US20160333437A1 - Bearing part, steel for bearing part and method for producing thereof - Google Patents

Bearing part, steel for bearing part and method for producing thereof Download PDF

Info

Publication number
US20160333437A1
US20160333437A1 US15/110,351 US201515110351A US2016333437A1 US 20160333437 A1 US20160333437 A1 US 20160333437A1 US 201515110351 A US201515110351 A US 201515110351A US 2016333437 A1 US2016333437 A1 US 2016333437A1
Authority
US
United States
Prior art keywords
content
bearing part
less
steel
wire rod
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US15/110,351
Other languages
English (en)
Inventor
Masashi Sakamoto
Junichi Kodama
Yutaka Neishi
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nippon Steel Corp
Original Assignee
Nippon Steel and Sumitomo Metal Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nippon Steel and Sumitomo Metal Corp filed Critical Nippon Steel and Sumitomo Metal Corp
Assigned to NIPPON STEEL & SUMITOMO METAL CORPORATION reassignment NIPPON STEEL & SUMITOMO METAL CORPORATION ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: KODAMA, JUNICHI, NEISHI, YUTAKA, SAKAMOTO, MASASHI
Publication of US20160333437A1 publication Critical patent/US20160333437A1/en
Assigned to NIPPON STEEL CORPORATION reassignment NIPPON STEEL CORPORATION CHANGE OF NAME (SEE DOCUMENT FOR DETAILS). Assignors: NIPPON STEEL & SUMITOMO METAL CORPORATION
Abandoned legal-status Critical Current

Links

Images

Classifications

    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/40—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for rings; for bearing races
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22D—CASTING OF METALS; CASTING OF OTHER SUBSTANCES BY THE SAME PROCESSES OR DEVICES
    • B22D23/00—Casting processes not provided for in groups B22D1/00 - B22D21/00
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
    • C21D1/18—Hardening; Quenching with or without subsequent tempering
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
    • C21D1/26—Methods of annealing
    • C21D1/32—Soft annealing, e.g. spheroidising
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/06—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of rods or wires
    • C21D8/065—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of rods or wires of ferrous alloys
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/36—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for balls; for rollers
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/38—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for roll bodies
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/52—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for wires; for strips ; for rods of unlimited length
    • C21D9/54—Furnaces for treating strips or wire
    • C21D9/68—Furnace coilers; Hot coilers
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/001—Ferrous alloys, e.g. steel alloys containing N
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/002—Ferrous alloys, e.g. steel alloys containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/08—Ferrous alloys, e.g. steel alloys containing nickel
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/20—Ferrous alloys, e.g. steel alloys containing chromium with copper
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/22—Ferrous alloys, e.g. steel alloys containing chromium with molybdenum or tungsten
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/32—Ferrous alloys, e.g. steel alloys containing chromium with boron
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/44—Ferrous alloys, e.g. steel alloys containing chromium with nickel with molybdenum or tungsten
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/54—Ferrous alloys, e.g. steel alloys containing chromium with nickel with boron
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F16—ENGINEERING ELEMENTS AND UNITS; GENERAL MEASURES FOR PRODUCING AND MAINTAINING EFFECTIVE FUNCTIONING OF MACHINES OR INSTALLATIONS; THERMAL INSULATION IN GENERAL
    • F16C—SHAFTS; FLEXIBLE SHAFTS; ELEMENTS OR CRANKSHAFT MECHANISMS; ROTARY BODIES OTHER THAN GEARING ELEMENTS; BEARINGS
    • F16C33/00—Parts of bearings; Special methods for making bearings or parts thereof
    • F16C33/30—Parts of ball or roller bearings
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F16—ENGINEERING ELEMENTS AND UNITS; GENERAL MEASURES FOR PRODUCING AND MAINTAINING EFFECTIVE FUNCTIONING OF MACHINES OR INSTALLATIONS; THERMAL INSULATION IN GENERAL
    • F16C—SHAFTS; FLEXIBLE SHAFTS; ELEMENTS OR CRANKSHAFT MECHANISMS; ROTARY BODIES OTHER THAN GEARING ELEMENTS; BEARINGS
    • F16C33/00—Parts of bearings; Special methods for making bearings or parts thereof
    • F16C33/30—Parts of ball or roller bearings
    • F16C33/58—Raceways; Race rings
    • F16C33/62—Selection of substances
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F16—ENGINEERING ELEMENTS AND UNITS; GENERAL MEASURES FOR PRODUCING AND MAINTAINING EFFECTIVE FUNCTIONING OF MACHINES OR INSTALLATIONS; THERMAL INSULATION IN GENERAL
    • F16C—SHAFTS; FLEXIBLE SHAFTS; ELEMENTS OR CRANKSHAFT MECHANISMS; ROTARY BODIES OTHER THAN GEARING ELEMENTS; BEARINGS
    • F16C33/00—Parts of bearings; Special methods for making bearings or parts thereof
    • F16C33/30—Parts of ball or roller bearings
    • F16C33/58—Raceways; Race rings
    • F16C33/64—Special methods of manufacture
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/001—Austenite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/003—Cementite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/004—Dispersions; Precipitations
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/005—Ferrite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/008—Martensite
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F16—ENGINEERING ELEMENTS AND UNITS; GENERAL MEASURES FOR PRODUCING AND MAINTAINING EFFECTIVE FUNCTIONING OF MACHINES OR INSTALLATIONS; THERMAL INSULATION IN GENERAL
    • F16C—SHAFTS; FLEXIBLE SHAFTS; ELEMENTS OR CRANKSHAFT MECHANISMS; ROTARY BODIES OTHER THAN GEARING ELEMENTS; BEARINGS
    • F16C2204/00—Metallic materials; Alloys
    • F16C2204/60—Ferrous alloys, e.g. steel alloys
    • F16C2204/66—High carbon steel, i.e. carbon content above 0.8 wt%, e.g. through-hardenable steel
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F16—ENGINEERING ELEMENTS AND UNITS; GENERAL MEASURES FOR PRODUCING AND MAINTAINING EFFECTIVE FUNCTIONING OF MACHINES OR INSTALLATIONS; THERMAL INSULATION IN GENERAL
    • F16C—SHAFTS; FLEXIBLE SHAFTS; ELEMENTS OR CRANKSHAFT MECHANISMS; ROTARY BODIES OTHER THAN GEARING ELEMENTS; BEARINGS
    • F16C2204/00—Metallic materials; Alloys
    • F16C2204/60—Ferrous alloys, e.g. steel alloys
    • F16C2204/70—Ferrous alloys, e.g. steel alloys with chromium as the next major constituent
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F16—ENGINEERING ELEMENTS AND UNITS; GENERAL MEASURES FOR PRODUCING AND MAINTAINING EFFECTIVE FUNCTIONING OF MACHINES OR INSTALLATIONS; THERMAL INSULATION IN GENERAL
    • F16C—SHAFTS; FLEXIBLE SHAFTS; ELEMENTS OR CRANKSHAFT MECHANISMS; ROTARY BODIES OTHER THAN GEARING ELEMENTS; BEARINGS
    • F16C2204/00—Metallic materials; Alloys
    • F16C2204/60—Ferrous alloys, e.g. steel alloys
    • F16C2204/70—Ferrous alloys, e.g. steel alloys with chromium as the next major constituent
    • F16C2204/72—Ferrous alloys, e.g. steel alloys with chromium as the next major constituent with nickel as further constituent, e.g. stainless steel
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F16—ENGINEERING ELEMENTS AND UNITS; GENERAL MEASURES FOR PRODUCING AND MAINTAINING EFFECTIVE FUNCTIONING OF MACHINES OR INSTALLATIONS; THERMAL INSULATION IN GENERAL
    • F16C—SHAFTS; FLEXIBLE SHAFTS; ELEMENTS OR CRANKSHAFT MECHANISMS; ROTARY BODIES OTHER THAN GEARING ELEMENTS; BEARINGS
    • F16C2220/00—Shaping
    • F16C2220/40—Shaping by deformation without removing material
    • F16C2220/44—Shaping by deformation without removing material by rolling
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F16—ENGINEERING ELEMENTS AND UNITS; GENERAL MEASURES FOR PRODUCING AND MAINTAINING EFFECTIVE FUNCTIONING OF MACHINES OR INSTALLATIONS; THERMAL INSULATION IN GENERAL
    • F16C—SHAFTS; FLEXIBLE SHAFTS; ELEMENTS OR CRANKSHAFT MECHANISMS; ROTARY BODIES OTHER THAN GEARING ELEMENTS; BEARINGS
    • F16C2223/00—Surface treatments; Hardening; Coating
    • F16C2223/02—Mechanical treatment, e.g. finishing
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F16—ENGINEERING ELEMENTS AND UNITS; GENERAL MEASURES FOR PRODUCING AND MAINTAINING EFFECTIVE FUNCTIONING OF MACHINES OR INSTALLATIONS; THERMAL INSULATION IN GENERAL
    • F16C—SHAFTS; FLEXIBLE SHAFTS; ELEMENTS OR CRANKSHAFT MECHANISMS; ROTARY BODIES OTHER THAN GEARING ELEMENTS; BEARINGS
    • F16C2223/00—Surface treatments; Hardening; Coating
    • F16C2223/10—Hardening, e.g. carburizing, carbo-nitriding

Definitions

  • the present invention relates to a bearing part such as needle bearings, roller bearings and ball bearings, steel for a bearing part which is a material for the bearing part, and a method for producing thereof.
  • Bearing parts such as needle bearings, roller bearings and ball bearings are continually used under a situation where a foreign material such as burr or abrasion powder is mixed into lubricating oil, that is, are continually used even in contaminated environments. Therefore, it is important to improve rolling contact fatigue life of a bearing part in contaminated environments. In order to improve the rolling contact fatigue life of the bearing part in contaminated environments, it is known that an increase in retained austenite is effective. Accordingly, steel for the bearing part is subjected to a surface treatment such as a carburizing or nitriding.
  • Patent Document 1 discloses a bearing part including large amount of retained austenite manufactured by quenching and tempering and without carburizing or a nitriding.
  • a bearing part disclosed in the Patent Document 1 secures the amount of retained austenite by lowering the martensite start temperature (Ms point) by including C, Mn and Ni, or Mo into the steel.
  • Ms point martensite start temperature
  • a content of Mn, which is added to the steel is increased in order to secure the amount of retained austenite, the hardenability of the steel is raised.
  • a supercooled structure such as martensite is generated during cooling after hot rolling, and the workability, ductility and toughness of hot rolled wire rod is deteriorated.
  • Patent Document 2 discloses a method of generating retained austenite while suppressing grain coarsening by using spherical cementite.
  • spheroidizing at high temperature is performed for long period of time.
  • C is solid-soluted into an austenite phase and the number density of spherical cementite is insufficient.
  • the grain size of austenite is coarsened and an improvement effect of rolling contact fatigue life cannot be obtained sufficiently.
  • the Patent Document 3 discloses a high-carbon steel rolled wire rod for bearing parts that was invented by some of the present inventors and the high-carbon steel rolled wire rod for bearing parts is capable of wire drawing without spheroidizing annealing.
  • Patent Document 4 discloses a method in which the rolled wire rod is subjected to the wire drawing after the hot rolling is completed and the spheroidizing annealing is performed so that the spheroidizing annealing before the wire drawing can be omitted.
  • the method disclosed in the Patent Document 4 is not intended to shorten the treatment time of the spheroidizing annealing.
  • Patent Document 1 Japanese Unexamined Patent Application, First Publication No. 2004-124215
  • Patent Document 2 Japanese Unexamined Patent Application, First Publication No. 2007-077432
  • Patent Document 3 PCT International Publication WO 2013/108828
  • Patent Document 4 Japanese Unexamined Patent Application, First Publication No. 2004-100016
  • Patent Document 1 when the content of Mn in the steel is increased, it is difficult to process the hot rolled wire rod by omitting spheroidizing annealing, and it is necessary to perform spheroidizing several times so as to obtain the bearing part for the foregoing reasons.
  • the present inventors found that it is necessary to control the microstructure through the use of wire drawing and quenching where the quenching temperature is controlled, in order to manufacture a bearing part having an excellent rolling contact fatigue life in contaminated environments using the material disclosed in Patent Document 3.
  • the present invention has been made in view of such circumstances, and the aim of the present invention is to provide a bearing part having an excellent rolling contact fatigue life in environment including contaminated environments, steel for a bearing part which is a material for the bearing part, and a method for manufacturing them, in which the number of spheroidizing annealing is only one and which takes a short amount of time.
  • the present inventors found that the average grain size of prior-austenite of a bearing part can be refined by subjecting steel including Cr in which the metallographic structure consists of pearlite to spheroidizing annealing at a lower temperature than usual after wire drawing. Furthermore, the present inventors found that the amount of retained austenite can be secured by refining the average grain size of the prior-austenite. Then, the present inventors found that the rolling contact fatigue life of the bearing part can be improved not only under normal conditions, but also in contaminated environments by securing the amount of retained austenite.
  • a bearing part includes, as a chemical composition, by mass %: C: 0.95% to 1.10%; Si: 0.10% to 0.70%; Mn: 0.20% to 1.20%; Cr: 0.90% to 1.60%; Al: 0.010% to 0.100%; N: 0.003% to 0.030%; P: 0.025% or less; S: 0.025% or less; O: 0.0010% or less; optionally one or more of the group consisting of: Mo: 0.25% or less, B: 0.0050% or less, Cu: 1.0% or less, Ni: 3.0% or less, and Ca: 0.0015% or less; and a remainder including Fe and impurities; a metallographic structure includes a retained austenite, a spherical cementite and a martensite; an amount of the retained austenite is 18% to 25%, by volume %; an average grain size of a prior-austenite is 6.0 ⁇ m or less; an average grain size of the sp
  • the bearing part according to (1) may include, as the chemical composition, by mass %, one or more of Mo: 0.01% to 0.25%, B: 0.0001% to 0.0050%, Cu: 0.1% to 1.0%, Ni: 1.0% to 3.0%, and Ca: 0.0001% to 0.0015%.
  • a steel for a bearing part includes, as a chemical composition, by mass %: C: 0.95% to 1.10%; Si: 0.10% to 0.70%; Mn: 0.20% to 1.20%; Cr: 0.90% to 1.60%; Al: 0.010% to 0.100%; N: 0.003% to 0.030%; S: 0.025% or less; P: 0.025% or less; O: 0.0010% or less; and optionally one or more of the group consisting of; Mo: 0.25% or less, B: 0.0050% or less, Cu: 1.0% or less, Ni: 3.0% or less, and Ca: 0.0015% or less; and a remainder including Fe an impurities; a metallographic structure includes a spherical cementite and a ferrite; a number density of the spherical cementite having a grain size of 0.5 ⁇ m to 3.0 ⁇ m is 2.0 ⁇ 10 6 mm ⁇ 2 or more in the metallographic structure.
  • the steel for the bearing part according to (3) may include, as the chemical composition, by mass %, one or more of Mo: 0.01% to 0.25%, B: 0.0001% to 0.0050%, Cu: 0.1% to 1.0%, Ni: 1.0% to 3.0%, and Ca: 0.0001% to 0.0015%.
  • a method for producing a steel for a bearing part includes: a casting process for obtaining a steel piece having a chemical composition according to (3) or (4); a heating process of heating the steel piece to 900° C. to 1300° C.; a hot rolling process for obtaining a hot rolled wire rod by subjecting the steel piece to hot rolling at a finish rolling temperature of 850° C. or less after the heating process; a winding process of winding the hot rolled wire rod after the hot rolling process at a winding temperature of 800° C. or less; a cooling process for making a microstructure of the hot rolled wire rod a pearlite by cooling the hot rolled wire rod to 600° C.
  • a 1 represents a temperature at which A 1 transformation starts, and is a predicted value which is calculated by a following equation 1 based on the chemical composition
  • [C], [Si] [Mn], [Cu], [Ni], [Cr], [Mo], [Al] and [B] in the equation 1 represent, by mass %, the content of C, the content of Si, the content of Mn, the content of Cu, the content of Ni, the content of Cr, the content of Mo, the content of Al and the content of B, respectively, in the hot rolled wire rod.
  • a method for producing a bearing part according to one aspect of the present invention includes: a casting process for obtaining a steel piece having a chemical composition according to (1) or (2); a heating process of heating the steel piece to 900° C. to 1300° C.; a hot rolling process for obtaining a hot rolled wire rod by subjecting the steel piece to hot rolling at a finish rolling temperature of 850° C. or less after the heating process; a winding process of winding the hot rolled wire rod after the hot rolling process at a winding temperature of 800° C. or less; a cooling process for making a microstructure of the hot rolled wire rod a pearlite by cooling the hot rolled wire rod to 600° C.
  • a 1 represents a temperature at which A 1 transformation starts, and is a predicted value which is calculated by a following equation 2 based on the chemical composition
  • [C], [Si], [Mn], [Cu], [Ni] [Cr] [Mo], [Al] and [B] in the equation 2 represent, by mass %, the content of C, the content of Si, the content of Mn, the content of Cu, the content of Ni, the content of Cr, the content of Mo, the content of Al and the content of B, respectively, in the hot rolled wire rod.
  • a bearing part having an excellent rolling contact fatigue life can be obtained by controlling the average grain size of prior-austenite, the amount of retained austenite and the number density of spherical cementite and by performing spheroidizing annealing for a short amount of time and once, not only under the normal conditions, but also in contaminated environments, without performing carburizing, nitriding and spheroidizing annealing for a long period of time.
  • steel for a bearing part which is a material for a bearing part can be obtained by controlling the metallographic structure.
  • manufacture thereof is possible. Therefore, when the bearing parts according to the above aspects are applied to a vehicle or industrial machinery, it is possible to extend the life of the machine and reduce the manufacturing cost. That is, contribution of the present invention to the industry is extremely significant.
  • FIG. 1 is a view showing a metallographic structure of a bearing part.
  • FIG. 2 is a view showing a metallographic structure of steel for a bearing part.
  • FIG. 3 is a view showing a relationship between the number density of spherical cementite in steel for a bearing part and the average grain size of prior-austenite of a bearing part.
  • FIG. 4 is a view showing a relationship between the average grain size of prior-austenite and the amount of retained austenite of a bearing part.
  • FIG. 5 is a view showing a relationship between the amount of retained austenite and the rolling contact fatigue life of a bearing part in a contaminated environment.
  • FIG. 6 is a view showing a relationship between the number density of spherical cementite in a bearing part and the rolling contact fatigue life of a bearing part.
  • the present inventors investigated the appropriate amount of retained austenite and the manufacturing conditions for controlling the amount of retained austenite and found the following.
  • the amount of retained austenite (volume %) can be determined by, for example, calculating the ratio of the diffraction intensity of retained austenite ⁇ (220) to the diffraction intensity of martensite ⁇ (211) measured by X-ray diffraction.
  • the amount of retained austenite (the amount of V ⁇ ) can be determined by, for example, obtaining the X-ray diffraction peaks of the microstructures of the steel sheet using an X-ray diffraction measuring apparatus (RAD-RU300 made by Rigaku Denki), in which a Co target is used and the target output is set to 40 kV-200 mA, and calculating the theoretical intensity ratio by Rietveld analyses.
  • RAD-RU300 made by Rigaku Denki
  • the rolling contact fatigue life can be improved even in contaminated environments.
  • the essential amount of retained austenite is 18% or more, by volume %.
  • the amount of retained austenite is more than 25% by volume %, the hardness is reduced, the normal rolling contact fatigue strength of the bearing part is reduced, and aging of dimensions become larger. As a result, the functional usage of the bearing part is reduced. Therefore, in order to improve the rolling contact fatigue life of the bearing part in contaminated environments, it is necessary to control the amount of retained austenite to be 18% to 25%, by volume %.
  • Ms point martensite start temperature
  • the Ms point is affected by solid-soluted amount of the elements such as C, Si and Mn in the austenite phase, particularly, is greatly affected by an amount of solid-soluted C in the austenite phase.
  • the heating temperature during the quenching is increased in order to increase the amount of solid-soluted C, the average grain size of prior-austenite coarsens.
  • the amount of solid-soluted C in martensite is increased after the quenching. Therefore, the rolling contact fatigue life and the toughness of the bearing part are reduced.
  • the present inventors focused their investigation on stabilization of the austenite phase due to grain refinement. As a result, the present inventors found the following.
  • processing strain is introduced by wire drawing a hot rolled wire rod having pearlite structure (pearlite steel).
  • the hot rolled wire rod is subjected to spheroidizing annealing at a lower than conventional temperature after the wire drawing. It was found that spherical cementite can be finely dispersed due to this spheroidizing annealing. Then, it was found that when the spherical cementite is finely dispersed, the average grain size of prior-austenite after quenching of steel for a bearing part, which had been subjected to the spheroidizing annealing, can be refined.
  • the present inventors found that the amount of retained austenite can be controlled to 18% to 25% by setting the average grain size of the prior-austenite of the bearing part to 6.0 ⁇ m or less.
  • the total reduction of area during the wire drawing and the heating temperature of the spheroidizing annealing In order to reduce the average grain size of the prior-austenite, it is preferable to control the total reduction of area during the wire drawing and the heating temperature of the spheroidizing annealing. In addition, after the spherical cementite is finely precipitated due to these controls, it is preferable to perform the quenching. Specifically, after the hot rolled wire rod (pearlite steel) is subjected to wire drawing with a total reduction of area of 50% or more, the spheroidizing annealing is performed at a temperature of 650° C. to the lower of 750° C. and A 1 ⁇ 5° C. Then, the hot rolled wire rod is cooled to 400° C.
  • the hot rolled wire rod pearlite steel
  • the hot rolled wire rod is heated to 800° C. to 890° C., and the quenching is performed.
  • the average grain size of the prior-austenite can be suppressed to 6.0 ⁇ m or less and the amount of retained austenite can be controlled to be 18% to 25%.
  • the average grain size of the prior-austenite can be obtained by the following method. Firstly, in the center of a longitudinal direction of a bearing part, a C cross section perpendicular to the longitudinal direction is polished and corroded, and thus, a grain boundary of the prior-austenite appears. Secondary, a range within a radius of 3 mm from a center of the C cross section is set as the center portion, and photographs are taken of the center portion using an optical microscope at 400 times magnification. Then, the captured images are measured by a counting method defined in JIS G 0551. In addition, four visual fields are measured in each sample, and the average value of grain sizes of the prior-austenite in the obtained four visual fields is set as the average grain size of the prior-austenite.
  • the spherical cementite When the total reduction of area during the wire drawing is less than 50%, the spherical cementite is not sufficiently spheroidized during the spheroidizing annealing, and the number density of spherical cementite having a grain size of 0.50 ⁇ m to 3.0 ⁇ m in the metallographic structure of the steel for the bearing part is decreased. As a result, the average grain size of the prior-austenite of the bearing part after the quenching is increased, and there are cases where the average grain size of prior-austenite is more than 6.0 ⁇ m.
  • FIG. 3 shows a relationship between the number density of spherical cementite having a grain size of 0.50 ⁇ m to 3.00 ⁇ m in steel for a bearing part after spheroidizing annealing and the average grain size of prior-austenite of a bearing part which is obtained through subsequent quenching and tempering.
  • FIG. 4 shows the relationship between the average grain size of prior-austenite of a bearing part and the amount of retained austenite of a bearing part.
  • the average grain size of the prior-austenite of the bearing part is 6.0 ⁇ m or less
  • the amount of retained austenite of the bearing part is 18% or more, by volume %.
  • the average grain size of the prior-austenite of the bearing part is more than 6.0 ⁇ m
  • the amount of retained austenite of the bearing part is reduced to less than 18%, by volume %.
  • FIG. 5 shows the relationship between the amount of retained austenite in a bearing part and the rolling contact fatigue life of a bearing part in a contaminated environment.
  • the rolling contact fatigue life of the bearing part in a contaminated environment is good.
  • the rolling contact fatigue life of the bearing part in a contaminated environment is reduced.
  • the present inventors investigated the method for increasing the number density of spherical cementite having an average grain size of 0.45 ⁇ m or less in the bearing part after the quenching.
  • the spherical cementite When spherical cementite, which is fine and hard, is dispersed in the steel, the spherical cementite contributes to strengthening of the bearing part. Therefore, when the number density of spherical cementite having the prescribed size is increased, the rolling contact fatigue life or an impact property of the bearing part is improved.
  • the present inventors found that it is important that the average grain size of spherical cementite of the bearing part be set to 0.45 ⁇ m or less and the number density of spherical cementite be set to 0.45 ⁇ 10 6 mm ⁇ 2 or more. When the number density of spherical cementite is less than 0.45 ⁇ 10 6 mm ⁇ 2 , the rolling contact fatigue life of the bearing part is decreased.
  • the number density of spherical cementite is preferably 0.5 ⁇ 10 6 mm ⁇ 2 or more.
  • the average grain size of the spherical cementite of the bearing part is more than 0.45 ⁇ m, generation and extension of fatigue crack is promoted. Therefore, it is necessary that the average grain size of spherical cementite of the bearing part is 0.45 ⁇ m or less. On the other hand, in normal operating conditions, it is difficult to reduce the average grain size of spherical cementite to less than 0.10 ⁇ m.
  • the spherical cementite is conventionally solid-soluted into an austenite phase which is a base metal
  • the number density of spherical cementite of the bearing part is lowered than the number density of spherical cementite in the steel for the bearing part which is a material for the bearing part.
  • the heating temperature of the quenching is set to a lower temperature, the number density of spherical cementite in the bearing part is increased; however, the amount of retained austenite in the bearing part is reduced. Therefore, the rolling contact fatigue life of the bearing part in the contaminated environment is reduced.
  • the present inventors found that when the number density of spherical cementite having a grain size of 0.5 ⁇ m to 3.0 ⁇ m in steel for a bearing part before quenching is increased to 2.0 ⁇ 10 6 mm ⁇ 2 or more, the number density of spherical cementite having an average grain size of 0.45 ⁇ m or less can be secured for 0.45 ⁇ 10 6 mm ⁇ 2 or more in a bearing part after the quenching.
  • FIG. 6 shows a relationship between the number density of spherical cementite having the prescribed size in a bearing part and the rolling contact fatigue property of a bearing part. As shown in FIG. 6 , when the number density of spherical cementite having an average grain size of 0.45 ⁇ m or less is 0.45 ⁇ 10 6 mm ⁇ 2 or more, the rolling contact fatigue life of the bearing part is good.
  • the number density of spherical cementite having the prescribed size can be obtained by the following method.
  • the bearing part In the center of the longitudinal direction of steel for a bearing part and a bearing part, the bearing part is cut with a cross section perpendicular to the longitudinal direction.
  • a cut C cross section is mirror-polished; the observation is performed at the center portion of the C cross section using a scanning electron microscope (SEM) with 5000 times magnification; and photographs are taken at ten visual fields. Then, the number of spherical cementite having the prescribed size is measured at each visual field and the number is divided by the visual field area, therefore, the number density of spherical cementite having the prescribed size can be obtained.
  • the center portion of the C cross section means a circle region which is 3 mm of radius from the center point of the C cross section, and the observation field is 0.02 mm 2 .
  • FIG. 1 shows a SEM image of the microstructure of the bearing part according to the present embodiment.
  • the SEM image of FIG. 1 shows the microstructure where the spherical cementite 2 precipitates in the martensite 1. Because retained austenite cannot be observed with SEM, retained austenite can be determined by the ratio of the diffraction intensity of martensite to the diffraction intensity of retained austenite with X diffraction method (XRD).
  • XRD X diffraction method
  • the amount of retained austenite is 18% to 25% by volume %.
  • the sum of spherical cementite and martensite is preferably 75% to 82% by volume %, which is obtained by subtracting the amount of retained austenite from the total volume.
  • the metallographic structure of the steel for the bearing part according to the present embodiment includes spherical cementite and ferrite. However, in order to obtain the rolling contact fatigue life and the hardness of the bearing part, it is preferable that microstructures other than spherical cementite and ferrite are not included in the steel for the bearing part.
  • FIG. 2 shows a SEM image of the metallographic structure of the steel for the bearing part after the spheroidizing annealing according to the present embodiment. The SEM image of FIG. 2 shows the microstructure where the spherical cementite 5 precipitates in the ferrite 4.
  • C Carbon is an element for enhancing the strength of a bearing part.
  • the content of C is less than 0.95%, the strength and the rolling contact fatigue life of the bearing part in the contaminated environment cannot be improved.
  • the content of C is more than 1.10%, carbide becomes coarse and the amount of retained austenite is excessive.
  • the content of C is set to 0.95% to 1.10%.
  • the content of C is preferably 0.96% to 1.05%. More preferably, the content of C is 0.97% to 1.03%.
  • Si is an element for enhancing strength and functions as a deoxidizer.
  • the content of Si is less than 0.10%, these effects cannot be obtained.
  • the content of Si is more than 0.70%, SiO 2 -based inclusion generates in steel, and thus, the rolling contact fatigue life of the bearing part is reduced. Therefore, the content of Si is set to 0.10% to 0.70%.
  • the content of Si is preferably 0.12% to 0.56%. More preferably, the content of Si is 0.15% to 0.50%.
  • Mn Manganese
  • Mn is an element which functions as a deoxidizer and as a desulfurizer. Furthermore, Mn is an element useful for securing the hardenability of the steel and the amount of retained austenite.
  • Mn is less than 0.20%, deoxidation is insufficient and oxide is generated. As a result, the rolling contact fatigue life of the bearing part is reduced.
  • the content of Mn is more than 1.20%, supercooled structure such as martensite is generated during cooling after hot rolling, and thus voids occur during wire drawing.
  • the content of Mn is more than 1.20%, the amount of retained austenite is excessive, and thus, the hardness of the bearing part is reduced.
  • the content of Mn is set to 0.20% to 1.20%.
  • the content of Mn is preferably 0.21% to 1.15%. More preferably, the content of Mn is 0.25% to 1.00%.
  • Cr Chromium
  • Cr is an element for improving the hardenability of the steel. Furthermore, Cr is an extremely effective element for promoting spheroidizing of carbide and for increasing the amount of carbide.
  • the content of Cr is less than 0.90%, the amount of solid-soluted C into austenite is increased, and excessive retained austenite is generated in the bearing part.
  • the content of Cr is more than 1.60%, dissolution of carbide is limited during quenching, and thus, the amount of retained austenite is reduced or the hardenability of the bearing part is reduced. Therefore, the content of Cr is set to 0.90% to 1.60%.
  • the content of Cr is preferably 0.91% to 1.55%. More preferably, the content of Cr is 1.10% to 1.50%. Most preferably, the content of Cr is 1.30% to 1.50%.
  • Al is an element which functions as a deoxidizer.
  • the content of Al is less than 0.010%, deoxidation becomes insufficient and oxide precipitates. As a result, the rolling contact fatigue life of the bearing part is reduced.
  • the content of Al is more than 0.100%, AlO-based inclusion are generated. As a result, the wire drawability of the steel for the bearing part is reduced or the rolling contact fatigue life of the bearing part is reduced. Therefore, the content of Al is set to 0.010% to 0.100%.
  • the content of Al is preferably 0.015% to 0.078%. More preferably, the content of Al is 0.018% to 0.050%.
  • N forms nitride with Al or B. These nitrides function as pinning particles, and thus, grains are refined. Therefore, N (Nitrogen) is an element which suppresses grain coarsening. When the content of N is less than 0.003%, this effect cannot be obtained. On the other hand, when the content of N is more than 0.030%, coarse inclusions are generated, and thus, the rolling contact fatigue life is reduced. Therefore, the content of N is set to 0.003% to 0.030%. In order to more reliably not lower the rolling contact fatigue life, the content of N is preferably 0.005% to 0.029%. More preferably, the content of N is 0.009% to 0.020%.
  • P Phosphorus
  • P is an impurity that is unavoidably included in steel.
  • the content of P is more than 0.025%, P segregates in an austenite grain boundary and embrittles an austenite grain boundary.
  • the rolling contact fatigue life of the bearing part is reduced. Therefore, it is necessary for the content of P to be limited to 0.025% or less.
  • the content of P may be limited to 0.020% or less, and more preferably limited to 0.015% or less.
  • the lower limit of the content of P may be set to 0.001%. Considering normal operating conditions, the content of P is preferably 0.004% to 0.012%.
  • S is an impurity that is unavoidably included in steel.
  • the content of S is more than 0.025%, coarse MnS forms, and thus, the rolling contact fatigue life of the bearing part is lowered. Therefore, it is necessary that the content of S is limited to 0.025% or less.
  • the content of S may be limited to 0.020% or less, and preferably limited to 0.015% or less. Since the content of S is desirably as small as possible, and thus, a case where the content of S is 0% is contained into the above limited range. However, controlling the content of S to be 0% is not technically easy. Therefore, from the viewpoint of steelmaking cost, the lower limit of the content of S may be set to 0.001%. Considering the normal operating conditions, the content of S is preferably 0.003% to 0.011%.
  • O Oxygen
  • Oxygen is an impurity that is unavoidably included in steel.
  • the content of O is more than 0.0010%, oxide inclusion forms, and thus, the rolling contact fatigue life of the bearing part is lowered. Therefore, it is necessary that the content of O is limited to 0.0010% or less. Since the content of O is desirably as small as possible, and thus, a case where the content of O is 0% is contained into the above limited range. However, controlling the content of O to be 0% is not technically easy. Therefore, from the viewpoint of steelmaking cost, the lower limit of the content of O may be set to 0.0001%. Considering the normal operating conditions, the content of O is preferably 0.0005% to 0.0010%.
  • the bearing part according to the present embodiment may optionally include at least one of the group consisting of Mo, B, Cu, Ni and Ca.
  • the group consisting of Mo, B, Cu, Ni and Ca one or more of Mo, B, Cu and Ni for improving the hardenability, and Ca for refining the inclusion can be selected.
  • the lower limits of these chemical elements are 0% and are not limited.
  • Mo is an element for improving the hardenability.
  • Mo has effects for improving grain boundary strength of the steel after quenching is performed and for enhancing the toughness of the steel. If it is desirable to more reliably secure the hardenability and toughness, the content of Mo is preferably set to 0.01% or more. However, when the content of Mo is more than 0.25%, these effects are saturated. Therefore, the content of Mo is preferably 0.01% to 0.25%. More preferably, the content of Mo is 0.01% to 0.23%. Even more preferably, the content of Mo is 0.10% to 0.23%.
  • B is an element for improving the hardenability, even if the content of B is small.
  • B also has effects for suppressing segregation of P or S at the austenite grain boundary during quenching. If it is desirable to obtain these effects, the content of B is preferably set to 0.0001% or more. However, when the content of B is more than 0.0050%, these effects are saturated. Therefore, the content of B is preferably 0.0001% to 0.0050%. More preferably, the content of B is 0.0003% to 0.0050%. Even more preferably, the content of B is 0.0005% to 0.0025%. Most preferably, the content of B is 0.0010% to 0.0025%.
  • Cu is an element for improving the hardenability. If it is desirable to more reliably secure the hardenability, the content of Cu is preferably set to 0.05% or more. However, when the content of Cu is more than 1.0%, this effect is saturated, furthermore, hot workability is deteriorated. Therefore, the content of Cu is preferably 0.05% to 1.0%. More preferably, the content of Cu is 0.10% to 0.50%. Even more preferably, the content of Cu is 0.19% to 0.31%.
  • Ni is an element for improving the hardenability.
  • Ni has an effect of improving the toughness of the steel after quenching is performed. If it is desirable to more reliably secure the hardenability and toughness, the content of Ni is preferably set to 0.05% or more. However, when the content of Ni is more than 3.0%, this effect is saturated. Therefore, the content of Ni is preferably 0.05% to 3.0%. More preferably, the content of Ni is 0.10% to 1.5%. Even more preferably, the content of Ni is 0.21% to 1.2%. Most preferably, the content of Ni is 0.21% to 1.0%.
  • Ca is an element that is solid-soluted into sulfide and forms CaS, and thus, refines the sulfide. If it is desirable to more improve the rolling contact fatigue life by refining the sulfide, the content of Ca is preferably set to 0.0003% or more. However, when the content of Ca is more than 0.0015%, this effect is saturated. Furthermore, since oxide inclusion coarsens, and it causes a lowering of the rolling contact fatigue life. Therefore, the content of Ca is preferably 0.0003% to 0.0015%. More preferably, the content of Ca is 0.0003% to 0.0011%. Even more preferably, the content of Ca is 0.0005% to 0.0011%.
  • the bearing part and the steel for the bearing part according to the present embodiment include the above described components, and the remainder of the chemical composition consists of substantially Fe and unavoidable impurities.
  • the metallographic structure of the bearing part according to the present embodiment is retained austenite, spherical cementite and martensite.
  • the amount of retained austenite is 18% to 25%, by volume %.
  • the average grain size of spherical cementite be 0.45 ⁇ m or less
  • the number density of spherical cementite be 0.45 ⁇ 10 6 mm ⁇ 2 or more.
  • the number density of spherical cementite is preferably 0.5 ⁇ 10 6 mm ⁇ 2 or more.
  • the upper limit of the number density of spherical cementite is not particularly limited; however, the upper limit of the number density of spherical cementite is preferably 1.0 ⁇ 10 6 mm ⁇ 2 in view of considering the constraints on production or securing the rolling contact fatigue life.
  • the average grain size of spherical cementite is reduced excessively, the effect for improving the rolling contact fatigue life is small, and it is difficult to produce them. Therefore, the average grain size of the spherical cementite of the bearing part is preferably 0.25 ⁇ m or more. That is, the preferred average grain size of spherical cementite of the bearing part according to the present embodiment is 0.25 ⁇ m to 0.45 ⁇ m.
  • the average grain size of spherical cementite can be obtained by the following method. Firstly, the bearing part is cut on the cross section (C cross section) perpendicular to the longitudinal direction in a center of a longitudinal direction of the bearing part. A range within a radius of 3 mm from a center of the C cross section is set to a center portion, and photographs are taken at the center portion using a SEM with 2000 times magnification. Next, the spherical cementite among the captured images is copied using the tracing sheet or the like; and the grain size of cementite is measured by image analyzing the tracing sheet. In addition, four visual fields are measured in each sample, and an average value of grain sizes of spherical cementite in the obtained four visual fields is set to the average grain size of spherical cementite.
  • the average grain size of prior-austenite of the bearing part according to the present embodiment is 6.0 ⁇ m or less.
  • the average grain size of prior-austenite is more than 6.0 ⁇ m, the necessary amount of retained austenite cannot be obtained.
  • the average grain size of prior-austenite of the bearing part is refined to less than 3.0 ⁇ m or less, the manufacturing load is increased. Therefore, the average grain size of prior-austenite of the bearing part is preferably 3.0 ⁇ m or more. That is, the average grain size of prior-austenite of the bearing part according to the present embodiment is preferably 3.0 ⁇ m to 6.0 ⁇ m.
  • the metallographic structure of the steel for the bearing part according to the present embodiment includes spherical cementite and ferrite.
  • the number density of spherical cementite having a grain size of 0.5 ⁇ m to 3.0 ⁇ m is 2.0 ⁇ 10 6 mm ⁇ 2 or more.
  • the number density of spherical cementite having a prescribed size in the steel for the bearing part is less than 2.0 ⁇ 10 6 mm ⁇ 2 , the spherical cementite of the bearing part after quenching and tempering is reduced and the rolling contact fatigue life of the bearing part is lowered.
  • the upper limit of the number density of spherical cementite is not particularly limited; however, the upper limit of the number density of spherical cementite is preferably 5.0 ⁇ 10 6 mm ⁇ 2 in view of considering the constraints on production or securing the rolling contact fatigue life.
  • the hot rolled wire rod has the same chemical composition as the bearing part. Then, it is preferable that the hot rolled wire rod has a metallographic structure consisting of pearlite and 5% or less of proeutectoid cementite by area ratio. When the hot rolled wire rod has supercooled structure such as martensite in the metallographic structure, it cannot be uniformly deformed during wire drawing. As a result, it may cause breaking wire. Therefore, it is preferable that the hot rolled wire rod does not include martensite and mainly include pearlite as the microstructure.
  • the size of the pearlite block has a very strong correlation with ductility.
  • the wire drawability can be improved by refining the pearlite. Therefore, it is preferable that the average grain size of the pearlite block (circle equivalent diameter) be 15 ⁇ m or less.
  • the grain size of the pearlite block is preferably 1 ⁇ m to 15 ⁇ m. More preferably, the grain size of the pearlite block is 1 ⁇ m to 10 ⁇ m.
  • the average grain size of the pearlite block (circle equivalent diameter) can be measured with an electron backscatter diffraction apparatus (EBSD).
  • EBSD electron backscatter diffraction apparatus
  • the proeutectoid cementite generally has little plastic deformability. Therefore, the proeutectoid cementite is divided by wire drawing, and it results in formation of voids.
  • the proeutectoid cementite be 5% or less by area ratio and the thickness of the proeutectoid cementite be 1.0 ⁇ m or less. More preferably, the proeutectoid cementite is 3% or less by area ratio and the thickness of the proeutectoid cementite is 0.8 ⁇ m or less.
  • the area ratio of the proeutectoid cementite and the thickness of the proeutectoid cementite can be measured by observation with SEM.
  • the bearing part When the above described chemical composition and metallographic structure are satisfied, a bearing part having an excellent rolling contact fatigue life can be obtained even in a contaminated environment.
  • the bearing part may be produced by the manufacturing method, which will be described later.
  • a bearing part according to the present embodiment can be manufactured as follows.
  • the method for producing a bearing part, steel for a bearing part which is a material for a bearing part and the method for producing a hot rolled wire rod which is a material for steel for a bearing part as described below are examples to obtain a bearing part according to the present invention; and the present invention is not limited to the following procedures and methods. As long as the method can realize the configuration of the present invention, it is possible to adopt any methods.
  • Normal manufacturing conditions can be employed as a method for producing a hot rolled wire rod which is a material for steel for a bearing part.
  • steel having the chemical composition adjusted in the usual manner is melted and casted, and then, the steel is subjected to soaking treatment and blooming as needed, to form a billet. Next, the obtained billet is heated and is subjected to hot rolling. Then, after the hot rolled steel is annularly wound, the wound steel is cooled.
  • the hot rolled wire rod which is the material for the steel for the bearing part according to the present embodiment can be manufactured through the above processes.
  • the method for casting is not particularly limited, and a vacuum casting, a continuous casting or the like may be used.
  • the soaking treatment (soaking diffusion treatment), to which cast piece after the casting process is subjected as needed, is a heat treatment for reducing segregation which the casting or the like causes.
  • the steel piece obtained through these processes is commonly referred to as a billet.
  • a heating temperature during the soaking treatment is preferably 1100° C. to 1200° C.
  • a holding time of the soaking treatment is preferably 10 hours to 20 hours.
  • the heating temperature of the billet is preferably set to 900° C. to 1300° C.
  • a finish rolling temperature is preferably set to 850° C. or less.
  • the finish rolling temperature is 850° C. or less
  • the proeutectoid cementite is dispersed and precipitated.
  • the thickness of the proeutectoid cementite can be reduced.
  • the finish rolling temperature is 850° C. or less
  • a nucleation site of pearlite is increased during a transformation.
  • the pearlite block can be refined.
  • the finish rolling temperature is 800° C. or less.
  • the finish rolling temperature is preferably 650° C. or more.
  • a temperature of the billet during the hot rolling can be measured with radiation thermometer.
  • Steel which has passed through the hot rolling process and is a material for steel for a bearing part, that is, steel after the finish rolling is commonly referred to as the hot rolled wire rod.
  • the hot rolled wire rod is annularly wound at a temperature of 800° C. or less. This process is commonly referred to as the winding process.
  • the winding temperature is preferably 800° C. or less. More preferably, the winding temperature is 770° C. or less. On the other hand, when the winding temperature is less than 650° C., there is a case where the wire breakage occurs. Therefore, the winding temperature is preferably 650° C. or more.
  • the rolled wire rod is cooled to 600° C. This process is commonly referred to as the cooling process.
  • the cooling rate to 600° C. is preferably set to 0.5° C./s to 3.0° C./s.
  • the cooling rate after winding influences the transformation to pearlite from austenite. Therefore, in order to suppress the precipitation of the supercooled structure such as martensite or bainite, the cooling rate after winding is preferably 3.0° C./s or less. More preferably, the cooling rate after winding is 2.3° C./s or less. On the other hand, there is a case where the cooling rate after winding also influences the precipitation of proeutectoid cementite.
  • the cooling rate after winding is preferably 0.5° C./s or more. More preferably, the cooling rate after winding is 0.8° C./s or more.
  • steel for a bearing part does not have the spheroidizing annealing process before the wire drawing. That is, the hot rolled wire rod obtained through the above processes is not subjected to the spheroidizing annealing and is subjected to the wire drawing in which the total reduction of area is 50% or more. Then, after the wire drawing, the spheroidizing annealing is performed at a temperature of 650° C. to the lower of 750° C. and A 1 ⁇ 5° C.; thereby, the steel for the bearing part is manufactured.
  • the bearing part is obtained by performing the quenching and the tempering.
  • the hot rolled wire rod which is a material for the steel for the bearing part is subjected to the wire drawing in which the total reduction of area is 50% or more, spheroidizing of the cementite is promoted during the spheroidizing annealing because of introduced strain. Therefore, the cementite is spheroidized at a low temperature in a short time; the average grain size of spherical cementite of the steel for the bearing part can be refined and the number density of spherical cementite in the steel for the bearing part can be larger. Since the steel for the bearing part manufactured in this manner has a sufficient amount of spherical cementite, the average grain size of austenite can be refined during quenching. Then, when the average grain size of austenite is refined, the amount of retained austenite of the bearing part can be secured and the grain size of the prior-austenite of the bearing part can be refined.
  • the total reduction of area is less than 50%, a prescribed amount of retained austenite cannot be secured in the steel for the bearing part.
  • the prior-austenite of the bearing part cannot be refined due to insufficient spheroidizing of cementite.
  • the total reduction of area is preferably set to 50% to 97%.
  • a heating temperature of the spheroidizing annealing after the wire drawing is set to less than 750° C. and to A 1 ⁇ 5° C. or less in order to increase the number density of spherical cementite in the steel for the bearing part.
  • the number of times of the spheroidizing annealing is set to one.
  • the spheroidizing annealing is performed at a high temperature that is 750° C. or more or more than A 1 ⁇ 5° C.
  • the number density of spherical cementite in the steel for the bearing part is lowered.
  • transformation to austenite is started in the steel for the bearing part, there is a case where changes in wire diameter become larger. Therefore, it is preferably heated at a temperature of 750° C. or A 1 ⁇ 5° C., whichever is less.
  • the heating temperature of the spheroidizing annealing after the wire drawing is less than 650° C.
  • the cementite is spheroidized in the steel for the bearing part insufficiently, and thus, the cementite remains as the pearlite. Therefore, since grain size of austenite is coarsened during quenching and the hardness is increased, and there is a concern that workability of the bearing part is reduced. Accordingly, the heating temperature of the spheroidizing annealing after the wire drawing is preferably 650° C. or more.
  • the heating temperature of the spheroidizing annealing is a temperature of 650° C. to the lower of 750° C. and A 1 ⁇ 5° C.
  • a 1 means a temperature at which A 1 transformation starts and unit thereof is Celsius degree (° C.). Furthermore, A 1 can be calculated simply by the following equation 1 based on the chemical components.
  • [C], [Si], [Mn], [Cu], [Ni], [Cr], [Mo], [Al] and [B] in the equation represent, by mass %, the content of C, the content of Si the content of Mn, the content of Cu, the content of Ni, the content of Cr, the content of Mo, the content of Al and the content of B in the hot rolled wire rod, respectively.
  • the holding time is less than 0.5 hours, spheroidizing is insufficient.
  • the holding time is more than 5 hours, there is a case where the number density of prescribed spherical cementite is reduced.
  • the steel for the bearing part after the spheroidizing annealing is formed (rough formed), and then the quenching is performed.
  • the heating temperature of quenching in the quenching after the spheroidizing annealing is preferably set to 820° C. or more so that a certain amount of cementite can be solid-soluted into the austenite.
  • the heating temperature of the quenching is less than 820° C., the cementite is not solid-soluted into the austenite sufficiently, and thus, there is a case where hardness of the bearing part is reduced.
  • the heating temperature of the quenching is more than 890° C., there is a concern that the average grain size of the prior-austenite in the bearing part coarsens. Therefore, the heating temperature of the quenching is preferably set to 820° C. to 890° C.
  • a holding time in the quenching is preferably 0.5 hours to 2 hours.
  • the holding time is less than 0.5 hours, the cementite is not solid-soluted into the austenite sufficiently.
  • the holding time is more than 2 hours, the cementite is resolved and C is solid-soluted into the austenite excessively.
  • the retained austenite of the bearing part may be increased, or the average grain size of the prior-austenite of the bearing part may be coarsened.
  • a tempering temperature in the tempering is preferably 150° C. or more in order to secure the toughness and adjust the hardness.
  • the tempering temperature is less than 150° C., there is a case where the toughness of the bearing part cannot be secured.
  • the tempering temperature is more than 250° C., the hardness of the bearing part is lowered, and there is a concern that the rolling contact fatigue life is reduced. Therefore, the tempering temperature is preferably set to 150° C. to 250° C.
  • a holding time in the tempering is preferably 0.5 hours to 3 hours.
  • the holding time is less than 0.5 hours, there is a case where the toughness of the bearing part is not secured. Even when the tempering is performed for more than 3 hours, properties are not changed, and thus, only productivity is reduced.
  • the finish machining is subjected to the steel for the bearing part after the tempering; therefore the bearing part can be obtained.
  • the metallographic structure of the bearing part and the metallographic structure of the steel for the bearing part can be within the scope of the present invention.
  • hot rolled wire rods having microstructure shown in Table 2-1 and Table 2-2 were obtained.
  • the hot rolled wire rods were subjected to cold wire drawing until diameters were ⁇ 10 mm.
  • the hot rolled wire rods obtained by the wire drawing were cut (into lengths of 10 mm) so that the length in the longitudinal direction was 10 mm.
  • the hot rolled wire rods obtained by cutting were subjected to the spheroidizing annealing at spheroidizing temperature as shown in Table 2-1 and Table 2-2 for 0.5 hours to 3 hours, and thereby they were adjusted to the microstructures including spherical cementite and ferrite.
  • steels for bearing parts were obtained.
  • the steels for bearing parts were formed into sphere types of ⁇ 9.5 mm.
  • the steels for bearing parts were subjected to the finish machining; thereby manufacturing the bearing parts.
  • the quenching was performed at the quenching temperature as shown in Table 2-1 and Table 2-2, in which the holding time of the quenching was 60 minutes, and the cooling was oil cooling.
  • the tempering was performed at the tempering temperature as shown in Table 2-1 and Table 2-2, and the holding time of the tempering was 90 minutes.
  • Table 2 The structures of the hot rolled wire rods, the reduction of area during the wire drawing, the temperatures of the quenching and the tempering are shown in Table 2.
  • the microstructures of the hot rolled wire rods, the microstructures of the steels for bearing parts and the bearing parts were evaluated using an optical microscope. Then, the average grain size of prior-austenite (m) of the bearing parts was measured using a SEM. In addition, the measurements of the average grain size of spherical cementite ( ⁇ m) of the steels for bearing parts and the bearing parts, and the measurements of the number density of spherical cementite (mm ⁇ 2 ) in the steels for bearing parts and the bearing parts were carried out using a SEM. In addition, the measurement of the amount of retained austenite (volume %) of the bearing parts was carried out using X-ray diffraction method.
  • the measurement of the rolling contact fatigue life of the bearing parts was carried out using a radial type fatigue testing machine.
  • Normal rolling contact fatigue life of the bearing parts was tested in an environment including only lubricating oil. Furthermore, rolling contact fatigue life of the bearing parts was measured in a contaminated environment where 1 g of an iron powder having a hardness of 750 Hv to 800 Hv and a particle size of 100 ⁇ m to 180 ⁇ m was mixed into 1 L of lubricating oil. Then, life of the cumulative failure probability of 10% was obtained using the measured rolling contact fatigue life with Weibull statistical analysis. The rolling contact fatigue life in a normal and contaminated environment was based on the life of B1, which has the same component as SUJ2, manufactured in the current production method, and it was expressed by the ratio to the life of B1, in Table 2-1 and Table 2-2.
  • the evaluation results of the microstructures of the materials, the producing method, the microstructures of the bearing parts and the rolling contact fatigue life are shown in Table 2-1 and Table 2-2.
  • A1 to A19 are within the appropriate range of the present invention in the Table 1-1 and Table 2-1; the ratio of the normal rolling contact fatigue life is 1.5 times or more of the B1, the rolling contact fatigue life in a contaminated environment is 2 times or more of the B1, and thus, A1 to A19 have an excellent rolling contact fatigue life.
  • All of the metallographic structures of the steels for the bearing part consisted of spherical cementite and ferrite in examples of the present invention.
  • all of the metallographic structures of the bearing parts consisted of spherical cementite and martensite.
  • A20 to A38, B1 and B2 are Comparative Examples. Since Comparative Examples of A20 to A38, B1 and B2 failed to satisfy one or both of the chemical composition and microstructures of the bearing parts, which are defined by the present invention, the rolling contact fatigue life was equivalent to a conventional bearing part, or inferior to a conventional bearing part.
  • the chemical compositions of A20 to A31 were out of the scope of the present invention. Since the content of C was small in A20, the number density of spherical cementite in the steel for the bearing part was lowered. Therefore, since the average grain size of austenite was coarsened during quenching and the amount of retained austenite was insufficient, the rolling contact fatigue life of the bearing part in the contaminated environment was lowered. In addition, since the content of C was small, the number density of the spherical cementite in the bearing part was also insufficient. When the content of C was small, the strength during quenching was also low, and thus, the rolling contact fatigue life even under the normal conditions was lowered. On the other hand, the content of C was excessive in A21. Therefore, since the amount of retained austenite and the average grain size of the spherical cementite were excessive, the normal rolling contact fatigue life was not improved.
  • the content of Mn was excessive in A23. Therefore, since cracks occurred during wire drawing due to martensite of the steel for the bearing part, both the normal rolling contact fatigue life and the rolling contact fatigue life in the contaminated environment were lowered in the bearing part. Furthermore, since wire drawability was lowered, enough amount of wire drawing could not be secured. Therefore, the number density of the spherical cementite during the spheroidizing annealing was lowered. Accordingly, since sufficient pinning effect could not be ensured, the average grain size of austenite was coarsened during the quenching. In addition, since the spherical cementite of the steel for the bearing part was few, the number density of the spherical cementite in the bearing part after quenching was insufficient.
  • the content of Si was excessive in A22, the content of Al was excessive in A26 and the content of O was excessive in A30. Due to inclusions, both the normal rolling contact fatigue life and the rolling contact fatigue life in the contaminated environment were inferior to those of the conventional, in A22, A26 and A30. Since the content of S was excessive in A28, both the normal rolling contact fatigue life and the rolling contact fatigue life in the contaminated environment were inferior to those of the conventional due to sulfide. Since the content of N was excessive in A31, both the normal rolling contact fatigue life and the rolling contact fatigue life in the contaminated environment were inferior to those of the conventional due to nitride. Since the content of P was excessive in A29, grain boundary was embrittled. Therefore, both the normal rolling contact fatigue life and the rolling contact fatigue life in the contaminated environment were lowered in A29.
  • 131 and 132 are the current materials in which the spheroidizing annealing was performed before the wire drawing.
  • the number density of the spherical cementite in the steel for the bearing part was small. Therefore, the average grain size of austenite was coarsened during the quenching and the amount of retained austenite was decreased. As a result, the number density of the spherical cementite in the bearing part was lowered. Then, in the B1, the rolling contact fatigue life in the contaminated environment was low. In addition, since the content of Mn is increased in B2, the amount of retained austenite was increased compared with the B1. However, since the number density of the spherical cementite in the bearing part was small, the normal rolling contact fatigue property was insufficient.
  • a bearing part can be obtained by suppressing the content of Mn and by shortening spheroidizing annealing in order to secure good wire drawability.
  • the present invention is highly applicable to industries.

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Mechanical Engineering (AREA)
  • Metallurgy (AREA)
  • Materials Engineering (AREA)
  • Organic Chemistry (AREA)
  • General Engineering & Computer Science (AREA)
  • Physics & Mathematics (AREA)
  • Thermal Sciences (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Manufacturing & Machinery (AREA)
  • Rolling Contact Bearings (AREA)
  • Heat Treatment Of Steel (AREA)
  • Heat Treatment Of Strip Materials And Filament Materials (AREA)
  • Heat Treatment Of Articles (AREA)
US15/110,351 2014-01-10 2015-01-09 Bearing part, steel for bearing part and method for producing thereof Abandoned US20160333437A1 (en)

Applications Claiming Priority (5)

Application Number Priority Date Filing Date Title
JP2014-003338 2014-01-10
JP2014003338 2014-01-10
JP2014-084952 2014-04-16
JP2014084952 2014-04-16
PCT/JP2015/050528 WO2015105186A1 (ja) 2014-01-10 2015-01-09 軸受部品、軸受部品用鋼材及びそれらの製造方法

Publications (1)

Publication Number Publication Date
US20160333437A1 true US20160333437A1 (en) 2016-11-17

Family

ID=53524009

Family Applications (2)

Application Number Title Priority Date Filing Date
US15/110,390 Expired - Fee Related US10246757B2 (en) 2014-01-10 2015-01-09 Bearing part
US15/110,351 Abandoned US20160333437A1 (en) 2014-01-10 2015-01-09 Bearing part, steel for bearing part and method for producing thereof

Family Applications Before (1)

Application Number Title Priority Date Filing Date
US15/110,390 Expired - Fee Related US10246757B2 (en) 2014-01-10 2015-01-09 Bearing part

Country Status (8)

Country Link
US (2) US10246757B2 (ko)
EP (2) EP3093363B1 (ko)
JP (2) JP6079903B2 (ko)
KR (2) KR101826458B1 (ko)
CN (2) CN105899704B (ko)
PL (2) PL3093363T3 (ko)
SG (2) SG11201605568SA (ko)
WO (2) WO2015105187A1 (ko)

Families Citing this family (17)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP6703385B2 (ja) * 2015-09-18 2020-06-03 国立大学法人大阪大学 高硬度かつ靭性に優れた鋼
KR101664193B1 (ko) * 2015-12-11 2016-10-11 주식회사 세아베스틸 오스템퍼링 열처리를 이용한 고수명의 베어링용 강의 제조방법
CN105782245A (zh) * 2016-02-26 2016-07-20 惠州市金力电机有限公司 一种不锈钢基粉末冶金含油轴承
JP6472146B2 (ja) * 2017-01-31 2019-02-20 山陽特殊製鋼株式会社 高硬度かつ靭性に優れる鋼製部材および高負荷ボールねじのナット
JP6827914B2 (ja) * 2017-12-18 2021-02-10 Ntn株式会社 軸受部品及び転がり軸受
JP6843786B2 (ja) * 2017-03-03 2021-03-17 Ntn株式会社 軸受部品及び転がり軸受、ならびに軸受部品の製造方法
CN110494584A (zh) 2017-03-03 2019-11-22 Ntn株式会社 轴承部件、滚动轴承、和轴承部件的制造方法
CN108559913A (zh) * 2018-05-16 2018-09-21 浙江健力股份有限公司 一种GCr15轴承钢管及其制备工艺
KR102704263B1 (ko) * 2019-06-03 2024-09-09 현대자동차주식회사 고탄소 베어링강의 제조방법 및 이로부터 제조된 고탄소 베어링강
JP7422527B2 (ja) * 2019-12-05 2024-01-26 日本製鉄株式会社 転動部品及びその製造方法
KR102421642B1 (ko) * 2019-12-20 2022-07-18 주식회사 포스코 베어링용 선재 및 이의 제조방법
JP7464821B2 (ja) * 2020-02-14 2024-04-10 日本製鉄株式会社 軸受軌道用鋼材、および軸受軌道
US20240035515A1 (en) * 2020-09-24 2024-02-01 Ntn Corporation Bearing part and rolling bearing
CN114134403B (zh) * 2021-05-19 2023-01-13 江阴兴澄特种钢铁有限公司 一种大规格风电轴承滚动体用钢及其生产方法
KR20220169272A (ko) * 2021-06-18 2022-12-27 주식회사 포스코 신선 가공성이 우수한 선재 및 그 제조방법
CN113755755A (zh) * 2021-08-30 2021-12-07 西安交通大学 用于高速精密轴承的超高碳轴承钢材料及其制备方法和应用
CN114790531A (zh) * 2022-05-09 2022-07-26 中科西王特钢有限公司 一种风电主轴轴承用钢

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2007224410A (ja) * 2006-01-24 2007-09-06 Kobe Steel Ltd 伸線性に優れた軸受鋼線材およびその製造方法
US20070277913A1 (en) * 2006-06-06 2007-12-06 Kabushiki Kaisha Kobe Seiko Sho (Kobe Steel, Ltd.) Wire rod excellent in wire-drawing workability and method for producing same
US7763124B2 (en) * 2003-04-16 2010-07-27 Jfe Steel Corporation Steel material with excellent rolling fatigue life and method of producing the same
JP2012201984A (ja) * 2011-03-28 2012-10-22 Kobe Steel Ltd 冷間鍛造性およびねじり強度に優れた高周波焼入れ用鋼、およびその製造方法

Family Cites Families (12)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH07127643A (ja) 1993-10-29 1995-05-16 Nippon Seiko Kk 転がり軸受
JP2001234286A (ja) 2000-02-24 2001-08-28 Nippon Steel Corp 伸線加工性に優れた細径高炭素低合金鋼熱間圧延線材とその製造方法
JP3463651B2 (ja) * 2000-04-18 2003-11-05 住友金属工業株式会社 軸受用鋼材
JP3889931B2 (ja) 2001-01-26 2007-03-07 Ｊｆｅスチール株式会社 軸受材料
JP3949926B2 (ja) 2001-10-16 2007-07-25 株式会社神戸製鋼所 伸線前の熱処理が省略可能な伸線加工性に優れた線状または棒状鋼、および軸受部品
JP4008320B2 (ja) 2002-09-12 2007-11-14 株式会社神戸製鋼所 軸受用圧延線材および伸線材
JP2004124215A (ja) 2002-10-04 2004-04-22 Daido Steel Co Ltd 異物混入環境下での転動寿命に優れた軸受用鋼
JP4487748B2 (ja) 2004-11-30 2010-06-23 Ｊｆｅスチール株式会社 軸受部品の製造方法
JP4569961B2 (ja) 2005-09-13 2010-10-27 山陽特殊製鋼株式会社 ボールネジまたはワンウェイクラッチ用部品の製造方法
JP5292897B2 (ja) * 2008-03-31 2013-09-18 Ｊｆｅスチール株式会社 異物環境下での疲労特性に優れた軸受部品およびその製造方法
WO2013108828A1 (ja) * 2012-01-20 2013-07-25 新日鐵住金株式会社 圧延線材、及びその製造方法
CN103320704B (zh) * 2013-07-12 2015-02-04 安徽工业大学 一种高性能的轴承钢的生产方法

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US7763124B2 (en) * 2003-04-16 2010-07-27 Jfe Steel Corporation Steel material with excellent rolling fatigue life and method of producing the same
JP2007224410A (ja) * 2006-01-24 2007-09-06 Kobe Steel Ltd 伸線性に優れた軸受鋼線材およびその製造方法
US20070277913A1 (en) * 2006-06-06 2007-12-06 Kabushiki Kaisha Kobe Seiko Sho (Kobe Steel, Ltd.) Wire rod excellent in wire-drawing workability and method for producing same
JP2012201984A (ja) * 2011-03-28 2012-10-22 Kobe Steel Ltd 冷間鍛造性およびねじり強度に優れた高周波焼入れ用鋼、およびその製造方法

Also Published As

Publication number Publication date
EP3093363B1 (en) 2019-07-10
KR20160099671A (ko) 2016-08-22
CN105899703A (zh) 2016-08-24
CN105899704A (zh) 2016-08-24
JPWO2015105186A1 (ja) 2017-03-23
EP3093363A1 (en) 2016-11-16
JP6079903B2 (ja) 2017-02-15
WO2015105186A1 (ja) 2015-07-16
KR20160101133A (ko) 2016-08-24
EP3093361A4 (en) 2017-11-22
EP3093361B1 (en) 2019-07-17
EP3093361A1 (en) 2016-11-16
US10246757B2 (en) 2019-04-02
EP3093363A4 (en) 2017-11-22
US20160333438A1 (en) 2016-11-17
CN105899704B (zh) 2017-12-22
KR101826457B1 (ko) 2018-02-06
JP6079904B2 (ja) 2017-02-15
WO2015105187A1 (ja) 2015-07-16
CN105899703B (zh) 2017-09-08
SG11201605568SA (en) 2016-08-30
PL3093363T3 (pl) 2019-12-31
SG11201605570XA (en) 2016-08-30
PL3093361T3 (pl) 2020-03-31
KR101826458B1 (ko) 2018-02-06
JPWO2015105187A1 (ja) 2017-03-23

Similar Documents

Publication Publication Date Title
US20160333437A1 (en) Bearing part, steel for bearing part and method for producing thereof
US9598752B2 (en) Bearing steel
KR101599163B1 (ko) 비조질 기계 부품용 선재, 비조질 기계 부품용 강선 및 비조질 기계 부품과 그들의 제조 방법
JP5026626B2 (ja) 冷間鍛造性に優れた鋼線及びその製造方法
JP5257082B2 (ja) 低温焼鈍後の冷間鍛造性に優れた鋼線材及びその製造方法並びに冷間鍛造性に優れた鋼線材の製造方法
US20100212786A1 (en) High-Strength Steel Wire Excellent In Ductility and Method of Manufacturing the Same
US10597748B2 (en) Steel wire rod for wire drawing
KR20120118059A (ko) 내지연파괴 특성이 우수한 고강도 강재와 고강도 볼트 및 그 제조 방법
JP5590256B2 (ja) 圧延線材、及びその製造方法
JP3851095B2 (ja) 高強度ばね用熱処理鋼線
JP5391711B2 (ja) 高炭素パーライト系レールの熱処理方法
KR102154575B1 (ko) 선재, 강선 및 부품
JP2010150566A (ja) 真空浸炭または真空浸炭窒化用の鋼材
JP2009275250A (ja) 冷間加工性に優れた鋼線材およびその製造方法
CN111601908A (zh) 渗碳轴承钢部件及渗碳轴承钢部件用棒钢
JP6226082B2 (ja) 伸線加工性および伸線加工後のコイル成形性に優れた軸受用鋼線材
EP3279357A1 (en) Heat-treated steel wire having excellent fatigue-resistance characteristics
EP3483293A1 (en) Rolled wire rod
JP2006299313A (ja) 転がり支持装置
JP5976581B2 (ja) 転動疲労特性に優れた軸受用鋼材、および軸受部品
JPWO2017069064A1 (ja) 機械構造用鋼及び高周波焼入鋼部品
KR20240151817A (ko) 강재
KR20240146676A (ko) 강재

Legal Events

Date Code Title Description
AS Assignment

Owner name: NIPPON STEEL & SUMITOMO METAL CORPORATION, JAPAN

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:SAKAMOTO, MASASHI;KODAMA, JUNICHI;NEISHI, YUTAKA;REEL/FRAME:039106/0564

Effective date: 20160705

STPP Information on status: patent application and granting procedure in general

Free format text: NON FINAL ACTION MAILED

AS Assignment

Owner name: NIPPON STEEL CORPORATION, JAPAN

Free format text: CHANGE OF NAME;ASSIGNOR:NIPPON STEEL & SUMITOMO METAL CORPORATION;REEL/FRAME:049257/0828

Effective date: 20190401

STPP Information on status: patent application and granting procedure in general

Free format text: FINAL REJECTION MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: ADVISORY ACTION MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: DOCKETED NEW CASE - READY FOR EXAMINATION

STPP Information on status: patent application and granting procedure in general

Free format text: NON FINAL ACTION MAILED

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION