WO2004026385A1 - 医療用ガイドワイヤー及びその製造方法 - Google Patents
医療用ガイドワイヤー及びその製造方法 Download PDFInfo
- Publication number
- WO2004026385A1 WO2004026385A1 PCT/JP2003/011807 JP0311807W WO2004026385A1 WO 2004026385 A1 WO2004026385 A1 WO 2004026385A1 JP 0311807 W JP0311807 W JP 0311807W WO 2004026385 A1 WO2004026385 A1 WO 2004026385A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- fluororesin
- particulate matter
- coating layer
- medical
- fluororesin coating
- Prior art date
Description
Claims