WO2003033578A1 - Composition de matiere de revetement - Google Patents

Composition de matiere de revetement Download PDF

Info

Publication number
WO2003033578A1
WO2003033578A1 PCT/JP2002/010467 JP0210467W WO03033578A1 WO 2003033578 A1 WO2003033578 A1 WO 2003033578A1 JP 0210467 W JP0210467 W JP 0210467W WO 03033578 A1 WO03033578 A1 WO 03033578A1
Authority
WO
WIPO (PCT)
Prior art keywords
urethane
coating
furniture
resin
emulsion
Prior art date
Application number
PCT/JP2002/010467
Other languages
English (en)
French (fr)
Inventor
Noboru Kiriya
Kenji Yamashita
Kaoru Kato
Hideaki Tojo
Original Assignee
Rinrei Wax Co., Ltd.
Honda Giken Kogyo Kabushiki Kaisha
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Rinrei Wax Co., Ltd., Honda Giken Kogyo Kabushiki Kaisha filed Critical Rinrei Wax Co., Ltd.
Priority to EP02801514A priority Critical patent/EP1435370A4/en
Priority to US10/491,534 priority patent/US20040249052A1/en
Priority to JP2003536312A priority patent/JP3895727B2/ja
Publication of WO2003033578A1 publication Critical patent/WO2003033578A1/ja

Description

明 細 書 コーティ ング剤組成物 技術分野
本発明は、 例えば自動車等の移動体や家具調度等といった物体の 内外装に使用される有機系部材に塗布し、 劣化した表面を初期の状 態に近い状態に復元し、 表面を保護し美観を維持するコーティ ング 剤組成物に関する。 背景技術
例えば、 自動車のルーフやサイ ド、 ドア回りのモール、 タイヤや 室内のダッシュボードのような内外装の他に自動二輪車、 低圧タイ ャを装着したパギ一車両、 自転車、 パワーショベル等の建機、 耕運 機等の農業機械、 鉄道車両、 モノレール、 ロープウエイ、 遊園地等 の遊具、 力ヌ一、 ヨッ ト、 船舶、 潜水艦、 ロケヅ ト、 飛行機、 ヘリ コブ夕、 飛行船、 気球、 ハングライダー、 グライダー、 エレべ一 夕、 エスカレ一夕等の移動体の内外装に、 また、 箪笥、 テーブル、 暖炉等室内に配置されて日常生活で用いられる家具や手回りの道具 類等の調度の内外装に有機系部材が多く使用されている。
これら移動体や家具調度等の物体の内外装に使用される有機系部 材の素材樹脂と して、 一般に、 P V C (ポリ塩化ビエル） 、 P P (ポリプロピレン） 、 E P D M (エチレンプロピレンゴム） 、 P E
(ポリエチレン） 、 P S (ポリスチレン） 、 A B S、 アクリル樹脂 等が使用されている。
これら自動車のモールその他移動体や家具調度等の物体の内外装 に使用される有機系部材は、 経時により、 酸性雨や紫外線等が原因 で白化を起こしたり、 また傷を付けられたり して劣化し、 当初の美 観が損なわれてしまう。 このようなダメージを受けたモール等の有 機系部材の補修については、 研磨を施したり、 またシリコーンオイ ルゃシリコーンレジン等を配合した艷出し剤を塗布したりすること によって行われている。
しかしながら、 ダメージを受けたモール等の有機系部材の研磨に よる補修では、 傷による表面の凹凸については修復できるものの、 酸性雨や紫外線等が原因の表面の白化を改善することはできないと いった問題点がある。
また、 シリコーンオイルを主成分とした艷出し剤では、 油の反射 のような艷となり見苦しく、 また、 液体であるために重ね塗りを繰 り返しても形成される塗膜の厚さに限界があり、 傷による表面の凹 凸を十分に補修することができないという問題点がある。
また、 シリコーンレジンを主成分とした艷出し剤では、 液体であ るシリコーンオイルとは異なり、 固体膜を形成するが、 水不溶性材 料でありコ一夕ピリティ （重ね塗り性） が悪く、 表面の凹凸を十分 に補修することができないという問題点がある。
本発明者らは、 酸性雨や紫外線等が原因で白化を起こしたり、 ま た傷を付けられた り して劣化した有機系部材を、 その白化を改善 し、 傷による表面の凹凸を十分に補修して、 初期の美観に近い状態 に復元できるようにすることについて研究を重ねた結果、 アク リル ェマルジヨンやウレタンディスパ一ジョン等を主原料とした水性の 樹脂コ一ティ ング剤が、 有機系部材の表面の白化を改善するととも に優れたリコー夕ピリティを有することに着目し、 本発明を完成す るに至った。
本発明の目的は、 移動体や家具調度等の物体の内外装に備えられ た有機系部材の表面を初期の美観に近い状態に復元するとともに、 表面を保護し美観を維持する塗膜を形成することができるコ一ティ ング剤組成物を提供することにある。 発明の開示 本発明のコーティ ング剤組成物は、 有効成分と して、 下記
( a ) 、 （b ) 、 （ c ) 、 （ d ) 、 （ e ) を含有する、 物体の内外 装に備えられた有機系部材に用いられるコ一ティ ング剤組成物であ る o
( a ) アクリル系共重合物のェマルジヨン
( b ) 水性ウレタン系樹脂
( c ) ワックスェマルジヨン
( d ) アル力リ可溶性樹脂
( e ) 紫外線吸収剤。
また、 本発明のコーティ ング剤組成物は、 前記 （b ) 水性ウレ夕 ン系樹脂が、 ウレタンディスパージヨンであるコ一ティ ング剤組成 物である。
また、 本発明のコーティ ング剤組成物は、 前記ウレタンディスパ 一ジョンのウレタンが、 脂肪族ポリエステル系ゥレ夕ンであるコー ティ ング剤組成物である。
また、 本発明のコーティ ング剤組成物は前記のコ一ティ ング剤組 成物に、 有機系部材の光沢に合わせるために艷消し剤が加えられて いるコ一ティ ング剤組成物である。
また、 本発明のコ一ティ ング剤組成物は、 前記に記載の物体が、 移動体であることを特徴とする。
また、 本発明のコーティ ング剤組成物は、 前記に記載の物体が、 家具調度であることを特徴とする。
このような移動体や家具調度等の物体の内外装に備えられた有機 系部材に用いられるコーティ ング剤組成物によれば、 酸性雨や紫外 線等が原因で白化を起こしたり、 また傷を付けられたり して劣化し た有機系部材の表面に塗布することにより、 白化を改善し、 また、 重ね塗りにより表面の凹凸を十分に補修し、 有機系部材の表面を初 期の美観に近い状態に復元するとともに、 表面を保護し美観を維持 する塗膜を有機系部材の表面に形成することができる。 前記水性ゥレ夕ン系樹脂が、 ウレタンディスパ一ジョンである と、 破断強度、 耐熱性、 耐溶剤性、 耐光性等に優れた塗膜特性を有 するとともに、 レペリ ングや伸長度に優れるので、 傷隠蔽性ゃ耐傷 付き性に優れ、 有機系部材の表面の保護と美観の維持に一層優れた ものとなる。
前記ゥレタンディスパ一ジョンのウレ夕ンが脂肪族ポリエステル 系ウレタンであると、 特に破断強度に優れた塗膜特性を有するの で、 耐傷付き性により優れたものとなり、 有機系部材の表面の保護 と美観の維持により一層優れたものとなる。
また、 有機系部材の素材の光沢に合わせるために艷消し剤を加え れば、 有機系部材の当初の艷 （艷の程度、 艷無し） に、 より近い状 態に復元することができる。 発明を実施するための最良の形態
以下、 本発明に係る移動体や家具調度等の物体の内外装に備えら れた有機系部材に用いられるコ一ティング剤組成物の実施の形態に ついて説明する。
本発明は、 有効成分と して、 下記 （ a ) 、 ( b ) 、 ( c ) 、 ( d ) 、 ( e ) を含有する、 移動体や家具調度等の物体の内外装に 備えられた有機系部材に用いられるコ一ティ ング剤組成物である。
( a ) アクリル系共重合物のェマルジヨン
( b ) 水性ウレタン系樹脂
( c ) ワックスェマルジヨン
( d ) アル力リ可溶性樹脂
( e ) 紫外線吸収剤。
また、 本発明はこのような移動体や家具調度等の物体の内外装に 備えられた有機系部材の素材の光沢に合わせるため、 艷消し剤を加 えることができる。
前記ァクリル系共重合物のェマルジヨンとしては、 アクリル酸メ チル、 アクリル酸ェチル、 アクリル酸 n —プロピル、 アクリル酸ィ ソプロビル、 アク リル酸 n —ブチル、 アクリル酸イソブチル、 ァク リル酸 2—ェチルへキシル等のァク リル酸エステルの 1種若しくは 2種以上及び又はメ夕ク リル酸メチル、 メ夕クリル酸ェチル、 メタ ク リル酸 n—プロビル、 メタクリル酸イソプロピル、 メ夕クリル酸 n —プチル、 メ夕クリル酸イソプチル、 メタクリル酸 2—ェチルへ キシル、 メ夕ク リル酸ステアリル、 メ夕ク リル酸ラウリル等のメタ ク リル酸エステルの 1種若しくは 2種以上との共重合体、 また、 こ れらとスチレン、 アク リロニ ト リル、 メ夕クリロ二ト リル、 塩化ビ ニル、 塩化ビニリデン、 酢酸ビニル、 メチルビ二ルェ一テル、 n— プロピルビニルエーテル、 イソプロピルビニルエーテル、 n—ブチ ルビ二ルェ一テル、 ィ ソブチルビ二ルェ一テル等のビニルェ一テ ル、 アクリル酸、 メ夕ク リル酸、 ィタコン酸、 シ トラコン酸、 クロ トン酸等のカルボキシル基含有ビニル単量体、 5—ハイ ドロキシェ チルァクリレート、 ?—ハイ ドロキシェチルメタクリ レート、 β— ハイ ドロキシプロビルァクリ レート、 ?—ハイ ドロキシプロビルメ タク リ レー ト、 ァリルアルコール、 Ν —メチロールアク リルアミ ド、 Ν—メチ口一ルメタク リルアミ ド等の水酸基含有ビニル単量 体、 グリシジルァクリ レート、 グリシジルメ夕ク リ レート、 グリシ ジルァリルエーテル等のエポキシ基含有ビニル単量体等の上記ァク リル酸エステル及び又はメタクリル酸エステルと共重合可能なビニ ル単量体の 1種若しくは 2種以上との共重合体であり、 該共重合体 で通常 3 0 〜 6 0 %のェマルジョンで提供される。
前記水性ウレタン系樹脂としては、 芳香族系または脂肪族、 脂環 族イソシァネートとポリエステル又はポリカーボネート、 ポリエー テル系ポリオールから生成されるゥレ夕ン樹脂の水溶性、 コロイダ ルディスパージヨン、 ェマルジヨ ン等が利用できる。 このうち特 に、 傷隠蔽性ゃ耐傷付き性といった面から、 水性ウレタン系樹脂が ウレタンディスパ一ジョンであることが好ましく、 そして、 このな かでも特に耐傷付き性といった面から、 ウレタンディスパ一ジョン のウレ夕ンが脂肪族ポリエステル系ウレタンであることが好まし い o
前記ワックスェマルジヨンとしては、 植物系のキャンデリラヮヅ クス、 カルナバワックス、 ライスワックス、 木ロウなど、 動物系の 蜜ロウ、 ラノ リ ン、 鯨ロウなど、 鉱物系のモンタンワックス、 ォゾ ケライ ト、 セレシンなど、 石油系のパラフィ ンワックス、 マイクロ ク リス夕リンワックス、 ペトロラ夕ムなど、 合成炭化水素系のフィ ッシヤートロプシュワックス、 酸化ポリエチレンワックス、 ポリエ チレンワックス、 アク リル一エチレン共重合体ワックスなど、 変性 ワックス系のモンタンヮックス誘導体、 パラフィ ンヮックス誘導 体、 マイクロク リス夕 リンワックス誘導体、 水素添加ヒマシ油など のワックスを乳化分散したものが利用できる。
前記アル力リ可溶性樹脂としては、 スチレンマレイン酸共重合物 やロジン、 アク リルオリゴマーなどの樹脂を、 例えばアンモニア水 溶液のようなアル力リ水溶液として利用する。
前記紫外線吸収剤としては、 2 , 4—ジヒ ドロキシベンゾフエノ ン、 2 —ヒ ドロキシ一 4ーメ トキシベンゾフエノ ン、 2 —ヒ ドロキ シ一 4 —メ トキシベンゾフエノン 5—スルホン酸、 2 —ヒ ドロキシ 一 4 _ n—ォク トキシベンゾフエノン、 2 —ヒ ドロキシ一 4 一 n— ドデシルォキシベンゾフエノン、 2—ヒ ドロキシ一 4 —ベンジルォ キシペンゾフエノン、 2 , 2 ' —ジヒ ドロキシ一 4 —メ トキシベン ゾフエノン、 2 , 2， ， 4 , 4， 一テ トラヒ ドロキシペンゾフエノ ン、 2， 2 ' —ジヒ ドロキシー 4 , 4 ' —ジメ トキシペンゾフエノ ン等のベンゾフエノン系、 2— （ 2， ーヒ ドロキシ一 5， 一メチル フエニル） 一ペンゾ ト リアゾール、 2— ( 2， 一ヒ ドロキシー 3 ， ， 5， ージー t —ブチルフエニル） 一 5—クロローべンゾ ト リア ゾール、 2— （ 2， ーヒ ドロキシ一 3， _ t—ブチル一 5， ーメチ ルフエニル） 一 5 —クロローペンゾ ト リアゾ一ル、 2— ( 2， 一ヒ 訂正された 期 91) ドロキシ— 3， ， 5， 一ジー t ーァミルフエニル） 一べンゾ ト リア ゾ一ル、 2— （ 2， 一ヒ ドロキシー 3， ， 5， 一ジ一 t—プチルフ ェニル） 一ベンゾ 卜 リアゾ一ル、 2— ( 2， ーヒ ドロキシ一 5， - t—ブチルフエニル） 一ベンゾ 卜 リアゾール、 2— （ 2， ーヒ ドロ キシ— 5 ' —t —才クチルフエ二ル） 一べンゾ ト リァゾ一ル、 2， 4ージ— t一プチルフエ二ル— 3， ， 5， —ジ— t—ブチル 4， 一 ヒ ドロキシベンゾェ一ト等のベンゾ ト リァゾール系及びべンゾト リ ァゾ一ル骨格にメ夕ク リ ロイル基を導入した反応型紫外線吸収剤 (例えば 「R U V A— 9 3」 （大塚化学社製） ） 等が利用できる。 前記艷消し剤としては、 例えばホワイ トカーボンに代表される無 機系材料や例えばポリエチレン樹脂に代表される有機系材料等が利 用できる。
以上のような移動体や家具調度の内外装に備えられた有機系部材 に用いられるコ一ティ ング剤組成物には、 その他必要に応じて防腐 剤、 消泡剤を添加することができる。
以下、 本発明の実施例及び比較例を挙げて、 本発明の特徴につい て例証する。 但し、 本発明はこれらの実施例及び比較例によって何 ら制限されるものではない。
実施例 1〜 4及び比較例 1〜 5
表 1 (実施例） 、 表 2 (比較例） に示す組成を有するコ一ティ ン グ剤組成物を調整し、 傷隠蔽性、 重ね塗り性、 密着性、 促進耐候 性、 耐傷付き性、 を評価した。 表中の数字は重量％を示す。
【表 1】
実施例 1 US例 2 実施例 3 実施例 4 ァクリル系共重合物ェマルジョン 注 1 20 < - 20 - 水性ウレタン系樹脂ェマルジヨン 注 2 5
非脂肪族ポリエステル系ディスパ一ジョン 5
注 3
脂肪族ポリエステル系ディスパ一ジョン 5
注 4
ポリェチレンヮックスェマルジョン 5 <r- 注 5
アル力リ可溶性樹脂 ( 15 %水溶液） 2 < - 注 6
紫外線吸収剤 注 7 0. 02 < - 可塑剤 注 8 1 < - < - 造膜助剤 注 9 2
水 残り 残り 残り 残り 防腐剤 注 10 0. 05 « - < - < - 消泡剤 注 11 0. 50 < - 分散剤 注 12 0. 03
艷消し剤 注 13 0， 3
口 ¾ p| 100 100 100 100 備 考 艷有り 艷無し 艷有り 艷有り
【表 2】
Figure imgf000011_0001
注 1 ： ロ一ムアンドハ一ス社製 プライマル E— 2409
注 2 ：三洋化成社製 パーマリン U A— 1 50
注 3 :三洋化成社製 ュ一コート UX— 4300
注 4 ：大日本ィンキ社製 スベンゾール L 54
注 5 ：東邦化学社製 ハイテック E― 6020 R
注 6 ： アトケミ社製 SMA 17352 Pのアンモニゥム水溶液 注 7 ： ペンゾトリアゾール系のチヌビン P
注 8 ： ジブチルフ夕レート （D B P)
注 9 ：ェチルジグリコール
注 10 ： 夕イショ一テクノス社製 ピオサイ ド # 8 1 0
注 l l : Mun z i ng Chemi e社製 Ag i t an E 2 56
注 1 2 ：三洋化成社製 キヤ リボン L 400
耵正された用弒 (規則 91) 注 1 3 ： デグサヒュルス社製 エースマッ ト T S— 1 0 0
(試験項目の評価方法）
試験では、 移動体や家具調度等の物体の内外装に備えられた有機 系部材として、 自動車等のモールに使用されるモール素材ゴム板を 用意し、 このモール素材ゴム板を使用して傷隠蔽性、 重ね塗り性、 密着性、 促進耐候性、 耐傷付き性の試験を行った。 傷隠蔽性は、 モ ール素材ゴム板表面を # 4 0 0サン ドペーパーで均一に擦り、 その 表面にサンプルを塗布し隠蔽性を確認した。 重ね塗り性は、 モール 素材ゴム板上にサンプルを塗布。 乾燥後重ね塗りを実施し、 濡れ性 を評価した。 密着性は、 モール素材ゴム板に対して塗布し、 乾燥後 テープを貼り付け、 その後一気に剥がしテープへの塗膜の移行を調 ベた。 促進耐候性は、 サンシャインゥヱザオメ一夕一に連続 3 0 0 時間かけた後の表面の塗膜状況を観察評価した。 耐傷付き性は、 モ ール素材ゴム板に塗布、 S A E J 4 0 0の規定に準拠したグラ ぺロメ一夕一試験機にて塗布板にシヨッ ト材 （ 6号砕石） が 4 5 ° の角度で当たるようにセ ヅ ト し、 吹き付け圧力 5 k g / c m 2 、 2 5 0 gで吹き付け、 吹き付け終了後表面の傷付き程度を目視評価し た。 これらの試験結果を表 3に示す。
【表 3 】
Figure imgf000012_0001
◎ :優れる 〇 ： 良い △ ： 普通 X ：悪い 産業上の利用の可能性
以上のように、 本発明に係る移動体や家具調度等の物体の内外装 に備えられた有機系部材に用いられるコ一ティ ング剤組成物によれ ば、 酸性雨や紫外線等が原因で白化を起こしたり、 また傷を付けら れたり して劣化した有機系部材の表面に塗布することにより、 白化 を改善し、 また、 重ね塗りにより表面の凹凸を十分に補修し、 モー ルの表面を初期の美観に近い状態に復元するとともに、 表面を保護 し美観を維持する塗膜を有機系部材の表面に形成することができ る。

Claims

請 求 の 範 囲
1 . 有効成分と して、 下記 （ a ) 、 （ b ) 、 （ c ) 、 （ d ) 、 ( e ) を含有する、 物体の内外装に備えられた有機系部材に用いら れるコ一ティ ング剤組成物。
(a) アクリル系共重合物のェマルジヨン
(b ) 水性ウレタン系樹脂
( c ) ヮックスェマルジョン
(d) アル力リ可溶性樹脂
( e ) 紫外線吸収剤
2. 前記 （b) 水性ウレタン系樹脂が、 ウレタンディスパ一ジョン であることを特徴とする請求項 1に記載のコ一ティ ング剤組成物。
3. 前記ウレタンディスパージヨンのウレタンが、 脂肪族ポリエス テル系ウレタンであることを特徴とする請求項 2に記載のコーティ ング剤組成物。
4. 有機系部材の光沢に合わせるために艷消し剤が加えられている ことを特徴とする請求項 1， 2又は 3に記載のコーティ ング剤組成 物。
5. 前記物体が、 移動体であることを特徴とする請求項 1 , 2 , 3 又は 4に記載のコ一ティ ング剤組成物。
6. 前記物体が、 家具調度であることを特徴とする請求項 1 , 2， 3又は 4に記載のコーティ ング剤組成物。
PCT/JP2002/010467 2001-10-10 2002-10-09 Composition de matiere de revetement WO2003033578A1 (fr)