Classifications

• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
  • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
  • B29C49/00—Blow-moulding, i.e. blowing a preform or parison to a desired shape within a mould; Apparatus therefor
  • B29C49/0005—Blow-moulding, i.e. blowing a preform or parison to a desired shape within a mould; Apparatus therefor characterised by the material
  • B29C49/0006—Blow-moulding, i.e. blowing a preform or parison to a desired shape within a mould; Apparatus therefor characterised by the material for heating or cooling
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
  • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
  • B29C49/00—Blow-moulding, i.e. blowing a preform or parison to a desired shape within a mould; Apparatus therefor
  • B29C49/02—Combined blow-moulding and manufacture of the preform or the parison
  • B29C49/04—Extrusion blow-moulding
  • B29C49/0411—Means for defining the wall or layer thickness
  • B29C49/04114—Means for defining the wall or layer thickness for keeping constant thickness
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
  • C08L67/00—Compositions of polyesters obtained by reactions forming a carboxylic ester link in the main chain; Compositions of derivatives of such polymers
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
  • C08L67/00—Compositions of polyesters obtained by reactions forming a carboxylic ester link in the main chain; Compositions of derivatives of such polymers
  • C08L67/02—Polyesters derived from dicarboxylic acids and dihydroxy compounds
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
  • C08L69/00—Compositions of polycarbonates; Compositions of derivatives of polycarbonates
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
  • B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
  • B29K2067/00—Use of polyesters or derivatives thereof, as moulding material
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
  • B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
  • B29K2069/00—Use of PC, i.e. polycarbonates or derivatives thereof, as moulding material
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
  • B29L—INDEXING SCHEME ASSOCIATED WITH SUBCLASS B29C, RELATING TO PARTICULAR ARTICLES
  • B29L2031/00—Other particular articles
  • B29L2031/712—Containers; Packaging elements or accessories, Packages
  • B29L2031/7158—Bottles
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
  • C08G63/00—Macromolecular compounds obtained by reactions forming a carboxylic ester link in the main chain of the macromolecule
  • C08G63/02—Polyesters derived from hydroxycarboxylic acids or from polycarboxylic acids and polyhydroxy compounds
  • C08G63/12—Polyesters derived from hydroxycarboxylic acids or from polycarboxylic acids and polyhydroxy compounds derived from polycarboxylic acids and polyhydroxy compounds
  • C08G63/16—Dicarboxylic acids and dihydroxy compounds
  • C08G63/20—Polyesters having been prepared in the presence of compounds having one reactive group or more than two reactive groups
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
  • C08L2205/00—Polymer mixtures characterised by other features
  • C08L2205/02—Polymer mixtures characterised by other features containing two or more polymers of the same C08L -group

Definitions

• This invention generally relates to blends of polycarbonate and copolyesters that are capable of being extrusion blow-molded.
• the invention also relates to containers and shaped articles made from the blends as well as a method of making the articles.
• polycarbonate often requires complicated annealing procedures to remove residual stresses formed during processing.
• Blends of polycarbonate and certain polyesters are used in injection molding and sheet extrusion applications. These blends are clear and can provide a good balance of chemical resistance and heat resistance.
• existing commercial transparent blends of polycarbonate and polyesters cannot be processed by extrusion blow- molding due to lack of melt strength.
• the polymer should possess sufficient melt strength.
• the polymer should also possess adequate physical, tensile, and thermal properties.
• melt strength can be related to the viscosity of a polymer measured at a low shear rate, such as 1 radian/second. Viscosity can be measured by typical viscometers, such as a parallel plate viscometer. Typically, viscosity is measured at the typical processing temperature for the polymer and is measured at a series of shear rates, often between 1 radian/second and 400 radian/second. In extrusion blow- molding, the viscosity at 1 radian/second at processing temperatures typically needs to be above 30,000 poise in order to blow a bottle. Larger parisons require higher viscosities.
• the polymer is "melt processed" at shear rates ranging anywhere from about 10 s “1 to 1000 s "1 in the die/extruder.
• a typical shear rate encountered in the barrel or die during extrusion blow-molding or profile extrusion is 400 radians/second. These high shear rates are encountered as the polymer flows down the extruder screw, or as it passes through the die. These high shear rates are desired to maintain reasonably fast production rates.
• shear heating can lead to viscous dissipation of heat, in a process referred to as shear heating.
• Shear heating raises the temperature of the polymer, and the extent of temperature rise is directly proportional to the viscosity at that shear rate. Since viscosity decreases with increasing temperature, shear heating decreases the low shear rate viscosity of the polymer, and thus, its melt strength decreases.
• melt fracture is a flow instability phenomenon occurring during extrusion of thermoplastic polymers at the fabrication surface/polymer melt boundary.
• the occurrence of melt fracture produces severe surface irregularities in the extrudate as it emerges from the orifice. The naked eye detects this surface roughness in the melt-fractured sample as a frosty appearance or matte finish as
• melt fracture can occur whenever the wall shear stress in the die exceeds a certain value, typically 0.1 to 0.2 MPa.
• the wall shear stress is directly related to the volume throughput or line speed (which dictates the shear rate) and the viscosity of the polymer melt. By reducing either the line speed or the viscosity at high shear rates, the wall shear stress is reduced, lowering the possibility for melt fracture to occur.
• line speed or the viscosity at high shear rates the wall shear stress is reduced, lowering the possibility for melt fracture to occur.
• a typical shear rate that is associated with the onset of melt fracture is 400 radian/sec.
• the viscosity at this shear rate typically needs to be below 10,000 poise.
• shear thinning a degree of viscosity reduction between low and high shear rates. Based on the preceding discussion, one definition of shear thinning relevant to extrusion blow- molding would be the ratio of the viscosity measured at 1 radian/second to the viscosity measured at 400 radians/second when both viscosities are
• the measurement temperature selected should be typical of the actual processing conditions and one that
• the invention relates to a blend that is capable of being extrusion blow-molded.
• the blend comprises:
• diacid residues comprising terephthalic acid residues
• diol residues comprising about 45 to 75 mole percent of 1 ,4-cyclohexanedimethanol residues and about 25 to 55 mole
• the blend comprises between 45 and 90 weight percent of the copolyester mixture and between 10 and 55 weight percent of the polycarbonate, and the first copolyester preferably has an inherent viscosity of about 0.5 to 1.1 and a shear thinning ratio of at least about 5, and comprises:
• diol residues comprising about 52 to 75 mole percent of 1 ,4- cyclohexanedimethanol residues and about 25 to 48 mole percent of ethylene glycol residues;
• the invention in another aspect, relates to a method of making a clear article.
• the method comprises the steps of: (a) blending a polycarbonate, a first copolyester, and optionally a second copolyester;
• step (b) before, during, or after step (a), melting the polycarbonate, the first copolyester, and optionally the second copolyester to form a melt blend;
• the invention relates to shaped articles extrusion blow-molded from the blends according this invention. [0015] In yet another aspect, the invention relates to containers extrusion blow-molded from the blends according this invention.
• the blends have a shear thinning ratio of at least about 3 and are comprised of (A) about 1 to 99% (more preferably, 10 to 55%) by weight of a linear or branched polycarbonate and (B) about 1 to 99% (more preferably, 45 to 90%) by weight of a mixture of 40 to 100% by weight of a first copolyester and 0 to 60% by weight of a second copolyester.
• the average amount of 1 ,4-cyclohexanedimethanol residues in the mixture of the first copolyester and the second copolyester ranges from 52 to 75 mole percent. 5 039886
• the first copolyesters provided by our invention preferably have an inherent viscosity of about 0.5 to 1.1 and a shear thinning ratio of at least about 5, and are comprised of:
• diol residues comprising about 45 to 75 mole percent 1 ,4- cyclohexanedimethanol residues and about 25 to 55 mole percent ethylene glycol residues;
• An especially preferred group of the first copolyesters has an inherent viscosity of about 0.6 to 0.9 and a shear thinning ratio of at least about 5, and comprises:
• diol residues consisting essentially of about 52 to 75 mole percent of 1 ,4-cyclohexanedimethanol residues and about 25 to 48 mole percent of ethylene glycol residues;
• trimellitic acid or anhydride residues C. about 0.1 to 0.25 mole percent of trimellitic acid or anhydride residues.
• An optional second copolyester provided by our invention preferably has an inherent viscosity of about 0.5 to 1.1 and a shear thinning ratio of at least about 2, and is comprised of:
• copolyesters have been found to be useful for making blends with polycarbonate that can be extrusion blow-molded to produce transparent, noncrystalline articles such as containers. These containers exhibit good resistance to deformation when filled with liquids heated up to
• diacid residues A contain at least 40 mole percent, and more preferably 100 mole percent, of terephthalic acid residues.
• the remainder of the diacid component A may be made up of one more alicyclic and/or aromatic dicarboxylic acid residues commonly present in polyesters.
• dicarboxylic acids examples include 1 ,2-, 1 ,3- and 1 ,4- cyclohexanedicarboxylic; 2,6- and 2,7-naphthalenedicarboxylic; isophthalic; and the like.
• Diacid residues A may be derived from the dicarboxylic acids or from ester forming derivatives thereof such as dialkyl esters or acids chlorides.
• the trifunctional residues C can be derived from tricarboxylic acids or ester forming derivatives thereof such as trimellitic (1,2,4- benzenetricarboxylic) acid and anhydride, hemimellitic (1 ,2,3- benzenetricarboxylic) acid and anhydride, trimesic (1 ,3,5- benzenetricarboxylic) acid, and tricarballyic (1 ,2,3-propanetricarboxylic) acid.
• trimellitic (1,2,4- benzenetricarboxylic) acid and anhydride hemimellitic (1 ,2,3- benzenetricarboxylic) acid and anhydride
• trimesic (1 ,3,5- benzenetricarboxylic) acid trimesic (1 ,3,5- benzenetricarboxylic) acid
• tricarballyic (1 ,2,3-propanetricarboxylic) acid.
• the trifunctional residue may also be derived from an aliphatic triol containing about 3 to 8 carbon atoms such as glycerin, trimethylolethane, and trimethylolpropane.
• the amount of the trifunctional monomer residue present in the first copolyester is preferably in the range of about 0.10 to 0.25 mole percent.
• the preferred trifunctional monomer residues are residues of benzenetricarboxylic acids (including anhydrides), especially trimellitic acid or anhydride.
• the mole percentages referred to herein are based on 100 mole percent (or the total number of moles) of the particular component in question.
• diacid residues comprising at least 40 mole percent terephthalic residues means that at least 40 percent of the moles of diacid residues in the copolyester are terephthalic residues.
• the balance of the diacid residues can be some other species.
• the mole percent of the trifunctional component C in the first copolyester is based on (1 ) the moles of diacid component A when component C is a triacid residue or (2) the moles of diol component B when component C is a triol residue.
• an especially preferred group of our first copolyesters has an inherent viscosity of about 0.6 to 0.9 and a shear thinning ratio of at least about 5, and is comprised of:
• diol residues consisting essentially of about 48 to 65 mole percent 1 ,4-cyclohexanedimethanol residues and about 35 to 52 mole percent ethylene glycol residues;
• trimellitic acid or anhydride residues C. about 0.1 to 0.25 mole percent of trimellitic acid or anhydride residues.
• the copolyesters of our invention may be prepared using procedures well known in the art for the preparation of high molecular weight polyesters.
• the copolyesters may be prepared by direct condensation using a dicarboxylic acid or by ester interchange using a dialkyl dicarboxylate.
• a dialkyl terephthalate such as dimethyl terephthalate is ester interchanged with the diols at elevated temperatures in the presence of a catalyst.
• Polycondensation is carried out at increasing temperatures and at reduced pressures until a copolyester having the desired inherent viscosity is obtained.
• the inherent viscosities I.V., dl/g
• Examples of the catalyst materials that may be used in the synthesis of the polyesters utilized in the present invention include titanium, manganese, zinc, cobalt, antimony, gallium, lithium, calcium, silicon, and germanium. Such catalyst systems are described in U.S. Patent Nos. 3,907,754; 3,962,189; 4,010,145; 4,356,299; 5,017,680; 5,668,243; and 5,681 ,918, the contents of which are herein incorporated by reference in their e.ntirety.
• Preferred catalyst metals include titanium and manganese and most preferred is titanium.
• the amount of catalytic metal used may range from about 5 to 100 ppm, but the use of catalyst concentrations of about 5 to 35 ppm titanium is preferred in order to provide polyesters having good color, thermal stability, and electrical properties.
• Phosphorus compounds frequently are used in combination with the catalyst metals, and any of the phosphorus compounds normally used in making polyesters may be used. Up to about 100 ppm phosphorus typically may be used.
• the polycarbonate portion of the present blend preferably has a diol component containing about 90 to 100 mole percent bisphenol A units, and 0 to about 10 mole percent can be substituted with units of other modifying aliphatic or aromatic diols, besides bisphenol A, having from 2 to 16 carbons.
• the polycarbonate can contain branching agents, such as tetraphenolic compounds, tri-(4-hydroxyphenyl) ethane, pentaerythritol triacrylate and others discussed in U.S. Patent Nos. 6,160,082; 6,022,941 ; 5,262,51 ; 4,474,999; and 4,286,083. Other suitable branching agents are mentioned herein below.
• modifying aromatic diols include the aromatic diols disclosed in U.S. Patent Nos. 3,030,335 and 3,317,466.
• the inherent viscosity of the polycarbonate portion of the blends according to the present invention is preferably at least about 0.3 dL/g, more preferably at least 0.5 dL/g, determined at 25 0 C in 60/40 wt/wt phenol/tetrachloroethane.
• the melt flow of the polycarbonate portion of the blends according to the present invention is preferably between 1 and 20, and more preferably between 2 and 18, as measured according to ASTM D1238
• the polycarbonate portion of the present blend can be prepared in the melt, in solution, or by interfacial polymerization techniques well known in the art. Suitable methods include the steps of reacting a carbonate source with a diol at a temperature of about 0 0 C to 315 0 C at a pressure of about 0.1 to 760 mm Hg for a time sufficient to form a polycarbonate.
• Commercially available polycarbonates that can be used in the present invention are normally made by reacting an aromatic diol with a carbonate source such as phosgene, dibutyl carbonate, or diphenyl carbonate, to incorporate 100 mol percent of carbonate units, along with 100 mol percent diol units into the polycarbonate.
• a carbonate source such as phosgene, dibutyl carbonate, or diphenyl carbonate
• linear or branched polycarbonate that can be used in the invention disclosed herein is not limited to or bound by the polycarbonate type or its production method.
• a dihydric phenol such as bisphenol A
• phosgene is reacted with phosgene with the use of optional mono-functional compounds as chain terminators and tri-functional or higher functional compounds as branching or crosslinking agents.
• Reactive acyl halides are also condensation polymerizable and have been used in polycarbonates as terminating compounds (mono-functional), comonomers (di-functional), or branching agents (tri-functional or higher).
• One method of forming branched polycarbonates involves the incorporation of an aromatic polycarboxylic acid or functional derivative thereof in a conventional polycarbonate-forming reaction mixture.
• the examples in the '884 patent demonstrate such incorporation in a reaction in which phosgene undergoes reaction with a bisphenol, under alkaline conditions typically involving a pH above 10.
• a preferred aromatic polycarboxylic acid derivative is trimellitic acid trichloride.
• a monohydric phenol as a molecular weight regulator; it functions as a chain termination agent by reacting with chloroformate groups on the forming polycarbonate chain.
• U.S. Patent No. 4,367,186 disclose a process for producing cross-linked polycarbonates wherein a cross-linkable polycarbonate contains methacrylic acid chloride as a chain terminator.
• a mixture of bisphenol A, aqueous sodium hydroxide, and methylene chloride is prepared.
• a solution of methacrylic acid chloride in methylene chloride is added.
• phosgene is added, and an additional amount of aqueous sodium hydroxide is added to keep the pH between 13 and 14.
• the triethylamine coupling catalyst is added.
• This polycarbonate is prepared in a conventional manner using a branching agent, such as trimellityl trichloride and an acryloyl chloride to provide the reactive end groups.
• a branching agent such as trimellityl trichloride and an acryloyl chloride to provide the reactive end groups.
• the process is carried out by mixing water, methylene chloride, triethylamine, bisphenol A, and optionally para-t-butyl phenol as a chain terminating agent.
• the pH is maintained at 9 to 10 by addition of aqueous sodium hydroxide.
• Randomly branched polycarbonates and methods of preparing them are known from U.S. Patent No. 4,001 ,184. At least 20 weight percent of a stoichiometric quantity of a carbonate precursor, such as an acyl halide or a haloformate, is reacted with a mixture of a dihydric phenol and at least 0.05 mole percent of a polyfunctional aromatic compound in a medium of water and a solvent for the polycarbonate.
• a carbonate precursor such as an acyl halide or a haloformate
• the medium contains at least 1.2 mole percent of a polymerization catalyst. Sufficient alkali metal hydroxide is added to the reaction medium to maintain a pH range of 3 to 6, and then sufficient alkali metal hydroxide is added to raise the pH to at least 9 but less than 12 while reacting the remaining carbonate precursor.
• U.S. Patent No. 6,225,436 discloses a process for preparing polycarbonates which allows the condensation reaction incorporation of an acyl halide compound into the polycarbonate in a manner which is suitable in batch processes and in continuous processes.
• acyl halide compounds can be mono-, di-, tri- or higher-functional and are preferably for branching or terminating the polymer molecules or providing other functional moieties at terminal or pendant locations in the polymer molecule.
• U.S. Patent No. 5,142,088 discloses the preparation of branched polycarbonates, and more particularly to novel intermediates useful in the preparation and a method for conversion of the intermediates via chloroformate oligomers to the branched polycarbonates.
• One method for making branched polycarbonates with high melt strength is a variation of the melt-polycondensation process where the diphenyl carbonate and Bisphenol A are polymerized together with polyfunctional alcohols or phenols as branching agents.
• DE 19727709 discloses a process to make branched polycarbonate in the melt-polymerization process using aliphatic alcohols. It is known that alkali metal compounds and alkaline earth compounds, when used as catalysts added to the monomer stage of the melt process, will not only generate the desired polycarbonate compound, but also other products after a rearrangement reaction known as the "Fries" rearrangement. This is discussed in U.S. Patent No. 6,323,304. The presence of the Fries rearrangement products in a certain range can increase the melt strength of the polycarbonate resin to make it suitable for bottle and sheet applications.
• JP 09059371 discloses a method for producing an aromatic polycarbonate in the presence of a polycondensation catalyst, without the use of a branching agent, which results in a polycarbonate possessing a branched structure in a specific proportion.
• JP 09059371 discloses the fusion-polycondensation reaction of a specific type of aromatic dihydroxy compound and diester carbonate in the presence of an alkali metal compound and/or alkaline earth metal compound and/or a nitrogen-containing basic compound to produce a polycarbonate having an intrinsic viscosity of at least 0.2.
• the polycarbonate is then subject to further reaction in a special self-cleaning style horizontal-type biaxial reactor having a specified range of the ratio L/D of 2 to 30 (where L is the length of the horizontal rotating axle and D is the rotational diameter of the stirring fan unit).
• JP 09059371 teaches the addition of the catalysts directly to the aromatic dihydroxy compound and diester carbonate monomers.
• 6,504,002 discloses a method for production of a branched polycarbonate composition, having increased melt strength, by late addition of branch-inducing catalysts to the polycarbonate oligomer in a melt polycondensation process, the resulting branched polycarbonate composition, and various applications of the branched polycarbonate composition.
• polyhydric phenols having three or more hydroxy groups per molecule for example, 1 ,1 ,1-tris-(4-hydroxyphenyl)ethane (THPE), 1,3,5-tris-(4-hydroxyphenyl)benzene, 1 ,4-bis-[di-(4- hydroxyphenyl)phenylmethyl]benzene, and the like, as branching agents for high melt strength blow-moldable polycarbonate 30 resins prepared interfacially has been described in U.S. Patent Nos. Re. 27,682 and 3,799,953.
• Trimellitic triacid chloride has also been used as a branching agent in the interfacial preparation of branched polycarbonate.
• U.S. Patent No. 5,191 ,038 discloses branched polycarbonate compositions having improved melt strength and a method of preparing them from aromatic cyclic polycarbonate oligomers in a melt equilibration process.
• the novel polymer blends of the present invention preferably contain a phosphorus catalyst quencher component, typically one or more phosphorus compounds such as a phosphorus acid, e.g., phosphoric and/or phosphorous acids, or an ester of a phosphorus acid such as a phosphate or phosphite ester.
• the amount of phosphorus catalyst quencher present typically provides an elemental phosphorus content of about 0 to 0.5 weight percent, preferably 0.1 to 0.25 weight percent, based on the total weight of the blend.
• the blends may also include other additives, such as heat stabilizers, UV stabilizers, antioxidants, UV absorbers, mold releases, biocides, plasticizers, or fillers such as clay, mica, talc, ceramic spheres, glass spheres, glass flakes, and the like. Additives such as these are typically used in relatively small quantities. These additives may be incorporated into the blends of the invention by way of concentrates. These concentrates may use polyesters that are not of the composition described above. If so, these other polyesters are preferably not added in quantities exceeding 5 weight percent.
• the blends may be prepared using procedures well known in the art including, but not restricted to, compounding in a single screw extruder, compounding in a twin screw extruder, or simply pellet blending the components together prior to extrusion blow-molding.
• a typical method of preparing the blends involves 1) adding pellets of the polycarbonate, the first copolyester, and optionally the second copolyester to an extruder using additive feeders, melt feeders or by preblending the pellets; 2) melting the polycarbonate, the first copolyester, and optionally the second copolyester in the extruder; 3) blending the polycarbonate, the first copolyester, and optionally the second copolyester by shearing action of the extruder screw to form a melt blend; and 4) cooling the melt blend to form clear pellets.
• extruder should be set at greater than 230 0 C, preferably greater than
• the compounding process may use either a single or twin screw
• the pellets of the polycarbonate, the first copolyester, and optionally the second copolyester may be placed directly into the extruder used to extrusion blow-mold the final articles, without a prior compounding step.
• a typical extrusion blow-molding manufacturing process involves: 1 ) melting the resin in an extruder; 2) extruding the molten resin through a die to form a tube of molten polymer (i.e., a parison) having a uniform side wall thickness; 3) clamping a mold having the desired finished shape around the parison; 4) blowing air into the parison, causing the extrudate to stretch and expand to fill the mold; 5) cooling the molded article; and 6) ejecting the article from the mold.
• molten polymer i.e., a parison
• the polymer blends of the invention are capable of being extrusion blow molded, they are also capable of being melt extruded or injection molded.
• the invention includes molded or formed articles, film, sheet, and/or fibers comprising the polymer blends of the invention which may be formed by any conventional method known in the art as well as a process for making such articles, film, sheet, and/or fibers comprising the steps of injection molding, extrusion blow molding, film/sheet extruding or calendering the polymer blend(s).
• polyesters or polyester blends into film or sheet typically involves extruding a polyester melt through a manifold of a flat die. Manual or automatic die lip adjustment is used to control thickness across a web of material. Water-cooled chill rolls are used to quench the molten web and impart a smooth surface finish.
• the polymer blends of the present invention are characterized by a novel combination of properties including low haze. Haze can be determined by two methods. The first method is visual observation of the blend extrudate where about 300 grams of the melt blended material is collected in a pile and set aside and allowed to slowly cool to room temperature. The pile of cooled blend is then examined visually for haze.
• melt viscosity of the materials used herein is measured at 24O 0 C and is determined with a Rheometrics Mechanical Spectrometer (RMS 800) with 25 mm parallel plates. Samples are vacuum dried at 7O 0 C overnight or longer before testing. The units are reported in Poise (P).
• the glass transition temperatures (Tgs) of the blends were determined using a TA Instruments 2950 differential scanning calorimeter (DSC) at a scan rate of 20°C/minute. The values reported below are from the second DSC scan.
• Blends were prepared by combining polyester with polycarbonate and a phosphorus additive. A summary of materials used is shown in Table
• copolyesters and polycarbonates used in the blends are listed below and were prepared by methods well known in the art for the preparation of high molecular weight polyesters.
• Copolyester A is a branched copolyester comprising a diacid component containing 100 mole percent terephthalic acid residues and a diol component containing 59-63 mole percent 1 ,4-cyclohexanedimethanol (CHDM) residues and 37-41 mole percent ethylene glycol residues and also containing 0.18 mole percent trimellitic anhydride (TMA) residues.
• CHDM 1,4-cyclohexanedimethanol
• TMA trimellitic anhydride
• Copolyester B is a branched copolyester comprising a diacid component containing 100 mole percent terephthalic acid residues and a diol component containing 56 mole percent CHDM residues and 44 mole percent ethylene glycol residues and also containing 0.18 mole percent TMA residues.
• Copolyester C is a branched copolyester comprising a diacid component containing 100 mole percent terephthalic acid residues and a diol component containing 48-52 mole percent CHDM residues and 52-48 mole percent ethylene glycol residues and also containing 0.18 mole percent TMA residues.
• Copolyester D is a linear copolyester comprising a diacid component containing 100 mole percent terephthalic acid residues and a diol component containing 62 mole percent CHDM residues and 38 mole percent ethylene glycol residues and also containing 0.18 mole percent TMA residues.
• Copolyester E is a linear copolyester comprising a diacid component containing 100 mole percent terephthalic acid residues and a diol component containing 81 mole percent CHDM residues and 19 mole percent ethylene glycol.
• Polycarbonate X is a linear polycarbonate produced by Dow Chemical Company under the commercial name Calibre 300-10. It has a
• melt flow rate (MFR) of 10 measured according to ASTM D 1238 at 300 0 C
• Polycarbonate Y is a branched polycarbonate produced by Dow Chemical Company under the commercial name Calibre 603-3. It has a
• melt flow rate (MFR) 3 measured according to ASTM D 1238 at 300 0 C
• the phosphorus concentrate (designated “cone” in Table 1 ) was prepared by first compounding Weston 619, a distearyl pentaerythritol diphosphite available from GE Specialty Plastics, into copolyester D on a single screw extruder at 27O 0 C. This composition is then tumble-blended with 5 wt% water at 8O 0 C for 8 hours to hydrolyze the Weston 619. The final phosphorus content of the pellets is 5 weight percent elemental phosphorus based on total pellet weight.
• Comparative Example 1 is an example of neat copolyester C. This material has a good shear thinning ratio, but does not possess a sufficiently high glass transition temperature (Tg) for high heat applications.
• Comparative Example 2 is an example of a blend that does not contain any branched copolyester. This blend does possess a sufficiently high glass transition temperature for high heat applications, but does not have a high enough shear thinning ratio to be blown into bottles.
• Comparative Example 3 is an example of a blend of polycarbonate with a copolyester that has too low a level of CHDM. This blend is hazy.
• Examples 1-5 are examples of the invention that possess high glass transition temperatures, possess good shear thinning ratios, and are free of haze.
• Bottles were generated from the blends prepared in Comparative Example 3 using an 80 mm Bekum H-121 continuous extrusion blow- molding machine fitted with a barrier screw. The materials were dried for 12 hours at 65°C (150 0 F) prior to extrusion. The extruder was run at 12 revolutions per minute (RPM) using a 215°C (42O 0 F) barrel temperature and a 199°C (390 0 F) head temperature. The temperature of the melt was 232 0 C (449°F), measured by inserting a melt probe directly into the parison 5mm out from the die. The materials were extruded into water bottles having a volume of 3.785 liters (1 U.S. gallon), using a 100 mm die. The bottles weighed 175 grams. Haze in the bottle sidewall was measured to be 3.94%.
• Bottles were generated from the blend prepared in Example 1 using an 80 mm Bekum H-121 continuous extrusion blow-molding machine fitted with a barrier screw. The materials were dried for 12 hours at 65 0 C (150 0 F) prior to extrusion. The extruder was run at 27 revolutions per minute (RPM) using a 199 0 C (39O 0 F) barrel temperature and a 199°C (390 0 F) head temperature. The temperature of the melt was 239°C (452 0 F), measured by inserting a melt probe directly into the parison 5mm out from the die. The materials were extruded into water bottles having a volume of 3.785 liters (1 U.S. gallon), using a 100 mm die. The bottles weighed 150 grams. Haze in the bottle sidewall was measured to be 0.38%.
• Bottles were generated from the blend prepared in Example 2 using an 80 mm Bekum H-121 continuous extrusion blow-molding machine fitted with a barrier screw. The materials were dried for 8 hours at 65 0 C (150 0 F) prior to extrusion. The extruder was run at 21 revolutions per minute (RPM) using a 200°C (392 0 F) barrel temperature and a 190 0 C (375°F) head temperature. The temperature of the melt was 218°C (425°F), measured by inserting a melt probe directly into the parison 5mm out from the die. The materials were extruded into water bottles having a volume of 3.785 liters (1 U.S. gallon), using a 100 mm die. The bottles weighed 150 grams. Haze in the bottle sidewall was measured to be 0.71%.
• Bottles were generated from the blend prepared in Example 3 using an 80 mm Bekum H-121 continuous extrusion blow-molding machine fitted with a barrier screw containing a Maddock mixing section. The materials were dried for 8 hours at 65 0 C (15O 0 F) prior to extrusion. The extruder was run at 10 revolutions per minute (RPM) using a 232 0 C (45O 0 F) barrel temperature and a 232 0 C (450 0 F) head temperature. The temperature of the melt was 249 0 C (481 0 F), measured by inserting a melt probe directly into the parison 5mm out from the die. The materials were extruded into handleware bottles having a volume of 1.89 liters (64 ounces), using a 70 mm die. The bottles weighed 120 grams. Haze in the bottle sidewall was measured to be 0.59%.
• Bottles were generated from the blend prepared in Example 4 using an 80 mm Bekum H-121 continuous extrusion blow-molding machine fitted with a barrier screw containing a Maddock mixing section. The materials were dried for 8 hours at 65 0 C (150 0 F) prior to extrusion. The extruder was run at 10 revolutions per minute (RPM) using a 232°C (450°F) barrel temperature and a 232°C (450 0 F) head temperature. The temperature of the melt was 25O 0 C (483°F), measured by inserting a melt probe directly into the parison 5mm out from the die.
• RPM revolutions per minute

Landscapes

• Chemical & Material Sciences (AREA)
• Medicinal Chemistry (AREA)
• Health & Medical Sciences (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Polymers & Plastics (AREA)
• Organic Chemistry (AREA)
• Mechanical Engineering (AREA)
• Manufacturing & Machinery (AREA)
• Engineering & Computer Science (AREA)
• Compositions Of Macromolecular Compounds (AREA)
• Manufacture Of Macromolecular Shaped Articles (AREA)
• Containers Having Bodies Formed In One Piece (AREA)
• Wrappers (AREA)
• Blow-Moulding Or Thermoforming Of Plastics Or The Like (AREA)

Priority Applications (2)

Applications Claiming Priority (2)

Publications (1)

Family

ID=36021783

Family Applications (1)

Country Status (4)

Cited By (2)

Families Citing this family (6)

Citations (4)

Family Cites Families (48)

• 2004
  • 2004-11-05 US US10/982,305 patent/US7345104B2/en not_active Expired - Fee Related
• 2005
  • 2005-11-01 WO PCT/US2005/039886 patent/WO2006052697A1/en not_active Ceased
  • 2005-11-01 JP JP2007540051A patent/JP2008519130A/ja active Pending
  • 2005-11-01 EP EP05824765A patent/EP1807473A1/en not_active Withdrawn