WO2005115055A1 - Electric resistance heater, made of synthetic resin - Google Patents

Electric resistance heater, made of synthetic resin Download PDF

Info

Publication number
WO2005115055A1
WO2005115055A1 PCT/DE2005/000899 DE2005000899W WO2005115055A1 WO 2005115055 A1 WO2005115055 A1 WO 2005115055A1 DE 2005000899 W DE2005000899 W DE 2005000899W WO 2005115055 A1 WO2005115055 A1 WO 2005115055A1
Authority
WO
WIPO (PCT)
Prior art keywords
synthetic resin
resistance heating
layer
electrical
heating
Prior art date
Application number
PCT/DE2005/000899
Other languages
German (de)
French (fr)
Inventor
Klaus Peter Steppler
Original Assignee
Sika Deutschland Gmbh
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from DE202004008114U external-priority patent/DE202004008114U1/en
Priority claimed from DE200420018668 external-priority patent/DE202004018668U1/en
Application filed by Sika Deutschland Gmbh filed Critical Sika Deutschland Gmbh
Priority to DE112005001804T priority Critical patent/DE112005001804A5/en
Priority to EP05753060A priority patent/EP1757167A1/en
Publication of WO2005115055A1 publication Critical patent/WO2005115055A1/en

Abstract

The invention relates to a flat, electric heating element wherein electrically conductive particles are added to a synthetic resin binder in order to make said binder electrically conductive. The synthetic resin layer is warmed when it is cross-flown. The flat, electric heating element, which is made of synthetic resin, sticks in a secure manner to the base thereof and can be applied in very thin layers. After the application of an insulation layer, which is made of non-conductive synthetic resin, onto the flat, electric heating element, which is made of synthetic resin, any particular upper layer can be applied. The starting material of the flat, electric heating element, which is made of synthetic resin, is controlled in such a manner that it becomes elastic during hardening and is resistant to tearing during the formation of cracks in the base. It does not contain any organic solvents and can be diluted with water. The material also has a high water-vapour permeability which prevents the formation of bubbles. The flat electric heating element, which is made of synthetic resin, can also be used in the inside of buildings as the main heating element or an auxiliary heating element, as well as on the outside in order to prevent the formation ice.

Description

Beschreibung elektrische Kunstharz - Widerstandsheizung Description electrical synthetic resin - resistance heating
Bei elektrischen Widerstandsheizungen handelt es sich um Flächenheizungen, bei denen die Heizwirkung darin besteht, dass sich elektrisch leitfähige Materialien in Folge ihres Widerstandes beim Durchfließen des Stromes erwärmen.Electrical resistance heaters are surface heating systems, where the heating effect is that electrically conductive materials heat up as a result of their resistance when the current flows through.
Diese elektrisch leitfähigen Materialien liegen meist in Form von Kabeln, Metallgittern, Geweben aus Metallfäden, Metallfolien oder gefüllten Kunststofffolien vor.These electrically conductive materials are usually in the form of cables, metal grids, fabrics made of metal threads, metal foils or filled plastic foils.
Solche elektrische Widerstandsheizungen sind in der Patentanmeldung PCT/DE 90/00693 ausführlich beschrieben. In dieser Patentanmeldung wird eine elektrische Kunstharz - Widerstandsheizung beschrieben, bei der die Widerstandsheizung als Fußbodenheizung wirkt. Es wird eine elektrische Widerstandsbeschichtung beschrieben, bei der eine Schicht aus elektrisch leitenden Partikeln und einem Bindemittel auf den Fußboden aufgestrichen oder aufgewalzt wird. Im Ausgangsmaterial des Bindemittels können zur Einstellung der Zähigkeit noch Lösungsmittel Weichmacher etc. enthalten sein. Die Schichtdicke sollte zwischen 0,1 und 1 Millimeter liegen. Auf dieser Widerstandsheizung wird eine Oberschicht aus mineralischem Material aufgebracht, das eine Dicke zwischen 2 und 15 mm aufweist. Vorzugsweise soll diese Oberschicht aus einem Anhydritmaterial bestehen.Such electrical resistance heaters are described in detail in patent application PCT / DE 90/00693. In this patent application, an electrical synthetic resin resistance heater is described, in which the resistance heater acts as underfloor heating. An electrical resistance coating is described in which a layer of electrically conductive particles and a binder is brushed onto or rolled onto the floor. Solvents, plasticizers, etc. can also be contained in the starting material of the binder to adjust the toughness. The layer thickness should be between 0.1 and 1 millimeter. A top layer of mineral material is applied to this resistance heater, which has a thickness between 2 and 15 mm. This top layer should preferably consist of an anhydrite material.
Bei der praktischen Anwendung dieses beschriebenen Verfahrens hat sich dann jedoch gezeigt, dass diese Kunstharz - Widerstandsheizung nur dann ausreichend gut verarbeitbar war, wenn dem Ausgangsmaterial organisches Lösemittel zugegeben wurde. Dieses organische Lösemittel verflüchtigte sich dann jedoch während der Heizperiode und führte zu schädlichen Luftverunreinigungen in den Räumen. Bei den in der Patentanmeldung aufgeführten Siebdruckpasten handelte es sich um elektrisch leitfähige Kunstharze, die wesentlich zu zähflüssig für die Verwendung als streichbare Flächenheizung waren. Aus diesem Grunde mussten die Siebdruckharze mit diesen organischen Lösemitteln verdünnt werden.In the practical application of this described method, however, it was found that this synthetic resin resistance heater could only be processed sufficiently well if organic solvent was added to the starting material. However, this organic solvent then evaporated during the heating period and led to harmful air pollution in the rooms. The screen printing pastes listed in the patent application were electrically conductive synthetic resins which were significantly too viscous for use as a brushable surface heating. For this reason, the screen printing resins had to be diluted with these organic solvents.
Darüber hinaus konnte aufgrund der elektrischen Widerstandsberechnung dieses Material nur in sehr dünnen Schichten aufgetragen werden, so dass Fehlstellen im Untergrund insbesondere bei unebenen Betondecken oder Estrichen nicht ausreichend ausgefüllt werden konnten, so dass immer wieder kleine Inseln entstanden, in denen die Widerstandsheizung nicht funktionierte. Als weiterer wesentlichen Nachteil dieser beschriebenen Kunstharz - Flächenheizung hat sich herausgestellt, dass bei geringsten Rissbildungen im Untergrund die Widerstandsheizung ebenfalls über diesem Riss getrennt wurde, so dass die Widerstandsheizung vollständig ihre Wirkung verlor, da dann im Bereich des Risses der Stromfluss unterbrochen war. Die Kunstharz - Widerstandsheizung hatte den entscheidenden Nachteil, eine zu geringe rissüberbrückende Wirkung zu haben und die Materialien waren für den Einsatz als Kunstharz - Flächenheizung zu spröde.In addition, due to the electrical resistance calculation, this material could only be applied in very thin layers, so that imperfections in the subsurface, particularly with uneven concrete ceilings or screeds, could not be filled in sufficiently, so that small islands were repeatedly created in which the resistance heating did not work. Another significant disadvantage of this synthetic resin surface heating has been found to be that, with the slightest crack formation in the subsoil, the resistance heating was also separated above this crack, so that the resistance heating completely lost its effect, since the current flow was then interrupted in the area of the crack. The synthetic resin resistance heating had the decisive disadvantage that it had too little crack bridging effect and the materials were too brittle for use as synthetic resin surface heating.
Darüber hinaus besaß die Kunstharz - Widerstandsheizung in der beschriebenen Form nahezu keinerlei Wasserdampfdurchlässigkeit, so dass sich bei der Benutzung der Heizung immer wieder Blasen ausbildeten, da aus dem Untergrund ausdiffundierende Restfeuchtigkeit sich unter der Heizschicht ansammelte und in Folge des entstehenden Dampfdruckes es zu einer Loslösung der Kunstharzschicht vom Untergrund kam.In addition, the synthetic resin resistance heater in the described form had almost no water vapor permeability, so that bubbles continued to form when the heater was used, since residual moisture diffusing out of the subsurface accumulated under the heating layer and, as a result of the resulting steam pressure, caused it to separate Resin layer came from the underground.
In dieser Patentanmeldung ist als Oberschicht eine mineralische Oberschicht mit einer Dicke von 2 bis 15 mm beschrieben. Diese mineralische Oberschicht hat keinerlei isolierende Wirkung und auch hier hat die Praxis gezeigt, dass es unbedingt erforderlich ist auf die Kunstharz - Widerstandsheizung eine zusätzliche Isolationsschicht aufzubringen. Auf dieser zusätzlichen Isolationsschicht kann dann jede beliebige Art von Oberschicht aufgebracht werden.In this patent application, a mineral top layer with a thickness of 2 to 15 mm is described as the top layer. This mineral top layer has no insulating effect and here too practice has shown that it is absolutely necessary to apply an additional insulation layer to the synthetic resin resistance heater. Any type of top layer can then be applied to this additional insulation layer.
Mit dieser Erfindung wird erreicht, dass diese Nachteile einer kunstharzgebundenen Widerstandsheizung nicht mehr auftreten. Dies wird durch folgende Maßnahmen erreicht:With this invention it is achieved that these disadvantages of a resin-bonded resistance heater no longer occur. This is achieved through the following measures:
Verwendung eines Kunstharzes, dessen Viskosität durch die Zugabe von Wasser so gesteuert werden kann, dass das Material einwandfrei durch Rollen, Streichen oder Verlaufen auf eine Oberfläche aufgebracht werden kann.Use of a synthetic resin, the viscosity of which can be controlled by the addition of water so that the material can be applied perfectly to a surface by rolling, brushing or running.
Zur Herstellung der elektrischen Leitfähigkeit wird diesem Material Graphit und/oder andere elektrisch leitfähige Materialien zugegeben, deren Menge, Reinheit und Feinheit so variiert werden kann, dass je nach benötigter Leistung der Widerstandsheizung unterschiedliche Mischungsverhältnisse verwendet werden unter Berücksichtigung der erforderlichen Verarbeitbar- keit des Materials.To produce the electrical conductivity, graphite and / or other electrically conductive materials are added to this material, the amount, purity and fineness of which can be varied so that different mixing ratios are used depending on the required power of the resistance heating, taking into account the required processability of the material.
Das verwendete Kunstharz, das nach der Erhärtung ein zähelastisches Verformungsverhalten aufweist, ist ausreichend elastifiziert, um bei Rissbildungen im Untergrund ein Durchreißen der Heizschicht über diesen Rissen zu verhindern. Die Formulierung des Kunstharzes ist so eingestellt, dass hier eine größtmögliche Sicherheit gegen Rissbildungen in der Heizschicht selbst besteht. Durch solche Rissbildungen würde der Stromfluss unterbrochen und die Widerstandsheizung würde wirkungslos werden.The synthetic resin used, which has a tough elastic deformation behavior after hardening, is sufficiently elastic to prevent cracking of the heating layer above these cracks if the substrate is cracked. The formulation of the synthetic resin is adjusted so that there is the greatest possible security against crack formation in the heating layer itself. Such cracks would interrupt the current flow and the resistance heating would become ineffective.
Die Kunstharz - Widerstandsheizung kann so eingestellt werden, dass sie in verschiedenen Dicken auftragbar ist. Durch die Kombination der verwendeten Graphite und der sonstigen e- lektrisch leitfähigen Materialien und der Viskosität des Kunstharzes ist es möglich die Kunstharz - Widerstandsheizung sowohl als sehr dünne Schicht im Bereich von 0,1 bis 1 Millimeter als auch als mehrere Millimeter dicke Schicht auszuführen. Letzteres ist dann von Bedeutung, wenn der Untergrund Unebenheiten aufweist die mit der Widerstandsheizung ausgeglichen werden müssen.The synthetic resin resistance heater can be set so that it can be applied in different thicknesses. The combination of the graphite used and the other electrically conductive materials and the viscosity of the synthetic resin make it possible to design the synthetic resin resistance heating both as a very thin layer in the range from 0.1 to 1 millimeter and as a layer several millimeters thick. The latter is important if the surface has unevenness that has to be compensated with the resistance heating.
Die elektrische Kunstharz - Widerstandsheizung wird im Gebaudeinnern zum Beheizen unterschiedlicher Flächen eingesetzt. Sie kann auf Wände aufgestrichen werden um eine Strahlungsheizung zu erzeugen. Sie kann ebenso auf Fußböden aufgestrichen werden um auch hier eine flächige Fußbodenheizung zu erreichen.The electrical synthetic resin resistance heating is used inside the building to heat different surfaces. It can be spread on walls to create radiant heating. It can also be spread on floors in order to achieve extensive underfloor heating.
Als dritte Möglichkeit ist der Einsatz der Widerstandsheizung an bestehenden Wärmebrücken eines Gebäudes zu sehen, bei denen das betroffene Bauteil wie beispielsweise eine Raumecke oder der Sturzbereich über einem Fenster mit der Widerstandsheizung eingestrichen wird. Die Oberflächentemperatur dieser Kältebrücke wird dann um einige Kelvin erhöht um eine spätere Schimmelbildung zu verhindern.The third option is the use of resistance heating on existing thermal bridges in a building, in which the affected component, such as a corner of the room or the lintel area, is coated with the resistance heating over a window. The surface temperature of this cold bridge is then increased by a few Kelvin to prevent mold from forming later.
In allen drei genannten Fällen ist es möglich die dünn aufgetragene Widerstandsheizung zum Beispiel mit einer Tapete zu überkleben, zu überstreichen oder mit Fliesen oder sonstigen Bodenbelägen zu versehen.In all three cases mentioned, it is possible to cover the thinly applied resistance heating, for example with wallpaper, paint it over or provide it with tiles or other floor coverings.
Beim Einsatz der Kunstharz - Widerstandsheizung im Freien ist es möglich, zum Beispiel Treppen oder Treppenpodeste sowie Wege eisfrei zu halten. In diesem Fall wird die Kunstharz - Widerstandsheizung entweder auf die Bauelemente aufgestrichen und später mit einer weiteren Schutzschicht versehen oder sie kann auf die Rückseite der Fliesen oder Platten appliziert werden. Es besteht auch die Möglichkeit zum Beispiel bei Naturstein - Platten diese wie ein Sandwich aufzuschneiden, die Widerstandsheizung auf den aufgeschnittenen Flächen aufzutragen und anschließend die beiden Sandwichhälften mit der Widerstandsheizung wieder zu verkleben. Das Kunstharzmaterial der Widerstandsheizung dient nicht nur als Bindemittel für die elektrisch leitfähigen Graphit - Partikel sondern es hat auch eine hervorragende klebende oder verbindende Wirkung.When using synthetic resin resistance heating outdoors, it is possible to keep stairs or stair landings and paths free of ice, for example. In this case, the synthetic resin resistance heating is either brushed onto the components and later provided with a further protective layer, or it can be applied to the back of the tiles. There is also the possibility, for example, of cutting natural stone slabs like a sandwich, applying the resistance heater to the cut surfaces and then gluing the two sandwich halves back together with the resistance heater. The synthetic resin material of the resistance heater not only serves as a binder for the electrically conductive graphite particles, it also has an excellent adhesive or connecting effect.
Mit der elektrischen Kunstharz - Widerstandsheizung können im Freien zum Beispiel auch Ablaufrinnen oder dergleichen beschichtet werden, so dass sie bei Frost so beheizt werden, dass Vereisungen oder Verstopfungen der Ablaufrinnen verhindert werden.The electrical synthetic resin resistance heater can also be used to coat gutters or the like, for example, so that they are heated in freezing conditions to prevent icing or clogging of the gutters.
Prinzipiell sind alle anderen Anwendungsfälle denkbar, bei denen eine flächige Vereisung aus verschiedenen Gründen verhindert werden soll. Der Vorteil der Kunstharz - Widerstandsheizung liegt zum einen darin, dass sie sehr dünn und gleichmäßig aufgetragen werden kann und darüber hinaus, dass sie mit beliebigen Materialien beschichtet werden kann und gleichzeitig als Haftbrücke oder Kleber dient.In principle, all other applications are conceivable in which flat icing is to be prevented for various reasons. The advantage of the synthetic resin resistance heating is that it can be applied very thinly and evenly, and also that it can be coated with any material and at the same time serves as an adhesive bridge or adhesive.
Die praktische Anwendung hat ebenfalls gezeigt, dass es nicht möglich ist die elektrische Widerstandsheizung ohne Isolationsschicht einzusetzen. Beim Fehlen dieser Isolationsschicht werden elektrische Ableitströme erzeugt, die durch eine ausreichend dimensionierte Isolation verhindert werden müssen.Practical application has also shown that it is not possible to use electrical resistance heating without an insulation layer. In the absence of this insulation layer, electrical leakage currents are generated, which must be prevented by an adequately dimensioned insulation.
In den beiden nationalen Gebrauchsmustern „Isolationsschicht für eine elektrische Kunstharz- Widerstandsheizung" und „Richtrezeptur für eine elektrische Kunstharz- Widerstandsheizung" werden Lösungen für diese Aufgabenstellung aufgezeigt. In den beiliegenden Zeichnungen ist das Prinzip der elektrischen Kunstharz- Widerstandsheizung und der Isolationsschicht jeweils aufgezeigt. Solutions for this task are shown in the two national utility models "insulation layer for an electrical synthetic resin resistance heating" and "standard formulation for an electrical synthetic resin resistance heating". The principle of electrical synthetic resin resistance heating and the insulation layer is shown in the accompanying drawings.

Claims

Schutzansprüche protection claims
1. elektrische Kunstharz - Widerstandsheizung als dünne, elektrisch leitfähige Beschichtung dadurch gekennzeichnet, dass diese aus elektrisch leitfähigen Partikeln und einem Kunstharz besteht, das frei ist von organischen Lösemitteln und mit Wasser soweit verdünnt wird, bis die gewünschte Konsistenz eingestellt ist. Diese Heizschicht kann in Schichtdicken von 0,1 bis mehreren Millimetern aufgetragen werden. Auf diese Heizschicht wird dann eine Isolationsschicht aufgebracht. Auf die Isolationsschicht wird anschließend ein beliebiger Oberbelag verlegt.1. electrical synthetic resin - resistance heating as a thin, electrically conductive coating, characterized in that it consists of electrically conductive particles and a synthetic resin that is free from organic solvents and diluted with water until the desired consistency is achieved. This heating layer can be applied in layer thicknesses of 0.1 to several millimeters. An insulation layer is then applied to this heating layer. Any surface covering is then laid on the insulation layer.
Die erforderliche Stromzuführung erfolgt an zwei Seiten der Kunstharz- Widerstandsheizung, wobei die Zuführung über das Phasenkabel auf der einen Seite und über den Nullleiter auf der anderen Seite erfolgt.The required power supply takes place on two sides of the synthetic resin resistance heating, the supply via the phase cable on one side and via the neutral conductor on the other side.
2. elektrische Kunstharz - Widerstandsheizung nach Anspruch 1 , dadurch gekennzeichnet, dass das elektrisch leitfähige Kunstharzmaterial durch Streichen, Sprühen, Rollen oder Rakeln auf den Untergrund aufgetragen wird. Der Untergrund ist dabei beliebig und kann zum Beispiel aus Beton, Putz, Holz, Metall oder sonstigen Materialien bestehen. Zwischen Untergrund und Heizschicht wird vorzugsweise eine Haftbrücke (Primer) aufgebracht, die nach unten hin eine elektrisch isolierende Wirkung besitzt und darüber hinaus das Nachrücken von Feuchtigkeit aus dem Untergrund verhindert. Diese Haftbrücke besteht ebenfalls aus einem Kunstharz, das nach Bedarf mit Wasser verdünnt werden kann. Diesem Kunstharz der Haftbrücke sind keine elektrisch leitfähigen Partikel zugegeben.2. Electrical synthetic resin - resistance heating according to claim 1, characterized in that the electrically conductive synthetic resin material is applied to the substrate by brushing, spraying, rolling or knife coating. The surface is arbitrary and can consist of concrete, plaster, wood, metal or other materials, for example. An adhesive bridge (primer) is preferably applied between the substrate and the heating layer, which has an electrically insulating effect at the bottom and also prevents moisture from moving up from the substrate. This adhesive bridge also consists of a synthetic resin that can be diluted with water as required. No electrically conductive particles are added to this synthetic resin of the adhesive bridge.
3. elektrische Kunstharz - Widerstandsheizung nach den vorgenannten Ansprüchen, dadurch gekennzeichnet, dass das Kunstharzmaterial so eingestellt ist, dass es ein zähelastisches Verhalten aufweist und somit Risse im Untergrund sich nicht in der aufgebrachten Kunstharz- Widerstandsheizung fortsetzen.3. electrical synthetic resin - resistance heating according to the preceding claims, characterized in that the synthetic resin material is adjusted in such a way that it exhibits tough elastic behavior and therefore cracks in the substrate do not continue in the applied synthetic resin resistance heating.
4. elektrische Kunstharz - Widerstandsheizung nach den vorgenannten Ansprüchen, dadurch gekennzeichnet, dass das verwendete Kunstharz eine ausreichende Wasserdampfdurchlässigkeit aufweist um Blasenbildungen der Kunstharz- Widerstandsheizung bei Restfeuchtigkeit im Untergrund zu verhindern.4. electrical synthetic resin - resistance heating according to the preceding claims, characterized in that the synthetic resin used has a sufficient water vapor permeability to prevent bubbles of the synthetic resin resistance heating in case of residual moisture in the underground.
5. elektrische Kunstharz - Widerstandsheizung nach den vorgenannten Ansprüchen, dadurch gekennzeichnet, dass auf der Kunstharz - Widerstandsheizung eine Isolationsschicht aufgebracht wird, die einen Isolationswiderstand von mindestens 2 Megaohm zur direkten Applikation auf der elektrisch leitfähigen Kunstharzschicht aufweist. Diese Kunstharz - Isolationsschicht besteht in Innenräumen aus lösemittelfreien Kunstharzen, die lediglich durch die Zugabe von Wasser verdünnt werden können. Bei Außenanwendungen können auch lösemittelhaltige Kunstharze dafür verwendet werden. Das flüssige Kunstharz ist in seiner Viskosität so eingestellt, dass es auf die erhärtete elektrisch leitfähige Kunstharz - Widerstandsheizung zum Beispiel durch Streichen, Rollen oder Aufsprühen appliziert werden kann.5. electrical synthetic resin resistance heating according to the preceding claims, characterized in that an insulating layer is applied to the synthetic resin resistance heating, which has an insulation resistance of at least 2 megohms for direct application on the electrically conductive synthetic resin layer. In the interior, this synthetic resin insulation layer consists of solvent-free synthetic resins that can only be thinned by adding water. Solvent-based synthetic resins can also be used for outdoor applications. The viscosity of the liquid synthetic resin is adjusted so that it can be applied to the hardened, electrically conductive synthetic resin resistance heating, for example by brushing, rolling or spraying.
6. elektrische Kunstharz - Widerstandsheizung nach einem der vorgenannten Ansprüche, dadurch gekennzeichnet, dass für die Stromeinführung in die elektrische Kunstharz - Widerstandsheizung an den beiden Seiten selbstklebende Kupferfolien verwendet werden. Diese selbstklebenden Kupferfolien haben vorzugsweise eine Breite von wenigen Zentimetern. 6. electrical synthetic resin resistance heating according to one of the preceding claims, characterized in that self-adhesive copper foils are used on both sides for the current introduction into the electrical synthetic resin resistance heating. These self-adhesive copper foils preferably have a width of a few centimeters.
7. elektrische Kunstharz - Widerstandsheizung nach einem der vorgenannten Ansprüche, dadurch gekennzeichnet, dass die Kunstharzschicht auf ein Bauteil zum Beispiel einen Fenstersturz aufgetragen wird, der aus konstruktiven Mängeln eine Kältebrücke darstellt. Auf diese Heizschicht wird dann im Innenraum eine Tapete mit Anstrich aufgebracht (Figur 1).7. electrical synthetic resin - resistance heating according to one of the preceding claims, characterized in that the synthetic resin layer is applied to a component, for example a lintel, which constitutes a thermal bridge due to structural defects. A wallpaper with paint is then applied to this heating layer in the interior (FIG. 1).
8. elektrische Kunstharz - Widerstandsheizung nach einem der vorgenannten Ansprüche, dadurch gekennzeichnet, dass der als Heizschicht wirkende Kunstharzanstrich mit den stromzuführenden Elementen zwischen zwei Natursteinplatten als Kleber eingebracht wird (Figur 2). Sie dient bei diesem Bauteil, das im Freien auf Treppenstufen oder im Eiήgangsbereich eingebaut wird, gleichzeitig als Klebe- und Heizschicht.8. electrical synthetic resin - resistance heating according to one of the preceding claims, characterized in that the synthetic resin coating acting as a heating layer is introduced with the current-carrying elements between two natural stone slabs as an adhesive (Figure 2). With this component, which is installed outdoors on stairs or in the entrance area, it also serves as an adhesive and heating layer.
9. elektrische Kunstharz - Widerstandsheizung nach einem der vorgenannten Ansprüche, dadurch gekennzeichnet, dass die elektrische Kunstharz - Flächenheizung im Gebaudeinnern als Fußbodenheizung eingesetzt wird, wobei auf die Heizschicht ein beliebiger Oberbelag aufgebracht wird (Figur 3).9. electrical synthetic resin resistance heating according to one of the preceding claims, characterized in that the electrical synthetic resin surface heating is used in the interior of the building as underfloor heating, any top covering being applied to the heating layer (FIG. 3).
10. elektrische Kunstharz - Widerstandsheizung nach einem der vorgenannten Ansprüche, dadurch gekennzeichnet, dass die Kunstharzschicht auf steile Rampen, die von Fahrzeugen befahren werden, aufgebracht wird. Auf die Kunstharz - Widerstandsheizung wird dann eine entsprechende abriebfeste Nutzschicht aufgebracht (Figur 4). 10. electrical synthetic resin - resistance heating according to one of the preceding claims, characterized in that the synthetic resin layer is applied to steep ramps which are used by vehicles. A corresponding abrasion-resistant wear layer is then applied to the synthetic resin resistance heater (FIG. 4).
1. elektrische Kunstharz - Widerstandsheizung nach einem der vorgenannten Ansprüche dadurch gekennzeichnet, dass die elektrische Widerstandsheizung zum Beispiel auf Flügel von Windkraftanlagen oder sonstigen Flugkörpern aufgetragen wird um die Bildung von Eis auf diesen Flügeln zu verhindern (Figur 5 und 6). 1. electrical synthetic resin - resistance heating according to one of the preceding claims, characterized in that the electrical resistance heating is applied, for example, to wings of wind turbines or other missiles to prevent the formation of ice on these wings (Figures 5 and 6).
PCT/DE2005/000899 2004-05-22 2005-05-18 Electric resistance heater, made of synthetic resin WO2005115055A1 (en)