US20190283100A1 - Method and semifinished product for producing an at least partially hardened profiled component - Google Patents

Method and semifinished product for producing an at least partially hardened profiled component Download PDF

Info

Publication number
US20190283100A1
US20190283100A1 US16/349,658 US201716349658A US2019283100A1 US 20190283100 A1 US20190283100 A1 US 20190283100A1 US 201716349658 A US201716349658 A US 201716349658A US 2019283100 A1 US2019283100 A1 US 2019283100A1
Authority
US
United States
Prior art keywords
profiled
segment
semi
finished product
sectional shape
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US16/349,658
Other languages
English (en)
Inventor
Hermann Miß
Daniela Neul
Peter Kopfer
Martin BELL
Elmar Vogt
Werner Schmidt
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Linde and Wiemann SE and Co KG
Original Assignee
Linde and Wiemann SE and Co KG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Linde and Wiemann SE and Co KG filed Critical Linde and Wiemann SE and Co KG
Assigned to Linde + Wiemann SE & Co. KG reassignment Linde + Wiemann SE & Co. KG ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: BELL, MARTIN, MISS, Hermann, NEUL, Daniela, VOGT, ELMAR, SCHMIDT, WERNER, KOPFER, Peter
Publication of US20190283100A1 publication Critical patent/US20190283100A1/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B21—MECHANICAL METAL-WORKING WITHOUT ESSENTIALLY REMOVING MATERIAL; PUNCHING METAL
    • B21C—MANUFACTURE OF METAL SHEETS, WIRE, RODS, TUBES OR PROFILES, OTHERWISE THAN BY ROLLING; AUXILIARY OPERATIONS USED IN CONNECTION WITH METAL-WORKING WITHOUT ESSENTIALLY REMOVING MATERIAL
    • B21C37/00—Manufacture of metal sheets, bars, wire, tubes or like semi-manufactured products, not otherwise provided for; Manufacture of tubes of special shape
    • B21C37/06—Manufacture of metal sheets, bars, wire, tubes or like semi-manufactured products, not otherwise provided for; Manufacture of tubes of special shape of tubes or metal hoses; Combined procedures for making tubes, e.g. for making multi-wall tubes
    • B21C37/15—Making tubes of special shape; Making tube fittings
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B21—MECHANICAL METAL-WORKING WITHOUT ESSENTIALLY REMOVING MATERIAL; PUNCHING METAL
    • B21D—WORKING OR PROCESSING OF SHEET METAL OR METAL TUBES, RODS OR PROFILES WITHOUT ESSENTIALLY REMOVING MATERIAL; PUNCHING METAL
    • B21D22/00—Shaping without cutting, by stamping, spinning, or deep-drawing
    • B21D22/02—Stamping using rigid devices or tools
    • B21D22/022—Stamping using rigid devices or tools by heating the blank or stamping associated with heat treatment
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B21—MECHANICAL METAL-WORKING WITHOUT ESSENTIALLY REMOVING MATERIAL; PUNCHING METAL
    • B21D—WORKING OR PROCESSING OF SHEET METAL OR METAL TUBES, RODS OR PROFILES WITHOUT ESSENTIALLY REMOVING MATERIAL; PUNCHING METAL
    • B21D22/00—Shaping without cutting, by stamping, spinning, or deep-drawing
    • B21D22/02—Stamping using rigid devices or tools
    • B21D22/025—Stamping using rigid devices or tools for tubular articles
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B21—MECHANICAL METAL-WORKING WITHOUT ESSENTIALLY REMOVING MATERIAL; PUNCHING METAL
    • B21D—WORKING OR PROCESSING OF SHEET METAL OR METAL TUBES, RODS OR PROFILES WITHOUT ESSENTIALLY REMOVING MATERIAL; PUNCHING METAL
    • B21D26/00—Shaping without cutting otherwise than using rigid devices or tools or yieldable or resilient pads, i.e. applying fluid pressure or magnetic forces
    • B21D26/02—Shaping without cutting otherwise than using rigid devices or tools or yieldable or resilient pads, i.e. applying fluid pressure or magnetic forces by applying fluid pressure
    • B21D26/033—Deforming tubular bodies
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B21—MECHANICAL METAL-WORKING WITHOUT ESSENTIALLY REMOVING MATERIAL; PUNCHING METAL
    • B21D—WORKING OR PROCESSING OF SHEET METAL OR METAL TUBES, RODS OR PROFILES WITHOUT ESSENTIALLY REMOVING MATERIAL; PUNCHING METAL
    • B21D26/00—Shaping without cutting otherwise than using rigid devices or tools or yieldable or resilient pads, i.e. applying fluid pressure or magnetic forces
    • B21D26/02—Shaping without cutting otherwise than using rigid devices or tools or yieldable or resilient pads, i.e. applying fluid pressure or magnetic forces by applying fluid pressure
    • B21D26/053—Shaping without cutting otherwise than using rigid devices or tools or yieldable or resilient pads, i.e. applying fluid pressure or magnetic forces by applying fluid pressure characterised by the material of the blanks
    • B21D26/057—Tailored blanks
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B21—MECHANICAL METAL-WORKING WITHOUT ESSENTIALLY REMOVING MATERIAL; PUNCHING METAL
    • B21D—WORKING OR PROCESSING OF SHEET METAL OR METAL TUBES, RODS OR PROFILES WITHOUT ESSENTIALLY REMOVING MATERIAL; PUNCHING METAL
    • B21D35/00—Combined processes according to or processes combined with methods covered by groups B21D1/00 - B21D31/00
    • B21D35/002—Processes combined with methods covered by groups B21D1/00 - B21D31/00
    • B21D35/005—Processes combined with methods covered by groups B21D1/00 - B21D31/00 characterized by the material of the blank or the workpiece
    • B21D35/006—Blanks having varying thickness, e.g. tailored blanks
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B21—MECHANICAL METAL-WORKING WITHOUT ESSENTIALLY REMOVING MATERIAL; PUNCHING METAL
    • B21D—WORKING OR PROCESSING OF SHEET METAL OR METAL TUBES, RODS OR PROFILES WITHOUT ESSENTIALLY REMOVING MATERIAL; PUNCHING METAL
    • B21D39/00—Application of procedures in order to connect objects or parts, e.g. coating with sheet metal otherwise than by plating; Tube expanders
    • B21D39/04—Application of procedures in order to connect objects or parts, e.g. coating with sheet metal otherwise than by plating; Tube expanders of tubes with tubes; of tubes with rods
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
    • B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
    • B23K26/00—Working by laser beam, e.g. welding, cutting or boring
    • B23K26/20—Bonding
    • B23K26/21—Bonding by welding
    • B23K26/24—Seam welding
    • B23K26/28—Seam welding of curved planar seams
    • B23K26/282—Seam welding of curved planar seams of tube sections
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
    • B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
    • B23K31/00—Processes relevant to this subclass, specially adapted for particular articles or purposes, but not covered by only one of the preceding main groups
    • B23K31/02—Processes relevant to this subclass, specially adapted for particular articles or purposes, but not covered by only one of the preceding main groups relating to soldering or welding
    • B23K31/027—Making tubes with soldering or welding
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
    • C21D1/02—Hardening articles or materials formed by forging or rolling, with no further heating beyond that required for the formation
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0221—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0221—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
    • C21D8/0236—Cold rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/10—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of tubular bodies
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/08—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for tubular bodies or pipes
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/50—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for welded joints
    • C21D9/505—Cooling thereof
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
    • B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
    • B23K2101/00—Articles made by soldering, welding or cutting
    • B23K2101/006—Vehicles

Definitions

  • the invention relates to a method for producing an at least partially hardened profiled component, in which method a semi-finished product, after being heated up to a hardening temperature, is shaped in a forming tool by means of hydroforming or by means of pressing so as to produce the profiled component which, after being shaped in the forming tool, is hardened by means of quenching.
  • the invention relates to structural profiled components for motor vehicles such as, for example, A-pillars, B-pillars or other frame components that can be used for the production of monocoque car bodies.
  • the profiled component can especially be an A-pillar for a convertible car.
  • profiled components which are especially used in automotive construction, are also subject to various requirements in terms of their mechanical strength.
  • Such components should be configured so as to be, for example, mechanically stiffer in a first section, and more easily deformable in another section.
  • an A-pillar or a B-pillar as part of the crumple zone of a motor vehicle, should have a higher strength so that it does not fail in case of an impact in the area of the greatest load.
  • that same component should convert as much impact energy as possible into deformation work.
  • the A-pillars should provide sufficient support for the window frame of the windshield in order to create a survival space for the vehicle occupants, for example, in the eventuality of a vehicle roll-over. For this reason, such an A-pillar should exhibit a very high mechanical strength, especially in the transition area between the fender and the window frame.
  • profiled components are sometimes used which have a non-uniform cross section along their extension in order to be very rigid, for example, in certain places in a certain direction.
  • the shape of the cross section along the extension of the component in question makes a transition, for example, from a round basic shape to a box-like shape and then again to a round or oval shape so that different places of the component are provided with the appertaining section-specific contours of the profile and the corresponding transitions of the various profile cross sections.
  • Such components can be produced, for instance, by means of the so-called U/O bending method in which a flat metal blank is used to first create a component with a U-shaped cross section and it is then shaped in a second work step to create a closed O-profile.
  • the component can be bent in the direction of its extension so that an extension that was originally configured as a straight line is shaped into a two-dimensional or three-dimensional extension curve.
  • a semi-finished product can be made which, in another work step, ensures a collapse of the cross section by means of a shaping mandrel that is inserted into the blank.
  • European patent specification EP 2 282 853 B1 discloses a support core for such a U/O shaping method which is employed to shape blanks into a structured hollow profile.
  • the support core has a plurality of support members connected to each other, whereby, when the individual support members are in a position where they have been pushed together, they form the inside contour of the hollow profile that is to be produced so as to be at least partially flat and they are connected to each other via coupling elements.
  • a blank is first imparted with a U-shape. Then, the support core is inserted into the U-shaped blank in order to then shape the blank into a hollow profile by means of a U/O shaping process or by employing a rolling technique.
  • German patent specification DE 10 2009 003 668 A1 discloses a method and a device for the production of closed profiles, whereby a blank is placed onto the upward-facing edges of the side walls of a first die.
  • a U-shaped punch is moved into the matrix of the first die, thereby pre-shaping the blank.
  • the blank acquires an at least partially U-shaped cross section, whereby the U-shaped punch remains positioned in the matrix of the first die.
  • the U-shaped punch is then removed from the U-shaped blank and from the matrix of the first die, and a support core is inserted into the U-shaped blank.
  • a second die located opposite from the first die is put into position. Via the side walls of the second die, which rest on the side walls of the first die, the side walls of the first die are moved relative to the matrix of the first die, so that the U-shaped, bent blank is shaped into a profile with a closed cross section.
  • sections of a tube having a round or circular cross-section are shaped in such a way that the cross-section along the extension of the tube is tapered.
  • a bending method is employed to impart the thus-formed tube with a shape that follows a two-dimensional or three-dimensional curve.
  • the thus-created semi-finished product is imparted with its final shape by means of hydroforming.
  • the semi-finished product has to undergo an intermediate heat treatment so that it can be shaped by means of the hydroforming step.
  • the semi-finished product can also consist of two profiled segments that have been welded together and that have already been pre-shaped so as to be conical, and after these profiled segments have been welded, they are bent in a bending machine so as to approximate the envisaged final shape. All in all, however, this method proves to be quite complex since the cold-work hardening that takes place during the production of the semi-finished product has to be compensated for by means of a heat treatment prior to the hydroforming process.
  • the semi-finished product is consist of two pre-shaped tubular profiled segments.
  • the ends of the individual profiled segments are arranged in such a way that they can be slid into each other in order to ensure a gas-tight closure for the subsequent hydroforming process.
  • This requires for both ends of the profiled segments to undergo a special treatment—which is also subject to strict tolerance requirements—so as to achieve a gas-tight seal between the two profiled segments.
  • both profiled segments are then joined by means of a positive-fit, radially circumferential connection which, however, has an influence on the final shape of the profiled component that is to be produced.
  • the invention is based on an objective of putting forward an improved method and an improved semi-finished product for said method, thus allowing a simplification of the development process as well as a reduction in the investment costs for the requisite production machines.
  • the method according to the invention for producing an at least partially hardened profiled component provides that, to start with, a first profiled segment, which has a uniform cross-sectional shape along its extension, and a second profiled segment, which has a non-uniform cross-sectional shape along its extension, are joined together at a joint in order to form at least part of a semi-finished product, wherein the first and the second profiled segments have cross-sectional shapes that essentially match at the joint.
  • the semi-finished product After the semi-finished product has been heated up to a hardening temperature, it is then shaped in a forming tool by means of hydroforming or by means of pressing so as to produce the profiled component which is subsequently hardened inside the forming tool by means of quenching.
  • the first profile can be configured as a round tube.
  • the first profiled segment can be configured as a uniform oval or box-like profile. Both profiled segments can be produced by means of profile rolling processes that are relatively simple and manageable, as a result of which the production costs for the individual sections of the semi-finished product as well as the investment costs for the requisite tools can be significantly reduced.
  • the invention also assumes that only a few areas, or even just one single area—for example, in the form of the second profiled segment having a non-uniform cross-sectional shape along its extension as the transition area has to be configured between two uniform profiled segments in order to meet the necessary requirements made of the mechanical properties.
  • the total length of this second profile element can be reduced from about 1.5 m to about 0.4 m. This permits the use of considerably smaller and thus cheaper tools.
  • the present method entails the advantage that any structural changes in the profiled segments are automatically compensated for if these changes result from the production process of the profiled segments or from the creation of the joined connection between the profiled segments. Owing to the heat treatment prior to the hydroforming process, such structural changes do not occur in the finished profiled component.
  • the first profiled segment can be made in a way that is geometrically extremely simple and cost-effective, a process in which the cost-intensive shaping steps for producing the semi-finished product are then limited to the second profiled segment.
  • the shaping in the forming tool can be carried out by means of simple pressing. This is particularly the case for geometrically simple profiled components in which collapsing of the profile caused by the pressing procedure is not to be expected at all or else only to a tolerable extent. In contrast, if collapsing of the profile has to be prevented—that is to say, if it has to be ensured that the wall of the semi-finished product will come to rest against the contour of the forming tool—then hydroforming is employed.
  • the second profiled segment when the second profiled segment is produced, it is made with a connecting end whose cross-sectional shape essentially matches the cross-sectional shape of the first profiled component.
  • the profiled segments can be joined by an integral bond, for instance, by means of welding, especially preferably by means of laser welding, particularly by means of orbital laser welding.
  • Such joining operations allow a very simple production of the joined connection between the profiled segments.
  • the profiled segments are especially preferably butt-welded, a measure that allows high throughput rates in the production facility.
  • At least a third profiled segment is joined to the first or to the second profiled segment, said third segment having either a uniform or a non-uniform cross-sectional shape along its extension.
  • At least one of the profiled segments is made of a hardenable alloy.
  • the alloy in question can be hardened in that it is heated to a hardening temperature and subsequently quenched, in other words, it is quickly cooled off.
  • the alloy preferably consists of steel, particularly a boron-alloyed steel. During the hardening procedure, the component is heated up to the hardening temperature.
  • the hardening temperature is a temperature above the structural transformation temperature which, for example, in the case of a steel material, causes a structural transformation into an austenitic structure. Due to the subsequent rapid cooling, i.e. the quenching, the structure is transformed into a martensitic structure that is permanently retained when the material is in its cooled state. In comparison to the initial structure, the martensitic structure is harder.
  • the hardness of the material is particularly high after the hardening when compared to the hardness that prevailed before. Particularly well-suited for this are steel materials, especially preferably boron-alloyed steel grades.
  • At least partially high-strength steel components can be made.
  • An example of such a steel grade is 22MnB5 (see the German publication titled SZFG material sheet 11-112, status as of May 2014, which can be downloaded at: http://www.salzgitter-flachstahl.de/fileadmin/mediadb/szfg/informationsmaterial/ istinformatione n/kaltgewalztes_feinblech/deu/22mnb5.pdf).
  • the hydroforming is carried out by a pressurized gas that serves as the forming medium, especially at a pressure between 300 bar and 600 bar, whereby the quenching is carried out with a separate cooling medium which is conveyed into the forming tool, especially into the shaped profiled component, after the hydroforming process.
  • pressurized gas for shaping the semi-finished product into the finished component has the advantage that, on the one hand, the provision of the gas in the above-mentioned pressure range is considerably cheaper than the provision of a pressurized liquid of the type employed in hydroforming.
  • the hydroforming or pressing of the semi-finished product is carried out at a hardening temperature, for instance, above 950° C.
  • This temperature has to be present before the beginning of the quenching in order for the desired hardening to be achieved.
  • the high temperature during the shaping renders the steel more resilient so that it can be shaped by means of the pressurized gas at pressures that are well below the pressures normally employed during hydroforming.
  • a gas fundamentally exhibits a lower thermal capacity and thermal conductivity than a liquid, so that the temperature of the semi-finished product is only negligibly lowered when the forming medium is introduced.
  • a gas or a liquid having a relatively higher thermal conductivity or thermal capacity is preferably employed as the cooling medium; for instance, water or a water-oil emulsion can be used as the cooling medium.
  • the method for the hydroforming and the subsequent quenching can be based on the method disclosed in international patent application WO 98/54370 A1.
  • the first profiled segment can be produced by means of a profile rolling method, especially by means of roller/roll profiling, while the second profiled segment is produced by means of a U/O bending method.
  • a U/O bending method is the so-called T3® method of ThyssenKrupp Steel, which is described, for example, in European patent specification EP 2 205 370 B1, in European patent specification EP 2 282 853 B1 or in German patent application DE 10 2009 003 668 A1.
  • the profile segment in question is joined at the seam of the sides that are bent onto each other, preferably by means of welding, to form a closed hollow profile that is sufficiently liquid-tight so that it can be expanded during the subsequent hydroforming process or at least so that, following a pressing operation, it can hold the cooling medium needed for the quenching.
  • the structural changes and tensions introduced into the material by this welding operation and the resultant structural transformation processes are largely or completely compensated for when the material is heated up to a hardening temperature, so that the appertaining seam on the finished profiled components no longer, or almost no longer, constitutes a weak spot.
  • a semi-finished product for producing an at least partially hardened profiled component has at least two profiled segments whose extensions are arranged one after the other and which are joined together at a joint in such a way that the semi-finished product can be shaped by means of hydroforming or by means of pressing, whereby, along their appertaining extensions, the first profiled segment has a uniform cross-sectional shape while the second profiled segment has a non-uniform cross-sectional shape, and the profiled segments have essentially matching cross-sectional shapes at the joint.
  • a semi-finished product configured in this manner and preferably produced by means of the method described above can be adapted very well to the pressing process or to the hydroforming process, whereby, on the one hand, the strength properties of the produced profiled component are optimized with respect to the amount of material that has been used and shaped. In particular, this also makes it possible to meet the recent requirements for lightweight construction in modern motor vehicles since less material can be used in the areas of the profiled components that are less stressed.
  • the second profiled segment can be provided with a connecting end whose cross-sectional shape essentially matches the cross-sectional shape of the first profiled component.
  • the profiled segments can be joined by an integral bond, for instance, by means of welding, especially preferably by means of laser welding, particularly by means of orbital laser welding.
  • the profiled segments can have connecting ends that are preferably butt-welded at the joint.
  • Such joining operations allow a very simple creation of the joined connection between the profiled segments.
  • the profiled segments are especially preferably butt-welded, a measure that allows high throughput rates in the production facility.
  • the semi-finished product prefferably, it can be provided for the semi-finished product to have at least a third profiled segment that has either a uniform or else a non-uniform cross-sectional shape along its extension.
  • the semi-finished product can already be pre-shaped as a function of the desired final shape so that it can be optimally adapted to the subsequent hydroforming process.
  • the at least one profiled segment consists of an alloy that can be hardened by being heated up to a hardening temperature and subsequently quenched, whereby the alloy preferably consists of steel, particularly a boron-alloyed steel.
  • the semi-finished product can already be pre-shaped or pre-bent so as to match the final shape of the profiled components so that the degrees of bending necessary during the hydroforming method can be reduced to an extent that is permissible for the material in question.
  • the second profiled segment follows a two-dimensional and/or a three-dimensional curve, whereby the first profiled segment or else other profiled segments attached to the second profiled segment are shaped so as to be straight, in other words, so as to follow in the direction of the extension of a straight line.
  • complex production steps such as, for instance, the bending of the profiled segment or the creation of a bent shape, can be concentrated on the second profiled segment, which is already more cost-intensive to produce anyway.
  • extension of the appertaining profiled segment refers to the part that is subsequently shaped in the forming tool.
  • a conical expansion that might be provided at one end of the profiled segment for attaching a feed connection piece for the hydroforming medium or for the cooling medium is not included under the concept of “extension”.
  • FIG. 1 a view of the first profiled segment according to the invention, of the second profiled segment and of a profiled segment before being joined;
  • FIG. 2 a side view of a semi-finished product according to the invention
  • FIG. 3 a side view from the left onto a profiled component according to the invention
  • FIG. 4 a side view from the right onto a profiled component according to the invention
  • FIG. 5 a schematic view from below of a semi-finished product consisting of a first profiled segment and of a second profiled segment;
  • FIG. 6 a schematic view from below of a semi-finished product with a first profiled segment and a second profiled segment;
  • FIG. 7 a schematic view of a production system according to the invention.
  • FIG. 8 a schematic view of the production method according to the invention, in individual steps.
  • FIG. 1 schematically shows the constituents with which the semi-finished product 1 according to the invention can be produced, said product being shown in the joined state in FIG. 2 .
  • a profiled component 2 is shown in side views from the left in FIG. 3 and in side views from the right in FIG. 4 .
  • the profiled component 2 forms an A-pillar 8 of a convertible that has to be configured so as to be very stable in case the convertible rolls over.
  • the area between an upper tube 3 and a lower tube 4 has to be configured so as to be very stable, and in the present case, this area is formed by an intermediate piece 5 .
  • FIG. 1 shows the upper tube 3 that forms the first profiled segment 19 as set forth in the invention.
  • the profiled segment 19 has a uniform cross-sectional shape along its extension 22 .
  • the cross-sectional shape 9 which is shown here as being circular by way of an example, is the same at every place along the extension 22 .
  • the extension 22 itself follows a straight line 29 in the first profiled segment 19 .
  • the first profiled segment 19 is provided with at least one connecting end 31 . Owing to the uniform cross-sectional shape 9 , which can be seen, for example, in FIG. 5 , the connecting ends 31 of the first profiled segment 19 are likewise configured so as to be the same.
  • connection piece for feeding in a forming medium or a cooling medium can be attached so as to create a seal.
  • conical expansion is located in a part of the appertaining profiled segment that does not have to be included in the concept of “extension”.
  • the second profiled segment 20 has a non-uniform cross-sectional shape 9 , 10 along its extension 22 , whereby in the present case, said shape expands starting at a connecting end 31 towards a connecting end 32 of the second profiled segment 20 .
  • the extension 22 of the second profiled segment 20 follows an at least two-dimensional curve 30 .
  • the two-dimensional curve 30 can also be a three-dimensional curve 30 which, in the views of FIGS. 1 and 2 , additionally extends into the plane of the page.
  • the second profiled segment as an intermediate piece 5 , has the two differently configured connecting ends 35 , 36 , whereby the connecting end 35 is shaped during the production of the profiled segment 20 in such a way that it essentially matches the first profiled segment 19 .
  • the second connecting end 36 which lies on the second profiled segment 20 along the extension 22 opposite from the first connecting end 35 —in turn, is shaped so as essentially match another connecting end 32 of a third profiled segment 21 .
  • the third profiled segment 21 is shown at the bottom of FIG. 1 . It forms the lower tube 4 of the A-pillar 8 shown in FIG. 2 and it fundamentally has the same properties as the first profiled segment 19 . Diverging from this, however, the cross-sectional shape of the third profiled segment 21 according to the view of FIG. 6 does not have a circular shape but rather, for example, can have an oval cross-sectional shape. It is also possible to select a box-like shape or a shape that is different but that is uniform over the course of the extension 22 . These cross-sectional shapes 9 , 10 would also be possible for the first profiled segment 19 . Other, different profiled segments can adjoin the first profiled segment 19 or else the other profiled segments 20 , 21 so as to form the semi-finished product 1 according to the invention.
  • FIG. 2 shows the semi-finished product 1 with the joined upper tube 3 , the lower tube 4 and the intermediate piece 5 joined between them, and they are welded at the joints 6 , 7 .
  • a well-suited welding method here is especially one in which the individual profiled segments 19 , 20 , 21 are positioned so as to abut each other.
  • the addition of welding filler is likewise possible.
  • the semi-finished product 1 likewise has an extension 22 , whereby the result is that it has a non-uniform cross-sectional shape along its extension 22 .
  • the extension 22 of the semi-finished product 1 here follows a curve 30 that can be configured so as to be two-dimensional or else three-dimensional.
  • FIGS. 3 and 4 show the finished profiled components 2 in the form of the A-pillars 8 , whereby it can be seen here that the joints 6 , 7 shown in FIG. 2 are hardly or not at all present on the finished profiled components 2 .
  • FIGS. 5 and 6 show the various cross-sectional shapes 9 , 10 of the profiled segments 19 , 20 , 21 , whereby the cross-sectional shape 9 should depict an approximately circular form and the cross-sectional shape 10 an approximately oval form. Instead of a circle or an oval, there can also be an irregularly shaped contour or a box-like shape. This depends on the desired final shape of the profiled component 2 as well as on the production parameters of the hydroforming method with which the semi-finished product 1 is formed into its final shape.
  • FIG. 7 schematically shows a production system 33 in which the profiled component 2 according to the invention can be produced.
  • This production system 33 has an installation 16 for producing the semi-finished product 16 in which there is a tube feed mechanism 14 for producing the first profiled segment 19 , that is to say, the upper tube 3 , as well as for producing and feeding in the third profiled segment, i.e. the lower tube 4 .
  • the production installation 16 for the semi-finished product has a U/O processing station where the second profiled segment 20 , that is to say, the intermediate piece 5 , is produced.
  • the upper tube 3 , the lower tube 4 as well as the intermediate piece 5 are then fed inside the production installation 16 for the semi-finished product to a joining station 13 where the semi-finished product 1 is created by joining the upper tube 3 , the lower tube 4 and the intermediate piece 5 .
  • the semi-finished product 1 is then fed to a heating device 17 where it is heated up to a hardening temperature, for example, above 950° C., in order to subsequently be fed in its heated state to the forming tool 11 for the subsequent shaping.
  • the shaping takes place inside the forming tool 11 .
  • the semi-finished product 1 is shaped into the profiled component 2 either by means of pressing or hydroforming 26 .
  • the hydroforming 26 is carried out in that a pressurized and optionally preheated gas that serves as the forming medium is fed into the interior of the semi-finished product 1 so that the material of the semi-finished product 1 , under the influence of the gas pressure, comes to rest against the contour of the forming tool 11 and in this process, the profiled component 2 acquires its final shape. The profiled component 2 thus produced then remains in the forming tool 11 for the time being.
  • the gas that serves as the forming medium is subsequently vented from the forming tool 11 and replaced by a cooling medium that then performs the quenching 27 of the profiled component 2 and thus the hardening.
  • the forming tool 11 and the heating device 17 can each be part of a physically interrelated hydroforming installation 18 .
  • the formed and hardened profiled component 2 in its final shape can still be fed to an aftertreatment station 12 where, for instance, by means of laser cutting, any protruding edges or burrs or else conical expansions that might have been provided at the ends for the hydroforming 26 can then be removed.
  • the production method 34 schematically shown in FIG. 8 is as follows:
  • the profile production 23 is carried out for the first and second and optionally additional profiled segments 19 , 20 21 which are subsequently put together to create the semi-finished product 1 by means of joining 24 .
  • the semi-finished product 1 is brought to a hardening temperature, for instance, above 950° C., in order to subsequently impart the profiled component 2 with its final shape by means of hydroforming 26 .
  • the profiled component 2 is hardened by means of quenching 27 and by the structural transformation that takes place in this process.
  • an aftertreatment 28 can be carried out in order to remove any protruding edges and burrs.
  • the method 34 according to the invention or the semi-finished product 1 according to the invention make it possible to produce partially as well as completely hardened profiled components.
  • Putting together the semi-finished product 1 out of various profiled components 19 , 20 , 21 allows the use of profiled segments made of different materials having, for example, different hardening characteristics, so that in a single work step, differing degrees of hardening occur in the same profiled component 2 during the quenching 27 down from the hardening temperature.

Landscapes

  • Engineering & Computer Science (AREA)
  • Mechanical Engineering (AREA)
  • Chemical & Material Sciences (AREA)
  • Physics & Mathematics (AREA)
  • Thermal Sciences (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Materials Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Fluid Mechanics (AREA)
  • Optics & Photonics (AREA)
  • Plasma & Fusion (AREA)
  • Manufacturing & Machinery (AREA)
  • Shaping Metal By Deep-Drawing, Or The Like (AREA)
  • Bending Of Plates, Rods, And Pipes (AREA)
  • Heat Treatment Of Articles (AREA)
US16/349,658 2016-01-12 2017-11-20 Method and semifinished product for producing an at least partially hardened profiled component Abandoned US20190283100A1 (en)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
DE102016123265.3A DE102016123265A1 (de) 2016-12-01 2016-12-01 Verfahren und Halbzeug zur Herstellung eines wenigstens partiell gehärteten Profilbauteils
DE102016123265.3 2016-12-01
PCT/EP2017/079725 WO2018099744A1 (de) 2016-12-01 2017-11-20 Verfahren und halbzeug zur herstellung eines wenigstens partiell gehärteten profilbauteils

Publications (1)

Publication Number Publication Date
US20190283100A1 true US20190283100A1 (en) 2019-09-19

Family

ID=60388071

Family Applications (1)

Application Number Title Priority Date Filing Date
US16/349,658 Abandoned US20190283100A1 (en) 2016-01-12 2017-11-20 Method and semifinished product for producing an at least partially hardened profiled component

Country Status (7)

Country Link
US (1) US20190283100A1 (ja)
EP (1) EP3548197B1 (ja)
JP (1) JP7043496B2 (ja)
CN (1) CN110267750B (ja)
DE (1) DE102016123265A1 (ja)
ES (1) ES2887341T3 (ja)
WO (1) WO2018099744A1 (ja)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2022132610A1 (en) * 2020-12-14 2022-06-23 Novelis Inc. Roll forming system with heat treatment and associated methods
US11383767B2 (en) * 2018-09-21 2022-07-12 Toyota Jidosha Kabushiki Kaisha Front pillar and manufacturing method therefor
EP4110682A4 (en) * 2020-02-24 2024-04-03 Multimatic Inc. MULTI-THICK WELDED VEHICLE RAIL

Families Citing this family (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP7368294B2 (ja) 2020-03-31 2023-10-24 三菱電機株式会社 冷却配管およびアンテナ装置

Family Cites Families (25)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5333775A (en) * 1993-04-16 1994-08-02 General Motors Corporation Hydroforming of compound tubes
SE9702058L (sv) * 1997-05-30 1998-11-16 Accra Teknik Ab Förfarande för framställning av härdade metalliska hålkroppar av tunnväggig stålplåt genom formblåsning
DE10016025B4 (de) * 2000-03-31 2005-06-16 Hde Solutions Gmbh Verfahren zur Herstellung von Hohlkörpern
JP2001321843A (ja) * 2000-05-17 2001-11-20 Nippon Steel Corp 車体の骨格部材およびその骨格部材の成形方法
JP3816405B2 (ja) * 2002-02-01 2006-08-30 アイシン高丘株式会社 ハイドロフォーム法、ハイドロフォーム筒状部材
CA2417248A1 (en) * 2003-01-17 2004-07-17 Robert Walther Method of manufacturing a fuel filler tube
JP2005118811A (ja) * 2003-10-15 2005-05-12 Toyota Motor Corp ハイドロフォーム用素管、ハイドロフォーム用素管の製造方法およびハイドロフォーム成形品
DE102004013511B4 (de) * 2004-03-19 2007-03-01 Daimlerchrysler Ag Karosseriesäule
US7484298B2 (en) * 2006-02-21 2009-02-03 Gm Global Technology Operations, Inc. Method for forming a complex-shaped tubular structure
DE102007018281A1 (de) 2007-04-18 2008-10-23 Volkswagen Ag Werkzeug zum Innenhochdruckformen, sowie Verfahren zum Innenhochdruckformen
DE102007050337B4 (de) 2007-10-18 2009-12-31 Thyssenkrupp Steel Ag Formgestauchter Hohlkörper
JP2009220141A (ja) * 2008-03-14 2009-10-01 Marujun Co Ltd パイプ製品の製造方法及び同製造装置
DE102008022402A1 (de) 2008-05-06 2009-11-19 Ps Werkzeuge Vorrichtungen Metallbearbeitungs Gmbh Stützkern für die Herstellung von Hohlprofilen
US9694413B2 (en) 2009-03-19 2017-07-04 Magna International Inc. Method of producing tailored tubes
DE102009003668B4 (de) 2009-03-24 2011-05-26 Thyssenkrupp Steel Europe Ag Vorrichtung und Verfahren zur Herstellung zumindest teilweise geschlossener Profile oder Halbzeuge aus einer Platine
JP5287565B2 (ja) * 2009-07-15 2013-09-11 新日鐵住金株式会社 鋼管の熱間成形装置およびその方法
US9033398B2 (en) * 2010-03-29 2015-05-19 GM Global Technology Operations LLC Multi-thickness tube for hydroformed members
JP4920772B2 (ja) * 2010-06-18 2012-04-18 リンツリサーチエンジニアリング株式会社 フランジ付金属製パイプ製造装置及びその製造方法並びにブロー成形金型
DE102011051965A1 (de) * 2011-07-20 2013-01-24 Benteler Automobiltechnik Gmbh Verfahren zur Herstellung eines rohrförmigen Strukturbauteils für ein Kraftfahrzeug und Strukturbauteil
DE102011055643A1 (de) * 2011-11-23 2013-05-23 Thyssenkrupp Steel Europe Ag Verfahren und Umformwerkzeug zum Warmumformen und Presshärten von Werkstücken aus Stahlblech, insbesondere verzinkten Werkstücken aus Stahlblech
DE102012008003A1 (de) * 2012-04-20 2013-10-24 Knorr-Bremse Systeme für Nutzfahrzeuge GmbH Scheibenbremse für Fahrzeuge
CN105216573B (zh) * 2014-06-06 2017-11-28 上海宝钢高新技术零部件有限公司 管状扭力梁及成形方法
CN104512472A (zh) * 2014-12-17 2015-04-15 无锡朗贤汽车组件研发中心有限公司 车辆上的b柱及制造方法
JP5869158B1 (ja) * 2015-01-13 2016-02-24 リンツリサーチエンジニアリング株式会社 フランジ付アルミニウム製パイプを製造する為のブロー成型金型及びその金型を備えたフランジ付アルミニウム製パイプ装置、並びにフランジ付アルミニウム製パイプの製造方法
CN105921584A (zh) * 2016-04-19 2016-09-07 南京航空航天大学 超高强度钢空心构件气压胀形方法

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US11383767B2 (en) * 2018-09-21 2022-07-12 Toyota Jidosha Kabushiki Kaisha Front pillar and manufacturing method therefor
EP4110682A4 (en) * 2020-02-24 2024-04-03 Multimatic Inc. MULTI-THICK WELDED VEHICLE RAIL
WO2022132610A1 (en) * 2020-12-14 2022-06-23 Novelis Inc. Roll forming system with heat treatment and associated methods

Also Published As

Publication number Publication date
ES2887341T3 (es) 2021-12-22
CN110267750B (zh) 2021-12-14
JP2020500714A (ja) 2020-01-16
WO2018099744A1 (de) 2018-06-07
CN110267750A (zh) 2019-09-20
EP3548197B1 (de) 2021-07-21
DE102016123265A1 (de) 2018-06-07
EP3548197A1 (de) 2019-10-09
JP7043496B2 (ja) 2022-03-29

Similar Documents

Publication Publication Date Title
US20190283100A1 (en) Method and semifinished product for producing an at least partially hardened profiled component
JP5418624B2 (ja) 自動車車体の側部構造
US9248490B2 (en) Method of manufacturing a tubular structural part, and tubular structural part
DE102009040935B4 (de) Verfahren zum Herstellen von Bauteilen, insbesondere Karosseriebauteilen für ein Kraftfahrzeug, sowie Karosseriebauteil
US20140191536A1 (en) Method, vehicle reinforcement & vehicle
US20100086803A1 (en) Hot-formed profile
US8776568B2 (en) Bent member and an apparatus and method for its manufacture
CN102199699A (zh) 用于制造汽车元件的方法和车身构件
US20160258035A1 (en) Method for producing a hot-formed and quench-hardened motor vehicle component formed by internal high-pressure forming
JP2009509775A (ja) スタンピングされたシート（ｓｔａｍｐｅｄｓｈｅｅｔ）をロール成形する連続プロセス
TWI791637B (zh) 製造冷軋構件的方法
CN115151476B (zh) 多厚度焊接式车用钢材管状结构及其制备方法
KR101028647B1 (ko) 하이드로포밍을 이용한 고강도 스테인레스 엔진크레이들제조방법
EP1342515A1 (en) Process for the manufacture of closed, hardened sections with no cross-sectional limits
US9283602B2 (en) Process and apparatus for producing a hollow body, and hollow body

Legal Events

Date Code Title Description
AS Assignment

Owner name: LINDE + WIEMANN SE & CO. KG, GERMANY

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:MISS, HERMANN;NEUL, DANIELA;KOPFER, PETER;AND OTHERS;SIGNING DATES FROM 20190430 TO 20190507;REEL/FRAME:049167/0325

STPP Information on status: patent application and granting procedure in general

Free format text: DOCKETED NEW CASE - READY FOR EXAMINATION

STPP Information on status: patent application and granting procedure in general

Free format text: RESPONSE TO NON-FINAL OFFICE ACTION ENTERED AND FORWARDED TO EXAMINER

STPP Information on status: patent application and granting procedure in general

Free format text: NON FINAL ACTION MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: RESPONSE TO NON-FINAL OFFICE ACTION ENTERED AND FORWARDED TO EXAMINER

STPP Information on status: patent application and granting procedure in general

Free format text: FINAL REJECTION MAILED

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION