Classifications

• • G—PHYSICS
  • G03—PHOTOGRAPHY; CINEMATOGRAPHY; ANALOGOUS TECHNIQUES USING WAVES OTHER THAN OPTICAL WAVES; ELECTROGRAPHY; HOLOGRAPHY
  • G03F—PHOTOMECHANICAL PRODUCTION OF TEXTURED OR PATTERNED SURFACES, e.g. FOR PRINTING, FOR PROCESSING OF SEMICONDUCTOR DEVICES; MATERIALS THEREFOR; ORIGINALS THEREFOR; APPARATUS SPECIALLY ADAPTED THEREFOR
  • G03F7/00—Photomechanical, e.g. photolithographic, production of textured or patterned surfaces, e.g. printing surfaces; Materials therefor, e.g. comprising photoresists; Apparatus specially adapted therefor
• • G—PHYSICS
  • G03—PHOTOGRAPHY; CINEMATOGRAPHY; ANALOGOUS TECHNIQUES USING WAVES OTHER THAN OPTICAL WAVES; ELECTROGRAPHY; HOLOGRAPHY
  • G03F—PHOTOMECHANICAL PRODUCTION OF TEXTURED OR PATTERNED SURFACES, e.g. FOR PRINTING, FOR PROCESSING OF SEMICONDUCTOR DEVICES; MATERIALS THEREFOR; ORIGINALS THEREFOR; APPARATUS SPECIALLY ADAPTED THEREFOR
  • G03F7/00—Photomechanical, e.g. photolithographic, production of textured or patterned surfaces, e.g. printing surfaces; Materials therefor, e.g. comprising photoresists; Apparatus specially adapted therefor
  • G03F7/004—Photosensitive materials
  • G03F7/027—Non-macromolecular photopolymerisable compounds having carbon-to-carbon double bonds, e.g. ethylenic compounds
  • G03F7/028—Non-macromolecular photopolymerisable compounds having carbon-to-carbon double bonds, e.g. ethylenic compounds with photosensitivity-increasing substances, e.g. photoinitiators
  • G03F7/029—Inorganic compounds; Onium compounds; Organic compounds having hetero atoms other than oxygen, nitrogen or sulfur
• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61K—PREPARATIONS FOR MEDICAL, DENTAL OR TOILETRY PURPOSES
  • A61K6/00—Preparations for dentistry
  • A61K6/20—Protective coatings for natural or artificial teeth, e.g. sealings, dye coatings or varnish
• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61K—PREPARATIONS FOR MEDICAL, DENTAL OR TOILETRY PURPOSES
  • A61K6/00—Preparations for dentistry
  • A61K6/30—Compositions for temporarily or permanently fixing teeth or palates, e.g. primers for dental adhesives
• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61K—PREPARATIONS FOR MEDICAL, DENTAL OR TOILETRY PURPOSES
  • A61K6/00—Preparations for dentistry
  • A61K6/80—Preparations for artificial teeth, for filling teeth or for capping teeth
  • A61K6/884—Preparations for artificial teeth, for filling teeth or for capping teeth comprising natural or synthetic resins
  • A61K6/887—Compounds obtained by reactions only involving carbon-to-carbon unsaturated bonds
• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61K—PREPARATIONS FOR MEDICAL, DENTAL OR TOILETRY PURPOSES
  • A61K6/00—Preparations for dentistry
  • A61K6/80—Preparations for artificial teeth, for filling teeth or for capping teeth
  • A61K6/884—Preparations for artificial teeth, for filling teeth or for capping teeth comprising natural or synthetic resins
  • A61K6/891—Compounds obtained otherwise than by reactions only involving carbon-to-carbon unsaturated bonds
• • G—PHYSICS
  • G03—PHOTOGRAPHY; CINEMATOGRAPHY; ANALOGOUS TECHNIQUES USING WAVES OTHER THAN OPTICAL WAVES; ELECTROGRAPHY; HOLOGRAPHY
  • G03F—PHOTOMECHANICAL PRODUCTION OF TEXTURED OR PATTERNED SURFACES, e.g. FOR PRINTING, FOR PROCESSING OF SEMICONDUCTOR DEVICES; MATERIALS THEREFOR; ORIGINALS THEREFOR; APPARATUS SPECIALLY ADAPTED THEREFOR
  • G03F7/00—Photomechanical, e.g. photolithographic, production of textured or patterned surfaces, e.g. printing surfaces; Materials therefor, e.g. comprising photoresists; Apparatus specially adapted therefor
  • G03F7/004—Photosensitive materials
  • G03F7/038—Macromolecular compounds which are rendered insoluble or differentially wettable
• • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
  • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
  • Y10S—TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
  • Y10S522/00—Synthetic resins or natural rubbers -- part of the class 520 series
  • Y10S522/908—Dental utility

Definitions

• the invention relates to photocurable, addition polymerizable compositions that contain a ternary photoinitiator system that is activated on exposure to actinic radiation in the visible spectrum and methods of curing addition polymerizable compositions using the photoinitiator system.
• the invention is additionally directed to methods of curing addition polymerizable compositions using the ternary photoinitiator system.
• Epoxy containing compounds are known to be curable using various cationic initiator systems.
• Smith in U.S. Patent No. 4,256,828, describes photopolymerizable compositions that contain epoxides, an organic compound with hydroxyl functionality, and a photosensitive aromatic sulfonium or iodonium salt of a halogen containing complex ion.
• Hayase et al. U.S. Patent No. 4,835,193
• photohardenable compositions that comprise a cationically polymerizable compound, a xanthene or fiuorone dye, a hydrogen donor, and an onium salt.
• Palazzotto et al. U.S. Patent No. 5,545,676, describes addition polymerization of free-radically polymerizable materials.
• the photoinitiator system described in that patent comprises an aryliodonium salt, a sensitizer, and an electron donor having an oxidation potential less than or equal to that ofp-dimethoxybenzene.
• PCT published application No. WO 96/13538 describes a system for curing epoxy compounds by exposure to visible light by use of a system comprising an aryliodonium salt and a sensitizer.
• Comparative Example 34 of this disclosure describes the use of one of the initiator systems of Palazzotto et al., U.S. Patent No. 5,545,676 in an epoxy/polyol resin system. N, N-dimethylbenzylamine is used as the electron donor. The results of this experiment indicated that the use of this amine donor tended to retard the cure of the resin system.
• a photopolymerizable composition that contains an epoxy resin and a photoinitiator system containing an iodonium salt, a visible light sensitizer, and an electron donor compound, wherein the photoinitiator system has a photoinduced potential greater than or equal to that of 3-dimethylamino benzoic acid in a standard solution of 2.9x10 "3 moles/g diphenyl iodonium hexafluoroantimonate and 1.5xl0 "5 moles/g camphorquinone in 2-butanone.
• 3-dimethylamino benzoic acid in this standard exhibits a photoinduced potential of at least about 115mV relative to a standard solution of 2.9x10 "5 moles/g diphenyl iodonium hexafluoroantimonate and 1.5xl0 "5 moles/g camphorquinone in 2-butanone.
• compositions are curable on exposure to light having a wavelength of about 400 to 1000 nm
• the invention provides a method of addition photopolymerization comprising the step of irradiating a photopolymerizable composition with light having a wavelength of about 400 to 1000 nm until the composition gels or hardens, the composition comprising an epoxy resin and a photoinitiator system containing an iodonium salt, a visible light sensitizer, and an electron donor compound wherein the photoinitiator system has a photoinduced potential of at least about lOOmV relative to a standard solution of
• the initiator systems of the invention allow efficient cationic polymerization under conditions of room temperature and standard pressure.
• the initiator systems can, under appropriate conditions, initiate both cationic and free-radical polymerization. This property permits their use with a variety of photopolymerizable compositions. The use of these initiator systems actually results in the ability to cure epoxy systems otherwise not readily curable at room temperature with sensitizers and iodonium salts.
• the photopolymerizable compositions of the invention are sensitive throughout the visible spectral region and photocure without appreciable application of heat.
• the term "visible light” is used throughout this application to refer to light having a wavelength of about 400 to 1000 nanometers (nm). Photopolymerization of the compositions takes place on exposure of the compositions to a source of actinic radiation having a wavelength within this spectral region.
• the cationically polymerizable epoxy resins useful in the compositions of the invention are organic compounds having an oxirane ring, i.e., a group of the formula I I
• epoxides include monomeric epoxy compounds and epoxides of the polymeric type and can be aliphatic, cycloaliphatic, aromatic or heterocyclic. These materials generally have, on the average, at least 1 polymerizable epoxy group per molecule, preferably at least about 1.5 and more preferably at least about 2 polymerizable epoxy groups per molecule.
• the polymeric epoxides include linear polymers having terminal epoxy groups (e.g., a diglycidyl ether of a polyoxyalkylene glycol), polymers having skeletal oxirane units (e.g., polybutadiene polyepoxide), and polymers having pendent epoxy groups (e.g., a glycidyl methacrylate polymer or copolymer).
• the epoxides may be pure compounds or may be mixtures of compounds containing one, two, or more epoxy groups per molecule. The "average" number of epoxy groups per molecule is determined by dividing the total number of epoxy groups in the epoxy-containing material by the total number of epoxy-containing molecules present.
• epoxy-containing materials may vary from low molecular weight monomeric materials to high molecular weight polymers and may vary greatly in the nature of their backbone and substituent groups.
• the backbone may be of any type and substituent groups thereon can be any group that does not substantially interfere with cationic cure at room temperature.
• permissible substituent groups include halogens, ester groups, ethers, sulfonate groups, siloxane groups, nitro groups, phosphate groups, and the like.
• the molecular weight of the epoxy-containing materials may vary from about 58 to about 100,000 or more.
• Useful epoxy-containing materials include those which contain cyclohexene oxide groups such as epoxycyclohexanecarboxylates, typified by 3,4- epoxycyclohexylmethyl-3 ,4-epoxycyclohexanecarboxylate, 3 ,4-epoxy-2- methylcyclohexylmet_ ⁇ yl-3,4-epoxy-2-methylcyclohexane carboxylate, and bis(3,4- epoxy-6-methylcyclohexylmethyl) adipate.
• cyclohexene oxide groups such as epoxycyclohexanecarboxylates, typified by 3,4- epoxycyclohexylmethyl-3 ,4-epoxycyclohexanecarboxylate, 3 ,4-epoxy-2- methylcyclohexylmet_ ⁇ yl-3,4-epoxy-2-methylcyclohexane carboxylate, and bis(3,4- epoxy-6-methylcyclohexylmethyl
• epoxy-containing materials which are useful in the compositions of this invention include glycidyl ether monomers of the formula
• R' is alkyl or aryl and n is an integer of 1 to 6.
• glycidyl ethers of polyhydric phenols obtained by reacting a polyhydric phenol with an excess of chlorohydrin such as epichlorohydrin (e.g., the diglycidyl ether of 2,2-bis-(2,3- epoxypropoxyphenol)-propane).
• chlorohydrin e.g., epichlorohydrin
• epoxides of this type are described in U.S. Patent No. 3,018,262, which is incorporated herein by reference, and in "Handbook of Epoxy Resins" by Lee and Neville, McGraw-Hill Book Co., New York (1967).
• Epoxy Resins There are a host of commercially available epoxy resins which can be used in this invention.
• epoxides which are readily available include octadecylene oxide, epichlorohydrin, styrene oxide, vinyl cyclohexene oxide, glycidol, glycidylmethacrylate, diglycidyl ether of Bisphenol A (e.g., those available under the trade designations "Epon 828", “Epon 825”, “Epon 1004" and “Epon 1010" from Shell Chemical Co., "DER-331”, “DER-332", and “DER-334", from Dow Chemical Co.), vinylcyclohexene dioxide (e.g., "ERL-4206” from Union Carbide Corp.), 3,4-epoxycyclohexylmethyl-3,4-epoxycyclohexene carboxylate (e.g., "ERL-4221” or “CYRACURE UVR 6110" or UVR 6105" from Union Carbide Corp.), 3,4-epoxy-6-methylcyclohexylmethyl-3
• silicone resin containing epoxy functionality silicone resin containing epoxy functionality
• flame retardant epoxy resins e.g., "DER-580", a brominated bisphenol type epoxy resin available from Dow Chemical Co.
• 1 ,4-butanediol diglycidyl ether of phenolformaldehyde novolak e.g., "DEN-431” and “DEN-438” from Dow Chemical Co.
• resorcinol diglycidyl ether e.g., "Kopoxite” from Koppers Company, Inc.
• bis(3,4-epoxycyclohexyl)adipate e.g., "ERL-4299” or “UVR-6128", from Union Carbide Corp.
• 2-(3,4-epoxycyclohexyl-5, 5-spiro-3,4-epoxy) cyclohexane-meta- dioxane e.g., "ERL-4234" from Union Carbide Corp.
• alkyl C, 2 -C 14 glycidyl ether e.g., "HELOXY Modifier 8" from Shell Chemical Co.
• butyl glycidyl ether e.g., "HELOXY Modifier 61" from Shell Chemical Co.
• cresyl glycidyl ether e.g., "HELOXY Modifier 62” from Shell Chemical Co.
• p-ter butylphenyl glycidyl ether e.g., "HELOXY Modifier 65” from Shell Chemical Co.
• polyfunctional glycidyl ethers such as diglycidyl ether of 1 ,4-butanediol (e.g., "HELOXY Modifier 67" from
• polyglycidyl ether of an aliphatic polyol e.g., "HELOXY Modifier 84" from Shell Chemical Co.
• polyglycol diepoxide e.g., "HELOXY Modifier 32” from Shell Chemical Co.
• bisphenol F epoxides e.g., "EPN-1138” or “GY-281” from Ciba-Geigy Corp.
• 9,9-bis[4-(2,3-epoxypropoxy)- phenyl] fluorenone e.g., "Epon 1079" from Shell Chemical Co.
• Still other epoxy resins contain copolymers of acrylic acid esters or glycidol such as glycidylacrylate and glycidylmethacrylate with one or more copolymerizable vinyl compounds.
• copolymers are 1 : 1 styrene- glycidylmethacrylate, 1 :1 methylmethacrylate-glycidylacrylate and a 62.5:24:13.5 methylmethacrylate-ethyl acrylate-glycidylmethacrylate.
• epoxy resins are well known and contain such epoxides as epichlorohydrins, alkylene oxides, e.g., propylene oxide, styrene oxide; alkenyl oxides, e.g., butadiene oxide; glycidyl esters, e.g., ethyl glycidate.
• alkylene oxides e.g., propylene oxide, styrene oxide
• alkenyl oxides e.g., butadiene oxide
• glycidyl esters e.g., ethyl glycidate.
• the polymers of the epoxy resin may optionally contain other functionalities that do not substantially interfere with cationic cure at room temperature.
• Blends of various epoxy-containing materials are also contemplated in this invention.
• examples of such blends include two or more weight average molecular weight distributions of epoxy-containing compounds, such as low molecular weight (below 200), intermediate molecular weight (about 200 to
• the epoxy resin may contain a blend of epoxy-containing materials having different chemical natures, such as aliphatic and aromatic, or functionalities, such as polar and non-polar. Other cationically polymerizable polymers may additionally be incorporated, if desired.
• the composition can also contain a free-radically polymerizable material, including ethylenically unsaturated monomer, monomers or oligomers or polymers. Suitable materials contain at least one ethylenically unsaturated bond, and are capable of undergoing addition polymerization.
• Such free radically polymerizable materials include mono-, di- or poly- acrylates and methacrylates such as methyl acrylate, methyl methacrylate, ethyl acrylate, isopropyl methacrylate, n-hexyl acrylate, stearyl acrylate, allyl acrylate, glycerol diacrylate, glycerol triacrylate, ethyleneglycol diacrylate, diethyleneglycol diacrylate, triethyleneglycol dimethacrylate, 1,3-propanediol diacrylate, 1,3- propanediol dimethacrylate, trimethylolpropane triacrylate, 1,2,4-butanetriol trimethacrylate, 1 ,4-cyclohexanediol diacrylate, pentaerythritol triacrylate, pentaerythritol tetraacrylate, pentaerythritol tetramethacrylate, sorb
• the polymerizable material(s) may contain both epoxy and free-radically polymerizable functionalities in a single molecule. These may be obtained by reacting a di- or poly-epoxide with one or more equivalents of an ethylenically unsaturated carboxylic acid.
• Examples of such materials include the reaction product of UVR-6105 (available from Union Carbide) or DER 332 with one equivalent of methacrylic acid.
• Commercially available materials having epoxy and free-radically polymerizable functionalities include the "Cyclomer” series, such as Cyclomer Ml 00 or Ml 01, available from Daicel Chemical, Japan.
• the epoxy resin and optional free radically polymerizable material(s) are combined with a three component or ternary photoinitiator system.
• Three component initiator systems are described in Palazzotto et al., U.S. Patent
• the first component in the photoinitiator system is an iodonium salt, i.e., a diaryliodonium salt.
• the iodonium salt should be soluble in the monomer and preferably is shelf-stable, meaning it does not spontaneously promote polymerization when dissolved therein in the presence of the sensitizer and donor. Accordingly, selection of a particular iodonium salt may depend to some extent upon the particular monomer, sensitizer and donor chosen. Suitable iodonium salts are described in U.S. Pat. Nos.
• the iodonium salt can be a simple salt, containing an anion such as Cl “ , Br “ , I “ or C 4 H 5 SO 3 " ; or a metal complex salt containing an antimonate, arsenate, phosphate or borate such as SbF 5 OH “ or AsF 6 " . Mixtures of iodonium salts can be used if desired.
• aromatic iodonium complex salt photoinitiators include: diphenyliodonium tetrafluoroborate; di(4-methylphenyl)iodonium tetrafluoroborate; phenyl-4-methylphenyliodonium tetrafluoroborate; di(4- heptylphenyl)iodonium tetrafluoroborate; di(3 -nitrophenyl)iodonium hexafluorophosphate; di(4-chlorophenyl)iodonium hexafluorophosphate; di(naphthyl)iodonium tetrafluoroborate; di(4-trifluoromethylphenyl)iodonium tetrafluoroborate; diphenyliodonium hexafluorophosphate; di(4- methylphenyl)iodonium hexafluorophosphate; diphenyliodonium hex
• diaryliodonium hexafluorophosphate and diary liodonium hexafluoroantimonate are among the preferred salts. These salts are preferred because, in general, they promote faster reaction, and are more soluble in inert organic solvents than are other aromatic iodonium salts of complex ions.
• the aromatic iodonium complex salts may be prepared by metathesis of corresponding aromatic iodonium simple salts (such as, for example, diphenyliodonium bisulfate) in accordance with the teachings of Beringer et al., Am. Chem. Soc. 81,342 (1959).
• the complex salt diphenyliodonium tetrafluoroborate is prepared by the addition at 60°C of an aqueous solution containing 29.2 g silver fluoroborate, 2 g fluoroboric acid, and 0.5 g phosphorous acid in about 30 ml of water to a solution of 44 g (139 millimoles) of diphenyliodonium chloride.
• the silver halide that precipitates is filtered off and the filtrate concentrated to yield diphenyliodonium fluoroborate which may be purified by recrystallization.
• the aromatic iodonium simple salts may be prepared in accordance with Beringer et al., above, by various methods including (1) coupling of two aromatic compounds with iodyl sulfate in sulfuric acid, (2) coupling of two aromatic compounds with an iodate in acetic acid-acetic anhydride-sulfuric acid, (3) coupling of two aromatic compounds with an iodine acrylate in the presence of an acid, and (4) condensation of an iodoso compound, an iodoso diacetate, or an iodoxy compound with another aromatic compound in the presence of an acid.
• Diphenyliodonium bisulfate is prepared by method (3), for example, by the addition over a period of eight hours at below 5°C of a mixture of 35 ml of cone. sulfuric acid and 50 ml of acetic anhydride to a well-stirred mixture of 55.5 ml of benzene, 50 ml of acetic anhydride, and 53.5g of potassium iodate. The mixture is stirred for an additional four hours at 0°-5°C and at room temperature (about 25°C) for 48 hours and treated with 300 ml of diethyl ether. On concentration, crude diphenyliodonium bisulfate precipitates and may be purified by recrystallization if desired.
• the second component in the photoinitiator system is the sensitizer.
• the sensitizer should be soluble in the photopolymerizable composition, free of functionalities that would substantially interfere with the cationic curing process, and capable of light absorption somewhere within the range of wavelengths between about 300 and about 1000 nanometers.
• Suitable sensitizers are believed to include compounds in the following categories: ketones, coumarin dyes (e.g., ketocoumarins), xanthene dyes, acridine dyes, thiazole dyes, thiazine dyes, oxazine dyes, azine dyes, aminoketone dyes, porphyrins, aromatic polycyclic hydrocarbons, p-substituted aminostyryl ketone compounds, aminotriaryl methanes, merocyanines, squarylium dyes and pyridinium dyes.
• Ketones e.g., monoketones or alpha-diketones
• ketocoumarins aminoarylketones
• p-substituted aminostyryl ketone compounds are preferred sensitizers.
• sensitizers having an extinction coefficient below about 1000 lmole "1 cm “1 , more preferably about or below 100 lmole 'cm "1 , at the desired wavelength of irradiation for photopolymerization.
• the alpha-diketones are an example of a class of sensitizers having this property, and are particularly preferred for dental applications
• ketone sensitizers has the formula:
• X is CO or CR'R 2 where R 1 and R 2 can be the same different, and can be hydrogen, alkyl, alkaryl or aralkyl, b is zero, and A and B can be the same or different and can be substituted (having one or more non-interfering substituents) or unsubstituted aryl, alkyl, alkaryl, or aralkyl groups, or together A and B can form a cyclic structure which can be a substituted or unsubstituted cycloaliphatic, aromatic, heteroaromatic or fused aromatic ring.
• 2-fluoro-9-fluorenone 2-chlorothioxanthone, acetophenone, benzophenone, 1 - or 2-acetonaphthone, 9-acetylanthracene, 2-, 3- or 9-acetylphenanthrene, 4- acetylbiphenyl, propiophenone, n-butyrophenone, valerophenone, 2-, 3- or 4- acetylpyridine, 3-acetylcoumarin and the like.
• Suitable diketones include aralkyldiketones such as anthraquinone, phenanthrenequinone, o-, m- and p- diacetylbenzene, 1,3-, 1,4-, 1,5-, 1,6-, 1,7- and 1 ,8-diacetylnaphthalene, 1,5-, 1,8- and 9, 10-diacetylanthracene, and the like.
• Suitable I-diketones include 2,3-butanedione, 2,3-pentanedione, 2,3-hexanedione, 3,4-hexanedione, 2,3- heptanedione, 3,4-heptanedione, 2,3-octanedione, 4,5-octanedione, benzil, 2,2'- 3 3'- and 4,4'-dihydroxylbenzil, furil, di-3,3'-indolylethanedione, 2,3-bornanedione
• Examples of particularly preferred visible light sensitizers include camphorquinone; glyoxal; biacetyl; 3,3,6,6-tetramethylcyclohexanedione; 3,3,7,7- tetramethyl-l,2-cycloheptanedione; 3,3,8,8-tetramethyl-l,2-cyclooctanedione;
• camphorquinone is the most highly preferred sensitizer.
• the third component of the initiator system is an electron donor.
• the electron donor compound(s) should meet one of the requirements set forth below and should be soluble in the polymerizable composition.
• the donor can also be selected in consideration of other factors, such as shelf stability and the nature of the polymerizable materials, iodonium salt and sensitizer chosen.
• a class of donor compounds that may be useful in the inventive systems may be selected from some of the donors described in Palazzotto et al., U.S. Patent No. 5,545,676. Possible donor compounds that meet the criteria set forth by Palazzotto et al. must then be tested using one or both of the methods set forth below to determine if they will be useful donors for the photopolymerizable compositions of the invention.
• the donor is typically an alkyl aromatic polyether or an alkyl, aryl amino compound wherein the aryl group is substituted by one or more electron withdrawing groups.
• suitable electron withdrawing groups include carboxylic acid, carboxylic acid ester, ketone, aldehyde, sulfonic acid, sulfonate and nitrile groups.
• the suitability of a compound for usefulness in the compositions of the invention may be determined by measuring the photoinduced potential of a sample photoinitiator system that includes the compound. The photoinduced potential can be evaluated using one of two methods.
• a standard solution is prepared that contains 2.9X10 "5 moles/g of diphenyl iodonium hexafluoroantimonate and 1.5X10 "5 moles/g of camphorquinone in 2-butanone.
• a pH electrode is then immersed in the solution and a pH meter is calibrated to zero mV.
• a test solution of the standard solution and the compound is prepared next using the compound at a concentration of 2.9X10 "5 moles/g. This test solution is irradiated using blue light having a wavelength of about 400 to 500 nm having an intensity of about 200 to 400 mW/cm 2 for about 5 to 10 seconds.
• Millivolts relative to the standard solution are then determined by immersing the pH electrode in the test solution and obtaining a mV reading on the pH meter.
• useful donors are those compounds that provide a reading of at least 1 OOmV relative to the standard solution and provide a gel time for the compositions that fail to gel at 25 C in the absence of donor. Higher mV readings are generally indicative of greater activity, and to obtain a more rapid cure reading of at least about 1 OOmV are preferred.
• the second method involves the evaluation of the photoinduced potential of an initiator system that includes the compound compared to a system that includes 3-dimethylamino benzoic acid.
• a standard solution of 2.9X10 "5 moles/g diphenyl iodonium hexafluoroantimonate, 1.5X10 "5 moles/g camphorquinone and 2.9X10 "5 moles/g of 3-dimethylamino benzoic acid in 2- butanone is prepared.
• a pH electrode is then immersed in the solution and a pH meter is calibrated to zero mV.
• the standard solution is irradiated with blue light having a wavelength of between about 400-500 nm and an intensity of about 200 to
• test solution 400 mW/cm 2 for about 5 to 10 seconds using a focused light source such as a dental curing light.
• a focused light source such as a dental curing light.
• the potential of the solution is measured by immersing a pH electrode in the irradiated standard solution and reading the potential in mV using a pH meter.
• a test solution is then prepared using 2.9X10 " 5 moles/g of diphenyl iodonium hexafluoroantimonate, 1.5X10 "5 moles/g of camphorquinone and 2.9X10 "5 moles/g of the compound in 2-butanone.
• the test solution is irradiated and the photoinduced potential measured using the same technique as described for the standard solution. If the test solution has a photoinduced potential that is the same as or greater than that of the 3- dimethylamino benzoic acid containing standard solution, then the compound is a useful donor.
• alkyl, aryl amine donor compounds A preferred group of alkyl, aryl amine donor compounds is described by the following structural formula:
• R R wherein R 1 are independently H, C,. 18 alkyl that is optionally substituted by one or more halogen, -CN, -OH, -SH, C,. lg alkoxy, C,. ]g alkylthio, C 3 . 18 cycloalkyl, aryl, COOH, COOC,. lg alkyl, (C,., 8 alkyl)o_ r CO-C,. 18 alkyl, SO 3 R 2 , CN or or aryl that is optionally substituted by one or more electron withdrawing groups; and Ar is aryl that is substituted by one or more electron withdrawing groups. Suitable electron withdrawing groups include -COOH, -COOR 2 , -SO 3 R 2 , -CN, -CO-C,. lg alkyl and - C(O)H groups.
• a preferred group ' of aryl alkyl polyethers has the following structural formula:
• each R 3 is independently H or C, .lg alkyl that is optionally substituted by one or more halogen, -CN, -OH, -SH, C g alkoxy, C,. lg alkylthio, C 3 . lg cycloalkyl, aryl, substituted aryl, -COOH, -COOC 8 alkyl, -(C,. 18 alkyl) 0 . r COH, -(C,. lg alkyl ⁇ -CO-C,.,, alkyl, -CO-C,., 8 alkyl, -C(O)H or -C 2 .
• each R 4 can be C,. 18 alkyl that is optionally substituted by one or more halogen, -CN, -OH, -SH, C,. 18 alkoxy, C,. I8 alkylthio, C 3 . 18 cycloalkyl, aryl, substituted aryl, -COOH, -COOC 8 alkyl, -(C,. lg alkyl) 0 .,-COH, -(C,. Ig alkyl) 0 . r CO-C,. lg alkyl, -CO-C,. 18 alkyl, -C(O)H or -C 2 . l8 alkenyl groups.
• the alkyl groups can be straight-chain or branched, and the cycloalkyl group preferably has 3 to 6 ring carbon atoms but may have additional alkyl substitution up to the specified number of carbon atoms.
• the aryl groups may be carbocyclic or heterocyclic aryl, but are preferably carbocyclic and more preferably phenyl rings.
• Preferred donor compounds include 4-dimethylaminobenzoic acid, ethyl 4-dimethylaminobenzoate, 3-dimethylaminobenzoic acid, 4- dimethylaminobenzoin, 4-dimethylaminobenzaldehyde, 4- dimethylaminobenzoni trile and 1 ,2,4-trimethoxybenzene.
• the photoinitiator compounds are provided in an amount effective to initiate or enhance the rate of cure of the resin system. It has been found that the amount of donor that is used can be critical particularly when the donor is an amine. Too much donor can be deleterious to cure properties.
• the sensitizer is present in about 0.05-5.0 weight percent based on resin compounds of the overall composition. More preferably, the sensitizer is present at 0.10-1.0 weight percent.
• the iodonium initiator is preferably present at 0.05-10.0 weight percent, more preferably at 0.10-5.0 weight percent, and most preferably 0.50-3.0 weight percent.
• the donor is preferably present at 0.01-5.0 weight percent, more preferably 0.05-1.0 weight percent, and most preferably 0.05-
• the photopolymerizable compositions of the invention are prepared by simply admixing, under "safe light” conditions, the components of the inventive compositions. Suitable inert solvents may be employed if desired when effecting this mixture. Any solvent may be used which does not react appreciably with the components of the inventive compositions. Examples of suitable solvents include acetone, dichloromethane, and acetonitrile. A liquid material to be polymerized may be used as a solvent for another liquid or solid material to be polymerized. Solventless compositions can be prepared by simply dissolving the aromatic iodonium complex salt and sensitizer in the epoxy resin polyol mixture with or without the use of mild heating to facilitate dissolution.
• compositions of the present invention provide a very useful combination of cure speed, cure depth and shelf life. They cure well even when loaded with large amounts of fillers, and can be used in a variety of applications including graphic arts imaging (e.g. for color proofing systems, curable inks, or silverless imaging), printing plates (e.g. projection plates or laser plates), photoresists, solder masks, electronic conformal coatings, coated abrasives, magnetic media, photocurable adhesives (e.g. for orthodontics) and photocurable composites (e.g., for autobody repair or dentistry).
• graphic arts imaging e.g. for color proofing systems, curable inks, or silverless imaging
• printing plates e.g. projection plates or laser plates
• photoresists e.g. projection plates or laser plates
• solder masks e.g. projection plates or laser plates
• electronic conformal coatings e.g. coatings
• coated abrasives e.g. for magnetic media
• photocurable adhesives
• Suitable inert solvents may be employed if desired when effecting this mixture. Any solvent may be used which does not react appreciably with the components of the inventive compositions. Examples of suitable solvents include acetone, dichloromethane, and acetonitrile. A liquid material to be polymerized may be used as a solvent for another liquid or solid material to be polymerized. Solventless compositions can be prepared by simply dissolving the aromatic iodonium complex salt and sensitizer in the epoxy resin with or without the use of mild heating to facilitate dissolution.
• Dental applications particularly benefit from the unique compositions of the present invention.
• acrylate and methacrylate chemistry has been used extensively for adhesive and restorative dental compositions.
• This chemistry has the advantage of being curable with visible light using photoinitiator systems, but has the disadvantage of undergoing a relatively high degree of shrinkage during the polymerization process.
• the epoxy resins found in the compositions of the present invention shrink significantly less than the acrylate and methacrylate resins of the prior art.
• the present invention provides a system for curing epoxy resins in an acceptable time frame and to a sufficient depth using visible light source equipment already available in the dental office.
• the dental materials may be filled or unfilled and include dental materials such as direct esthetic restorative materials (e.g., anterior and posterior restoratives), prostheses, adhesives and primers for oral hard tissues, sealants, veneers, cavity liners, orthodontic bracket adhesives for use with any type of bracket (such as metal, plastic and ceramic), crown and bridge cements, artificial crowns, artificial teeth, dentures, and the like.
• dental materials are used in the mouth and are disposed adjacent to natural teeth.
• the phrase "disposed adjacent to" as used herein refers to the placing of a dental material in temporary or permanent bonding (e.g., adhesive) or touching (e.g., occlusal or proximal) contact with a natural tooth.
• composite refers to a filled dental material.
• storage refers to a composite which is polymerized after it is disposed adjacent to a tooth.
• prosthesis refers to a composite which is shaped and polymerized for its final use (e.g., as crown, bridge, veneer, inlay, onlay or the like) before it is disposed adjacent to a tooth.
• silant refers to a lightly filled composite or to an unfilled dental material which is cured after it is disposed adjacent to a tooth.
• Polymerizable refers to curing or hardening the dental material, e.g., by free- radical, cationic or mixed reaction mechanisms.
• the use of a filler may be appropriate.
• the choice of filler affects important properties of the composite such as its appearance, radiopacity and physical and mechanical properties. Appearance is affected in part by adjustment of the amounts and relative refractive indices of the ingredients of the composite, thereby allowing alteration of the translucence, opacity or pearlescence of the composite.
• Epoxy resin compositions of the invention can be prepared with refractive indices which approach or approximate the refractive indices of fillers such as quartz (refractive index 1.55), submicron silica (refractive index 1.46), and 5.5:1 mole ratio SiO:ZrO, non-vitreous microparticles (refractive index 1.54).
• fillers such as quartz (refractive index 1.55), submicron silica (refractive index 1.46), and 5.5:1 mole ratio SiO:ZrO, non-vitreous microparticles (refractive index 1.54).
• Radiopacity is a measurement of the ability of the composite to be detected by x-ray examination. Frequently a radiopaque composite will be desirable, for instance, to enable the dentist to determine whether or not a dental restoration remains sound.
• the amount of filler which is incorporated into the composite referred to herein as the "loading level" and expressed as a weight percent based on the total weight of the dental material, will vary depending on the type of filler, the epoxy resin and other components of the composition, and the end use of the composite.
• the epoxy resin compositions of the invention can be lightly filled (e.g., having a loading level of less than about 40 weight percent) or unfilled.
• the viscosity of the dental material is sufficiently low to allow its penetration into pits and fissures of occlusal tooth surfaces as well as into etched areas of enamel, thereby aiding in the retention of the dental material.
• the loading level can be as high as about 95 weight percent.
• a loading level of between about 70 and 90 weight percent is generally preferred.
• Fillers may be selected from one or more of any material suitable for incorporation in compositions used for medical applications, such as fillers currently used in dental restorative compositions and the like.
• the filler is finely divided and preferably has a maximum particle diameter of less than about 50 micrometers and an average particle diameter of less than about 10 micrometers.
• the filler can have a unimodal or polymodal (e.g., bimodal) particle size distribution.
• the filler can be an inorganic material. It can also be a crosslinked organic material that is insoluble in the polymerizable resin, and is optionally filled with inorganic filter.
• the filler should in any event be non-toxic and suitable for use in the mouth.
• the filler can be radiopaque, radiolucent or nonradiopaque.
• suitable inorganic fillers are naturally-occurring or synthetic materials such as quartz, nitrides (e.g., silicon nitride), glasses derived from, for example Ce, Sb, Sn, Zr, Sr, Ba and Al, colloidal silica, feldspar, borosilicate glass, kaolin, talc, titania, and zinc glass; low Mohs hardness fillers such as those described in U.S. Patent No. 4,695,251 ; and submicron silica particles (e.g., pyrogenic silicas such as the "Aerosil" Series "OX 50", "130",
• suitable organic filler particles include filled or unfilled pulverized polycarbonates, polyepoxides, and the like.
• Preferred filler particles are quartz, submicron silica, and non-vitreous microparticles of the type described in U.S. Patent No. 4,503,169.
• Metallic fillers may also be incorporated, such as particulate metal filler made from a pure metal such as those of Groups IV A, V A, VIA, VIIA, VIII, IB, or IIB, aluminum, indium, and thallium of Group 1KB, and tin and lead of Group IVB, or alloys thereof.
• Conventional dental amalgam alloy powders typically mixtures of silver, tin, copper, and zinc, may also optionally be incorporated.
• the particulate metallic filler preferably has an average particle size of about 1 micron to about 100 microns, more preferably 1 micron to about 50 microns. Mixtures of these fillers are also contemplated, as well as combination fillers made from organic and inorganic materials. Fluoroaluminosilicate glass fillers, either untreated or silanol treated, are particularly preferred. These glass fillers have the added benefit of releasing fluoride at the site of dental work when placed in the oral environment.
• the surface of the filler particles may be treated with a surface treatment such as a coupling agent in order to enhance the bond between the filler and the polymerizable resin.
• the coupling agent may be functionalized with reactive curing groups, such as acrylates, methacrylates, epoxies, and the like.
• Examples of coupling agents include silanes such as gamma-methacryloxypropyl- trimethoxy silane, gamma-mercaptopropy ltriethoxysilane, beta-(3 ,4- epoxycyclohexyl)ethyltrimethoxysilane, gamma-glycidoxypropyltrimethoxysilane, and the like.
• the materials of the present invention can also contain suitable adjuvants such as accelerators, inhibitors, absorbers, stabilizers, pigments, dyes, viscosity modifiers, surface tension depressants and wetting aids, antioxidants, and other ingredients well known to those skilled in the art.
• suitable adjuvants such as accelerators, inhibitors, absorbers, stabilizers, pigments, dyes, viscosity modifiers, surface tension depressants and wetting aids, antioxidants, and other ingredients well known to those skilled in the art.
• each ingredient in the dental material should be adjusted to provide the desired physical and handling properties before and after cure.
• the cure rate, cure stability, fluidity, compressive strength, tensile strength and durability of the dental material typically are adjusted in part by altering the types and amounts of polymerization initiator(s) and, if present, the loading and particle size distribution of filler(s). Such adjustments typically are carried out empirically based on experience with dental materials of the prior art.
• the tooth When the dental material is applied to a tooth, the tooth can optionally be pre-treated with a primer such as dentin or enamel adhesive by methods known to those skilled in the art.
• a primer such as dentin or enamel adhesive
• a stock solution of an epoxy resin material was prepared by combining 0.50 g camphorquinone, 1.50 g diphenyliodoniumhexafluoroantimonate
• UVR 6105 is a cycloaliphatic diepoxide having the following formula:
• a stock solution of an epoxy resin/acrylate material was prepared by transferring 0.50 g camphorquinone and 1.50 g DPI SbF 6 to a glass jar followed by the addition of approximately 0.20 gram of dichloromethane solvent, 88.2 grams of UVR 6105 and 9.80 grams of Ebecryl 1830 polyester hexacrylate from Radcure Specialties. The mixture was stirred until homogeneous in the absence of light.
• a variety of donor compounds were evaluated for their photoinduced potential.
• a stock initiator solution was prepared by transferring 0.50 grams camphorquinone and 3.00 grams of DPI SbF 6 to a 250 ml polyethylene screw-top bottle. Two hundred grams of 99.5+% 2-butanone were transferred to the polyethylene bottle and the contents mixed until homogeneous. The resulting solution contained approximately 2.9 x 10 "5 moles DPISbF6/gram of stock initiator solution and 1.5 x
• the electrode was rinsed, cleaned thoroughly with ethanol, blotted dry and immersed in the irradiated solution. The millivolts relative to the control was established by pressing the mV button on the pH meter until a stable reading was obtained. The above procedure was repeated with the various donor solutions. The electrode was calibrated with unirradiated stock initiator solution before each run as described previously. The donor compounds were evaluated for their effect on cure speed of two stock resin solutions. Approximately one gram samples were prepared by transferring 2.9x10 "5 moles of each prospective donor to 1 dram glass vials followed by 1 drop of dichloromethane solvent and 1.0 grams of the stock epoxy resin or epoxy resin acrylate material. The ingredients were mixed until homogeneous.
• the data illustrates that a variety of donor compounds selected from aromatic ethers or a alkyl, aryl amino compounds wherein the aryl group has one or more electron withdrawing substituents including: carboxylic acids and esters, ketones, aldehydes, sulfonic acids and esters, nitriles and halogens serve as effective coinitiators for enhancing the cure speed of epoxy materials in the presence of the visible light sensitizer CPQ and DPISbF 6 .
• composition A The effect of an aromatic amine donor on the photopolymerization of a cycloaliphatic epoxide was evaluated.
• Two compositions were prepared as follows: Composition A
• composition A did not cure after a 60 second exposure;
• Composition B was cured to a hard solid after a 15 second exposure.
• the composition with the electron donor EDMAB exhibited a rapid photopolymerization, whereas the composition without EDMAB failed to polymerize.
• composition A(l) The effect of various diphenyl iodonium salts was evaluated in epoxy resin compositions with and without the presence of an aromatic amine.
• Three epoxy containing compositions were prepared as follows: Composition A(l)
• compositions were prepared by combining the ingredients at room temperature and stirring until homogeneous. Each composition was evaluated for cure speed by irradiation of a 2 mm thick sample with light at a wavelength of 400-500 nm from a Visilux 2 light source at a distance of 10 mm. Irradiation continued for 120s or until a soft or hard gel was formed. Results are reported in Table 2.
• the data illustrates that an epoxy composition can be rapidly photopolymerized when the amine donor EDMAB is used in combination with an iodonium salt with a PF 6 or SbF 6 counterion. No curing was observed when DPI Cl was used with or without EDMAB.
• Example 3 The experiment of Example 3 was repeated using an epoxy /acrylate resin in place of the epoxy resin.
• the epoxy /acrylate resin was prepared by combining 45.00 g UVR 6105 and 5.00 g Ebecryl 1830 at room temperature and stirring until homogeneous.
• Three epoxy/acrylate containing compositions were prepared as follows:
• a stock solution was prepared as follows:
• a second stock solution containing the aromatic amine EDMAB was prepared as follows:
• Sample solutions were prepared by varying the relative proportions of Stock Solution A and Stock Solution B in a 1 g sample. Each solution contained 2.9X10 "
• sample solutions having various concentrations of the TMB donor.
• a 2 mm thick sample of each sample solution was irradiated at a distance of 10 mm using a Visilux 2 light source.
• the gel times are reported in Table 5.
• the data illustrates that the addition of various amounts of the aromatic ether TMB results in the photopolymerization of an epoxy composition.
• a filler composition was prepared as follows: 200.3 grams of deionized water was weighed into a 1000 ml rigid poly beaker and adjusted to a pH of 3.02 with trifluoroacetic acid (Aldrich Chem. Co., Milwaukee, WI). 9.9099 grams of 3-glycidoxypropyltrimethoxysilane (United Chemical Technologies, Inc., Bristol, PA) was slowly added to the water while stirring with a magnetic teflon coated stirring rod. About 50 ml of denatured ethanol was used to rinse the silane addition beaker, and then added to the hydrolyzing aqueous silane solution. The solution was allowed to stir for about 65 minutes at room temperature to thoroughly hydrolyze the silane.
• Example 8 The dried cake from each beaker was recombined, mortar and pestled, and then screen in a sealed container on a shaker through a 74 micron nylon screen. The screened powder was then placed in a one pint jar and dried for a final time for 2 hours at 80°C. After a short cool down the jar was then sealed with a metal cap with foil lined paper seal to reduce the moisture vapor transmission into or out of the jar.
• This Example describes the preparation of epoxy resin-based composite materials containing an iodonium salt, an alpha-diketone and an optional amine electron donor.
• composition A Composition A
• composition was prepared by combining the ingredients at room temperature and stirring until homogeneous.
• Two composite materials were further prepared by combining 7.50 grams of the filler from Example 7 with 2.50 grams of Compositions A and B respectively. Samples were spatulated until a thick homogeneous paste was obtained.
• Composition A 2.50 g
• Composition B 2.50 g
• Samples were evaluated for photopolymerization by determining the hardness of a 2mm thick sample according to the following procedure.
• a 2mm thick Teflon block which had a cylindrical hole measuring about 6 mm in diameter extending through the thickness of the block was placed on a film of transparent polyethylene terephthalate (PET) such that one end of the open cylindrical hole of the die was covered by the PET film.
• PET polyethylene terephthalate
• the Teflon die was filled with the sample and another film of PET placed on top of the die covering the sample. Hand pressure was applied to the PET film to provide an approximately 2mm thick sample.
• Samples were irradiated with a Visilux 2 light source for 30 seconds by placing the light wand directly on the PET film which covered the sample at the top of the die.
• composite B which contains the donor EDMAB, exhibits significant top and bottom polymerization when post-cured for 20 or more minutes at 37°C or for 24 hrs at 25°C, whereas Composite A without EDMAB fails to exhibit significant polymerization under any of the experimental conditions.
• composition A This Example describes the preparation of epoxy-methacrylate resin-based composite materials containing an iodonium salt, an alpha-diketone and an optional amine electron donor.
• Two compositions were prepared as follows: Composition A
• composition was prepared by combining the ingredients at room temperature and stirring until homogeneous.
• Two composite materials were further prepared by combining 7.50 grams of the filler from Example 7 with 2.50 grams of Compositions A and B respectively. Samples were spatulated until a thick homogeneous paste was obtained.
• composition A Composition A
• Composition A 2.50 g
• Composition B 2.50 g
• Composite B which contains the donor EDMAB exhibits significant top and bottom polymerization when post-cured for

Landscapes

• Health & Medical Sciences (AREA)
• Oral & Maxillofacial Surgery (AREA)
• Physics & Mathematics (AREA)
• Epidemiology (AREA)
• Life Sciences & Earth Sciences (AREA)
• Animal Behavior & Ethology (AREA)
• General Health & Medical Sciences (AREA)
• Public Health (AREA)
• Veterinary Medicine (AREA)
• General Physics & Mathematics (AREA)
• Spectroscopy & Molecular Physics (AREA)
• Plastic & Reconstructive Surgery (AREA)
• Inorganic Chemistry (AREA)
• Chemical & Material Sciences (AREA)
• Epoxy Resins (AREA)
• Dental Preparations (AREA)
• Adhesives Or Adhesive Processes (AREA)
• Polymerisation Methods In General (AREA)

Priority Applications (7)

Applications Claiming Priority (2)

Publications (1)

Family

ID=25278172

Family Applications (1)

Country Status (11)

Cited By (20)

Families Citing this family (113)

Citations (2)

Family Cites Families (19)

• 1997
  • 1997-04-11 US US08/838,835 patent/US6025406A/en not_active Expired - Lifetime
• 1998
  • 1998-03-03 AU AU64443/98A patent/AU744244B2/en not_active Ceased
  • 1998-03-03 BR BR9807973-5A patent/BR9807973A/pt not_active IP Right Cessation
  • 1998-03-03 JP JP54387798A patent/JP4009753B2/ja not_active Expired - Fee Related
  • 1998-03-03 EP EP98910122A patent/EP0968459B1/en not_active Expired - Lifetime
  • 1998-03-03 DE DE69816283T patent/DE69816283T2/de not_active Expired - Lifetime
  • 1998-03-03 CN CN98804069A patent/CN1252138A/zh active Pending
  • 1998-03-03 CA CA002285420A patent/CA2285420C/en not_active Expired - Fee Related
  • 1998-03-03 KR KR1019997009260A patent/KR20010006181A/ko not_active Abandoned
  • 1998-03-03 WO PCT/US1998/004029 patent/WO1998047046A1/en not_active Ceased
• 1999
  • 1999-07-28 US US09/362,410 patent/US6043295A/en not_active Expired - Lifetime
  • 1999-10-11 NO NO994954A patent/NO994954L/no not_active Application Discontinuation