US20180010259A1 - Surface-treated steel sheet, metal container, and method for producing surface-treated steel sheet - Google Patents
Surface-treated steel sheet, metal container, and method for producing surface-treated steel sheet Download PDFInfo
- Publication number
- US20180010259A1 US20180010259A1 US15/546,624 US201515546624A US2018010259A1 US 20180010259 A1 US20180010259 A1 US 20180010259A1 US 201515546624 A US201515546624 A US 201515546624A US 2018010259 A1 US2018010259 A1 US 2018010259A1
- Authority
- US
- United States
- Prior art keywords
- steel sheet
- tin
- aluminum
- compound layer
- phosphate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Links
- 229910000831 Steel Inorganic materials 0.000 title claims abstract description 265
- 239000010959 steel Substances 0.000 title claims abstract description 265
- 229910052751 metal Inorganic materials 0.000 title claims description 17
- 239000002184 metal Substances 0.000 title claims description 17
- 238000004519 manufacturing process Methods 0.000 title claims description 9
- CQBLUJRVOKGWCF-UHFFFAOYSA-N [O].[AlH3] Chemical compound [O].[AlH3] CQBLUJRVOKGWCF-UHFFFAOYSA-N 0.000 claims abstract description 130
- 229910019142 PO4 Inorganic materials 0.000 claims abstract description 106
- -1 phosphate compound Chemical class 0.000 claims abstract description 102
- 239000010452 phosphate Substances 0.000 claims abstract description 93
- 238000007747 plating Methods 0.000 claims abstract description 49
- QUBMWJKTLKIJNN-UHFFFAOYSA-B tin(4+);tetraphosphate Chemical compound [Sn+4].[Sn+4].[Sn+4].[O-]P([O-])([O-])=O.[O-]P([O-])([O-])=O.[O-]P([O-])([O-])=O.[O-]P([O-])([O-])=O QUBMWJKTLKIJNN-UHFFFAOYSA-B 0.000 claims abstract description 45
- XOLBLPGZBRYERU-UHFFFAOYSA-N tin dioxide Chemical compound O=[Sn]=O XOLBLPGZBRYERU-UHFFFAOYSA-N 0.000 claims abstract description 25
- ATJFFYVFTNAWJD-UHFFFAOYSA-N Tin Chemical compound [Sn] ATJFFYVFTNAWJD-UHFFFAOYSA-N 0.000 claims abstract description 24
- 229910001887 tin oxide Inorganic materials 0.000 claims abstract description 23
- 238000004833 X-ray photoelectron spectroscopy Methods 0.000 claims abstract description 12
- 238000001228 spectrum Methods 0.000 claims abstract description 11
- 230000010354 integration Effects 0.000 claims abstract description 10
- 239000000470 constituent Substances 0.000 claims abstract description 6
- 239000010410 layer Substances 0.000 claims description 309
- 239000007788 liquid Substances 0.000 claims description 88
- 239000011247 coating layer Substances 0.000 claims description 53
- 239000011368 organic material Substances 0.000 claims description 27
- NBIIXXVUZAFLBC-UHFFFAOYSA-K phosphate Chemical compound [O-]P([O-])([O-])=O NBIIXXVUZAFLBC-UHFFFAOYSA-K 0.000 claims description 26
- 229910052782 aluminium Inorganic materials 0.000 claims description 18
- OAICVXFJPJFONN-UHFFFAOYSA-N Phosphorus Chemical compound [P] OAICVXFJPJFONN-UHFFFAOYSA-N 0.000 claims description 17
- 229910052698 phosphorus Inorganic materials 0.000 claims description 17
- 239000011574 phosphorus Substances 0.000 claims description 17
- XAGFODPZIPBFFR-UHFFFAOYSA-N aluminium Chemical compound [Al] XAGFODPZIPBFFR-UHFFFAOYSA-N 0.000 claims description 16
- ILRRQNADMUWWFW-UHFFFAOYSA-K aluminium phosphate Chemical compound O1[Al]2OP1(=O)O2 ILRRQNADMUWWFW-UHFFFAOYSA-K 0.000 claims description 9
- 229910001128 Sn alloy Inorganic materials 0.000 claims description 6
- PXGOKWXKJXAPGV-UHFFFAOYSA-N Fluorine Chemical compound FF PXGOKWXKJXAPGV-UHFFFAOYSA-N 0.000 claims description 2
- 229910052731 fluorine Inorganic materials 0.000 claims description 2
- 239000011737 fluorine Substances 0.000 claims description 2
- 235000021317 phosphate Nutrition 0.000 description 89
- 238000000034 method Methods 0.000 description 33
- 238000011156 evaluation Methods 0.000 description 30
- 239000011248 coating agent Substances 0.000 description 29
- 238000000576 coating method Methods 0.000 description 29
- 238000005260 corrosion Methods 0.000 description 28
- 230000007797 corrosion Effects 0.000 description 28
- 150000002500 ions Chemical class 0.000 description 28
- 230000000052 comparative effect Effects 0.000 description 23
- 239000000243 solution Substances 0.000 description 19
- NBIIXXVUZAFLBC-UHFFFAOYSA-N Phosphoric acid Chemical compound OP(O)(O)=O NBIIXXVUZAFLBC-UHFFFAOYSA-N 0.000 description 15
- 239000007864 aqueous solution Substances 0.000 description 15
- 238000007669 thermal treatment Methods 0.000 description 15
- 229910000147 aluminium phosphate Inorganic materials 0.000 description 10
- 238000005259 measurement Methods 0.000 description 10
- 229920000139 polyethylene terephthalate Polymers 0.000 description 9
- 239000005020 polyethylene terephthalate Substances 0.000 description 9
- 238000012360 testing method Methods 0.000 description 9
- 239000000463 material Substances 0.000 description 8
- NBIIXXVUZAFLBC-UHFFFAOYSA-L Phosphate ion(2-) Chemical compound OP([O-])([O-])=O NBIIXXVUZAFLBC-UHFFFAOYSA-L 0.000 description 7
- QQVIHTHCMHWDBS-UHFFFAOYSA-L isophthalate(2-) Chemical compound [O-]C(=O)C1=CC=CC(C([O-])=O)=C1 QQVIHTHCMHWDBS-UHFFFAOYSA-L 0.000 description 7
- 239000000203 mixture Substances 0.000 description 7
- 229920001225 polyester resin Polymers 0.000 description 7
- 239000004645 polyester resin Substances 0.000 description 7
- 229910001432 tin ion Inorganic materials 0.000 description 7
- PXHVJJICTQNCMI-UHFFFAOYSA-N Nickel Chemical compound [Ni] PXHVJJICTQNCMI-UHFFFAOYSA-N 0.000 description 6
- RTAQQCXQSZGOHL-UHFFFAOYSA-N Titanium Chemical compound [Ti] RTAQQCXQSZGOHL-UHFFFAOYSA-N 0.000 description 6
- KRKNYBCHXYNGOX-UHFFFAOYSA-N citric acid Chemical compound OC(=O)CC(O)(C(O)=O)CC(O)=O KRKNYBCHXYNGOX-UHFFFAOYSA-N 0.000 description 6
- 238000004445 quantitative analysis Methods 0.000 description 6
- 150000003606 tin compounds Chemical class 0.000 description 6
- 239000010936 titanium Substances 0.000 description 6
- 229910052719 titanium Inorganic materials 0.000 description 6
- 230000000007 visual effect Effects 0.000 description 6
- NHNBFGGVMKEFGY-UHFFFAOYSA-N Nitrate Chemical compound [O-][N+]([O-])=O NHNBFGGVMKEFGY-UHFFFAOYSA-N 0.000 description 5
- 239000002253 acid Substances 0.000 description 5
- 230000015572 biosynthetic process Effects 0.000 description 5
- 238000005868 electrolysis reaction Methods 0.000 description 5
- 150000003013 phosphoric acid derivatives Chemical class 0.000 description 5
- 229920005989 resin Polymers 0.000 description 5
- 239000011347 resin Substances 0.000 description 5
- 229920005992 thermoplastic resin Polymers 0.000 description 5
- XLYOFNOQVPJJNP-UHFFFAOYSA-N water Substances O XLYOFNOQVPJJNP-UHFFFAOYSA-N 0.000 description 5
- VEXZGXHMUGYJMC-UHFFFAOYSA-N Hydrochloric acid Chemical compound Cl VEXZGXHMUGYJMC-UHFFFAOYSA-N 0.000 description 4
- QAOWNCQODCNURD-UHFFFAOYSA-N Sulfuric acid Chemical compound OS(O)(=O)=O QAOWNCQODCNURD-UHFFFAOYSA-N 0.000 description 4
- 235000013361 beverage Nutrition 0.000 description 4
- HTXDPTMKBJXEOW-UHFFFAOYSA-N dioxoiridium Chemical compound O=[Ir]=O HTXDPTMKBJXEOW-UHFFFAOYSA-N 0.000 description 4
- 238000004090 dissolution Methods 0.000 description 4
- 238000002149 energy-dispersive X-ray emission spectroscopy Methods 0.000 description 4
- 229910000457 iridium oxide Inorganic materials 0.000 description 4
- 238000010409 ironing Methods 0.000 description 4
- BASFCYQUMIYNBI-UHFFFAOYSA-N platinum Chemical compound [Pt] BASFCYQUMIYNBI-UHFFFAOYSA-N 0.000 description 4
- 238000004876 x-ray fluorescence Methods 0.000 description 4
- QTBSBXVTEAMEQO-UHFFFAOYSA-N Acetic acid Chemical compound CC(O)=O QTBSBXVTEAMEQO-UHFFFAOYSA-N 0.000 description 3
- OKTJSMMVPCPJKN-UHFFFAOYSA-N Carbon Chemical compound [C] OKTJSMMVPCPJKN-UHFFFAOYSA-N 0.000 description 3
- 229910000640 Fe alloy Inorganic materials 0.000 description 3
- 229910002651 NO3 Inorganic materials 0.000 description 3
- UCKMPCXJQFINFW-UHFFFAOYSA-N Sulphide Chemical compound [S-2] UCKMPCXJQFINFW-UHFFFAOYSA-N 0.000 description 3
- 230000002378 acidificating effect Effects 0.000 description 3
- 238000004458 analytical method Methods 0.000 description 3
- 229910052799 carbon Inorganic materials 0.000 description 3
- 239000003795 chemical substances by application Substances 0.000 description 3
- ZCDOYSPFYFSLEW-UHFFFAOYSA-N chromate(2-) Chemical compound [O-][Cr]([O-])(=O)=O ZCDOYSPFYFSLEW-UHFFFAOYSA-N 0.000 description 3
- BNIILDVGGAEEIG-UHFFFAOYSA-L disodium hydrogen phosphate Chemical compound [Na+].[Na+].OP([O-])([O-])=O BNIILDVGGAEEIG-UHFFFAOYSA-L 0.000 description 3
- 230000000694 effects Effects 0.000 description 3
- 238000010438 heat treatment Methods 0.000 description 3
- BHEPBYXIRTUNPN-UHFFFAOYSA-N hydridophosphorus(.) (triplet) Chemical compound [PH] BHEPBYXIRTUNPN-UHFFFAOYSA-N 0.000 description 3
- 238000007654 immersion Methods 0.000 description 3
- 229910052759 nickel Inorganic materials 0.000 description 3
- 229910052760 oxygen Inorganic materials 0.000 description 3
- 229940085991 phosphate ion Drugs 0.000 description 3
- 238000012545 processing Methods 0.000 description 3
- 239000000047 product Substances 0.000 description 3
- AJPJDKMHJJGVTQ-UHFFFAOYSA-M sodium dihydrogen phosphate Chemical compound [Na+].OP(O)([O-])=O AJPJDKMHJJGVTQ-UHFFFAOYSA-M 0.000 description 3
- 239000000126 substance Substances 0.000 description 3
- 239000002344 surface layer Substances 0.000 description 3
- 239000008399 tap water Substances 0.000 description 3
- 235000020679 tap water Nutrition 0.000 description 3
- AEMRFAOFKBGASW-UHFFFAOYSA-N Glycolic acid Chemical compound OCC(O)=O AEMRFAOFKBGASW-UHFFFAOYSA-N 0.000 description 2
- CPELXLSAUQHCOX-UHFFFAOYSA-N Hydrogen bromide Chemical compound Br CPELXLSAUQHCOX-UHFFFAOYSA-N 0.000 description 2
- 239000004698 Polyethylene Substances 0.000 description 2
- CDBYLPFSWZWCQE-UHFFFAOYSA-L Sodium Carbonate Chemical compound [Na+].[Na+].[O-]C([O-])=O CDBYLPFSWZWCQE-UHFFFAOYSA-L 0.000 description 2
- UIIMBOGNXHQVGW-UHFFFAOYSA-M Sodium bicarbonate Chemical compound [Na+].OC([O-])=O UIIMBOGNXHQVGW-UHFFFAOYSA-M 0.000 description 2
- FAPWRFPIFSIZLT-UHFFFAOYSA-M Sodium chloride Chemical compound [Na+].[Cl-] FAPWRFPIFSIZLT-UHFFFAOYSA-M 0.000 description 2
- 239000000654 additive Substances 0.000 description 2
- WNROFYMDJYEPJX-UHFFFAOYSA-K aluminium hydroxide Chemical compound [OH-].[OH-].[OH-].[Al+3] WNROFYMDJYEPJX-UHFFFAOYSA-K 0.000 description 2
- QVGXLLKOCUKJST-UHFFFAOYSA-N atomic oxygen Chemical compound [O] QVGXLLKOCUKJST-UHFFFAOYSA-N 0.000 description 2
- 230000005540 biological transmission Effects 0.000 description 2
- 238000004364 calculation method Methods 0.000 description 2
- 150000001875 compounds Chemical class 0.000 description 2
- 238000005520 cutting process Methods 0.000 description 2
- NBIIXXVUZAFLBC-UHFFFAOYSA-M dihydrogenphosphate Chemical compound OP(O)([O-])=O NBIIXXVUZAFLBC-UHFFFAOYSA-M 0.000 description 2
- 229910000397 disodium phosphate Inorganic materials 0.000 description 2
- 238000001035 drying Methods 0.000 description 2
- 125000001153 fluoro group Chemical group F* 0.000 description 2
- 239000012535 impurity Substances 0.000 description 2
- NNIPDXPTJYIMKW-UHFFFAOYSA-N iron tin Chemical compound [Fe].[Sn] NNIPDXPTJYIMKW-UHFFFAOYSA-N 0.000 description 2
- JVTAAEKCZFNVCJ-UHFFFAOYSA-N lactic acid Chemical compound CC(O)C(O)=O JVTAAEKCZFNVCJ-UHFFFAOYSA-N 0.000 description 2
- 238000002844 melting Methods 0.000 description 2
- 230000008018 melting Effects 0.000 description 2
- 229910000403 monosodium phosphate Inorganic materials 0.000 description 2
- 235000019799 monosodium phosphate Nutrition 0.000 description 2
- LGQLOGILCSXPEA-UHFFFAOYSA-L nickel sulfate Chemical compound [Ni+2].[O-]S([O-])(=O)=O LGQLOGILCSXPEA-UHFFFAOYSA-L 0.000 description 2
- 229910000363 nickel(II) sulfate Inorganic materials 0.000 description 2
- 239000001301 oxygen Substances 0.000 description 2
- 150000002927 oxygen compounds Chemical class 0.000 description 2
- 239000002245 particle Substances 0.000 description 2
- 239000005011 phenolic resin Substances 0.000 description 2
- 229910052697 platinum Inorganic materials 0.000 description 2
- 229920000573 polyethylene Polymers 0.000 description 2
- 239000002244 precipitate Substances 0.000 description 2
- 238000000926 separation method Methods 0.000 description 2
- 238000003756 stirring Methods 0.000 description 2
- 238000004381 surface treatment Methods 0.000 description 2
- KKEYFWRCBNTPAC-UHFFFAOYSA-L terephthalate(2-) Chemical compound [O-]C(=O)C1=CC=C(C([O-])=O)C=C1 KKEYFWRCBNTPAC-UHFFFAOYSA-L 0.000 description 2
- ISIJQEHRDSCQIU-UHFFFAOYSA-N tert-butyl 2,7-diazaspiro[4.5]decane-7-carboxylate Chemical compound C1N(C(=O)OC(C)(C)C)CCCC11CNCC1 ISIJQEHRDSCQIU-UHFFFAOYSA-N 0.000 description 2
- 239000004634 thermosetting polymer Substances 0.000 description 2
- BNGXYYYYKUGPPF-UHFFFAOYSA-M (3-methylphenyl)methyl-triphenylphosphanium;chloride Chemical compound [Cl-].CC1=CC=CC(C[P+](C=2C=CC=CC=2)(C=2C=CC=CC=2)C=2C=CC=CC=2)=C1 BNGXYYYYKUGPPF-UHFFFAOYSA-M 0.000 description 1
- HNSDLXPSAYFUHK-UHFFFAOYSA-N 1,4-bis(2-ethylhexyl) sulfosuccinate Chemical compound CCCCC(CC)COC(=O)CC(S(O)(=O)=O)C(=O)OCC(CC)CCCC HNSDLXPSAYFUHK-UHFFFAOYSA-N 0.000 description 1
- BVKZGUZCCUSVTD-UHFFFAOYSA-L Carbonate Chemical compound [O-]C([O-])=O BVKZGUZCCUSVTD-UHFFFAOYSA-L 0.000 description 1
- RYGMFSIKBFXOCR-UHFFFAOYSA-N Copper Chemical compound [Cu] RYGMFSIKBFXOCR-UHFFFAOYSA-N 0.000 description 1
- FEWJPZIEWOKRBE-JCYAYHJZSA-N Dextrotartaric acid Chemical compound OC(=O)[C@H](O)[C@@H](O)C(O)=O FEWJPZIEWOKRBE-JCYAYHJZSA-N 0.000 description 1
- 239000004593 Epoxy Substances 0.000 description 1
- UFHFLCQGNIYNRP-UHFFFAOYSA-N Hydrogen Chemical compound [H][H] UFHFLCQGNIYNRP-UHFFFAOYSA-N 0.000 description 1
- 229910001030 Iron–nickel alloy Inorganic materials 0.000 description 1
- 229910000655 Killed steel Inorganic materials 0.000 description 1
- JHWNWJKBPDFINM-UHFFFAOYSA-N Laurolactam Chemical compound O=C1CCCCCCCCCCCN1 JHWNWJKBPDFINM-UHFFFAOYSA-N 0.000 description 1
- 229910021586 Nickel(II) chloride Inorganic materials 0.000 description 1
- 229920000571 Nylon 11 Polymers 0.000 description 1
- 229920000299 Nylon 12 Polymers 0.000 description 1
- 229920002292 Nylon 6 Polymers 0.000 description 1
- 229920002302 Nylon 6,6 Polymers 0.000 description 1
- 239000004952 Polyamide Substances 0.000 description 1
- 229920001328 Polyvinylidene chloride Polymers 0.000 description 1
- VYPSYNLAJGMNEJ-UHFFFAOYSA-N Silicium dioxide Chemical compound O=[Si]=O VYPSYNLAJGMNEJ-UHFFFAOYSA-N 0.000 description 1
- 229920002125 Sokalan® Polymers 0.000 description 1
- 229930006000 Sucrose Natural products 0.000 description 1
- CZMRCDWAGMRECN-UGDNZRGBSA-N Sucrose Chemical compound O[C@H]1[C@H](O)[C@@H](CO)O[C@@]1(CO)O[C@@H]1[C@H](O)[C@@H](O)[C@H](O)[C@@H](CO)O1 CZMRCDWAGMRECN-UGDNZRGBSA-N 0.000 description 1
- 238000003917 TEM image Methods 0.000 description 1
- FEWJPZIEWOKRBE-UHFFFAOYSA-N Tartaric acid Natural products [H+].[H+].[O-]C(=O)C(O)C(O)C([O-])=O FEWJPZIEWOKRBE-UHFFFAOYSA-N 0.000 description 1
- YEDTWOLJNQYBPU-UHFFFAOYSA-N [Na].[Na].[Na] Chemical compound [Na].[Na].[Na] YEDTWOLJNQYBPU-UHFFFAOYSA-N 0.000 description 1
- PYWICZIXLIWNGZ-UHFFFAOYSA-N [Sn].[Ni].[Fe] Chemical compound [Sn].[Ni].[Fe] PYWICZIXLIWNGZ-UHFFFAOYSA-N 0.000 description 1
- 230000002745 absorbent Effects 0.000 description 1
- 239000002250 absorbent Substances 0.000 description 1
- WNLRTRBMVRJNCN-UHFFFAOYSA-L adipate(2-) Chemical compound [O-]C(=O)CCCCC([O-])=O WNLRTRBMVRJNCN-UHFFFAOYSA-L 0.000 description 1
- 230000000274 adsorptive effect Effects 0.000 description 1
- 239000012670 alkaline solution Substances 0.000 description 1
- 229910021502 aluminium hydroxide Inorganic materials 0.000 description 1
- PNEYBMLMFCGWSK-UHFFFAOYSA-N aluminium oxide Inorganic materials [O-2].[O-2].[O-2].[Al+3].[Al+3] PNEYBMLMFCGWSK-UHFFFAOYSA-N 0.000 description 1
- BFNBIHQBYMNNAN-UHFFFAOYSA-N ammonium sulfate Chemical compound N.N.OS(O)(=O)=O BFNBIHQBYMNNAN-UHFFFAOYSA-N 0.000 description 1
- 229910052921 ammonium sulfate Inorganic materials 0.000 description 1
- 235000011130 ammonium sulphate Nutrition 0.000 description 1
- 238000004873 anchoring Methods 0.000 description 1
- 239000010405 anode material Substances 0.000 description 1
- 239000003963 antioxidant agent Substances 0.000 description 1
- 230000003078 antioxidant effect Effects 0.000 description 1
- 239000002216 antistatic agent Substances 0.000 description 1
- 125000004429 atom Chemical group 0.000 description 1
- 239000004566 building material Substances 0.000 description 1
- VQWFNAGFNGABOH-UHFFFAOYSA-K chromium(iii) hydroxide Chemical compound [OH-].[OH-].[OH-].[Cr+3] VQWFNAGFNGABOH-UHFFFAOYSA-K 0.000 description 1
- 235000015165 citric acid Nutrition 0.000 description 1
- 239000010960 cold rolled steel Substances 0.000 description 1
- 238000005097 cold rolling Methods 0.000 description 1
- 238000013329 compounding Methods 0.000 description 1
- 238000001816 cooling Methods 0.000 description 1
- 229920001577 copolymer Polymers 0.000 description 1
- 229910052802 copper Inorganic materials 0.000 description 1
- 239000010949 copper Substances 0.000 description 1
- 229910052593 corundum Inorganic materials 0.000 description 1
- GVJHHUAWPYXKBD-UHFFFAOYSA-N d-alpha-tocopherol Natural products OC1=C(C)C(C)=C2OC(CCCC(C)CCCC(C)CCCC(C)C)(C)CCC2=C1C GVJHHUAWPYXKBD-UHFFFAOYSA-N 0.000 description 1
- 239000013527 degreasing agent Substances 0.000 description 1
- 238000005237 degreasing agent Methods 0.000 description 1
- 230000008021 deposition Effects 0.000 description 1
- 230000006866 deterioration Effects 0.000 description 1
- 238000009792 diffusion process Methods 0.000 description 1
- 235000019800 disodium phosphate Nutrition 0.000 description 1
- 230000005611 electricity Effects 0.000 description 1
- 238000000605 extraction Methods 0.000 description 1
- 238000007765 extrusion coating Methods 0.000 description 1
- 239000000796 flavoring agent Substances 0.000 description 1
- 235000019634 flavors Nutrition 0.000 description 1
- 238000009472 formulation Methods 0.000 description 1
- 229910001679 gibbsite Inorganic materials 0.000 description 1
- 229910052736 halogen Inorganic materials 0.000 description 1
- 150000002367 halogens Chemical class 0.000 description 1
- 229910052739 hydrogen Inorganic materials 0.000 description 1
- 150000002431 hydrogen Chemical class 0.000 description 1
- 239000001257 hydrogen Substances 0.000 description 1
- 229910000042 hydrogen bromide Inorganic materials 0.000 description 1
- 239000008235 industrial water Substances 0.000 description 1
- 239000011256 inorganic filler Substances 0.000 description 1
- 229910003475 inorganic filler Inorganic materials 0.000 description 1
- 239000012212 insulator Substances 0.000 description 1
- 238000004255 ion exchange chromatography Methods 0.000 description 1
- 238000010884 ion-beam technique Methods 0.000 description 1
- 229920000554 ionomer Polymers 0.000 description 1
- 239000004310 lactic acid Substances 0.000 description 1
- 235000014655 lactic acid Nutrition 0.000 description 1
- 238000010030 laminating Methods 0.000 description 1
- 238000000465 moulding Methods 0.000 description 1
- QMMRZOWCJAIUJA-UHFFFAOYSA-L nickel dichloride Chemical compound Cl[Ni]Cl QMMRZOWCJAIUJA-UHFFFAOYSA-L 0.000 description 1
- CLDVQCMGOSGNIW-UHFFFAOYSA-N nickel tin Chemical compound [Ni].[Sn] CLDVQCMGOSGNIW-UHFFFAOYSA-N 0.000 description 1
- 150000007524 organic acids Chemical class 0.000 description 1
- 235000005985 organic acids Nutrition 0.000 description 1
- TWNQGVIAIRXVLR-UHFFFAOYSA-N oxo(oxoalumanyloxy)alumane Chemical compound O=[Al]O[Al]=O TWNQGVIAIRXVLR-UHFFFAOYSA-N 0.000 description 1
- 239000003973 paint Substances 0.000 description 1
- QQVIHTHCMHWDBS-UHFFFAOYSA-N perisophthalic acid Natural products OC(=O)C1=CC=CC(C(O)=O)=C1 QQVIHTHCMHWDBS-UHFFFAOYSA-N 0.000 description 1
- ISWSIDIOOBJBQZ-UHFFFAOYSA-N phenol group Chemical group C1(=CC=CC=C1)O ISWSIDIOOBJBQZ-UHFFFAOYSA-N 0.000 description 1
- 125000004437 phosphorous atom Chemical group 0.000 description 1
- 238000005554 pickling Methods 0.000 description 1
- QVLTXCYWHPZMCA-UHFFFAOYSA-N po4-po4 Chemical compound OP(O)(O)=O.OP(O)(O)=O QVLTXCYWHPZMCA-UHFFFAOYSA-N 0.000 description 1
- 229920001200 poly(ethylene-vinyl acetate) Polymers 0.000 description 1
- 239000004584 polyacrylic acid Substances 0.000 description 1
- 229920002647 polyamide Polymers 0.000 description 1
- 229920001707 polybutylene terephthalate Polymers 0.000 description 1
- 229920006267 polyester film Polymers 0.000 description 1
- 239000004800 polyvinyl chloride Substances 0.000 description 1
- 229920000915 polyvinyl chloride Polymers 0.000 description 1
- 239000005033 polyvinylidene chloride Substances 0.000 description 1
- 238000001556 precipitation Methods 0.000 description 1
- 230000002035 prolonged effect Effects 0.000 description 1
- 239000004065 semiconductor Substances 0.000 description 1
- 239000012748 slip agent Substances 0.000 description 1
- 229910000030 sodium bicarbonate Inorganic materials 0.000 description 1
- 235000017557 sodium bicarbonate Nutrition 0.000 description 1
- 229910000029 sodium carbonate Inorganic materials 0.000 description 1
- 239000011780 sodium chloride Substances 0.000 description 1
- 239000001488 sodium phosphate Substances 0.000 description 1
- ANOBYBYXJXCGBS-UHFFFAOYSA-L stannous fluoride Chemical compound F[Sn]F ANOBYBYXJXCGBS-UHFFFAOYSA-L 0.000 description 1
- 238000003860 storage Methods 0.000 description 1
- 239000005720 sucrose Substances 0.000 description 1
- 239000011975 tartaric acid Substances 0.000 description 1
- 235000002906 tartaric acid Nutrition 0.000 description 1
- 235000010384 tocopherol Nutrition 0.000 description 1
- 229960001295 tocopherol Drugs 0.000 description 1
- 229930003799 tocopherol Natural products 0.000 description 1
- 239000011732 tocopherol Substances 0.000 description 1
- 238000007740 vapor deposition Methods 0.000 description 1
- 238000005406 washing Methods 0.000 description 1
- 229910001845 yogo sapphire Inorganic materials 0.000 description 1
- GVJHHUAWPYXKBD-IEOSBIPESA-N α-tocopherol Chemical compound OC1=C(C)C(C)=C2O[C@@](CCC[C@H](C)CCC[C@H](C)CCCC(C)C)(C)CCC2=C1C GVJHHUAWPYXKBD-IEOSBIPESA-N 0.000 description 1
Images
Classifications
-
- C—CHEMISTRY; METALLURGY
- C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
- C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
- C25D9/00—Electrolytic coating other than with metals
- C25D9/04—Electrolytic coating other than with metals with inorganic materials
- C25D9/08—Electrolytic coating other than with metals with inorganic materials by cathodic processes
- C25D9/12—Electrolytic coating other than with metals with inorganic materials by cathodic processes on light metals
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B32—LAYERED PRODUCTS
- B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
- B32B15/00—Layered products comprising a layer of metal
- B32B15/04—Layered products comprising a layer of metal comprising metal as the main or only constituent of a layer, which is next to another layer of the same or of a different material
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B32—LAYERED PRODUCTS
- B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
- B32B15/00—Layered products comprising a layer of metal
- B32B15/04—Layered products comprising a layer of metal comprising metal as the main or only constituent of a layer, which is next to another layer of the same or of a different material
- B32B15/043—Layered products comprising a layer of metal comprising metal as the main or only constituent of a layer, which is next to another layer of the same or of a different material of metal
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B32—LAYERED PRODUCTS
- B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
- B32B15/00—Layered products comprising a layer of metal
- B32B15/04—Layered products comprising a layer of metal comprising metal as the main or only constituent of a layer, which is next to another layer of the same or of a different material
- B32B15/08—Layered products comprising a layer of metal comprising metal as the main or only constituent of a layer, which is next to another layer of the same or of a different material of synthetic resin
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B32—LAYERED PRODUCTS
- B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
- B32B15/00—Layered products comprising a layer of metal
- B32B15/18—Layered products comprising a layer of metal comprising iron or steel
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B32—LAYERED PRODUCTS
- B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
- B32B9/00—Layered products comprising a layer of a particular substance not covered by groups B32B11/00 - B32B29/00
-
- C—CHEMISTRY; METALLURGY
- C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
- C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
- C25D11/00—Electrolytic coating by surface reaction, i.e. forming conversion layers
- C25D11/36—Phosphatising
-
- C—CHEMISTRY; METALLURGY
- C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
- C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
- C25D5/00—Electroplating characterised by the process; Pretreatment or after-treatment of workpieces
- C25D5/48—After-treatment of electroplated surfaces
-
- C—CHEMISTRY; METALLURGY
- C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
- C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
- C25D7/00—Electroplating characterised by the article coated
-
- C—CHEMISTRY; METALLURGY
- C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
- C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
- C25D7/00—Electroplating characterised by the article coated
- C25D7/06—Wires; Strips; Foils
- C25D7/0614—Strips or foils
-
- C—CHEMISTRY; METALLURGY
- C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
- C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
- C25D9/00—Electrolytic coating other than with metals
- C25D9/04—Electrolytic coating other than with metals with inorganic materials
-
- C—CHEMISTRY; METALLURGY
- C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
- C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
- C25D9/00—Electrolytic coating other than with metals
- C25D9/04—Electrolytic coating other than with metals with inorganic materials
- C25D9/06—Electrolytic coating other than with metals with inorganic materials by anodic processes
-
- C—CHEMISTRY; METALLURGY
- C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
- C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
- C25D9/00—Electrolytic coating other than with metals
- C25D9/04—Electrolytic coating other than with metals with inorganic materials
- C25D9/08—Electrolytic coating other than with metals with inorganic materials by cathodic processes
-
- C—CHEMISTRY; METALLURGY
- C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
- C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
- C25D9/00—Electrolytic coating other than with metals
- C25D9/04—Electrolytic coating other than with metals with inorganic materials
- C25D9/08—Electrolytic coating other than with metals with inorganic materials by cathodic processes
- C25D9/10—Electrolytic coating other than with metals with inorganic materials by cathodic processes on iron or steel
-
- C—CHEMISTRY; METALLURGY
- C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
- C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
- C25D3/00—Electroplating: Baths therefor
- C25D3/02—Electroplating: Baths therefor from solutions
- C25D3/30—Electroplating: Baths therefor from solutions of tin
-
- C—CHEMISTRY; METALLURGY
- C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
- C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
- C25D5/00—Electroplating characterised by the process; Pretreatment or after-treatment of workpieces
- C25D5/34—Pretreatment of metallic surfaces to be electroplated
- C25D5/36—Pretreatment of metallic surfaces to be electroplated of iron or steel
Definitions
- the present invention relates to a surface-treated steel sheet, a metal container, and a method for producing a surface-treated steel sheet.
- Patent Document 1 discloses, for example, a non-chromic surface treatment technique of forming a metal-oxygen compound film containing aluminum on a base material surface by means of cathode electrolytic treatment using an electrolytic treatment liquid containing aluminum ions.
- the surface-treated steel sheet obtained by the conventional art described in the above Patent Document 1 may exhibit poorer corrosion resistance than that of a surface-treated steel sheet of which surface is chromate-treated when used in cans for food and beverages and the like.
- the present inventors have found that the above object can be achieved by a surface-treated steel sheet obtained by forming a phosphate compound layer containing tin phosphate on a tin-plated steel sheet followed by forming an aluminum-oxygen compound layer mainly formed of an aluminum-oxygen compound on this phosphate compound layer wherein the content ratio between tin oxide and tin phosphate contained in the aluminum-oxygen compound layer is adjusted.
- the inventors have thus accomplished the present invention.
- a surface-treated steel sheet including: a tin-plated steel sheet obtained by tin-plating a steel sheet; a phosphate compound layer containing tin phosphate formed on the tin-plated steel sheet; and an aluminum-oxygen compound layer formed on the phosphate compound layer, a main constituent being an aluminum-oxygen compound, wherein, when the 3d 5/2 spectrum of tin in the aluminum-oxygen compound layer is determined using an X-ray photoelectron spectroscopy, the ratio of the integration value of the profile derived from tin oxide to the integration value of the profile derived from tin phosphate (tin oxide/tin phosphate) is 6.9 or more.
- the aluminum-oxygen compound layer preferably contains aluminum phosphate.
- the total amount of phosphorus contained in each of the layers formed on the tin-plated steel sheet is preferably 0.5 to 20 mg/m 2 .
- the content of aluminum in the aluminum-oxygen compound layer is preferably 5 to 15 mg/m 2 .
- the aluminum-oxygen compound layer preferably contains substantially no fluorine.
- the tin-plated steel sheet preferably consists of the steel sheet, a tin alloy layer formed on the steel sheet, and a tin-plating layer formed on the tin alloy layer, and a total amount of tin in the tin alloy layer and the tin-plating layer is preferably 1.0 g/m 2 or more.
- a metal container formed of the surface-treated steel sheet is provided.
- a metal container including the surface-treated steel sheet and a coating layer formed on the aluminum-oxygen compound layer of the surface-treated steel sheet, a main constituent of the coating layer being an organic material.
- a method for producing a surface-treated steel sheet including: a phosphate compound layer-formation step of forming a phosphate compound layer on a tin-plated steel sheet by means of cathode electrolytic treatment, wherein the tin-plated steel sheet is obtained by tin-plating a steel sheet; and an aluminum-oxygen compound layer-formation step of forming an aluminum-oxygen compound layer on the phosphate compound layer by means of electrolytic treatment using an electrolytic treatment liquid containing aluminum.
- the phosphate compound layer-formation step of the production method of the present invention the phosphate compound layer is preferably formed on the tin-plated steel sheet by means of cathode electrolytic treatment after anode electrolytic treatment is conducted.
- a treatment liquid having a phosphate content of 0.55 g/L or less in terms of phosphorus is preferably used as the electrolytic treatment liquid in the aluminum-oxygen compound layer-formation step.
- a phosphate compound layer and an aluminum-oxygen compound layer is formed on a tin-plated steel sheet while setting the ratio the ratio of the above tin oxide/tin phosphate to 6.9 or more in the aluminum-oxygen compound layer. Then, there can be provided a surface-treated steel sheet having excellent corrosion resistance due to action of tin oxide and phosphate such as tin phosphate contained in the aluminum-oxygen compound layer.
- FIG. 1 is a cross-sectional view illustrating a configuration of a surface-treated steel sheet according to an embodiment of the present invention.
- FIG. 2 is a schematic view illustrating a process of forming a phosphate compound layer and an aluminum-oxygen compound layer on a tin-plated steel sheet.
- FIG. 3 is a graph showing an exemplary result of measurement of an aluminum-oxygen compound layer by an X-ray photoelectron spectroscopy (XPS).
- XPS X-ray photoelectron spectroscopy
- FIGS. 4(A) and 4(B) each are views illustrating an example of a metal container formed using the surface-treated steel sheet according to an embodiment of the present invention.
- FIGS. 5(A) and 5(B) are graphs showing the result of analysis of an aluminum-oxygen compound layer by an X-ray photoelectron spectroscopy (XPS) in Example 5 and Example 6 according to the present invention, respectively.
- XPS X-ray photoelectron spectroscopy
- FIG. 6 includes a cross-sectional view obtained by a transmission electron microscope (TEM) illustrating a state where a phosphate compound layer and an aluminum-oxygen compound layer are formed on a tin-plated steel sheet in Example according to the present invention, and the result of quantitative analysis thereof at each point.
- TEM transmission electron microscope
- FIG. 1 is a cross-sectional view illustrating a configuration of a surface-treated steel sheet 1 according to an embodiment of the present invention.
- the surface-treated steel sheet 1 of the present embodiment is obtained by the following method: first, a tin-plated steel sheet 10 obtained by forming a tin-plating layer 12 on a steel sheet 11 is subjected to electrolytic treatment in an electrolytic treatment liquid containing phosphate ions to form a phosphate compound layer 20 on the tin-plated steel sheet 10 while dissolving a portion of the tin-plating layer 12 , and subsequently the tin-plated steel sheet 10 thus subjected to electrolytic treatment is further subjected to electrolytic treatment in an electrolytic treatment liquid containing Al ions to form an aluminum-oxygen compound layer 30 on the phosphate compound layer 20 while dissolving a portion of the phosphate compound layer 20 .
- the surface-treated steel sheet 1 of the present embodiment may be used as, but not particularly limited to, a member such as a can container or can lid, for example.
- the surface-treated steel sheet 1 may be used as is (used in applications requiring no coating, in which no coating layer is formed on the surface) to be shaped into a non-coated can container or can lid.
- the steel sheet 1 may also be shaped into a can container or can lid, after a coating layer 40 foamed of an organic material is formed on the aluminum-oxygen compound layer 30 of the surface-treated steel sheet 1 .
- the tin-plated steel sheet 10 which is to be the base material of the surface-treated steel sheet 1 of the present invention, can be obtained by tin-plating the steel sheet 11 to form a tin-plating layer 12 on the steel sheet 11 .
- the steel sheet 11 to be tin-plated may be any steel sheet having excellent drawing formability, drawing and ironing formability, and formability in drawing and thin redrawing (DTR).
- a hot-rolled steel sheet such as one based on an aluminum-killed steel continuously cast material and a cold-rolled steel sheet obtained by cold-rolling such a hot-rolled steel sheet.
- a steel sheet can be used whose corrosion resistance is improved by forming a nickel-plating layer on the steel sheet, heating the resulting steel sheet for thermal diffusion, and forming a nickel-iron alloy layer between the steel sheet and the nickel-plating layer.
- the adhesion of the coating layer can be increased by an anchoring effect.
- the method for tin-plating the steel sheet 11 is not particularly limited, and examples thereof include methods using a known plating bath such as a ferrostan bath, a halogen bath, and a sulfuric acid bath.
- the method for nickel-plating is also not particularly limited, and a known Watt bath including nickel sulfate and nickel chloride can be used.
- a bath composition including nickel sulfate and ammonium sulfate is preferably used.
- a tin-iron alloy layer may be formed between the steel sheet 11 and the tin-plating layer 12 by conducting treatment of heating the tin-plated steel sheet to a temperature equal to or higher than the melting temperature of tin followed by rapid cooling (reflow treatment).
- the tin-plated steel sheet 10 obtained by being subjected to this reflow treatment will be one in which the tin-iron alloy layer and the tin-plating layer 12 are formed on the steel sheet 11 in this order, resulting in improved corrosion resistance.
- tin-nickel and tin-nickel-iron alloys may be formed between the steel sheet 11 and the tin-plating layer 12 by this reflow treatment.
- An unduly large amount of the oxide film layer formed of SnO x tends to reduce the adhesion of the phosphate compound layer 20 formed on the tin-plated steel sheet 10 .
- an unduly small amount of the oxide film layer tends to easily cause sulfide blackening of the tin-plated steel sheet 10 .
- the amount of the oxide film layer is desirably adjusted appropriately.
- treatment to adjust the amount of the oxide film layer by removing a part or all of the oxide film layer on the surface may be conducted on the tin-plated steel sheet 10 .
- treatment to remove the oxide film layer on the surface of the tin-plated steel sheet 10 may be conducted on the tin-plated steel sheet 10 by conducting at least one of cathode electrolytic treatment or anode electrolytic treatment under conditions of a current density of 0.5 to 20 A/dm 2 and an energizing time of 0.1 to 1.0 seconds using a carbonate alkaline solution such as sodium carbonate and sodium hydrogen carbonate.
- the oxide film layer may be removed also using an acidic aqueous solution such as hydrochloric acid.
- the immersion time of the tin-plated steel sheet 10 in an acidic aqueous solution is preferably 2 seconds or less.
- An immersion time of the tin-plated steel sheet 10 in an acidic aqueous solution within the above range allows efficient removal of the oxide film layer formed of SnO x while reducing dissolution of the metal tin portion of the tin-plating layer 12 .
- the thickness of the tin-plating layer 12 formed on the steel sheet 11 is not particularly limited.
- the thickness may be selected appropriately depending on the intended usage of the surface-treated steel sheet 1 to be produced, and is preferably 1.0 g/m 2 or more, more preferably 1.0 to 15 g/m 2 in terms of tin.
- the thickness of the nickel-plating layer is not particularly limited.
- the thickness of the nickel-plating layer is preferably 0.01 to 15 g/m 2 in terms of nickel.
- the average particle size of the granular nickel is preferably 0.01 to 0.7 ⁇ m.
- the total thickness of the tin-plated steel sheet 10 is not particularly limited.
- the thickness may be selected appropriately depending on the intended usage of the surface-treated steel sheet 1 to be produced, and is preferably 0.07 to 0.4 mm.
- the phosphate compound layer 20 which is a layer containing tin phosphate, is formed by immersing the tin-plated steel sheet 10 in an electrolytic treatment liquid containing phosphate ions and conducting cathode electrolytic treatment using the tin-plated steel sheet 10 as the cathode.
- tin-plated steel sheet 10 immersed in an electrolytic treatment liquid containing phosphate ions when the tin-plated steel sheet 10 immersed in an electrolytic treatment liquid containing phosphate ions is energized as the cathode side, tin dissolves from the tin-plated steel sheet 10 to generate divalent tin ions (Sn 2+ ) as shown in the left figure in FIG. 2 .
- FIG. 2 is a schematic view illustrating a process of forming a phosphate compound layer 20 and an aluminum-oxygen compound layer 30 being formed on a tin-plated steel sheet 10 .
- the left figure in FIG. 2 illustrates a state in which the tin-plating layer 12 of the tin-plated steel sheet 10 is subjected to cathode electrolytic treatment using an electrolytic treatment liquid containing phosphate ions.
- the middle figure in FIG. 2 illustrates a state in which Sn 3 (PO 4 ) 2 formed as the phosphate compound layer 20 is subjected to cathode electrolytic treatment for forming the aluminum-oxygen compound layer 30 .
- FIG. 2 illustrates a state in which Sn 3 (PO 4 ) 2 and AlPO 4 as the phosphate compound layer 20 and AlPO 4 , Al 2 O 3 .nH 2 O, and Al(OH) 3 as the aluminum-oxygen compound layer 30 are formed on the tin-plated steel sheet 10 .
- AlPO 4 is contained in both the phosphate compound layer 20 and the aluminum-oxygen compound layer 30 .
- the tin ions Sn 2+ generated from the tin-plated steel sheet 10 react with phosphate ions PO 4 3 ⁇ in the electrolytic treatment liquid to be deposited on the tin-plated steel sheet 10 as tin phosphate such as Sn 3 (PO 4 ) 2 .
- the tin ions Sn 2+ generated from the tin-plated steel sheet 10 are deposited on the tin-plated steel sheet 10 also as tin oxide (SnO x ).
- Phosphates in the aqueous solution are known to have changes in the ionization equilibrium among dihydrogen phosphate ions (H 2 PO 4 ⁇ ), hydrogen phosphate ions (HPO 4 2 ⁇ ), and phosphate ions (PO 4 3 ⁇ ) depending on the pH of the aqueous solution. As the pH of the aqueous solution becomes lower, the ionization equilibrium moves towards the side where the abundance ratio of dihydrogen phosphate ions H 2 PO 4 ⁇ is high.
- tin-plated steel sheet 10 when the tin-plated steel sheet 10 is subjected to cathode electrolytic treatment with an electrolytic treatment liquid containing phosphate ions, tin oxide formed on the surface of the tin-plating layer 12 is reduced, and at the same time, hydroxide ions (OH ⁇ ) are generated as shown in the left figure in FIG. 2 . It is presumed that this brings the pH into the range where the abundance ratio of hydrogen phosphate ions becomes higher and that these hydrogen phosphate ions react with tin ions to form tin phosphate such as Sn 3 (PO 4 ) 2 .
- the tin phosphate partly dissolves to form aluminum phosphate when the aluminum-oxygen compound layer 30 is formed by means of electrolytic treatment, as described later.
- the tin-plated steel sheet 10 when the phosphate compound layer 20 is formed, the tin-plated steel sheet 10 may be subjected to anode electrolytic treatment using an electrolytic treatment liquid containing phosphate ions before the cathode electrolytic treatment aforementioned is conducted.
- the oxide film layer formed on the surface of the tin-plated steel sheet 10 is moderately removed by anode electrolytic treatment, and thereafter, the anode electrolytic treatment allows the tin-plating layer 12 of the tin-plated steel sheet 10 to dissolve easily. This facilitates formation of the phosphate compound layer 20 .
- This anode electrolytic treatment is preferably conducted as follows: the tin-plated steel sheet 10 is immersed in an electrolytic treatment liquid and subjected to anode electrolytic treatment; and thereafter, while the tin-plated steel sheet 10 remains immersed in the electrolytic treatment liquid, the polarities of the anode and cathode are reversed in the energization control circuit, followed by conducting the cathode electrolytic treatment aforementioned. This facilitates control of the solution and also improves the working efficiency when anode electrolytic treatment and cathode electrolytic treatment are conducted.
- the coating layer 40 on the surface-treated steel sheet 1 has excellent adhesion due to the formation of phosphate compound layer 20 containing tin phosphate by the cathode electrolytic treatment aforementioned.
- the coating layer 40 is formed by baking coating or the like, an oxide film layer covering the tin-plating layer 12 of the surface-treated steel sheet 1 grows due to the heat from baking, and this growth may cause the aluminum-oxygen compound layer 30 and the coating layer 40 to delaminate from this oxide film layer.
- the surface-treated steel sheet 1 to be obtained will have improved corrosion resistance.
- the present inventors have found that the tin-plated steel sheet 10 is subjected to cathode electrolytic treatment to cause hydrogen phosphate ions to react with tin ions to thereby form tin phosphate as aforementioned and that, accordingly, the chemical bonding state and surface morphology of the tin phosphate formed by these hydrogen phosphate ions makes the tin phosphate difficult to dissolve in an electrolytic treatment liquid used when the aluminum-oxygen compound layer 30 described later is formed by means of electrolytic treatment.
- the corrosion resistance of the surface-treated steel sheet 1 to be obtained can be improved.
- the surface-treated steel sheet 1 to be obtained accordingly will have sufficient corrosion resistance even when the coating layer 40 mainly formed of an organic material is not formed on its surface and thus can be suitably used for a metal container including no coating layer 40 in applications requiring no coating.
- the tin-plating layer 12 of the tin-plated steel sheet 10 partly dissolves to form the phosphate compound layer 20 and this phosphate compound layer 20 partly dissolves to form the aluminum-oxygen compound layer 30 , as aforementioned.
- the tin-plating layer 12 , the phosphate compound layer 20 , and the aluminum-oxygen compound layer 30 are structured such that they are intermixed with one another near each boundary.
- both the phosphate compound layer 20 and the aluminum-oxygen compound layer 30 may contain tin phosphate and aluminum phosphate.
- FIG. 6 is a cross-sectional photograph and the result of quantitative analysis by means of energy dispersive X-ray spectrometry (EDS) at each point of the phosphate compound layer 20 and the aluminum-oxygen compound layer 30 of the surface-treated steel sheet obtained in Example of the present invention.
- EDS energy dispersive X-ray spectrometry
- phosphoric acid H 3 PO 4
- sodium dihydrogen phosphate NaH 2 PO 4
- disodium hydrogen phosphate Na 2 HPO 4
- phosphorous acid H 3 PO 3
- phosphoric acid and phosphates may be used singly or in admixture.
- a mixture of phosphoric acid and sodium dihydrogen phosphate which enables tin phosphate to deposit satisfactorily as the phosphate compound layer 20 , is suitable.
- the concentration of the phosphate ions in the electrolytic treatment liquid is not particularly limited and is preferably 5 to 200 g/L in terms of phosphorus. A concentration of the phosphate ions in the electrolytic treatment liquid within the above range enables tin phosphate to deposit satisfactorily on the tin-plated steel sheet 10 .
- the pH of the electrolytic treatment liquid is not particularly limited and is preferably 1 to 7. With a pH of less than 1, the tin phosphate formed tends to dissolve. In contrast, with a pH of more than 7, the oxide film layer on the surface of the tin-plated steel sheet 10 insufficiently dissolves, which makes it difficult to form the phosphate compound layer 20 on a portion in which the oxide film layer is much remaining, and thus it may be impossible to form the homogeneous phosphate compound layer 20 on the tin-plated steel sheet 10 .
- the current density when the anode electrolytic treatment or cathode electrolytic treatment aforementioned is conducted is not particularly limited and is preferably 1 to 30 A/dm 2 . A current density within the above range enables satisfactory formation of the phosphate compound layer 20 on the tin-plated steel sheet 10 .
- a counter electrode plate placed opposite to the tin-plated steel sheet 10 may be any counter electrode plate that does not dissolve in the electrolytic treatment liquid while the electrolytic treatment is conducted. Because of difficulty to dissolve in the electrolytic treatment liquid, a titanium plate coated with iridium oxide or a titanium plate coated with platinum is preferable.
- the energizing time when anode electrolytic treatment or cathode electrolytic treatment is conducted is not particularly limited and is preferably 0.15 to 3.0 seconds, more preferably 0.15 to 1.0 seconds.
- the energizing time of cathode electrolytic treatment is preferably is equivalent to the energizing time of anode electrolytic treatment.
- the number of cycles of the energizing time and stop of energization when anode electrolytic treatment or anode electrolysis after cathode electrolytic treatment is conducted is preferably 1 to 10. The number of cycles may be adjusted together with the energizing time so as to achieve an appropriate phosphorous content in the phosphate compound layer 20 .
- the appropriate phosphorous content in the phosphate compound layer 20 is preferably 0.5 to 20 mg/m 2 , more preferably 0.5 to 5.0 mg/m 2 , particularly preferably 0.7 to 4.0 mg/m 2 .
- the tin-plated steel sheet 10 including the phosphate compound layer 20 formed thereon is washed with water as appropriate and subsequently subjected to electrolytic treatment in an electrolytic treatment liquid containing Al ions to allow an aluminum-oxygen compound to deposit on the phosphate compound layer 20 to thereby form the aluminum-oxygen compound layer 30 .
- the electrolytic treatment method may be either anode electrolytic treatment or cathode electrolytic treatment. Cathode electrolytic treatment is preferable, in view of capable of satisfactorily forming the aluminum-oxygen compound layer 30 .
- the content of the Al ion in the electrolytic treatment liquid for forming the aluminum-oxygen compound layer 30 can be appropriately selected depending on the amount of the film of the aluminum-oxygen compound layer 30 and is preferably 0.5 to 10 g/L, more preferably 1 to 5 g/L in terms of the mass concentration of the Al atom.
- a content of the Al ion in the electrolytic treatment liquid within the above range can improve the stability of the electrolytic treatment liquid and also improve the deposition efficiency of the aluminum-oxygen compound.
- nitrate ions may be added to the electrolytic treatment liquid used for forming the aluminum-oxygen compound layer 30 .
- the content of the nitrate ion in the electrolytic treatment liquid is preferably 11,500 to 25,000 ppm by weight.
- a content of the nitrate ion within the above range in the electrolytic treatment liquid enables adjustment of the electrical conductivity within a suitable range.
- the electrolytic treatment liquid used for forming the aluminum-oxygen compound layer 30 is preferably free of F ions.
- the electrolytic treatment liquid used for forming the aluminum-oxygen compound layer 30 is free of F ions, the aluminum-oxygen compound layer 30 having a small particle size and being dense can be formed, and thus, the corrosion resistance of the surface-treated steel sheet 1 to be obtained can be improved. If F ions are contained in the electrolytic treatment liquid, they cause formation of SnF 2 , which is then captured in the aluminum-oxygen compound layer 30 to thereby reduce the sulfide blackening resistance and corrosion resistance.
- the electrolytic treatment liquid may be any electrolytic treatment liquid containing substantially no F ion, or may contain F ions in an amount of an impurity level approximately.
- F atoms are included at a very low level in industrial water, and thus, F ions derived from such F atoms may be included in the electrolytic treatment liquid.
- the F ions are present in a form of F ions forming complex ions with metal, free F ions, and the like, in the electrolytic treatment liquid.
- the total amount of these F ions is preferably 50 ppm by weight or less, more preferably 20 ppm by weight or less, more preferably 5 ppm by weight or less, it can be determined that the amount of F ions contained in the electrolytic treatment liquid is approximately an impurity level, i.e., that the electrolytic treatment liquid contains substantially no F ion.
- the method to measure the content of F ions and nitrate ions in the electrolytic treatment liquid for example, a method of measurement by quantitative analysis using an ion chromatography can be used.
- the electrolytic treatment liquid for forming the aluminum-oxygen compound layer 30 at least one or more of additives selected from organic acids (citric acid, lactic acid, tartaric acid, glycolic acid and the like), polyacrylic acid, polyitaconic acid, phenol resin and the like may be added.
- organic acids citric acid, lactic acid, tartaric acid, glycolic acid and the like
- polyacrylic acid polyitaconic acid
- phenol resin and the like may be added to the electrolytic treatment liquid for .
- appropriately adding one of these additives singly or two or more of these in combination to this electrolytic treatment liquid enables the aluminum-oxygen compound layer 30 to be formed to contain an organic material. This can improve the adhesion of the coating layer 40 to be formed on the aluminum-oxygen compound layer 30 .
- the content of the phosphate ion in the electrolytic treatment liquid for forming the aluminum-oxygen compound layer 30 is desirably adjusted.
- the content of phosphate ion in the electrolytic treatment liquid is preferably 0.55 g/L or less, more preferably 0.33 g/L or less, more preferably 0.11 g/L in terms of phosphorus.
- the aluminum-oxygen compound layer 30 when the aluminum-oxygen compound layer 30 is formed by means of electrolytic treatment, tin phosphate and the like dissolve from the phosphate compound layer 20 into the electrolytic treatment liquid used for forming the aluminum-oxygen compound layer 30 , and phosphate ions are generated. With an unduly large amount of the phosphate ions, the phosphate ions bind to Al ions to precipitate as aluminum phosphate in the electrolytic treatment liquid. This leads to decrease in the amount of Al ions in the electrolytic treatment liquid used for forming the aluminum-oxygen compound layer 30 to thereby reduce the efficiency of forming the aluminum-oxygen compound layer 30 . Moreover, the aluminum-oxygen compound layer 30 to be formed by precipitation of aluminum phosphate in the electrolytic treatment liquid becomes inhomogeneous and exhibits spots, which tend to reduce the quality of appearance although without any quality problems.
- a content of phosphate ions in the electrolytic treatment liquid for forming the aluminum-oxygen compound layer 30 within the above range makes the aluminum-oxygen compound layer 30 to be formed homogeneous and improves the quality of appearance of the surface-treated steel sheet 1 to be obtained.
- the total energization time for the base material (the total energization time when the cycle of energization and stop of energization is repeated for several times) is preferably 1.5 seconds or less, more preferably 1 second or less.
- the number of cycles of energization and stop of energization is preferably 1 to 10 and may be adjusted together with the energizing time so as to achieve an appropriate content of aluminum in the aluminum-oxygen compound layer 30 .
- the appropriate content of aluminum in the aluminum-oxygen compound layer 30 is preferably 3 to 40 mg/m 2 , more preferably 5 to 15 mg/m 2 , particularly preferably 5.1 to 10.6 mg/m 2 .
- a counter electrode plate placed opposite to the base material may be any counter electrode plate that does not dissolve in the electrolytic treatment liquid while the electrolytic treatment is conducted.
- a titanium plate coated with iridium oxide or a titanium plate coated with platinum is preferable.
- the aluminum-oxygen compound layer 30 formed as described above is mainly formed of aluminum oxide and the like and also contains aluminum hydroxide and phosphates.
- Example of the phosphate include aluminum phosphate and oxygen compounds containing phosphoric acid (such as Al(PO 4 ) y O z ). This phosphate precipitates as the aluminum-oxygen compound layer 30 as follows.
- the tin-plated steel sheet 10 including the phosphate compound layer 20 formed thereon is subjected to electrolytic treatment with an electrolytic treatment liquid containing Al ions, as aforementioned, a portion of tin phosphate forming the phosphate compound layer 20 dissolves, and phosphate ions generated by this dissolution cause phosphates such as aluminum phosphate and oxygen compounds containing phosphoric acid to precipitate. Furthermore, in formation of the aluminum-oxygen compound layer 30 , dissolution of the phosphate compound layer 20 or dissolution of a portion which is not coated the phosphate compound and thus from which tin plating is exposed leads to production of tin ions Sn 2+ in the electrolytic treatment liquid.
- tin oxide SnO x
- allowing the aluminum-oxygen compound layer 30 to contain phosphate can reduce growth of the oxide film layer of the tin-plated steel sheet 10 due to the heat from baking when the coating layer 40 is formed on the aluminum-oxygen compound layer 30 by baking coating.
- the adhesion of the coating layer 40 to be formed on the surface-treated steel sheet 1 can be improved.
- the adhesion of the coating layer 40 to be formed on the surface-treated steel sheet 1 is improved.
- the tin phosphate coating film deteriorates over time; therefore, though increase in oxide film in the coating and baking steps can be reduced in the initial stage, the coating film gradually becomes fragile; and thus, the adhesion to the coating layer 40 is reduced.
- the ratio of the integration value of the profile derived from tin oxide to the integration value of the profile derived from tin phosphate (a value obtained by integrating the spectrum intensity by the binding energy) (tin oxide/tin phosphate) is 6.9 or more.
- the peak of the profile derived from tin phosphate is observed at around 489.0 eV and the peak of the profile derived from tin oxide is observed at around 487.5 eV. The peak at around 485.0 eV seems to be derived from metal tin.
- FIG. 3 herein is a graph showing a spectrum obtained by measuring the aluminum-oxygen compound layer 30 of the surface-treated steel sheet 1 of Example 6 described later by an X-ray photoelectron spectroscopy.
- the vertical axis represents the spectrum intensity and the horizontal axis represents the binding energy (eV).
- setting the ratio of tin oxide/tin phosphate aforementioned within the above range allows the surface-treated steel sheet 1 to be obtained to have excellent corrosion resistance as well as to have excellent adhesion of the coating layer 40 to be formed on the surface.
- the content of aluminum in the aluminum-oxygen compound layer 30 is preferably form 5 to 15 mg/m 2 , more preferably 5.1 to 10.6 mg/m 2 .
- An unduly low content of aluminum in the aluminum-oxygen compound layer 30 leads to increase in the oxide film layer on the surface of the tin-plated steel sheet 10 when the coating layer 40 formed of an organic material is formed by baking coating.
- the aluminum-oxygen compound layer 30 and the coating layer 40 tend to easily delaminate from the oxide film layer.
- an unduly high content of aluminum in the aluminum-oxygen compound layer 30 may make the aluminum-oxygen compound layer 30 brittle to lead to cohesive failure.
- the aluminum-oxygen compound layer 30 contain phosphate as aforementioned.
- the content ratio of the amount of phosphorus (mol/m 2 ) to the amount of aluminum (mol/m 2 ) in the aluminum-oxygen compound layer 30 (P/Al) is preferably 0.06 to 0.35, more preferably 0.07 to 0.27.
- the oxide film layer on the surface of the tin-plated steel sheet 10 grows due to the heat from baking when the coating layer 40 formed of an organic material is formed by baking coating.
- the aluminum-oxygen compound layer 30 and the coating layer 40 tend to easily delaminate from the oxide film layer.
- the above content ratio (P/Al) is more than 0.35, the aluminum-oxygen compound layer 30 to be formed becomes inhomogeneous and exhibits spots, which tend to reduce the quality of appearance although without any quality problems.
- the surface-treated steel sheet 1 of the present embodiment is obtained in the above manner.
- the total amount of phosphorus contained in each of layers to be formed on the steel sheet 11 is preferably 0.5 to 10 mg/m 2 , more preferably 0.7 to 2.5 mg/m 2 .
- the oxide film layer on the tin-plated steel sheet 10 grows due to the heat from baking when the coating layer 40 formed of an organic material is formed by baking coating.
- the aluminum-oxygen compound layer 30 and the coating layer 40 tend to easily delaminate from the oxide film layer.
- an example of the method for measuring the total amount of phosphorus contained in each of layers formed on the steel sheet 11 include a method involving quantitatively analyzing the surface-treated steel sheet 1 using an X-ray fluorescence spectrometer.
- the surface-treated steel sheet 1 of the present embodiment may be used as, but not particularly limited to, a member such as a can container or can lid.
- the surface-treated steel sheet 1 may be used as is (used in applications requiring no coating, in which no coating layer 40 is formed on the surface) to be shaped into a non-coated can container or can lid.
- a coating layer 40 formed of an organic material is formed on the aluminum-oxygen compound layer 30 of the surface-treated steel sheet 1
- the steel sheet 1 may be shaped into a can container or can lid.
- the organic material forming the coating layer 40 is not particularly limited and may be selected appropriately depending on the usage of the surface-treated steel sheet 1 (for example, a usage of can containers to be filled with a specific content). Examples thereof include thermoplastic resins and thermoset resins.
- thermoplastic resin olefinic resin films such as polyethylene, polypropylene, ethylene-propylene copolymers, ethylene-vinyl acetate copolymers, ethylene-acryl ester copolymers, and ionomers, polyester films such as polyethylene terephthalate and polybutylene terephthalate, unstretched film or biaxially oriented films such as polyvinyl chloride films and polyvinylidene chloride films, or polyamide films such as nylon 6, nylon 6,6, nylon 11, and nylon 12 or the like can be used.
- unoriented polyethylene terephthalate prepared by copolymerizing with isophtalic acid is particularly preferable.
- such an organic material for forming the coating layer 40 may be used singly or may be blended with a different organic material.
- thermoset resin epoxy-phenol resins, polyester resins or the like can be used.
- the layer may be a single resin layer or may be a multi-layered resin layer prepared by coextrusion or the like.
- a multi-layered polyester resin layer is advantageous for the following reason: a polyester resin having a composition excellent in the adhesion property can be selected as the material of an underlying layer located at the side of the surface-treated steel sheet 1 , and a polyester resin of a composition excellent in the resistance to the contents of cans, i.e., resistance to extraction and non-adsorptive property for flavor constituents, can be selected as the material for a surface layer.
- Examples of the multi-layered polyester resin layer include, indicated as surface layer/lower layer, polyethylene terephthalate/polyethylene terephthalate.isophthalate, polyethylene terephthalate/poly ethylene.cyclohexylene dimethylene.terephthalate, polyethylene terephthalate.isophthalate having a low isophthalate content/polyethylene terephthalate.isophthalate having a high isophthalate content, and polyethylene terephthalate.isophthalate/[blended product of polyethylene terephthalate.isophthalate and polybuthylene terephthalate.adipate], of course, without limited to limitation to the above examples.
- the thickness ratio of surface layer:lower layer is desirably in the range of 5:95 to 95:5.
- compounding agents for resins known per se for example, an antiblocking agent such as amorphous silica, an inorganic filler, various antistatic agents, a slip agent, an antioxidant (such as tocopherol), an ultraviolet absorbent and the like can be compounded in accordance with known formulations.
- an antiblocking agent such as amorphous silica, an inorganic filler, various antistatic agents, a slip agent, an antioxidant (such as tocopherol), an ultraviolet absorbent and the like can be compounded in accordance with known formulations.
- the thickness of the coating layer 40 to be formed on the surface-treated steel sheet 1 obtained by the present invention be generally in the range of 3 to 50 ⁇ m, particularly of 5 to 40 ⁇ m in the case of thermoplastic resin coating.
- the thickness after backing be in the range of 1 to 50 ⁇ m, particularly of 3 to 30 ⁇ m. If the thickness is below the above range, the corrosion resistance will be insufficient, while if the thickness is above the above range, problems in formability may arise.
- Thermal bonding of a polyester resin to the surface-treated steel sheet 1 is conducted using the quantity of heat held by the molten-resin layer and the quantity of heat held by the surface-treated steel sheet 1 .
- the heating temperature of the surface-treated steel sheet 1 is appropriately 90° C. to 290° C. in general, particularly 100° C. to 230° C., whereas the temperature of the laminating rolls is appropriately in the range of 10° C. to 150° C.
- the coating layer 40 to be formed on the surface-treated steel sheet 1 can be also formed by thermally bonding a polyester resin film made in advance with the T-die method or inflation film-formation method to the surface-treated steel sheet 1 .
- a polyester resin film made in advance with the T-die method or inflation film-formation method
- an unstretched film prepared with the cast molding method in which the extruded film is immediately cooled can also be used.
- a biaxially-stretched film obtained by biaxially stretching this film at a stretching temperature, either subsequently or simultaneously, and thermally fixing the film after stretching can also be used.
- the coating layer 40 is formed to obtain an organic material-coated steel sheet, which then can be processed and shaped into a can container.
- the can container include, but not particularly limited to, a seamless can 5 (two-piece can) shown in FIG. 4(A) and a three-piece can 5 a (welded can) shown in FIG. 4(B) .
- a body 51 and an upper lid 52 constituting the seamless can 5 and a body 51 a, an upper lid 52 a, and a lower lid 53 constituting the three-piece can 5 a are all formed using the organic material-coated steel sheet obtained by forming the coating layer 40 on the surface-treated steel sheet 1 of the present embodiment.
- the cross-sectional views of the seamless can 5 and the three-piece can 5 a are views obtained by rotating FIG. 1 above by 90° such that the coating layer 40 is located inside the can.
- the cans 5 and 5 a respectively shown in FIGS. 4(A) and 4(B) may be produced such that the coating layer 40 is located inside the can by any conventionally known means, such as drawing process, drawing/redrawing process, stretching process via drawing/redrawing, stretching/ironing process via drawing/redrawing, or drawing/ironing process.
- the seamless can 5 which is subjected to a highly sophisticated process, such as stretching process via drawing/redrawing and stretching/ironing process via drawing/redrawing, preferably has the coating layer 40 formed of thermoplastic resin coating by an extrusion coating method.
- the organic material-coated steel sheet having excellent processing adhesion, has excellent coating adhesion even when subjected to severe processing, and is capable of provide a seamless can having excellent corrosion resistance.
- the coating layer 40 is formed to obtain an organic material-coated steel sheet as aforementioned, which then can be processed and produced into a can lid.
- the can lid include, but not particularly limited to, flat lids, stay-on-tub type easy-open can lids, and pull-open type easy-open can lids.
- an electrolytic treatment liquid the phosphate ion concentration or Al ion concentration was measured using an ICP emission spectrometer (manufactured by SHIMADZU CORPORATION, ICPE-9000), and the F ion concentration and nitrate ion concentration were measured with an ion chromatograph (manufactured by Dionex Corporation, DX-500).
- the pH of the above electrolytic treatment liquid was also measured using a pH meter (manufactured by HORIBA, Ltd.).
- the amount of phosphorus and the amount of aluminum contained in each of the layers on the steel sheet 11 were measured in the unit of mg/m 2 using an X-ray fluorescence spectrometer (manufactured by Rigaku Corporation, ZSX100e).
- the content ratio of the amount of phosphorus (mol/m 2 ) to the amount of aluminum (mol/m 2 ) (P/Al) was calculated by converting the measurement values obtained into the unit of mol/m 2 .
- Measurement of the amount of phosphorus and the amount of aluminum and calculation of P/Al were conducted on all the Examples and Comparative Examples described later.
- the 3d 5/2 spectrum of tin was measured using an X-ray photoelectron spectroscopy under the following conditions to thereby determine the ratio of the integration value of the profile derived from tin oxide to the integration value of the profile derived from tin phosphate (tin oxide/tin phosphate) in the aluminum-oxygen compound layer 30 .
- Measurement of the tin compound in the aluminum-oxygen compound layer 30 and calculation of the above ratio (tin oxide/tin phosphate) were conducted only on Examples 6 described later.
- Measurement apparatus JPS-9200 manufactured by JEOL Ltd.
- Photoelectron take-off angle 90° (0° with respect to the normal of the sample)
- Waveform separation conditions binding energy of tin oxide 487.5 eV, binding energy of tin phosphate 489.1 eV, and binding energy of metal tin 485.4 eV
- the surface-treated steel sheet 1 was subjected to carbon vapor deposition, and then further deposited with carbon to a thickness of about 1 ⁇ m in an FIB apparatus.
- a sample was cut out by a microsampling method and fixed on a copper support. Thereafter, a cross-sectional TEM specimen was prepared by FIB processing and quantitatively analyzed by conducting TEM observation and EDS analysis on each point.
- the organic material-coated steel sheet obtained by forming the coating layer 40 on the surface-treated steel sheet 1 was subjected to retort treatment at a temperature of 125° C. for 30 minutes.
- a grid having a spacing of 5 mm and a depth reaching the steel sheet 11 was formed on the steel sheet, and the coating layer was peeled off with tape. The degree of peeling was visually observed and evaluated based on the following criteria.
- Score 2 As a determination result of visual observation, peeling of the coating was observed at an area ratio of 1/5 or less.
- Score 1 As a determination result of visual observation, peeling of the coating was observed at an area ratio of more than 1/5.
- the surface-treated steel sheet 1 had sufficient coating adhesion for applications of cans for food and beverages.
- the surface-treated steel sheet 1 was thermally treated at a temperature of 205° C. for 30 minutes.
- the amount of the oxide film layer of tin formed on the surface of tin-plated steel sheet 10 was determined both before and after the thermal treatment.
- the amount of electricity required to remove the oxide film layer by electrochemical reduction was taken as the amount of the oxide film layer was determined.
- a 1/1000 N hydrogen bromide solution was used as the electrolytic liquid, and electrolysis was conducted under a condition of a current density of 25 ⁇ A/cm 2 .
- Growth of the oxide film layer was evaluated by a value obtained by dividing the amount of the oxide film layer after the thermal treatment by the amount of the oxide film layer before the thermal treatment (oxide film layer after the thermal treatment/oxide film layer before the thermal treatment). It was considered that the oxide film layer is likely to grow by the thermal treatment as the value is larger. Evaluation of growth of the oxide film layer was carried out on all the Examples and Comparative Examples described later.
- Oxide film layer after thermal treatment/oxide film layer before thermal treatment was 1.2 or less.
- Oxide film layer after thermal treatment/oxide film layer before thermal treatment was more than 1.2 and 1.4 or less.
- Test pieces were prepared by cutting the organic material-coated steel sheet obtained by forming the coating layer 40 on the surface-treated steel sheet 1 into 40-mm square pieces and protecting the cut face with 3-mm wide tape. Subsequently, a crosscut scratch having a depth reaching the steel sheet was made on the test piece prepared using a cutter. The test piece was subjected to 3 mm bulging process by an Erichsen tester (manufactured by Coating Tester Co., Ltd.) such that the intersection of the crosscut would be the apex of the bulging-processed portion. Then, the test piece bulging-processed was placed in a sealed container. After the container was filled with the following model solution and stored under an environment of 90° C. for 24 hours.
- Model solution an aqueous solution containing NaCl and citric acid each dissolved at 1.5% by weight
- Test pieces were prepared by cutting the surface-treated steel sheet 1 into a disc having a diameter of 49 mm and protecting the cut face with 3-mm wide tape. The amount of Sn in the test pieces prepared was measured with X-ray fluorescence. Then, the test piece was placed in a sealable container. After the container was filled with the following model solution and stored under an environment of 37° C. for 10 days.
- Model solution an aqueous solution containing 1% by weight of acetic acid and 10% by weight of sucrose dissolved
- the sealed container was opened.
- the amount of Sn in the test piece after storage under an environment of 37° C. for 10 days was measured with X-ray fluorescence, and the % of the amount of Sn remaining was calculated using the following formula.
- Amount of Sn remaining (%) (Amount of Sn before the lapse of the time ⁇ Amount of Sn after the lapse of the time)/Amount of Sn before the lapse of the time ⁇ 100
- a low carbon cold-rolled sheet (thickness: 0.225 mm) was provided as a steel sheet 11 .
- the steel sheet provided was degreased by subjecting the steel sheet to cathode electrolytic treatment using an aqueous solution of an alkaline degreasing agent (manufactured by Nippon Quaker Chemical, Ltd., Formula 618-TK2) under conditions of 60° C. and 10 seconds.
- an alkaline degreasing agent manufactured by Nippon Quaker Chemical, Ltd., Formula 618-TK2
- the steel sheet degreased was acid pickled by immersion in an acid pickling agent (an aqueous solution of 5% by volume of sulfuric acid) at normal temperature for five seconds.
- the steel sheet was washed with tap water and subjected to tin plating using a known ferrostan bath under the following conditions to form a tin-plating layer 12 having an amount of tin of 2.8 g/m 2 on the surface of the steel sheet.
- the steel sheet including the tin-plating layer 12 formed was washed with water and made to generate heat by supplying a direct current thereto.
- the steel sheet was subjected to reflow treatment, in which the steel sheet was heated to a temperature equal to or higher than the melting temperature of tin and then rapidly cooled by sprinkling tap water thereon, to thereby prepare a tin-plated steel sheet 10 .
- Anode material commercially available 99.999% metal tin
- Total energizing time 5 seconds (number of cycles: 5, when one cycle included energizing time of 1 second and stop time of 0.5 seconds)
- the tin-plated steel sheet 10 obtained was immersed in an electrolytic treatment liquid with stirring and subjected to anode electrolytic treatment under the following conditions using an iridium oxide-coated titanium plate positioned at an interelectrode distance of 17 mm as the cathode to thereby form a phosphate compound layer 20 on the tin-plated steel sheet 10 .
- Electrolytic treatment liquid an aqueous solution having a pH of 1.3 containing phosphorous acid dissolved at a concentration of 10 g/L (treatment liquid A in Table 1)
- Total energizing time 0.5 seconds (energizing time 0.5 seconds, number of cycles 1)
- the electrolytic treatment liquid used for forming the phosphate compound layer 20 was analyzed in accordance with the method aforementioned. The result is listed in Table 1. Table 1 also shows the concentration of phosphorous atoms (g/L) calculated depending on the concentration of the phosphate compound dissolved.
- the electrolytic treatment liquid shown as the treatment solution A in Table 1 was used for forming the phosphate compound layer 20 .
- a treatment liquid B was used in Examples 2 and 3 described later
- a treatment liquid C was used in Examples 4 to 6 and Comparative Example 2 described later.
- the conditions for the electrolytic treatment when the phosphate compound layer 20 was formed on the tin-plated steel sheet 10 are shown in Table 2.
- the tin-plated steel sheet 10 including the phosphate compound layer 20 formed thereon was washed with water. Then, the steel sheet 10 was immersed in an electrolytic treatment liquid and subjected to cathode electrolytic treatment with stirring under the following conditions using an iridium oxide-coated titanium plate positioned at an interelectrode distance of 17 mm as the anode to thereby form an aluminum-oxygen compound layer 30 . Thereafter, immediate water washing with flowing water and drying provided the surface-treated steel sheet 1 in which the phosphate compound layer 20 and the aluminum-oxygen compound layer 30 were formed on the tin-plated steel sheet 10 in this order.
- the electrolytic treatment liquid used for forming the aluminum-oxygen compound layer 30 was analyzed in accordance with the method aforementioned. The result is listed in Table 1. In all the Examples and Comparative Examples except Comparative Example 6, the electrolytic treatment liquid shown as the treatment liquid E in Table 1 was used for forming the aluminum-oxygen compound layer 30 . In addition, the conditions for the electrolytic treatment when the aluminum-oxygen compound layer 30 was formed are shown in Table 2.
- Electrolytic treatment liquid an aqueous solution having a pH of 3.0 containing aluminum nitrate dissolved as an Al compound and having an Al ion concentration of 1,500 ppm by weight, a nitrate ion concentration of 15,000 ppm by weight, and a F ion concentration of 0 ppm by weight (treatment liquid E in Table 1)
- the surface-treated steel sheet 1 obtained was subjected to measurement of the amount of phosphorus and the amount of aluminum in accordance with the method aforementioned. The result is listed in Table 3.
- the surface-treated steel sheet 1 and organic material-coated steel sheet were prepared and evaluated in the same manner as in Example 1 except that an aqueous solution having a pH of 1.8 containing phosphoric acid at a concentration of 30 g/L and disodium phosphate at a concentration of 30 g/L each dissolved (treatment liquid B in Table 1) was used as the electrolytic treatment liquid when the phosphate compound layer 20 was formed on the tin-plated steel sheet 10 .
- treatment liquid B in Table 1 treatment liquid having a pH of 1.8 containing phosphoric acid at a concentration of 30 g/L and disodium phosphate at a concentration of 30 g/L each dissolved
- the surface-treated steel sheet 1 and organic material-coated steel sheet were prepared and evaluated in the same manner as in Example 2 except that the energizing time of the electrolytic treatment was set to 0.3 seconds when the phosphate compound layer 20 was formed and the energizing time of the electrolytic treatment was set to 0.15 seconds when the aluminum-oxygen compound layer 30 was formed.
- the surface-treated steel sheet 1 and organic material-coated steel sheet were prepared and evaluated in the same manner as in Example 1 except that an aqueous solution having a pH of 2.4 containing phosphoric acid at a concentration of 10 g/L and sodium dihydrogen phosphate at a concentration of 30 g/L each dissolved (treatment liquid C in Table 1) was used as the electrolytic treatment liquid when the phosphate compound layer 20 was formed on the tin-plated steel sheet 10 and that the energizing time of the electrolytic treatment was set to 0.15 seconds when the aluminum-oxygen compound layer 30 was formed.
- treatment liquid C in Table 1 treatment liquid having a pH of 2.4 containing phosphoric acid at a concentration of 10 g/L and sodium dihydrogen phosphate at a concentration of 30 g/L each dissolved
- the surface-treated steel sheet 1 and organic material-coated steel sheet were prepared and evaluated in the same manner as in Example 4 except that the treatment liquid C in Table 1 was used as the electrolytic treatment liquid when the phosphate compound layer 20 was formed on the tin-plated steel sheet 10 .
- the result is listed in Table 3.
- Example 5 the tin compound in the aluminum-oxygen compound layer 30 was measured, and the spectrum obtained when the tin compound in the aluminum-oxygen compound layer 30 was measured using an X-ray photoelectron spectroscopy is shown in FIG. 5(A) .
- Example 6 Anode electrolytic treatment was conducted under the same conditions except that treatment in which only the polarities were reversed (anode electrolytic treatment) was conducted before the cathode electrolytic treatment aforementioned was conducted when the phosphate compound layer 20 was formed on the tin-plated steel sheet 10 . Except for this, the surface-treated steel sheet 1 and organic material-coated steel sheet were prepared and evaluated in the same manner as in Example 5. The result is listed in Table 3. As for Example 6, the tin compound in the aluminum-oxygen compound layer 30 was measured, and the spectrum obtained when the tin compound in the aluminum-oxygen compound layer 30 was measured using an X-ray photoelectron spectroscopy is shown in FIG. 5(B) , and the TEM image and quantitative analysis results obtained by cross-section observation of the surface-treated steel sheet are shown in FIG. 6 .
- the surface-treated steel sheet 1 and organic material-coated steel sheet were prepared and evaluated in the same manner as in Example 6 except that the current density of the electrolytic treatment when the phosphate compound layer 20 was formed on the tin-plated steel sheet 10 and the current density of the electrolytic treatment, energizing time, and number of cycles when the aluminum-oxygen compound layer 30 was formed were changed as listed in Table 2.
- a tin oxide film formed on the surface of the tin-plated steel sheet was removed by immersing the steel sheet in a hydrochloric acid aqueous solution. The result is listed in Table 3.
- a surface-treated steel sheet was obtained by forming the aluminum-oxygen compound layer 30 in the same manner as in Example 1 directly on the tin-plated steel sheet 10 prepared in Example 1 without forming the phosphate compound layer 20 . Subsequently, the coating adhesion evaluation, evaluation of growth of the oxide film layer, and corrosion resistance evaluation (model solution) were conducted on the surface-treated steel sheet obtained. The result is listed in Table 3.
- Examples 1 to 7 in which the tin-plated steel sheet 10 was subjected to cathode electrolytic treatment to form the phosphate compound layer 20 and the aluminum-oxygen compound layer 30 was formed on this phosphate compound layer 20 , were satisfactory in all of the results of the coating adhesion evaluation, evaluation of growth of the oxide film layer, and corrosion resistance evaluation (model solution), had excellent corrosion resistance and adhesion of the coating layer 40 , and were suitable for applications such as metal containers and the like used for a prolonged period.
- Comparative Example 1 in which the aluminum-oxygen compound layer 30 had not been formed, had unsatisfactory results of the evaluation of growth of the oxide film layer. Accordingly, it is presumed that adhesion of the coating layer 40 may decrease due to growth of the oxide film layer. Additionally, it was confirmed that Comparative Example 2, in which the aluminum-oxygen compound layer 30 was formed directly on the tin-plated steel sheet 10 without forming the phosphate compound layer 20 , had results of the coating adhesion evaluation and evaluation of growth of the oxide film layer both worse than those of Examples and had poor adhesion of the coating layer 40 .
- the surface-treated steel sheet 1 was prepared in the same manner as in Example 1 except that the total energizing time was set to 7.5 seconds and the amount of tin in the tin-plating layer 12 was set to 11.2 g/m 2 when tin-plating layer 12 was formed and that the conditions of the electrolytic treatment for forming the phosphate compound layer and of the electrolytic treatment for forming the aluminum-oxygen compound layer were as listed in Table 2.
- the detinning evaluation (model solution) was conducted on the surface-treated steel sheet 1 obtained in accordance with the method aforementioned. The result is listed in Table 4.
- the surface-treated steel sheet 1 was prepared in the same manner as in Example 1 except that the total energizing time was set to 7.5 seconds and the amount of tin in the tin-plating layer 12 was set to 11.2 g/m 2 when tin-plating layer 12 was formed and that the conditions of the electrolytic treatment for forming the aluminum-oxygen compound layer were as listed in Table 2 without forming the phosphate compound layer 20 .
- the detinning evaluation (model solution) was conducted on the surface-treated steel sheet obtained in the same manner as in Example 8. The result is listed in Table 4.
- the tin-plated steel sheet 10 was prepared with setting the total energizing time set to 7.5 seconds and the amount of tin in the tin-plating layer 12 set to 11.2 g/m 2 when tin-plating layer 12 is formed. Thereafter, chromium hydroxide was formed by electrolytic treatment on the surface of the tin-plated steel sheet 10 to prepare a surface-treated steel sheet. The detinning evaluation (model solution) was conducted on the surface-treated steel sheet obtained in the same manner as in Example 8. The result is listed in Table 4. Reference Example 1 corresponds to a product of currently commercially available surface-treated steel sheets.
- Example 4 the amount of Sn remaining of Example 8, in which the tin-plated steel sheet 10 was subjected to cathode electrolytic treatment to form the phosphate compound layer 20 and the aluminum-oxygen compound layer 30 was formed on this phosphate compound layer 20 , was equivalent to or more than that of Reference Example 1, which is an existing product, and more than that of Comparative Example 3, in which the aluminum-oxygen compound layer 30 was formed directly on the tin-plated steel sheet 10 without forming the phosphate compound layer 20 .
- the surface-treated steel sheet 1 of Example 8 obtained by forming only the phosphate compound layer 20 and the aluminum-oxygen compound layer 30 on the tin-plated steel sheet 10 , had a large amount of Sn remaining even in an uncoated state without the coating layer 40 provided, thus was excellent in corrosion resistance and sulfide blackening resistance, and suitable for applications for metal containers and the like used uncoated.
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Electrochemistry (AREA)
- Materials Engineering (AREA)
- Metallurgy (AREA)
- Organic Chemistry (AREA)
- Inorganic Chemistry (AREA)
- Other Surface Treatments For Metallic Materials (AREA)
- Chemical Treatment Of Metals (AREA)
- Electroplating Methods And Accessories (AREA)
- Laminated Bodies (AREA)
Applications Claiming Priority (3)
| Application Number | Priority Date | Filing Date | Title |
|---|---|---|---|
| JP2015012634 | 2015-01-26 | ||
| JP2015-012634 | 2015-01-26 | ||
| PCT/JP2015/085947 WO2016121276A1 (ja) | 2015-01-26 | 2015-12-24 | 表面処理鋼板、金属容器及び表面処理鋼板の製造方法 |
Related Parent Applications (1)
| Application Number | Title | Priority Date | Filing Date |
|---|---|---|---|
| PCT/JP2015/085947 A-371-Of-International WO2016121276A1 (ja) | 2015-01-26 | 2015-12-24 | 表面処理鋼板、金属容器及び表面処理鋼板の製造方法 |
Related Child Applications (1)
| Application Number | Title | Priority Date | Filing Date |
|---|---|---|---|
| US17/352,059 Division US11939693B2 (en) | 2015-01-26 | 2021-06-18 | Surface-treated steel sheet, metal container, and method for producing surface-treated steel sheet |
Publications (1)
| Publication Number | Publication Date |
|---|---|
| US20180010259A1 true US20180010259A1 (en) | 2018-01-11 |
Family
ID=56542909
Family Applications (2)
| Application Number | Title | Priority Date | Filing Date |
|---|---|---|---|
| US15/546,624 Abandoned US20180010259A1 (en) | 2015-01-26 | 2015-12-24 | Surface-treated steel sheet, metal container, and method for producing surface-treated steel sheet |
| US17/352,059 Active US11939693B2 (en) | 2015-01-26 | 2021-06-18 | Surface-treated steel sheet, metal container, and method for producing surface-treated steel sheet |
Family Applications After (1)
| Application Number | Title | Priority Date | Filing Date |
|---|---|---|---|
| US17/352,059 Active US11939693B2 (en) | 2015-01-26 | 2021-06-18 | Surface-treated steel sheet, metal container, and method for producing surface-treated steel sheet |
Country Status (6)
| Country | Link |
|---|---|
| US (2) | US20180010259A1 (ja) |
| EP (2) | EP3252190B1 (ja) |
| JP (1) | JP5986343B1 (ja) |
| CN (1) | CN107208300B (ja) |
| TW (1) | TW201641705A (ja) |
| WO (1) | WO2016121276A1 (ja) |
Cited By (1)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| US20230257898A1 (en) * | 2020-06-26 | 2023-08-17 | Toyo Kohan Co., Ltd. | Surface-treated steel sheet, metal container, and method for manufacturing surface-treated steel sheet |
Families Citing this family (3)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| JP2018035394A (ja) * | 2016-08-31 | 2018-03-08 | 東洋鋼鈑株式会社 | 表面処理鋼板、有機樹脂被覆鋼板、及びこれらを用いた容器 |
| CN110029381B (zh) * | 2019-04-25 | 2020-12-15 | 首钢集团有限公司 | 一种高镀锡量镀锡板的生产方法 |
| CN112557298B (zh) * | 2019-09-26 | 2023-05-09 | 上海梅山钢铁股份有限公司 | 一种冷轧电镀锡钢板表面附着力的检测方法 |
Citations (5)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| US20040138058A1 (en) * | 2002-07-24 | 2004-07-15 | Sankar Sambasivan | Aluminum phosphate compounds, compositions, materials and related metal coatings |
| US20100310898A1 (en) * | 2008-02-18 | 2010-12-09 | Hiromitsu Date | Plated steel sheet for cans and method for production of the same |
| EP2312016A1 (en) * | 2008-07-10 | 2011-04-20 | JFE Steel Corporation | Tin-plated steel sheet and method for producing same |
| US20110168563A1 (en) * | 2008-07-10 | 2011-07-14 | Jfe Steel Corporation | Tin-plated steel sheet and method for manufacturing the same |
| US20130209829A1 (en) * | 2010-09-15 | 2013-08-15 | Jfe Steel Corporation | Steel sheet for containers |
Family Cites Families (14)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| GB1199089A (en) * | 1967-11-22 | 1970-07-15 | Nippon Kokan Kk | A Method of Electrolytically Treating Metal Articles |
| JPS5275626A (en) * | 1975-12-19 | 1977-06-24 | Nippon Steel Corp | Subsequent treating process for galvanized steel sheet |
| JPS5843473B2 (ja) * | 1979-12-06 | 1983-09-27 | 東洋鋼飯株式会社 | 錫めつき鋼板の表面処理法 |
| JP4693207B2 (ja) | 2000-05-23 | 2011-06-01 | 関西ペイント株式会社 | カチオン電着塗料 |
| MXPA04004590A (es) * | 2001-11-14 | 2005-05-16 | Jfe Steel Corp | Hoja de metal de superficie tratada y el agente de tratamiento de la superficie. |
| JP4805613B2 (ja) * | 2005-06-17 | 2011-11-02 | 東洋製罐株式会社 | 表面処理金属板及びその表面処理方法、並びに樹脂被覆金属板、缶及び缶蓋 |
| EP1942208B1 (en) * | 2005-10-20 | 2016-01-06 | JFE Steel Corporation | Method for manufacturing tin-plated steel sheet |
| JP4125765B2 (ja) * | 2006-09-28 | 2008-07-30 | 日本パーカライジング株式会社 | 金属のセラミックス皮膜コーティング方法およびそれに用いる電解液ならびにセラミックス皮膜および金属材料 |
| JP2010180452A (ja) * | 2009-02-05 | 2010-08-19 | Nippon Steel Corp | 缶用めっき鋼板及びその製造方法 |
| JP5365335B2 (ja) | 2009-04-30 | 2013-12-11 | Ｊｆｅスチール株式会社 | 錫めっき鋼板およびその製造方法 |
| KR101484642B1 (ko) | 2012-10-24 | 2015-01-20 | 엘지디스플레이 주식회사 | 유기 발광 표시 장치 |
| JP6081224B2 (ja) * | 2013-02-27 | 2017-02-15 | 東洋鋼鈑株式会社 | 表面処理鋼板の製造方法 |
| JP5671566B2 (ja) * | 2013-02-27 | 2015-02-18 | 東洋鋼鈑株式会社 | 表面処理鋼板の製造方法 |
| MY194625A (en) * | 2013-07-01 | 2022-12-07 | Jfe Steel Corp | Steel sheet for containers |
-
2015
- 2015-12-24 EP EP15880168.8A patent/EP3252190B1/en active Active
- 2015-12-24 US US15/546,624 patent/US20180010259A1/en not_active Abandoned
- 2015-12-24 CN CN201580074640.XA patent/CN107208300B/zh active Active
- 2015-12-24 EP EP20192629.2A patent/EP3786319B1/en active Active
- 2015-12-24 WO PCT/JP2015/085947 patent/WO2016121276A1/ja active Application Filing
- 2015-12-24 JP JP2016530022A patent/JP5986343B1/ja active Active
-
2016
- 2016-01-07 TW TW105100390A patent/TW201641705A/zh unknown
-
2021
- 2021-06-18 US US17/352,059 patent/US11939693B2/en active Active
Patent Citations (5)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| US20040138058A1 (en) * | 2002-07-24 | 2004-07-15 | Sankar Sambasivan | Aluminum phosphate compounds, compositions, materials and related metal coatings |
| US20100310898A1 (en) * | 2008-02-18 | 2010-12-09 | Hiromitsu Date | Plated steel sheet for cans and method for production of the same |
| EP2312016A1 (en) * | 2008-07-10 | 2011-04-20 | JFE Steel Corporation | Tin-plated steel sheet and method for producing same |
| US20110168563A1 (en) * | 2008-07-10 | 2011-07-14 | Jfe Steel Corporation | Tin-plated steel sheet and method for manufacturing the same |
| US20130209829A1 (en) * | 2010-09-15 | 2013-08-15 | Jfe Steel Corporation | Steel sheet for containers |
Cited By (1)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| US20230257898A1 (en) * | 2020-06-26 | 2023-08-17 | Toyo Kohan Co., Ltd. | Surface-treated steel sheet, metal container, and method for manufacturing surface-treated steel sheet |
Also Published As
| Publication number | Publication date |
|---|---|
| WO2016121276A1 (ja) | 2016-08-04 |
| JPWO2016121276A1 (ja) | 2017-04-27 |
| EP3786319A1 (en) | 2021-03-03 |
| US11939693B2 (en) | 2024-03-26 |
| EP3252190B1 (en) | 2020-09-02 |
| EP3252190A1 (en) | 2017-12-06 |
| US20210310146A1 (en) | 2021-10-07 |
| EP3786319B1 (en) | 2023-08-09 |
| TW201641705A (zh) | 2016-12-01 |
| CN107208300A (zh) | 2017-09-26 |
| JP5986343B1 (ja) | 2016-09-06 |
| CN107208300B (zh) | 2018-09-14 |
| EP3252190A4 (en) | 2018-09-26 |
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| US11753737B2 (en) | Surface-treated steel sheet, metal container, and method for producing surface-treated steel sheet | |
| US11939693B2 (en) | Surface-treated steel sheet, metal container, and method for producing surface-treated steel sheet | |
| JP5986344B1 (ja) | 表面処理鋼板の製造方法 | |
| US20230257898A1 (en) | Surface-treated steel sheet, metal container, and method for manufacturing surface-treated steel sheet | |
| EP3051006B1 (en) | Method for producing surface-treated steel sheet | |
| US10309028B2 (en) | Method for producing surface-treated steel sheet, surface-treated steel sheet, and organic resin coated metal container | |
| JP6052305B2 (ja) | 容器用鋼板 | |
| US20240035182A1 (en) | Surface-treated steel sheet and method of producing the same | |
| JP6146402B2 (ja) | 容器用鋼板 |
Legal Events
| Date | Code | Title | Description |
|---|---|---|---|
| AS | Assignment |
Owner name: TOYO KOHAN CO., LTD., JAPAN Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:YOSHIMURA, KUNIHIRO;MATSUBARA, MASANOBU;SASAKI, MARIE;AND OTHERS;SIGNING DATES FROM 20170607 TO 20170613;REEL/FRAME:043144/0052 Owner name: TOYO SEIKAN CO., LTD., JAPAN Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:YOSHIMURA, KUNIHIRO;MATSUBARA, MASANOBU;SASAKI, MARIE;AND OTHERS;SIGNING DATES FROM 20170607 TO 20170613;REEL/FRAME:043144/0052 |
|
| STPP | Information on status: patent application and granting procedure in general |
Free format text: DOCKETED NEW CASE - READY FOR EXAMINATION |
|
| STPP | Information on status: patent application and granting procedure in general |
Free format text: NON FINAL ACTION MAILED |
|
| STPP | Information on status: patent application and granting procedure in general |
Free format text: RESPONSE TO NON-FINAL OFFICE ACTION ENTERED AND FORWARDED TO EXAMINER |
|
| STPP | Information on status: patent application and granting procedure in general |
Free format text: FINAL REJECTION MAILED |
|
| STPP | Information on status: patent application and granting procedure in general |
Free format text: RESPONSE TO NON-FINAL OFFICE ACTION ENTERED AND FORWARDED TO EXAMINER |
|
| STPP | Information on status: patent application and granting procedure in general |
Free format text: FINAL REJECTION MAILED |
|
| STCB | Information on status: application discontinuation |
Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION |