Classifications

• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F10/00—Homopolymers and copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F10/00—Homopolymers and copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond
  • C08F10/02—Ethene
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
  • C08L23/00—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers
  • C08L23/02—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers not modified by chemical after-treatment
  • C08L23/04—Homopolymers or copolymers of ethene
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
  • C08L23/00—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers
  • C08L23/02—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers not modified by chemical after-treatment
  • C08L23/04—Homopolymers or copolymers of ethene
  • C08L23/06—Polyethylene
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F110/00—Homopolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond
  • C08F110/02—Ethene
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
  • C08L2203/00—Applications
  • C08L2203/16—Applications used for films
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
  • C08L2203/00—Applications
  • C08L2203/18—Applications used for pipes
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
  • C08L2205/00—Polymer mixtures characterised by other features
  • C08L2205/02—Polymer mixtures characterised by other features containing two or more polymers of the same C08L -group
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
  • C08L2314/00—Polymer mixtures characterised by way of preparation
  • C08L2314/02—Ziegler natta catalyst
• • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
  • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
  • Y10S—TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
  • Y10S526/00—Synthetic resins or natural rubbers -- part of the class 520 series
  • Y10S526/901—Monomer polymerized in vapor state in presence of transition metal containing catalyst

Definitions

• Olefin polymerization catalyst component its preparation and use
• the invention relates to a process for the preparation of a high activity catalyst component for the production of olefin polymers.
• the invention also relates to a procatalyst prepared by said process and the use of such a procatalyst in the polymerization of olefins.
• Olefinic unsaturated monomers such as ethylene can often be polymerized in the presence of a catalyst composition, which has essentially two components: a compound of a transition metal belonging to one of groups 4 to 6 of the Periodic Table of Elements (Hubbard, IUPAC 1990) which is often called a procatalyst, and a compound of a metal belonging to any of groups 1 to 3 of said Table which is often called a cocatalyst.
• This kind of Ziegler-Natta catalyst composition has been further developed by depositing the procatalyst on a more or less inert and particulate support and by adding to the catalyst composition in the stages of its preparation several additives, among others electron donating compounds. These compounds have improved the polymerization activity of the catalyst, the operating life and other properties of the catalyst composition and first of all properties of the polymers which are obtained by means of the catalyst composition.
• the polymer molecules formed are not similar by molecular weight, but a mixture having a narrow or broad molecular weight distribution is developed.
• the broadness of the molecular weight distribution may be described by utilization of the ratio of two different averages, namely the weight average molecular M w and the number average molecular weight M n , where a high value of M w /M n indicates a broad molecular distribution.
• a so called chain transfer agent can be added to the polymerization reaction mixture.
• different amounts of the chain transfer agent for controlling the molecular weight must be fed into the polymerization reaction mixture.
• the most usual and preferable chain transfer agent is hydrogen, because when using it no foreign atoms or atom groups are left in the growing molecule, that would cause inconveniencies for the polymerization process or disadvantageous properties of the polymer produced. How well the molecular weight of the produced polymer varies as function of the hydrogen amount, i.e. how much the so called hydrogen sensibility changes, greatly depends on the catalyst composition. Generally the problem is, that in polyethylene production the polymerization activity decreases to quite an extent the more hydrogen is present.
• the activity balance discussed above is important in production of bimodal polyethylene. There, a low molecular weight component is produced in one stage at a high hydrogen concentration and a high molecular weight component is produced in another stage at a low hydrogen concentration. Since no fresh catalyst is added between these polymerization stages, the catalyst employed in production of bimodal polyethylene must be able to produce the different molecular weights with a high productivity.
• EP-A-32307 discloses a procatalyst that has been prepared by treating an inorganic support like silica with a chlorination agent like ethyl aluminium dichloride which support is then contacted with a magnesium alkyl compound like butyl ethyl magnesium, and with titanium tetrachloride (see claim 1, example 1, table 1).
• WO-A-96/05236 discloses a catalyst component comprising (i) a particulate support where the majority of particles is in the form of an agglomerate of subparticles and (ii) a magnesium halide.
• the publication discusses the preparation of the support material. It also describes catalyst preparation and polymerization examples. The catalyst is prepared by adding titanium tetrachloride and DEAC on the agglomerated carrier containg magnesium chloride. The polymerization examples show that a higher bulk density and a higher MFR (better hydrogen response) as well as a lower FRR (narrower molecular weight distribution) is obtaines by the catalyst prepared according to the disclosure.
• the publication does no refer to the homogeneity of the material.
• EP-A-688 794 discloses a process for the preparation of a high activity procatalyst, wherein an inorganic support is reacted with an alkyl metal chloride, the first reaction product is reacted with a compound containing hydrocarbyl and hydrocarbyl oxide linked to magnesium, and the obtained second reaction product is contacted with a titanium chloride compound.
• the obtained procatalyst has good activity both at high and low MFR polymerization conditions, but it has the drawback of giving an inhomogeneous ethylene polymer product, resulting in gels and white spots in the polymer material. These inhomogenities have detrimental effect on the appearance and mechanical properties of polyethylene film.
• R is a C1-C20 alkyl or a C7-C26 aralkyl, each same or different X is a halogen, and n is an integer 1 or 2,
• M is B or Al
• each same or different Rl is a CJ-CJO alkyl
• each same or different X* is a halogen
• n is 1 or 2 when m l is 1 and nl is an integer from 1 to 5 when ml is 2
• magnesium composition containing magnesium bonded to a hydrocarbyl and magnesium bonded to a hydrocarbyl oxide, said magnesium composition having the empirical formula (3):
• each same or different R2 is a C1-C2O alkyl
• each same or different R ⁇ is a C1 -C20 alkyl or a C -C20 alkyl containing a hetero element
• n2 is between 0.01 and 1.99
• each same or different R is a C1-C20 alkyl
• each same or different ⁇ 2 is a halogen
• n ⁇ is 0 or an integer 1-3
• Ti is quadrivalent titanium
• the inorganic support may be coated by MgCl2 or RoMgCl.
• n is 1 or 2.
• magnesium composition a mixture or a compound.
• formula (3) is an empirical formula and expresses the molar amounts of alkyl R and alkoxy OR- relative to the amount of magnesium Mg, which has been defined as 1, and differs from formulas (1), (2) and (4), which disclose the molecular composition of distinct compounds only.
• a procatalyst has now been discovered by which ethylene homopolymers or copolymers having low or high molecular weights can be produced with an even and high activity as well as a homogeneous consistence. Independently of the amount of hydrogen introduced into the polymerization reactor, the activity of the catalyst remains more or less unchanges and a homogeneous ethylene polymer product is obtained.
• the unique feature of the catalyst according to the invention now lies over its good balance in activity and a homogeneous product in a very wide range of molar mass regulating hydrogen partial pressures used in the polymerization. It is thus possible to carry out an ethylene polymerization by the use of this catalyst at high and low melt flow and still have very similar high productivity as well as a homogeneous, gel free product.
• This MFR/activity balance renders the catalyst universally applicable for most types of PE resins in all polymerization processes using heterogeneous catalyst systems.
• the claimed process comprises the subsequent steps of:
• the support used in the process is preferably in the form of particles, the size of which is from about 1 ⁇ m to about 1000 ⁇ m, preferably about 10 ⁇ m to about 100 ⁇ m.
• the support material must have a suitable particle size distribution, a high porosity and a large specific surface area. A good result is achieved if the support material has a specific surface area between 100 and 500 m 2 /g support and a pore volume of 1-3 ml/g support.
• catalyst components (2) to (4) are reacted with a suitable catalyst support. If the catalyst components (2) to (4) are in the form of a solution of low viscosity, a good catalyst morphology and therewith a good polymer morphology can be achieved.
• R is a -C 20 alkoxy or a C 7 -C 26 aralkoxy.
• said compound (1) is a magnesium dihalide, most preferably MgCl2.
• the support may comprise solid MgCi2, either alone as a powder, or as a powder mixture with other inorganic powders.
• the support comprising a magnesium halide compound having the formula (1) also comprises an inorganic oxide.
• an inorganic oxide Several oxides are suitable, but silicon, aluminium, titanium, chromium and zirconium oxide or mixtures thereof are preferred.
• the most preferred inorganic oxides are silica, alurnina, silica-alumina, magnesia and mixtures thereof, uttermost preferably silica.
• the inorganic oxide can also be chemically pretreated, e.g. by silylation or by treatment with aluminium alkyls.
• the support comprises particles having a core comprising said inorganic oxide and a shell comprising said magnesium halide compound having the formula (1).
• the support comprising a magnesium halide compound having the formula (1) and an inorganic oxide can conveniently be prepared by treating particles of the inorganic oxide with a solution of the magnesium halide and removing the solvent by evaporation.
• the amount of magnesium halide compound (1) is such that the support contains from 1 to 20 % by weight, preferably from 2 to 6 % by weight, of magnesium.
• the invention further comprises a step of reacting an alkyl metal halide compound of the formula (2):
• Me is preferably Al.
• Each same or different R! is preferably a Ci -C ⁇ alkyl, and, independently, the preferred same or different halogen ⁇ l is chlorine, nl is preferably 1 and ml is preferably the integer 1 or 2.
• the alkyl metal halide compound having the formula (2) is an alkyl aluminium dichloride, e.g. ethyl aluminium dichloride (EADC).
• the alkyl metal halide compound is preferably deposited on the support material.
• An even deposition is preferably achieved if the viscosity of the halide or its solution is below 10 mPa*s at the temperature applied.
• the alkyl metal halide can be diluted by a non-polar hydrocarbon.
• the best deposition is however achieved if the total volume of the absorbed alkyl metal halide solution is not exceeding the pore volume of the support.
• a good choice is to use a 5-25% hydrocarbon solution of ethyl aluminium dichloride.
• step b) can advantageously be performed so that undiluted alkyl metal halide (2) is used to treat the support comprising a magnesium halide compound having the formula (1).
• the support is contacted with a solution of the alkyl metal halide compound having the formula (2) in an essentially non-polar solvent, preferably a non-polar hydrocarbon solvent, most preferably a C 4 -C 10 hydrocarbon.
• the concentration of the alkyl metal halide compound having the formula (2) in said non-polar solvent is usually 1-80% by weight, preferably 5-40% by weight, most preferably 10-30% by weight.
• the support is contacted with a solution of said alkyl metal halide compound (2) in a ratio mol of the alkyl metal halide compound (2) to grams of the support of between about 0.01 mmol/g and about 100 mmol/g, preferably between about 0.5 mmol/g and about 2.0 mmol/g.
• the amount of reactants can also be expressed as molar ratio, whereby it is advantageous, if the molar ratio of said alkyl metal halide compound (2) to said magnesium halide compound (1) of the support is between about 0.01 mol/mol to about 100, preferably about 0.1 mol/mol to about 10, most preferably from about 0.2 to about 3.0.
• the temperature at said contacting is e.g. 5-80 °C, preferably 10-50 °C, most preferably 20-40°C.
• the duration of said contacting is 0.1-3 h, preferably 0.5- 1.5 h.
• the magnesium composition containing magnesium bonded to a hydrocarbyl and magnesium bonded to a hydrocarbyl oxide and having the empirical formula (3) each same or different R2 is preferably a C j-Cio alkyl, most preferably a C2-C8 alkyl.
• Each same or different R ⁇ is preferably a C3-C20 alkyl, more preferably a branched C4-C10 alkyl, most preferably a 2-ethyl-l-hexyl or a 2- propyl-1-pentyl.
• the magnesium composition containing magnesium bonded to a hydrocarbyl and magnesium bonded to a hydrocarbyl oxide having the empirical formula (3) can also be defined by its preparation. According to one embodiment of the invention, it is a contact product of a dialkyl magnesium having the formula (5):
• dialkyl magnesium having the formula (5) is dibutyl magnesium, butyl ethyl magnesium or butyl octyl magnesium. 8
• the magnesium composition can thus be defined in that the magnesium composition containing magnesium bonded to a hydrocarbyl and magnesium bonded to a hydrocarbyl oxide having the empirical formula (3) is a contact product of a dialkyl magnesium and an alcohol having the formula (6):
• the alcohol having the formula (6) is a 2-alkyl alkanol, most preferably 2-ethyl hexanol or 2- propyl pentanol. It has been found that such branched alcohols give better results than linear alcohols.
• the magnesium composition containing magnesium bonded to a hydrocarbyl and magnesium bonded to a hydrocarbyl oxide having the empirical formula (3) is a contact product of a dialkyl magnesium and an alcohol in a molar ratio alcohol to dialkyl magnesium of 0.01-100 mol/mol, preferably 1.0-5.0 mol/mol, more preferably 1.7-2.0 mol/mol, most preferably 1.8-1.98 mol/mol.
• the dialkyl magnesium and the alcohol are conveniently contacted by adding the alcohol to a solution of said dialkyl magnesium in an organic solvent, e.g. a C -C 10 hydrocarbon. Then, the concentration of the solution is preferably between 1 and 50% by weight, most preferably between 10 and 30% by weight.
• the contacting temperature between the dialkyl magnesium and the alcohol is preferably 10-50 °C, more preferably from about 20 °C to about 35 °C.
• said first product is contacted with said magnesium composition (3) in a ratio moles of magnesium/g of the support of between 0.001-1000 mmol/g, preferably 0.01-100 mmol/g, most preferably 0.1-10 mmol/g (g of the support means, in the case of said first reaction product, the support which was used as starting material for the first reaction product).
• a good deposition of said magnesium composition as a solution is achieved if the volume of the magnesium composition (3) solution is about two times the pore volume of the support material. This is achieved if the concentration of the composition in a hydrocarbon solvent is between 5-60% in respect of the hydrocarbon used.
• its hydrocarbon solution should have a viscosity that is lower than 10 mPa*s at the temperature applied.
• the viscosity of the magnesium complex solution can be adjusted for example by the choice of the group R 4 in the formula (3), by the choice of the concentration of the hydrocarbon solution, by the choice of the ratio between the magnesium alkyl and the alcohol or by using some viscosity lowering agent.
• the titanium compound can be added to the support material with or without a previous drying of the catalyst to remove the volatile hydrocarbons. Remaining hydrocarbons can if desired be removed by using slight underpressure, elevated temperature or nitrogen flash.
• the transition metal compound is a titanium halide compound having the formula (4).
• R4 is preferably a C2-C8 alkyl, most preferably a C2-C6 alkyl.
• ⁇ 2 is preferably chlorine and, independently, n 3 is preferably 0.
• Said titanium halide compound having the formula (4) is advantageously titanium tetra- chloride.
• a titanium compound having the formula (7) in addition to said titanium compound having the formula (4), a titanium compound having the formula (7):
• each same or different R ⁇ is a C -C20 alkyl, preferably a C2-C8 alkyl, most preferably a C2-C6 alkyl, each same or different X 3 is a halogen, preferably chlorine, n ⁇ is an integer 1-4, and Ti is quadrivalent titanium, is reacted.
• the titanium compound (7) always has at least one alkoxy group, which helps dissolving the titanium compound (4) which does not necessarily contain alkoxide, into an organic solvent before the contacting. Naturally, the more alkoxide groups compound (4) has, the less is the need for compound (7). If compound (7) is used, the preferable combination is that of titanium tetrachloride and a titanium tetra Ci-C -alkoxide.
• step d) of the preferred step sequence a) ⁇ - d) said second product is advantageously contacted with the titanium compound having the formula (4) in a ratio moles of said titanium compound/g of the support of 0.01-10 mmol/g, preferably 0.1-2 mmol/g.
• said second reaction product is contacted with said titanium compound (4) in a ratio moles of said titanium compound (4)/moles of the magnesium compound (3) of 0.05-2 mol/mol, preferably 0.1-1.2 mol/mol, most preferably 0.2-0.7 mol/mol.
• the temperature is usually 10-80 °C, preferably 30- 10
• the contacting time is usually 0.5-10 h, preferably 2-8 h, most preferably from about 3.5 h to about 6.5 h.
• the invention also relates to such a high activity catalyst component.
• the suitability for both low and high molecular weight polymerization means, that the claimed catalyst component has high activity both when producing low melt flow rate ethylene polymer and high melt flow rate polymer.
• High molecular weight polymer has high melt viscosity, i.e. low melt flow rate, and low molecular weight polymer has low melt viscosity, i.e. high melt flow rate.
• ethylene homopolymer and copolymer with low gel content preferably produces ethylene homopolymer having a Gel number, measured under specified test conditions, of approximatively 0/0 l/m2.
• the claimed catalyst components can be used to produce totally homogenous (gelless) low and high molecular weight ethylene polymer.
• the invention also relates to the use of a catalyst component according to the invention in the polymerization of olefins, preferably in the homo- or copolymerization of ethylene.
• the advantage of the use is based on the fact that the claimed catalyst is suitable for both low molecular weight and high molecular weight ethylene polymerization and that the ethylene polymer produced is of high quality.
• said alkyl metal halide compound of the formula (2) can, if used, also act completely or partially as a cocatalyst.
• R ⁇ is a C1-C20 alkyl, preferably a Ci -Cjo alkyl, most preferably a C2-C6 alkyl such as ethyl
• X is a halogen, preferably chlorine
• n is 1 to 3, more preferably 2 or 3, most preferably 3, to the polymerization mixture.
• the cocatalyst having the formula (9) is optional depending on whether said alkyl metal halide compound (2) is acting as cocatalyst or not. 11
• the gel level is influenced by two properties of the polymer, the average molecular weight (for which the melt flow rate, or MFR, is an often used measure) and the broadness of the molecular weight distribution (for which the shear thinning index, or SHI, and the flow rate ratio, or FRR, are often used measures).
• MFR melt flow rate
• FRR flow rate ratio
• Pelletized material samples were blown to a film on a pilot film line.
• the film blowing conditions were:
• a sample of the size 210 mm x 297 mm was cut from a film blown on the Collin line.
• the film sample was put into a gel scanner, which classifies the gels according to their size.
• the scanner gives the number of gels in three size classes, ⁇ 0.3 mm, 0.3...0.7 mm and > 0.7 mm.
• the number of gels in the smallest class can be affected by different random factors, so often only the numbers of the intermediate (0.3...0.7 mm) and large (> 0.7 mm) gels are given.
• the dispersion indicates the homogeneity of the black samples in a similar fashion as the gel level indicates the homogeneity of the film samples. It is measured from the black pellets according to the ISO/DIS 11420 method as follows:
• ISO value indicating the dispersion is attributed to the material.
• a high ISO rating denotes a poor homogeneity (large inhomogeneities).
• the polymer samples were produced in a continuously operating pilot plant as follows:
• the catalyst used in this example was one known in the art, prepared according to patent application EP-A-688794 on a 40 ⁇ m silica carrier.
• the catalyst was fed into a 50 dm loop prepolymerization reactor, where a small amount of polymer was formed on the catalyst particles.
• the polymer slurry was taken out of the loop reactor into a flash unit, where the hydrocarbons were separated from the polymer.
• the polymer was then passed into a gas phase reactor where the polymerization was continued at a rate of about 35 kg/h.
• the reactor conditions were set so that MFR 2 ⁇ of the polymer collected from the reactor was about 9 and the density about 946 kg/m 3 . 13
• Composition of the catalyst was: Al 2.4%, Mg 2.0%, Ti 2.0%, Cl 12.5%.
• the polymer was prepared as in Comparative example 1.
• the material was produced according to Comparative Example 1, except that a catalyst was prepared on a 20 ⁇ m silica carrier. Also, the material targets were changed to some extend.
• the gas phase reactor was operated so that the production was 39 kg/h, MFR 21 of the final material was 9 and density was 948.
• the polymer was then blended with additives including an additive containing carbon black to give the material a black colour.
• the material was then pelletized. The dispersion was then determined from the black pellets according to the procedure described earlier. Table 1 shows some data of the material.
• Example 1 (Catalyst APS 11 ⁇ m)
• Composition of the catalyst was: Al 1.8%, Mg 3.9%, Ti 2.1%, Cl 18.5%. 14
• the polymerization was performed as in Comparative example 1.
• the catalyst was prepared according to Example 1, with the exception that a carrier having 29 ⁇ m average particle size was used.
• the bimodal polyethylene material was produced according to Comparative Example 1. Table 1 shows process and evaluation data.
• the catalyst was prepared according to Example 1, with the exception that a carrier having 20 ⁇ m average particle size was used.
• the bimodal polyethylene material was produced according to Comparative Example 3. Table 1 shows process and evaluation data.
• the catalysts have been tested in bimodal Loop-Gas-phase process under fixed split and loop melt index.
• the number of gels was calculated from film blown to film with pilot line. Comparative results to pilot film line were also obtained from the film analysis with large scale film lines.
• the representative polymer lots were characterized by rheology, where SHI 5/300 comparison is made to polymer with same molecular weight.
• SHI5/300 ⁇ 5kPa / ⁇ 300 kPa, where ⁇ 5k p a and ⁇ 3 oo kP a are ⁇ * at a constant G* of 5 kPa and 300 kPa, respectively.

Landscapes

• Chemical & Material Sciences (AREA)
• Health & Medical Sciences (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Medicinal Chemistry (AREA)
• Polymers & Plastics (AREA)
• Organic Chemistry (AREA)
• Transition And Organic Metals Composition Catalysts For Addition Polymerization (AREA)
• Manufacture Of Macromolecular Shaped Articles (AREA)
• Compositions Of Macromolecular Compounds (AREA)

Priority Applications (4)

Applications Claiming Priority (2)

Publications (1)

Family

ID=8551476

Family Applications (1)

Country Status (14)

Cited By (148)

Families Citing this family (36)

Citations (3)

Family Cites Families (10)

• 1998
  • 1998-04-06 FI FI980788A patent/FI111372B/fi active
• 1999
  • 1999-04-01 EP EP99660058A patent/EP0949274A3/en not_active Ceased
  • 1999-04-05 MY MYPI99001301A patent/MY121053A/en unknown
  • 1999-04-06 AR ARP990101530A patent/AR018835A1/es active IP Right Grant
  • 1999-04-06 BR BRPI9909435-5A patent/BR9909435B1/pt not_active IP Right Cessation
  • 1999-04-06 WO PCT/FI1999/000286 patent/WO1999051646A1/en not_active Ceased
  • 1999-04-06 CN CNB998056995A patent/CN1202140C/zh not_active Expired - Lifetime
  • 1999-04-06 AU AU33342/99A patent/AU3334299A/en not_active Abandoned
  • 1999-04-06 JP JP2000542367A patent/JP4813657B2/ja not_active Expired - Lifetime
  • 1999-04-06 KR KR10-2000-7011120A patent/KR100531509B1/ko not_active Expired - Lifetime
  • 1999-04-06 CA CA002325632A patent/CA2325632A1/en not_active Abandoned
  • 1999-04-06 US US09/286,437 patent/US6620758B1/en not_active Expired - Lifetime
  • 1999-04-13 TW TW088105818A patent/TWI251598B/zh not_active IP Right Cessation
• 2000
  • 2000-09-20 ZA ZA200005015A patent/ZA200005015B/xx unknown
• 2003
  • 2003-04-24 US US10/423,771 patent/US20030208010A1/en not_active Abandoned
• 2004
  • 2004-06-14 US US10/868,509 patent/US6924343B2/en not_active Expired - Lifetime

Patent Citations (3)

Also Published As

Similar Documents

Legal Events