USRE45175E1 - Process for silver plating in printed circuit board manufacture - Google Patents
Process for silver plating in printed circuit board manufacture Download PDFInfo
- Publication number
- USRE45175E1 USRE45175E1 US13/655,159 US201213655159A USRE45175E US RE45175 E1 USRE45175 E1 US RE45175E1 US 201213655159 A US201213655159 A US 201213655159A US RE45175 E USRE45175 E US RE45175E
- Authority
- US
- United States
- Prior art keywords
- silver
- process according
- plating composition
- complexing agent
- metal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Abstract
Description
TABLE 1 | |||
Wet | WetForce/ | ||
Coating | Treatment | Time/Sec | Arb. Unit |
Example 1 | As prepared | 0.6 | 0.32 |
Example 1 | 3 Reflow Passes | 0.7 | 0.26 |
Example 1 | 18 hrs 40° C./93% RH 0 Reflows | 0.65 | 0.30 |
Example 1 | 18 hrs 40° C./93% RH 3 Reflows | 0.95 | 0.17 |
Example 5 | As prepared | 0.6 | 0.31 |
Example 5 | 3 Reflows Passes | 0.7 | 0.31 |
Example 5 | 16 hrs 40° C./93% RH 3 Reflows | 0.7 | 0.28 |
Example 5 | 17 days 40° C./93% RH | 1.7 | 0.12 |
Example 5 | 17 days 40° C./93% RH 3 Reflows | 1.9 | 0.04 |
Example 6 | As prepared | 0.7 | 0.29 |
Example 6 | 3 Reflow Passes | 0.7 | 0.25 |
Example 6 | 10 days 40° C./93% RH 3 Reflows | 0.9 | 0.28 |
Sn | As prepared | 0.95 | 0.34 |
Sn | 3 Reflow Passes | >5 | −0.24 |
Sn | 18 hrs 40° C./93% RH 0 Reflows | >5 | −0.2 |
Sn | 18 hrs 40° C./93% RH 3 Reflows | >5 | −0.42 |
Benzimid A | 3 Reflow Passes | 0.9 | 0.19 |
Benzimid B | As prepared | 0.8 | 0.28 |
Benzimid B | 1 Reflow | 0.95 | 0.26 |
Claims (31)