WO2002077080A1 - Compositions pour films et lamines composees d'un copolymere de polyhydroxyalkanoate et d'un polymere d'acide polylactique - Google Patents

Compositions pour films et lamines composees d'un copolymere de polyhydroxyalkanoate et d'un polymere d'acide polylactique Download PDF

Info

Publication number
WO2002077080A1
WO2002077080A1 PCT/US2002/007680 US0207680W WO02077080A1 WO 2002077080 A1 WO2002077080 A1 WO 2002077080A1 US 0207680 W US0207680 W US 0207680W WO 02077080 A1 WO02077080 A1 WO 02077080A1
Authority
WO
WIPO (PCT)
Prior art keywords
film
copolymer
films
pla
composition
Prior art date
Application number
PCT/US2002/007680
Other languages
English (en)
Inventor
Isao Noda
Eric Bryan Bond
David Harry Melik
Original Assignee
The Procter & Gamble Company
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from US10/051,724 external-priority patent/US6808795B2/en
Priority claimed from US10/051,723 external-priority patent/US6905987B2/en
Application filed by The Procter & Gamble Company filed Critical The Procter & Gamble Company
Priority to MXPA03008886A priority Critical patent/MXPA03008886A/es
Priority to EP02723426A priority patent/EP1373378A1/fr
Priority to BR0208377-9A priority patent/BR0208377A/pt
Priority to JP2002576535A priority patent/JP2004536897A/ja
Priority to KR1020037012531A priority patent/KR100563799B1/ko
Priority to AU2002254207A priority patent/AU2002254207B2/en
Priority to CA002440544A priority patent/CA2440544A1/fr
Publication of WO2002077080A1 publication Critical patent/WO2002077080A1/fr

Abstract

L'invention porte sur des films dégradables dans l'environnement composés d'un mélange d'un copolymère de polyhydroxyalkanoate (PHA) et d'un polymère ou copolymère d'acide polylactique (PLA), sur des laminés comportant une premier couche de copolymère de PHA et une deuxième couche de polymère ou copolymère de PLA, et sur des articles à jeter comprenant lesdits films ou laminés dégradables dans l'environnement.
PCT/US2002/007680 2001-03-27 2002-03-15 Compositions pour films et lamines composees d'un copolymere de polyhydroxyalkanoate et d'un polymere d'acide polylactique WO2002077080A1 (fr)

Priority Applications (7)

Application Number Priority Date Filing Date Title
MXPA03008886A MXPA03008886A (es) 2001-03-27 2002-03-15 Composiciones de baja respuesta glicemica.
EP02723426A EP1373378A1 (fr) 2001-03-27 2002-03-15 Compositions pour films et lamines composees d'un copolymere de polyhydroxyalkanoate et d'un polymere d'acide polylactique
BR0208377-9A BR0208377A (pt) 2001-03-27 2002-03-15 Composição ambientalmente degradável, saco, envoltório, laminado de múltiplas camadas, bem como pelìcula do referido laminado e pelìcula ambientalmente degradável
JP2002576535A JP2004536897A (ja) 2001-03-27 2002-03-15 積層体及びフィルムのためのポリヒドロキシアルカノエートコポリマー及びポリ乳酸組成物
KR1020037012531A KR100563799B1 (ko) 2001-03-27 2002-03-15 적층체 및 필름용 폴리히드록시알카노에이트 공중합체 및폴리락트산 중합체 조성물
AU2002254207A AU2002254207B2 (en) 2001-03-27 2002-03-15 Polyhydroxyalkanoate copolymer and polylactic acid polymer compositions for laminates and films
CA002440544A CA2440544A1 (fr) 2001-03-27 2002-03-15 Compositions pour films et lamines composees d'un copolymere de polyhydroxyalkanoate et d'un polymere d'acide polylactique

Applications Claiming Priority (6)

Application Number Priority Date Filing Date Title
US27894801P 2001-03-27 2001-03-27
US60/278,948 2001-03-27
US10/051,724 US6808795B2 (en) 2001-03-27 2002-01-17 Polyhydroxyalkanoate copolymer and polylactic acid polymer compositions for laminates and films
US10/051,723 US6905987B2 (en) 2001-03-27 2002-01-17 Fibers comprising polyhydroxyalkanoate copolymer/polylactic acid polymer or copolymer blends
US10/051,723 2002-01-17
US10/051,724 2002-01-17

Publications (1)

Publication Number Publication Date
WO2002077080A1 true WO2002077080A1 (fr) 2002-10-03

Family

ID=27368008

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2002/007680 WO2002077080A1 (fr) 2001-03-27 2002-03-15 Compositions pour films et lamines composees d'un copolymere de polyhydroxyalkanoate et d'un polymere d'acide polylactique

Country Status (9)

Country Link
EP (1) EP1373378A1 (fr)
JP (1) JP2004536897A (fr)
KR (1) KR100563799B1 (fr)
CN (1) CN1500114A (fr)
AU (1) AU2002254207B2 (fr)
BR (1) BR0208377A (fr)
CA (1) CA2440544A1 (fr)
MX (1) MXPA03008886A (fr)
WO (1) WO2002077080A1 (fr)

Cited By (18)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2004076582A1 (fr) * 2003-02-21 2004-09-10 Metabolix Inc. Melanges de pha
WO2004101683A1 (fr) * 2003-05-08 2004-11-25 The Procter & Gamble Company Articles moules ou extrudes comprenant un copolymere de polyhydroxyalkanoate et un polymere thermoplastique degradable dans l'environnement
WO2007109128A2 (fr) * 2006-03-17 2007-09-27 The Procter & Gamble Company Article absorbant comprenant un polymère synthétique dérivé d'une ressource renouvelable et procédés de production dudit article
WO2008028344A1 (fr) 2006-08-29 2008-03-13 Tianjin Greenbio Material Co. Ltd. Composition contenant un copolymère de polyhydroxyalcanoate et de l'acide polylactique, utilisée en tant que mousse
WO2008045260A2 (fr) * 2006-10-06 2008-04-17 Alcan Packaging Flexible France Applications d'emballage utilisant un film d'acide polylactique
US7422782B2 (en) 2005-02-01 2008-09-09 Curwood, Inc. Peelable/resealable packaging film
EP1980235A1 (fr) * 2007-03-13 2008-10-15 Riken Film biodégradable absorbant de l'huile
US20120201983A1 (en) * 2007-08-23 2012-08-09 Innovia Films, Ltd. Packaging article
WO2013100473A1 (fr) * 2011-12-26 2013-07-04 (주)엘지하우시스 Composition de plastique biologique
WO2015102831A1 (fr) * 2013-12-30 2015-07-09 Avery Dennison Corporation Films clairs et flexibles comprenant de l'acide polylactique et un plastifiant dérivé d'une source renouvelable
EP3060601A1 (fr) * 2013-10-27 2016-08-31 Tipa Corp. Ltd. Feuille biodégradable
US10030135B2 (en) 2012-08-17 2018-07-24 Cj Cheiljedang Corporation Biobased rubber modifiers for polymer blends
US10611903B2 (en) 2014-03-27 2020-04-07 Cj Cheiljedang Corporation Highly filled polymer systems
US10669417B2 (en) 2013-05-30 2020-06-02 Cj Cheiljedang Corporation Recyclate blends
CN111332599A (zh) * 2020-03-30 2020-06-26 浙江正庄实业有限公司 轻量化可降解旋转锁外置弹簧乳液泵及其材料制备方法
CN111453179A (zh) * 2020-03-30 2020-07-28 浙江正庄实业有限公司 抗菌可降解内衬乳液喷头及其材料制备方法
US11135823B2 (en) 2016-09-16 2021-10-05 Ethicon, Inc. Method of laminating absorbable semi-crystalline polymeric films
CN113493599A (zh) * 2020-03-19 2021-10-12 东丽先端材料研究开发（中国）有限公司 一种取向薄膜及含有该取向薄膜的多层薄膜

Families Citing this family (17)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP5215513B2 (ja) * 2001-04-13 2013-06-19 三井化学株式会社 生分解性樹脂組成物
CN100372881C (zh) * 2006-08-10 2008-03-05 同济大学 一种生物全降解聚酯共聚物的制备方法
CA2719409A1 (fr) * 2008-03-24 2009-10-01 Biovation, Llc Ensemble composite biostratifie et procedes associes
CN101327345B (zh) * 2008-07-21 2012-10-24 南开大学 超细纤维多孔膜材料及其制备方法
KR101014931B1 (ko) * 2008-09-12 2011-02-15 윤영진 음료수 용기
KR20100075085A (ko) 2008-12-24 2010-07-02 제일모직주식회사 폴리히드록시 알카노에이트　수지 조성물
JP5353768B2 (ja) * 2009-03-06 2013-11-27 国立大学法人東京工業大学 樹脂組成物
CN101824210A (zh) * 2009-12-28 2010-09-08 天津国韵生物材料有限公司 一种可完全生物分解的多组分薄膜材料及其制备方法
EP2571936B1 (fr) * 2010-05-17 2019-02-06 CJ CheilJedang Corporation Trempe de l'acide polylactique à l'aide de polyhydroxyalcanoates
KR101456330B1 (ko) * 2012-04-09 2014-11-04 (주)엘지하우시스 친환경 고강도 수지 복합재
JP5955471B2 (ja) * 2012-12-18 2016-07-20 ヴェオリア・ウォーター・ソリューションズ・アンド・テクノロジーズ・サポート 改良された機械的特性を有するポリヒドロキシアルカノエート複合プラスチックの生産方法
CN105667031B (zh) * 2014-11-21 2018-07-20 江苏华信新材料股份有限公司 Pha/pla/pha共挤薄膜及其挤出成型工艺
KR101930986B1 (ko) * 2015-01-20 2018-12-19 (주)엘지하우시스 아크릴계 탄성수지 조성물 및 이를 이용하여 제조된 필름
US10709806B2 (en) * 2015-07-22 2020-07-14 Everyone's Earth Inc. Biodegradable absorbent articles
MX2023001212A (es) * 2020-07-31 2023-04-14 Kimberly Clark Co Artículos absorbentes autobiodegradables.
EP4215366A4 (fr) * 2020-09-17 2024-10-16 Kaneka Corp Stratifié et corps moulé
EP4324647A1 (fr) * 2021-04-16 2024-02-21 SK microworks Co., Ltd. Film étiré biaxialement, stratifié et matériau d'emballage écologique comprenant un film

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1995020615A1 (fr) * 1994-01-28 1995-08-03 The Procter & Gamble Company Copolymeres biodegradables et articles plastiques comprenant des copolymeres biodegradables de 3-hydroxyhexanoate
WO1996008535A1 (fr) * 1994-09-16 1996-03-21 The Procter & Gamble Company Compositions polymeres biodegradables et produits en etant faits
EP0753539A1 (fr) * 1995-07-13 1997-01-15 Mitsubishi Gas Chemical Company, Inc. Composition de polymères de polyesters aliphatiques à base de polymères d'acide lactique, procédé de préparation et procédé de moulage de ceux-ci
US5685756A (en) * 1994-01-28 1997-11-11 The Procter & Gamble Company Nonwoven materials comprising biodegradable copolymers
JPH10147653A (ja) * 1996-11-20 1998-06-02 Gunze Ltd 微生物分解性延伸フィルム
EP0993832A1 (fr) * 1998-10-16 2000-04-19 The Procter & Gamble Company Article absorbant pourvu d'un film microporeux avec une couche adhesive

Patent Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1995020615A1 (fr) * 1994-01-28 1995-08-03 The Procter & Gamble Company Copolymeres biodegradables et articles plastiques comprenant des copolymeres biodegradables de 3-hydroxyhexanoate
US5536564A (en) * 1994-01-28 1996-07-16 The Procter & Gamble Company Biodegradable copolymers and plastic articles comprising biodegradable copolymers of 3-hydroxyhexanoate
US5685756A (en) * 1994-01-28 1997-11-11 The Procter & Gamble Company Nonwoven materials comprising biodegradable copolymers
WO1996008535A1 (fr) * 1994-09-16 1996-03-21 The Procter & Gamble Company Compositions polymeres biodegradables et produits en etant faits
EP0753539A1 (fr) * 1995-07-13 1997-01-15 Mitsubishi Gas Chemical Company, Inc. Composition de polymères de polyesters aliphatiques à base de polymères d'acide lactique, procédé de préparation et procédé de moulage de ceux-ci
JPH10147653A (ja) * 1996-11-20 1998-06-02 Gunze Ltd 微生物分解性延伸フィルム
EP0993832A1 (fr) * 1998-10-16 2000-04-19 The Procter & Gamble Company Article absorbant pourvu d'un film microporeux avec une couche adhesive

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
PATENT ABSTRACTS OF JAPAN vol. 1998, no. 11 30 September 1998 (1998-09-30) *

Cited By (41)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP2241605A3 (fr) * 2003-02-21 2012-03-21 Metabolix, Inc. Mélanges de polyhydroxyalcanoates
JP2006518799A (ja) * 2003-02-21 2006-08-17 メタボリックス インコーポレイティッド Ｐｈａブレンド
JP4724111B2 (ja) * 2003-02-21 2011-07-13 メタボリックス インコーポレイティッド Ｐｈａブレンド
WO2004076582A1 (fr) * 2003-02-21 2004-09-10 Metabolix Inc. Melanges de pha
EP1935945A1 (fr) * 2003-02-21 2008-06-25 Metabolix, Inc. Mélanges de PHA
WO2004101683A1 (fr) * 2003-05-08 2004-11-25 The Procter & Gamble Company Articles moules ou extrudes comprenant un copolymere de polyhydroxyalkanoate et un polymere thermoplastique degradable dans l'environnement
KR100887198B1 (ko) * 2003-05-08 2009-03-06 메레디언, 인크. 폴리하이드록시알카노에이트 공중합체 및 환경적으로분해가능한 열가소성 중합체를 포함하는 성형품 또는압출품
US7422782B2 (en) 2005-02-01 2008-09-09 Curwood, Inc. Peelable/resealable packaging film
US10166312B2 (en) 2006-03-17 2019-01-01 The Procter & Gamble Company Absorbent article comprising a synthetic polymer derived from a renewable resource and methods of producing said article
WO2007109128A3 (fr) * 2006-03-17 2007-11-22 Procter & Gamble Article absorbant comprenant un polymère synthétique dérivé d'une ressource renouvelable et procédés de production dudit article
US10815653B2 (en) 2006-03-17 2020-10-27 The Procter & Gamble Company Absorbent article comprising a synthetic polymer derived from a renewable resource and methods of producing said article
WO2007109128A2 (fr) * 2006-03-17 2007-09-27 The Procter & Gamble Company Article absorbant comprenant un polymère synthétique dérivé d'une ressource renouvelable et procédés de production dudit article
US10501920B2 (en) 2006-03-17 2019-12-10 The Procter & Gamble Company Absorbent article comprising a synthetic polymer derived from a renewable resource and methods of producing said article
US10822783B2 (en) 2006-03-17 2020-11-03 The Proctor & Gamble Company Absorbent article comprising a synthetic polymer derived from a renewable resource and methods of producing said article
US10920407B2 (en) 2006-03-17 2021-02-16 The Procter & Gamble Company Absorbent article comprising a synthetic polymer derived from a renewable resource and methods of producing said article
US11186976B2 (en) 2006-03-17 2021-11-30 The Procter & Gamble Company Absorbent article comprising a synthetic polymer derived from a renewable resource and methods of producing said article
US12054928B2 (en) 2006-03-17 2024-08-06 The Procter & Gamble Company Absorbent article comprising a synthetic polymer derived from a renewable resource and methods of producing said article
WO2008028344A1 (fr) 2006-08-29 2008-03-13 Tianjin Greenbio Material Co. Ltd. Composition contenant un copolymère de polyhydroxyalcanoate et de l'acide polylactique, utilisée en tant que mousse
EP2060605A4 (fr) * 2006-08-29 2012-10-24 Tianjin Greenbio Material Co Ltd Composition contenant un copolymère de polyhydroxyalcanoate et de l'acide polylactique, utilisée en tant que mousse
EP2060605A1 (fr) 2006-08-29 2009-05-20 Tianjin Greenbio Material Co., Ltd. Composition contenant un copolymère de polyhydroxyalcanoate et de l'acide polylactique, utilisée en tant que mousse
WO2008045260A2 (fr) * 2006-10-06 2008-04-17 Alcan Packaging Flexible France Applications d'emballage utilisant un film d'acide polylactique
WO2008045260A3 (fr) * 2006-10-06 2009-07-16 Alcan Packaging Flexible France Applications d'emballage utilisant un film d'acide polylactique
EP1980235A1 (fr) * 2007-03-13 2008-10-15 Riken Film biodégradable absorbant de l'huile
US20120201983A1 (en) * 2007-08-23 2012-08-09 Innovia Films, Ltd. Packaging article
US8709559B2 (en) * 2007-08-23 2014-04-29 Innovia Films, Ltd. Packaging article
US9656787B2 (en) 2007-08-23 2017-05-23 Innovia Films Limited Packaging article
WO2013100473A1 (fr) * 2011-12-26 2013-07-04 (주)엘지하우시스 Composition de plastique biologique
US10030135B2 (en) 2012-08-17 2018-07-24 Cj Cheiljedang Corporation Biobased rubber modifiers for polymer blends
US10669417B2 (en) 2013-05-30 2020-06-02 Cj Cheiljedang Corporation Recyclate blends
US10647093B2 (en) 2013-10-27 2020-05-12 Tipa Corp. Ltd. Biodegradable sheet
US10239292B2 (en) 2013-10-27 2019-03-26 Tipa Corp. Ltd. Biodegradable sheet
AU2014338515B2 (en) * 2013-10-27 2017-12-14 Tipa Corp. Ltd Biodegradable sheet
EP3060601A4 (fr) * 2013-10-27 2017-05-03 Tipa Corp. Ltd. Feuille biodégradable
US11007758B2 (en) 2013-10-27 2021-05-18 Tipa Corp. Ltd Biodegradable sheet
EP3060601A1 (fr) * 2013-10-27 2016-08-31 Tipa Corp. Ltd. Feuille biodégradable
WO2015102831A1 (fr) * 2013-12-30 2015-07-09 Avery Dennison Corporation Films clairs et flexibles comprenant de l'acide polylactique et un plastifiant dérivé d'une source renouvelable
US10611903B2 (en) 2014-03-27 2020-04-07 Cj Cheiljedang Corporation Highly filled polymer systems
US11135823B2 (en) 2016-09-16 2021-10-05 Ethicon, Inc. Method of laminating absorbable semi-crystalline polymeric films
CN113493599A (zh) * 2020-03-19 2021-10-12 东丽先端材料研究开发（中国）有限公司 一种取向薄膜及含有该取向薄膜的多层薄膜
CN111332599A (zh) * 2020-03-30 2020-06-26 浙江正庄实业有限公司 轻量化可降解旋转锁外置弹簧乳液泵及其材料制备方法
CN111453179A (zh) * 2020-03-30 2020-07-28 浙江正庄实业有限公司 抗菌可降解内衬乳液喷头及其材料制备方法

Also Published As

Publication number Publication date
KR20030088475A (ko) 2003-11-19
KR100563799B1 (ko) 2006-03-28
CN1500114A (zh) 2004-05-26
BR0208377A (pt) 2004-06-15
JP2004536897A (ja) 2004-12-09
CA2440544A1 (fr) 2002-10-03
EP1373378A1 (fr) 2004-01-02
AU2002254207B2 (en) 2006-02-16
MXPA03008886A (es) 2003-12-08

Similar Documents

Publication Publication Date Title
US6808795B2 (en) Polyhydroxyalkanoate copolymer and polylactic acid polymer compositions for laminates and films
AU2002254207B2 (en) Polyhydroxyalkanoate copolymer and polylactic acid polymer compositions for laminates and films
CA2463806C (fr) Compositions de copolymeres de polyhydroxyalcanoate et d'amidon destinees a des stratifies et des films
AU2002254207A1 (en) Polyhydroxyalkanoate copolymer and polylactic acid polymer compositions for laminates and films
AU2002341940A1 (en) Polyhydroxyalkanoate copolymer/starch compositions for laminates and films
EP0781309B1 (fr) Compositions polymeres biodegradables et produits en etant faits
CA2440545C (fr) Fibres comprenant un copolymere de polyhydroxyalkanoate et un polymere d'acide polylactique ou des melanges de copolymeres
EP1325079B1 (fr) Produits plastiques contenant des compositions de melanges de polyester biodegradables
EP1322345B1 (fr) Articles absorbants contenant des compositions a base de melanges de polyesters biodegradables
AU2002258508A1 (en) Fibers comprising polyhydroxyalkanoate copolymer/polylactic acid polymer or copolymer blends
JPH07508437A (ja) 生分解性を有する液体不透過性の単層フィルム組成物
US7265188B2 (en) Biodegradable polyester blend compositions and methods of making the same
EP1360237B1 (fr) Compositions a base de melanges de polyesters biodegradables et leurs procedes de preparation
CN1326940C (zh) 用于制造层压材料和薄膜的聚羟基链烷酸酯共聚物/淀粉组合物

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AE AG AL AM AT AT AU AZ BA BB BG BR BY BZ CA CH CN CO CR CU CZ CZ DE DE DK DK DM DZ EC EE EE ES FI FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX MZ NO NZ OM PH PL PT RO RU SD SE SG SI SK SK SL TJ TM TN TR TT TZ UA UG UZ VN YU ZA ZM ZW

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): GH GM KE LS MW MZ SD SL SZ TZ UG ZM ZW AM AZ BY KG KZ MD RU TJ TM AT BE CH CY DE DK ES FI FR GB GR IE IT LU MC NL PT SE TR BF BJ CF CG CI CM GA GN GQ GW ML MR NE SN TD TG

DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
121 Ep: the epo has been informed by wipo that ep was designated in this application
WWE Wipo information: entry into national phase

Ref document number: 1438/DELNP/2003

Country of ref document: IN

WWE Wipo information: entry into national phase

Ref document number: 2440544

Country of ref document: CA

WWE Wipo information: entry into national phase

Ref document number: 2002723426

Country of ref document: EP

WWE Wipo information: entry into national phase

Ref document number: 2002576535

Country of ref document: JP

WWE Wipo information: entry into national phase

Ref document number: 028073614

Country of ref document: CN

Ref document number: 2002254207

Country of ref document: AU

Ref document number: 1020037012531

Country of ref document: KR

WWE Wipo information: entry into national phase

Ref document number: PA/a/2003/008886

Country of ref document: MX

WWP Wipo information: published in national office

Ref document number: 2002723426

Country of ref document: EP

REG Reference to national code

Ref country code: DE

Ref legal event code: 8642

WWW Wipo information: withdrawn in national office

Ref document number: 2002723426

Country of ref document: EP