WO2000050360A1 - Materiau de compensation thermique et dispositif de communication optique utilisant ce materiau - Google Patents
Materiau de compensation thermique et dispositif de communication optique utilisant ce materiau Download PDFInfo
- Publication number
- WO2000050360A1 WO2000050360A1 PCT/JP2000/000714 JP0000714W WO0050360A1 WO 2000050360 A1 WO2000050360 A1 WO 2000050360A1 JP 0000714 W JP0000714 W JP 0000714W WO 0050360 A1 WO0050360 A1 WO 0050360A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- powder
- crystal
- glass powder
- thermal expansion
- coefficient
- Prior art date
Description
Claims