオン性反応性 乳化剤として「アデカリアソープ NE_ 30」（旭電化工業株式会社製) 40. 5g、ァゾ基 含有ポリジメチルシロキサンとして「VPS— 1001」（和光純薬工業株式会社製） 6. Og 及び過酸化ラウロイル 1. 25gをカロえ、ドライアイス一メタノールで _ 50°Cまで冷却し た後、再度窒素ガスで系内の酸素を除去した。
次いでへキサフルォロプロピレン 97. 4gをカロえ、昇温を開始した。オートクレーブ 内の温度が 60°Cに達した時点での圧力は 5. 3 X 105Paを示した。その後、 70°Cで 2 0時間攪拌下に反応を継続し、圧力が 1. 7 X 105Paに低下した時点でオートクレー ブを水冷し、反応を停止させた。室温に達した後、未反応モノマーを放出しオートク レーブを開放し、固形分濃度 26. 4%のポリマー溶液を得た。得られたポリマー溶液 をメタノールに投入しポリマーを析出させた後、メタノールにて洗浄し、 50°Cにて真空 乾燥を行い 220gの含フッ素重合体 (B— 2)を得た。
[0139] 製造例 10
[エチレン性不飽和基含有含フッ素重合体 (B1)の製造]
電磁攪拌機、ガラス製冷却管及び温度計を備えた容量 1リットルのセパラブルフラ スコに、製造例 9で得られた水酸基含有含フッ素重合体 (B— 2)を 50.0g、重合禁止 剤として 2, 6 ジー t ブチルメチルフエノール 0. Olg及び MIBK374gを仕込み、 20°Cで水酸基含有含フッ素重合体 (B— 2)が MIBKに溶解して、溶液が透明、均一 になるまで攪拌を行った。次いで、この系に、 2—アタリロイルォキシェチルイソシァネ ート 16. Ogを添カ卩し、溶液が均一になるまで攪拌した後、ジブチルチンジラウレート 0 . lgを添加して反応を開始し、系の温度を 55〜65°Cに保持し 5時間攪拌を継続する ことにより、エチレン性不飽和基含有含フッ素重合体 (B1)の MIBK溶液を得た。この 溶液をアルミ皿に 2g秤量後、 150°Cのホットプレート上で 5分間乾燥、秤量して固形 分含量を求めたところ、 15. 0%であった。
[0140] 製造例 11 [紫外線硬化性樹脂組成物 1の調製]
製造例 8で得られたアルミナ、ジルコニァ被覆 TiO粒子ゾル (A) 11 Og (反応性粒
2
子として 34. 8g)、製造例 10で得られたエチレン性不飽和基含有含フッ素重合体 (B l) 285g (エチレン性不飽和基含有フッ素重合体として 42. 7g)、ジペンタエリスリト 一ルペンタアタリレート（DPPA) 15. 4g、 2_ベンジル _ 2—ジメチルァミノ _ 1 _ (4 —モルフォリノフエ二ル）一 1—ブタノン（ィルガキュア 369、チノく'スペシャルティ'ケミ カルズ社製光ラジカル重合開始剤） 3. 9g、製造例 2で得られた式（11)で示される化 合物 3. 2g、メチノレエチノレケトン 530g、メチルイソブチルケトン 150g、ノルマルブタノ ール 100gを加え攪拌した。得られた紫外線硬化性樹脂組成物の固形分濃度は 8. 4%であった。
[0141] 製造例 12〜： 16
[紫外線硬化性樹脂組成物 2〜6の調製]
各成分を表 1に示す割合で配合した以外は製造例 11と同様にして紫外線硬化性 樹脂組成物 2〜6を得た。
[0142] 実施例 1
[積層体の作製]
(1)ハードコート層の作製
製造例 3で調製したシリカ粒子含有ハードコート層用組成物（固形分濃度 45%)を 、ワイヤーバーコータ（# 12)を用いて、トリァセチルセルロースフィルム（LOFO製、 膜厚 80 / m)に塗工した後、オーブン中 80°Cで 1分間乾燥した。続いて、空気下、 高圧水銀ランプを用いて、 0. 6j/cm2の光照射条件で紫外線を照射することにより 、硬化膜層を形成した。硬化膜層の膜厚を触針式膜厚計にて測定したところ 5 z mで あった。
[0143] (2)ポリチォフェン層（導電層、帯電防止層）の作製
酸化剤としての FeClを、メチルアルコール、 2 _ブチルアルコール及びェチルセ口
2
ソルブがそれぞれ 6： 3： 1の割合で混合された溶剤に 3重量％溶解させて触媒溶液を 調製した。
ハードコート層を設けたトリァセチルセルロースフィルム表面に、前記で調製した触 媒溶液をスピンコーティングした後、得られた触媒塗膜を 60°Cで 3分間乾燥させた。 次いでこのハードコート層および触媒塗膜が形成されたポリエステルフィルムを飽 和状態の 3, 4—エチレンジォキシチォフェン単量体が生成されるように設計された C VDチャンバ一に載置し、 3, 4—エチレンジォキシチォフェンを 30秒間重合反応さ せた後、未反応物を除去するためにメタノール溶剤で洗浄し導電層を形成した。
[0144] (3)中屈折率層の作製
製造例 4で調製したジルコニァ粒子含有組成物（固形分濃度 4%)を、ワイヤーバ ーコーター（# 3)を用いて、（2)で作製したポリチォフェン層上に塗工した後、オーブ ン中 80°Cで 1分間乾燥した。続いて、窒素雰囲気下、高圧水銀ランプを用いて、 0. 6j/cm2の光照射条件で紫外線を照射することにより、硬化膜層を形成した。硬化 膜層の膜厚を反射分光計にて算出したところ 65nmであった。
[0145] (4)高屈折率層と低屈折率層の作製
製造例 11〜： 16で得られた紫外線硬化性樹脂組成物:!〜 6を、それぞれ、ワイヤー バーコータ（# 3)を用いて、（3)で作製した中屈折率層上に塗工した後、オーブン中 80°Cで 1分間乾燥した。続いて、窒素雰囲気下、高圧水銀ランプを用いて、 0. 9J/ cm2の光照射条件で紫外線を照射することにより、膜厚が 0. 2 μ ΐηの硬化膜層を形 成した。
[0146] 実施例 2
[積層体の作製]
(1)ポリチォフェン層（導電層、帯電防止層）の作製
トリァセチルセルロースフィルム表面に、実施例 1 (2)で調製した触媒溶液をスピン コーティングした後、得られた触媒塗膜を 60°Cで 3分間乾燥させた。
次いでこのハードコート層および触媒塗膜が形成されたポリエステルフィルムを飽 和状態の 3， 4_エチレンジォキシチォフェン単量体が生成されるように設計された C VDチャンバ一に載置し、 3, 4—エチレンジォキシチォフェンを 30秒間重合反応さ せた後、未反応物を除去するためにメタノール溶剤で洗浄し導電層を形成した。
(2)ハードコート層の作製
製造例 3で調製したシリカ粒子含有ハードコート層用組成物（固形分濃度 45%)を 、ワイヤーバーコータ（# 12)を用いて、 （1)で形成した導電層上に塗工した後、ォー ブン中 80°Cで 1分間乾燥した。続いて、空気下、高圧水銀ランプを用いて、 0. 6j/c m2の光照射条件で紫外線を照射することにより、硬化膜層を形成した。
(3)中屈折率層の作製
製造例 5で調製した ITO粒子含有組成物（固形分濃度 4%)を、ワイヤーバーコ一 ター（# 3)を用いて、 （2)で作製したハードコート層上に塗工した後、オーブン中 80 °Cで 1分間乾燥した。続いて、窒素雰囲気下、高圧水銀ランプを用いて、 0. 6j/cm 2の光照射条件で紫外線を照射することにより、硬化膜層を形成した。硬化膜層の膜 厚を反射分光計にて算出したところ 65nmであった。
(4)高屈折率層と低屈折率層の作製
製造例 11〜： 16で得られた紫外線硬化性樹脂組成物:!〜 6を、それぞれ、ワイヤー バーコータ（# 3)を用いて、（3)で作製した中屈折率層上に塗工した後、オーブン中 80°Cで 1分間乾燥した。続いて、窒素雰囲気下、高圧水銀ランプを用いて、 0. 9J/ cm2の光照射条件で紫外線を照射することにより、膜厚が 0. 2 μ ΐηの硬化膜層を形 成した。
実施例 3, 4
[積層体の作製]
(1)ポリチォフェン層（導電層、帯電防止層）の作製
実施例 2 (1)と同様にして作製した。
(2)ハードコート層の作製
実施例 2 (2)と同様にして作製した。
(3)中屈折率層の作製
製造例 5で調製した ΙΤΟ粒子の代わりに、製造例 6又は 7で調製した ΑΤΟ粒子含 有組成物（固形分濃度 5%)又は A1ドープ ΖηΟ粒子含有組成物（固形分濃度 4%)を 、ワイヤーバーコ一ター（# 3)を用いて、（2)で作製したハードコート層上に塗工した 後、オーブン中 80°Cで 1分間乾燥した。続いて、窒素雰囲気下、高圧水銀ランプを 用いて、 0. 6j/cm2の光照射条件で紫外線を照射することにより、硬化膜層を形成 した。硬化膜層の膜厚を反射分光計にて算出したところ 65nmであった。 (4)高屈折率層と低屈折率層の作製
製造例 11〜： 16で得られた紫外線硬化性樹脂組成物:!〜 6を、それぞれ、ワイヤー バーコータ（# 3)を用いて、（3)で作製した中屈折率層上に塗工した後、オーブン中 80°Cで 1分間乾燥した。続いて、窒素雰囲気下、高圧水銀ランプを用いて、 0. 9J/ cm2の光照射条件で紫外線を照射することにより、膜厚が 0. 2 x mの硬化膜層を形 成した。
[0148] 実施例 5
[積層体の作製]
(1)ポリチォフェン層（導電層、帯電防止層）の作製
実施例 2 (1)と同様にして作製した。
(2)ハードコート層の作製
実施例 2 (2)と同様にして作製した。
(3)高屈折率層と低屈折率層の作製
製造例 11〜： 16で得られた紫外線硬化性樹脂組成物:!〜 6を、それぞれ、ワイヤー バーコータ（# 3)を用いて、（2)で作製したハードコート層上に塗工した後、オーブン 中 80°Cで 1分間乾燥した。続いて、窒素雰囲気下、高圧水銀ランプを用いて、 0. 9J /cm2の光照射条件で紫外線を照射することにより、膜厚が 0. 2 μ ΐηの硬化膜層を 形成した。
[0149] 評価例 1
[積層体の評価]
実施例:!〜 5で得られた積層体の断面を、透過型電子顕微鏡で観察したところ、何 れの積層体においても、低屈折率層と高屈折率層が 2層に層分離していることが確 認された。このとき、低屈折率層が金属酸化物粒子が実質的に存在しない層であり、 高屈折率層が金属酸化物粒子が高密度に存在する層であった。
図 8は、二層分離、分離せず (一部凝集)及び均一構造の各状態の概念を示す。 得られた反射防止用積層体の反射防止性を、分光反射率測定装置 (大型試料室 積分球付属装置 150— 09090を組み込んだ自記分光光度計 U— 3410、 日立製作 所 (株)製）により、波長 550nmの反射率を測定して評価した。具体的には、アルミの 蒸着膜における反射率を基準（100%)として、反射防止用積層体 (反射防止膜)の 反射率を測定した。その結果、何れの積層体も波長 550nmにおける反射率が 1 % 以下であった。ただし、実施例 5において組成物 6を用いた積層体だけは、反射率力 S 1 %を超えた。
[表 1]
Figure imgf000051_0001
表 1中の略称等は、下記のものを示す。
DPPA:ジペンタエリスリトールペンタアタリレート； UV硬化性架橋剤（5官能) イノレガキュア 369： 2—ベンジル一 2 -ジメチルアミノー 1— (4—モルフォリノフエ二 ノレ）一 1—ブタノン；チバ ·スペシャルティ ·ケミカルズ社製光重合開始剤
産業上の利用可能性
本発明の積層体の製造方法は、導電層を気相重合で形成できるため、均一な導電 層を製造できる。また、 1の塗膜から、 2以上の層を形成することができるため、二層 以上の多層構造を有する積層体の製造工程を簡略化できる。従って、本発明の積層 体の製造方法は、特に、反射防止膜、レンズ、選択透過膜フィルタ等の光学材料の 形成に有利に用いることができる。また、得られる積層体は、フッ素含量が高い層を 含むことができることを利用して、耐候性が要求される基材に対する塗料、耐候フィル ム、コーティング、その他として好適に使用することができる。しかも、当該積層体は、 基材に対する密着性に優れ、耐擦傷性が高ぐ良好な反射防止効果を付与すること から、反射防止膜として極めて有用であり、各種の表示装置に適用することにより、そ の視認性を向上させることができる。

Claims

請求の範囲
[1] 基材と、その上に導電層及び多層構造を有する積層体の製造方法であって、 ピロ一ノレ、チォフェン、フラン、セレノフェン、 3, 4 _エチレンジォキシチォフェン及 びこれらの誘導体からなる群から選択される少なくとも一種の単量体を気相重合する ことにより導電層を形成し、
前記基材上又は基材上に形成された層の上に、下記成分 (A)〜（D)を含む紫外 線硬化性樹脂組成物を塗布して塗膜を形成し、
この丄の塗膜力 溶媒を蒸発させることにより、 2以上の層を形成することを特徴とす る積層体の製造方法。
[紫外線硬化性樹脂組成物]
(A)重合性不飽和基を有する有機化合物 (Ab)を結合させてなる金属酸化物粒子
(B)エチレン性不飽和基含有含フッ素重合体
(C) (B)エチレン性不飽和基含有含フッ素重合体の溶解性が高い、 1種又は 2種 以上の溶剤（以下、「（C)速揮発溶剤」という）
(D) (A)重合性不飽和基を有する有機化合物 (Ab)を結合させてなる金属酸化物 粒子の分散安定性が高ぐかつ、（C)速揮発溶剤と相溶性である、 1種又は 2種以上 の溶剤（以下、「（D)遅揮発溶剤」という）
かつ、 (C)速揮発溶剤の相対蒸発速度が、（D)遅揮発溶剤の相対蒸発速度よりも大 きレ、紫外線硬化性樹脂組成物
[2] 前記 2以上の層の各層が、金属酸化物粒子が高密度に存在する層又は金属酸化 物粒子が実質的に存在しない層であって、少なくとも 1層は金属酸化物粒子が高密 度に存在する層であることを特徴とする請求項 1に記載の積層体の製造方法。
[3] 前記 2以上の層が、 2層であることを特徴とする請求項 2に記載の積層体の製造方 法。
[4] さらに、前記 2以上の層を放射線照射することにより硬化させることを特徴とする請 求項 1〜3のいずれか一項に記載の積層体の製造方法。
[5] 積層体が光学用部品であることを特徴とする請求項 1〜4のいずれか一項に記載 の積層体の製造方法。 [6] 積層体が反射防止膜であることを特徴とする請求項 1〜4のいずれか一項に記載 の積層体の製造方法。
[7] 前記積層体が、基材上に、少なくとも帯電防止層、高屈折率層及び低屈折率層が 、基材に近い側からこの順に積層されている反射防止膜であって、
前記導電層が、帯電防止層であり、
請求項 3に記載の 2層が、高屈折率層及び低屈折率層からなる
ことを特徴とする請求項 3に記載の積層体の製造方法。
[8] 低屈折率層の 589nmにおける屈折率が 1. 20〜： 1. 55であり、
高屈折率層の 589nmにおける屈折率が 1. 50-2. 20であって、低屈折率の屈折 率より高いことを特徴とする請求項 7に記載の積層体の製造方法。
[9] 前記積層体が、基材上に、少なくとも、帯電防止層、中屈折率層、高屈折率層及び 低屈折率層が、基材に近い側からこの順に積層されている反射防止膜であって、 前記導電層が、帯電防止層であり、
請求項 3に記載の 2層が、高屈折率層及び低屈折率層からなる
ことを特徴とする請求項 3に記載の積層体の製造方法。
[10] 低屈折率層の 589nmにおける屈折率が 1. 20〜： 1. 55であり、
中屈折率層の 589nmにおける屈折率が 1. 50〜： 1. 90であって、低屈折率の屈折 率より高ぐ
高屈折率層の 589nmにおける屈折率が 1. 51〜2. 20であって、中屈折率の屈折 率より高いことを特徴とする請求項 9に記載の積層体の製造方法。
[11] さらに、基材上に、ハードコート層を形成することを特徴とする請求項 7〜： 10のいず れか一項に記載の積層体の製造方法。
[12] 紫外線硬化性樹脂組成物にぉレ、て、前記 (Ab)重合性不飽和基を有する有機化 合物が、重合性不飽和基に加えて、下記式 (A— 1)に示す基を有することを特徴と する請求項:!〜 11のいずれか一項に記載の積層体の製造方法。
[化 22]
|_|
— U— C— — (A— 1)
II
V [式中、 Uは、 NH、 O (酸素原子）又は S (ィォゥ原子）を示し、 Vは、〇又は Sを示す。
]
[13] 紫外線硬化性樹脂組成物にぉレ、て、前記 (Ab)重合性不飽和基を有する有機化 合物が、分子内にシラノール基を有する化合物又は加水分解によってシラノール基 を生成する化合物であることを特徴とする請求項 1〜： 12のいずれか一項に記載の積 層体の製造方法。
[14] 前記（B)エチレン性不飽和基含有含フッ素重合体が、 1個のイソシァネート基と、少 なくとも 1個のエチレン性不飽和基とを含有する化合物（B— 1)と、水酸基含有含フッ 素重合体 (B— 2)と、を反応させて得られることを特徴とする請求項 1〜： 13のいずれ か一項に記載の積層体の製造方法。
[15] 前記水酸基含有含フッ素重合体 (B_ 2)力 下記構造単位（a) 20〜70モル％、 (b ) 10〜70モノレ％及び（。）5〜70モノレ％を含んでなり、かつ、ゲルパーミエーシヨンク 口マトグラフィ一で測定したポリスチレン換算数平均分子量が 5, 000〜500, 000で ある請求項 14に記載の積層体の製造方法。
(a)下記一般式（1)で表される構造単位。
(b)下記一般式 (2)で表される構造単位。
(c)下記一般式 (3)で表される構造単位。
[化 23]
F R1
— c-c— (
[式中、 R1はフッ素原子、フルォロアルキル基、又は OR2で表される基（R2はアルキ ル基、又はフルォロアルキル基を示す）を示す]
[化 24]
H R3
— C-C― (2)
H R4
[式中、 R3は水素原子又はメチル基を、 R4はアルキル基、—(CH 2 ) OR5若しくは OCOR5で表される基（R5はアルキル基、又はグリシジル基を、 Xは 0又は 1の数を示 す）、カルボキシル基、又はアルコキシカルボ二ル基を示す]
[化 25]
H R6
— C-C—— (3)
H (CH2)vOR7
[式中、 R6は水素原子、又はメチル基を、 R7は水素原子、又はヒドロキシアルキル基 を、 Vは 0又は 1の数を示す]
[16] さらに、前記水酸基含有含フッ素重合体 (B_ 2)が、ァゾ基含有ポリシロキサンィ匕 合物に由来する下記構造単位（d) 0. 1〜： 10モル％を含む請求項 14又は 15に記載 の積層体の製造方法。
(d)下記一般式 (4)で表される構造単位。
[化 26]
R8
— Si-O— (4)
R9
[式中、 R8及び R9は、同一でも異なっていてもよぐ水素原子、アルキル基、ハロゲン 化アルキル基、又はァリール基を示す]
[17] 前記水酸基含有含フッ素重合体 (B— 2)が、前記構造単位 (d)を下記構造単位 (e )の一部として含むことを特徴とする請求項 16に記載の積層体の製造方法。
(e)下記一般式 (5)で表される構造単位。
[化 27] )
Figure imgf000056_0001
[式中、 R1Q〜R13は水素原子、アルキル基、又はシァノ基を示し、 R14〜R17は水素原 子又はアルキル基を示し、 p、 qは:!〜 6の数、 s、 tは 0〜6の数、 yは:!〜 200の数を示 す。 ]
[18] さらに、前記水酸基含有含フッ素重合体 (B— 2)が、下記構造単位 (f) 0. 1〜5モ ル％を含む請求項 14〜： 17のいずれ力 1項に記載の積層体の製造方法。
(f )下記一般式 (6)で表される構造単位。
[化 28]
Figure imgf000057_0001
[式中、 R は乳化作用を有する基を示す]
[19] 前記化合物（B— 1)が、 2_ (メタ）アタリロイルォキシェチルイソシァネートである請 求項 14〜： 18のいずれ力 4項に記載の積層体の製造方法。
[20] 紫外線硬化性樹脂組成物の（C)速揮発溶剤は、 (A)重合性不飽和基を有する有 機化合物 (Ab)を結合させてなる金属酸化物粒子の分散安定性が低レ、、 1種又は 2 種以上の溶剤であり、（D)遅揮発溶剤は、 （B)エチレン性不飽和基含有含フッ素重 合体の溶解性が低い、 1種又は 2種以上の溶剤であることを特徴とする請求項 1〜19 のレ、ずれか一項に記載の積層体の製造方法。
[21] 紫外線硬化性樹脂組成物が、さらに、成分 (E)少なくとも 2個以上の（メタ）アタリ口 ィル基を含有する多官能 (メタ）アタリレート化合物及び Z又は少なくとも 1個以上の（ メタ）アタリロイル基を含有する含フッ素 (メタ）アタリレート化合物を含有することを特 徴とする請求項 1〜20のいずれか一項に記載の積層体の製造方法。
[22] 紫外線硬化性樹脂組成物が、さらに、成分 (F)光ラジカル重合開始剤を含むことを 特徴とする請求項 1〜21のいずれか一項に記載の積層体の製造方法。
[23] 請求項 1〜22のいずれか一項に記載された積層体の製造方法により、製造された 積層体。
PCT/JP2005/020568 2004-11-16 2005-11-10 積層体の製造方法 WO2006054470A1 (ja)