US20170152579A1 - Method for Producing a High Strength Coated Steel Sheet having Improved Strength, Ductility and Formability - Google Patents

Method for Producing a High Strength Coated Steel Sheet having Improved Strength, Ductility and Formability Download PDF

Info

Publication number
US20170152579A1
US20170152579A1 US15/322,829 US201515322829A US2017152579A1 US 20170152579 A1 US20170152579 A1 US 20170152579A1 US 201515322829 A US201515322829 A US 201515322829A US 2017152579 A1 US2017152579 A1 US 2017152579A1
Authority
US
United States
Prior art keywords
steel sheet
temperature
coated steel
quenching
mpa
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
US15/322,829
Other languages
English (en)
Inventor
Rashmi Ranjan Mohanty
Hyun Jo Jun
Dongwei Fan
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ArcelorMittal SA
Original Assignee
ArcelorMittal SA
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Family has litigation
First worldwide family litigation filed litigation Critical https://patents.darts-ip.com/?family=52000882&utm_source=google_patent&utm_medium=platform_link&utm_campaign=public_patent_search&patent=US20170152579(A1) "Global patent litigation dataset” by Darts-ip is licensed under a Creative Commons Attribution 4.0 International License.
Application filed by ArcelorMittal SA filed Critical ArcelorMittal SA
Assigned to ARCELORMITTAL reassignment ARCELORMITTAL ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: FAN, Dongwei, MOHANTY, Rashmi Ranjan, JUN, Hyun Jo
Publication of US20170152579A1 publication Critical patent/US20170152579A1/en
Pending legal-status Critical Current

Links

Images

Classifications

    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/01—Layered products comprising a layer of metal all layers being exclusively metallic
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/01—Layered products comprising a layer of metal all layers being exclusively metallic
    • B32B15/013—Layered products comprising a layer of metal all layers being exclusively metallic one layer being formed of an iron alloy or steel, another layer being formed of a metal other than iron or aluminium
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
    • C21D1/18—Hardening; Quenching with or without subsequent tempering
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
    • C21D1/18—Hardening; Quenching with or without subsequent tempering
    • C21D1/19—Hardening; Quenching with or without subsequent tempering by interrupted quenching
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
    • C21D1/26—Methods of annealing
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0221—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
    • C21D8/0226—Hot rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0221—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
    • C21D8/0236—Cold rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0247—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/04—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing
    • C21D8/0447—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing characterised by the heat treatment
    • C21D8/0473—Final recrystallisation annealing
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
    • C21D9/48—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals deep-drawing sheets
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/34—Ferrous alloys, e.g. steel alloys containing chromium with more than 1.5% by weight of silicon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/38—Ferrous alloys, e.g. steel alloys containing chromium with more than 1.5% by weight of manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/58—Ferrous alloys, e.g. steel alloys containing chromium with nickel with more than 1.5% by weight of manganese
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/022—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating
    • C23C2/0224—Two or more thermal pretreatments
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/024—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by cleaning or etching
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
    • C23C2/06—Zinc or cadmium or alloys based thereon
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/34—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the shape of the material to be treated
    • C23C2/36—Elongated material
    • C23C2/40—Plates; Strips
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/001—Austenite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/002—Bainite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/008—Martensite

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Mechanical Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Physics & Mathematics (AREA)
  • Thermal Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Heat Treatment Of Sheet Steel (AREA)
  • Coating With Molten Metal (AREA)
US15/322,829 2014-07-03 2015-07-03 Method for Producing a High Strength Coated Steel Sheet having Improved Strength, Ductility and Formability Pending US20170152579A1 (en)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
PCT/IB2014/002275 WO2016001702A1 (en) 2014-07-03 2014-07-03 Method for producing a high strength coated steel sheet having improved strength, ductility and formability
IBPCT/IB2014/002275 2014-07-03
PCT/IB2015/055039 WO2016001895A2 (en) 2014-07-03 2015-07-03 Method for producing a high strength coated steel sheet having improved strength, ductility and formability

Related Parent Applications (1)

Application Number Title Priority Date Filing Date
PCT/IB2015/055039 A-371-Of-International WO2016001895A2 (en) 2014-07-03 2015-07-03 Method for producing a high strength coated steel sheet having improved strength, ductility and formability

Related Child Applications (1)

Application Number Title Priority Date Filing Date
US16/931,001 Division US11492676B2 (en) 2014-07-03 2020-07-16 Method for producing a high strength coated steel sheet having improved strength, ductility and formability

Publications (1)

Publication Number Publication Date
US20170152579A1 true US20170152579A1 (en) 2017-06-01

Family

ID=52000882

Family Applications (2)

Application Number Title Priority Date Filing Date
US15/322,829 Pending US20170152579A1 (en) 2014-07-03 2015-07-03 Method for Producing a High Strength Coated Steel Sheet having Improved Strength, Ductility and Formability
US16/931,001 Active US11492676B2 (en) 2014-07-03 2020-07-16 Method for producing a high strength coated steel sheet having improved strength, ductility and formability

Family Applications After (1)

Application Number Title Priority Date Filing Date
US16/931,001 Active US11492676B2 (en) 2014-07-03 2020-07-16 Method for producing a high strength coated steel sheet having improved strength, ductility and formability

Country Status (15)

Country Link
US (2) US20170152579A1 (de)
EP (2) EP3831965A1 (de)
JP (2) JP6623183B2 (de)
KR (1) KR102455942B1 (de)
CN (1) CN106471139B (de)
BR (1) BR112017000005B1 (de)
CA (1) CA2954146C (de)
ES (1) ES2855500T3 (de)
HU (1) HUE054278T2 (de)
MA (2) MA53357A (de)
MX (1) MX2016017399A (de)
PL (1) PL3164522T3 (de)
RU (1) RU2686729C2 (de)
UA (1) UA118792C2 (de)
WO (2) WO2016001702A1 (de)

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US10995383B2 (en) 2014-07-03 2021-05-04 Arcelormittal Method for producing a high strength coated steel sheet having improved strength and ductility and obtained sheet
US11279984B2 (en) 2016-12-21 2022-03-22 Arcelormittal High-strength cold rolled steel sheet having high formability and a method of manufacturing thereof
US11492676B2 (en) 2014-07-03 2022-11-08 Arcelormittal Method for producing a high strength coated steel sheet having improved strength, ductility and formability
US11555226B2 (en) 2014-07-03 2023-01-17 Arcelormittal Method for producing a high strength steel sheet having improved strength and formability and obtained sheet
US11618931B2 (en) 2014-07-03 2023-04-04 Arcelormittal Method for producing a high strength steel sheet having improved strength, ductility and formability

Families Citing this family (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2018115935A1 (en) * 2016-12-21 2018-06-28 Arcelormittal Tempered and coated steel sheet having excellent formability and a method of manufacturing the same
WO2018115936A1 (en) 2016-12-21 2018-06-28 Arcelormittal Tempered and coated steel sheet having excellent formability and a method of manufacturing the same
WO2019122963A1 (en) 2017-12-19 2019-06-27 Arcelormittal Cold rolled and heat treated steel sheet and a method of manufacturing thereof
CN110180957B (zh) * 2018-06-28 2020-11-03 镕凝精工新材料科技(上海)有限公司 一种镀锌钢板的热处理方法及热冲压工艺
CA3149331A1 (en) * 2019-08-07 2021-02-11 United States Steel Corporation High ductility zinc-coated steel sheet products
KR102321285B1 (ko) * 2019-12-18 2021-11-03 주식회사 포스코 가공성이 우수한 고강도 강판 및 그 제조방법
WO2022242859A1 (en) * 2021-05-20 2022-11-24 Nlmk Clabecq Method for manufacturing a high strength steel plate and high strength steel plate
JP2023054990A (ja) 2021-10-05 2023-04-17 国立大学法人京都大学 面発光レーザ素子

Citations (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US6114656A (en) * 1997-06-20 2000-09-05 Exxonmobil Upstream Research Company Welding methods for producing ultra-high strength weldments with weld metals having excellent cryogenic temperature fracture toughness
US6264760B1 (en) * 1997-07-28 2001-07-24 Exxonmobil Upstream Research Company Ultra-high strength, weldable steels with excellent ultra-low temperature toughness
US20080251161A1 (en) * 2005-03-30 2008-10-16 Kabushiki Kaisha Kobe Seiko Sho (Kobe Steel, Ltd.) High Strength Cold Rolled Steel Sheet and Plated Steel Sheet Excellent in the Balance of Strength and Workability
JP2009173959A (ja) * 2008-01-21 2009-08-06 Nakayama Steel Works Ltd 高強度鋼板およびその製造方法
JP2010126770A (ja) * 2008-11-28 2010-06-10 Jfe Steel Corp 成形性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
US20130276940A1 (en) * 2010-09-17 2013-10-24 Jfe Steel Corporation High strength hot rolled steel sheet having excellent fatigue resistance and method for manufacturing the same
US8697252B2 (en) * 2007-01-29 2014-04-15 Kobe Steel, Ltd. High-strength hot-dip galvannealed steel sheet with superior phosphatability
US20140234655A1 (en) * 2011-09-29 2014-08-21 Jfe Steel Corporation Hot-dip galvanized steel sheet and method for producing same
US9011614B2 (en) * 2008-02-08 2015-04-21 Jfe Steel Corporation High-strength galvanized steel sheet with excellent formability and method for manufacturing the same

Family Cites Families (42)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB243069A (en) 1924-08-21 1925-11-23 Robert Benson North Improvements in and connected with magneto electric machines
US4159218A (en) 1978-08-07 1979-06-26 National Steel Corporation Method for producing a dual-phase ferrite-martensite steel strip
JP4608822B2 (ja) 2001-07-03 2011-01-12 Ｊｆｅスチール株式会社 プレス成形性と歪時効硬化特性に優れた高延性溶融亜鉛めっき鋼板およびその製造方法
US6746548B2 (en) 2001-12-14 2004-06-08 Mmfx Technologies Corporation Triple-phase nano-composite steels
US20060011274A1 (en) * 2002-09-04 2006-01-19 Colorado School Of Mines Method for producing steel with retained austenite
EP1707645B1 (de) 2004-01-14 2016-04-06 Nippon Steel & Sumitomo Metal Corporation Feuerverzinkte hochfeste stahlplatte mit hervorragender überzugshaftung und hervorragenden lochexpansionseigenschaften
JP4510488B2 (ja) 2004-03-11 2010-07-21 新日本製鐵株式会社 成形性および穴拡げ性に優れた溶融亜鉛めっき複合高強度鋼板およびその製造方法
JP4367300B2 (ja) 2004-09-14 2009-11-18 Ｊｆｅスチール株式会社 延性および化成処理性に優れる高強度冷延鋼板およびその製造方法
US8025982B2 (en) * 2005-12-06 2011-09-27 Kobe Steel, Ltd. High-strength hot dip galvannealed steel sheet having high powdering resistance and method for producing the same
JP4174592B2 (ja) * 2005-12-28 2008-11-05 株式会社神戸製鋼所 超高強度薄鋼板
US7887648B2 (en) 2005-12-28 2011-02-15 Kobe Steel, Ltd. Ultrahigh-strength thin steel sheet
EP1832667A1 (de) * 2006-03-07 2007-09-12 ARCELOR France Herstellungsverfahren von Stahlblechen mit hoher Festigkeit, Duktilität sowie Zähigkeit und so hergestellte Bleche.
JP4974341B2 (ja) * 2006-06-05 2012-07-11 株式会社神戸製鋼所 成形性、スポット溶接性、および耐遅れ破壊性に優れた高強度複合組織鋼板
JP4291860B2 (ja) 2006-07-14 2009-07-08 株式会社神戸製鋼所 高強度鋼板およびその製造方法
EP1990431A1 (de) 2007-05-11 2008-11-12 ArcelorMittal France Verfahren zur Herstellung von kalt gewalzten und geglühten Stahlblechen mit sehr hoher Festigkeit und so hergestellte Bleche
EP2020451A1 (de) 2007-07-19 2009-02-04 ArcelorMittal France Verfahren zur Herstellung von Stahlblechen mit hoher Widerstandsfähigkeit und Duktilität und damit hergestellte Bleche
EP2031081B1 (de) * 2007-08-15 2011-07-13 ThyssenKrupp Steel Europe AG Dualphasenstahl, Flachprodukt aus einem solchen Dualphasenstahl und Verfahren zur Herstellung eines Flachprodukts
EP2028282B1 (de) 2007-08-15 2012-06-13 ThyssenKrupp Steel Europe AG Dualphasenstahl, Flachprodukt aus einem solchen Dualphasenstahl und Verfahren zur Herstellung eines Flachprodukts
EP2198067A4 (de) 2007-09-10 2011-10-05 Pertti J Sippola Verfahren und vorrichtung zur verbesserten formbarkeit von glavanisiertem stahl mit hoher zugfestigkeit
EP2202327B1 (de) 2007-10-25 2020-12-02 JFE Steel Corporation Herstellungsverfahren für hochfestes galvanisiertes stahlblech mit hervorragender formbarkeit
KR101018131B1 (ko) 2007-11-22 2011-02-25 주식회사 포스코 저온인성이 우수한 고강도 저항복비 건설용 강재 및 그제조방법
CN101225499B (zh) * 2008-01-31 2010-04-21 上海交通大学 低合金超高强度复相钢及其热处理方法
JP5418047B2 (ja) 2008-09-10 2014-02-19 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法
JP5412182B2 (ja) 2009-05-29 2014-02-12 株式会社神戸製鋼所 耐水素脆化特性に優れた高強度鋼板
JP5807368B2 (ja) 2010-06-16 2015-11-10 新日鐵住金株式会社 圧延方向に対して４５°の方向の均一伸びが極めて高い高強度冷延鋼板及びその製造方法
JP5136609B2 (ja) * 2010-07-29 2013-02-06 Ｊｆｅスチール株式会社 成形性および耐衝撃性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
WO2012120020A1 (en) * 2011-03-07 2012-09-13 Tata Steel Nederland Technology Bv Process for producing high strength formable steel and high strength formable steel produced therewith
JP5821260B2 (ja) 2011-04-26 2015-11-24 Ｊｆｅスチール株式会社 成形性及び形状凍結性に優れた高強度溶融亜鉛めっき鋼板、並びにその製造方法
UA112771C2 (uk) * 2011-05-10 2016-10-25 Арселормітталь Інвестігасьон І Десароло Сл Сталевий лист з високою механічною міцністю, пластичністю і формованістю, спосіб виготовлення та застосування таких листів
EP2524970A1 (de) * 2011-05-18 2012-11-21 ThyssenKrupp Steel Europe AG Hochfestes Stahlflachprodukt und Verfahren zu dessen Herstellung
JP2012240095A (ja) * 2011-05-20 2012-12-10 Kobe Steel Ltd 高強度鋼板の温間成形方法
JP5824283B2 (ja) 2011-08-17 2015-11-25 株式会社神戸製鋼所 室温および温間での成形性に優れた高強度鋼板
JP5632904B2 (ja) * 2012-03-29 2014-11-26 株式会社神戸製鋼所 加工性に優れた高強度冷延鋼板の製造方法
JP2013237923A (ja) 2012-04-20 2013-11-28 Jfe Steel Corp 高強度鋼板およびその製造方法
JP2014019928A (ja) 2012-07-20 2014-02-03 Jfe Steel Corp 高強度冷延鋼板および高強度冷延鋼板の製造方法
IN2014DN11262A (de) 2012-07-31 2015-10-09 Jfe Steel Corp
JP5857909B2 (ja) 2012-08-09 2016-02-10 新日鐵住金株式会社 鋼板およびその製造方法
WO2016001700A1 (en) 2014-07-03 2016-01-07 Arcelormittal Method for producing a high strength steel sheet having improved strength, ductility and formability
WO2016001710A1 (en) 2014-07-03 2016-01-07 Arcelormittal Method for producing a high strength coated steel having improved strength and ductility and obtained sheet
WO2016001702A1 (en) 2014-07-03 2016-01-07 Arcelormittal Method for producing a high strength coated steel sheet having improved strength, ductility and formability
WO2016001706A1 (en) 2014-07-03 2016-01-07 Arcelormittal Method for producing a high strength steel sheet having improved strength and formability and obtained sheet
US9802074B2 (en) 2014-07-18 2017-10-31 Landscape Structures Inc. Outdoor fitness resistance mechanism and housing

Patent Citations (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US6114656A (en) * 1997-06-20 2000-09-05 Exxonmobil Upstream Research Company Welding methods for producing ultra-high strength weldments with weld metals having excellent cryogenic temperature fracture toughness
US6264760B1 (en) * 1997-07-28 2001-07-24 Exxonmobil Upstream Research Company Ultra-high strength, weldable steels with excellent ultra-low temperature toughness
US20080251161A1 (en) * 2005-03-30 2008-10-16 Kabushiki Kaisha Kobe Seiko Sho (Kobe Steel, Ltd.) High Strength Cold Rolled Steel Sheet and Plated Steel Sheet Excellent in the Balance of Strength and Workability
US8697252B2 (en) * 2007-01-29 2014-04-15 Kobe Steel, Ltd. High-strength hot-dip galvannealed steel sheet with superior phosphatability
JP2009173959A (ja) * 2008-01-21 2009-08-06 Nakayama Steel Works Ltd 高強度鋼板およびその製造方法
US9011614B2 (en) * 2008-02-08 2015-04-21 Jfe Steel Corporation High-strength galvanized steel sheet with excellent formability and method for manufacturing the same
JP2010126770A (ja) * 2008-11-28 2010-06-10 Jfe Steel Corp 成形性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
US20130276940A1 (en) * 2010-09-17 2013-10-24 Jfe Steel Corporation High strength hot rolled steel sheet having excellent fatigue resistance and method for manufacturing the same
US20140234655A1 (en) * 2011-09-29 2014-08-21 Jfe Steel Corporation Hot-dip galvanized steel sheet and method for producing same

Non-Patent Citations (3)

* Cited by examiner, † Cited by third party
Title
Hance, Brandon M. "Practical Application of the Hole Expansion Test." SAE International Journal of Engines, vol. 10, no. 2, 2017, pp. 247–257 (Year: 2017) *
Honeycombe , R. W. K., and F. B. Pickering. Ferrite and Bainite in Alloy Steels. Metallurgical Transactions, vol. 3, no 5, 1972, pp. 10991112 *
Machine Translation of JP-2010126770-A` (Year: 2010) *

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US10995383B2 (en) 2014-07-03 2021-05-04 Arcelormittal Method for producing a high strength coated steel sheet having improved strength and ductility and obtained sheet
US11492676B2 (en) 2014-07-03 2022-11-08 Arcelormittal Method for producing a high strength coated steel sheet having improved strength, ductility and formability
US11555226B2 (en) 2014-07-03 2023-01-17 Arcelormittal Method for producing a high strength steel sheet having improved strength and formability and obtained sheet
US11618931B2 (en) 2014-07-03 2023-04-04 Arcelormittal Method for producing a high strength steel sheet having improved strength, ductility and formability
US11279984B2 (en) 2016-12-21 2022-03-22 Arcelormittal High-strength cold rolled steel sheet having high formability and a method of manufacturing thereof

Also Published As

Publication number Publication date
JP6823148B2 (ja) 2021-01-27
US20200347477A1 (en) 2020-11-05
JP6623183B2 (ja) 2019-12-18
WO2016001895A3 (en) 2016-03-17
KR102455942B1 (ko) 2022-10-17
RU2016151385A (ru) 2018-06-26
JP2017527690A (ja) 2017-09-21
MX2016017399A (es) 2017-05-01
RU2016151385A3 (de) 2018-12-06
KR20170028328A (ko) 2017-03-13
EP3164522B1 (de) 2021-03-03
BR112017000005B1 (pt) 2021-04-13
US11492676B2 (en) 2022-11-08
MA53357A (fr) 2021-06-09
JP2020045573A (ja) 2020-03-26
BR112017000005A2 (pt) 2017-11-07
EP3831965A1 (de) 2021-06-09
CA2954146A1 (en) 2016-01-07
WO2016001895A2 (en) 2016-01-07
ES2855500T3 (es) 2021-09-23
PL3164522T3 (pl) 2021-09-06
MA40196A (fr) 2017-05-10
EP3164522A2 (de) 2017-05-10
CN106471139A (zh) 2017-03-01
HUE054278T2 (hu) 2021-08-30
MA40196B1 (fr) 2021-03-31
CA2954146C (en) 2022-07-12
RU2686729C2 (ru) 2019-04-30
CN106471139B (zh) 2018-08-31
WO2016001702A1 (en) 2016-01-07
UA118792C2 (uk) 2019-03-11

Similar Documents

Publication Publication Date Title
US11492676B2 (en) Method for producing a high strength coated steel sheet having improved strength, ductility and formability
US20210095357A1 (en) Method for producing a high strength coated steel sheet having improved strength and ductility and obtained sheet
US20220298598A1 (en) Method for producing a high strength steel sheet having improved strength and formability and obtained sheet
US11001904B2 (en) Method for producing an ultra high strength coated or not coated steel sheet and obtained sheet
US11718888B2 (en) Method for producing a high strength coated steel sheet having improved strength, formability and obtained sheet
US10472692B2 (en) Method for manufacturing a high strength steel sheet having improved formability and ductility and sheet obtained
US20170233847A1 (en) Method for Producing a Coated Steel Sheet having Improved Strength, Ductility and Formability

Legal Events

Date Code Title Description
AS Assignment

Owner name: ARCELORMITTAL, LUXEMBOURG

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:MOHANTY, RASHMI RANJAN;JUN, HYUN JO;FAN, DONGWEI;SIGNING DATES FROM 20161110 TO 20161122;REEL/FRAME:041150/0580

STPP Information on status: patent application and granting procedure in general

Free format text: NON FINAL ACTION MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: RESPONSE TO NON-FINAL OFFICE ACTION ENTERED AND FORWARDED TO EXAMINER

STPP Information on status: patent application and granting procedure in general

Free format text: FINAL REJECTION MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: DOCKETED NEW CASE - READY FOR EXAMINATION

STPP Information on status: patent application and granting procedure in general

Free format text: NON FINAL ACTION MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: NON FINAL ACTION MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: RESPONSE TO NON-FINAL OFFICE ACTION ENTERED AND FORWARDED TO EXAMINER

STPP Information on status: patent application and granting procedure in general

Free format text: RESPONSE TO NON-FINAL OFFICE ACTION ENTERED AND FORWARDED TO EXAMINER

STPP Information on status: patent application and granting procedure in general

Free format text: FINAL REJECTION MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: DOCKETED NEW CASE - READY FOR EXAMINATION

STPP Information on status: patent application and granting procedure in general

Free format text: NON FINAL ACTION MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: RESPONSE TO NON-FINAL OFFICE ACTION ENTERED AND FORWARDED TO EXAMINER

STCV Information on status: appeal procedure

Free format text: NOTICE OF APPEAL FILED

STCV Information on status: appeal procedure

Free format text: APPEAL BRIEF (OR SUPPLEMENTAL BRIEF) ENTERED AND FORWARDED TO EXAMINER

STCV Information on status: appeal procedure

Free format text: EXAMINER'S ANSWER TO APPEAL BRIEF MAILED

STCV Information on status: appeal procedure

Free format text: ON APPEAL -- AWAITING DECISION BY THE BOARD OF APPEALS