US20180273869A1 - Steel wire with excellent corrosion resistance and appearance after processing - Google Patents

Steel wire with excellent corrosion resistance and appearance after processing Download PDF

Info

Publication number
US20180273869A1
US20180273869A1 US15/763,975 US201615763975A US2018273869A1 US 20180273869 A1 US20180273869 A1 US 20180273869A1 US 201615763975 A US201615763975 A US 201615763975A US 2018273869 A1 US2018273869 A1 US 2018273869A1
Authority
US
United States
Prior art keywords
steel wire
coating
wire rod
lubricating coating
water
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US15/763,975
Other languages
English (en)
Inventor
Hirotaka Ito
Shigehiro Yamane
Pham Van DUC
Tsuyoshi Hatakeyama
Shinobu Komiyama
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Kobe Steel Ltd
Nihon Parkerizing Co Ltd
Original Assignee
Kobe Steel Ltd
Nihon Parkerizing Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kobe Steel Ltd, Nihon Parkerizing Co Ltd filed Critical Kobe Steel Ltd
Priority claimed from PCT/JP2016/078500 external-priority patent/WO2017057385A1/ja
Assigned to NIHON PARKERIZING CO., LTD., KABUSHIKI KAISHA KOBE SEIKO SHO (KOBE STEEL, LTD.) reassignment NIHON PARKERIZING CO., LTD. ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: HATAKEYAMA, TSUYOSHI, KOMIYAMA, SHINOBU, DUC, Pham Van, YAMANE, Shigehiro, ITO, HIROTAKA
Publication of US20180273869A1 publication Critical patent/US20180273869A1/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B05—SPRAYING OR ATOMISING IN GENERAL; APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
    • B05D—PROCESSES FOR APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
    • B05D7/00—Processes, other than flocking, specially adapted for applying liquids or other fluent materials to particular surfaces or for applying particular liquids or other fluent materials
    • B05D7/14—Processes, other than flocking, specially adapted for applying liquids or other fluent materials to particular surfaces or for applying particular liquids or other fluent materials to metal, e.g. car bodies
    • B05D7/146—Processes, other than flocking, specially adapted for applying liquids or other fluent materials to particular surfaces or for applying particular liquids or other fluent materials to metal, e.g. car bodies to metallic pipes or tubes
    • C—CHEMISTRY; METALLURGY
    • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
    • C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
    • C10M105/00—Lubricating compositions characterised by the base-material being a non-macromolecular organic compound
    • C10M105/08—Lubricating compositions characterised by the base-material being a non-macromolecular organic compound containing oxygen
    • C10M105/22—Carboxylic acids or their salts
    • C10M105/24—Carboxylic acids or their salts having only one carboxyl group bound to an acyclic carbon atom, cycloaliphatic carbon atom or hydrogen
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B05—SPRAYING OR ATOMISING IN GENERAL; APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
    • B05D—PROCESSES FOR APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
    • B05D5/00—Processes for applying liquids or other fluent materials to surfaces to obtain special surface effects, finishes or structures
    • B05D5/08—Processes for applying liquids or other fluent materials to surfaces to obtain special surface effects, finishes or structures to obtain an anti-friction or anti-adhesive surface
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B05—SPRAYING OR ATOMISING IN GENERAL; APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
    • B05D—PROCESSES FOR APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
    • B05D7/00—Processes, other than flocking, specially adapted for applying liquids or other fluent materials to particular surfaces or for applying particular liquids or other fluent materials
    • B05D7/24—Processes, other than flocking, specially adapted for applying liquids or other fluent materials to particular surfaces or for applying particular liquids or other fluent materials for applying particular liquids or other fluent materials
    • C—CHEMISTRY; METALLURGY
    • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
    • C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
    • C10M103/00—Lubricating compositions characterised by the base-material being an inorganic material
    • C10M103/06—Metal compounds
    • C—CHEMISTRY; METALLURGY
    • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
    • C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
    • C10M125/00—Lubricating compositions characterised by the additive being an inorganic material
    • C10M125/02—Carbon; Graphite
    • C—CHEMISTRY; METALLURGY
    • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
    • C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
    • C10M125/00—Lubricating compositions characterised by the additive being an inorganic material
    • C10M125/10—Metal oxides, hydroxides, carbonates or bicarbonates
    • C—CHEMISTRY; METALLURGY
    • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
    • C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
    • C10M125/00—Lubricating compositions characterised by the additive being an inorganic material
    • C10M125/22—Compounds containing sulfur, selenium or tellurium
    • C—CHEMISTRY; METALLURGY
    • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
    • C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
    • C10M125/00—Lubricating compositions characterised by the additive being an inorganic material
    • C10M125/26—Compounds containing silicon or boron, e.g. silica, sand
    • C—CHEMISTRY; METALLURGY
    • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
    • C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
    • C10M129/00—Lubricating compositions characterised by the additive being an organic non-macromolecular compound containing oxygen
    • C10M129/02—Lubricating compositions characterised by the additive being an organic non-macromolecular compound containing oxygen having a carbon chain of less than 30 atoms
    • C10M129/26—Carboxylic acids; Salts thereof
    • C10M129/28—Carboxylic acids; Salts thereof having carboxyl groups bound to acyclic or cycloaliphatic carbon atoms
    • C10M129/38—Carboxylic acids; Salts thereof having carboxyl groups bound to acyclic or cycloaliphatic carbon atoms having 8 or more carbon atoms
    • C10M129/40—Carboxylic acids; Salts thereof having carboxyl groups bound to acyclic or cycloaliphatic carbon atoms having 8 or more carbon atoms monocarboxylic
    • C—CHEMISTRY; METALLURGY
    • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
    • C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
    • C10M141/00—Lubricating compositions characterised by the additive being a mixture of two or more compounds covered by more than one of the main groups C10M125/00 - C10M139/00, each of these compounds being essential
    • C10M141/10—Lubricating compositions characterised by the additive being a mixture of two or more compounds covered by more than one of the main groups C10M125/00 - C10M139/00, each of these compounds being essential at least one of them being an organic phosphorus-containing compound
    • C—CHEMISTRY; METALLURGY
    • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
    • C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
    • C10M143/00—Lubricating compositions characterised by the additive being a macromolecular hydrocarbon or such hydrocarbon modified by oxidation
    • C10M143/02—Polyethene
    • C—CHEMISTRY; METALLURGY
    • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
    • C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
    • C10M145/00—Lubricating compositions characterised by the additive being a macromolecular compound containing oxygen
    • C10M145/02—Macromolecular compounds obtained by reactions only involving carbon-to-carbon unsaturated bonds
    • C10M145/06—Macromolecular compounds obtained by reactions only involving carbon-to-carbon unsaturated bonds containing monomers having an unsaturated radical bound to an acyloxy radical of a saturated carboxylic or carbonic acid
    • C10M145/08—Vinyl esters of a saturated carboxylic or carbonic acid
    • C—CHEMISTRY; METALLURGY
    • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
    • C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
    • C10M145/00—Lubricating compositions characterised by the additive being a macromolecular compound containing oxygen
    • C10M145/02—Macromolecular compounds obtained by reactions only involving carbon-to-carbon unsaturated bonds
    • C10M145/10—Macromolecular compounds obtained by reactions only involving carbon-to-carbon unsaturated bonds containing monomers having an unsaturated radical bound to a carboxyl radical, e.g. acrylate
    • C10M145/16—Macromolecular compounds obtained by reactions only involving carbon-to-carbon unsaturated bonds containing monomers having an unsaturated radical bound to a carboxyl radical, e.g. acrylate polycarboxylic
    • C—CHEMISTRY; METALLURGY
    • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
    • C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
    • C10M173/00—Lubricating compositions containing more than 10% water
    • C10M173/02—Lubricating compositions containing more than 10% water not containing mineral or fatty oils
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C22/00—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals
    • C23C22/05—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions
    • C23C22/60—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions using alkaline aqueous solutions with pH greater than 8
    • C23C22/62—Treatment of iron or alloys based thereon
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23F—NON-MECHANICAL REMOVAL OF METALLIC MATERIAL FROM SURFACE; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL; MULTI-STEP PROCESSES FOR SURFACE TREATMENT OF METALLIC MATERIAL INVOLVING AT LEAST ONE PROCESS PROVIDED FOR IN CLASS C23 AND AT LEAST ONE PROCESS COVERED BY SUBCLASS C21D OR C22F OR CLASS C25
    • C23F11/00—Inhibiting corrosion of metallic material by applying inhibitors to the surface in danger of corrosion or adding them to the corrosive agent
    • C23F11/08—Inhibiting corrosion of metallic material by applying inhibitors to the surface in danger of corrosion or adding them to the corrosive agent in other liquids
    • C23F11/10—Inhibiting corrosion of metallic material by applying inhibitors to the surface in danger of corrosion or adding them to the corrosive agent in other liquids using organic inhibitors
    • C23F11/173—Macromolecular compounds
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23F—NON-MECHANICAL REMOVAL OF METALLIC MATERIAL FROM SURFACE; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL; MULTI-STEP PROCESSES FOR SURFACE TREATMENT OF METALLIC MATERIAL INVOLVING AT LEAST ONE PROCESS PROVIDED FOR IN CLASS C23 AND AT LEAST ONE PROCESS COVERED BY SUBCLASS C21D OR C22F OR CLASS C25
    • C23F11/00—Inhibiting corrosion of metallic material by applying inhibitors to the surface in danger of corrosion or adding them to the corrosive agent
    • C23F11/08—Inhibiting corrosion of metallic material by applying inhibitors to the surface in danger of corrosion or adding them to the corrosive agent in other liquids
    • C23F11/18—Inhibiting corrosion of metallic material by applying inhibitors to the surface in danger of corrosion or adding them to the corrosive agent in other liquids using inorganic inhibitors
    • C23F11/187—Mixtures of inorganic inhibitors
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23G—CLEANING OR DE-GREASING OF METALLIC MATERIAL BY CHEMICAL METHODS OTHER THAN ELECTROLYSIS
    • C23G1/00—Cleaning or pickling metallic material with solutions or molten salts
    • C23G1/02—Cleaning or pickling metallic material with solutions or molten salts with acid solutions
    • C23G1/08—Iron or steel
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23G—CLEANING OR DE-GREASING OF METALLIC MATERIAL BY CHEMICAL METHODS OTHER THAN ELECTROLYSIS
    • C23G1/00—Cleaning or pickling metallic material with solutions or molten salts
    • C23G1/14—Cleaning or pickling metallic material with solutions or molten salts with alkaline solutions
    • C23G1/19—Iron or steel
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B05—SPRAYING OR ATOMISING IN GENERAL; APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
    • B05D—PROCESSES FOR APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
    • B05D2202/00—Metallic substrate
    • B05D2202/10—Metallic substrate based on Fe
    • B05D2202/15—Stainless steel
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B05—SPRAYING OR ATOMISING IN GENERAL; APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
    • B05D—PROCESSES FOR APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
    • B05D2601/00—Inorganic fillers
    • C—CHEMISTRY; METALLURGY
    • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
    • C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
    • C10M2201/00—Inorganic compounds or elements as ingredients in lubricant compositions
    • C10M2201/04—Elements
    • C10M2201/041—Carbon; Graphite; Carbon black
    • C—CHEMISTRY; METALLURGY
    • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
    • C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
    • C10M2201/00—Inorganic compounds or elements as ingredients in lubricant compositions
    • C10M2201/06—Metal compounds
    • C10M2201/062—Oxides; Hydroxides; Carbonates or bicarbonates
    • C—CHEMISTRY; METALLURGY
    • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
    • C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
    • C10M2201/00—Inorganic compounds or elements as ingredients in lubricant compositions
    • C10M2201/06—Metal compounds
    • C10M2201/065—Sulfides; Selenides; Tellurides
    • C—CHEMISTRY; METALLURGY
    • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
    • C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
    • C10M2201/00—Inorganic compounds or elements as ingredients in lubricant compositions
    • C10M2201/06—Metal compounds
    • C10M2201/065—Sulfides; Selenides; Tellurides
    • C10M2201/066—Molybdenum sulfide
    • C—CHEMISTRY; METALLURGY
    • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
    • C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
    • C10M2201/00—Inorganic compounds or elements as ingredients in lubricant compositions
    • C10M2201/10—Compounds containing silicon
    • C10M2201/102—Silicates
    • C—CHEMISTRY; METALLURGY
    • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
    • C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
    • C10M2205/00—Organic macromolecular hydrocarbon compounds or fractions, whether or not modified by oxidation as ingredients in lubricant compositions
    • C10M2205/02—Organic macromolecular hydrocarbon compounds or fractions, whether or not modified by oxidation as ingredients in lubricant compositions containing acyclic monomers
    • C10M2205/026—Butene
    • C—CHEMISTRY; METALLURGY
    • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
    • C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
    • C10M2205/00—Organic macromolecular hydrocarbon compounds or fractions, whether or not modified by oxidation as ingredients in lubricant compositions
    • C10M2205/14—Synthetic waxes, e.g. polythene waxes
    • C—CHEMISTRY; METALLURGY
    • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
    • C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
    • C10M2207/00—Organic non-macromolecular hydrocarbon compounds containing hydrogen, carbon and oxygen as ingredients in lubricant compositions
    • C10M2207/10—Carboxylix acids; Neutral salts thereof
    • C10M2207/12—Carboxylix acids; Neutral salts thereof having carboxyl groups bound to acyclic or cycloaliphatic carbon atoms
    • C10M2207/125—Carboxylix acids; Neutral salts thereof having carboxyl groups bound to acyclic or cycloaliphatic carbon atoms having hydrocarbon chains of eight up to twenty-nine carbon atoms, i.e. fatty acids
    • C10M2207/126—Carboxylix acids; Neutral salts thereof having carboxyl groups bound to acyclic or cycloaliphatic carbon atoms having hydrocarbon chains of eight up to twenty-nine carbon atoms, i.e. fatty acids monocarboxylic
    • C—CHEMISTRY; METALLURGY
    • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
    • C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
    • C10M2207/00—Organic non-macromolecular hydrocarbon compounds containing hydrogen, carbon and oxygen as ingredients in lubricant compositions
    • C10M2207/10—Carboxylix acids; Neutral salts thereof
    • C10M2207/12—Carboxylix acids; Neutral salts thereof having carboxyl groups bound to acyclic or cycloaliphatic carbon atoms
    • C10M2207/125—Carboxylix acids; Neutral salts thereof having carboxyl groups bound to acyclic or cycloaliphatic carbon atoms having hydrocarbon chains of eight up to twenty-nine carbon atoms, i.e. fatty acids
    • C10M2207/128—Carboxylix acids; Neutral salts thereof having carboxyl groups bound to acyclic or cycloaliphatic carbon atoms having hydrocarbon chains of eight up to twenty-nine carbon atoms, i.e. fatty acids containing hydroxy groups; Ethers thereof
    • C—CHEMISTRY; METALLURGY
    • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
    • C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
    • C10M2209/00—Organic macromolecular compounds containing oxygen as ingredients in lubricant compositions
    • C10M2209/02—Macromolecular compounds obtained by reactions only involving carbon-to-carbon unsaturated bonds
    • C10M2209/08—Macromolecular compounds obtained by reactions only involving carbon-to-carbon unsaturated bonds containing monomers having an unsaturated radical bound to a carboxyl radical, e.g. acrylate type
    • C10M2209/086—Macromolecular compounds obtained by reactions only involving carbon-to-carbon unsaturated bonds containing monomers having an unsaturated radical bound to a carboxyl radical, e.g. acrylate type polycarboxylic, e.g. maleic acid
    • C—CHEMISTRY; METALLURGY
    • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
    • C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
    • C10M2213/00—Organic macromolecular compounds containing halogen as ingredients in lubricant compositions
    • C10M2213/06—Perfluoro polymers
    • C10M2213/062—Polytetrafluoroethylene [PTFE]
    • C—CHEMISTRY; METALLURGY
    • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
    • C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
    • C10M2215/00—Organic non-macromolecular compounds containing nitrogen as ingredients in lubricant compositions
    • C10M2215/08—Amides
    • C—CHEMISTRY; METALLURGY
    • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
    • C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
    • C10M2215/00—Organic non-macromolecular compounds containing nitrogen as ingredients in lubricant compositions
    • C10M2215/22—Heterocyclic nitrogen compounds
    • C10M2215/221—Six-membered rings containing nitrogen and carbon only
    • C10M2215/222—Triazines
    • C—CHEMISTRY; METALLURGY
    • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
    • C10N—INDEXING SCHEME ASSOCIATED WITH SUBCLASS C10M RELATING TO LUBRICATING COMPOSITIONS
    • C10N2020/00—Specified physical or chemical properties or characteristics, i.e. function, of component of lubricating compositions
    • C10N2020/01—Physico-chemical properties
    • C10N2020/055—Particles related characteristics
    • C10N2020/06—Particles of special shape or size
    • C—CHEMISTRY; METALLURGY
    • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
    • C10N—INDEXING SCHEME ASSOCIATED WITH SUBCLASS C10M RELATING TO LUBRICATING COMPOSITIONS
    • C10N2030/00—Specified physical or chemical properties which is improved by the additive characterising the lubricating composition, e.g. multifunctional additives
    • C10N2030/12—Inhibition of corrosion, e.g. anti-rust agents or anti-corrosives
    • C—CHEMISTRY; METALLURGY
    • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
    • C10N—INDEXING SCHEME ASSOCIATED WITH SUBCLASS C10M RELATING TO LUBRICATING COMPOSITIONS
    • C10N2030/00—Specified physical or chemical properties which is improved by the additive characterising the lubricating composition, e.g. multifunctional additives
    • C10N2030/40—Low content or no content compositions
    • C10N2030/42—Phosphor free or low phosphor content compositions
    • C—CHEMISTRY; METALLURGY
    • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
    • C10N—INDEXING SCHEME ASSOCIATED WITH SUBCLASS C10M RELATING TO LUBRICATING COMPOSITIONS
    • C10N2050/00—Form in which the lubricant is applied to the material being lubricated
    • C10N2050/015—Dispersions of solid lubricants
    • C10N2050/02—Dispersions of solid lubricants dissolved or suspended in a carrier which subsequently evaporates to leave a lubricant coating
    • C—CHEMISTRY; METALLURGY
    • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
    • C10N—INDEXING SCHEME ASSOCIATED WITH SUBCLASS C10M RELATING TO LUBRICATING COMPOSITIONS
    • C10N2080/00—Special pretreatment of the material to be lubricated, e.g. phosphatising or chromatising of a metal

Definitions

  • the present disclosure relates to a steel wire rod having a lubricating coating containing no phosphorus on a surface.
  • a surface of a metal material is coated in advance with a solid coating
  • inorganic coatings such as a borate coating and a phosphate crystal coating, which exist at an interface between a die and a workpiece and is therefore less likely to cause lubricating coating disruption even under high surface pressure, thus making it possible to avoid direct contact between metals.
  • Such lubricating coating has sufficient coating strength.
  • a composite coating composed of a zinc phosphate coating and a soap layer hereinafter sometimes referred to as a chemical conversion coating
  • a chemical conversion coating has widely been employed because of having high workability and corrosion resistance.
  • Patent Document 1 discloses an aqueous lubricating coating agent for plastic working of a metal material, which is a composition comprising a water-soluble inorganic salt (A) and a wax (B) dissolved or dispersed in water, wherein a solid component weight ratio (B)/(A) is in a range of 0.3 to 1.5; and a coating forming method thereof.
  • Patent Document 2 discloses an aqueous lubricating coating agent for plastic working of a metal material, comprising an alkali metal borate (A), wherein the alkali metal borate (A) contains lithium borate, a molar ratio of lithium to the entire alkali metal in the alkali metal borate (A) is in a range of 0.1 to 1.0, and also a molar ratio (B/M) of boric acid B to an alkali metal M of the alkali metal borate (A) is in a range of 1.5 to 4.0; and a coating forming method thereof. It is considered that this technology suppresses crystallization of a coating caused by moisture absorption of the coating, thus enabling formation of a coating having not only workability but also high corrosion resistance.
  • Patent Document 3 discloses a water-soluble lubricant for non-phosphorus based plastic working, comprising an inorganic solid lubricant as a component A, a wax as a component B, and a water-soluble inorganic metal salt as a component C, wherein a solid component dry mass ratio of the component A to the component B (component A/component B) is in a range of 0.1 to 5, and a solid component dry mass ratio of the component C to the total amount of the component A, the component B, and the component C (component C/(component A+component B+component C)) is in a range of 1 to 30%. It is considered that this technology is directed to a lubricant containing no phosphorus and enables realization of corrosion resistance equal to that of a chemical conversion coating.
  • Patent Document 4 discloses an aqueous lubricating coating agent comprising a water-soluble inorganic salt (A), at least one lubricant (B) selected from molybdenum disulfide and graphite, and a wax (C), these components being dissolved or dispersed in water, wherein (B)/(A) is in a range of 1.0 to 5.0 in terms of a solid component weight ratio, and (C)/(A) is in a range of 0.1 to 1.0 in terms of a solid component weight ratio; and a coating forming method thereof. It is considered that this technology enables realization of high workability having the same level as that of a chemical conversion coating by mixing a conventional aqueous lubricating coating agent with molybdenum disulfide and/or graphite.
  • A water-soluble inorganic salt
  • B lubricant
  • C wax
  • Patent Document 5 discloses a coating forming agent comprising a silicate (A), a polycarboxylate (B), a hydrophilic polymer and/or a hydrophilic organic lamellar structure (C), and a molybdate and/or a tungstate (D), a dry mass ratio of each component being a predetermined ratio.
  • the water-soluble inorganic salt is an essential component in the solid coating of the aqueous lubricating coating agent.
  • the lubricating coating composed of the water-soluble inorganic salt has sufficient coating strength and, as mentioned above, the lubricating coating exists at an interface between a die and a workpiece and is therefore less likely to cause lubricating coating disruption even under high surface pressure, thus making it possible to avoid direct contact between metals. Therefore, in the aqueous lubricating coating agent, it is possible to maintain a satisfactory lubricated state during plastic working by using a solid coating composed of a water-soluble inorganic salt and a water-soluble resin in combination with an appropriate lubricant capable of reducing a friction coefficient.
  • a water-soluble inorganic salt of a water-soluble component is in a state of being dissolved in water in a lubricating treatment solution and, when a lubricant is applied on a surface of a metal material and then dried, water as a solvent is vaporized to form a lubricating coating.
  • the water-soluble inorganic salt is precipitated as a solid substance on the surface of the metal material to form a solid coating.
  • the solid coating thus formed has a coating strength capable of enduring plastic working, and exhibits satisfactory lubricity during plastic working by mixing with an appropriate lubricant capable of reducing a friction coefficient.
  • Patent Document 1 WO 02/012420 A
  • Patent Document 2 JP 2011-246684 A
  • Patent Document 3 JP 2013-209625 A
  • Patent Document 4 WO 02/012419 A
  • Patent Document 5 JP 2002-363593 A
  • Patent Documents 1 to 5 rust prevention property over a long term of two or more months is drastically inferior as compared with the above-mentioned chemical conversion coatings, thus failing to enhance to a practical level.
  • a main component of the coating is a water-soluble component and therefore easily absorbs or transmits moisture in the atmosphere, leading to easy contact between a steel rod and moisture.
  • corrosion resistance is improved by suppressing crystallization of the coating due to moisture absorption, however, moisture absorption itself is not suppressed, thus failing to obtain sufficient corrosion resistance.
  • the aqueous lubricating coating mentioned in Patent Document 3 exhibited corrosion resistance, which is equal to or better than that of the chemical conversion coating, in a corrosion resistance test in a laboratory in which rusting is accelerated using a thermo-hygrostat.
  • the lubricating coating is actually used in the environment where dusts and powders, and mists of a pickling agent are adhesible. In such severe environment, corrosion resistance is actually inferior as compared with the chemical conversion coating.
  • Examples of the water-soluble inorganic salt capable of obtaining comparatively high corrosion resistance include an alkali metal salt of a silicate (hereinafter sometimes referred to as a silicate) and an alkali metal salt and/or an ammonium salt of a tungstate (hereinafter sometimes referred to as a tungstate).
  • a silicate an alkali metal salt of a silicate
  • an alkali metal salt and/or an ammonium salt of a tungstate hereinafter sometimes referred to as a tungstate.
  • Patent Document 1 Patent Document 4
  • Patent Document 5 Patent Document 5
  • they are far inferior in practical corrosion resistance as compared with the chemical conversion coating.
  • the water-soluble silicate has a property that is less likely to transmit moisture among the water-soluble inorganic salts and also has very high adhesion to a base material. Because of this property, it is a material that can exhibit comparatively high corrosion resistance, but not as much as the chemical conversion coating. This is because the water-soluble silicate is crosslinked to form a network structure in a coating formation process in which water as a solvent of a lubricant is vaporized. However, because of this network structure, the coating of the water-soluble silicate is too brittle as a lubricating coating. Therefore, when the base material is worked, it is sometimes impossible to sufficiently conform because of cracks of the coating, leading to decrease in coating retention amount.
  • the water-soluble tungstate is less likely to absorb moisture from external air when a coating is formed. This is because granular crystals are formed when the water-soluble tungstate forms a coating. Further, the water-soluble tungstate has a property that forms a passive coating having a self-repair function on a surface of a steel rod, and use of the water-soluble tungstate as the coating component enables expectation of formation of a coating having high corrosion resistance.
  • the water-soluble tungstate is crystalline and is therefore inferior in adhesion to a material and cannot form a uniform coating, thus failing to obtain corrosion resistance and workability as expected. For example, it is possible to enhance adhesion and uniformity of a coating by adding a synthetic resin component in a lubricant, but the corrosion resistance is drastically inferior as compared with a chemical conversion coating.
  • Patent Document 5 a coating treatment agent containing a silicate (A) as a main component and containing excessively large amount of an anti-corrosive agent (D) is inferior in lubricity since seizure occurs under high extrusion load. Therefore, it becomes difficult to perform stable operation, thus failing to obtain sufficient long-term rust prevention property.
  • pushing-in of the coating occurs at the place where friction is locally high, causing poor appearance such as formation of scaly patterns.
  • An inorganic salt to be mixed in a lubricating coating is comparatively hard, so that push-in traces are likely to be generated by a surface pressure during heading in a steel rod. These patterns and push-in traces can be visually confirmed with ease, thus drastically impair the appearance of the product.
  • the inventors of the present invention have intensively studied on a steel wire rod having a lubricating coating containing no phosphorus on a surface so as to solve the above problems, and found that it is possible to simultaneously obtain high corrosion resistance which has never been achieved by each component alone, and excellent appearance after heading which has never been obtained by mixing lubricants such as wax, by mixing a predetermined ratio of an alkali metal salt of fatty acid among various compounds used as a lubricant in a lubricating coating in which a ratio of silicon derived from a water-soluble silicate to tungsten derived from a water-soluble tungstate, i.e. a dry mass ratio of tungsten/silicon is controlled to a predetermined ratio, and thus the present invention has been completed.
  • the present invention was structured in the following manner so as to solve the above problems.
  • the steel wire rod of the embodiment of the present invention includes a lubricating coating on a surface thereof, the lubricating coating including silicon (A), tungsten (B) and an alkali metal salt of fatty acid (C), a dry mass ratio of (B)/(A) being in a range of 1.3 to 18, a dry mass ratio of (C)/ ⁇ (A)+(B) ⁇ being in a range of 0.14 to 2.0, and the lubricating coating containing no phosphorus.
  • the silicon is derived from a water-soluble silicate
  • the tungsten is derived from a water-soluble tungstate.
  • the silicon is derived from at least one selected from the group consisting of lithium silicate, sodium silicate, and potassium silicate
  • the tungsten is derived from at least one selected from the group consisting of lithium tungstate, sodium tungstate, potassium tungstate, and ammonium tungstate.
  • the lubricating coating further includes a lubricant (D) other than the alkali metal salt of fatty acid (C), and a dry mass ratio of ⁇ (C)+(D) ⁇ / ⁇ (A)+(B) ⁇ is in a range of 0.14 to 2.0.
  • D lubricant
  • C alkali metal salt of fatty acid
  • the lubricant (D) is at least one selected from the group consisting of wax, polytetrafluoroethylene, fatty acid metal soap, fatty acid amide, molybdenum disulfide, tungsten disulfide, graphite, and melamine cyanurate.
  • the lubricating coating further includes a resin (E), and a dry mass ratio of (E)/ ⁇ (A)+(B) ⁇ exceeds 0 and 1.4 or less.
  • the resin (E) is at least one selected from the group consisting of a vinyl resin, an acrylic resin, an epoxy resin, a urethane resin, a phenol resin, a cellulose derivative, a polymaleic acid, and a polyester resin.
  • a mass of a coating per unit area of the lubricating coating is in a range of 1.0 to 20 g/m 2 .
  • a lubricating coating is structured in the manner mentioned above, thus obtaining a steel wire rod which has excellent corrosion resistance such as long-term rust prevention property, and satisfactory appearance after heading.
  • the lubricating coating of the present disclosure is far better than a conventional aqueous lubricating coating in that all of these performances are equal to or better than those of steel wire rods having a chemical conversion coating.
  • FIG. 1 is a schematic view showing the procedure of heading in Examples.
  • the steel wire rod of the embodiment of the present invention is characterized by including a lubricating coating on a surface thereof, the lubricating coating including silicon (A), tungsten (B) and an alkali metal salt of fatty acid (C), a dry mass ratio of (B)/(A) being in a range of 1.3 to 18, a dry mass ratio of (C)/ ⁇ (A)+(B) ⁇ being in a range of 0.14 to 2.0, and the lubricating coating containing no phosphorus.
  • the lubricating coating including silicon (A), tungsten (B) and an alkali metal salt of fatty acid (C), a dry mass ratio of (B)/(A) being in a range of 1.3 to 18, a dry mass ratio of (C)/ ⁇ (A)+(B) ⁇ being in a range of 0.14 to 2.0, and the lubricating coating containing no phosphorus.
  • Steel used in the steel wire rod of the embodiment of the present invention include a carbon steel, an alloy steel, and a special steel.
  • Examples of such steel include a mild steel having a carbon content of 0.2% by mass or less (not including 0% by mass), a carbon steel having a carbon content of exceeding 0.2% by mass and 1.5% by mass or less.
  • the steel used in the steel wire rod also includes an alloy or special steel in which at least one selected from silicon, manganese, phosphorus, sulfur, nickel, chromium, copper, aluminum, molybdenum, vanadium, cobalt, titanium, and zirconium is added to the mild steel or carbon steel according to the application.
  • the steel wire rod commonly refers to those obtained by forming a steel into a wire rod through hot working.
  • a steel wire is also included in the steel wire rod of the present disclosure.
  • the steel wire is obtained by further subjecting the steel wire rod to a working treatment.
  • the working treatment include a wire drawing treatment, a heading treatment, and a forging treatment. Specific examples thereof include those obtained by drawing a steel wire rod into a wire having a specified size (wire diameter, circularity, etc.), those obtained by heading after wire drawing, and those obtained by forging the steel wire rod.
  • the steel wire also includes those obtained by further subjecting the product after the working treatment to surface treatments such as heat treatment and/or a plating treatment. Specific examples thereof include those obtained by machining into a product after the heading or forging, and subjecting the product to a heat treatment, or those obtained by further subjecting to a plating treatment after the heat treatment.
  • the steel wire rod of the embodiment of the present invention is not particularly limited as long as it is excellent in corrosion resistance and appearance after heading because of having the below-mentioned lubricating coating, and a coating film, namely, an undercoating may be further formed between a surface of the steel wire rod and the lubricating coating. Both of these coatings may be a single layer, or a layer composed of two or more layers.
  • Both the lubricating coating and the undercoating used in the embodiment of the present invention contain no phosphorus, and a lubricating coating agent used for formation of the lubricating coating does not contain a component containing phosphorus.
  • a component containing phosphorus is inevitably included in a coating of a surface of the steel wire rod in the operation process. Namely, although phosphorus may cause contamination as inevitable impurity in the actual operation, there is little possibility that phosphorus causes brittle fracture of a steel wire rod when the content of phosphorus is about 1% by mass or less, and thus it is possible to consider that phosphorizing does not occur.
  • the steel wire rod of the embodiment of the present invention includes a lubricating coating on a surface thereof, the lubricating coating including silicon (A), tungsten (B) and an alkali metal salt of fatty acid (C), a dry mass ratio of (B)/(A) being in a range of 1.3 to 18, and a dry mass ratio of (C)/ ⁇ (A)+(B) ⁇ being in a range of 0.14 to 2.0.
  • Formation of a lubricating coating including the above components in a ratio controlled in the above range on a surface of a steel wire rod enables simultaneous achievement of high corrosion resistance and excellent appearance after heading.
  • the below-mentioned water-soluble silicate and water-soluble tungstate are composited to form a lubricating coating, the water-soluble tungstate is incorporated into a network structure formed of the water-soluble silicate.
  • the water-soluble tungstate has drawbacks that it forms a crystalline coating.
  • Examples of the influence of the water-soluble tungstate on the water-soluble silicate include an increase in coating retention amount of the working portion involved in an improvement in coating conformability.
  • the water-soluble silicate is inferior in coating conformability since a firm continuous film is formed by polymerization of the water-soluble silicate.
  • the composited water-soluble tungstate interposes in the network structure of the water-soluble silicate, whereby, formation of a firm network structure is appropriately suppressed, and coating conformability is improved, thus enabling an increase in coating retention amount.
  • a dry mass ratio of tungsten (B)/silicon (A) is 1.3 or more, preferably 1.8 or more, and more preferably 2.0 or more.
  • the dry mass ratio is 18 or less, preferably 10 or less, and more preferably 5.4 or less. If the dry mass ratio of B/A is less than 1.3, sufficient corrosion resistance cannot be obtained and the coating retention amount of the working portion decreases. This is because the amount of the tungstate relatively decreases, thus failing to sufficiently form a passive film, while the amount of the silicate relatively increases to form a firm network structure. If a dry mass ratio of tungsten/silicon is more than 18, the thus formed coating cannot achieve sufficient corrosion resistance.
  • a dry mass ratio of tungsten/silicon is based on a ratio of tungsten element derived from a water-soluble tungstate to silicon element derived from a water-soluble silicate in the coating, and can be calculated as mentioned later.
  • silicon (A) is derived from a water-soluble silicate and tungsten (B) is derived from a water-soluble tungstate.
  • a dry mass ratio of tungsten (B)/silicon (A) in the below-mentioned Examples is based on a ratio of tungsten element derived from the water-soluble tungstate in the lubricating coating to a silicon element derived from the water-soluble silicate in the lubricating coating and can be calculated, for example, using inductively coupled plasma or fluorescent X-ray spectroscopy.
  • a dry mass ratio (b)/(a) thereof is 0.7 or more, preferably 0.9 or more, and more preferably 1.1 or more.
  • the dry mass ratio is 10 or less, preferably 6.0, and more preferably 3.0 or less.
  • water-soluble silicate examples include lithium silicate, sodium silicate, and potassium silicate. These water-soluble silicates may be used alone, or two or more water-soluble silicates may be used in combination.
  • water-soluble tungstate examples include lithium tungstate, sodium tungstate, potassium tungstate, and ammonium tungstate. These water-soluble tungstates may be used alone, or two or more water-soluble tungstates may be used in combination.
  • the alkali metal salt of fatty acid (C) is mixed to reduce friction of a lubricating coating and to prevent poor appearance after heading.
  • the alkali metal salt of fatty acid (C) has slight water solubility and, in the process for forming a lubricating coating, the dissolved alkali metal salt of fatty acid (C) is precipitated finely and uniformly.
  • a conventional lubricating coating is likely to cause coarse distribution of a lubricant component in the coating, leading to a local difference in a friction state between the place where a lubricant content is high and the place where a lubricant content is low during heading.
  • the alkali metal salt of fatty acid (C) can exist finely and uniformly in the coating, so that a local difference in a friction state is less likely to occur, thus obtaining satisfactory appearance (heading appearance) after heading.
  • Mixing of the alkali metal salt of fatty acid (C) exerts the effect of softening a lubricating coating, and thus the lubricating coating becomes harder to push in the steel wire rod.
  • alkali metal salt of fatty acid (C), (C)/ ⁇ (A)+(B) ⁇ which is a dry mass ratio of silicon (A), tungsten (B), and the alkali metal salt of fatty acid (C), is 0.14 or more, preferably 0.2 or more, and more preferably 0.4 or more.
  • the dry mass ratio is 2.0 or less, and preferably 1.5 or less. If the dry mass ratio is less than 0.14, it becomes impossible to obtain satisfactory heading appearance.
  • each amount of silicon (A) and tungsten (B) relatively decreases, thus causing degradation of corrosion resistance, degradation of the seizure resistance of the coating during heading, and reduction in service life of the die caused thereby.
  • a dry mass ratio (C)/ ⁇ (a)+(b) ⁇ is 0.043 or more, preferably 0.062 or more, and more preferably 0.09 or more.
  • the dry mass ratio is 0.95 or less, and more preferably 0.8 or less.
  • the alkali metal salt of fatty acid (C) used in the embodiment of the present invention means an alkali metal salt (for example, sodium salt, potassium salt, lithium salt) of a long-chain fatty acid having 12 or more carbon atoms (higher fatty acid).
  • a hydrocarbon group constituting fatty acid may be either linear or branched.
  • Examples of the alkali metal salt of fatty acid (C) include sodium myristate, potassium myristate, lithium myristate, sodium palmitate, potassium palmitate, lithium palmitate, sodium stearate, potassium stearate, lithium stearate, sodium 12-hydroxystearate, potassium 12-hydroxystearate, and lithium 12-hydroxystearate.
  • These alkali metal salts of fatty acid may be used alone, or two or more alkali metal salts of fatty acid may be used in combination.
  • the steel wire rod of the embodiment of the present invention may further include a lubricant (D) and/or a resin (E) other than the fatty acid alkali metal salt (C) in the lubricating coating.
  • the lubricant (D) itself has slipperiness, and has a function of reducing a friction force. In general, if the friction force increases during plastic working, an increase in working energy, heat generation, seizure, and the like occur. If the lubricant (D) is included in a lubricating coating of the steel wire rod of the embodiment of the present invention, the lubricant exists in the lubricating coating in the form of a solid, thus suppressing an increase in friction force.
  • lubricant (D) having such function and property examples include wax, polytetrafluoroethylene, fatty acid metal soap, fatty acid amide, molybdenum disulfide, tungsten disulfide, graphite, and melamine cyanurate. These lubricants may be used alone, or two or more lubricants may be used in combination.
  • the wax include polyethylene wax, paraffin wax, microcrystalline wax, polypropylene wax, and carnauba wax.
  • Specific examples of the fatty acid metal soap include calcium stearate, zinc stearate, barium stearate, and magnesium stearate.
  • the fatty acid amide is an amide compound having two fatty acids, and specific examples thereof include ethylenebislauric acid amide, ethylenebisstearic acid amide, ethylenebisbehenic acid amide, N,N′-distearyladipic acid amide, ethylenebisoleic acid amide, ethylenebiserucic acid amide, hexamethylenebisoleic acid amide, and N,N′-dioleyladipic acid amide.
  • a dry mass ratio of ⁇ (C)+(D) ⁇ / ⁇ (A)+(B) ⁇ is preferably 0.14 or more, more preferably 0.2 or more, and still more preferably 0.4 or more.
  • the dry mass ratio is preferably 2.0 or less, and more preferably 1.5 or less. If the dry mass ratio is less than 0.14, the content of the lubricant (D) is too small to exhibit the above-mentioned performances. Meanwhile, if the dry mass ratio is more than 2.0, each amount of silicon and tungsten relatively decreases, leading to degradation of corrosion resistance.
  • the resin (E) enables the binder effect, an improvement in adhesion between a base material and a coating, imparting of leveling property by the thickening effect, and stabilization of a dispersion component.
  • the resin having such function and property include a vinyl resin, an acrylic resin, an epoxy resin, a urethane resin, a phenol resin, a cellulose derivative, a polymaleic acid, and a polyester resin.
  • a methacrylic resin is also included in the acrylic resin. These resins may be either polymers or copolymers.
  • copolymer examples include a copolymer of vinyl-acrylic acid, a copolymer of vinyl-epoxy, a copolymer of vinyl-urethane, a copolymer of vinyl-phenol, a copolymer of vinyl-(anhydrous) maleic acid, a copolymer of acrylic acid-epoxy, a copolymer of acrylic acid-urethane, a copolymer of acrylic acid-phenol, a copolymer of acrylic acid-(anhydrous) maleic acid, a copolymer of epoxy-urethane, a copolymer of epoxy-phenol, a copolymer of epoxy-(anhydrous) maleic acid, a copolymer of urethane-phenol, a copolymer of urethane-phenol, a copolymer of urethane-(anhydrous) maleic acid, a copolymer of urethane-phenol, a copolymer of urethane-(anhydrous
  • a dry mass ratio of (E)/ ⁇ (A)+(B) ⁇ is preferably 0.01 or more, and more preferably 0.05 or more.
  • the dry mass ratio is preferably 1.4 or less, and more preferably 0.9 or less. If the dry mass ratio is less than 0.01, the above-mentioned action may not be sufficiently exerted. Meanwhile, if the dry mass ratio is more than 1.4, poor appearance is likely to occur after heading.
  • the lubricating coating constituting the embodiment of the present invention can be further mixed with, in addition to the above-mentioned basic components (silicon, tungsten, an alkali metal salt of fatty acid) and selective components (a resin, a lubricant other than an alkali metal salt of fatty acid), a viscosity modifier.
  • a working treatment which means a steel wire rod requiring a working treatment, namely, a steel wire rod before a working treatment
  • leveling property and thixotrophy are imparted, thus making it possible to ensure a uniform coated state.
  • viscosity modifier examples include smectite-based clay minerals such as montmorillonite, sauconite, beidellite, hectorite, nontronite, saponite, iron-rich saponite, and stevensite; and inorganic thickeners such as pulverized silica, bentonite, and kaolin.
  • the lubricating coating may further include water-soluble salts to improve adhesion.
  • Type of the water-soluble salt is not particularly limited, and either or both of an inorganic salt and an organic salt can be used.
  • examples of the inorganic salt include sulfates such as sodium sulfate and potassium sulfate; and borates such as sodium metaborate, potassium metaborate, and ammonium metaborate.
  • organic salt examples include salts of formic acid, acetic acid, butyric acid, oxalic acid, succinic acid, lactic acid, ascorbic acid, tartaric acid, citric acid, malic acid, malonic acid, maleic acid, phthalic acid, and the like, with alkali metals, alkali earth metals, and the like.
  • the lubricating coating of the steel wire rod of the embodiment of the present invention can be imparted with high corrosion resistance before and after wire drawing, and may be mixed with other water-soluble rust preventives and inhibitors for the purpose of further improving corrosion resistance.
  • rust preventives and inhibitors include various organic acids such as oleic acid, dimer acid, tartaric acid, and citric acid; various chelating agents such as EDTA, NTA, HEDTA, and DTPA; mixed components of alkanolamine such as triethanolamine; amine salts of p-t-butylbenzoic acid; a carboxylic acid amine salt, a dibasic acid amine salt, an alkenylsuccinic acid, and a water-soluble salt thereof; and aminotetrazole and a water-soluble salt thereof.
  • These rust preventives and inhibitors may be used alone, or two or more rust preventives and inhibitors may be used in combination.
  • the lubricating coating constituting the steel wire rod of the embodiment of the present invention can be fabricated by adding the above-mentioned components (water-soluble silicate which is a typical source of supply of silicon, water-soluble tungstate which is typical source of supply of tungsten, and essential components of an alkali metal salt of fatty acid; and, if necessary, lubricants other than an alkali metal salt of fatty acid, resins, viscosity modifiers, and water-soluble salts) to a liquid medium, followed by mixing to prepare a lubricating coating agent, and coating the lubricating coating agent on a surface of a steel wire rod which is subjected to a working treatment.
  • water-soluble silicate which is a typical source of supply of silicon
  • water-soluble tungstate which is typical source of supply of tungsten
  • the amount of the water-soluble silicate is preferably exceeding 5% by mass, more preferably 10% by mass or more, and still more preferably 15% by mass or more, and is also preferably 58% by mass or less, more preferably 52% by mass or less, and still more preferably 45% by mass or less, based on 100% by dry mass of the total amount of a component a, a component b, a component C, a component D, and a component E in the lubricating coating agent.
  • the amount of the water-soluble tungstate is preferably 10% by mass or more, more preferably 15% by mass or more, and still more preferably 20% by mass or more, and is also preferably less than 88% by mass, more preferably 85% by mass or less, and still more preferably 80% by mass or less, based on 100% by dry mass of the total amount of a component a, a component b, a component C, a component D, and a component E in the lubricating coating agent.
  • the amount of the alkali metal salt of fatty acid is preferably exceeding 3% by mass, more preferably exceeding 7% by mass, still more preferably 12% by mass or more, and particularly preferably 16% by mass or more, and is also preferably 50% by mass or less, more preferably 40% by mass or less, and still more preferably 30% by mass or less, based on 100% by dry mass of the total amount of a component a, a component b, a component C, a component D, and a component E in the lubricating coating agent.
  • the amount of the water-soluble silicate is 5% by mass or less and the amount of the water-soluble tungstate is 88% by mass or more, sufficient long-term rust prevention property cannot be obtained, and poor appearance after heading occurs. This is because the amount of the water-soluble silicate relatively decreases, thus making it easier to transmit moisture, while crystals of tungsten are precipitated, thus degrading adhesion and uniformity of the coating. Meanwhile, if the amount of the water-soluble silicate exceeds 58% by mass and the amount of the water-soluble tungstate is less than 10% by mass, neither sufficient corrosion resistance nor satisfactory appearance after heading can be obtained. This is because the amount of the tungstate relatively decreases, thus failing to sufficiently form a passive film, while the amount of the water soluble silicate relatively increases to form a firm network structure.
  • each amount of silicon (A) and tungsten (B) relatively decreases, thus degrading corrosion resistance. Meanwhile, if the amount of the alkali metal salt of fatty acid is 3% by mass or less, poor appearance is likely to occur after heading.
  • a dry lubricant may be adhered onto the lubricating coating.
  • type of the dry lubricant there is no limitation on type of the dry lubricant and it is possible to use, for example, a common lubricating powder and/or wire drawing powder which contains, as main components, higher fatty acid soap, borax, lime, and molybdenum disulfide.
  • a liquid medium (solvent, dispersion medium) in a lubricating coating agent for forming a lubricating coating is water.
  • the lubricating coating agent may contain a water-soluble strong alkali component.
  • a water-soluble strong alkali component include lithium hydroxide, sodium hydroxide, and potassium hydroxide. These water-soluble strong alkali components may be used alone, or two or more water-soluble strong alkali components may be used in combination.
  • the production method includes a cleaning step of a steel wire rod which is subjected to a working treatment, a step of producing (treating) a lubricating coating, a drying step, and a working step. After the working step, a step of a heat treatment and/or a surface treatment, and the like may be further performed. Each step will be described below.
  • At least one cleaning treatment selected from the group consisting of shot blasting, sand blasting, wet blasting, peeling, alkali degreasing, and pickling is preferably performed. Cleaning as used herein is performed for the purpose of removing oxide scales grown by annealing, and various contaminations (oils, etc.).
  • the degree of coating is not particularly limited as long as a surface of the steel wire rod is sufficiently coated with a lubricating coating agent used in the embodiment of the present invention, and also the coating time is not particularly limited.
  • the steel wire rod may be brought into contact with the lubricating coating agent after heating to a temperature in a range of 60 to 80° C.
  • the steel wire rod may also be brought into contact with the lubricating coating agent heated to a temperature in a range of 40 to 70° C.
  • Drying may be performed by being left to stand at a normal temperature, or may performed at 60 to 150° C. for 1 to 30 minutes.
  • the steel wire rod having a lubricating coating obtained by performing the production step of a lubricating coating and the drying step falls within the scope of steel wire rod according to the embodiment of the present invention. Even those obtained by subjecting the steel wire rod having a lubricating coating to a working treatment by the working step fall within the scope of steel wire rod according to the embodiment of the present invention as long as they have a lubricating coating.
  • the working treatment include a wire drawing treatment, a heading treatment, a forging treatment, and the like.
  • the mass of the coating per unit area of the lubricating coating formed on the steel wire rod is appropriately controlled by the degree of subsequent working.
  • the mass of the coating per unit area is preferably 1.0 g/m 2 or more, and more preferably 2.0 g/m 2 or more, and is also preferably 20 g/m 2 or less, and more preferably 15 g/m 2 or less.
  • the mass of the coating per unit area can be calculated from a difference in mass between steel wire rods before and after a treatment, and a surface area. To control so as to adjust in a range of the above-mentioned mass of the coating, the solid component mass (concentration) of the lubricating coating agent is appropriately adjusted.
  • the thus obtained dilution is often used.
  • water used for dilution and adjustment and, for example, pure water, deionized water, tap water, ground water, industrial water, and the like can be used.
  • the steel wire rod of the embodiment of the present invention can be further subjected to steps of a heat treatment, a surface treatment such as a plating treatment and the like.
  • the heat treatment is performed for the purpose of imparting strength and/or toughness by making the steel wire rod obtained by working step hard.
  • a common method can be employed and includes, for example, common heat treatments such as hardening and tempering; and surface heat treatments such as carburizing and quenching, and nitridization.
  • the plating treatment is performed for the purpose of imparting corrosion resistance, and is mainly applied to those after the heat treatment.
  • a common method can be employed and includes, for example, electroplating, hot dipping and the like.
  • type of plating and common plating can be performed and includes, for example, zinc plating, chromium plating, and nickel plating.
  • film removal can be performed by immersing the lubricating coating formed of the lubricating coating agent in an aqueous alkali cleaner, or spraying the aqueous alkali cleaner.
  • the alkali cleaner is a solution prepared by dissolving a common alkali component such as sodium hydroxide or potassium hydroxide in water and, when the alkali cleaner is brought into contact with the lubricating coating, the lubricating coating dissolves in the cleaning solution, thus making it possible to easily perform film removal. It is also possible to obtain a coating capable of easily falling off by a heat treatment after working. Therefore, alkali cleaning and/or heat treatment enable prevention of contamination and poor plating in the subsequent step caused by insufficient film removal.
  • D-1) Anionic polyethylene wax (average particle size of 5 ⁇ m)
  • D-2) Calcium stearate (average particle size of 8 ⁇ m)
  • a pretreatment, a lubricating coating treatment, and a drying treatment were carried out with respect to a surface of a ⁇ 12.5 mm steel wire rod (steel type: SCM435) by the following steps.
  • heading was performed by the procedure shown in FIG. 1 .
  • the steel wire rod was drawn through a ⁇ 11.05 die to fabricate a ⁇ 11.05 steel wire rod.
  • two-stage heading was carried out by a heading former. More specifically, as shown in the left figure of FIG. 1 , the steel wire rod was cut to the proper length. The steel wire rod thus cut was formed into the dimension shown in the center figure of FIG. 1 at a first stage, and then formed into the size of ⁇ 7.2 mm at a second stage as shown in the right figure of FIG. 1 .
  • former oil (DiaPress No. 17B manufactured by Kansaiyushi Kogyo Co., Ltd.) was applied immediately before heading in all levels.
  • the coating retention amount of the steel wire rod after heading, and the presence of poor appearance were evaluated in the following manner.
  • the coating retention amount after heading was determined as follows: a coating was removed (film removal) by the following method, and then the coating retention amount was calculated from the weight of the steel wire rod before and after removal, after heading.
  • Coating film remover commercially available alkali remover (FC-E6463, manufactured by Nihon Parkerizing Co., Ltd.), 20 g/L
  • Film removal method The coating film remover was heated to a liquid temperature of 60° C. and a steel wire rod after heading was immersed in the remover for 60 minutes, and then a coating film was removed by rubbing with a sponge. Thereafter, rinsing with deionized water was performed and water was completely brown away by compressed air.
  • the coating film retention amount was calculated in the following manner and then coating film retention properties were evaluated by the following criteria. The more the coating film retention amount increases, the more seizure resistance after heading becomes satisfactory. In this Example, the case where the coating retention amount is 0.8 g/m 2 or more was determined to be pass.
  • Coating retention amount (g/m 2 ) (weight of test piece before film removal ⁇ weight of test piece after film removal)/surface area of test piece
  • Coating retention amount is 1.8 g/m 2 or more.
  • C Coating retention amount is 0.8 g/m 2 or more and less than 1.8 g/m 2
  • D Coating retention amount is less than 0.8 g/m 2 (Evaluation Criteria of Poor Appearance after Heading) B: No poor appearance occurs.
  • D Poor appearance occurs over the entire surface of the heading portion.
  • A Extremely excellent as compared with performance of a lubricating coating in SPCC-SD of Comparative Example 8 (rust area of 3% or less)
  • B Excellent as compared with performance of a lubricating coating in SPCC-SD of Comparative Example 8 (rust area of exceeding 3% or 10% or less)
  • C Equivalent to performance of a lubricating coating in SPCC-SD of Comparative Example 8 (rust area of exceeding 10% or 20% or less)
  • the steel wire rod of Comparative Example 1 is a steel wire rod or SPCC-SD having a lubricating coating, which does not contain a water-soluble silicate as a source of supply of silicon (A).
  • the steel wire rod of Comparative Example 2 is a steel wire rod or SPCC-SD having a lubricating coating, which does not contain a water-soluble tungstate as a source of supply of tungsten (B).
  • the steel wire rod of Comparative Example 3 is a steel wire rod or SPCC-SD having a lubricating coating, in which a dry mass ratio (B)/(A) of A and B is high.
  • the steel wire rod of Comparative Example 4 is a steel wire rod or SPCC-SD having a lubricating coating, in which a dry mass ratio (B)/(A) of A and B is low. All the steel wire rods of Comparative Examples 1 to 4 were inferior in corrosion resistance.
  • the steel wire rods of Comparative Examples 5 to 7 are steel wire rods having a lubricating coating or SPCC-SD, in which the dry mass ratio of (C)/ ⁇ (A)+(B) ⁇ does not satisfy the scope of the present disclosure, or steel wire rods or SPCC-SD having a lubricating coating, in which the dry mass ratio does not satisfy the scope of the present disclosure, and an alkali metal salt of fatty acid (C) is not contained.
  • the steel wire rod of Comparative Example 5 is a steel wire rod or SPCC-SD having a lubricating coating, which does not contain an alkali metal salt of fatty acid (C) and contains only a wax (D) as the lubricant, was inferior in heading appearance.
  • the steel wire rod of Comparative Example 6 is a steel wire rod or SPCC-SD having a lubricating coating, in which the dry mass ratio of (C)/ ⁇ (A)+(B) ⁇ is lower than the scope of the present disclosure. Since the addition effect of an alkali metal salt of fatty acid (C) is not effectively exerted, heading appearance was poor.
  • the steel wire rod of Comparative Example 7 is a steel wire rod or SPCC-SD having a lubricating coating, in which the dry mass ratio of (C)/ ⁇ (A)+(B) ⁇ is higher than the scope of the present disclosure. Due to the addition effect of an alkali metal salt of fatty acid (C), appearance after heading was satisfactory. Because of too large amount of an alkali metal salt of fatty acid, the coating retention amount after heading decreased, leading to the occurrence of microseizure.
  • the steel wire rod of Comparative Example 8 is a steel wire rod or SPCC-SD (Conventional Example) having a phosphate coating formed by performing a reaction soap treatment. When heat treatments such as hardening and tempering are performed, phosphorizing may occur, leading to brittle steel wire rod.
  • the steel wire rod of the present disclosure includes no phosphorus in a lubricating coating, and is therefore free from phosphorizing property, and has satisfactory long-term corrosion resistance, which is identical to or higher than that of a conventional phosphate and a soap-treated material, and is also free from poor appearance after heading. Therefore, the steel wire rod of the present disclosure has significantly high industrial value of utilization.
  • a steel wire rod including a lubricating coating on a surface thereof, wherein the lubricating coating including silicon (A), tungsten (B) and an alkali metal salt of fatty acid (C), a dry mass ratio of (B)/(A) is in a range of 1.3 to 18 and a dry mass ratio of (C)/ ⁇ (A)+(B) ⁇ is in a range of 0.14 to 2.0, and the lubricating coating contains no phosphorus.
  • the steel wire rod according to aspect 1 or 2 wherein the silicon is derived from at least one selected from the group consisting of lithium silicate, sodium silicate, and potassium silicate, and the tungsten is derived from at least one selected from the group consisting of lithium tungstate, sodium tungstate, potassium tungstate, and ammonium tungstate.
  • the lubricating coating further includes a lubricant (D) other than the alkali metal salt of fatty acid (C), and a dry mass ratio of ⁇ (C)+(D) ⁇ / ⁇ (A)+(B) ⁇ is in a range of 0.14 to 2.0.
  • D lubricant
  • C alkali metal salt of fatty acid
  • lubricant (D) is at least one selected from the group consisting of wax, polytetrafluoroethylene, fatty acid metal soap, fatty acid amide, molybdenum disulfide, tungsten disulfide, graphite, and melamine cyanurate.
  • the lubricating coating further includes a resin (E), and a dry mass ratio of (E)/ ⁇ (A) ⁇ (B) ⁇ exceeds 0 and 1.4 or less.
  • the resin (E) is at least one selected from the group consisting of a vinyl resin, an acrylic resin, an epoxy resin, a urethane resin, a phenol resin, a cellulose derivative, a polymaleic acid, and a polyester resin.
  • a mass of a coating per unit area of the lubricating coating is in a range of 1.0 to 20 g/m 2 .

Landscapes

  • Chemical & Material Sciences (AREA)
  • Organic Chemistry (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • General Chemical & Material Sciences (AREA)
  • Oil, Petroleum & Natural Gas (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Metallurgy (AREA)
  • Mechanical Engineering (AREA)
  • Inorganic Chemistry (AREA)
  • Life Sciences & Earth Sciences (AREA)
  • Wood Science & Technology (AREA)
  • Health & Medical Sciences (AREA)
  • Emergency Medicine (AREA)
  • Lubricants (AREA)
  • Chemical Treatment Of Metals (AREA)
  • Other Surface Treatments For Metallic Materials (AREA)
US15/763,975 2015-09-30 2016-09-27 Steel wire with excellent corrosion resistance and appearance after processing Abandoned US20180273869A1 (en)

Applications Claiming Priority (5)

Application Number Priority Date Filing Date Title
JP2015-195149 2015-09-30
JP2015195149 2015-09-30
JP2016-121490 2016-06-20
JP2016121490A JP6694769B2 (ja) 2015-09-30 2016-06-20 耐食性及び加工後の外観に優れた鋼線材
PCT/JP2016/078500 WO2017057385A1 (ja) 2015-09-30 2016-09-27 耐食性及び加工後の外観に優れた鋼線材

Publications (1)

Publication Number Publication Date
US20180273869A1 true US20180273869A1 (en) 2018-09-27

Family

ID=58491941

Family Applications (1)

Application Number Title Priority Date Filing Date
US15/763,975 Abandoned US20180273869A1 (en) 2015-09-30 2016-09-27 Steel wire with excellent corrosion resistance and appearance after processing

Country Status (5)

Country Link
US (1) US20180273869A1 (ja)
JP (1) JP6694769B2 (ja)
KR (1) KR102105304B1 (ja)
CN (1) CN108138327B (ja)
MX (1) MX2018003548A (ja)

Families Citing this family (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN113118234B (zh) * 2021-04-16 2022-09-27 江西富鸿金属有限公司 一种医疗设备用镀锡合金线的生产工艺
CN113399483B (zh) * 2021-06-07 2022-10-18 威海银兴预应力线材有限公司 一种用于冷拔钢丝的环保型润滑涂膜剂及其制备方法与应用
JP2024035325A (ja) * 2022-09-02 2024-03-14 日本パーカライジング株式会社 金属表面処理剤、並びに皮膜を有する金属材料およびその製造方法

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2000309793A (ja) * 1999-04-27 2000-11-07 Nippon Parkerizing Co Ltd 金属材料塑性加工用水系潤滑剤
WO2015146848A1 (ja) * 2014-03-28 2015-10-01 株式会社神戸製鋼所 耐食性及び加工性に優れた潤滑皮膜を有する鋼線材

Family Cites Families (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
TW588108B (en) * 2000-08-07 2004-05-21 Nihon Parkerizing Aqueous lubricant for plastic working of metallic material and method for forming lubricant film
JP3984158B2 (ja) 2000-08-07 2007-10-03 日本パーカライジング株式会社 金属材料塑性加工用水系潤滑剤および潤滑皮膜の処理方法
JP4031213B2 (ja) 2001-06-07 2008-01-09 株式会社神戸製鋼所 皮膜形成剤及び皮膜
US7884058B2 (en) * 2003-09-30 2011-02-08 Chevron Oronite Company Llc Stable colloidal suspensions and lubricating oil compositions containing same
JP5181393B2 (ja) * 2008-11-20 2013-04-10 日本パーカライジング株式会社 締結部品用鋼線材
EP2450423B1 (en) * 2009-06-29 2019-05-15 Nihon Parkerizing Co., Ltd. Water-based lubricant for plastic processing having excellent corrosion resistance and metal material having excellent plastic processability
JP5682021B2 (ja) 2010-05-25 2015-03-11 日本パーカライジング株式会社 難結晶性を有し、耐吸湿性、耐食性及び加工性に優れる金属材料塑性加工用水系潤滑剤及びその潤滑皮膜を形成させた金属材料
JP2013209625A (ja) 2012-02-27 2013-10-10 Kobe Steel Ltd 塑性加工用水溶性潤滑剤、塑性加工用金属材および金属加工品

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2000309793A (ja) * 1999-04-27 2000-11-07 Nippon Parkerizing Co Ltd 金属材料塑性加工用水系潤滑剤
WO2015146848A1 (ja) * 2014-03-28 2015-10-01 株式会社神戸製鋼所 耐食性及び加工性に優れた潤滑皮膜を有する鋼線材
US20170175021A1 (en) * 2014-03-28 2017-06-22 Kabushiki Kaisha Kobe Seiko Sho (Kobe Steel, Ltd.) Steel wire rod having lubricating coating film that has excellent corrosion resistance and workability

Also Published As

Publication number Publication date
KR102105304B1 (ko) 2020-04-28
KR20180044997A (ko) 2018-05-03
JP2017066515A (ja) 2017-04-06
CN108138327A (zh) 2018-06-08
JP6694769B2 (ja) 2020-05-20
CN108138327B (zh) 2020-07-21
MX2018003548A (es) 2018-06-19

Similar Documents

Publication Publication Date Title
JP5457452B2 (ja) 耐食性に優れる塑性加工用水系潤滑剤および塑性加工性に優れる金属材料
US20170175021A1 (en) Steel wire rod having lubricating coating film that has excellent corrosion resistance and workability
JP6039075B2 (ja) 吸湿後の加工性及び耐カス詰まり性に優れた金属材料塑性加工用水系潤滑剤
JP5682021B2 (ja) 難結晶性を有し、耐吸湿性、耐食性及び加工性に優れる金属材料塑性加工用水系潤滑剤及びその潤滑皮膜を形成させた金属材料
CN105899650B (zh) 耐腐蚀性、加工性优异的水系润滑皮膜处理剂及金属材料
US20180273869A1 (en) Steel wire with excellent corrosion resistance and appearance after processing
US20180187119A1 (en) Steel wire rod having coating film that has excellent corrosion resistance and workability, and method for producing same
WO2017057385A1 (ja) 耐食性及び加工後の外観に優れた鋼線材
JP6216208B2 (ja) 塑性加工用非りん化成処理剤、処理液、化成皮膜及び化成皮膜を有する金属材料

Legal Events

Date Code Title Description
AS Assignment

Owner name: NIHON PARKERIZING CO., LTD., JAPAN

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:ITO, HIROTAKA;YAMANE, SHIGEHIRO;DUC, PHAM VAN;AND OTHERS;SIGNING DATES FROM 20180131 TO 20180219;REEL/FRAME:045372/0872

Owner name: KABUSHIKI KAISHA KOBE SEIKO SHO (KOBE STEEL, LTD.)

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:ITO, HIROTAKA;YAMANE, SHIGEHIRO;DUC, PHAM VAN;AND OTHERS;SIGNING DATES FROM 20180131 TO 20180219;REEL/FRAME:045372/0872

STPP Information on status: patent application and granting procedure in general

Free format text: DOCKETED NEW CASE - READY FOR EXAMINATION

STPP Information on status: patent application and granting procedure in general

Free format text: NON FINAL ACTION MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: RESPONSE TO NON-FINAL OFFICE ACTION ENTERED AND FORWARDED TO EXAMINER

STPP Information on status: patent application and granting procedure in general

Free format text: FINAL REJECTION MAILED

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION