Classifications

• • E—FIXED CONSTRUCTIONS
  • E04—BUILDING
  • E04C—STRUCTURAL ELEMENTS; BUILDING MATERIALS
  • E04C2/00—Building elements of relatively thin form for the construction of parts of buildings, e.g. sheet materials, slabs, or panels
  • E04C2/02—Building elements of relatively thin form for the construction of parts of buildings, e.g. sheet materials, slabs, or panels characterised by specified materials
  • E04C2/04—Building elements of relatively thin form for the construction of parts of buildings, e.g. sheet materials, slabs, or panels characterised by specified materials of concrete or other stone-like material; of asbestos cement; of cement and other mineral fibres
  • E04C2/043—Building elements of relatively thin form for the construction of parts of buildings, e.g. sheet materials, slabs, or panels characterised by specified materials of concrete or other stone-like material; of asbestos cement; of cement and other mineral fibres of plaster
• • D—TEXTILES; PAPER
  • D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
  • D21H—PULP COMPOSITIONS; PREPARATION THEREOF NOT COVERED BY SUBCLASSES D21C OR D21D; IMPREGNATING OR COATING OF PAPER; TREATMENT OF FINISHED PAPER NOT COVERED BY CLASS B31 OR SUBCLASS D21G; PAPER NOT OTHERWISE PROVIDED FOR
  • D21H19/00—Coated paper; Coating material
  • D21H19/80—Paper comprising more than one coating
  • D21H19/82—Paper comprising more than one coating superposed
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B32—LAYERED PRODUCTS
  • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
  • B32B13/00—Layered products comprising a a layer of water-setting substance, e.g. concrete, plaster, asbestos cement, or like builders' material
  • B32B13/04—Layered products comprising a a layer of water-setting substance, e.g. concrete, plaster, asbestos cement, or like builders' material comprising such water setting substance as the main or only constituent of a layer, which is next to another layer of the same or of a different material
  • B32B13/08—Layered products comprising a a layer of water-setting substance, e.g. concrete, plaster, asbestos cement, or like builders' material comprising such water setting substance as the main or only constituent of a layer, which is next to another layer of the same or of a different material of paper or cardboard
• • D—TEXTILES; PAPER
  • D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
  • D21H—PULP COMPOSITIONS; PREPARATION THEREOF NOT COVERED BY SUBCLASSES D21C OR D21D; IMPREGNATING OR COATING OF PAPER; TREATMENT OF FINISHED PAPER NOT COVERED BY CLASS B31 OR SUBCLASS D21G; PAPER NOT OTHERWISE PROVIDED FOR
  • D21H21/00—Non-fibrous material added to the pulp, characterised by its function, form or properties; Paper-impregnating or coating material, characterised by its function, form or properties
  • D21H21/14—Non-fibrous material added to the pulp, characterised by its function, form or properties; Paper-impregnating or coating material, characterised by its function, form or properties characterised by function or properties in or on the paper
  • D21H21/16—Sizing or water-repelling agents
• • D—TEXTILES; PAPER
  • D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
  • D21H—PULP COMPOSITIONS; PREPARATION THEREOF NOT COVERED BY SUBCLASSES D21C OR D21D; IMPREGNATING OR COATING OF PAPER; TREATMENT OF FINISHED PAPER NOT COVERED BY CLASS B31 OR SUBCLASS D21G; PAPER NOT OTHERWISE PROVIDED FOR
  • D21H11/00—Pulp or paper, comprising cellulose or lignocellulose fibres of natural origin only
  • D21H11/14—Secondary fibres
• • D—TEXTILES; PAPER
  • D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
  • D21H—PULP COMPOSITIONS; PREPARATION THEREOF NOT COVERED BY SUBCLASSES D21C OR D21D; IMPREGNATING OR COATING OF PAPER; TREATMENT OF FINISHED PAPER NOT COVERED BY CLASS B31 OR SUBCLASS D21G; PAPER NOT OTHERWISE PROVIDED FOR
  • D21H17/00—Non-fibrous material added to the pulp, characterised by its constitution; Paper-impregnating material characterised by its constitution
  • D21H17/03—Non-macromolecular organic compounds
  • D21H17/05—Non-macromolecular organic compounds containing elements other than carbon and hydrogen only
  • D21H17/14—Carboxylic acids; Derivatives thereof
  • D21H17/15—Polycarboxylic acids, e.g. maleic acid
  • D21H17/16—Addition products thereof with hydrocarbons
• • D—TEXTILES; PAPER
  • D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
  • D21H—PULP COMPOSITIONS; PREPARATION THEREOF NOT COVERED BY SUBCLASSES D21C OR D21D; IMPREGNATING OR COATING OF PAPER; TREATMENT OF FINISHED PAPER NOT COVERED BY CLASS B31 OR SUBCLASS D21G; PAPER NOT OTHERWISE PROVIDED FOR
  • D21H17/00—Non-fibrous material added to the pulp, characterised by its constitution; Paper-impregnating material characterised by its constitution
  • D21H17/20—Macromolecular organic compounds
  • D21H17/21—Macromolecular organic compounds of natural origin; Derivatives thereof
  • D21H17/24—Polysaccharides
  • D21H17/28—Starch
• • D—TEXTILES; PAPER
  • D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
  • D21H—PULP COMPOSITIONS; PREPARATION THEREOF NOT COVERED BY SUBCLASSES D21C OR D21D; IMPREGNATING OR COATING OF PAPER; TREATMENT OF FINISHED PAPER NOT COVERED BY CLASS B31 OR SUBCLASS D21G; PAPER NOT OTHERWISE PROVIDED FOR
  • D21H17/00—Non-fibrous material added to the pulp, characterised by its constitution; Paper-impregnating material characterised by its constitution
  • D21H17/20—Macromolecular organic compounds
  • D21H17/33—Synthetic macromolecular compounds
  • D21H17/34—Synthetic macromolecular compounds obtained by reactions only involving carbon-to-carbon unsaturated bonds
  • D21H17/37—Polymers of unsaturated acids or derivatives thereof, e.g. polyacrylates
• • D—TEXTILES; PAPER
  • D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
  • D21H—PULP COMPOSITIONS; PREPARATION THEREOF NOT COVERED BY SUBCLASSES D21C OR D21D; IMPREGNATING OR COATING OF PAPER; TREATMENT OF FINISHED PAPER NOT COVERED BY CLASS B31 OR SUBCLASS D21G; PAPER NOT OTHERWISE PROVIDED FOR
  • D21H17/00—Non-fibrous material added to the pulp, characterised by its constitution; Paper-impregnating material characterised by its constitution
  • D21H17/20—Macromolecular organic compounds
  • D21H17/33—Synthetic macromolecular compounds
  • D21H17/34—Synthetic macromolecular compounds obtained by reactions only involving carbon-to-carbon unsaturated bonds
  • D21H17/37—Polymers of unsaturated acids or derivatives thereof, e.g. polyacrylates
  • D21H17/375—Poly(meth)acrylamide
• • D—TEXTILES; PAPER
  • D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
  • D21H—PULP COMPOSITIONS; PREPARATION THEREOF NOT COVERED BY SUBCLASSES D21C OR D21D; IMPREGNATING OR COATING OF PAPER; TREATMENT OF FINISHED PAPER NOT COVERED BY CLASS B31 OR SUBCLASS D21G; PAPER NOT OTHERWISE PROVIDED FOR
  • D21H17/00—Non-fibrous material added to the pulp, characterised by its constitution; Paper-impregnating material characterised by its constitution
  • D21H17/20—Macromolecular organic compounds
  • D21H17/33—Synthetic macromolecular compounds
  • D21H17/34—Synthetic macromolecular compounds obtained by reactions only involving carbon-to-carbon unsaturated bonds
  • D21H17/41—Synthetic macromolecular compounds obtained by reactions only involving carbon-to-carbon unsaturated bonds containing ionic groups
  • D21H17/42—Synthetic macromolecular compounds obtained by reactions only involving carbon-to-carbon unsaturated bonds containing ionic groups anionic
  • D21H17/43—Carboxyl groups or derivatives thereof
• • D—TEXTILES; PAPER
  • D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
  • D21H—PULP COMPOSITIONS; PREPARATION THEREOF NOT COVERED BY SUBCLASSES D21C OR D21D; IMPREGNATING OR COATING OF PAPER; TREATMENT OF FINISHED PAPER NOT COVERED BY CLASS B31 OR SUBCLASS D21G; PAPER NOT OTHERWISE PROVIDED FOR
  • D21H19/00—Coated paper; Coating material
  • D21H19/10—Coatings without pigments
  • D21H19/14—Coatings without pigments applied in a form other than the aqueous solution defined in group D21H19/12
  • D21H19/24—Coatings without pigments applied in a form other than the aqueous solution defined in group D21H19/12 comprising macromolecular compounds obtained otherwise than by reactions only involving carbon-to-carbon unsaturated bonds
  • D21H19/32—Coatings without pigments applied in a form other than the aqueous solution defined in group D21H19/12 comprising macromolecular compounds obtained otherwise than by reactions only involving carbon-to-carbon unsaturated bonds obtained by reactions forming a linkage containing silicon in the main chain of the macromolecule
• • D—TEXTILES; PAPER
  • D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
  • D21H—PULP COMPOSITIONS; PREPARATION THEREOF NOT COVERED BY SUBCLASSES D21C OR D21D; IMPREGNATING OR COATING OF PAPER; TREATMENT OF FINISHED PAPER NOT COVERED BY CLASS B31 OR SUBCLASS D21G; PAPER NOT OTHERWISE PROVIDED FOR
  • D21H19/00—Coated paper; Coating material
  • D21H19/36—Coatings with pigments
  • D21H19/38—Coatings with pigments characterised by the pigments
• • D—TEXTILES; PAPER
  • D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
  • D21H—PULP COMPOSITIONS; PREPARATION THEREOF NOT COVERED BY SUBCLASSES D21C OR D21D; IMPREGNATING OR COATING OF PAPER; TREATMENT OF FINISHED PAPER NOT COVERED BY CLASS B31 OR SUBCLASS D21G; PAPER NOT OTHERWISE PROVIDED FOR
  • D21H19/00—Coated paper; Coating material
  • D21H19/80—Paper comprising more than one coating
  • D21H19/84—Paper comprising more than one coating on both sides of the substrate
• • D—TEXTILES; PAPER
  • D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
  • D21H—PULP COMPOSITIONS; PREPARATION THEREOF NOT COVERED BY SUBCLASSES D21C OR D21D; IMPREGNATING OR COATING OF PAPER; TREATMENT OF FINISHED PAPER NOT COVERED BY CLASS B31 OR SUBCLASS D21G; PAPER NOT OTHERWISE PROVIDED FOR
  • D21H27/00—Special paper not otherwise provided for, e.g. made by multi-step processes
  • D21H27/30—Multi-ply
• • D—TEXTILES; PAPER
  • D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
  • D21H—PULP COMPOSITIONS; PREPARATION THEREOF NOT COVERED BY SUBCLASSES D21C OR D21D; IMPREGNATING OR COATING OF PAPER; TREATMENT OF FINISHED PAPER NOT COVERED BY CLASS B31 OR SUBCLASS D21G; PAPER NOT OTHERWISE PROVIDED FOR
  • D21H27/00—Special paper not otherwise provided for, e.g. made by multi-step processes
  • D21H27/30—Multi-ply
  • D21H27/38—Multi-ply at least one of the sheets having a fibrous composition differing from that of other sheets

Definitions

• the present invention relates to a paper liner for plasterboard, a method for making plasterboard and a plasterboard product.
• the plasterboard product is especially a decorative plasterboard panel.
• Plasterboard also widely referred to as gypsum board, is widely used in the building and construction industry. Plasterboard finds especially wide use as an internal wall cladding and ceiling infill material.
• a gypsum slurry is cast between top and bottom paper liner sheets and dried in a kiln to convert the gypsum slurry to CaS0 4 .2H 2 0.
• the drying process requires removal of water from the slurry. As the slurry is essentially completely encased in the paper, the water that is removed from the slurry during drying must pass through the paper liner sheets.
• the paper in addition to having sufficient strength to support the gypsum paper, the paper must also be sufficiently permeable to allow water or water vapor to pass therethrough during drying at a sufficient rate to ensure that acceptable drying rates are achieved.
• the paper liner used in plasterboard manufacture has a gypsum side and an external side in the final plasterboard product.
• the gypsum side of the paper liner is conventionally coated during it manufacture with a silicone or polysiloxane containing agent prior to casting of the gypsum slurry.
• the silicone or polysiloxane containing agent strengthens the adhesion between the gypsum and the liner in the plasterboard product.
• the plasterboard product also has two external faces, with the external faces comprising the respective external faces of the two paper liner sheets.
• plasterboard will, in use, face into a room and accordingly provides a visible surface. Therefore, the appearance of this surface is somewhat more important. Plasterboard almost invariably is manufactured such that this external surface has a fairly dull colour that darkens with age. However, this surface does accept a paint coating or wallpaper and such steps have traditionally been used to obtain an aesthetically pleasing appearance in the completed building.
• AU 19322/92 The paper described in AU 19322/92 is coated with a pigment layer. Although the patent application states that the paper provides "durable aesthetic qualities", the application unambiguously states that the coated paper is in turn intended to be coated with a decorative layer, for example, of wallpaper or of paint. Accordingly, AU 19322/92 does not provide a long-term solution to providing a plasterboard that has acceptable aesthetic appearance without requiring painting or wallpapering.
• the paper described in AU 19322/92 includes a top ply that is made from bleached, predominantly chemical, cellulose fibers and a light coloured, preferably white, inorganic filler.
• the paper is coated with a coating that includes at least one light-coloured (preferably white) inorganic filler and at least one binder, together with other adjuvants.
• the coating is applied at a rate of 6 g/m 2 , more preferably 8- 30 g/m 2 .
• the permeability of the coated paper is generally higher than 100 sec (Gurley) and is more generally of the order of 150 sec (Gurley).
• AU 19322/92 requires that the amount of unbleached - 3 - chemical pulps, thermomechanical pulps, semichemical pulps and mechanical pulps in the top ply be held to less than 30% and that the pulp in the top ply be predominantly bleached pulp.
• Ceilings in office buildings and other commercial buildings frequently comprise "hanging ceilings" in which a supporting structure is hung from the roof or the floor above and infill panels are supported by the supporting structure. Such ceilings allow sufficient space for electrical cabling, plumbing and air-conditioning ducts to be placed whilst providing a pleasing appearance that hides the building services running above the ceiling.
• the ceiling infill panels are commonly made from fibrous lightweight materials and present a speckled appearance.
• the present invention provides a paper liner for a plasterboard including a base paper having a surface size applied to one surface thereof, the surface size including oxidized starch, wood rosin and cationic styrene/acrylic esters co-polymer, a sizing agent selected from alkenyl succinic anhydride, succinic acid anhydride, wood rosin, alkyl ketene dimer and mixtures thereof, and an acrylic-containing polymer, said paper further including a coating applied to the one surface thereof, said coating including at least one inorganic filler and at least one binder.
• the base paper used in the present invention preferably comprises a multiply paper, more preferably a three-ply paper.
• the base is preferably of relatively low grammage, such as 160-180 g/m 2 .
• the top ply of the base paper may be made from white deinked pulp, for example, white deinked pulp obtained from recycling of newsprint and waste office paper. Other pulps may be used in the manufacture of the top ply, including white quality unprinted waste paper, chemical bleached - 4 - cellulose fibres and optionally bleached mechanical, CMP, TMP and CTMP cellulose fibres.
• the base paper should have sufficient porosity to render it suitable for use in the manufacture of gypsum board.
• the base paper preferably has a porosity in the range of 18-28 sec, determined in accordance with Australian Standard 1301.4205-89 for the Gurley air permeance of paper. This test measures the time in seconds required for 100ml of air at specified conditions to permeate through the paper. For convenience, this test will hereinafter be referred to as "Gurley".
• the base paper should also have sufficient strength for gypsum board manufacture and its end uses.
• An especially preferred base paper has the following properties: Thickness: 300 ⁇ 6 ⁇ m
• Machine Direction (MD) 10.0 - 10.3 kN/m
• the base paper is preferably at least two ply, more preferably three ply.
• the base paper preferably includes an inorganic filler and a cationic acrylamide copolymer. These components are added to the pulp suspension used to manufacture at least the top ply of the base paper and preferably to all plies and become incorporated into the base paper. These components control the porosity and density of the paper.
• the inorganic filler may be bentonite clay such as hydrocol HSI or hydrocol ONZ, both manufactured by Allied Colloids.
• the cationic acrylamide copolymer may be NALCO 7541 manufactured by Nalco or PERCOL 47 or PERCOL 57, both manufactured by Allied Colloids.
• the paper liner in accordance with the present invention is intended to have a gypsum side and a decorative side.
• the base paper has an external surface size applied to one surface thereof and a coating also applied to that surface. That - 5 - surface of the paper liner is intended to be the decorative side of the plasterboard. For convenience, this surface will hereinafter be referred to as “the decorative surface” or “the decorative side” of the paper liner.
• the external surface size applied to the decorative surface of the base paper controls the distance that the coating penetrates into the paper. This is important for controlling the void area (porosity) of the final paper liner.
• the external surface size includes three main components, which may be identified broadly as oxidized starch, a sizing agent and an acrylic-containing polymer.
• the three main components of the external surface size may be applied sequentially, with the starch being applied first, followed by the sizing agent and then the acrylic-containing copolymer.
• the three main components may be mixed to form a sizing composition and the sizing composition applied to the paper at one location.
• the oxidized starch is preferably oxidized wheaten starch. Sizing with oxidized starch assists in improving the strength of the base paper which in turn provides increased strength to the plasterboard. Increased plasterboard strength is desirable to minimise or prevent sagging of the plasterboard during use. Furthermore, the thickness of the plasterboard may be minimised.
• the oxidized starch has preferably a balance between film forming and sheet penetration properties. When the coating is applied, it can migrate just sufficiently to form a bond with the paper.
• degree of oxidation of the starch may be an important parameter in the present invention, although further work is required to confirm this.
• a degree of oxidation equivalent to oxidizing the starch with 0.18 to 0.40% wt of ammonium persulphate, more preferably 0.18 to 0.35% wt of ammonium persulphate (calculated as a weight percentage on the weight of starch) is especially preferred.
• the original starch may have a particle size in the range of 2 to lOO ⁇ m.
• Cis alkenyl succinic anhydride Such compounds have been widely used as paper sizing agents and need not be described further.
• a suitable alkenyl succinic anhydride is NALSIZE 7540, manufactured by Nalco.
• alkenyl succinic anhydride it is preferred that an acrylamide copolymer is also included in the sizing composition.
• the acrylamide copolymer is preferably added in colloidal form and it acts to aid emulsion formation, as a protectant and retention aid to the alkenyl succinic anhydride.
• Alkyl ketene dimer and wood rosin may also be used as the sizing agent. Both are well known paper sizing agents and need not be described further.
• a suitable wood rosin is DSPC4 manufactured by Hercules.
• a suitable alkyl ketene dimer is KEYDIME C100 manufactured by Eka Nobel.
• the external surface size includes an acrylic-containing copolymer. This is preferably a cationic styrene/acrylic ester copolymer, for example, the product sold under the trade name Baysynthol manufactured by Bayer.
• the components of the external surface size are preferably added in the following amounts, based upon a base paper of nominal grammage of 170 g/m : Oxidized starch: 3 - 4% on total mass
• Acrylic containing polymer 1.3g/m
• the external surface sizing up is preferably applied to the paper as a mixed composition. It is preferably applied to the paper on the paper machine during manufacture.
• the paper that comes off the paper making machine preferably has the external surface sizing applied to the decorative side of the paper.
• the decorative side of the paper preferably has a brightness of about 60 ISO brightness units at this stage. - 7 -
• the back of the paper may be surface sized with a silicone or polysiloxane sizing agent.
• silicone or polysiloxane sizing agent The person skilled in the art of plasterboard manufacture would readily appreciate which silicone/polysiloxane surface agents would be suitable.
• One suitable agent is RE29 silicone/polysiloxane manufactured by Union Carbide.
• the decorative side of the paper has a coating applied thereto.
• the coating may be described as a light weight, open coating of 7-l lg/m 2 .
• the coating comprises at least one inorganic filler and at least one binder.
• the inorganic fillers are preferably of or include a fraction of a relatively large particle size.
• the coating is preferably of high alkalinity. More preferably the coating composition has a pH of at least 8.5.
• the inorganic fillers may comprise a mixture of different inorganic fillers.
• the inorganic fillers may include calcium carbonate, clay, aluminium silicate, calcined clay and titanium dioxide.
• the inorganic fillers comprises a mixture of large particle sized precipitated calcium carbonate, aluminium silicate and clay, and titanium dioxide.
• the calcium carbonate preferably is sized such that most of the particles of calcium carbonate fall within the range of 10-40 ⁇ m.
• the aluminium silicate is preferably sized such that most of the particles of aluminium silicate fall within the range of 10-40 ⁇ m.
• the calcined clay particles are sized such that most of the particles fall within the range of 2-10 ⁇ m.
• the titanium dioxide is a very fine powder and has particles largely sized within the range of 0.1 -0.3 ⁇ m.
• the coating that is applied to the decorative side of the paper tends to decrease the permeability of the paper.
• the coated paper has to at least be able to "sweat" which thereby allows removal of at least some water from the drying gypsum slurry through the decorative side of the plasterboard.
• the amount of very fine inorganic filler particles should be minimized as the fine particles tend to fill the interstitial spaces in the coating thus forming a closed coating which has low permeability.
• binders are used. These binders may include styrene butadiene latex, polyvinyl acetate and acrylic latex.
• the coating is preferably applied to the decorative side of the paper by mixing the inorganic filler and the binder to form a coating composition and thereafter applying the coating composition to the paper.
• Coating may be achieved by use of a rod or air knife or trailing blade coater that has a gloss calendar.
• the applied coating may be dried by infra-red dryers, such as gas fired infra-red dryers.
• the coated paper provides a paper liner that has a coating on the decorative side that presents an attractive aesthetic appearance. Moreover, the coating has a low tendency to yellow or discolour over time and it presents a washable surface such that dust and smoke deposits can be removed therefrom.
• the coated paper also shows some permeability to water and allows water to sweat therethrough, which allows at least some water to be removed from the decorative side during drying in plasterboard manufacture .
• the decorative surface of the paper liner is printed with a pattern to further improve its appearance.
• Flexoprinting may be used to print the pattern, utilizing flexographic ink of improved light fastness.
• the printing may result in a speckled pattern being applied to the decorative surface of the paper liner such that, if the plasterboard is used as a ceiling infill panel, the panel has an appearance similar to the speckled appearance of conventional ceiling infill panels.
• Other patterns or designs may also be printed onto the decorative side of the paper liner.
• the present invention provides a unique solution to providing plasterboard having a decorative appearance.
• the present invention instead provides a paper liner that is coated and optionally printed and that provides a durable, washable decorative surface that does not require painting or wallpapering.
• the external surface size and coating on the decorative side surprisingly allow sufficient water permeability to let water permeate through the - 9 - decorative side and permit at least a degree of water removal through the decorative side of the plasterboard during the drying step in plasterboard manufacture. This has not herebefore thought to be possible.
• the present invention provides a method for producing a paper liner for plasterboard including the steps of applying an external surface sizing as hereinbefore described to a base paper and subsequently applying a coating as hereinbefore described to the paper.
• the method preferably further includes the step of printing a pattern onto the coated surface of the paper.
• the present invention also includes a method for producing plasterboard.
• the present invention provides a method for producing plasterboard including the steps of casting gypsum slurry between two liner sheets of paper and drying the slurry, wherein one of the liner sheets of paper comprises a paper liner as described herein.
• the other of the liner sheets of paper comprises the base paper used in the paper liner described herein.
• the liner sheet that comprises the paper liner as described herein will comprise the decorative side of the plasterboard.
• This liner has reduced permeability to water vapor and water but has sufficient permeability to enable water to sweat therethrough. Accordingly, at least some drying will occur through this paper liner.
• the other liner sheet may be the base paper described herein or any other high porosity paper suitable for use in the manufacture of plasterboard. In practice, a greater portion of drying will take place through this sheet.
• the drying rate of the plasterboard may have to be adjusted downwards in order to account for the reduced permeability of the decorative side paper liner. Simple trial will establish the required drying rate. The present inventors have found that satisfactory drying rates are able to be obtained in the method for producing plasterboard in accordance with the present invention.
• the invention also extends to encompass plasterboard produced in accordance with the method described above.
• the invention also encompasses plasterboard having a decorative side comprising a paper liner as described herein in accordance with the first aspect of - 10 the present invention.
• the decorative side does not require further processing to provide a suitable aesthetic appearance. In particular, painting or wallpapering is not required.
• the decorative side of the paper liner may have a brightness of 70-90 ISO brightness units.
• the decorative side accepts printing, especially flexoprinting, and presents a washable durable, colorfast surface.
• the coated and printed paper liner also has sufficient permeability to enable it to be used in the manufacture of plasterboard. This is due to the "open" coating that has been applied to the paper liner.
• Example 1 Specific embodiments of the present invention will now be described with reference to the following Examples. It will be appreciated that if Examples are intended to illustrate the present invention they should not be construed as limiting the present invention in any way.
• Example 1
• a 3 -ply sheet of paper was manufactured from deinked white office waste, corrugated waste, old corrugated cartons and selected brown waste. The following fillers/chemicals were added to the paper:
• An external surface size was applied to the top ply.
• This size included oxidized starch having 7% solids at size press oxidized by addition of 0.20-0.28%) ammonium persulphate.
• the starch was added to the paper in an amount of 25-40 kg/tonne.
• the size also included Baysynthol at l-2kg/tonne and alkenyl succinic acid (top ply -4.5kg/T, middle ply -4kg/T, back ply -5kg/T).
• a coating of inorganic fillers and binder was applied and the coated paper was flexoprinted. - 11 -
• the paper was used as one sheet in plasterboard manufacture and an acceptable plasterboard product was produced using a drying rate of 3.2kg H 2 0/m 2 /hr.
• Example 2
• a commercial run was carried out on a 3 ply paper machine to produce base paper for coating in order to make printable marketable gypsum board for ceiling in fills.
• the paper line was set to make convention plasterboard liner utilizing 100% deinked waste on the top ply and other conventional paper stock brown and mixed whites on the other plies. After the line is running, adjustment of the bentonite clay and cationic acrylamide occurs at the wet end of the paper machine.
• the rates of addition to T-top ply, M-middle ply and B-bottom ply are percol 57 (acrylamide) T-50-100g/t, M-300-500g/t, B-400-600g/t, hydrocol ONZ T-nil, M- 2.6kg/t, B-2.6kg/t.
• the initial paper is comprised of alkenyl succinic anhydride (nalco 7540) internally sized with the addition of cationic acrylamide (nalco 7541) at T-4.5kg/t, M-4kg/t, B-5.0kg/t.
• the change to process occurs at the size press where on the back of the sheet (the gypsum combining side) has silicone emulsion RE29 applied at 7.6kg/t and to the face or top side, the decorative side, oxidized starch 25-40kg/t together with wood rosin and cationic styrene/acrylic esters copolymer (Baysynthol) l-2kg/tonne is applied.
• the paper so formed are more porous and give up water by drainage and drying more readily than conventional plasterboard liner encasting sheets and the surface sizing of the paper allows the desired surface for the next process step i.e. coating.
• the off machine base sheet was then cut in two widths one width to suit subsequent backpaper for the gypsum board process and another width for the coater. Thence the face paper for gypsum board production.
• the face paper web was coated on its proposed decorative surface through a rod/airknife/rod coater that has a gross calendar. Both rod/air knife at coating weight of 12-18g/m 2 and air knife only coatings (8-l lg/t) were produced.
• the coater is a standard coater manufactured by Kohler and has gas fired infrared dryers after each coating station.
• the coating kitchen is of standard design and has standard equipment for preparation of coating mixes for rod air knife coaters desired for both flexographic and lithographic printing processes. 12 -
• a typical coating mix for flexographic printing is:
• the paper once coated is suitable for quality flexographic printing and is porous enough to be able to be used as face paper on a conventional gypsum board line and poses little drying problems.
• a gypsum board was produced on a conventional gypsum wallboard line using natural gypsum at 11 metres per minute.
• Standard known chemical additives were used with the stucco namely BGA, potash, boric acid, durasar, soap, starch and retarder. Liquid/plaster ratio of 85-89% and slump measurements of 95-105 were recorded.
• Drying was carried out in a two stage conventional gypsum board dryer and a drying rate of 3.2kg of H 2 0/m /hr was achieved.
• Bevaloid 211 Polycarboxylic Acid (Rhone-Poulenc) Bevaloid 6681 - Proprietary Mineral Oil
• Tioxide RHD-2 Titanium Dioxide (Tioxide Australia)

Priority Applications (4)

Applications Claiming Priority (4)

Publications (1)

Family

ID=25645770

Family Applications (1)

Country Status (5)

Cited By (16)

Families Citing this family (4)

Citations (3)

• 1999
  • 1999-05-03 TW TW088107166A patent/TW459084B/zh not_active IP Right Cessation
  • 1999-05-04 JP JP2000547313A patent/JP2002513873A/ja active Pending
  • 1999-05-04 KR KR1020007012201A patent/KR20010043253A/ko not_active Application Discontinuation
  • 1999-05-04 EP EP99916717A patent/EP1090184A4/en not_active Withdrawn
  • 1999-05-04 WO PCT/AU1999/000324 patent/WO1999057371A1/en not_active Application Discontinuation

Patent Citations (3)

Non-Patent Citations (2)

Also Published As

Similar Documents

Legal Events