WO2000063998A1 - Electrolyte polymere solide perfluore pour batteries ion-lithium - Google Patents

Electrolyte polymere solide perfluore pour batteries ion-lithium Download PDF

Info

Publication number
WO2000063998A1
WO2000063998A1 PCT/US1999/008625 US9908625W WO0063998A1 WO 2000063998 A1 WO2000063998 A1 WO 2000063998A1 US 9908625 W US9908625 W US 9908625W WO 0063998 A1 WO0063998 A1 WO 0063998A1
Authority
WO
WIPO (PCT)
Prior art keywords
polymer
separator
lithium
plasticizer
perfluorinated
Prior art date
Application number
PCT/US1999/008625
Other languages
English (en)
Inventor
Alan J. Cisar
Eric T. Clarke
Original Assignee
Lynntech, Inc.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Lynntech, Inc. filed Critical Lynntech, Inc.
Priority to PCT/US1999/008625 priority Critical patent/WO2000063998A1/fr
Priority to AU36552/99A priority patent/AU3655299A/en
Publication of WO2000063998A1 publication Critical patent/WO2000063998A1/fr

Abstract

L'invention concerne un électrolyte polymère solide en solution présentant des degrés de conductivité élevés et une intégrité structurelle importante, convenant pour des batteries secondaires ion-lithium. Une matrice de polymère perfluoré comprend des groupes échangeurs d'ions pendants qui forment des régions conductrices d'ions à travers la matrice, un plastifiant étant disposé à l'intérieur de la matrice et un ion de sel de métal alcalin associé aux régions conductrices. On prépare l'électrolyte polymère solide en solution en dissolvant une plastifiant dans un polymère organique compatible tel qu'un acide perfluorosulfonique. L'invention concerne également une cellule électrolytique comprenant une cathode de lithium, une anode de lithium reliée électriquement à la cathode, et un isolateur constitué d'un mélange à une seule phase comprenant un polymère perfluoré conducteur d'ions, un polymère conducteur et un sel de métal alcalin et un plastifiant.
PCT/US1999/008625 1999-04-20 1999-04-20 Electrolyte polymere solide perfluore pour batteries ion-lithium WO2000063998A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
PCT/US1999/008625 WO2000063998A1 (fr) 1999-04-20 1999-04-20 Electrolyte polymere solide perfluore pour batteries ion-lithium
AU36552/99A AU3655299A (en) 1999-04-20 1999-04-20 Perfluorinated solid polymer electrolyte for lithium ion batteries

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/US1999/008625 WO2000063998A1 (fr) 1999-04-20 1999-04-20 Electrolyte polymere solide perfluore pour batteries ion-lithium

Publications (1)

Publication Number Publication Date
WO2000063998A1 true WO2000063998A1 (fr) 2000-10-26

Family

ID=22272595

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US1999/008625 WO2000063998A1 (fr) 1999-04-20 1999-04-20 Electrolyte polymere solide perfluore pour batteries ion-lithium

Country Status (2)

Country Link
AU (1) AU3655299A (fr)
WO (1) WO2000063998A1 (fr)

Cited By (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP1635412A4 (fr) * 2003-05-13 2007-06-13 Asahi Glass Co Ltd Polymere electrolytique pour pile a combustible a polymeres solides, son procede de production, et ensemble d'electrode a membrane
CN102306832A (zh) * 2011-08-12 2012-01-04 上海交通大学 一种含锂离子聚合物电解质膜及其制备方法
CN102306831A (zh) * 2011-08-12 2012-01-04 上海交通大学 用于锂离子二次电池的凝胶聚合物电解质膜及其制备方法
WO2014022224A1 (fr) * 2012-08-02 2014-02-06 The Penn State Research Foundation Conducteur polymère pour des batteries à ion de lithium
CN103665417A (zh) * 2012-09-12 2014-03-26 通用汽车环球科技运作有限责任公司 用PFSA离聚物和ePTFE制成的反渗透膜
CN104852086A (zh) * 2015-05-29 2015-08-19 上海交通大学 一种锂空气电池用聚合物电解质及其制备方法
CN105006590A (zh) * 2015-05-29 2015-10-28 上海交通大学 一种锂空气电池用凝胶聚合物电解质及其制备方法
US20210226250A1 (en) * 2020-01-17 2021-07-22 Ford Global Technologies, Llc Lithiated perfluorinated polymer with mixed long and short side chains as a single- ion polymer electrolyte for lithium metal batteries
US11894514B2 (en) 2020-12-16 2024-02-06 United States Of America As Represented By The Secretary Of The Air Force Electronic connection in an all-solid state battery at the anode/electrolyte interface

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5491041A (en) * 1994-10-14 1996-02-13 Eic Laboratories, Inc. Solid-state secondary batteries with graphite anodes
US5633098A (en) * 1995-01-13 1997-05-27 Sri International Batteries containing single-ion conducting solid polymer electrolytes
WO1998011614A1 (fr) * 1996-09-13 1998-03-19 Gore Enterprise Holdings, Inc. Composite electrolyte solide pour dispositif a reaction electrochimique
WO1998020573A1 (fr) * 1996-11-01 1998-05-14 E.I. Du Pont De Nemours And Company Polymere echangeur d'ions a forte conductivite et procede

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5491041A (en) * 1994-10-14 1996-02-13 Eic Laboratories, Inc. Solid-state secondary batteries with graphite anodes
US5633098A (en) * 1995-01-13 1997-05-27 Sri International Batteries containing single-ion conducting solid polymer electrolytes
WO1998011614A1 (fr) * 1996-09-13 1998-03-19 Gore Enterprise Holdings, Inc. Composite electrolyte solide pour dispositif a reaction electrochimique
WO1998020573A1 (fr) * 1996-11-01 1998-05-14 E.I. Du Pont De Nemours And Company Polymere echangeur d'ions a forte conductivite et procede

Cited By (12)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP1635412A4 (fr) * 2003-05-13 2007-06-13 Asahi Glass Co Ltd Polymere electrolytique pour pile a combustible a polymeres solides, son procede de production, et ensemble d'electrode a membrane
US7488788B2 (en) 2003-05-13 2009-02-10 Asahi Glass Company, Limited Electrolyte polymer for polymer electrolyte fuel cells, process for its production and membrane-electrode assembly
CN102306832A (zh) * 2011-08-12 2012-01-04 上海交通大学 一种含锂离子聚合物电解质膜及其制备方法
CN102306831A (zh) * 2011-08-12 2012-01-04 上海交通大学 用于锂离子二次电池的凝胶聚合物电解质膜及其制备方法
CN102306831B (zh) * 2011-08-12 2014-06-11 上海交通大学 用于锂离子二次电池的凝胶聚合物电解质膜及其制备方法
WO2014022224A1 (fr) * 2012-08-02 2014-02-06 The Penn State Research Foundation Conducteur polymère pour des batteries à ion de lithium
US9790323B2 (en) 2012-08-02 2017-10-17 The Penn State Research Foundation Polymer conductor for lithium-ion batteries
CN103665417A (zh) * 2012-09-12 2014-03-26 通用汽车环球科技运作有限责任公司 用PFSA离聚物和ePTFE制成的反渗透膜
CN104852086A (zh) * 2015-05-29 2015-08-19 上海交通大学 一种锂空气电池用聚合物电解质及其制备方法
CN105006590A (zh) * 2015-05-29 2015-10-28 上海交通大学 一种锂空气电池用凝胶聚合物电解质及其制备方法
US20210226250A1 (en) * 2020-01-17 2021-07-22 Ford Global Technologies, Llc Lithiated perfluorinated polymer with mixed long and short side chains as a single- ion polymer electrolyte for lithium metal batteries
US11894514B2 (en) 2020-12-16 2024-02-06 United States Of America As Represented By The Secretary Of The Air Force Electronic connection in an all-solid state battery at the anode/electrolyte interface

Also Published As

Publication number Publication date
AU3655299A (en) 2000-11-02

Similar Documents

Publication Publication Date Title
Niu et al. Recent advances in application of ionic liquids in electrolyte of lithium ion batteries
Watanabe et al. Application of ionic liquids to energy storage and conversion materials and devices
CN1950970B (zh) 用于电解液的材料、含离子材料的组合物及其用途
EP2565886A1 (fr) Matériau pour solution électrolytique, composition contenant un matériau ionique et son utilisation
CN104143614B (zh) 一种锂硫电池
US20150249244A1 (en) Alkali metal-chalcogen battery having low self-discharge and high cycle life and performance
US8632926B2 (en) Solid proton conductor including acid treated oxide nanoparticles and fuel cell including the same
US20190006711A1 (en) Solid polymer electrolyte based on modified cellulose and its use in lithium or sodium secondary batteries
JP5025092B2 (ja) 電解液材料
CA1216325A (fr) Pile electrochimique
Zahoor et al. Lithium air battery: alternate energy resource for the future
CN112635709A (zh) 钠离子电池负极sei膜形成剂及预钠化方法、钠离子电池
CN113346126A (zh) 复合固态电解质、全固态锂离子电池及其制备方法
JP4883903B2 (ja) 電解液材料
WO2000063998A1 (fr) Electrolyte polymere solide perfluore pour batteries ion-lithium
Chen et al. A hydrogel-enabled free-standing polypyrrole cathode film for potassium ion batteries with high mass loading and low-temperature stability
Bushkova et al. Polymer Electrolytes Based on the Lithium Form of Nafion Sulfonic Cation-Exchange Membranes: Current State of Research and Prospects for Use in Electrochemical Power Sources
KR20050084872A (ko) 프로톤 전도체, 싱글 이온 전도체 및 그들의 제조 방법과전기 화학 캐패시터
Yoon et al. A novel gel polymer electrolyte with multi-functional additive for superior ionic conductivity, stability against Li, and redox activity of lithium-air batteries
US11817561B2 (en) Electrolyte and secondary battery
CN109888183B (zh) 一种有机无机杂化薄膜的制备方法及应用
Wang et al. High‐Energy‐Density Solid‐State Metal–Air Batteries: Progress, Challenges, and Perspectives
Zhu et al. Ionic liquid/ether-plasticized quasi-solid-state electrolytes for long-life lithium–oxygen cells
KR100408514B1 (ko) 고분자 고체 전해질 및 이를 채용하고 있는 리튬 2차전지
US20230063834A1 (en) Redox flow battery

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AL AM AT AU AZ BA BB BG BR BY CA CH CN CU CZ DE DK EE ES FI GB GE GH GM HU ID IL IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MD MG MK MN MW MX NO NZ PL PT RO RU SD SE SG SI SK SL TJ TM TR TT UA UG UZ VN YU ZW

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): GH GM KE LS MW SD SL SZ UG ZW AM AZ BY KG KZ MD RU TJ TM AT BE CH CY DE DK ES FI FR GB GR IE IT LU MC NL PT SE BF BJ CF CG CI CM GA GN GW ML MR NE SN TD TG

121 Ep: the epo has been informed by wipo that ep was designated in this application
REG Reference to national code

Ref country code: DE

Ref legal event code: 8642

122 Ep: pct application non-entry in european phase