WO1999023118A1 - Umsetzung eines polyhydroxypolymeren bzw. eines derivates davon mit einem lacton - Google Patents
Umsetzung eines polyhydroxypolymeren bzw. eines derivates davon mit einem lacton Download PDFInfo
- Publication number
- WO1999023118A1 WO1999023118A1 PCT/IB1998/001734 IB9801734W WO9923118A1 WO 1999023118 A1 WO1999023118 A1 WO 1999023118A1 IB 9801734 W IB9801734 W IB 9801734W WO 9923118 A1 WO9923118 A1 WO 9923118A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- derivative
- cellulose
- polymer
- reaction
- polyhydroxy
- Prior art date
Abstract
Description
Claims