WO2004011241A1 - 発泡断熱シートと発泡断熱容器、およびその製法 - Google Patents

発泡断熱シートと発泡断熱容器、およびその製法 Download PDF

Info

Publication number
WO2004011241A1
WO2004011241A1 PCT/JP2002/012922 JP0212922W WO2004011241A1 WO 2004011241 A1 WO2004011241 A1 WO 2004011241A1 JP 0212922 W JP0212922 W JP 0212922W WO 2004011241 A1 WO2004011241 A1 WO 2004011241A1
Authority
WO
WIPO (PCT)
Prior art keywords
foamed
foam
base paper
cells
heat insulating
Prior art date
Application number
PCT/JP2002/012922
Other languages
English (en)
French (fr)
Inventor
Osamu Chujo
Akio Morita
Original Assignee
Tokan Kogyo Co., Ltd.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from JP2002222083A external-priority patent/JP3722435B2/ja
Priority claimed from JP2002222082A external-priority patent/JP3722434B2/ja
Application filed by Tokan Kogyo Co., Ltd. filed Critical Tokan Kogyo Co., Ltd.
Priority to EP02788774A priority Critical patent/EP1547762A4/en
Priority to CNB028293967A priority patent/CN1291833C/zh
Priority to KR1020057001616A priority patent/KR100654523B1/ko
Priority to US10/523,569 priority patent/US20060165970A1/en
Publication of WO2004011241A1 publication Critical patent/WO2004011241A1/ja
Priority to US12/277,482 priority patent/US8636930B2/en

Description

明細書 発泡断熱シートと発泡断熱容器、 およびその製法 技術分野
この発明は、 主に原紙の水分を用いて発泡させた発泡セル群をバ キュームで真空吸引してなる発泡断熱シートと発泡断熱容器、 およ ぴその製法に関する。 背景技術
原紙を基材とした断熱力ップにおいて、 基材に積層したラミネー トフィルムを発泡させて触感の良さと断熱性を兼ね備えさせる構造 が種々提案されている。
例えば、 特開昭 5 7— 1 1 0 4 3 9号では、 紙の中に含まれてい る水分が加熱により気化し、 この気化した水分を発泡材と して用い て、 ポリエチレンフィルム等のような熱可塑性合成樹脂を発泡させ る構造が開示されている。
しかし、 この方法では、 発泡高さが限られてしまい、 加熱時間を 長く しても発泡高さを高くできない欠点があった。
—方、 特開昭 6 1 — 2 4 6 0 4 1号では、 発泡シートと多数の通 気用小孔を貫通形成した板紙とを、 多数の部分的接着剤で一体接合 した複合シートを形成し、 この発泡シートを加熱し軟化した後に部 分的接着部以外の位置で発泡シート側から真空吸引することによつ て発泡シートを成型金型に沿って膨出成形して、 発泡シートに膨出 凸部を形成している。
この場合は、 軟化した発泡シートを部分的接着部以外で吸引して 膨出させる構成となっており、 手間がかかると共に、 膨出部分が大 きく張り出して形成されるので、 力ップなどには適さず感触のよい 発泡面を形成することは困難であった。
また、 本出願人は、 別の方法として特開 2 0 0 0— 1 7 7 0 3 9 で、 板紙にシリ コンオイル等の接合阻止剤をスポッ ト状に塗布し、 その上にラミネートフィルムを接合し、 前記ラミネートフィルムの 接合された面を加熱した後、 ラミネ一トフイルムの接合阻止剤が塗 布された部分を真空吸引により膨出させた発泡構造を提案し、 相応 の成果を挙げている。
この構造では、 接合阻止剤が板紙にスポッ ト状に塗布されている ので、 加熱で可塑化したラミネ一トフイルムを上記塗布部分で真空 吸引により引き延ばして膨出させ発泡部としているので、 発泡部は 散点状に配置され隙間無く連続させた発泡面を形成することはでき ない。
本発明者らは、 上記事情に鑑みて研究の結果、 原紙の水分を発泡 剤として合成樹脂フィルムを発泡させて、 発泡セルが隙間無く連続 する発泡面を形成すると共に、 この発泡面を真空吸引して発泡高さ を可及的に高くする構成について開発を行った。
即ち、 前述の特開昭 5 7— 1 1 0 4 3 9号の水分発泡のように、 原紙の中に含まれている水分を加熱により気化し、 この気化した水 分を発泡材としてポリエチレンフィルム等のような熱可塑性合成樹 脂を発泡させる。
この発泡面を形成する合成樹脂フィルムは、 ポリエチレンが好ま しいが、 ポリ プロ ピレン、 ポリ塩化ビエル、 ポリ スチレン、 ポリエ ステル、 ナイロンなどのような熱可塑性のフィルムが用いられる。 原紙は、 1 0 0 8ノ111 2〜4 0 0 g Z m 2位の坪量のものが用いら れ、 約 2〜 1 0 %、 好ましくは 4 . 5〜 8 %程度の含水率を有する ものが使用される。
発泡のための加熱温度は、 一般には、 約 1 1 0 °C〜約 2 0 0 °Cの 範囲内であるが、 使用する原紙および熱可塑性樹脂フィルムの種類 により適宜決定される。
実験によると、 低密度ポリエチレンの場合、 加熱温度を 1 3 5 °C とし、 加熱時間を 9 0秒とした場合は 8倍の発泡倍率を得たが、 加 熱時間を 5分とすれば、 発泡高さを 1 5倍程度に大きくできること が確認された。
ここで加熱温度を上げると、 原紙中の含水分は減少するが、 発泡 倍率は低下した。
これは榭脂温度が融点を大きく超えて発泡セルが破れることと、 樹脂の強度が低下して、 冷却時に発泡セルが収縮しているものと推 測される。
このように原紙中の水分を利用した発泡の場合、 一時的に発泡倍 率を大きくできるが、 冷却時に発泡セルが収縮してしまい、 発泡高 さを維持することができないという致命的な欠点があった。
これに関して、 冷却時における発泡セルの収縮を防止するため、 急冷することにより発泡セルの強度を大きくする方法が考えられる c そこで、 水冷、 および一 5 °Cの急冷を行ったが、 発泡高さを高く 維持することはできなかった。
次に、 発泡面を負圧にして発泡セルの収縮を抑えると共に真空吸 引して発泡セルを高くする方法を試みた結果、 発泡面の高さを維持 することができることが判明し、 本発明を完成するに至った。
即ち、 この発明の主たる課題は、 主に原紙に含有する水分を利用 して合成樹脂フィルムを発泡させて連続する発泡セル群からなる発 泡面を形成すると共に、 この発泡面を真空吸引して発泡高さを高く することができるようにした発泡断熱シートおよびこれを用いた発 泡断熱容器、 その製法を提供することにある。 発明の開示
この発明の発泡断熱シートでは、 原紙に合成樹脂フィルムを積層 したシートを加熱し、 主に原紙に含有する水分を用いて合成樹脂フ イルムを発泡させて発泡セル群からなる発泡面を形成し、 該発泡面 の少なく とも一部を真空吸引して発泡セルの発泡倍率を高めている ので、 原紙に含まれた水分を用いて合成樹脂フィルムを発泡させる と共に、 発泡セルを真空吸引することにより、 高倍率に発泡した発 泡セルの収縮を妨げて高い発泡倍率を維持することができる。
また、 前記発泡面の少なく とも一部を真空吸引して、 発泡セル群 の一部の発泡セルを原紙から浮き上がらせると共に、 隣接する発泡 セル同士が一体にくつっき合って見かけの発泡高さを均一にしても よい。 前記発泡面は、 シー トの全部または一部に形成される。
これにより、 高倍率に発泡した発泡セルの収縮を妨げて高い発泡 倍率を維持することができる。
また、 加熱と真空吸引により発泡面を形成するので、 加熱温度を 下げたり、 加熱時間を短縮することができ、 更に真空吸引によりィ ンキゃ溶剤の臭い、 樹脂臭ゃラミ臭などの臭いの脱臭を同時に行う ことができる。
この発明の発泡断熱シートを用いた発泡断熱容器では、 前記発泡 断熱シートが、 少なく とも容器の胴部に用いられるので、 高い発泡 高さにより断熱性を高め、 また触感を良くすることができる。
前記発泡面を少なく とも胴部に有する発泡断熱容器の場合、 原紙 の少なく とも一方の面に合成樹脂フィルムを積層すると共に、 他方 の面もラミネートした上記胴部ないし容器を加熱し、 主に原紙に含 有する水分を用いて前記合成樹脂フィルムを発泡させて発泡セル群 からなる発泡面を形成し、 該発泡面の少なく とも一部を真空吸引し て、 発泡セルの発泡高さを高めてもよい。
また、 前記発泡面は、 胴部の一部または容器の一部に形成されて いるものでもよい。
更に、 前記真空吸引を行う際に、 発泡面に均等な吸引力が作用す るように、 発泡面が形成されたシートを金型内の所定位置で動いた り変形したり しないように拘束する拘束手段を設ければ、 より均質 な高い発泡高さを得ることができる。
次に、 この発明の発泡断熱シー トの製法では、 原紙に合成樹脂フ ィルムを積層したシートを加熱し、 主に原紙に含有する水分を用い て合成樹脂フィルムを発泡させて連続する発泡セル群からなる発泡 面を形成する工程と、 該発泡面の少なく とも一部を真空吸引して、 発泡セルの発泡高さを高める工程とからなつている。
また、 前記発泡面を少なく とも胴部に有する発泡断熱容器の製法 では、 原紙の両面がラミネートされており、 加熱により主に原紙に 含有する水分を用いて合成樹脂フィルムを発泡させて発泡セル群か らなる発泡面を形成する工程と、 該発泡面の少なく とも一部を真空 吸引して、 発泡セルの発泡高さを高める工程とからなつている。 そして、 前記真空吸引を行う際には、 発泡面に均等な吸引力が作 用するように、 発泡面が形成されたシートを金型内の所定位置で動 いたり変形したり しないように拘束する工程を設けることが好まし い。 図面の簡単な説明
第 1図は、 第 1実施例の発泡断熱シー トを模式的に示す部分断面 図である。 第 2図は、 第 2実施例の発泡断熱シートを模式的に示す 部分断面図である。 第 3図 （ a ) は、 内周面にシート固定用の縦リ ブを有する真空吸引用の金型の平面図、 （b ) は断面図である。 第 4図は、 内周面にシート固定用のリング状の横リブを有する真空吸 引用の金型の断面図である。 第 5図は内周面に拘束手段を有しない 真空吸引用の金型であって、 容器の内壁面に取り付けられて容器を 拘束する固定具を有し、 吸引時に内部にセッ トする金型の断面図で ある。 第 6図は発泡セルの先端の変形を説明する模式図である。 以下にこの発明の発泡断熱シートと発泡断熱容器、 およびその製 法の好適実施例について説明する。
発泡断熱シート 1は、 従来の水分発泡で用いられる構成と同様で あり、 第 1図および第 2図に示すように、 基材となる中層に原紙 3 を用い、 発泡面には点線で図示した低密度ポリエチレンなどの合成 樹脂ブイルム 2を積層し、 内層には発泡しにくい合成樹脂フィルム やアルミ箔などのラ ミネートフィルム 4が用いられる。
この発明で、 上記水分発泡は、 原紙に含有される水分が主に用い られるが、 例えば、 前記シート 1にインクが塗布されている場合や. 保水性物質が付加されている場合などは、 これらの水分が共に用い られて水分発泡が行われる場合も含む。
また、 前記シート 1は、 予め上記のように積層されたラミネート シートとして構成されている場合に限らず、 容器状に形成された後 に、 内外層のいずれか一方、 または双方のフィルムが一体に積層さ れて三層構造が完成するものでもよい。 要するに、 前記ラミネートシートを加熱する際に、 原紙 3の両面 がラミネートフィルム等で覆われていればよい。 これは、 加熱時に 原紙の一面が露出していると水分が直接大気に蒸散してしまうから である。
なお、 この発明では、 合成樹脂フィルムの発泡体の 1単位を発泡 セル 2 0 とし、 この発泡セル 2 0が連続して密集している状態を発 泡セル群 2 1 と し、 発泡セル群 2 1が面状に形成されている状態を 発泡面 2 2とする。
本実施例では、 水分発泡により成形された発泡セル 2 0は、 真空 吸引によって更に高さ方向に引き延ばされて完成された発泡セル 2 0 となるが、 この発明では水分発泡により成形された発泡セル 2 0 と、 真空吸引された発泡セル 2 0 とが実質的に高さが変わらない場 合、 即ち、 水分発泡後の収縮を真空吸引で抑えたものであってもよ い。
また、 上記水分発泡のための加熱工程とバキュームによる真空吸 引工程とは、 加熱工程の次に真空吸引工程が行われるもの、 あるい は加熱工程中に真空吸引工程が行われるものに限らず、 この発明で は、 前記加熱工程と真空吸引工程とが同時に行われるもの、 更には、 真空吸引工程のなかで、 加熱工程を行う場合も含むものとする。
次に、 サンプルを用いた実験例を基に説明する。
本実施例では、 サンプルは、 コップ状の断熱紙容器の胴部を構成 するシートと した。
この胴部のシートは、 基材となる中層に坪量 2 5 0 g / m 2の原紙 3を使用し、 発泡面となる外層 2には 5 0 μ mの低密度ポリェチレ ンを積層し、 内層 4に 1 8 mの低発泡の合成樹脂フィルムを使用 した 3層構造からなっている。 加熱方法としては、 恒温加熱装置のスーパーテンプオープン S T P H - 2 0 0 (タバイエスペック（株） 製） を使用し、 風速は L O W と し、 ダンパを全開し、 ギアモータを使用して、 サンプルを試料枠 上に載せて回転させながら均等に加熱し、 外層を発泡させた。
サンプル 1では、 1 3 5 °Cで 9 0秒加熱した。
サンプル 2では、 1 6 5 °Cで 4 5秒加熱した。
サンプル 3では、 1 6 5 °Cで 9 0秒加熱した。
対照品では、 1 3 5 °Cで 9 0秒加熱した。
上記のように発泡させた後に、 バキュームを用いて真空吸引を以 下のように行った。
加熱後、 前記オーブンから取り出してからすぐに、 バケツ ト状の バキューム用金型に入れ、 発泡面に負圧をかける。
本実施例で、 金型は、 発泡面を有するシート、 即ち、 カップ状の 容器の胴部を真空吸引するためのものであり、 力ップ状の容器は、 拘束手段によってその中心線を金型の中心線と同軸上に固定される ようにセッ トされる。
この拘束手段は、 金型内周面から突出して発泡面側と衝合するも の、 あるいは発泡面の裏面側を固定するもの、 あるいはシートの端 部を固定するものなど、 どのような方法が用いられてもよい。
そして、 金型は、 カップ状の容器の発泡面と、 金型の吸引面との 間に発泡セル 2 0を吸引するための隙間が生じるように内周面の大 きさが設定されている。
サンプル 1では、 縦リブ 1 2を拘束手段としてバケツ ト状の金型 1 0 (第 3図参照） の内面に設けている。
縦リブ 1 2は、 胴部の外周方向に沿って等間隔 （一例と して 2 mm ピッチ） に配置されており、 その先端が発泡面に衝合している。 そして、 サンプル 1 の発泡面が形成された容器を上記縦リブ 1 2 で固定し、 真空吸引によって 5 1 kpa の負圧を 1 0秒かけた。
この際に、 縦リブ 1 2は前記容器が金型内で僅かでも動いたり変 形したりすることがないように固定しており、 縦リブ 1 2の押圧で これと衝合する発泡セル群が押し潰されて扁平な面となり、 縦リブ 1 2の当たらない面の発泡セル群が真空吸引される。
サンプル 2では、 発泡面に対して衝合するリング状の横リブ 1 3 (第 4図参照） を拘束手段と してバケツ ト状の金型 1 0の内面に上 下多段に設け、 発泡面が形成された容器を上記横リブ 1 3で固定し. 真空吸引によって 6 7 kpa の負圧を 1 0秒かけた。
この場合も、 横リブ 1 3は前記容器が金型内で動いたり変形した り しないように固定しており、 横リブ 1 3の押圧でこれと衝合する 発泡セル群が押し潰されて扁平な面となり、 横リブ 1 3の当たらな い面の発泡セル群が真空吸引される。
サンプル 3では、 上記リブを設けないバケツ ト状の金型 1 0 (第
5図の下方部分のみ） に入れて、 真空吸引で 6 7 kpa の負圧を 1 0 秒かけた。
この場合、 金型内にリブ等の発泡面が形成されたシートを固定す る拘束手段は設けなかった。
対照品では、 前記真空吸引を行わなかった。
上記のようにして構成された発泡断熱容器を、 マイクロスコープ で断面観察し、 発泡高さを 4個所測定し平均値を求めた。
対照品では、 発泡高さの平均値は 2 8 3 mであった。
サンプル 1では発泡セルの上端の平均値は 9 6 7 // Π1であり、 発 泡倍率が約 2 0倍であった。
ここで、 発泡セル群が原紙に付着した発泡セルからなる第 1実施 例のサンプル 1の断面を第 1図に模式的に示す。 2 0は無数に形成 された発泡セルであって原紙 3に付着しており、 発泡セル 2 0相互 は密着し一体にく つっき合って発泡セル群 2 1ないし発泡面 2 2の 高さを維持している。
また、 第 2実施例のサンプル 1の断面を第 2図に模式的に示す。 第 2実施例は前記第 1実施例と同じ条件で構成されたものであって. 発泡の際に、 発泡セル群の各発泡セルの発泡倍率にパラツキを生じ させた場合である。
この場合、 発泡セルの真空吸引により、 発泡セル群の中の発泡倍 率の低い発泡セル 2 0 ' を原紙 3から浮き上がらせて分離した状態 となり、 発泡倍率の高い発泡セル 2 0は原紙 3に一体に付着した状 態となり、 これら隣接する発泡セル 2 0、 2 0 ' 同士は一体にくつ つき合う。
これにより、 発泡セル群 2 1は、 高倍率で発泡した発泡セル 2 0 の実際の発泡高さと、 これより低い倍率で発泡した発泡セル 2 0， の見かけの発泡高さが全てほぼ同じ高さに維持されるので、 発泡面 2 2の上面が均一に揃い、 凹凸が生じない。 なお、 図中 2 3は、 浮 き上がり部分に生じる空隙部である。
第 1実施例と第 2実施例とは、 発泡セルの一部に原紙 3に付着し ないものがあるか否かの相違であり、 その他は同じであるので、 以 後の説明も、 第 1実施例と第 2実施例の説明と して兼用する。
次ぎに、 上記サンプル 1 と同一条件で、 加熱時間を 7 0秒とした 場合の平均値は 8 7 0 μ m , 9 0秒では 1 0 0 1 mとなった。
サンプル 2では平均値は 8 5 9 μ mであった。
サンプル 3では平均値は 4 0 0 mであった。
また、 加熱後直ちに発泡面をバキュームして発泡セルを吸引する ことにより、 発泡セルは冷却によって収縮することがなく、 また水 分で発泡させるだけの場合に比べて発泡高さを極めて大きくするこ とが確認できた。
また、 発泡面の真空吸引は加熱後に行う場合を例示したが、 加熱 中に行う場合であってもよく、 負圧の大きさや吸引時間は最適値を 実験的に定めることができる。
また、 前述のように、 発泡面を有する容器、 またはシートが吸引 時に金型内で動いたり変形したり して発泡セル群に均等な吸引力を 作用させにくい場合には、 発泡面に均等な吸引力が作用するように 容器、 またはシートを所定位置で固定または拘束して発泡セルの真 空吸引を行うことが好ましい。
この場合、 吸引時において容器 （またはシート） の発泡面に対し て均一な真空吸引力が作用するので、 均質な高い発泡倍率が得られ る。
サンプル 3では、 他のサンプル 1、 2に比べて発泡高さが低かつ たが、 シートが真空吸引によって変形したためであり、 金型内で上 記シートを固定するための手段を設ける必要があることが確認され た。
この場合、 例えば第 5図の上部に示すように、 容器形状に形成さ れたシートを、 容器の内壁面で固定して、 金型 1 0の所定位置にセ ッ トしう るようにした固定具 1 4を用いれば、 他のサンプルと同様 に更に高い発泡倍率を得ることができる。
この容器状に形成されたシートを拘束する手段は、 前記実施例に 限らず、 要するに真空吸引時に発泡面が形成されたシートが金型内 で動いたり変形したり しないように金型中央の定位置に固定するも のであればよく、 金型と一体に形成されているものでも、 あるいは 別体に形成されているものでもよく、 また接触式でも非接触式でも よい。
更に、 容器を外壁面側から定位置に固定したが、 内壁側から定位 置に固定する手段でもよい。
また、 前記実施例の縦リブや横リブなどのように、 発泡面の一部 に押し付けられる衝合面を有する拘束手段を用いる場合は、 発泡面 で衝合面に対応した個所が押し潰されて凹部となり、 真空吸引され る個所が相対的に隆起して凸部となるため、 この発泡面に凹凸模様 を施すことができる。
そこで、 模様を星形や幾何図形、 その他の所望の形状とする場合 に、 拘束手段の衝合面の形状を直接に模様の形状と して模様を凹部 で表現し、 あるいは、 模様が浮き上がって凸部で表現されるように 衝合面の形状を模様の輪郭に沿って窪ませてもよく、 またこれらを 組合せて表現することもできる。
これにより、 真空吸引時に容器やシートを拘束すると同時に、 上 記拘束手段の衝合面の形状を転写したような凹凸模様を発泡面に形 成することが可能となる。
この模様は、 発泡面の一部に形成されるもの、 あるいは散点状に 形成されるものや、 エンボス状に形成されるもの、 または連続模様 のよ うに形成されるものなど、 衝合面の形状をデザインすることに より種々の模様を表現することができる。
次に、 このよ うに成形された発泡セルは、 真空吸引によってその 形状が維持されるが、 発泡セル内の空気が冷却により収縮し、 第 6 図に示すように、 その先端の緊張が解けて緩やかに橈む。
これにより、 完成された各発泡セル 2 0の先端 2 0 '' が柔らかく なるので、 手指で触った感触が優れる。 そして、 この製法によれば、 加熱時間と、 負圧の調整による発泡 高さのデータを実験的に得ることにより、 発泡面を所望の発泡高さ に調整することが可能である。
また、 発泡面を形成する合成樹脂製フィルムに印刷ィンキを予め 塗布しておく ことで、 発泡面を均一高さとせずに高さ調整を行うこ ともできる。
また、 原紙の水分を用いた発泡に比べて、 加熱時間の短縮が図れ れると共に、 加熱温度を下げることができ、 省力化やコス トダウン が図れる。
そして、 発泡倍率を高くすることができるので、 断熱性の向上が 図れる。
また、 真空吸引を行うので、 インキや溶剤などの成型時に生じる 各種臭いを同時に吸引し脱臭することができる。
上記実施例では、 発泡断熱シートをカップ状の容器とした場合を 例示したが、 容器以外のものであってもよい。
発泡面を形成する面は、 原紙の内外面のいずれの側でもよい。
また、 発泡、 吸引は、 予め所定形状に成型してから行うものでも. シートに行った後に、 このシートを所望形状に組み立てるものでも よい。
更に、 発泡面は、 シートや胴部の一部に形成され、 または容器に 部分的に形成されるようにしたものでもよい。

Claims

請求の範囲
1 . 原紙に合成樹脂フィルムを積層したシー トを加熱し、 主に原紙 に含有する水分を用いて合成樹脂フィルムを発泡させて発泡セル群 からなる発泡面を形成し、 該発泡面の少なく とも一部を真空吸引し て発泡セルの発泡高さを高めたことを特徴とする発泡断熱シート。
2 . 発泡セル群が原紙に付着した発泡セルからなっていることを特 徴とする請求項 1に記載の発泡断熱シート。
3 . 発泡セル群が、 原紙に付着した発泡セルと、 原紙から離れて浮 き上がった発泡セルとからなつており、 瞵接する発泡セル同士が一 体にくつっき合って見かけの発泡高さを均一にしたことを特徴とす る請求項 1に記載の発泡断熱シート。
4 . 前記発泡面が、 シートの一部に形成されていることを特徴とす る請求項 1に記載の発泡断熱シート。
5 . 真空吸引を行う際に、 発泡面に均等な吸引力が作用するように. 発泡面が形成されたシートを金型内の所定位置で動いたり変形した り しないように拘束する拘束手段を設けてなることを特徴とする請 求項 1に記載の発泡断熱シート。
6 . 請求項 1から 5のいずれかに記載の発泡断熱シートを、 少なく とも容器の胴部に用いてなることを特徴とする発泡断熱容器。
7 . 発泡面を少なく とも胴部に有する発泡断熱容器であって、 原紙の少なく とも一方の面に合成樹脂フィルムを積層すると共に、 他方の面もラミネートした上記胴部ないし容器を加熱し、 主に原紙 に含有する水分を用いて前記合成樹脂フィルムを発泡させて発泡セ ル群からなる発泡面を形成し、 該発泡面の少なく とも一部を真空吸 引して、 発泡セルの発泡高さを高めたことを特徴とする発泡断熱容
8 . 発泡セル群が原紙に付着した発泡セルからなっていることを特 徴とする請求項 7に記載の発泡断熱シート。
9 . 発泡セル群が、 原紙に付着した発泡セルと、 原紙から離れて浮 き上がった発泡セルとからなつており、 隣接する発泡セル同士が一 体にく つっき合って見かけの発泡高さを均一にしたことを特徴とす る請求項 7に記載の発泡断熱シート。
1 0 . 前記発泡面が、 胴部の一部または容器の一部に形成されてい ることを特徴とする請求項 7に記載の発泡断熱容器。
1 1 . 真空吸引を行う際に、 発泡面に均等な吸引力が作用するよう に、 発泡面が形成されたシートを金型内の所定位置で動いたり変形 したり しないよ うに拘束する拘束手段を設けてなることを特徴とす る請求項 7に記載の発泡断熱容器。
1 2 . 原紙に合成樹脂フィルムを積層したシー トを加熱し、 主に原 紙に含有する水分を用いて合成樹脂フィルムを発泡させて連続する 発泡セル群からなる発泡面を形成する工程と、
該発泡面の少なく とも一部を真空吸引して、 発泡セルの発泡高さ を高める工程とからなることを特徴とした発泡断熱シー トの製法。
1 3 . 発泡セル群が原紙に付着した発泡セルからなっていることを 特徴とする請求項 1 2に記載の発泡断熱シートの製法。
1 4 . 発泡セル群が、 原紙に付着した発泡セルと、 原紙から離れて 浮き上がった発泡セルとからなつており、 隣接する発泡セル同士が 一体にく つっき合って見かけの発泡高さを均一にしたことを特徴と する請求項 1 2に記載の発泡断熱シートの製法。
1 5 . 真空吸引を行う際に、 発泡面に均等な吸引力が作用するよう に、 発泡面が形成されたシートを金型内の所定位置で動いたり変形 したり しないよ うに拘束する工程を設けてなることを特徴とする請 求項 1 3に記載の発泡断熱シートの製法。
1 6 . 発泡面を少なく とも胴部に有する発泡断熱容器の製法であつ て、
原紙の両面がラミネートされており、 加熱により主に原紙に含有 する水分を用いて合成樹脂フィルムを発泡させて発泡セル群からな る発泡面を形成する工程と、
該発泡面の少なく とも一部を真空吸引して、 発泡セルの発泡高さ を高める工程とからなることを特徴とする発泡断熱容器の製法。
1 7 . 発泡セル群が原紙に付着した発泡セルからなっていることを 特徴とする請求項 1 6に記載の発泡断熱シートの製法。
1 8 . 発泡セル群が、 原紙に付着した発泡セルと、 原紙から離れて 浮き上がった発泡セルとからなつており、 隣接する発泡セル同士が 一体にくつっき合って見かけの発泡高さを均一にしたことを特徴と する請求項 1 6に記載の発泡断熱シートの製法。
1 9 . 真空吸引を行う際に、 発泡面に均等な吸引力が作用するよう に、 発泡面が形成されたシートを金型内の所定位置で動いたり変形 したり しないように拘束する工程を設けてなることを特徴とする請 求項 1 6に記載の発泡断熱容器の製法。
PCT/JP2002/012922 2002-07-30 2002-12-10 発泡断熱シートと発泡断熱容器、およびその製法 WO2004011241A1 (ja)