JP6146402B2 - 容器用鋼板 - Google Patents
容器用鋼板 Download PDFInfo
- Publication number
- JP6146402B2 JP6146402B2 JP2014242123A JP2014242123A JP6146402B2 JP 6146402 B2 JP6146402 B2 JP 6146402B2 JP 2014242123 A JP2014242123 A JP 2014242123A JP 2014242123 A JP2014242123 A JP 2014242123A JP 6146402 B2 JP6146402 B2 JP 6146402B2
- Authority
- JP
- Japan
- Prior art keywords
- film
- steel plate
- layer
- adhesion
- containers
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
[1]鋼板の表面の少なくとも一部を覆うNi層、Sn層、Ni−Fe合金層、Fe−Sn−Ni合金層およびFe−Sn合金層のうちから選ばれた少なくとも1層からなるめっき層を有するめっき鋼板と、上記めっき鋼板の上記めっき層側の表面上に配置された皮膜とを有する容器用鋼板であって、上記皮膜が、Ti、NiおよびCを含有し、上記皮膜は、上記めっき鋼板の片面あたりのTi換算の付着量が5.0mg/m2以上60.0mg/m2未満であり、上記めっき鋼板の片面あたりのNi換算の付着量が0.1〜3.0mg/m2であり、上記皮膜におけるCのTiに対する質量比(C/Ti)が0.01〜10である、容器用鋼板。
[2]上記皮膜は、上記めっき鋼板の片面あたりのTi換算の付着量が10.0〜30.0mg/m2である、上記[1]に記載の容器用鋼板。
[3]後述する式(2)で定義されるT値が0.50以下である、上記[1]または[2]に記載の容器用鋼板。
[4]上記めっき層が錫めっき層であり、上記皮膜がNi−Sn合金相を含む、上記[1]〜[3]のいずれかに記載の容器用鋼板。
[5]上記皮膜が含有するCが、フェノール樹脂またはフェノール化合物に由来する、上記[1]〜[4]のいずれかに記載の容器用鋼板。
本発明の容器用鋼板は、概略的には、めっき鋼板、および、めっき鋼板の表面上に配置された皮膜を有する。
以下に、めっき鋼板、および、皮膜の具体的な態様について詳述する。まず、めっき鋼板の態様について詳述する。
めっき鋼板は、鋼板と、鋼板の表面の少なくとも一部を覆うNi層、Sn層、Ni−Fe合金層、Fe−Sn−Ni合金層およびFe−Sn合金層のうちから選ばれた少なくとも1層からなるめっき層とを有する。
素材の鋼板としては、一般的な缶用の鋼板を使用できる。めっき層は、鋼板表面上の少なくとも一部を覆う層であり、連続層であってもよいし、不連続の島状であってもよい。また、めっき層は、鋼板の少なくとも片面に設けられていればよく、両面に設けられていてもよい。めっき層の形成は、含有される元素に応じた公知の方法で行える。
以下に、鋼板およびめっき層の好適態様について詳述する。
鋼板の種類は特に限定されるものではない。通常、容器材料として使用される鋼板(例えば、低炭素鋼板、極低炭素鋼板)を用いることができる。この鋼板の製造方法、材質なども特に限定されるものではない。通常の鋼片製造工程から熱間圧延、酸洗、冷間圧延、焼鈍、調質圧延等の工程を経て製造される。
Ni含有層としてはニッケルが含まれていればよい。例えば、Niめっき層(Ni層)、Ni−Fe合金層などが挙げられる。
鋼板にNi含有層を付与する方法は特に限定されない。例えば、公知の電気めっきなどの方法が挙げられる。また、Ni含有層としてNi−Fe合金層を付与する場合、電気めっきなどにより鋼板表面上にNi付与後、焼鈍することにより、鋼中にNiを拡散させ、Ni−Fe合金層を形成できる。
Ni含有層中のNi付着量は特に限定されず、片面当たりのNi換算量として50〜2000mg/m2が好ましい。上記範囲内であれば、コスト面でも有利となる。
ただし、後述するように、皮膜がNiを含むため、上記の蛍光X線による表面分析によりNi含有層中のNi付着量のみを測定することは困難である。このため、Ni含有層中のNi付着量は、蛍光X線により求めたNi付着量から後述する皮膜中に含まれるNi付着量を差し引いて求めることができる。
めっき鋼板が鋼板表面上に有するめっき層としては、Snを含有するめっき層(以下、「錫めっき層」ともいう)が好ましい。錫めっき層は鋼板の少なくとも片面に設けられていればよく、両面に設けられていてもよい。錫めっき層は、鋼板表面上の少なくとも一部を覆う層であり、連続層であってもよいし、不連続の島状であってもよい。
Sn付着量は、蛍光X線により表面分析して測定できる。蛍光X線の場合、Sn量既知のSn付着量サンプルを用いて、Sn量に関する検量線をあらかじめ特定しておき、同検量線を用いて相対的にSn付着量を特定する。
また、錫めっき層としては、Ni含有層を表面に有する鋼板に対して錫めっきを行い、さらに通電加熱などにより錫を加熱溶融させて得られる、Sn層の最下層(Sn層/鋼板界面)にFe−Sn−Ni合金層、Fe−Sn合金層などが一部形成した錫めっき層、または、Sn層の全Snが合金化しFe−Sn−Ni合金層、Fe−Sn合金層を形成した錫めっき層も含む。
例えば、フェノールスルフォン酸錫めっき浴、メタンスルフォン酸錫めっき浴、またはハロゲン系錫めっき浴を用い、片面あたりの付着量が所定量となるように鋼板表面にSnを電気めっきする。その後、Snの融点(231.9℃)以上の温度で加熱溶融処理を行って、錫単体のめっき層(Sn層)の最下層またはSn層の全Snを合金化しFe−Sn合金層を形成した錫めっき層を製造できる。加熱溶融処理を省略した場合、錫単体のめっき層(Sn層)を製造できる。
次に、上述しためっき鋼板のめっき層側の表面上に配置される皮膜について説明する。皮膜は、概略的には、その成分として、Ti(チタニウム元素)、Ni(ニッケル元素)およびC(炭素元素)を含有する皮膜であり、後述する処理液を用いて形成される。
なお、皮膜中のTi、Ni、C等は、それぞれ、各種のチタン化合物、ニッケル化合物、炭素化合物として含まれ、これら化合物の種類や態様は特に限定されない。
具体的には、皮膜中にNiおよびCは一定量必要であるが、皮膜中にNiが過剰に存在すると、フィルム密着性および塗料密着性が低下する。このメカニズム(理由)は明らかではないが、Tiを含む皮膜中に一定量以上のNiが存在しないと皮膜形成や皮膜と鋼板との接着などが不十分となるが、その一方で、過剰のNiが存在すると、Niが粒子状に析出して、皮膜とフィルムまたは塗料との密着を妨げるためと考えられる。
また、皮膜中のCのTiに対する質量比が一定範囲内であることにより、フィルム密着性および塗料密着性が優れる。このメカニズム(理由)も明らかではないが、皮膜中のCが有機樹脂であるフィルムまたは塗料と化学結合を生成して皮膜とフィルムまたは塗料に対する密着性を向上させるところ、皮膜中のCの量が少なすぎるとこの効果が小さく、一方で、多すぎると皮膜そのものの強度が低下してやはり密着性が劣るためと考えられる。
なお、上記メカニズムは推測であり、上記メカニズム以外であっても本発明の範囲内であるとする。
皮膜は、めっき鋼板の片面あたりのTi換算の付着量(以下、「Ti付着量」ともいう)が5.0mg/m2以上60mg/m2未満である。Ti付着量が5.0mg/m2未満または60mg/m2以上であるとフィルム密着性および塗料密着性は劣るが、5.0mg/m2以上60mg/m2未満であればフィルム密着性および塗料密着性に優れる。Ti付着量は、フィルム密着性および塗料密着性がより優れるという理由から、10〜30mg/m2が好ましく、10〜20mg/m2がより好ましい。
皮膜は、めっき鋼板の片面あたりのNi換算の付着量(以下、「Ni付着量」ともいう)が0.1〜3.0mg/m2である。Ni付着量が0.1〜3.0mg/m2であれば耐食性にも優れる。ここで、耐食性とは、具体的には、PETフィルムをラミネートした状態および塗料を塗装した状態で、容器用鋼板を酸性水溶液中に浸漬した際の傷部(鋼板まで到達する傷)の耐食性(それぞれ「フィルム貼付後耐食性」および「塗装後耐食性」ともいう)のことである。
耐食性がより優れるという理由から、Ni付着量は、0.1〜1.3mg/m2が好ましい。
皮膜におけるCのTiに対する質量比(C/Ti)が0.01〜10である。皮膜中のCが有機樹脂であるフィルムまたは塗料と化学結合を生成して皮膜とフィルムまたは塗料に対する密着性を向上させるが、質量比(C/Ti)が0.01未満であるとこの効果が十分に得られない。その一方で、質量比(C/Ti)が10超であると皮膜そのものの強度が低下してやはり密着性が劣る。しかし、質量比(C/Ti)が0.01〜10の範囲内であれば、フィルム密着性および塗料密着性が優れる。
質量比(C/Ti)は、フィルム密着性がより優れるという理由から、0.10〜5が好ましく、0.20〜5がより好ましく、0.20〜2がさらに好ましい。
蛍光X線分析は、例えば、下記条件により実施される。
・装置:リガク社製蛍光X線分析装置System3270
・測定径:30mm
・測定雰囲気:真空
・スペクトル:Ti−Kα、Ni−Kα、C−Kα
・スリット:COARSE
・分光結晶:LiF(Ti、Ni)、RX(C)
上記条件により測定した皮膜の蛍光X線分析のTi−Kα、Ni−Kα、C−Kαのピークカウント数を用いる。
その場合は、走査型電子顕微鏡(Scanning Electron Microscope:SEM)や透過型電子顕微鏡(Transmission Electron Microscope:TEM)による断面観察とグロー放電発光分析とを併用することで皮膜中に含まれるNi付着量とめっき層中に含まれるNi量とを区別できる。
具体的には、皮膜およびめっき層の断面を収束イオンビーム(Focused Ion Beam:FIB)加工により露出させ、SEMまたはTEMによる断面観察から皮膜の厚さを算出する。次いで、グロー放電発光分析によるスパッタリング深さとスパッタリング時間との関係を求める。その後、皮膜厚さに相当するスパッタリング時間までのグロー放電発光分析のNi元素による発光カウント積算値を求める。このNi元素による発光カウント積算値から、あらかじめ求めておいた検量線を用いて、Ni付着量を求めることができる。
ここで、検量線は以下の方法で作成する。
まず、Niを含まないめっき層上にNiを含む皮膜を有する、Ni付着量の異なる複数のサンプルについてグロー放電発光分析し、Ni元素による発光カウントが検出されなくなるスパッタリング時間までのカウント積算値を求める。次いでこれらのサンプルのNi付着量を蛍光X線による表面分析により求める。このようにして、グロー放電発光分析によるNiカウント積算値とNi付着量との検量線を作成する。
皮膜の厚さは、10〜120nmが好ましく、20〜60nmがより好ましい。皮膜の厚さは、皮膜の断面を収束イオンビーム(FIB)加工により露出させ、透過型電子顕微鏡(TEM)観察による断面プロファイルから測定できる。
皮膜は、下記式(2)で定義されるT値が0.50以下であることが好ましい。
T=[Ii(F)−Ib(F)]/Ib(F)・・・(2)
式(2)中、Ii(F)は、本発明の容器用鋼板を30分間沸騰水中で浸漬する前の皮膜の蛍光X線分析のFピークカウント数を表し、Ib(F)は、本発明の容器用鋼板を30分間沸騰水中で浸漬した後の皮膜の蛍光X線分析のFピークカウント数を表す。
ここで、[Ii(F)−Ib(F)]は、沸騰水中への浸漬により溶出するF量を示し、これをIb(F)で除する式(2)で定義されるT値は、皮膜中の可溶性F量の割合を示す指標となる。このT値が0.50以下である場合に、得られる容器用鋼板のフィルム密着性がより優れる。
・装置:リガク社製蛍光X線分析装置System3270
・測定径:30mm
・測定雰囲気:真空
・スペクトル:F−Kα
・スリット:COARSE
・分光結晶:TAP
上記条件により測定した皮膜の蛍光X線分析のF−Kαのピークカウント数を用いる。
また、めっき層が上述した錫めっき層である場合において、皮膜は、Ni−Sn合金相を含むことが好ましい。
Ni−Sn合金相における「Ni」は皮膜中のNiに由来し、「Sn」は錫めっき層中のSnに由来する。このようなNi−Sn合金相は、皮膜中において、皮膜と錫めっき層との界面に連続的な層として析出していてもよいし、皮膜中に分散した粒子として断続的に析出していてもよいし、その両方であってもよい。
錫めっき層のSnが皮膜中に入り込み表面近くまで到達すると、皮膜の色調などが劣る場合があるが、皮膜中にNi−Sn合金相が析出しているとSnの入り込みが抑制され、色調が良好となる。また、フィルム密着性および塗料密着性もより優れる。
なお、皮膜中におけるNi−Sn合金相の有無を確認する方法としては、例えば、透過型電子顕微鏡(Transmission Electron Microscope:TEM)の電子線回折またはエネルギー分散型X線分析(Energy dispersive X-ray spectrometry:EDX)を用いて、抽出レプリカ法または収束イオンビーム(Focused Ion Beam:FIB)加工により作製したサンプルの表面または断面について、点分析または線分析する方法が挙げられる。
上述した本発明の容器用鋼板を製造する方法としては、例えば、後述する皮膜形成工程を少なくとも備える方法(以下、便宜的に「本発明の製造方法」ともいう)が好ましい。
皮膜形成工程は、後述する処理液(以下、便宜的に「本発明の処理液」ともいう)中にめっき鋼板を浸漬する(浸漬処理)、または、本発明の処理液中に浸漬しためっき鋼板に陰極電解処理を施すことにより、めっき鋼板のめっき層側の表面上に、上述した皮膜を形成する工程である。陰極電解処理は、浸漬処理よりも、より高速に、均一な皮膜を得ることができるという理由から好ましい。なお、陰極電解処理と陽極電解処理とを交互に行う交番電解を実施してもよい。
以下に、使用される本発明の処理液や陰極電解処理の条件などについて詳述する。
《処理液のTi成分》
本発明の処理液は、上記皮膜にTi(チタニウム元素)を供給するためのTi成分(Ti化合物)を含有する。
このTi成分としては、特に限定されないが、例えば、チタンアルコキシド、シュウ酸チタニルアンモニウム、シュウ酸チタニルカリウム二水和物、硫酸チタン、チタンラクテート、チタンフッ化水素酸(H2TiF6)および/またはその塩などが挙げられる。なお、チタンフッ化水素酸の塩としては、例えば、六フッ化チタン酸カリウム(K2TiF6)、六フッ化チタン酸ナトリウム(Na2TiF6)、六フッ化チタン酸アンモニウム((NH4)2TiF6)等が挙げられる。
これらのうち、処理液の安定性、入手の容易性などの観点から、チタンフッ化水素酸および/またはその塩が好ましい。
本発明の処理液におけるTi成分の含有量は、特に限定されないが、チタンフッ化水素酸および/またはその塩を使用する場合、六フッ化チタン酸イオン(TiF6 2-)に換算した量が、0.004〜0.4mol/Lであるのが好ましく、0.02〜0.2mol/Lがより好ましい。
本発明の処理液は、上記皮膜にNi(ニッケル元素)を供給するためのNi成分(Ni化合物)を含有する。
このNi成分としては、特に限定されないが、硫酸ニッケル(NiSO4)、硫酸ニッケル六水和物、塩化ニッケル(NiCl2)、塩化ニッケル六水和物などが挙げられる。
本発明の処理液におけるNi成分の含有量は、特に限定されないが、Niイオン(Ni2+)に換算した量が、0.002〜0.04mol/Lであるのが好ましく、0.004〜0.02mol/Lがより好ましい。
本発明の処理液は、上記皮膜にC(炭素元素)を供給するためのC成分(C化合物)を含有する。
このC成分としては、例えば、フェノール樹脂またはフェノール化合物が挙げられる。例えば、フェノール樹脂またはフェノール化合物を添加した本発明の処理液中で、めっき鋼板に陰極電解処理を施すことにより、Ti中にC(フェノール樹脂)が析出し、Cを含有する皮膜が形成される。
質量比(C/Ti)は、0.1〜1.0が好ましい。
本発明の処理液中の溶媒としては、通常水が使用されるが有機溶媒を併用してもよい。
本発明の処理液のpHは、特に限定されないが、pH2.0〜5.0が好ましい。この範囲内であれば、処理時間を短くでき、かつ、処理液の安定性に優れる。pHの調整には公知の酸成分(例えば、リン酸、硫酸)・アルカリ成分(例えば、水酸化ナトリウム、アンモニア水)を使用できる。
また、本発明の処理液には、必要に応じて、ラウリル硫酸ナトリウム、アセチレングリコールなどの界面活性剤が含まれていてもよい。また、付着挙動の経時的な安定性の観点から、処理液には、ピロリン酸塩などの縮合リン酸塩が含まれていてもよい。
本発明の処理液の液温は、20〜80℃が好ましく、40〜60℃がより好ましい。
皮膜形成工程において、陰極電解処理を実施する際の電解電流密度は、形成される皮膜中のTiおよびNiが適量となって、フィルム密着性および塗料密着性がより優れるという理由から、1.0〜20.0A/dm2が好ましく、3.0〜15.0A/dm2がより好ましい。
陰極電解処理の通電時間は、0.1〜5秒が好ましく、0.3〜2秒がより好ましい。
陰極電解処理の際の電気量密度は、電流密度と通電時間との積であり適宜設定される。
水洗処理の方法は特に限定されず、例えば、連続ラインで製造を行う場合、本発明の処理液のタンクの後に水洗タンクを設け、皮膜を形成する処理の後に連続して水に浸漬する方法などが挙げられる。水洗処理に用いる水の温度は、40〜90℃が好ましい。
水洗時間は、水洗処理による効果がより優れるという理由から、0.5秒超が好ましく、1.0〜5.0秒が好ましい。
さらに、水洗処理に代えて、または、水洗処理の後に、乾燥を行ってもよい。乾燥の際の温度および方式は特に限定されず、例えば、通常のドライヤーや電気炉乾燥方式が適用できる。乾燥処理の際の温度としては、100℃以下が好ましい。上記範囲内であれば、皮膜の酸化を抑制でき、皮膜組成の安定性が保たれる。なお、下限は特に限定されないが、通常室温程度である。
本発明の製造方法は、上述した皮膜形成工程の前に、以下に説明する前処理工程を備えていてもよい。
前処理工程は、アルカリ性水溶液(特に、炭酸ナトリウム水溶液)中で、めっき鋼板に陰極電解処理を施す工程である。
めっき層が錫めっき層である場合、通常、錫めっき層の作製時にその表面は酸化されて、錫酸化物が形成される。このような錫めっき層を有するめっき鋼板に対して、陰極電解処理を施すことにより、不要な錫酸化物を除去して、錫酸化物量を調整できる。
前処理工程の陰極電解処理の際に使用される溶液としては、アルカリ性水溶液(例えば、炭酸ナトリウム水溶液)が挙げられる。アルカリ性水溶液中のアルカリ成分(例えば、炭酸ナトリウム)の濃度は特に限定されないが、錫酸化物の除去がより効率的に進行する点から、5〜15g/Lが好ましく、8〜12g/Lがより好ましい。
陰極電解処理の際のアルカリ性水溶液の液温は特に限定されないが、40〜60℃が好ましい。陰極電解処理の電解条件(電流密度、電解時間)は、適宜調整される。なお、陰極電解処理の後に、必要に応じて、水洗処理を施してもよい。
以下の方法によって、めっき鋼板を製造した。
まず、板厚0.22mmの鋼板(T4原板)を電解脱脂し、ワット浴を用いて第3表に示す片面当たりのNi付着量でニッケルめっき層を両面に形成後、10vol.%H2+90vol.%N2雰囲気中にて700℃で焼鈍してニッケルめっきを拡散浸透させることによりNi−Fe合金層(Ni含有層)(第3表にNi付着量を示す)を両面に形成した。
引き続き、上記表層にNi含有層を有する鋼板を、錫めっき浴を用い、第3表に示す片面当たりのSn付着量で錫めっきを両面に施した。その後、Snの融点以上で加熱溶融処理を施し、Fe−Sn−Ni合金層とその上に不連続のSn層とを形成し、めっき鋼板を製造した。このようにして、下層側から順に、Ni−Fe合金層/Fe−Sn−Ni合金層/Sn層からなるめっき層が鋼板の両面に形成された。
作製しためっき鋼板を用いて、以下にようにして、容器用鋼板の試験材を作製した。
液温50℃、10g/Lの炭酸ナトリウム水溶液中に上記めっき鋼板を浸漬し、第2表に示す条件にて、陰極電解処理を行った。
次いで、pHを4.0に調整した第1表に示す組成の処理液(溶媒:水)を用い、第2表に示す液温(処理温度)および電解条件(電流密度、通電時間、電気量密度)で陰極電解処理を施した。その後、85℃の水槽に0.2秒間だけ浸漬させることにより水洗処理を施し、ブロアを用いて室温で乾燥を行い、両面に皮膜を形成した。
なお、処理液に含まれるフェノール樹脂としては重量平均分子量が5,000のフェノール樹脂を用い、フェノール化合物としては重量平均分子量が2,000の富士化学工業社製のタンニン酸を用いた。
皮膜のTi付着量、Ni付着量および質量比(C/Ti)、Ii(F)、Ib(F)およびT、皮膜の厚さ、ならびに、皮膜中のNi−Sn合金相の有無は、上述した方法により測定ないし計算した。
フィルム密着性の評価として、以下に示す無加工フィルム密着性および加工後フィルム密着性の評価を行った。無加工フィルム密着性および加工後フィルム密着性のいずれかが優れるものと評価されない場合には、フィルム密着性は劣るものとする。
作製した容器用鋼板の表面に、市販のPETフィルム(Melinex850:デュポン社製)を、ロール加圧4kg/cm2、板送り速度40mpm、ロール通過後の板の表面温度が160℃となる条件で熱融着させ、次いで、バッチ炉中で後加熱(到達板温210℃で120秒保持)を行ない、ラミネート鋼板を作製した。
無加工フィルム密着性の評価は、作製したラミネート鋼板を、温度130℃、相対湿度100%のレトルト雰囲気に30分間保持した後、このレトルト雰囲気において180度ピール試験をすることにより行った。
180度ピール試験とは、図1(a)に示すようなフィルム2を残して鋼板1の一部3を切り取った試験片(サイズ:30mm×100mm)を用い、図1(b)に示すように、試験片の一端に重り4(100g)を付けてフィルム2側に180度折り返して30分間放置して行うフィルム剥離試験のことである。
図1(c)に示す剥離長5を測定した。下記基準で無加工フィルム密着性を評価した。結果が◎または○であれば無加工フィルム密着性に優れるものとして評価できる。
◎:剥離長が1mm未満
○:剥離長が1mm以上5mm未満
△:剥離長が5mm以上10mm未満
×:剥離長が10mm以上
上記方法で作製したラミネート鋼板に対し、先端径3/16インチRのポンチを用い、1kgの錘を25cmの高さから落下させ、フィルムを貼った面の側が凸になるようデュポン衝撃加工を行った。このような加工試験片を4つ作成し、レトルト装置内に、凸面が上になるように置き、130℃のレトルト環境で30分間保持後、取り出し、加工部のフィルム剥離の程度を目視で、下記5段階で評価した。4つの試験片の評点の平均値(小数点以下1桁)を用いて、加工後フィルム密着性を評価した。実用上、結果が3.0以上であれば、加工後フィルム密着性に優れるものとして評価できる。
5:剥離なし
4:加工部の面積の5%未満で剥離発生
3:加工部の面積の5%以上20%未満で剥離発生
2:加工部の面積の20%以上50%未満で剥離発生
1:加工部の面積の50%以上で剥離発生
作製した容器用鋼板(幅100mm×長さ150mm)の表面に、エポキシフェノール系塗料を塗布し、210℃で10分間の焼付を行い、付着量が50mg/dm2の塗装を施した。
次いで、上記塗装を施した、同一の条件で作製した2枚の容器用鋼板を、ナイロン接着フィルムを挟んで塗装面が向かい合わせになるように積層した後、圧力2.94×105Pa、温度190℃、圧着時間30秒の圧着条件下で貼り合わせた。その後、これを5mm幅の試験片に分割した。分割した試験片の2枚の容器用鋼板を引張試験機で引き剥がし、引き剥がしたときの引張強度を測定した。各試験材で、2つの試験片の平均値を下記基準で評価した。実用上、結果が○または△であれば、塗料密着性に優れるものとして評価できる。
○:2.0kgf以上
△:1.0kgf以上2.0kgf未満
×:1.0kgf未満
上記方法で作製したラミネート鋼板(幅70mm×長さ40mm)のフィルム面に、カッターを用いて地鉄(鋼板)に達する深さのクロスカットを入れた。クロスカットを入れたラミネート鋼板を、1.5質量%クエン酸と1.5質量%食塩とを含有する混合水溶液からなる55℃の試験液に、96時間浸漬した。浸漬後、洗浄および乾燥をした後、フィルム面にセロハン粘着テープを貼り付け、引き剥がすテープ剥離を行った。クロスカット部中心の任意の4箇所についてフィルム剥離幅(カット部から広がる左右の合計幅)を測定し、4箇所の平均値を求めた。フィルム剥離幅の平均値を腐食幅とみなし、下記基準で評価した。実用上、結果が◎または○であれば、耐食性に優れるものとして評価できる。
◎:腐食幅0.8mm未満
○:腐食幅0.8mm以上1.5mm未満
△:腐食幅1.5mm以上2.0mm未満
×:腐食幅2.0mm以上
作製した容器用鋼板(幅70mm×長さ40mm)の表面に、エポキシフェノール系塗料を塗布し、210℃で10分間の焼付を行い、付着量が50mg/dm2の塗装を施した。
次いで、上記塗装を施した容器用鋼板(塗装鋼板)の塗装面に、カッターを用いて地鉄(鋼板)に達する深さのクロスカットを入れた。クロスカットを入れた塗装鋼板を、1.5質量%クエン酸と1.5質量%食塩とを含有する混合水溶液からなる55℃の試験液に、96時間浸漬した。浸漬後、洗浄および乾燥をした後、塗膜にセロハン粘着テープを貼り付け、引き剥がすテープ剥離を行った。クロスカット部中心の任意の4箇所についてフィルム剥離幅(カット部から広がる左右の合計幅)を測定し、4箇所の平均値を求めた。フィルム剥離幅の平均値を腐食幅とみなし、下記基準で評価した。実用上、結果が◎または○であれば、耐食性に優れるものとして評価できる。
◎:腐食幅0.2mm未満
○:腐食幅0.2mm以上0.6mm未満
△:腐食幅0.6mm以上1.0mm未満
×:腐食幅1.0mm以上
これに対して、質量比(C/Ti)が0.01未満である比較例(試験材No.1〜3)は、無加工フィルム密着性、加工後フィルム密着性および塗料密着性の少なくともいずれかが劣っていた。
また、Ni付着量が0.1mg/m2未満である比較例(試験材No.4〜6)は、無加工フィルム密着性および加工後フィルム密着性の少なくともいずれかが劣っていた。
2:フィルム
3:鋼板の切り取った部位
4:重り
5:剥離長
Claims (5)
- 鋼板の表面の少なくとも一部を覆うNi層、Sn層、Ni−Fe合金層、Fe−Sn−Ni合金層およびFe−Sn合金層のうちから選ばれた少なくとも1層からなるめっき層を有するめっき鋼板と、前記めっき鋼板の前記めっき層側の表面上に配置された皮膜とを有する容器用鋼板であって、
前記皮膜が、Ti、NiおよびCを含有し、
前記皮膜は、前記めっき鋼板の片面あたりのTi換算の付着量が5.0mg/m2以上60.0mg/m2未満であり、前記めっき鋼板の片面あたりのNi換算の付着量が0.1〜3.0mg/m2であり、
前記皮膜におけるCのTiに対する質量比(C/Ti)が0.01〜10である、容器用鋼板。 - 前記皮膜は、前記めっき鋼板の片面あたりのTi換算の付着量が10.0〜30.0mg/m2である、請求項1に記載の容器用鋼板。
- 下記式(2)で定義されるT値が0.50以下である、請求項1または2に記載の容器用鋼板。
T=[Ii(F)−Ib(F)]/Ib(F)・・・(2)
(式(2)中、Ii(F)は前記皮膜の蛍光X線分析のFピークカウント数を表し、Ib(F)は前記容器用鋼板を30分間沸騰水中で浸漬した後の前記皮膜の蛍光X線分析のFピークカウント数を表す。) - 前記めっき層が錫めっき層であり、前記皮膜がNi−Sn合金相を含む、請求項1〜3のいずれか1項に記載の容器用鋼板。
- 前記皮膜が含有するCが、フェノール樹脂またはフェノール化合物に由来する、請求項1〜4のいずれか1項に記載の容器用鋼板。