US20190284728A1 - Exhaust gas treatment method, exhaust gas treatment device, and carbon fiber manufacturing system - Google Patents

Exhaust gas treatment method, exhaust gas treatment device, and carbon fiber manufacturing system Download PDF

Info

Publication number
US20190284728A1
US20190284728A1 US16/318,208 US201716318208A US2019284728A1 US 20190284728 A1 US20190284728 A1 US 20190284728A1 US 201716318208 A US201716318208 A US 201716318208A US 2019284728 A1 US2019284728 A1 US 2019284728A1
Authority
US
United States
Prior art keywords
exhaust gas
carbonizing
flameproofing
combusting
furnace
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US16/318,208
Other languages
English (en)
Inventor
Yasuyuki Yamamoto
Yoshiyuki Hagihara
Kimio Iino
Tomonobu Abe
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Taiyo Nippon Sanso Corp
Original Assignee
Taiyo Nippon Sanso Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Taiyo Nippon Sanso Corp filed Critical Taiyo Nippon Sanso Corp
Assigned to TAIYO NIPPON SANSO CORPORATION reassignment TAIYO NIPPON SANSO CORPORATION ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: ABE, TOMONOBU, HAGIHARA, YOSHIYUKI, IINO, KIMIO, YAMAMOTO, YASUYUKI
Publication of US20190284728A1 publication Critical patent/US20190284728A1/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F23—COMBUSTION APPARATUS; COMBUSTION PROCESSES
    • F23G—CREMATION FURNACES; CONSUMING WASTE PRODUCTS BY COMBUSTION
    • F23G7/00—Incinerators or other apparatus for consuming industrial waste, e.g. chemicals
    • F23G7/06—Incinerators or other apparatus for consuming industrial waste, e.g. chemicals of waste gases or noxious gases, e.g. exhaust gases
    • F23G7/061—Incinerators or other apparatus for consuming industrial waste, e.g. chemicals of waste gases or noxious gases, e.g. exhaust gases with supplementary heating
    • F23G7/065—Incinerators or other apparatus for consuming industrial waste, e.g. chemicals of waste gases or noxious gases, e.g. exhaust gases with supplementary heating using gaseous or liquid fuel
    • D—TEXTILES; PAPER
    • D01—NATURAL OR MAN-MADE THREADS OR FIBRES; SPINNING
    • D01F—CHEMICAL FEATURES IN THE MANUFACTURE OF ARTIFICIAL FILAMENTS, THREADS, FIBRES, BRISTLES OR RIBBONS; APPARATUS SPECIALLY ADAPTED FOR THE MANUFACTURE OF CARBON FILAMENTS
    • D01F9/00—Artificial filaments or the like of other substances; Manufacture thereof; Apparatus specially adapted for the manufacture of carbon filaments
    • D01F9/08—Artificial filaments or the like of other substances; Manufacture thereof; Apparatus specially adapted for the manufacture of carbon filaments of inorganic material
    • D01F9/12—Carbon filaments; Apparatus specially adapted for the manufacture thereof
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F23—COMBUSTION APPARATUS; COMBUSTION PROCESSES
    • F23G—CREMATION FURNACES; CONSUMING WASTE PRODUCTS BY COMBUSTION
    • F23G5/00—Incineration of waste; Incinerator constructions; Details, accessories or control therefor
    • F23G5/08—Incineration of waste; Incinerator constructions; Details, accessories or control therefor having supplementary heating
    • F23G5/14—Incineration of waste; Incinerator constructions; Details, accessories or control therefor having supplementary heating including secondary combustion
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F23—COMBUSTION APPARATUS; COMBUSTION PROCESSES
    • F23G—CREMATION FURNACES; CONSUMING WASTE PRODUCTS BY COMBUSTION
    • F23G5/00—Incineration of waste; Incinerator constructions; Details, accessories or control therefor
    • F23G5/08—Incineration of waste; Incinerator constructions; Details, accessories or control therefor having supplementary heating
    • F23G5/14—Incineration of waste; Incinerator constructions; Details, accessories or control therefor having supplementary heating including secondary combustion
    • F23G5/16—Incineration of waste; Incinerator constructions; Details, accessories or control therefor having supplementary heating including secondary combustion in a separate combustion chamber
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F23—COMBUSTION APPARATUS; COMBUSTION PROCESSES
    • F23G—CREMATION FURNACES; CONSUMING WASTE PRODUCTS BY COMBUSTION
    • F23G5/00—Incineration of waste; Incinerator constructions; Details, accessories or control therefor
    • F23G5/32—Incineration of waste; Incinerator constructions; Details, accessories or control therefor the waste being subjected to a whirling movement, e.g. cyclonic incinerators
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F23—COMBUSTION APPARATUS; COMBUSTION PROCESSES
    • F23G—CREMATION FURNACES; CONSUMING WASTE PRODUCTS BY COMBUSTION
    • F23G7/00—Incinerators or other apparatus for consuming industrial waste, e.g. chemicals
    • F23G7/06—Incinerators or other apparatus for consuming industrial waste, e.g. chemicals of waste gases or noxious gases, e.g. exhaust gases
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F23—COMBUSTION APPARATUS; COMBUSTION PROCESSES
    • F23G—CREMATION FURNACES; CONSUMING WASTE PRODUCTS BY COMBUSTION
    • F23G2202/00—Combustion
    • F23G2202/10—Combustion in two or more stages
    • F23G2202/101—Combustion in two or more stages with controlled oxidant supply
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F23—COMBUSTION APPARATUS; COMBUSTION PROCESSES
    • F23G—CREMATION FURNACES; CONSUMING WASTE PRODUCTS BY COMBUSTION
    • F23G2202/00—Combustion
    • F23G2202/10—Combustion in two or more stages
    • F23G2202/102—Combustion in two or more stages with supplementary heating
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F23—COMBUSTION APPARATUS; COMBUSTION PROCESSES
    • F23G—CREMATION FURNACES; CONSUMING WASTE PRODUCTS BY COMBUSTION
    • F23G2202/00—Combustion
    • F23G2202/10—Combustion in two or more stages
    • F23G2202/103—Combustion in two or more stages in separate chambers
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F23—COMBUSTION APPARATUS; COMBUSTION PROCESSES
    • F23G—CREMATION FURNACES; CONSUMING WASTE PRODUCTS BY COMBUSTION
    • F23G2202/00—Combustion
    • F23G2202/10—Combustion in two or more stages
    • F23G2202/105—Combustion in two or more stages with waste supply in stages
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F23—COMBUSTION APPARATUS; COMBUSTION PROCESSES
    • F23G—CREMATION FURNACES; CONSUMING WASTE PRODUCTS BY COMBUSTION
    • F23G2204/00—Supplementary heating arrangements
    • F23G2204/10—Supplementary heating arrangements using auxiliary fuel
    • F23G2204/103—Supplementary heating arrangements using auxiliary fuel gaseous or liquid fuel
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F23—COMBUSTION APPARATUS; COMBUSTION PROCESSES
    • F23G—CREMATION FURNACES; CONSUMING WASTE PRODUCTS BY COMBUSTION
    • F23G2207/00—Control
    • F23G2207/30—Oxidant supply
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F23—COMBUSTION APPARATUS; COMBUSTION PROCESSES
    • F23G—CREMATION FURNACES; CONSUMING WASTE PRODUCTS BY COMBUSTION
    • F23G2209/00—Specific waste
    • F23G2209/14—Gaseous waste or fumes
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
    • Y02E—REDUCTION OF GREENHOUSE GAS [GHG] EMISSIONS, RELATED TO ENERGY GENERATION, TRANSMISSION OR DISTRIBUTION
    • Y02E20/00—Combustion technologies with mitigation potential
    • Y02E20/34—Indirect CO2mitigation, i.e. by acting on non CO2directly related matters of the process, e.g. pre-heating or heat recovery

Definitions

  • the present invention relates to an exhaust gas treatment method, an exhaust gas treatment device, and a carbon fiber manufacturing system.
  • Carbon fibers have been used as a reinforcement for various materials because they have superior specific strength, specific modulus, het resistance, chemical resistance, and so on.
  • the production method includes a plurality of steps in order to obtain desired properties.
  • flameproofing fiber is produced by pre-oxidizing in the air at 200 to 300° C. in a first step (flameproofing step). Then, carbon fibers are produced by carbonizing at 300 to 2,000° C. in an inert atmosphere (carbonizing step).
  • carbonizing step carbonizing step
  • the carbon fibers obtained in the carbonizing step is graphitized at 2,000 to 3,000° C. in an inert atmosphere (graphitizing step).
  • an exhaust gas is generated.
  • gas containing hydrogen cyanide, ammonia, carbon monoxide, carbon dioxide, methane, tar, etc. which are decomposed components of the flameproofing fiber, and the inert gas, such as nitrogen, as a base component (below, exhaust gas generated in the carbonizing step and the graphitizing step is denoted respectively by “carbonizing step-exhaust gas” and “graphitizing step-exhaust gas”) is generated (Patent Document No. 3).
  • flameproofing step-exhaust gas gas containing hydrogen cyanide, ammonia, carbon monoxide, carbon dioxide, methane, tar, and so on which are decomposed components of the acrylic fiber, and oxygen, nitrogen, and argon, as base components (below, exhaust gas generated in the flameproofing step is denoted by “flameproofing step-exhaust gas”) is generated (Patent Documents Nos. 2 and 4).
  • the exhaust gas which is generated in the flameproofing step, the carbonizing step, and the graphitizing step contains strong harmful gas, such as hydrogen cyanide, ammonia, and so on. Accordingly, an exhaust gas treatment method for detoxifying the exhaust gas generated in these steps is required.
  • Patent Document No. 1 As a conventional exhaust gas treatment method, a method in which the flameproofing step-exhaust gas and the carbonizing step-exhaust gas are blown into one treatment furnace (combustion chamber), and decomposed by air combustion has been well-known (For example, Patent Document No. 1). As another conventional exhaust gas treatment method, a method in which the flameproofing step-exhaust gas and the carbonizing step-exhaust gas are decomposed by air combustion in a separate treatment furnace, respectively has been well-known (For example, Patent Document No. 2).
  • Patent Document 1 Japanese Unexamined Patent Application, First Publication No. 2011-021779
  • Patent Document 2 Japanese Unexamined Patent Application, First Publication No. 2001-324119
  • Patent Document 3 Japanese Unexamined Patent Application, First Publication No. 2012-067419
  • Patent Document 4 Japanese Unexamined Patent Application, First Publication No. 2003-113538
  • the flameproofing step-exhaust gas, and the carbonizing step-exhaust gas and the graphitizing step-exhaust gas are different from each other in the concentration of hydrogen cyanide, etc., and the composition of the base gas (existence of oxygen). Therefore, when the flameproofing step-exhaust gas, and the carbonizing step-exhaust gas and the graphitizing step-exhaust gas are decomposed in one treatment furnace, there is a problem that hydrogen cyanide, ammonia, etc. cannot be sufficiently decomposed, and a large amount of NO X is generated by the decomposition.
  • an object of the present invention is to provide an exhaust gas treatment method which prevents the generation of NO X , and treats the flameproofing step-exhaust gas and the carbonizing step-exhaust gas with a small amount of fuel, an exhaust gas treatment device which can treat the flameproofing step-exhaust gas and the carbonizing step-exhaust gas with a small amount of fuel, and an exhaust gas treatment system which can suppress a cost increase due to an increase in the amount of gas treated.
  • the present invention provides the following exhaust gas treatment devices, exhaust gas treatment methods, a carbon fiber manufacturing equipment, and carbon fiber manufacturing systems.
  • An exhaust gas treatment device which is configured to treat exhaust gases discharged from steps of manufacturing carbon fiber from a fibrous substance
  • the exhaust gas treatment device includes:
  • a first combustion furnace which is configured to combust a carbonizing step-exhaust gas discharged from a carbonizing step in which the fibrous substance is carbonized in an inert gas atmosphere;
  • a second combustion furnace which is provided at a post-stage of the first combustion furnace, and configured to combust a flameproofing step-exhaust gas discharged from a flameproofing step in which the fibrous substance is flameproofed in an air atmosphere and a first combusting step-exhaust gas discharged from the first combustion furnace;
  • the first combustion furnace and the second combustion furnace communicate through a throttle portion
  • the first combustion furnace is provided with a first burner which is configured to combust a carbonizing step-exhaust gas by a fuel and an oxygen-enriched air;
  • an air separation device which is configured to produce nitrogen for producing the inert gas atmosphere in the carbonizing step and the oxygen-enriched air supplied into the first burner.
  • exhaust gas treatment method includes:
  • a first combusting step in which a carbonizing step-exhaust gas discharged from a carbonizing step in which the fibrous substance is carbonized in an inert gas atmosphere is treated;
  • a second combusting step in which a flameproofing step-exhaust gas discharged from a flameproofing step in which the fibrous substance is flameproofed in an air atmosphere and a first combusting step-exhaust gas discharged from the first combustion step are treated;
  • the carbonizing step-exhaust gas is combusted at a low oxygen ratio of 0.8 or less by a fuel and an oxygen-enriched air;
  • the first combusting step-exhaust gas and the flameproofing step-exhaust gas are combusted by using heat of the first combusting step-exhaust gas;
  • nitrogen for producing the inert gas atmosphere in the carbonizing step, and the oxygen-enriched air used in the first combusting step are produced by separating air.
  • a carbon fiber manufacturing equipment including equipment which is configured to produce carbon fiber from a fibrous substance, and exhaust gas treatment equipment which is configured to treat exhaust gases from the equipment which is configured to produce carbon fiber from a fibrous substance,
  • carbon fiber manufacturing equipment includes:
  • a flameproofing furnace which is configured to pre-oxidize and flameproof the fibrous substance in an air atmosphere
  • a carbonizing furnace which is provided at a post-stage of the flameproofing furnace and configured to carbonize the fibrous substance after flameproofing in an inert atmosphere;
  • a first combustion furnace which is configured to combust a carbonizing step-exhaust gas discharged from the carbonizing furnace
  • a second combustion furnace which is configured to communicate with the first combustion furnace through a throttle portion, and combust a first combusting step-exhaust gas and a flameproofing step-exhaust gas discharged from the flameproofing furnace;
  • a first burner which is provided in the first combustion furnace so as to combust the carbonizing step-exhaust gas by a fuel and an oxygen-enriched air;
  • an air separation device which is configured to produce nitrogen for producing the inert gas atmosphere in the carbonizing furnace and the oxygen-enriched air supplied into the first burner from air.
  • a carbon fiber manufacturing system including a step in which carbon fiber is produced from a fibrous substance and a step in which exhaust gases discharged from the step in which carbon fiber is produced from a fibrous substance are treated,
  • carbon fiber manufacturing system includes:
  • a flameproofing step in which the fibrous substance is pre-oxidized and flameproofed at 200° C. to 300° C. in an air atmosphere;
  • a carbonizing step in which the fibrous substance after the flameproofing step is carbonized at 300° C. to 2,000° C. in an inert gas atmosphere;
  • a first combusting step in which a carbonizing step-exhaust gas discharged from the carbonizing step is combusted at a low oxygen ratio of 0.8 or less by a fuel and an oxygen-enriched air;
  • a second combusting step in which a first combusting step-exhaust gas discharged from the first combusting step and a flameproofing step-exhaust gas discharged from the flameproofing step are combusted using heat of the first combusting step-exhaust gas;
  • an air separating step in which nitrogen for producing the inert gas atmosphere in the carbonizing step, and the oxygen-enriched air used in the first combusting step are produced by separating air.
  • an exhaust gas treatment method which prevents the generation of NO X , and treats the flameproofing step-exhaust gas and the carbonizing step-exhaust gas with a small amount of fuel
  • an exhaust gas treatment device which can treat the flameproofing step-exhaust gas and the carbonizing step-exhaust gas with a small amount of fuel.
  • FIG. 1 is a view showing an exhaust gas treatment device in a carbon fiber manufacturing method of one embodiment according to the present invention.
  • FIG. 2 is a view showing another exhaust gas treatment device in a carbon fiber manufacturing method of one embodiment according to the present invention.
  • FIG. 3 is a view showing a carbon fiber manufacturing equipment of one embodiment according to the present invention.
  • FIG. 4 is a graph showing a relationship between a concentration of NH 3 and NO X and an oxygen ratio which are discharged from the exhaust gas treatment device.
  • FIG. 5 is a graph showing decomposition behavior of HCN and formation and decomposition behavior of NO obtained by reaction analysis.
  • FIG. 6 is a graph showing decomposition behavior of NO obtained by reaction analysis when NO is added.
  • FIG. 1 is a view showing a carbon fiber manufacturing equipment including an exhaust gas treatment device of the first embodiment according to the present invention.
  • the exhaust gas treatment device of the first embodiment mainly includes a first combustion furnace 10 , a carbonizing step-exhaust gas inlet 11 , a first burner 30 , a throttle portion 50 , a second combustion furnace 20 , a flameproofing step-exhaust gas inlet 21 , and an exhaust port 22 .
  • an exhaust gas treatment method which is explained below can be carried out. Specifically, a carbonizing step-exhaust gas which is discharged from the carbonizing furnace 2 is treated in the first combustion furnace 10 , and a flameproofing step-exhaust gas which is discharged from the flameproofing furnace 1 is treated in the second combustion furnace 20 .
  • the first combustion furnace 10 is a tubular (for example, cylindrical) furnace which decomposes harmful gasses such as hydrogen cyanide, and ammonia, contained in the carbonizing step-exhaust gas by combusting the carbonizing step-exhaust gas.
  • Material for the first combustion furnace 10 is not particularly limited, and examples of the material include an alumina refractory material, and an alumina-silica refractory material.
  • the first combustion furnace 10 is provided with the first burner 30 , a first thermometer (not shown in figures), and the carbonizing step-exhaust gas inlet 11 .
  • the first burner 30 is arranged at the end part of the first combustion furnace 10 so as to be coaxial with the first combustion furnace 10 .
  • the first burner 30 produces flam in the internal space of the first combustion furnace 10 by a fuel and a combustion-supporting gas.
  • the carbonizing step-exhaust gas inlet 11 is provided in the side wall of the first combustion furnace 10 in proximity to the first burner 30 .
  • the carbonizing step-exhaust gas introduced into the first combustion furnace 10 can be burned by the flame of the first burner 30 .
  • the combustion-supporting gas supplied to the first burner 30 contains a part of oxygen-enriched air after nitrogen is separated in an air separation device 100 for producing nitrogen to be supplied to the carbonizing furnace 2 .
  • Material for the fuel is not particularly limited, but preferable examples of the fuel include gas fuel, such as city gas, and LPG, and liquid fuel, such as kerosene, and a heavy oil.
  • gas fuel such as city gas, and LPG
  • liquid fuel such as kerosene, and a heavy oil.
  • the oxygen concentration may be adjusted by adding pure oxygen in the combustion-supporting gas conditioning equipment 101 and the gas may be supplied to the first burner 30 .
  • the temperature in the first combustion furnace 10 can be raised, and the decomposition speed can be increased.
  • the residence time of the carbonizing step-exhaust gas in the combustion furnace can be shortened, so that the first combustion furnace 10 can be reduced in size.
  • the exhaust gas treatment device is provided with a control unit (not shown in figures) which controls a combustion amount of the first burner 30 based on the temperature in the first combustion furnace 10 and the temperature of second combustion furnace 20 .
  • FIG. 1 shows a case in which the carbonizing step-exhaust gas inlet 11 is provided with the first combustion furnace 10 .
  • the carbonizing step-exhaust gas inlet may be provided with the first burner 30 .
  • the first burner 30 produces flame in an inert atmosphere in the first combustion furnace 10 , and supplies the carbonizing step-exhaust gas into the first combustion furnace 10 .
  • the second combustion furnace 20 is provided at the post-stage of the first combustion furnace 10 .
  • the second combustion furnace 20 is a tubular (for example, cylindrical) furnace which decomposes harmful gasses such as hydrogen cyanide, and ammonia, contained in the flameproofing step-exhaust gas by combusting the flameproofing step-exhaust gas.
  • Material for the second combustion furnace 20 is not particularly limited, but examples of the material include alumina refractory material, and alumina-silica refractory material, similar to the first combustion furnace 10 .
  • the first combustion furnace 10 and the second combustion furnace 20 communicate with each other via the throttle portion 50 .
  • the throttle portion 50 can prevent the combustion gas in the second combustion furnace 20 from entering the first combustion furnace 10 and maintain the interior of the first combustion furnace 10 in a reducing atmosphere.
  • the exhaust gas after combusting the carbonizing step-exhaust gas in the first combustion furnace 10 is supplied into the second combustion furnace 20 via the throttle portion 50 (hereinafter, the carbonizing step-exhaust gas after being combusted in the first combustion furnace 10 is defined as “first combusting step-exhaust gas”).
  • the heat of the first combusting step-exhaust gas can be used to combust the flameproofing step-exhaust gas, and harmful gas such as hydrogen cyanide contained in the flameproofing step-exhaust gas can be combusted and decomposed.
  • the second combustion furnace 20 is provided with a flameproofing step-exhaust gas inlet 21 and an exhaust port 22 .
  • the flameproofing step-exhaust gas inlet 21 is provided with the side wall of the second combustion furnace 20 on the side of the throttle portion 50 .
  • the flameproofing step-exhaust gas can be supplied into the second combustion furnace 20 from the flameproofing step-exhaust gas inlet 21 .
  • the flameproofing step-exhaust gas inlet 21 is provided so that the flameproofing step-exhaust gas can be blown in the tangential direction of the side wall of the second combustion furnace 20 . As a result, it is possible to form a swirling flow by the flameproofing step-exhaust gas in the second furnace 20 .
  • the flameproofing step-exhaust gas in the swirling flow involves the first combusting step-exhaust gas introduced from the throttle portion 50 , and efficiently combusts and decomposes the harmful gas contained in the flameproofing step-exhaust gas.
  • the second burner 31 may be provided at a position on the side wall of the second combustion furnace 20 opposite to the flameproofing step-exhaust gas inlet 21 . It is possible to finely adjust the temperature in the second combustion furnace 20 by supplying the fuel to the second burner.
  • the carbon fiber manufacturing system in the present embodiment includes a flameproofing step in which the fibrous substance is subjected to a flameproofing treatment at 200 to 300° C. in an air atmosphere in the flameproofing furnace 1 , and a carbonizing step in which a carbonizing treatment is carried out at 300 to 2,000° C. in an inert gas atmosphere in the carbonizing furnace 2 provided at the post-stage of the flameproofing furnace 1 .
  • nitrogen is separated from air using the air separation device 100 , and the nitrogen is supplied into the carbonizing furnace 2 .
  • the carbonizing step-exhaust gas generated in the carbonizing furnace 2 is subjected to a first combusting step in the first combustion furnace 10 .
  • the flameproofing step-exhaust gas generated in the flameproofing furnace 1 is subjected to a second combusting step in the second combustion furnace 20 .
  • the first combusting step is a combustion step in which the carbonizing step-exhaust gas is combusted at a low oxygen ratio, an oxygen ratio of 0.8 or less.
  • the exhaust gas carbonizing step-exhaust gas
  • nitrogen gas containing hydrogen cyanide, ammonia, etc. at high concentrations is supplied into the first combustion furnace 10 through the carbonizing step-exhaust gas inlet 11 .
  • a fuel and a combustion-supporting gas are combusted in a temperature range from 1,000 to 1,600° C. by the first burner 30 provided in the first combustion furnace 10 , and a flame is produced.
  • the combustion-supporting gas supplied to the first burner 30 is an oxygen-enriched air after separating nitrogen from raw air in the air separation device 100 .
  • the carbonizing step-exhaust gas is combusted in the first combustion furnace 10 by the flame produced by the first burner 30 using the oxygen-enriched air and the fuel.
  • the carbonizing step-exhaust gas may be supplied from the first burner 30 into the first combustion furnace 10 .
  • the temperature inside of the first combustion furnace 10 is measured by the first thermometer (not shown in figures).
  • the temperature inside of the second combustion furnace 20 is measured by a second thermometer (not shown in figures).
  • the control unit (not shown in figures) adjusts the combustion temperature by controlling the combustion amount of the first burner 30 .
  • the combustion amount can be controlled by adjusting the amount of the fuel gas and the combustion-supporting gas supplied.
  • combustion amount is an amount of heat generated per unit time caused by combusting a fuel. As the combustion amount increases, the amount of heat generated per unit time increases, so that the temperature of the furnace increases.
  • the carbonizing step-exhaust gas to be treated in the first combustion furnace 10 is a nitrogen-based exhaust gas containing hydrogen cyanide, ammonia, and the like at a high concentration, when the combustion treatment is carried out under conditions in which the oxygen ration is higher than the stoichiometric ratio (oxygen ratio is higher than 0.8), a large amount of NO X is produced. Therefore, in the first combustion furnace 10 , treatment is carried out while forming a reducing atmosphere under combustion conditions with an oxygen ratio of 0.8 or less.
  • the oxygen ratio is controlled to 0.8 or less by decreasing the ratio of oxygen contained in the combustion-supporting gas with respect to the fuel gas.
  • the “oxygen ratio” is a value obtained by dividing the oxygen amount supplied to the burner by the theoretical oxygen amount required for combusting the fuel supplied to the burner. Therefore, theoretically, it can be said that the state where the oxygen ratio is 1.0 is a state in which complete combustion can be carried out using excessive or insufficient oxygen.
  • the harmful gas such as hydrogen cyanide, ammonia and the like contained in the carbonizing step-exhaust gas is combusted and decomposed in the first combustion furnace 10 .
  • the first combusting step-exhaust gas generated by combustion is supplied into the second combustion furnace 20 via the throttle portion 50 .
  • the second combusting step is a combustion step in which the first combustion step-exhaust gas discharged in the first combusting step and the flameproofing step-exhaust gas are combusted using the heat of the first combustion step-exhaust gas.
  • the flameproofing step-exhaust gas is an air-based exhaust gas containing hydrogen cyanide and ammonia, and has a much larger discharge amount than that of the carbonizing step-exhaust gas. Therefore, when the oxygen ratio is reduced to 0.8 or less and the combustion decomposition is attempted in the same way as the carbonizing step-exhaust gas, it is necessary to use a large amount of fuel.
  • hydrogen cyanide and ammonia can be decomposed while suppressing generation of NO X by performing combustion treatment at a low temperature even in an atmosphere in which oxygen exists.
  • the first combusting step-exhaust gas supplied from the first combustion furnace 10 through the throttle portion 50 is mixed with the flameproofing step-exhaust gas supplied from the flameproofing step-exhaust gas inlet 21 provided in the second combustion furnace 20 .
  • the flameproofing step-exhaust gas is introduced from the side wall of the cylindrical second combustion furnace 20 in the tangential direction of the side wall.
  • the flameproofing step-exhaust gas introduced in this way forms a swirling flow while involving the first combusting step-exhaust gas.
  • the first combusting step-exhaust gas and the flameproofing step-exhaust gas can be sufficiently mixed.
  • the residence time in the second combustion furnace can be increased by making the swirling flow with the flameproofing step-exhaust gas.
  • the gas such as CO or H 2 contained in the first combusting step-exhaust gas and the oxygen contained in the flameproofing step-exhaust gas are combusted.
  • the temperature inside the second combustion furnace 20 can be raised to 700° C. or higher.
  • the harmful gas such as hydrogen cyanide contained in the flameproofing step-exhaust gas is combusted and decomposed.
  • the heat of the first combusting step-exhaust gas discharged in the first combusting step is effectively utilized.
  • the second burner 31 it is also possible to stably combust the flameproofing step-exhaust gas and the first combusting step-exhaust gas by providing the second burner 31 to the inside wall of the second combustion furnace 30 .
  • the combustion amount can be controlled by supplying the fuel to the second burner 31 and adjusting the flow rate of the fuel supplied to the second burner 31 . It is also possible to control the combustion conditions by supplying the fuel and the combustion-supporting gas to the second burner 31 .
  • the second burner 31 does not need to be constantly burned, and it may be ignited when the internal temperature of the second combustion furnace 20 becomes lower than the predetermined temperature.
  • the temperature inside the second combustion furnace 20 is measured by the second thermometer (not shown in figures).
  • the control unit By controlling the oxygen ratio of the first burner 30 by the control unit (not shown in figures) based on the measured temperature, the amount of uncombusted gas flowing into the second combustion furnace 20 is controlled.
  • the temperature in the second combustion furnace 20 can be controlled.
  • the exhaust gas generated by combustion in the second combustion furnace 20 is exhausted to the outside from the exhaust port 22 , thereby completing the exhaust gas treatment method of the present embodiment.
  • the carbon fiber manufacturing equipment including the exhaust gas treatment device of the present embodiment includes the flameproofing furnace 1 for subjecting the fibrous substance to the flameproofing treatment in an air atmosphere, the carbonizing furnace 2 for subjecting the fibrous substance after the flameproofing treatment to the carbonizing treatment in an inert gas atmosphere, the air separation device 100 for separating nitrogen, which is supplied into the carbonizing furnace 2 , from air, the first combustion furnace 10 for treating the carbonizing step-exhaust gas generated in the carbonizing furnace 2 , the first burner 30 which is provided in the first combustion furnace 10 and combusts the oxygen-enriched air from the air separation device 100 and the fuel, and the second combustion furnace 20 for treating the flameproofing step-exhaust gas generated in the flameproofing furnace, and the second combustion furnace 20 is provided at the post-stage of the first combustion furnace 10 , the first combustion furnace 10 and the second combustion furnace 20 communicate with each other via the throttle portion 50 , the first combusting step-exhaust gas after combustion in the first combustion furnace 10 can be supplied into the first combustion furnace
  • the flameproofing step-exhaust gas inlet 21 is provided in the second combustion furnace 20 so that the flameproofing step-exhaust gas can be blown in the tangential direction of the side wall of the second combustion furnace 20 .
  • the flameproofing step-exhaust gas forms the swirling flow in the second combustion furnace 20 .
  • the flameproofing step-exhaust gas is combusted by mixing with the first combusting step-exhaust gas supplied from the throttle portion 50 into the second combustion furnace.
  • the flameproofing step-exhaust gas can be efficiently combusted. As a result, the amount of the fuel used to treat the carbonizing step-exhaust gas and the flameproofing step-exhaust gas can be reduced. In addition, since the carbonizing step-exhaust gas and the flameproofing step-exhaust gas can be treated by one device, the equipment cost and the maintenance cost can be reduced.
  • the second combustion furnace 20 is communicated with the first combustion furnace 10 through the throttle portion 50 in the exhaust gas treatment device 1 of the present embodiment, it is possible to prevent the gas including oxygen in the second combustion furnace 20 from entering into the first combustion furnace 10 , and maintain the inside of the first combustion furnace 10 in the reducing atmosphere.
  • the nitrogen gas which is used in the carbonizing step in an inert gas atmosphere is produced by the air separation device 100 , the remaining oxygen-enriched air after separation of nitrogen from the air is used as the combustion-supporting gas in the first combusting step, it is possible to suppress the cost increase due to upsizing of the carbon fiber manufacturing equipment.
  • the carbonizing step-exhaust gas is combusted at a low oxygen ratio having an oxygen ratio of 0.8 or less in the first combusting step, the carbonizing step-exhaust gas can be treated while suppressing generation of NOx.
  • the second combusting step in which the first combustion step-exhaust gas and the flameproofing step-exhaust gas are combusted is carried out by using the heat of the first combusting step-exhaust gas discharged from the first combusting step in which the carbonizing step-exhaust gas is treated, the amount of the fuel used in the burner can be reduced.
  • the carbonizing step-exhaust gas and the flameproofing step-exhaust gas can be treated in continuous steps, the equipment cost and the maintenance cost can be reduced.
  • FIG. 3 is a view showing a carbon fiber manufacturing equipment of a second embodiment according to the present invention.
  • a description will be given focusing on parts different from the first embodiment.
  • the carbon fiber manufacturing equipment of this embodiment is different from the first embodiment in that the graphitizing furnace 3 is provided at the post-stage of the carbonization furnace 2 .
  • carbon fiber having high elasticity can be obtained by heating the carbonized fibrous substance in an inert gas atmosphere at 2,000° C. to 3,000° C.
  • the graphitizing treatment is performed in an inert gas atmosphere, so that a part of the nitrogen produced by the air separation device 100 is also introduced into the graphitizing furnace 3 .
  • a graphitizing step-exhaust gas is a nitrogen-based gas containing hydrogen cyanide, ammonia and the like at high concentrations. Therefore, the graphitizing step-exhaust gas can be treated in the first combustion furnace 10 together with the carbonizing step-exhaust gas.
  • the graphitizing step-exhaust gas may be introduced into the first combustion furnace 10 after mixing with the carbonizing step-exhaust gas, or may be separately introduced.
  • FIG. 3 shows a case in which these gases are introduced from the graphitizing step-exhaust gas inlet 11 after mixing the graphitizing step-exhaust gas and the carbonizing step-exhaust gas in a buffer tank (not shown) or the like.
  • the exhaust gas combusted in the second combustion furnace 20 is discharged to the outside through the exhaust port 22 .
  • a heat exchanger may be connected to the exhaust port 22 , the exhaust gas introduced into each combustion furnace may be preheated by utilizing the heat of the post-treatment exhaust gas discharged from the exhaust port 22 . Thereby, it possible to lower the combustion amount of the burner of each combustion furnace, and reduce the amount of fuel used.
  • Table 1 shows the composition and flow rate of the simulated gas (here, it is denoted by simulated gas A) of the carbonizing step-exhaust gas and the graphitizing step-exhaust gas, and the simulated gas (here, it is denoted by simulated gas B) of the flameproofing step-exhaust gas.
  • simulated gas NO was used as an alternative to HCN (the validity of using NO as a simulated gas will be described later).
  • simulated gas was treated under three conditions (Conditions 1-1, 1-2, and 1-3).
  • Table 2 shows the combustion conditions of the burner of the exhaust gas treatment device and the direct-combustion type exhaust gas treatment device as a comparative example.
  • oxygen-enriched air having an oxygen concentration of 40% was used as the combustion-supporting gas and combusted at an oxygen ratio of 0.7 in the first burner 30 .
  • the temperature of the first combustion furnace 10 was 1,600° C. and the temperature of the second combustion furnace 20 was 1000° C.
  • FIG 1 Exhaust Direct- gas treatment combustion device type exhaust shown in gas treatment FIG 1 device Flow rate of city gas [Nm 3 /h] 1.3 3 Flow rate of combustion-supporting 5.3 — gas [Nm 3 /h] Flow rate of air [Nm 3 /h] — 33 Oxygen concentration of 40 20.8 combustion-supporting gas [vol %]
  • Table 3 shows the treatment test results.
  • the results of the exhaust gas treatment device shown in FIG. 1 are represented as Inventions 1 to 3
  • the results of the direct-fire type exhaust gas treatment device are shown as Comparative Examples 1 to 3.
  • the carbonizing step-exhaust gas, the graphitizing step-exhaust gas, and the flameproofing step-exhaust gas are treated with fewer fuel in the exhaust gas treatment device shown in FIG. 1 than the direct-combustion type exhaust gas treatment device.
  • the concentration of NH 3 and NOx contained in the exhaust gas after treating the simulated gas A and the simulated gas B under the condition 1-2 of Table 3 were measured by changing the oxygen ratio of the first burner 30 as shown in Table 4.
  • FIG. 4 shows the relationship between the concentration of NH 3 and NOx in the exhaust gas after treating discharged from the exhaust port 22 of the exhaust gas treatment device and the oxygen ratio.
  • the oxygen ratio of the first burner 30 is set to be larger than 0.8, the NOx tends to rapidly increase. It was confirmed that the simulated gas A is treated while suppressing the generation of NOx by setting the oxygen ratio to 0.8 or less.
  • Table 5 shows the composition and flow rate of the simulated gas A of the carbonizing step-exhaust gas and the graphitizing step-exhaust gas, and the simulated gas B of the flameproofing step-exhaust gas.
  • the flow rate of the simulated gas B was adjusted to 300, 600, and 900 Nm 3 /h (conditions 3-1, 3-2, and 3-3).
  • Table 6 also shows the burner combustion conditions under each exhaust gas condition.
  • Condition Condition Condition 3-1 3-2 3-3 Flow rate of city gas [Nm 3 /h] 15 23 31 Flow rate of combustion-supporting 10 15 20 gas [Nm 3 /h] Flow rate of air [Nm 3 /h] 73 112 150 Oxygen concentration of combustion- 30 30 30 30 supporting gas [vol %]
  • Table 7 shows the concentrations of NH 3 and NO x in the exhaust gas after treating discharged from the exhaust port 22 of the exhaust gas treatment device. From these results, it was confirmed that the exhaust gas treatment device shown in FIG. 1 decomposes NH 3 to an extremely low concentration, and furthermore, it is possible to suppress generation of NOx accompanying combustion.
  • Condition 3-1 Condition 3-2
  • Condition 3-3 NH 3 concentration 0.8 0.6 0.5 [ppm] NOx concentration 55 38 25 [ppm]
  • NO was used as an alternative simulated gas for HCN.
  • the validity of using NO as simulated gas was studied by reaction analysis in the simulation.
  • Condition 4-1 is a case where HCN is added to the first combustion furnace 10 under a reducing atmosphere and condition 4-2 is a case where NO is added.
  • Condition 4-2 Fuel CH 4 [mol] 1.0 1.0 Oxygen O 2 [mol] 1.6 1.6 Gas to be treated HCN 0.1 — [mol] NO — 0.1 N 2 0.9 0.9 Reaction temperature [° C.] 1500 1500
  • FIG. 5 shows the decomposition behavior of HCN and the generation/decomposition behavior of NO by the reaction analysis under Condition 4-1.
  • FIG. 6 shows the NO decomposition behavior by the reaction analysis when NO is added under Condition 4-2.
  • nitrogen which was separated from a raw air by the air separation device is introduced into the carbonizing furnace and the remaining oxygen enriched-air after separation of the nitrogen from the raw air was used as the combustion-supporting gas for combusting the carbonizing step-exhaust gas.
  • city gas and oxygen-enriched air having an oxygen concentration of 40% were combusted at an oxygen ratio of 0.65 in the first burner 30 .
  • the temperature of the first combustion furnace 10 was 1,600° C. and the temperature of the second combustion furnace 20 was 1000° C.
  • nitrogen which was separated from a raw air by the air separation device is introduced into the carbonizing furnace and the graphitizing furnace, and the remaining oxygen enriched-air after separation of the nitrogen from the raw air was used as the combustion-supporting gas for combusting the carbonizing step-exhaust gas and graphitizing step-exhaust gas.
  • the exhaust gas treatment method and the exhaust gas treatment device of the present invention can be used as a method and a device for treating exhaust gas containing hydrogen cyanide, ammonia and the like.

Landscapes

  • Engineering & Computer Science (AREA)
  • Environmental & Geological Engineering (AREA)
  • Mechanical Engineering (AREA)
  • General Engineering & Computer Science (AREA)
  • Chemical & Material Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • General Chemical & Material Sciences (AREA)
  • Textile Engineering (AREA)
  • Incineration Of Waste (AREA)
  • Inorganic Fibers (AREA)
US16/318,208 2016-07-20 2017-07-20 Exhaust gas treatment method, exhaust gas treatment device, and carbon fiber manufacturing system Abandoned US20190284728A1 (en)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
JP2016-142873 2016-07-20
JP2016142873A JP6491147B2 (ja) 2016-07-20 2016-07-20 排ガス処理方法、排ガス処理装置及び炭素繊維製造システム
PCT/JP2017/026273 WO2018016583A1 (ja) 2016-07-20 2017-07-20 排ガス処理方法、排ガス処理装置及び炭素繊維製造システム

Publications (1)

Publication Number Publication Date
US20190284728A1 true US20190284728A1 (en) 2019-09-19

Family

ID=60992625

Family Applications (1)

Application Number Title Priority Date Filing Date
US16/318,208 Abandoned US20190284728A1 (en) 2016-07-20 2017-07-20 Exhaust gas treatment method, exhaust gas treatment device, and carbon fiber manufacturing system

Country Status (7)

Country Link
US (1) US20190284728A1 (zh)
EP (1) EP3460328B1 (zh)
JP (1) JP6491147B2 (zh)
KR (1) KR102216266B1 (zh)
CN (1) CN109477636B (zh)
TW (1) TWI706111B (zh)
WO (1) WO2018016583A1 (zh)

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3195608A (en) * 1963-04-08 1965-07-20 Coen Co Volatile waste incinerator
US4861262A (en) * 1984-08-17 1989-08-29 American Combustion, Inc. Method and apparatus for waste disposal
JP2009174077A (ja) * 2008-01-23 2009-08-06 Mitsubishi Rayon Co Ltd 炭素繊維製造装置および炭素繊維の製造方法
US20120272657A1 (en) * 2010-09-13 2012-11-01 Membrane Technology And Research, Inc Membrane technology for use in a power generation process

Family Cites Families (21)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4154567A (en) * 1977-01-07 1979-05-15 Continental Carbon Company Method and apparatus for the combustion of waste gases
GB2116531B (en) * 1982-03-11 1985-11-20 Shell Int Research Process and apparatus for the combustion of ammonia-containing waste gases
US6401633B2 (en) * 1998-04-06 2002-06-11 Minergy Corporation Closed cycle waste combustion
HU225373B1 (en) * 1998-04-17 2006-10-28 Allan Dr Inovius Method and apparatus for the prevention of global warming, through elimination of hazardous exhaust gases of waste and/or fuel burners
JP2001324119A (ja) 2000-05-12 2001-11-22 Mitsubishi Rayon Co Ltd 炭素化炉用排ガス処理装置および炭素化炉からの排ガス処理方法
JP3892263B2 (ja) 2001-10-01 2007-03-14 三菱レイヨン株式会社 耐炎化炉、及び耐炎化炉の温度制御方法
JP2005221150A (ja) * 2004-02-05 2005-08-18 Bussan Nanotech Research Institute Inc 気相法炭素繊維製造装置の排ガス処理装置
JP3106971U (ja) * 2004-08-02 2005-01-27 ロザイ工業株式会社 直接燃焼式脱臭装置
JP5075654B2 (ja) * 2008-01-23 2012-11-21 三菱レイヨン株式会社 炭素繊維製造装置および炭素繊維の製造方法
JP5492482B2 (ja) 2009-07-14 2014-05-14 株式会社桂精機製作所 直接燃焼式脱臭炉
PL217183B1 (pl) * 2010-07-02 2014-06-30 Ics Ind Comb Systems Spółka Z Ograniczoną Odpowiedzialnością Sposób niskoemisyjnego spalania gazów odpadowych, zwłaszcza niskokalorycznych w komorach spalania przemysłowych urządzeń energetycznych i układ do niskoemisyjnego spalania gazów odpadowych, zwłaszcza niskokalorycznych w komorach spalania przemysłowych urządzeń energetycznych
JP2012067419A (ja) 2010-09-24 2012-04-05 Mitsubishi Rayon Co Ltd 炭素化炉用排ガス処理装置
JP5573544B2 (ja) * 2010-09-24 2014-08-20 三菱レイヨン株式会社 焼成炉の排ガス燃焼装置
JP2013032608A (ja) * 2011-06-29 2013-02-14 Toray Ind Inc 排ガス処理方法
NL2007381C2 (en) * 2011-09-09 2013-03-12 Duiker Comb Engineers B V A process for incinerating nh3 and a nh3 incinerator.
EP2711066B1 (en) * 2012-09-20 2021-10-27 General Electric Technology GmbH Method for cleaning an industrial waste gas comprising co2 by incineration in an oxyfuel boiler
JP6263345B2 (ja) * 2013-08-19 2018-01-17 大陽日酸株式会社 燃焼除害装置
CN103575118B (zh) * 2013-10-14 2015-09-09 广州金发碳纤维新材料发展有限公司 一种碳化处理装置
CN203927948U (zh) * 2014-05-26 2014-11-05 广州市环境保护技术设备公司 一种用于聚丙烯腈基碳纤维生产的废气处理装置
CN104315524B (zh) * 2014-09-11 2016-06-29 中复神鹰碳纤维有限责任公司 一种碳纤维低温碳化废气处理系统
JP6307769B2 (ja) * 2015-01-21 2018-04-11 大陽日酸株式会社 排ガス処理方法及び排ガス処理装置

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3195608A (en) * 1963-04-08 1965-07-20 Coen Co Volatile waste incinerator
US4861262A (en) * 1984-08-17 1989-08-29 American Combustion, Inc. Method and apparatus for waste disposal
JP2009174077A (ja) * 2008-01-23 2009-08-06 Mitsubishi Rayon Co Ltd 炭素繊維製造装置および炭素繊維の製造方法
US20120272657A1 (en) * 2010-09-13 2012-11-01 Membrane Technology And Research, Inc Membrane technology for use in a power generation process

Also Published As

Publication number Publication date
CN109477636B (zh) 2020-01-14
EP3460328B1 (en) 2021-06-30
CN109477636A (zh) 2019-03-15
KR20190016576A (ko) 2019-02-18
EP3460328A4 (en) 2020-03-25
JP2018013292A (ja) 2018-01-25
EP3460328A1 (en) 2019-03-27
KR102216266B1 (ko) 2021-02-16
TW201809548A (zh) 2018-03-16
WO2018016583A1 (ja) 2018-01-25
JP6491147B2 (ja) 2019-03-27
TWI706111B (zh) 2020-10-01

Similar Documents

Publication Publication Date Title
US10502417B2 (en) Exhaust gas treatment method and exhaust gas treatment device
KR102277236B1 (ko) 방사 버너
JP2020112280A (ja) アンモニアを混焼できるボイラ装置及び火力発電設備
US20190284728A1 (en) Exhaust gas treatment method, exhaust gas treatment device, and carbon fiber manufacturing system
US20150184851A1 (en) Porous media burner for low calorific value fuel gases
JP5635285B2 (ja) ガラス溶解炉およびガラス溶解炉における排ガスの処理方法
US9004910B2 (en) Method for combustion of a low-grade fuel
WO2018230055A1 (ja) 炭素繊維の製造方法
EP2065457B1 (en) A method of operating a pyrolysis heater for reduced NOx
JP4246355B2 (ja) コークス炉の操業方法
JP2001003055A (ja) 複式コークス炉燃焼排ガス中の窒素酸化物低減方法

Legal Events

Date Code Title Description
AS Assignment

Owner name: TAIYO NIPPON SANSO CORPORATION, JAPAN

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:YAMAMOTO, YASUYUKI;HAGIHARA, YOSHIYUKI;IINO, KIMIO;AND OTHERS;REEL/FRAME:048031/0217

Effective date: 20181218

STPP Information on status: patent application and granting procedure in general

Free format text: DOCKETED NEW CASE - READY FOR EXAMINATION

STPP Information on status: patent application and granting procedure in general

Free format text: FINAL REJECTION MAILED

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION