WO2004035838A1 - Procede de fabrication de toles d'acier durcissables par cuisson, toles d'acier et pieces ainsi obtenues - Google Patents
Procede de fabrication de toles d'acier durcissables par cuisson, toles d'acier et pieces ainsi obtenues Download PDFInfo
- Publication number
- WO2004035838A1 WO2004035838A1 PCT/FR2003/002985 FR0302985W WO2004035838A1 WO 2004035838 A1 WO2004035838 A1 WO 2004035838A1 FR 0302985 W FR0302985 W FR 0302985W WO 2004035838 A1 WO2004035838 A1 WO 2004035838A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- steel
- weight
- temperature
- less
- sheet
- Prior art date
Abstract
Description
Claims