Classifications

• • G—PHYSICS
  • G02—OPTICS
  • G02B—OPTICAL ELEMENTS, SYSTEMS OR APPARATUS
  • G02B6/00—Light guides; Structural details of arrangements comprising light guides and other optical elements, e.g. couplings
  • G02B6/02—Optical fibres with cladding with or without a coating
  • G02B6/02057—Optical fibres with cladding with or without a coating comprising gratings
  • G02B6/02076—Refractive index modulation gratings, e.g. Bragg gratings
  • G02B6/02123—Refractive index modulation gratings, e.g. Bragg gratings characterised by the method of manufacture of the grating
• • C—CHEMISTRY; METALLURGY
  • C03—GLASS; MINERAL OR SLAG WOOL
  • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
  • C03C23/00—Other surface treatment of glass not in the form of fibres or filaments
  • C03C23/0005—Other surface treatment of glass not in the form of fibres or filaments by irradiation
  • C03C23/0025—Other surface treatment of glass not in the form of fibres or filaments by irradiation by a laser beam
• • C—CHEMISTRY; METALLURGY
  • C03—GLASS; MINERAL OR SLAG WOOL
  • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
  • C03C25/00—Surface treatment of fibres or filaments made from glass, minerals or slags
  • C03C25/62—Surface treatment of fibres or filaments made from glass, minerals or slags by application of electric or wave energy; by particle radiation or ion implantation
  • C03C25/6206—Electromagnetic waves
  • C03C25/6208—Laser
• • G—PHYSICS
  • G02—OPTICS
  • G02B—OPTICAL ELEMENTS, SYSTEMS OR APPARATUS
  • G02B6/00—Light guides; Structural details of arrangements comprising light guides and other optical elements, e.g. couplings
  • G02B6/02—Optical fibres with cladding with or without a coating
  • G02B6/02052—Optical fibres with cladding with or without a coating comprising optical elements other than gratings, e.g. filters
• • G—PHYSICS
  • G02—OPTICS
  • G02B—OPTICAL ELEMENTS, SYSTEMS OR APPARATUS
  • G02B6/00—Light guides; Structural details of arrangements comprising light guides and other optical elements, e.g. couplings
  • G02B6/24—Coupling light guides
  • G02B6/26—Optical coupling means
  • G02B6/28—Optical coupling means having data bus means, i.e. plural waveguides interconnected and providing an inherently bidirectional system by mixing and splitting signals
  • G02B6/2804—Optical coupling means having data bus means, i.e. plural waveguides interconnected and providing an inherently bidirectional system by mixing and splitting signals forming multipart couplers without wavelength selective elements, e.g. "T" couplers, star couplers
  • G02B6/2821—Optical coupling means having data bus means, i.e. plural waveguides interconnected and providing an inherently bidirectional system by mixing and splitting signals forming multipart couplers without wavelength selective elements, e.g. "T" couplers, star couplers using lateral coupling between contiguous fibres to split or combine optical signals
• • G—PHYSICS
  • G02—OPTICS
  • G02B—OPTICAL ELEMENTS, SYSTEMS OR APPARATUS
  • G02B6/00—Light guides; Structural details of arrangements comprising light guides and other optical elements, e.g. couplings
  • G02B6/02—Optical fibres with cladding with or without a coating
  • G02B6/02057—Optical fibres with cladding with or without a coating comprising gratings
  • G02B6/02076—Refractive index modulation gratings, e.g. Bragg gratings
  • G02B6/02123—Refractive index modulation gratings, e.g. Bragg gratings characterised by the method of manufacture of the grating
  • G02B6/02147—Point by point fabrication, i.e. grating elements induced one step at a time along the fibre, e.g. by scanning a laser beam, arc discharge scanning
• • G—PHYSICS
  • G02—OPTICS
  • G02B—OPTICAL ELEMENTS, SYSTEMS OR APPARATUS
  • G02B6/00—Light guides; Structural details of arrangements comprising light guides and other optical elements, e.g. couplings
  • G02B6/10—Light guides; Structural details of arrangements comprising light guides and other optical elements, e.g. couplings of the optical waveguide type
  • G02B6/105—Light guides; Structural details of arrangements comprising light guides and other optical elements, e.g. couplings of the optical waveguide type having optical polarisation effects
• • G—PHYSICS
  • G02—OPTICS
  • G02B—OPTICAL ELEMENTS, SYSTEMS OR APPARATUS
  • G02B6/00—Light guides; Structural details of arrangements comprising light guides and other optical elements, e.g. couplings
  • G02B6/24—Coupling light guides
  • G02B6/26—Optical coupling means
  • G02B6/264—Optical coupling means with optical elements between opposed fibre ends which perform a function other than beam splitting
  • G02B6/266—Optical coupling means with optical elements between opposed fibre ends which perform a function other than beam splitting the optical element being an attenuator
• • G—PHYSICS
  • G02—OPTICS
  • G02B—OPTICAL ELEMENTS, SYSTEMS OR APPARATUS
  • G02B6/00—Light guides; Structural details of arrangements comprising light guides and other optical elements, e.g. couplings
  • G02B6/24—Coupling light guides
  • G02B6/26—Optical coupling means
  • G02B6/28—Optical coupling means having data bus means, i.e. plural waveguides interconnected and providing an inherently bidirectional system by mixing and splitting signals
  • G02B6/2804—Optical coupling means having data bus means, i.e. plural waveguides interconnected and providing an inherently bidirectional system by mixing and splitting signals forming multipart couplers without wavelength selective elements, e.g. "T" couplers, star couplers
  • G02B6/2852—Optical coupling means having data bus means, i.e. plural waveguides interconnected and providing an inherently bidirectional system by mixing and splitting signals forming multipart couplers without wavelength selective elements, e.g. "T" couplers, star couplers using tapping light guides arranged sidewardly, e.g. in a non-parallel relationship with respect to the bus light guides (light extraction or launching through cladding, with or without surface discontinuities, bent structures)
• • G—PHYSICS
  • G02—OPTICS
  • G02B—OPTICAL ELEMENTS, SYSTEMS OR APPARATUS
  • G02B6/00—Light guides; Structural details of arrangements comprising light guides and other optical elements, e.g. couplings
  • G02B6/24—Coupling light guides
  • G02B6/42—Coupling light guides with opto-electronic elements
  • G02B6/4201—Packages, e.g. shape, construction, internal or external details
  • G02B6/4204—Packages, e.g. shape, construction, internal or external details the coupling comprising intermediate optical elements, e.g. lenses, holograms
  • G02B6/4214—Packages, e.g. shape, construction, internal or external details the coupling comprising intermediate optical elements, e.g. lenses, holograms the intermediate optical element having redirecting reflective means, e.g. mirrors, prisms for deflecting the radiation from horizontal to down- or upward direction toward a device

Definitions

• the invention relates to the creation of permanently altered refractive index zones in glass waveguiding devices, including optical fibers and optical waveguides preexisted in a glass substrate, using the focused light output of ultrafast pulsed lasers, and to all-fiber devices incorporating such zones exhibiting permanently altered refractive index characteristics.
• All-fiber optical devices have many practical advantages, including low loss, ease of coupling with other fibers, polarization insensitivity, temperature insensitivity, and simple packaging, which make them attractive and low-cost solutions in the optical telecommunications and other industries. All-fiber devices rely on refractive index variations for their functions, and various methods for making permanent refractive index changes have been used in the past. Older methods have relied on exposing photosensitive optical fiber, such as Germanium doped optical fiber, to ultraviolet light to produce refractive index changes in the glass. A more recent method relies on the use of ultrafast pulsed lasers for producing very high intensity light and the resulting non-linear optical effects which are responsible for the refractive index modification phenomenon, see for example, US Patent No.
• the present invention is directed to the creation of zones of permanently altered refractive index characteristics in glass, particularly in optical waveguides and optical fibers, based on the principles expounded by Glezer et al and by Davis et al.
• zones in which the refractive index has been permanently altered are created in glass using a very high intensity laser beam which is produced by focusing the light output from an ultrafast pulsed laser at a predetermined target region in the glass.
• the preferred laser system for this invention is one in which the output of a frequency- doubled Erbium-doped fiber laser is amplified in a laser regenerative amplifier that is based on a Ti: Sapphire gain material, providing light pulses of approximately 100 femtosecond duration, each with an energy of between about 1 nanojoule and 1 millijoule, and preferably at a pulse repetition rate of between 500 Hz and 1 GHz.
• the invention embodies the use of laser repetition rates selected so that the time interval between laser pulses interacting with the material is shorter than the thermal diffusion time out of the volume element being modified by the laser. This time depends on the laser spot size and thermal diffusivity of the specific material.. The temperature of the glass is raised to the liquefying point thereby enabling optimal compaction of the written area with minimal stress.
• one or more zones of permanently altered refractive index characteristics can be formed in a waveguiding device, such as an optical fiber, by utilizing a focused, pulsed, laser light source which generates a focal region having an intensity greater than the threshold for inducing permanent refractive index changes in the device.
• the focal region is aligned with the device and relative movement between the focal region and the device has the effect of sweeping the focal region across the device in a predetermined path.
• the result is a zone within the device in which the refractive index characteristics of the device have been permanently altered.
• the altered zones in optical waveguides and fibers have a threefold effect.
• refractive index changes in the core and in the core-cladding boundary region, and possibly in the evanescent region in the cladding allow light propagating in the core to escape to the cladding.
• the altered zone itself acts as an optical waveguide, allowing light propagating in the core to escape to and then from the altered zone.
• the surface of a suitably oriented altered zone acts as a reflecting surface.
• All-fiber attenuators utilizing the three effects mentioned above scatter light out of the core, thereby achieving adjustable losses of 0 - 40 dB which can be set in less than O.ldB increments.
• All-fiber taps can be made with a typical tap ratio of 1%.
• All-fiber polarimeters utilize the reflecting surfaces of altered zones that are oriented at Brewster angles to reflect s-polarized light out of the core.
• Such devices could be based, for example, on interconnecting different cores within a multiple core fiber using methods described herein to couple light into and out of altered index of refraction zones within the fiber and into and out of different cores in the fiber.
• Such a method could be used to create a wide variety of complex devices with a significant reduction in manufacturing, packaging and engineering costs. Such devices would be much more compact than similar devices manufactured using other methods.
• the creation of such altered zones to control the states of light propagation in a fiber eliminates the need for precision alignment at the input and/or the output of the fiber into another fiber.
• the process of the present invention is one that can be fully automated, thereby reducing the cost of achieving waveguides with the permanently altered zones therein and ensuring the production of consistent and high quality components.
• the present invention may be generally considered to provide a method of creating a zone of permanently altered refractive index characteristics in an optical waveguiding device made of glass material having at least one core and at least one cladding, using a beam which is generated by a focused pulsed laser light source having :(i) a wavelength greater than the absorption edge of the glass material; (ii) a pulse width of less than 1 picosecond, and a pulse energy of between 1 nanojoule and 1 millijoule; and (iii) capable of achieving a peak pulse intensity within a defined focal region; comprising the steps of: (a) aligning the laser beam focal region with a defined target region within the waveguiding device; and (b) operating the laser light source with the peak pulse intensity thereof and a repetition rate thereof selected to accumulate heat and to soften the glass material at the target region and to thereby induce permanent refractive index changes in the waveguiding device at the target region.
• the invention may also be considered to encompass an optical waveguiding device having at least one core, at least one cladding, and at least a single zone therein at which the refractive index characteristics of the waveguiding device have been permanently altered, whereby the altered waveguiding device can serve as an attenuator, a polarimeter, an optical tap, or a more complex device.
• beneficial material modification techniques that fall within the scope of this invention can be used for femtosecond-pulse-assisted microstructuring of an optical waveguide device.
• these special techniques involve the addition of externally applied stimuli to the femtosecond-pulse micro structuring methods described in the body of the specification. Combining additional stimuli together with femtosecond pulse exposure increases the functionality of femtosecond-pulse-modified optical-waveguide technology, as described below.
• Figure 1 is an end view of a waveguiding device showing the basic principles of the method of the present invention with a single laser beam.
• Figure 2 is a perspective, schematic view of a portion of a waveguiding- device with a zone of permanently altered refractive index characteristics created therein, illustrating as well the basic principles of the present method.
• Figure 3 is an end view similar to that of Figure 1 but showing the use of a pair of laser beams to create a zone of altered refractive index characteristics in the waveguiding device.
• Figure 4 is a view similar to that of Figure 1 but showing the use of an optical mirror to focus a single laser beam
• Figure 5 is a top plan view of a fiber showing a method of achieving a zone of altered refractive index characteristics which is greater in width or thickness than the width of the laser beam used to create the zone.
• Figure 6 is a top plan view of a waveguiding device or fiber having an angled zone of permanently altered refractive index characteristics therein, illustrating the effect thereof on light transmitted along the core, the device being used as an attenuator.
• Figure 7 is a top plan view of a waveguiding device or fiber having a zone of permanently altered refractive index characteristics therein, perpendicular to the longitudinal axis, illustrating the effect thereof on light transmitted along the core, the device being used as an attenuator.
• Figure 8 is a top plan view of a waveguiding device or fiber having a zone of permanently altered refractive index characteristics therein, perpendicular to the longitudinal axis, illustrating the effect thereof on light transmitted along the core, the device being used as a tap.
• Figure 9 is a top plan view of a waveguiding device or fiber having an angled zone of permanently altered refractive index characteristics therein, illustrating the effect thereof on light transmitted along the core, the device being used as a tap.
• Figure 10 is a top plan view of a waveguiding device or fiber having an angled zone of permanently altered refractive index characteristics therein, illustrating the effect thereof on light transmitted along the core, the device being used as a polarimeter.
• Figure 11A is a top plan view of a polarimeter having four altered zones and a ⁇ /2 wave plate between a pair of altered zones.
• Figure 11B is an end view of the polarimeter of Figure 11A.
• Figure 12A is a top plan view of a polarimeter having two identical altered zones therein.
• Figure 12B is an end view of the polarimeter of Figure 12A.
• Figure 13A is a top view of a fiber with, multiple cores and with altered zones interconnecting various cores of the fiber.
• Figure 13B is an end view of the fiber illustrated in Figure 13A.
• Figure 14A is an end view illustrating the application of mechanical stress to an optical fiber.
• Figure 14B is an end view illustrating the creation of a zone of permanently altered refractive index characteristics during the application of mechanical stress.
• Figure 14C is an end view illustrating an altered stress field within the fiber once the mechanical stress has been removed.
• Figure 15A is an end view illustrating the application of a strong electrical field to an optical fiber.
• Figure 15B is an end view illustrating the creation of a zone of permanently altered refractive index characteristics during the application of an external electrical field to the fiber.
• Figure 15C is an end view illustrating a static polarization field within the fiber once the electrical field has been removed.
• Figure 1 generally illustrates the basic principle of this invention, being the creation of a zone of permanently altered refractive index characteristics in a waveguiding device such as an optical fiber 10.
• the fiber is shown as including a central core 12 and a cladding 14 both of which are generally symmetrical about a longitudinal axis A.
• a laser to be described in greater detail hereinafter, is positioned relative to the waveguiding device so that a collimated beam 16 thereof is directed towards the waveguiding device, generally at 90 degrees to the longitudinal axis A.
• the laser is located above the waveguiding device, although it could just as easily be positioned to one side thereof.
• a lens 18 is positioned in the beam path so that the lens will focus the beam, creating a focal region 20 that will be of a predetermined size relative to the waveguiding device, especially relative to the diameter of the core 12, and that will be located with its center generally aligned laterally in the same plane as the longitudinal axis A.
• the lens can be any optic such as a parabolic mirror, axicon, spherical or cylindrical element that is further used to make a beam focus that produces a desired index profile in the interaction zone.
• the focusing condition represented by this lens can be improved by the use of index matching fluids to remove surface aberrations.
• Means are provided to move or sweep the focal region 20 laterally relative to the waveguiding device (arrow Y) so that the focal region 20 enters the device and is swept thereacross.
• the laser is operated within parameters that cause the focal region 20 to permanently alter the refractive index characteristics of the waveguiding device along the path that it follows as it is swept through the device.
• a permanently altered zone is one that cannot be erased, as for example by heating the fiber to a temperature sufficient to erase conventionally produced anomalies in the fiber but below the melting temperature of the fiber.
• Figure 2 shows in a perspective view the waveguiding device in the form of a glass fiber 10 including a central core 12 and a cladding 14 both of which are symmetrical about the longitudinal axis A.
• a zone 22 of permanently altered refractive index characteristics Extending across at least a portion of the fiber core 12 and/or at least a portion of the cladding 14 is a zone 22 of permanently altered refractive index characteristics, created using a method as described with reference to Figure 1.
• the height of the altered zone 22 is defined by the height of the focal region 20 and its lateral extent within the fiber is determined by the sweeping motion of the focal region along path Y and the intensity of the laser beam.
• the zone 22 is defined by the height of the focal region 20 and its lateral extent within the fiber is determined by the sweeping motion of the focal region along path Y and the intensity of the laser beam.
• Figure 3 illustrates a method of creating a zone of permanently altered refractive index within a waveguiding device 10 using a pair of laser beams 16 and 16'.
• the laser beams are focused by lenses 18, 18' and directed towards the waveguiding device so that the focal region 24 exhibits an intensity which is generally a summation of the individual laser beam intensities.
• This arrangement can be used to create a focal region of increased intensity if a pair of lasers generally the same as the single laser of Figure 1 is used.
• This arrangement also allows for the utilization of individual lasers of reduced intensity, when compared to the single-laser scenario of Figure 1, with the additive intensity at the focal region being generally equal to that of the single-laser scenario. It also provides a method of further localizing the altered zone 22, if desired.
• Figure 4 is a view similar to that of Figure 1, but showing that the laser beam 16 can be directed from an angle other than normal to the longitudinal axis A. In this case the beam is redirected and focused by a mirror 26 so that the desired focal region 20 is created at the desired location relative to the waveguiding device.
• the laser beam 16 can be swept across the fiber 10 in a path that not only crosses the fiber but also moves longitudinally thereof, thereby creating an altered zone 30 which has a width or thickness that is a multiple of the beam width.
• Each sweep adds a thickness or width to the zone equal to a beam width.
• the laser beam focal region 20 starts at the point B, sweeps across the fiber along a path Pj which is at an angle a to the longitudinal axis A to the point C at the other side of the fiber. It then is shifted longitudinally by a distance generally equal to a beam width to point D and then it is swept back across the fiber along the path P 2 , parallel to the path Pi. This sweeping pattern is followed until the zone 30 of altered refractive index characteristics of a desired width or thickness is achieved.
• Figure 6 is a top view of an optical fiber waveguiding device 32 having a zone 34 therein of permanently altered refractive index characteristics, created using one of the procedures previously described.
• Figure 6 illustrates the effect of such a zone on light that is normally being transmitted along the core 36.
• the transmitted light L j encounters the zone 34 a portion L 2 thereof will be scattered into the cladding; another portion L 3 will be guided outwardly along the altered zone 34; and yet another portion 1- 4 will be reflected as Fresnel reflected light.
• the remainder L 5 of the transmitted light x will continue along the core on the other side of the altered zone 34.
• new attenuators, taps and polarimeters are possible based on the principles of the present invention.
• An all-fiber attenuator is an optical waveguide or fiber which attenuates light propagating in the core.
• the attenuation is achieved by letting a portion of the light escape from the core, which is in turn achieved by creating an altered refractive index zone at the escape location.
• the altered zone may be created at an acute angle to the longitudinal axis of the optical waveguide or fiber ( Figure 6) or substantially perpendicularly to the longitudinal axis ( Figure 7).
• the altered zone 34, 35 may include refractive index changes in the core-cladding boundary region, in the evanescent region in the cladding, and/or in the core of the optical waveguide or fiber.
• refractive index changes in the core-cladding boundary region and in the evanescent region in the cladding lead to a coupling between the core and the cladding propagation modes and therefore to part of the light Li propagating in the core escaping into the cladding.
• refractive index changes in the core perturb the light t propagating in the core and part of it is scattered out of the core via two escape mechanisms.
• the first escape mechanism scatters part L 3 of the light out. of the core by coupling it to the waveguide formed by the altered zone 34 which is oriented at an acute angle to the longitudinal axis of the optical waveguide or fiber.
• the second scattering mechanism scatters part U of the light out of the core by way of Fresnel reflection at the surface of the altered zone 34 which is oriented at an acute angle to the longitudinal axis of the optical waveguide or fiber.
• the surface of a suitably oriented altered zone acts therefore as a reflecting surface.
• the achievable attenuation loss is between 0 - 40 dB depending on the length of exposure time for making the altered zone, the light pulse energy, the sweeping speed of the laser beam, the distance the write beam has been swept across the optical fiber, and the angle that the sweeping direction makes with respect to the longitudinal axis of the optical waveguide or fiber.
• losses due to altered refractive index zones can be as high as 40 dB with an accuracy of 0.05 dB.
• the loss can be accurately adjusted using a combination of loss induced with the refractive index changes in the core-cladding boundary region and loss induced with refractive index changes in the evanescent region in the cladding.
• the greater part of the loss can be induced with the refractive index changes in the core-cladding boundary region and fine adjustments to the loss in approximately 0.1 dB increments can be induced with refractive index changes in the evanescent region in the cladding.
• the loss may be induced by sweeping the laser beam substantially parallel to the optical fiber and centered in the evanescent region in the cladding, in the core-cladding boundary region, or in the core.
• typically the magnitude of the loss depends on the sweeping distance up to a loss of less than 1 dB for a single sweep, where the magnitude of the loss saturates for laser beam waist diameters of 10 - 20 micrometers.
• the loss can be adjusted by changing the length of the altered zone along the length of the optical waveguide or fiber.
• the achievable loss can be greater than 30 dB.
• the optical return loss is better than 40 dB, i.e. the intensity of light propagating in the core in the backward direction is more than 40 dB below the intensity of the light propagating in the core in the forward direction.
• All-Fiber Tap is an optical waveguide or fiber which couples a small portion of the light out of the core and out of the optical waveguide or fiber, which light can then be measured with an optical power detector such as a photodiode or a photomultiplier tube. See for example the arrangements shown in Figures 8 and 9.
• an optical tap can form the basis for a power monitor in which the detector is used to collect light from the tap and to send a signal indicative of power level to an appropriate information retrieval device.
• all-fiber taps light is coupled out of the core using similar altered zones as in the above described case of an all-fiber attenuator, although the portion of the light coupled out of the core in the case of an all-fiber tap is typically much smaller with a tap ratio of typically 1%.
• the all-fiber tap therefore allows for the monitoring of the amount of light propagating in the core by monitoring the amount of light coupled out of the optical waveguide or fiber at the expense of diverting only a small amount of light.
• the altered zone 38 is oriented perpendicularly to the longitudinal axis A of the optical waveguide or fiber 10 then the light L 6 coupled out of the core is at a grazing angle to the surface S of the optical waveguide or fiber, and index matching fluid F can be used to avoid total internal reflection at the surface of the optical waveguide or fiber, and to allow the light to escape from the optical waveguide or fiber and be detected by an optical detector 40.
• index matching fluid can be omitted, since the light coupled out of the core may be at a larger angle than the critical angle for total internal reflection, thereby avoiding total internal reflection at the surface of the optical waveguide or fiber.
• optical return loss for all-fiber taps is greater than 40 dB.
• An all-fiber polarimeter is an optical waveguide or fiber capable of measuring the polarization states of the light propagating in its core.
• a number of reflecting surfaces must be oriented substantially at a Brewster angle to the longitudinal axis of the optical waveguide or fiber, such that mainly s-polarized light will be reflected with negligible amount of p-polarized light reflection. Spacing the azimuthal angle of four reflecting surfaces along the length of an optical waveguide or fiber by 45 degrees allows for the measurement of all four Stokes parameters, thereby specifying the complete polarization state of the light propagating in the core.
• a prior art all-fiber polarimeter by Westbrook, Strasser, and Amsterdam uses a blazed fiber Bragg grating for each of the reflective surfaces (IEEE Photonics Technology Letters, Vol. 12, No. 10, pp. 1352 - 1354, October 2000).
• an embodiment of an all-fiber polarimeter implements each of the four reflective surfaces with an altered zone, taking advantage of the reflective properties of the surface of an altered zone.
• the Brewster angle of an altered zone depends on the pulse energy, the pulse width, the pulse repetition rate, the sweep speed, and the size of the waist of the write beam.
• a reflecting surface with a Brewster angle of 45 degrees which conveniently reflects s-polarized light L 7 in a direction perpendicular to the longitudinal axis A of the optical waveguide or fiber will have minimal contamination of p-polarized light.
• a polarimeter is shown with four altered zones 44 if 44 2 , 44 3 and 44 at substantially 90 degrees to each other.
• a ⁇ /2 wave plate 46 may be inserted between a pair of adjacent altered zones, such as the third and fourth altered zones 44 3 , 44 4 , to distinguish between right and left circularly polarized light.
• a UV-induced ⁇ /2 wave plate as in the quoted IEEE reference may be used. With the ⁇ /2 wave plate in the core, circularly polarized light will or will not be reflected by the fourth altered zone, depending on the direction of rotation of the E-vector of the light propagating in the core.
• the polarization axis of the ⁇ /2 wave plate can be oriented either along or at a right angle to the s-polarized direction of the fourth altered zone.
• Another embodiment of an all-fiber polarimeter uses two identical altered zones 48, 48 with the azimuthal angles spaced at substantially 90 degrees, and p-polarized light for the first reflecting surface is therefore s-polarized for the second reflecting surface.
• the light intensity of both polarization states in the fiber core may therefore be measured independently, although the full polarization state cannot be determined with only two reflecting surfaces. A slight deviation from the orthogonal azimuthal angles will balance the polarization dependence of the two zones, thereby reducing polarization-dependent losses.
• Both embodiments are shown with suitable detectors 50 for detecting the light directed outwardly by the associated altered zones.
• the return loss for all-fiber polarimeters is greater than 40 dB. It should be noted that certain losses in an attenuator and that polarization dependent tapping in a tap can be compensated for by including at least two altered refractive index zones within the attenuator or tap, with the zones being oriented relative to each other to achieve the desired degree of compensation. Such zones could be created by sweeping the beam through the workpiece from, for example, left to right, and then again (at the same relative angle) from top to bottom, possibly at the same location.
• a suitable type of ultrafast pulsed laser for producing a beam according to this invention is a laser emitting pulses each with a duration of less than 1 picosecond, preferably between 2 and 200 femtoseconds, and more preferably about 100 femtoseconds, and a pulse energy between 1 nanojoule and 1 millijoule.
• the laser can be operated using single pulses or with a variable pulse repetition rate between 500 Hz and 1 GHz, preferably between 1 kHz and 100 MHz.
• the laser repetition rate is selected to be higher than the thermal diffusion time out of the modified volume element to allow heat to accumulate between laser shots to soften the glass, ideally up to the liquefying point or glass temperature of the material, to enable the material to deform to the photoinduced changes in charge distribution and temperature profile.
• This accumulated heating effect both enables material flow to create the index of refraction changes and self anneals out stress within the written zone.
• the typical thermal diffusion time is on the order of 10 microseconds.
• the ideal laser repetition rate is greater than 100 KHz to provide pulses at time intervals shorter than 10 microseconds.
• the higher the repetition rate the better; however, practical limitations in laser average power, limit this prospect as the size of the volume element being created in the material increases. Larger volume elements require higher pulse energy and thereby are limited to lower repetition rates for any given average power laser system.
• the conditions for approaching liquefication of the glass scale as the square of the beam diameter.
• a second laser such as a C0 2 laser, can be used to heat the zone for increasing the compliance of the material to the writing laser.
• the wavelength of the light must be greater than that of the absorption region of the glass material in which a refractive index change is to be made. In the case of standard fused silica glass, which is commonly used in the manufacture of optical waveguides and fibers, the wavelength of the light must therefore be greater than 200 nanometers.
• the laser for this application is typically based on a TkSapphire, Chromium doped, or Erbium doped solid state mode-locked laser oscillator.
• the light pulses from the laser oscillator may also be amplified through an amplifier stage based on one or more of similar solid state laser media with broadband gain.
• the output from either the laser oscillator or the amplifier may also be used to pump an optical parametric amplifier to generate the light pulses used to expose the glass materials.
• a preferred laser system for this invention is therefore one in which the output of a frequency-doubled Erbium doped fiber laser is amplified in a laser regerative amplifier that is based on a TkSapphire gain material, providing light pulses of approximately 100 femtosecond duration each with an energy of between 1 nanojoule and 1 millijoule at a pulse repetition rate of between 1 kHz and 100 MHz.
• the laser light source beam diameter should be in the range of >0.1 to about 10mm; the focal length should be in the range of about 1mm to about 30cm; and the numerical aperture of any lens or mirror utilized therewith should be in the range of about 0.05 to about 1.3.
• the laser light can be focused with a lens or a mirror, thereby creating very high intensity light in the focal region.
• the focal region can be used as a write beam.
• the microstructure of the glass will be restructured to create a defined zone having permanently altered refractive index characteristics.
• the altered zone can be created by pin-point focusing, or line focusing, of the beam at a target region in the workpiece or by sweeping the write beam over the target region.
• the altered zone can be created in a variety of optical waveguides and fibers, including any glass substrate with an embedded optical waveguide, conventional optical fibers, polarization maintaining fibers, optical fibers with Germanium enriched core, optical fibers with rare-earth dopants either in the core or in the cladding region, hydrogen loaded optical fibers, optical waveguides and fibers having more than one core, such as the waist region of a taper coupler, optical waveguides and fibers having more than one cladding, such as W-fibers, holey fibers (photonic crystal fibers), fiber Bragg gratings, photonic bandgap materials, glasses doped to provide multiphoton resonance for improving laser writing performance by decreasing laser thresholds for material modification, and other optical waveguides and fibers with complicated refractive index profiles.
• any glass substrate with an embedded optical waveguide conventional optical fibers, polarization maintaining fibers, optical fibers with Germanium enriched core, optical fibers with rare-earth dopants either in the core or in the cladding region, hydrogen loaded
• One method for accurately creating altered zones in optical waveguides or fibers having a core has the optical waveguide or fiber mounted on a high precision stage with better than 1 micron positioning accuracy.
• the focal region of the laser beam is aligned with the core using the following alignment procedure.
• the peak pulse intensity of the laser source is first set at low power to avoid making permanent refractive index changes to the glass during the alignment procedure.
• the laser beam is oriented at a desired angle relative to the longitudinal axis of the core, depending on the desired shape of the altered zone to be created.
• the focal region is scanned over the optical waveguide or fiber, and a photomultiplier tube is used to detect the amount of multiphoton fluorescence from the core.
• the location of the focal region is optimally aligned to the location of the core when the detected amount of multiphoton fluorescence is at a maximum.
• the focal region is then moved, after the peak pulse intensity has been increased to at least the threshold for inducing permanent refractive index changes, to create altered zones in the optical waveguide or fiber.
• the laser beam can be directed towards the workpiece "from above”, “from below”, or “from the side” referring to a setup wherein the focal region of the laser source is initially positioned above, below, or to one side of the optical waveguide or fiber mounted in the precision stage.
• the focal region is initially positioned above the optical waveguide or fiber, and moved downwards.
• the alignment procedure is similar to the above, only the maximum fluorescence is now indicative of the focal regions being aligned relative to each other and to the core. The focal regions are then either moved in unison for creating the altered zone, or the workpiece is moved with respect to the focal regions.
• beneficial material modification techniques that fall within the scope of this invention can be used for femtosecond-pulse-assisted microstructuring of an optical waveguide.
• these special techniques involve the addition of externally applied stimuli to the femtosecond-pulse microstructuring methods described already in this specification. Combining additional stimuli together with femtosecond pulse exposure increases the functionality of femtosecond-pulse-modified optical-waveguide technology, as described below.
• the purpose of applying external stimuli to the optical waveguide during femtosecond-pulse microstructuring of an optical waveguide is, in a first instance, to create permanent regions of stress and/or stress birefringence in and around the femtosecond pulse modified region of the optical waveguide.
• the purpose is to build in a permanent electric field in and around the modified region of the optical waveguide.
• the femtosecond pulse focal spot can be characterized by a radius, a rad .
• the waveguide material has a thermal diffusivity constant, K.
• the energy of the femtosecond pulse is uniformly deposited within the spherical volume of material bounded by the radius, a rad .
• the characteristic time constant for diffusion of the thermal energy deposited by the pulse is, approximately, 0.1 a rad 2 / K.
• the thermal diffusivity coefficient K is 0.0082 cm 2 /sec. Therefore the characteristic time constant for diffusion of the thermal energy (for a 10 ⁇ m focal spot) in fused silica is approximately 1.2 x 10 "5 sec.
• Heat dissipation from the focal spot by blackbody radiation for temperatures below 1500°C can be neglected. Therefore, the focal spot in the material loses energy mainly by heat diffusion; of course, processes associated with a rearrangement of the material lattice within the focal spot retain some of the pulse energy.
• the lattice modification energy leads to refractive index modification, as already discussed.
• the pulse train has a pulse repetition period shorter than about 1.2 x 10 "5 sec (for this example)
• the condition is reached where the thermal energy in the focal volume is accumulated at a faster rate than it is dissipated, thereby leading to an increase in the temperature of the focal region.
• the energy per femtosecond pulse, the femtosecond pulse repetition rate and the radius of the focal spot together control the temperature of the material in and around the focal spot.
• Femtosecond processing conditions energy per femtosecond pulse, the femtosecond pulse repetition rate and the radius of the focal spot
• the material temperature in and around the focal spot is controlled to a value in the vicinity of, or above, the softening temperature of the waveguide glass. It will be realized that the waveguide region processed by femtosecond radiation does not support stress while the temperature of the region remains above the softening point of the glass.
• This apply-stress-while-writing method can be used to subject the core of an optical fiber to directional stress by tensioning/compressing the fiber while writing longitudinal stress members adjacent and parallel to the core of the fiber with a femtosecond pulse train. It can also be used to render birefringent waveguides written with a femtosecond pulse train by applying a transverse stress to the waveguide region during the writing process.
• Figures 14A, B and C illustrate diagrammatically the application of stress with this invention.
• Figure 14A shows an optical fiber (waveguide) 80 having a core 82 and cladding 84 within a clamping apparatus 86 that is capable of applying mechanical stress to the fiber. The result is a generally symmetrical stress field within the fiber, identified by stress lines 88.
• a write beam 90 having a focal region 92 is applied to the waveguide as in Figure 14B there will be localized heating in the target region as discussed hereinabove. This has the effect of relaxing the mechanical stress and redistributing the stress field in the vicinity of the focal region, as seen at 94.
• Figure 15A shows an optical fiber 100 having a core 102 and a cladding 104 positioned such that a strong electrical field, identified by 106, is applied thereto from top to bottom. This induces an electric polarization throughout the region of fiber over which the electric field is applied.
• This constant electric field up to a magnitude comparable to the electrical breakdown field of the waveguide material, is applied during the femtosecond pulse modification process as seen in Figure 15B.
• the write beam 108 has a focal region 110 which alters the electric field as at 112. Poling of the material when it is at a temperature in the vicinity of, or above, the softening temperature of the waveguide glass is facilitated by the high temperature.
• memory of the applied electric field is retained in the structure of the femtosecond pulse modified region of the material.
• Built-in or polled fields are used (in combination with periodic structures that phase match the process) for facilitating efficient nonlinear processes, such as second-harmonic generation.
• Figs. 13A and 13B Based on the above-described methods to couple light into and out of a fiber core to an altered zone, it is possible to create more complex devices in multiple core fiber as shown in Figs. 13A and 13B.
• light coupled into or out of one or more of the cores may be channelled between the cores by altered region interconnects based on mechanisms described herein.
• Different cores may have different cladding structures (including multiple cladding structures and photonic bandgap structures), sizes, doping, and may alter light in different ways, including but not limited to phase shifts, dispersion, amplification, attenuation, and frequency conversion.
• Devices based on this method may include but are not limited to Mach- Zehnder interferometers, interleavers, add-drop filters, and arrayed waveguide gratings.
• Another benefit of the present invention is found in the ability of improving the coupling between optical fibers or waveguides that have been altered in accordance with the present invention.
• the refractive index characteristics of the fiber or waveguide can be modified or altered at or near the interface point so as to match the characteristics of the fiber, waveguide or optical source to which it is to be coupled.
• this invention it is possible to substantially enlarge or reshape the waveguide's mode field pattern so as to reduce the divergence of the light exiting the waveguide.

Landscapes

• Physics & Mathematics (AREA)
• Optics & Photonics (AREA)
• Chemical & Material Sciences (AREA)
• General Physics & Mathematics (AREA)
• Life Sciences & Earth Sciences (AREA)
• Engineering & Computer Science (AREA)
• Organic Chemistry (AREA)
• Chemical Kinetics & Catalysis (AREA)
• General Chemical & Material Sciences (AREA)
• Geochemistry & Mineralogy (AREA)
• Materials Engineering (AREA)
• General Life Sciences & Earth Sciences (AREA)
• Health & Medical Sciences (AREA)
• Toxicology (AREA)
• Manufacturing & Machinery (AREA)
• Electromagnetism (AREA)
• Lasers (AREA)
• Optical Integrated Circuits (AREA)
• Optical Fibers, Optical Fiber Cores, And Optical Fiber Bundles (AREA)

Priority Applications (4)

Applications Claiming Priority (2)

Publications (2)

Family

ID=31193621

Family Applications (1)

Country Status (7)

Cited By (10)

Families Citing this family (70)

Family Cites Families (49)

• 2002
  • 2002-08-02 CA CA002396831A patent/CA2396831A1/en not_active Abandoned
• 2003
  • 2003-07-31 CN CNB038184583A patent/CN100419476C/zh not_active Expired - Lifetime
  • 2003-07-31 EP EP03766088.3A patent/EP1527363B1/en not_active Expired - Lifetime
  • 2003-07-31 WO PCT/CA2003/001158 patent/WO2004013668A2/en not_active Ceased
  • 2003-07-31 AU AU2003254667A patent/AU2003254667A1/en not_active Abandoned
  • 2003-07-31 JP JP2004525094A patent/JP2005538392A/ja active Pending
  • 2003-08-01 US US10/632,111 patent/US7095931B2/en not_active Expired - Lifetime
• 2006
  • 2006-08-08 US US11/500,299 patent/US7295731B2/en not_active Expired - Lifetime
• 2007
  • 2007-11-13 US US11/939,016 patent/US8107782B2/en not_active Expired - Lifetime
• 2009
  • 2009-11-30 US US12/627,026 patent/US8090233B2/en not_active Expired - Lifetime
• 2010
  • 2010-02-12 AU AU2010200548A patent/AU2010200548A1/en not_active Abandoned

Also Published As

Similar Documents

Legal Events