US20140141263A1 - Biocidal foul release coating systems - Google Patents
Biocidal foul release coating systems Download PDFInfo
- Publication number
- US20140141263A1 US20140141263A1 US14/126,226 US201214126226A US2014141263A1 US 20140141263 A1 US20140141263 A1 US 20140141263A1 US 201214126226 A US201214126226 A US 201214126226A US 2014141263 A1 US2014141263 A1 US 2014141263A1
- Authority
- US
- United States
- Prior art keywords
- biocide
- coating layer
- coating
- structure according
- subsequent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Links
- 0 [1*][Si]([2*])([2*])O[Si]([1*])([3*])O[Si]([3*])([4*])O[Si]([1*])([2*])[2*] Chemical compound [1*][Si]([2*])([2*])O[Si]([1*])([3*])O[Si]([3*])([4*])O[Si]([1*])([2*])[2*] 0.000 description 1
Classifications
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B63—SHIPS OR OTHER WATERBORNE VESSELS; RELATED EQUIPMENT
- B63B—SHIPS OR OTHER WATERBORNE VESSELS; EQUIPMENT FOR SHIPPING
- B63B59/00—Hull protection specially adapted for vessels; Cleaning devices specially adapted for vessels
- B63B59/04—Preventing hull fouling
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
- C09D5/00—Coating compositions, e.g. paints, varnishes or lacquers, characterised by their physical nature or the effects produced; Filling pastes
- C09D5/14—Paints containing biocides, e.g. fungicides, insecticides or pesticides
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
- C09D5/00—Coating compositions, e.g. paints, varnishes or lacquers, characterised by their physical nature or the effects produced; Filling pastes
- C09D5/16—Antifouling paints; Underwater paints
- C09D5/1606—Antifouling paints; Underwater paints characterised by the anti-fouling agent
- C09D5/1612—Non-macromolecular compounds
- C09D5/1625—Non-macromolecular compounds organic
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B05—SPRAYING OR ATOMISING IN GENERAL; APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
- B05D—PROCESSES FOR APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
- B05D1/00—Processes for applying liquids or other fluent materials
- B05D1/36—Successively applying liquids or other fluent materials, e.g. without intermediate treatment
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
- C09D183/00—Coating compositions based on macromolecular compounds obtained by reactions forming in the main chain of the macromolecule a linkage containing silicon, with or without sulfur, nitrogen, oxygen, or carbon only; Coating compositions based on derivatives of such polymers
- C09D183/04—Polysiloxanes
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
- C09D5/00—Coating compositions, e.g. paints, varnishes or lacquers, characterised by their physical nature or the effects produced; Filling pastes
- C09D5/08—Anti-corrosive paints
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
- C09D5/00—Coating compositions, e.g. paints, varnishes or lacquers, characterised by their physical nature or the effects produced; Filling pastes
- C09D5/16—Antifouling paints; Underwater paints
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
- C09D5/00—Coating compositions, e.g. paints, varnishes or lacquers, characterised by their physical nature or the effects produced; Filling pastes
- C09D5/16—Antifouling paints; Underwater paints
- C09D5/1656—Antifouling paints; Underwater paints characterised by the film-forming substance
- C09D5/1662—Synthetic film-forming substance
- C09D5/1675—Polyorganosiloxane-containing compositions
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
- C09D5/00—Coating compositions, e.g. paints, varnishes or lacquers, characterised by their physical nature or the effects produced; Filling pastes
- C09D5/16—Antifouling paints; Underwater paints
- C09D5/1693—Antifouling paints; Underwater paints as part of a multilayer system
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
- Y10T428/00—Stock material or miscellaneous articles
- Y10T428/31504—Composite [nonstructural laminate]
- Y10T428/31652—Of asbestos
- Y10T428/31663—As siloxane, silicone or silane
Definitions
- the present invention relates to the use of a foul release coating to control the leaching of biocide from a coating system comprising said foul release coating and a biocidal underlying coating.
- the present invention further relates to such a coating system, its use in inhibiting fouling on a substrate and a substrate coated with the coating system.
- Man-made marine structures such as ship and boat hulls, buoys, drilling platforms, dry dock equipment, oil production rigs, and pipes which are immersed in water are prone to fouling by aquatic organisms such as green and brown algae, barnacles, mussels, and the like.
- aquatic organisms such as green and brown algae, barnacles, mussels, and the like.
- Such structures are commonly of metal, but may also comprise other structural materials such as concrete. This fouling is a nuisance on boat hulls, because it increases frictional resistance during movement through the water, the consequence being reduced speeds and increased fuel costs.
- Fouling has been inhibited traditionally by antifouling paints containing a biocide, which biocide is gradually leached from the paint.
- the commercially most successful methods of inhibiting fouling have involved the use of antifouling coatings containing substances toxic to aquatic life, for example triorganotin compounds.
- Such coatings are being regarded with increasing disfavour because of the damaging effects some such toxins may have if released into the aquatic environment under certain circumstances.
- barnacle adhesion values have been recorded by this method: Silicone surface (0.05 MPa), Polypropylene surface (0.85 MPa), Polycarbonate surface (0.96 MPa), Epoxy surface (1.52 MPa) and Urethane surface (1.53 MPa) (J.C. Lewthwaite, A. F. Molland and K. W. Thomas, “An Investigation into the variation of ship skin fictional resistance with fouling”, Trans. R.I.N.A., Vol. 127, pp. 269-284, London (1984)).
- a foul-release coating usually has a mean barnacle adhesion value of less than 0.4 MPa.
- Silicone rubbers and silicone compounds generally have very low toxicity.
- a disadvantage of this foul release system when applied to boat hulls is that although the accumulation of fouling organisms is reduced, relatively high vessel speeds are needed to remove all fouling species. Thus, in some instances, it has been shown that it is necessary to sail with a speed of at least 10 knots to satisfactorily remove fouling from a hull that has been treated with such a coating. For this reason silicone rubbers have so far gained only limited commercial success.
- a suitable tie-coat with a second coating layer is sometimes referred to as a ‘duplex’ foul release system.
- the compositions described in the prior-art for use as the tie-coat in such duplex systems are generally free of added biocides and WO2008/013825 explicitly teaches away from using biocides as part of their systems.
- GB1409048 discloses a marine polyurethane top coat composition capable of imbibing 30 to 300% of its own weight of seawater which is applied over a biocidal antifouling coating.
- the polyurethane top coat of GB1409048 is not foul release coating within the context of the present invention (see: ‘Redefining antifouling coatings’, Journal of Protective Coatings and Linings, September 1999, pages 26-35 which discloses that polyurethanes have extremely high barnacle adhesion strengths in comparison to silicones). No subsequent foul release coating layer is disclosed or suggested in GB1409048.
- EP 0 313 233 describes an antifouling marine coating comprising a first layer of anti-fouling corrosion-resisting marine paint containing a toxicant to marine organisms and a second layer of porous organic polymeric membrane adhered to said first layer; the porous organic polymeric membrane preferably being polytetrafluoroethylene (EPTFE).
- EPTFE polytetrafluoroethylene
- a porous organic polymeric membrane is not a coating in the context of the present invention since is not applied as a liquid mixture which then dries or cures to form a dry continuous film.
- polytetrafluoroethylene is a material that is unsuitable for use as a foul release surface (see: the above-noted ‘Redefining antifouling coatings’ which indicates a high barnacle adhesion strength).
- the use of a subsequent foul release coating layer is neither disclosed nor suggested in EP 0 313 233.
- U.S. Pat. No. 4,129,610 describes a water soluble coating composition for ship bottoms comprising a vinyl copolymer and a water-soluble epoxy compound. The water soluble coating composition is applied on a primer coating layer having a toxic material.
- the water soluble coating composition of U.S. Pat. No. 4,129,610 is not considered a foul release coating within the context of the present invention (see the above-noted ‘Redefining antifouling coatings’ article which reports the barnacle adhesion strength of epoxy coatings is extremely high). The use of a subsequent foul release coating layer is neither disclosed nor suggested.
- FR2636958 describes a chlorinated adhesion primer for a silicone elastomer.
- a triorganotin oxide or halide biocide or copper oxide may be added to the primer.
- Tributyl tin oxide or fluoride and copper oxide are the only mentioned suitable biocide additives to such a system and there is no example or further description of a primer containing any biocide.
- the document is completely silent on leaching of biocide and there is no enabling teaching of a foul release system with a primer that contains any biocide.
- WO95/32862 discloses a duplex foul release system which can be used on a substrate for countering fouling by marine organisms.
- the duplex system consists of a bonding layer and a release layer wherein a 3-isothiazolone biocide is embedded in either the bonding layer or release layer.
- the document teaches exclusively that 3-isothiazolones should be used as the biocide and that the leaching rate of the biocide from the bonding layer is inversely proportional to the square root of time, and no other factors control the leaching rate other than potentially the solubility of the biocide in water.
- the leaching of biocide is therefore only poorly controlled in such systems and does not qualify as a biocidal foul release coating system having a controlled leaching rate of the biocide within the framework of the present invention. It was found that substrates coated with systems, like the one disclosed in WO 95/32862 where the leaching rate of the biocide from the bonding layer is inversely proportional to the square root of time, shortly after immersion of the substrate in seawater, the substrate remains substantially free of fouling and exhibit superior performance in comparison substrates coated with a biocide-free foul release coating system. However, the superior performance is not sustained, the coated substrates become progressively covered with biofouling, and within 4-6 months the system of WO 95/32862 shows similar severe fouling as substrates coated with a biocide-free foul release coating system.
- biocidal foul release coating systems as defined in the present application shows a controlled leaching of the biocide.
- the ratio of the release rate of biocide from the foul release coating system of this invention, 5 days after application of the coating (R 5 ) and the release rate of biocide 30 days after application of the coating (R 30 ) R 5 /R 30 is less than or equal to ( ⁇ ) 1.5, preferably ⁇ 1.33, more preferably ⁇ 1.11.
- biocidal foul release coating systems of the present invention show excellent fouling resistance both at short time and longer time after immersion of the substrates in seawater.
- a biocidal foul release coating system is a coating system having a surface which physically deters settlement and/or to which aquatic/marine organisms cannot easily adhere and where biocide is released from the coating system.
- the first coating layer there might be a tie-coat or adhesion promoter layer between the substrate and the first coating layer.
- a tie-coat or adhesion promoter layer between the substrate and the first coating layer.
- an anticorrosive coating applied on the substrate before the first coating layer is applied. More in general, there might be one or more coating layer(s) on the substrate before the first coating layer, comprising the biocide, is applied to the substrate.
- a coating composition is applied to the surface (e.g. to the substrate or another coating layer) as a liquid mixture; the coating composition then dries or cures to form a dry continuous coating film/layer over that surface.
- the rate of biocide leaching from the biocidal foul release coating system can be controlled by applying a subsequent coating layer or layers on top of a first coating layer, wherein the first coating layer contains a biocide, the subsequent coating layer(s) containing less biocide than the first coating layer and being free or substantially free of biocide.
- the advantage of this is that the biocide leaching rate can be tuned, made less dependent on time and indeed maintained in a more linear relationship with time. Therefore a desired and more constant rate of biocide leaching can be attained. This is advantageous as it leads to extended performance lifetimes, more efficient use of the biocide, and reduced environmental impact.
- biocide leaching can be controlled such that the ability of the fouling release coating system to prevent fouling under low speed or static conditions is especially enhanced.
- biocide leaching (sometimes known as biocide release) and biocide leaching rate (biocide release rate) should be clearly differentiated from foul release.
- Leaching rate is the rate at which the biocide is released by the coating system into the surrounding waters and is typically expressed as mass of biocide per unit area per unit time.
- Foul release is concerned with prevention of fouling and/or its ease of removal from the surface of an immersed substrate by non-biocidal means.
- foul release properties can be characterised by barnacle adhesion measurements that can be carried out using ASTM D 5618-94, Standard test method for measurement of barnacle adhesion strength in shear, or a related method. Both are complementary mechanisms to control fouling but are independent of each other.
- the present inventors have realised that the leaching rate can be controlled by varying the composition of the subsequent coating layer(s).
- the first coating layer behaves as a reservoir of biocide which contains a ready supply of biocide to be released.
- the leaching rate of the biocide can be controlled by varying certain attributes of the first and subsequent coating layer(s). These attributes include, but are not limited to: pigment volume concentration, cross link density, pigment size and shape, molecular weight of the polymer, the presence and amount of an incompatible fluid, the cross linking chemistry of the subsequent coating layer(s) and film thickness.
- the reservoir of biocide combined with the control mechanism of the subsequent coating layer(s), allows the biocide leaching rate to be tailored to the end use.
- a coating systems that shows a controlled leaching of biocide is a system where the release rate of biocide 30 days after immersion in water (R 30 ) is at least 67% of the release rate 5 days after immersion in water (R 5 ).
- a coating systems showing a controlled leaching of biocide is a system where R 5 /R 30 ⁇ 1.5.
- R 5 /R 30 ⁇ 1.5. In a further embodiment of the present invention, R 5 /R 30 ⁇ 1.33. In an even further embodiment of the present invention R 5 /R 30 ⁇ 1.11.
- the duplex foul release system is described as having a leaching rate of the biocide from the bonding layer that is inversely proportional to the square root of time, and no other factors control the leaching rate other than potentially the solubility of the biocide in water.
- the release rate of the biocide is described as F(t) ⁇ 36/t 0.5 , where F is the leach rate in ⁇ g/cm 2 /day ( ⁇ g cm ⁇ 2 day ⁇ 1 ) and t is the time in days.
- WO95/32862 fails to teach that a biocidal foul release coating system, wherein the substrate is first coated with a coating layer containing a biocide, which is then over-coated with subsequent layer(s) containing substantially no biocide would result in a more gradual and sustained release profile of biocide from the foul release coating surface.
- the subsequent coating layer(s) that are applied on top of the first coating layer contains less biocide than the first coating layer.
- the subsequent coating layer(s) is(are) free or substantially free of biocide.
- Substantially free of biocide means that the subsequent coating layer(s) contains less than 1.0 wt % (based on the total weight of the coating composition) of biocide.
- the subsequent coating layer(s) contain less than 0.5 wt % of biocide, more preferably less than 0.1 wt %.
- weight percent (wt %) is the weight percent, based on the total weight of the coating composition.
- the subsequent coating layer(s) further comprises an incompatible fluid.
- the incompatible fluid in the subsequent coating layer(s) helps to achieve an improved foul release performance. Without wishing to be bound by theory it is believed that the fluid may have an effect upon transportation of the biocide.
- biocide is either partially or wholly encapsulated or adsorbed or supported or bound.
- Encapsulation or absorption or supporting or binding of the biocide can provide a secondary mechanism for controlling biocide leaching from the coating system in order to achieve an even more gradual release and long lasting effect.
- the present invention relates to (i) a biocidal foul release coating system, and to (ii) a structure coated with the biocidal foul release coating system, the biocidal foul release coating system comprising
- the biocidal foul release coating system shows a controlled leaching of the biocide.
- One embodiment of the present invention is a structure coated with the biocidal foul release coating system defined above.
- the composition of the first coating layer is not especially limiting but preferably the first coating layer composition comprises a polymer.
- the polymer preferably forms an elastomer. More preferably this is a polyorganosiloxane. Even more preferably this is a polydimethylsiloxane.
- the polyorganosiloxane may also comprise two or more polyorganosiloxanes of different viscosity.
- the polyorganosiloxane has one or more, more preferably two or more reactive functional groups such as hydroxyl, alkoxy, acetoxy, carboxyl, hydrosilyl, amine, epoxy, vinyl or oxime functional groups.
- the polymer is present in an amount of 5 to 50 wt % based on the total weight of the coating composition. More preferably this is present in an amount of 8 to 20 wt %.
- the polymer is crosslinkable.
- the coating composition may require a cross-linker.
- the necessity for the presence of cross-linker will depend on the type and number of functional groups that are present in said polymer. If the polymer comprises alkoxy-silyl groups, the presence of a small amount of water, and optionally, a condensation catalyst is generally sufficient to achieve full cure of the coating after application. For these compositions, atmospheric moisture is generally sufficient to induce curing, and as a rule it will not be necessary to heat the coating composition after application.
- the optionally present cross-linker can be a cross-linking agent comprising a functional silane and/or one or more of any of acetoxy, alkoxy, amido, alkenoxy and oxime groups. Examples of such cross-linking agents are presented in WO 99/33927, page 19, line 9, through page 21, line 17. Mixtures of different cross-linkers can also be used.
- the crosslinking agent is present in an amount of 0.1% to 20 wt % based on the total weight of the coating composition.
- the first coating layer contains a biocide.
- a biocide By “contains”/“containing”, we mean that the biocide is present within the body of the coating layer (in the sense that it was mixed in the coating composition prior to curing/drying).
- the biocide of the present invention can be one or more of an inorganic, organometallic, metal-organic or organic biocide for marine or freshwater organisms.
- inorganic biocides include copper salts such as copper oxide, copper thiocyanate, copper bronze, copper carbonate, copper chloride, copper nickel alloys, and silver salts such as silver chloride or nitrate;
- organometallic and metal-organic biocides include zinc pyrithione (the zinc salt of 2-pyridinethiol-1-oxide), copper pyrithione, bis(N-cyclohexyl-diazenium dioxy) copper, zinc ethylene-bis(dithiocarbamate) (i.e.
- organic biocides include formaldehyde, dodecylguanidine monohydrochloride, thiabendazole, N-trihalomethyl thiophthalimides, trihalomethyl thiosulphamides, N-aryl maleimides such as N-(2,4,6-trichlorophenyl) maleimide, 3-(3,4-dichlorophenyl)-1,1-dimethylurea (diuron), 2,3,5,6-tetrachloro-4-(methylsulphonyl) pyridine, 2-methylthio-4-butylamino-6-cyclopopylamino-s-triazine, 3-benzo[b]thien-yl-5,6-dihydro-1,4,2-oxathiazine 4-oxide, 4,5-d
- the biocide may be a 3-isothiazolone, however the inventors have found that this biocide should preferably be in an encapsulated, adsorbed or bound form. In another embodiment, the biocide is not a 3-isothiazolone.
- the biocide is organic or metal-organic.
- leaching of the biocide involves physical diffusion of the biocide from the first coating layer through the subsequent coating layer(s) by passive transport processes.
- the flux of biocide from the coating system will therefore be controlled in part by the diffusion of the biocide through, and compatibility with, the subsequent coating layer(s). If the diffusion or compatibility are inherently high, as would be anticipated for organometallic biocides such as organotins and the like, then the resulting leaching rate will also be inherently high and difficult to control, such that the lifetime of the coating will be reduced and undesirable environmental impact may result.
- the leaching rate will also be inherently low and fouling may result.
- the use of an organic or metal-organic biocide allows the leaching rate to be suitably controlled through use of the coating system of the present invention and unacceptable environmental damage to be avoided.
- an inorganic biocide is a biocide whose chemical structure comprises a metal atom and which is free of carbon atoms;
- an organometallic biocide is a biocide whose chemical structure comprises a metal atom, a carbon atom, and a metal-carbon bond;
- a metal-organic biocide is a biocide whose chemical structure comprises a metal atom, a carbon atom, and which is free of metal-carbon bonds;
- an organic biocide is biocide whose chemical structure comprises a carbon atom and which is free of metal atoms.
- the biocide is one or more of a 2-trihalogenomethyl-3-halogeno-4-cyano pyrrole derivative substituted in position 5 and optionally in position 1, such as tralopyril, 1,4-dithiaanthraquinone-2,3-dicarbonitrile (dithianon), copper pyrithione, zinc pyrithione, tolylfluanid, dichlofluanid, and N-cyclopropyl-N′-(1,1-dimethylethyl)-6-(methylthio)-1,3,5-triazine-2,4-diamine.
- the biocide(s) is(are) present in the first coating layer composition in an amount of 0.05 to 50 wt %, more preferably 3 to 30 wt %, and most preferably 10 to 20 wt % based on the total weight of the composition of the first coating layer.
- the amount of biocide present in the first coating layer must be more than the amount of biocide in the at least one subsequent coating layer(s) at the time the coating layers are applied to the substrate.
- biocide may optionally be wholly or partially encapsulated, adsorbed or supported or bound. Certain biocides are difficult or hazardous to handle and are advantageously used in an encapsulated or absorbed or supported or bound form. Additionally, encapsulation, absorption or support or binding of the biocide can provide a secondary mechanism for controlling biocide leaching rate from the coating system in order to achieve an even more gradual release and long lasting effect.
- the method of encapsulation, adsorption or support or binding of the biocide is not particularly limiting for the present invention.
- Examples of ways in which an encapsulated biocide may be prepared for use in the present invention include mono and dual walled amino-formaldehyde or hydrolysed polyvinyl acetate-phenolic resin capsules or microcapsules as described in EP1791424.
- An example of a suitable encapsulated biocide is encapsulated 4,5-dichloro-2-(n-octyl)-3(2H)-isothiazolone marketed as by Dow Microbial Control as Sea-Nine CR2 Marine Antifoulant Agent.
- an absorbed or supported or bound biocide may be prepared include the use of host-guest complexes such as clathrates as described in EP0709358, phenolic resins as described in EP0880892, carbon-based adsorbents such as those described in EP1142477, or inorganic microporous carriers such as the amorphous silicas, amorphous aluminas, pseudoboehmites or zeolites described in EP1115282.
- host-guest complexes such as clathrates as described in EP0709358, phenolic resins as described in EP0880892, carbon-based adsorbents such as those described in EP1142477, or inorganic microporous carriers such as the amorphous silicas, amorphous aluminas, pseudoboehmites or zeolites described in EP1115282.
- the composition may optionally comprise a catalyst.
- suitable catalysts are the carboxylic acid salts of various metals, such as tin, zinc, iron, lead, barium, and zirconium.
- the salts preferably are salts of long-chain carboxylic acids, for example dibutyltin dilaurate, dibutyltin dioctoate, iron stearate, tin (II) octoate, and lead octoate.
- suitable catalysts include organobismuth and organotitanium compounds and organo-phosphates such as bis(2-ethyl-hexyl) hydrogen phosphate.
- catalysts include chelates, for example dibutyltin acetoacetonate.
- the catalyst may comprise a halogenated organic acid which has at least one halogen substituent on a carbon atom which is in the [alpha]-position relative to the acid group and/or at least one halogen substituent on a carbon atom which is in the [beta]-position relative to the acid group, or a derivative which is hydrolysable to form such an acid under the conditions of the condensation reaction.
- the catalyst may be as described in any of WO2007122325A1, WO2008055985A1, WO2009106717A2, WO2009106718A2, WO2009106719A1, WO2009106720A1, WO2009106721 A1, WO2009106722A1, WO2009106723A1, WO2009106724A1, WO2009103894A1, WO2009118307A1, WO2009133084A1, WO2009133085A1, WO2009156608A2, and WO2009156609A2.
- the catalyst of the biocidal first coating layer composition is preferably present in an amount of 0.01 to 4 wt %, based on the total weight of the coating composition.
- the biocidal first coating layer composition according to the invention also comprises one or more fillers, pigments, additional catalysts, and/or solvents.
- suitable fillers are barium sulphate, calcium sulphate, calcium carbonate, silicas or silicates (such as talc, feldspar, and china clay), aluminium paste/flakes, bentonite or other clays.
- Some fillers such as fumed silica may have a thixotropic effect on the coating composition.
- the proportion of fillers may be in the range of from 0 to 25 wt %, based on the total weight of the coating composition.
- the clay is present in an amount of from 0 to 1 wt % and preferably the thixotrope is present in an amount of from 0 to 5 wt %, based on the total weight of the coating composition.
- suitable pigments are black iron oxide, red iron oxide, yellow iron oxide, titanium dioxide, zinc oxide, carbon black, graphite, red molybdate, bismuth vanadate yellow, yellow molybdate, zinc sulfide, antimony oxide, cobalt/zinc titanium oxide greens, zinc/tin titanate oranges, lanthanide sulphide oranges and reds, manganese pyrophosphate violets, sodium aluminium sulfosilicates, quinacridones, phthalocyanine blue, phthalocyanine green, black iron oxide, indanthrone blue, cobalt aluminium oxide, carbazoledioxazine, chromium (III) oxide, isoindoline orange, bis-acetoaceto-tolidiole, benzimidazolone, quinaphthalone yellow, isoindoline yellow, tetrachloroisoindolinone, and quinophthalone yellow.
- the proportion of pigments may be in the range of from 0 to 10 wt %, based on the total weight of the coating composition.
- Suitable solvents include aromatic hydrocarbons, alcohols, ketones, esters, and mixtures of the above with one another or an aliphatic hydrocarbon.
- Preferable solvents include methyl isoamylketone and/or xylene.
- Preferably the solvent is present in an amount of 10 to 40 wt % based on the total weight of the composition.
- the composition optionally includes an adhesion promoting material, typically in an amount of 0.01-0.5 wt % based on the total weight of the composition.
- adhesion promoters include silanes such as aminosilanes, epoxysilanes, methacryoyloxypropylsilanes and mercaptosilanes.
- adhesion promoter is an aminosilane of the type:
- each R independently is selected from C1-8 alkyl (e.g. methyl, ethyl, hexyl, octyl, etc.), C1-4 alkyl, 0, C2-4 alkyl; aryl (e.g. phenyl) and aryl C1-4 alkyl (e.g. benzyl); R 1 is selected from (CH 2 ) 1-4 , methyl-substituted trimethylene and (CH2) 2-3 , O, (CH 2 ) 2-3 ; R 2 is selected from hydrogen, an alkyl, cycloalkyl, arakyl or aryl group or (CH 2 ) 2-4 —NH 2 .
- C1-8 alkyl e.g. methyl, ethyl, hexyl, octyl, etc.
- R 1 is selected from (CH 2 ) 1-4 , methyl-substituted trimethylene and (CH2) 2-3 , O, (CH 2 ) 2-3
- R 2 is selected
- the adhesion promoter is a “dipodal” silane as mentioned in WO2010018164 of the type
- R 1 , R 2 and R 5 independently are C1 to C5 alkylene groups and R 3 and R 4 independently are selected from methyl or ethyl.
- the adhesion promoter is an epoxysilane of the type:
- A is an epoxide substituted monovalent hydrocarbon radical having 2 to 12 carbon atoms; and each R independently is selected from C1-8 alkyl (e.g. methyl, ethyl, hexyl, octyl, etc.), C1-4-alkyl-, O—, C2-4-alkyl; aryl (e.g. phenyl) and aryl C1-4 alkyl (e.g. benzyl); and a is 0 or 1.
- the group A in the epoxysilane is preferably a glycidoxy-substituted alkyl group, for example 3-glycidoxypropyl.
- the epoxysilane can for example be 3-glycidoxypropyltrimethoxysilane, 3-glycidoxypropyltriethoxysilane, 3-glycidoxypropyldiethoxymethoxysilane, 2-glycidoxypropyltrimethoxysilane, 2-(3,4-epoxy-4-methylcyclohexyl)-ethyltrimethoxysilane, 5,6-epoxy-hexyltriethoxysilane; or their oligomers.
- adhesion promoter is N-2-aminoethyl-3-aminopropyltrimethoxysilane.
- Additional optional additives include dispersants such as an unsaturated polyamide acid ester salt.
- composition of the subsequent coating layer(s) is not especially limiting but the composition preferably comprises a polymer.
- the polymer forms an elastomer. More preferably this is a polyorganosiloxane. Even more preferably this is a polydimethylsiloxane.
- the polyorganosiloxane may also comprise two or more polyorganosiloxanes of different viscosity.
- the polyorganosiloxane has one or more, preferably two or more reactive functional groups such as hydroxyl, alkoxy, acetoxy, carboxyl, hydrosilyl, amine, epoxy, vinyl or oxime functional groups.
- the polymer may be as described in WO2008132196, wherein the polymer is a polyorganosiloxane polyoxyalkylene block copolymer of the form PS-(A-PO-A-PS)n, wherein PS represents a polyorganosiloxane block, PO represents a polyoxyalkylene block, A represents a divalent moiety, and n has a value of 1 or more than 1.
- the polymer has two or three reactive groups X on a polyorganosiloxane block per molecule which may self-condense and crosslink in the presence or absence of a catalyst (as defined earlier in this document) which can, optionally, be crosslinked with another organosilicon crosslinking agent containing two or more groups Y which are reactive with the said groups X.
- a catalyst as defined earlier in this document
- the polyorganosiloxane(s) polymer(s) is(are) present in an amount of 30 to 90 wt %, based on the total weight of the coating composition.
- the polymer is crosslinkable.
- the coating composition may require a cross-linker.
- the presence of a cross-linker is only necessary if the curable polymer cannot be cured by condensation. This will depend on the type and number of functional groups that are present in said polymer. If the polymer comprises alkoxy-silyl groups, the presence of a small amount of water, and optionally a condensation catalyst is generally sufficient to achieve full cure of the coating after application For these compositions, atmospheric moisture is generally sufficient to induce curing, and as a rule it will not be necessary to heat the coating composition after application.
- the optionally present cross-linker can be a cross-linking agent comprising a functional silane and/or one or more of any of acetoxy, alkoxy, amido, alkenoxy and oxime groups. Examples of such cross-linking agents are presented in WO 99/33927, page 19, line 9, through page 21, line 17. Mixtures of different cross-linkers can also be used.
- the crosslinking agent is present in an amount of 1 to 25 wt % based on the total weight of the coating composition.
- the composition may optionally comprise a catalyst.
- suitable catalysts are the carboxylic acid salts of various metals, such as tin, zinc, iron, lead, barium, and zirconium.
- the salts preferably are salts of long-chain carboxylic acids, for example dibutyltin dilaurate, dibutyltin dioctoate, iron stearate, tin (II) octoate, and lead octoate.
- suitable catalysts include organobismuth and organotitanium compounds and organo-phosphates such as bis(2-ethyl-hexyl) hydrogen phosphate.
- catalysts include chelates, for example dibutyltin acetoacetonate.
- the catalyst may comprise a halogenated organic acid which has at least one halogen substituent on a carbon atom which is in the [alpha]-position relative to the acid group and/or at least one halogen substituent on a carbon atom which is in the [beta]-position relative to the acid group, or a derivative which is hydrolysable to form such an acid under the conditions of a condensation reaction.
- the catalyst may be as described in any of WO2007122325A1, WO2008055985A1, WO2009106717A2, WO2009106718A2, WO2009106719A1, WO2009106720A1, WO2009106721 A1, WO2009106722A1, WO2009106723A1, WO2009106724A1, WO2009103894A1, WO2009118307A1, WO2009133084A1, WO2009133085A1, WO2009156608A2, and WO2009156609A2.
- the catalyst is present in an amount of 0.05 to 4 wt % based on the total weight of the coating composition.
- the subsequent coating layer composition according to the invention also comprises one or more fillers, pigments, catalysts, and/or solvents.
- fillers examples include barium sulphate, calcium sulphate, calcium carbonate, silicas or silicates (such as talc, feldspar, and china clay), aluminium paste/flakes, bentonite or other clays.
- Some fillers such as fumed silica may have a thixotropic effect on the coating composition.
- the proportion of fillers may be in the range of from 0 to 25 wt %, based on the total weight of the coating composition.
- the clay is present in an amount of from 0 to 1 wt % and preferably the thixotrope is present in an amount of from 0 to 5 wt %, based on the total weight of the coating composition.
- suitable pigments are black iron oxide, red iron oxide, yellow iron oxide, titanium dioxide, zinc oxide, carbon black, graphite, red molybdate, yellow molybdate, zinc sulfide, antimony oxide, sodium aluminium sulfosilicates, quinacridones, phthalocyanine blue, phthalocyanine green, black iron oxide, indanthrone blue, cobalt aluminium oxide, carbazoledioxazine, chromium oxide, isoindoline orange, bis-acetoaceto-tolidiole, benzimidazolone, quinaphthalone yellow, isoindoline yellow, tetrachloroisoindolinone, and quinophthalone yellow.
- the proportion of pigments may be in the range of from 0 to 25 wt %, based on the total weight of the coating composition.
- Suitable solvents include aromatic hydrocarbons, alcohols, ketones, esters, and mixtures of the above with one another or an aliphatic hydrocarbon.
- Preferable solvents include methyl isoamyl ketone and/or xylene.
- Preferably the solvent is present in an amount of 0-40 wt %, based on the total weight of the composition.
- the foul release properties of the coating system of the present invention are generally improved when the subsequent coating layer(s) composition forms a generally hydrophobic or amphiphilic foul release coat when dried or cured.
- the bulk and surface hydrophobicity of the subsequent coating layer(s) can be characterised by various means, for example, by seawater uptake measurements or surface contact angle measurements.
- the seawater uptake of the subsequent coating layer(s) is less than 30% by mass, more preferably less than 25% by mass.
- the equilibrium water contact angle of the subsequent coating layer(s) is greater than 30 degrees at 23° C.
- the subsequent coating layer(s) composition comprises an incompatible fluid or grease.
- an incompatible fluid means a silicone, organic or inorganic molecule or polymer, usually a liquid, but optionally also an organosoluble grease or wax, which is immiscible (either wholly or partly) with (the elastomer network of) the subsequent coating layer(s).
- the incompatible fluid is a fluorinated polymer or oligomer in a a polysiloxane coating; the process of enrichment of the fluorinated polymer/oligomer at the surface of the cured polysiloxane coating layer is thermodynamically driven due to the difference in surface energy.
- the low surface energy provided by the fluorinated polymer or oligomer in combination with the elastic properties provided by the cured polysiloxane improves the fouling release properties of the coating.
- Suitable fluids are:
- fluorinated alkyl-or alkoxy containing polymer or oligomer does not substantially take part in any cross-linking reaction.
- Other mono- and diorgano-functional end-capped fluorinated alkyl- or alkoxy-containing polymers or oligomers can also be used (eg carboxy-, ester-functional fluorinated alkyl- or alkoxy-containing polymers or oligomers).
- the fluid can be a silicone oil, for example of the formula:
- each group Q represents a hydrocarbon radical having 1-10 carbon atoms and n is an integer such that the silicone oil has a viscosity of 20 to 5000 m Pa s.
- At least 10% of the groups Q are generally methyl groups and at least 2% of the groups Q are phenyl groups.
- at least 10% of the —SiQ 2 -O— units are methyl-phenylsiloxane units.
- Most preferably the silicone oil is a methyl terminated poly(methylphenylsiloxane).
- the oil preferably has a viscosity of 20 to 1000 m Pa s. Examples of suitable silicone oils are sold under the trademarks Rhodorsil Huile 510V100 and Rhodorsil Huile 550 by Bluestar Silicones. The silicone oil improves the resistance of the coating system to aquatic fouling.
- the fluid may also be an organosilicone as shown:
- the fluid is present in 0.01 to 10 wt %, based on the total weight of the coating composition. Most preferably the fluid is present in the range of 2 to 7 wt %.
- a method of controlling the rate of release of biocide from a foul release coating system wherein the ratio of the release rate of biocide from a foul release coating system wherein the ratio of the release rate of biocide from the foul release coating system 5 days after application of the coating (R 5 ) and the release rate of biocide 30 days after application of the coating (R 30 ) R 5 /R 30 ⁇ 1.5, the method comprising
- the method of the invention is capable of controlling the rate of release of biocide from a foul release coating system such that the ratio R 5 /R 30 is less than or equal to ( ⁇ ) 1.33, and preferably less than or equal to ( ⁇ )1.11.
- the first coating layer and/or the subsequent coating layer(s) comprises an elastomeric polymer.
- the elastomeric polymer is as described in all preceding paragraphs.
- the first coating layer and/or the subsequent coating layer(s) comprise a polyorganosiloxane.
- the subsequent coating layer(s) are as described in all preceding paragraphs.
- the substrate is coated with an anticorrosion coating and the first coating layer is used as a tie coat over said anticorrosion coating.
- the biocide in the first coating layer is an organic or metal-organic biocide.
- the biocide is as described in all preceding paragraphs.
- the biocide is one or more of any of the biocides previously mentioned, and most suitably a 2-trihalogenomethyl-3-halogeno-4-cyano pyrrole derivative substituted in position 5 and optionally in position 1 or 1,4-dithiaanthraquinone-2,3-dicarbonitrile.
- the subsequent coating layer(s) comprises an incompatible fluid such as a silicone, organic or inorganic molecule or polymer, which is immiscible with the subsequent coating layer(s).
- an incompatible fluid such as a silicone, organic or inorganic molecule or polymer, which is immiscible with the subsequent coating layer(s).
- the coating system can be used for both dynamic and static structures, such as ship and boat hulls, buoys, drilling platforms, oil rigs, floating production storage and offloading vessels (FPSOs), pipes, cooling water intakes in power plants, fish nets, fish cages and other aquaculture and marine apparatus/structures and the like which are wholly or partially immersed in water.
- the coating system can be applied on any substrate that is used for these structures, such as metal e.g. steel, aluminium, concrete, wood, plastic or fibre-reinforced resin.
- the coating system according to the present invention having a controlled rate of release of biocide from a foul release coating system such that the ratio of the release rate of biocide from the foul release coating system 5 days after application of the coating (R 5 ) and the release rate of biocide 30 days after application of the coating (R 30 ) R 5 /R 30 is less than or equal to ( ⁇ ) 1.5 (preferably ⁇ 1.33), it has also been found to be effective against a broader range of fouling-types including (i) slime fouling, (ii) weed fouling, (iii) soft bodied fouling and (iv) hard bodied fouling, particularly on slow moving aquatic vessels, compared to systems which do not comprise a biocide or a foul-release coating layer.
- the coating system may be applied directly to a non-treated substrate.
- the coating system of the present invention may be applied to a substrate to which surface treatments or other coating layers have been previously applied.
- surface treatments and other coating layers include anticorrosion coatings, biocidal antifouling coatings, sealer coats, tie-coats, adhesion promoting layers, and the like.
- the system For application to ship and boat hulls at newbuilding, the system would typically be applied directly over a substrate having one or more anticorrosive coatings.
- the scheme At maintenance and repair or recoat, the scheme would typically be applied optionally over the existing coating scheme (with optional link coat) or directly over the substrate after removal of the existing coating scheme and reapplication of one or more anticorrosive coatings.
- the substrate for which fouling is to be inhibited is not especially limited and includes any of steel, plastic, concrete, wood, fibre-reinforced resin and aluminium.
- the first coating layer would be applied to result in a dry film thickness in the range of 100-200 ⁇ m, and the subsequent coating layer(s) would be applied to result in a dry film thickness in the range of 100-200 ⁇ m. Where a greater dry film thickness is required, the required film thickness may be produced by successive applications, each with a dry film thickness of 100-200 ⁇ m.
- the first coating layer would be applied to result in a dry film thickness in the range of 50-500 ⁇ m, and the subsequent coating layer(s) would be applied to result in a dry film thickness in the range of 50-500 ⁇ m.
- the biocide leaching rate for each coating system was experimentally determined.
- duplicate panels coated with each coating system were immersed in a holding tank of synthetic seawater.
- the panels were periodically transferred to a leaching rate measuring container of fresh synthetic seawater and gently agitated for a fixed period. At the end of this period, the panels were returned to the holding tank and the amount of biocide that had leached into the container was determined by chemical analysis. From knowledge of the determined amount of leached biocide, the exposed surface area of the coated panel, and the period of immersion in the leaching rate measuring container, the biocide leaching rate can be determined and expressed as ⁇ g cm ⁇ 2 d ⁇ 1 .
- the panels were fully immersed in 40 litres of artificial seawater in a rigorously clean glass tank and the water was constantly circulated through an activated carbon filter to avoid build up of the biocide or its degradation products.
- the temperature of the holding tank was maintained at around 22-23° C. All panels remained immersed in the holding tank for the duration of the experiment, except during leaching rate measurements which took place on predefined measurement days using the leaching rate measuring container.
- the concentration of biocide in the leaching rate measuring container may be determined using standard analytical methods known to one skilled in the art, for example high performance liquid chromatography (HPLC). The concentration of biocide in the leaching rate measuring container can then be used to determine the leaching rate R using the equation below.
- HPLC high performance liquid chromatography
- C is the equivalent concentration of the biocide in the leaching rate measurement container
- V is the volume of artificial seawater in the leaching rate measuring container (litres)
- t is period of immersion of the panel in the leaching rate measuring container (hours)
- A is the exposed surface area of the coating system on the panel (cm 2 ).
- the concentration of BCCPCA in the treated sample was determined by high performance liquid chromatography (HPLC) by direct injection using an Agilent 1100 HPLC system equipped with a Pursuit UPS 2.4 ⁇ m C18 column (50 ⁇ 3 mm) and using a mixture of acetonitrile, water, and orthophosphoric acid at a ratio of 50:49.95:0.05 parts by volume as mobile phase.
- HPLC high performance liquid chromatography
- a minimum of 6 calibration standards covering the range from 10 to 500 ⁇ g litre ⁇ 1 were freshly prepared each day by appropriate dilution with artificial seawater of a 1000 ⁇ g litre ⁇ 1 stock solution of BCCPCA in tetrahydrofuran. Artificial seawater blanks were analysed before and after the standards and after each sample set. Check standards were run after every 5 samples to check for reproducibility of the analytical method. At every time point, the analytical method was proven to be reproducible.
- the equivalent concentration of tralopyril in the leaching rate measuring container at the end of the agitation period is calculated by multiplying the determined BCCPCA concentration by the relative molar masses of tralolopyril and BCCPCA, and the leaching rate of tralopyril, R, is then calculated according to the following equation:
- R C tralopyril ⁇ V ⁇ 24 t ⁇ A ⁇ ⁇ ⁇ ⁇ g ⁇ ⁇ cm - 2 ⁇ ⁇ d - 1
- C tralopyril is the equivalent concentration of tralopyril in the leaching rate measurement container
- V is the volume of artificial seawater in the leaching rate measuring container (litres)
- t is period of immersion of the panel in the leaching rate measuring container (hours)
- A is the exposed surface area of the coating system on the panel (cm 2 ).
- Table 3 shows the leaching rate results collected on measurement days 5 (R 5 ) and 30 (R 30 ), and R 5 /R 30 . In each case, the results are the mean results of duplicate panels for each coating system.
- each coating systems demonstrates controlled leaching as defined within the framework of the present invention and none of the coatings shows biocide leaching rate behaviour that corresponds to the biocide leaching rate being proportional to the square root of time. Moreover, by varying particular parameters of the subsequent coating layer, control can be exercised over the biocide leaching rate behaviour, which can be made to fall, rise or remain essentially constant over time.
- biocide leaching rate can be controlled such that a higher or lower biocide leaching rate can be obtained at any given point in time.
- Example Ingredient 1 2 3 4 5 6 7 8 Short chain 59.5 Poly Dimethyl siloxane (viscosity of 7.5 stokes) Silicone 78.6 polyether block copolymer* Poly Dimethyl 65.6 59.5 59.5 59.5 59.5 siloxane (viscosity of 35 strokes) Fumed silica 1.5 1.8 1.5 1.5 1.5 1.5 (Hydrophobic) Red iron oxide 13.2 Micaceous iron 7.9 oxide Disparlon 6500 2 amide (commercial product) Titanium 6.5 6.5 6.5 6.5 dioxide Carbon black 1.4 1.4 1.4 1.4 Xylene 18.4 20.5 18.4 18.4 23.6 18.4 Tetra-ethyl 2.7 3 2.7 2.7 2.7 ortho silicate polymethyl 5.2 5.7 5.2 5.2 5.2 phenylsiloxane oil 2,4- 4.3 3.9 4.7 4.3 4.3 4.3 4.3 4.3 Pentanedione Dio
- Example 9 As shown in Table 4, further coating systems in accordance with the present invention (Examples 9 to 12) were prepared for comparison with a commercial biocide-free foul release coating system (all Examples).
- Test panels were prepared in order to determine the ability of each coating system to control the leaching of biocide from the first coating layer and inhibit fouling.
- the coating systems of Examples 9 to 12 were applied to 60 ⁇ 60 cm marine plywood panels by roller to give a dry film thicknesses for the first coating layer and subsequent coating layer of about 100 and 150 ⁇ m respectively.
- the boards had been pre-primed with one coat of a 2 pack epoxy anticorrosive paint (Intershield 300, International Paint) with a DFT of about 125 ⁇ m per coat.
- Test panels were simultaneously immersed in natural tropical marine waters at a depth of 0.5 to 1.0 m in Changi, Singapore where fouling growth is known to be severe. The panels were periodically removed from the water, photographed and the growth of fouling on the coating systems was assessed prior to re-immersion of the panels.
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Life Sciences & Earth Sciences (AREA)
- Materials Engineering (AREA)
- Wood Science & Technology (AREA)
- Organic Chemistry (AREA)
- Mechanical Engineering (AREA)
- Combustion & Propulsion (AREA)
- Ocean & Marine Engineering (AREA)
- Plant Pathology (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Paints Or Removers (AREA)
- Application Of Or Painting With Fluid Materials (AREA)
- Agricultural Chemicals And Associated Chemicals (AREA)
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US14/126,226 US20140141263A1 (en) | 2011-06-21 | 2012-07-19 | Biocidal foul release coating systems |
Applications Claiming Priority (5)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US201161499430P | 2011-06-21 | 2011-06-21 | |
EP11170712 | 2011-06-21 | ||
EP11170712.1 | 2011-06-21 | ||
PCT/EP2012/061625 WO2012175459A1 (en) | 2011-06-21 | 2012-06-19 | Biocidal foul release coating systems |
US14/126,226 US20140141263A1 (en) | 2011-06-21 | 2012-07-19 | Biocidal foul release coating systems |
Publications (1)
Publication Number | Publication Date |
---|---|
US20140141263A1 true US20140141263A1 (en) | 2014-05-22 |
Family
ID=44904675
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US14/126,226 Abandoned US20140141263A1 (en) | 2011-06-21 | 2012-07-19 | Biocidal foul release coating systems |
Country Status (12)
Country | Link |
---|---|
US (1) | US20140141263A1 (es) |
EP (1) | EP2723821A1 (es) |
JP (1) | JP5993451B2 (es) |
KR (1) | KR101980220B1 (es) |
CN (1) | CN103608411A (es) |
AU (1) | AU2012271948B2 (es) |
BR (1) | BR112013032015A2 (es) |
MX (1) | MX2013015164A (es) |
MY (1) | MY163188A (es) |
SA (1) | SA112330621B1 (es) |
TW (1) | TWI575038B (es) |
WO (1) | WO2012175459A1 (es) |
Cited By (21)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20130337201A1 (en) * | 2010-07-06 | 2013-12-19 | Fletcher Eyster | Formable aquatic coverings for preventing biofouling |
US20140341962A1 (en) * | 2011-12-29 | 2014-11-20 | Rohm And Haas Company | Encapsulated actives |
US20160024314A1 (en) * | 2013-03-20 | 2016-01-28 | Hempel A/S | Novel polysiloxane-based fouling control coating systems |
US9586381B1 (en) | 2013-10-25 | 2017-03-07 | Steriplate, LLC | Metal plated object with biocidal properties |
US9625075B2 (en) | 2012-05-24 | 2017-04-18 | Massachusetts Institute Of Technology | Apparatus with a liquid-impregnated surface to facilitate material conveyance |
US9709689B2 (en) | 2014-02-07 | 2017-07-18 | Pgs Geophysical As | Geophysical cable preparation for antifouling paint |
EP3196115A1 (en) * | 2016-01-19 | 2017-07-26 | Shell Internationale Research Maatschappij B.V. | Water intake riser for a floating plant |
WO2018108693A1 (en) * | 2016-12-16 | 2018-06-21 | Renolit Se | Self-fusing antifouling tape |
US10064273B2 (en) | 2015-10-20 | 2018-08-28 | MR Label Company | Antimicrobial copper sheet overlays and related methods for making and using |
WO2018182499A1 (en) | 2017-03-29 | 2018-10-04 | I-Tech Ab | Antifouling article |
WO2018235092A1 (en) * | 2017-06-21 | 2018-12-27 | Garware-Wall Ropes Limited | FABRIC REDUCING TRAINING AND BIOLOGICAL ENCRASION FOR AQUACULTURE |
US10273367B2 (en) * | 2016-08-08 | 2019-04-30 | Autonomic Materials, Inc. | Biocidal protective formulations |
US10519327B2 (en) * | 2018-04-20 | 2019-12-31 | Redjak, L.L.C. | Methods and coatings for protecting surfaces from bio-fouling species |
US20200024462A1 (en) * | 2017-01-17 | 2020-01-23 | Akzo Nobel Coatings International B.V. | Foul release coating composition |
US10882085B2 (en) | 2012-11-19 | 2021-01-05 | Massachusetts Institute Of Technology | Apparatus and methods employing liquid-impregnated surfaces |
US10968035B2 (en) | 2012-03-23 | 2021-04-06 | Massachusetts Institute Of Technology | Self-lubricating surfaces for food packaging and food processing equipment |
US11058803B2 (en) | 2012-05-24 | 2021-07-13 | Massachusetts Institute Of Technology | Medical devices and implements with liquid-impregnated surfaces |
US11105352B2 (en) | 2012-06-13 | 2021-08-31 | Massachusetts Institute Of Technology | Articles and methods for levitating liquids on surfaces, and devices incorporating the same |
US11492500B2 (en) | 2012-11-19 | 2022-11-08 | Massachusetts Institute Of Technology | Apparatus and methods employing liquid-impregnated surfaces |
WO2023187731A1 (en) * | 2022-03-31 | 2023-10-05 | Asian Paints Limited | Coating composition and a process for its preparation |
US11933551B2 (en) | 2011-08-05 | 2024-03-19 | Massachusetts Institute Of Technology | Liquid-impregnated surfaces, methods of making, and devices incorporating the same |
Families Citing this family (12)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN105229091B (zh) * | 2013-02-15 | 2019-03-08 | 莫门蒂夫性能材料股份有限公司 | 包含硅水凝胶的防污体系 |
BR112015019146B1 (pt) | 2013-02-26 | 2022-01-04 | Akzo Nobel Coatings International B.V. | Composição anti-incrustações que compreende um polímero curável e um polímero ou oligômero que contém oxialquileno fluoretado, e método de inibição de incrustações de um substrato em ambiente aquático por meio de aplicação da composição anti-incrustações |
MX2016006848A (es) * | 2013-12-03 | 2016-09-13 | Akzo Nobel Coatings Int Bv | Un metodo para el recubrimiento de una capa de recubrimiento antiguo sobre un sustrato y una composicion de recubrimiento adecuada para uso en este metodo. |
KR102591554B1 (ko) * | 2014-07-11 | 2023-10-20 | 헴펠 에이/에스 | 폴리(옥시알킬렌)-개질 알코올을 포함하는 신규한 폴리실록산-기반 오염-방출 코트 |
CN104370985B (zh) * | 2014-09-30 | 2020-04-28 | 上海化学试剂研究所有限公司 | 一种类辣椒素类化合物及其制备方法和应用 |
CN106999981B (zh) * | 2014-12-02 | 2020-12-04 | 中国涂料株式会社 | 污损抑制涂膜的增强方法 |
EP3048141B1 (en) * | 2015-01-26 | 2017-11-22 | Avery Dennison Corporation | Self adhesive fouling release coating composition |
KR20180064501A (ko) * | 2015-10-15 | 2018-06-14 | 아크조노벨코팅스인터내셔널비.브이. | 물에 적어도 부분적으로 침지될 인공 물체의 외부 표면에 코팅을 적용하는 방법 |
JP7046542B2 (ja) * | 2016-09-29 | 2022-04-04 | 日東電工株式会社 | 構造物上の塗膜、塗膜を形成するための塗料セット及び下塗層用塗料並びに塗工方法 |
CN108225535B (zh) * | 2017-12-25 | 2021-01-29 | 海鹰企业集团有限责任公司 | 水声换能器性能测试方法及水声换能器 |
WO2019189694A1 (ja) * | 2018-03-28 | 2019-10-03 | 日東電工株式会社 | 下塗層形成用組成物、下塗層、及び塗膜 |
WO2023118480A1 (en) * | 2021-12-23 | 2023-06-29 | Ppg Coatings Europe B.V. | Self adhesive fouling release coating composition |
Citations (27)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4401703A (en) * | 1981-10-22 | 1983-08-30 | Rodgers Stephen D | Antifouling tile containing antifoulant reservoirs for in situ replenishment |
US5334389A (en) * | 1992-10-15 | 1994-08-02 | Duke University | Antifouling coating and method for using same |
US5691019A (en) * | 1995-05-01 | 1997-11-25 | General Electric Company | Foul release system |
US6069189A (en) * | 1996-09-19 | 2000-05-30 | Sigma Coatings, B.V. | Light-and bright-colored antifouling paints |
US6180249B1 (en) * | 1998-09-08 | 2001-01-30 | General Electric Company | Curable silicone foul release coatings and articles |
US6291549B1 (en) * | 1996-10-24 | 2001-09-18 | Bayer Aktiengesellschaft | Antifouling paints |
US6451437B1 (en) * | 1999-10-13 | 2002-09-17 | Chugoku Marine Paints, Ltd. | Curable composition, coating composition, paint, antifouling paint, cured product thereof and method of rendering base material antifouling |
US6607826B1 (en) * | 1999-12-09 | 2003-08-19 | Brunswick Corporation | Plastic anti-fouling film for boat hull protection |
US6723376B1 (en) * | 1997-12-23 | 2004-04-20 | International Coatings Limited | Fouling inhibition |
US20050013843A1 (en) * | 2003-01-07 | 2005-01-20 | Detty Michael R. | Hybrid anti-fouling coating compositions and methods for preventing the fouling of surfaces subjected to a marine environment |
US20050159504A1 (en) * | 2002-04-29 | 2005-07-21 | Institut Fuer Neue Materialien Gemeinnuetzige Gmbh | Substrates having a biofilm-inhibiting coating |
US20050227092A1 (en) * | 2004-04-07 | 2005-10-13 | Shin-Etsu Chemical Co., Ltd. | Antifouling coating compositions and coated articles |
US20070042199A1 (en) * | 2005-05-09 | 2007-02-22 | Ndsu Research Foundation | Anti-fouling materials containing cationic polysiloxanes |
US20070092738A1 (en) * | 2003-10-03 | 2007-04-26 | Hempel A/S | Tie-coat composition comprising at least two types of functional polysiloxane compounds and a method for using the same for establishing a coating on a substrate |
US20070203307A1 (en) * | 2006-02-24 | 2007-08-30 | Goldschmidt Gmbh | Polymers of organically modified siloxane resins with release effect |
US20070213426A1 (en) * | 2005-09-06 | 2007-09-13 | Novus International Inc. | Marine antifouling coating compositions |
US20080124298A1 (en) * | 2004-02-03 | 2008-05-29 | Akzo Nobel Coating International B.V. | Antifouling Coating Composition and Its Use on Man Made Structures |
US20100130665A1 (en) * | 2006-10-18 | 2010-05-27 | Nanocyl S.A. | Marine anti-biofouling and fouling release composition |
US7739974B1 (en) * | 2008-09-05 | 2010-06-22 | Brunswick Corporation | Submersible object with antifouling paint configuration |
US20100178316A1 (en) * | 2007-05-30 | 2010-07-15 | Anuj Chauhan | Extended release of bioactive molecules from silicone hydrogels |
US20110212333A1 (en) * | 2008-05-29 | 2011-09-01 | Bluestar Silicones France | Article having antifouling properties for aquatic and particularly sea use |
US20110287268A1 (en) * | 2008-04-30 | 2011-11-24 | Bluestar Silicones France | Article having antisoiling properties and intended to be employed in aquatic uses, in particular marine uses |
US20120202076A1 (en) * | 2009-10-13 | 2012-08-09 | Ryo Ehara | Antifouling coating composition, antifouling film, composite film, and in-water structure |
US20140377552A1 (en) * | 2011-12-21 | 2014-12-25 | Nitto Denko Corporation | Adhesive tape preventing adhesion by aquatic organisms |
US20150024157A1 (en) * | 2012-01-19 | 2015-01-22 | Jotun A/S | Fouling release coatings |
US20150079345A1 (en) * | 2012-03-29 | 2015-03-19 | Nitto Denko Corporation | Adhesive tape for preventing aquatic biofouling |
US20160024314A1 (en) * | 2013-03-20 | 2016-01-28 | Hempel A/S | Novel polysiloxane-based fouling control coating systems |
Family Cites Families (29)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
GB1307001A (en) | 1970-01-12 | 1973-02-14 | Kroyer K K K | Marine structure having a surface coating for the prevention of accumulation of marine organisms |
US3702778A (en) | 1970-03-23 | 1972-11-14 | Battelle Memorial Institute | Ship's hull coated with antifouling silicone rubber |
GB1409048A (en) | 1971-10-20 | 1975-10-08 | Int Paint Co | Marine top coat composition |
JPS5263225A (en) * | 1975-10-23 | 1977-05-25 | Hitachi Chem Co Ltd | Water-soluble compositions for ship bottom paints |
US4865909A (en) * | 1987-10-21 | 1989-09-12 | W. L. Gore & Associates, Inc. | Microporous anti-fouling marine coating |
FR2636958A1 (fr) | 1988-09-29 | 1990-03-30 | Rhone Poulenc Chimie | Primaire d'adherence chlore pour elastomere silicone |
DE69102535T2 (de) | 1990-03-27 | 1995-01-05 | Courtaulds Coatings (Holdings) Ltd., London | Beschichtungszusammensetzung. |
EP0709358B1 (en) | 1993-06-23 | 1999-10-13 | Nippon Soda Co., Ltd. | Novel clathrate compound, process for producing the same, and antifouling agent |
KR970703398A (ko) | 1994-05-31 | 1997-07-03 | 윌리암 씨. 가버트 | 방오제 및 오염물 박리 코팅(Antifouling and Foul-Release Coatings) |
JP2983197B2 (ja) * | 1997-03-03 | 1999-11-29 | 菊水化学工業株式会社 | 塗料組成物および塗装方法 |
US6221374B1 (en) | 1997-05-28 | 2001-04-24 | Rohm And Haas Company | Controlled release compositions |
GB9818778D0 (en) | 1998-08-28 | 1998-10-21 | Crosfield Joseph & Sons | Particulate carrier for biocide formulations |
US6126991A (en) * | 1999-04-19 | 2000-10-03 | General Electric Company | Method for enhancing the properties of biofouling release coatings |
US6676954B2 (en) | 2000-04-06 | 2004-01-13 | Rohm And Haas Company | Controlled release compositions |
AU2002257684B2 (en) * | 2001-03-21 | 2007-01-18 | Akzo Nobel N.V. | Anti-fouling compositions with a fluorinated alkyl- or alkoxy-containing polymer or oligomer |
CN101137288B (zh) | 2004-09-14 | 2011-09-28 | 微技术实验室公司 | 微胶囊化的杀生物剂和防污剂 |
KR100916887B1 (ko) * | 2004-12-14 | 2009-09-09 | 주고꾸 도료 가부시키가이샤 | 에폭시 방식도료 조성물, 방식도막, 오르가노폴리실록산계방오성 복합도막 및 상기 복합도막으로 피복된 선박 또는수중 구조물 |
JP4947596B2 (ja) * | 2005-04-05 | 2012-06-06 | 中国塗料株式会社 | オルガノポリシロキサン系防汚塗膜用タイコート、複合塗膜、および該塗膜で被覆された船舶、水中構造物 |
GB0515185D0 (en) | 2005-07-22 | 2005-08-31 | Fox Andrew J | Beam definable antenna |
KR20080110781A (ko) * | 2006-03-06 | 2008-12-19 | 요툰 에이/에스 | 파울링 방출 조성물 |
FR2900153B1 (fr) | 2006-04-21 | 2008-07-18 | Rhodia Recherches & Tech | Procede de condensation de motifs silyles a l'aide d'un catalyseur de type carbene |
CL2007002176A1 (es) | 2006-07-25 | 2008-06-13 | Fujifilm Hunt Smart Surfaces L | Mezcla de polimeros de recubrimiento adhesivo de liberacion de anti-fouling que comprende polimeros de polisiloxano y polimero organico que comprende monomeros que polimerizan en polimeros de cadena simple; sistemas de liberacion de anti-fouling; pro |
CA2685747C (en) | 2007-05-01 | 2013-06-18 | Akzo Nobel Coatings International B.V. | Antifouling coating composition based on curable polyorganosiloxane polyoxyalkylene copolymers |
JP5222291B2 (ja) * | 2007-06-26 | 2013-06-26 | 中国塗料株式会社 | 安定性が改良されたトリフェニルボロン化合物含有防汚塗料組成物、それに用いる防汚剤セット、およびトリフェニルボロン化合物の分解抑制・制御方法 |
DE102008001014A1 (de) * | 2008-04-04 | 2009-10-08 | Bio-Gate Ag | Schichtmaterial |
WO2009133085A1 (fr) * | 2008-04-30 | 2009-11-05 | Bluestar Silicones France | Article presentant des proprietes antisalissures et destine a etre utilise dans des applications aquatiques en particulier marines. |
WO2010018164A1 (en) | 2008-08-11 | 2010-02-18 | Hempel A/S | Novel tie-coat compositions |
EP2348853B1 (en) * | 2008-10-08 | 2015-08-19 | Janssen Pharmaceutica N.V. | High solid dispersions comprising biocides |
US9562163B2 (en) * | 2009-02-26 | 2017-02-07 | Severn Marine Technologies, Llc | Optically clear biofouling resistant compositions and methods for marine instruments |
-
2012
- 2012-06-19 AU AU2012271948A patent/AU2012271948B2/en not_active Ceased
- 2012-06-19 KR KR1020147000765A patent/KR101980220B1/ko active IP Right Grant
- 2012-06-19 BR BR112013032015A patent/BR112013032015A2/pt not_active Application Discontinuation
- 2012-06-19 CN CN201280029226.3A patent/CN103608411A/zh active Pending
- 2012-06-19 JP JP2014516298A patent/JP5993451B2/ja not_active Expired - Fee Related
- 2012-06-19 EP EP12728529.4A patent/EP2723821A1/en not_active Withdrawn
- 2012-06-19 WO PCT/EP2012/061625 patent/WO2012175459A1/en active Application Filing
- 2012-06-19 SA SA112330621A patent/SA112330621B1/ar unknown
- 2012-06-19 MX MX2013015164A patent/MX2013015164A/es unknown
- 2012-06-19 MY MYPI2013702423A patent/MY163188A/en unknown
- 2012-06-20 TW TW101122093A patent/TWI575038B/zh not_active IP Right Cessation
- 2012-07-19 US US14/126,226 patent/US20140141263A1/en not_active Abandoned
Patent Citations (27)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4401703A (en) * | 1981-10-22 | 1983-08-30 | Rodgers Stephen D | Antifouling tile containing antifoulant reservoirs for in situ replenishment |
US5334389A (en) * | 1992-10-15 | 1994-08-02 | Duke University | Antifouling coating and method for using same |
US5691019A (en) * | 1995-05-01 | 1997-11-25 | General Electric Company | Foul release system |
US6069189A (en) * | 1996-09-19 | 2000-05-30 | Sigma Coatings, B.V. | Light-and bright-colored antifouling paints |
US6291549B1 (en) * | 1996-10-24 | 2001-09-18 | Bayer Aktiengesellschaft | Antifouling paints |
US6723376B1 (en) * | 1997-12-23 | 2004-04-20 | International Coatings Limited | Fouling inhibition |
US6180249B1 (en) * | 1998-09-08 | 2001-01-30 | General Electric Company | Curable silicone foul release coatings and articles |
US6451437B1 (en) * | 1999-10-13 | 2002-09-17 | Chugoku Marine Paints, Ltd. | Curable composition, coating composition, paint, antifouling paint, cured product thereof and method of rendering base material antifouling |
US6607826B1 (en) * | 1999-12-09 | 2003-08-19 | Brunswick Corporation | Plastic anti-fouling film for boat hull protection |
US20050159504A1 (en) * | 2002-04-29 | 2005-07-21 | Institut Fuer Neue Materialien Gemeinnuetzige Gmbh | Substrates having a biofilm-inhibiting coating |
US20050013843A1 (en) * | 2003-01-07 | 2005-01-20 | Detty Michael R. | Hybrid anti-fouling coating compositions and methods for preventing the fouling of surfaces subjected to a marine environment |
US20070092738A1 (en) * | 2003-10-03 | 2007-04-26 | Hempel A/S | Tie-coat composition comprising at least two types of functional polysiloxane compounds and a method for using the same for establishing a coating on a substrate |
US20080124298A1 (en) * | 2004-02-03 | 2008-05-29 | Akzo Nobel Coating International B.V. | Antifouling Coating Composition and Its Use on Man Made Structures |
US20050227092A1 (en) * | 2004-04-07 | 2005-10-13 | Shin-Etsu Chemical Co., Ltd. | Antifouling coating compositions and coated articles |
US20070042199A1 (en) * | 2005-05-09 | 2007-02-22 | Ndsu Research Foundation | Anti-fouling materials containing cationic polysiloxanes |
US20070213426A1 (en) * | 2005-09-06 | 2007-09-13 | Novus International Inc. | Marine antifouling coating compositions |
US20070203307A1 (en) * | 2006-02-24 | 2007-08-30 | Goldschmidt Gmbh | Polymers of organically modified siloxane resins with release effect |
US20100130665A1 (en) * | 2006-10-18 | 2010-05-27 | Nanocyl S.A. | Marine anti-biofouling and fouling release composition |
US20100178316A1 (en) * | 2007-05-30 | 2010-07-15 | Anuj Chauhan | Extended release of bioactive molecules from silicone hydrogels |
US20110287268A1 (en) * | 2008-04-30 | 2011-11-24 | Bluestar Silicones France | Article having antisoiling properties and intended to be employed in aquatic uses, in particular marine uses |
US20110212333A1 (en) * | 2008-05-29 | 2011-09-01 | Bluestar Silicones France | Article having antifouling properties for aquatic and particularly sea use |
US7739974B1 (en) * | 2008-09-05 | 2010-06-22 | Brunswick Corporation | Submersible object with antifouling paint configuration |
US20120202076A1 (en) * | 2009-10-13 | 2012-08-09 | Ryo Ehara | Antifouling coating composition, antifouling film, composite film, and in-water structure |
US20140377552A1 (en) * | 2011-12-21 | 2014-12-25 | Nitto Denko Corporation | Adhesive tape preventing adhesion by aquatic organisms |
US20150024157A1 (en) * | 2012-01-19 | 2015-01-22 | Jotun A/S | Fouling release coatings |
US20150079345A1 (en) * | 2012-03-29 | 2015-03-19 | Nitto Denko Corporation | Adhesive tape for preventing aquatic biofouling |
US20160024314A1 (en) * | 2013-03-20 | 2016-01-28 | Hempel A/S | Novel polysiloxane-based fouling control coating systems |
Cited By (27)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20130337201A1 (en) * | 2010-07-06 | 2013-12-19 | Fletcher Eyster | Formable aquatic coverings for preventing biofouling |
US11623716B2 (en) | 2010-07-06 | 2023-04-11 | Biofouling Technologies, Inc. | Formable aquatic coverings for preventing biofouling |
US11933551B2 (en) | 2011-08-05 | 2024-03-19 | Massachusetts Institute Of Technology | Liquid-impregnated surfaces, methods of making, and devices incorporating the same |
US20140341962A1 (en) * | 2011-12-29 | 2014-11-20 | Rohm And Haas Company | Encapsulated actives |
US10968035B2 (en) | 2012-03-23 | 2021-04-06 | Massachusetts Institute Of Technology | Self-lubricating surfaces for food packaging and food processing equipment |
US9625075B2 (en) | 2012-05-24 | 2017-04-18 | Massachusetts Institute Of Technology | Apparatus with a liquid-impregnated surface to facilitate material conveyance |
US12005161B2 (en) | 2012-05-24 | 2024-06-11 | Massachusetts Institute Of Technology | Medical devices and implements with liquid-impregnated surfaces |
US11684705B2 (en) | 2012-05-24 | 2023-06-27 | Massachusetts Institute Of Technology | Medical devices and implements with liquid-impregnated surfaces |
US11058803B2 (en) | 2012-05-24 | 2021-07-13 | Massachusetts Institute Of Technology | Medical devices and implements with liquid-impregnated surfaces |
US11105352B2 (en) | 2012-06-13 | 2021-08-31 | Massachusetts Institute Of Technology | Articles and methods for levitating liquids on surfaces, and devices incorporating the same |
US11492500B2 (en) | 2012-11-19 | 2022-11-08 | Massachusetts Institute Of Technology | Apparatus and methods employing liquid-impregnated surfaces |
US10882085B2 (en) | 2012-11-19 | 2021-01-05 | Massachusetts Institute Of Technology | Apparatus and methods employing liquid-impregnated surfaces |
US11787953B2 (en) * | 2013-03-20 | 2023-10-17 | Hempel A/S | Polysiloxane-based fouling control coating systems |
US20160024314A1 (en) * | 2013-03-20 | 2016-01-28 | Hempel A/S | Novel polysiloxane-based fouling control coating systems |
US20210261793A1 (en) * | 2013-03-20 | 2021-08-26 | Hempel A/S | Novel polysiloxane-based fouling control coating systems |
US9586381B1 (en) | 2013-10-25 | 2017-03-07 | Steriplate, LLC | Metal plated object with biocidal properties |
US9709689B2 (en) | 2014-02-07 | 2017-07-18 | Pgs Geophysical As | Geophysical cable preparation for antifouling paint |
US10064273B2 (en) | 2015-10-20 | 2018-08-28 | MR Label Company | Antimicrobial copper sheet overlays and related methods for making and using |
EP3196115A1 (en) * | 2016-01-19 | 2017-07-26 | Shell Internationale Research Maatschappij B.V. | Water intake riser for a floating plant |
US10273367B2 (en) * | 2016-08-08 | 2019-04-30 | Autonomic Materials, Inc. | Biocidal protective formulations |
WO2018108693A1 (en) * | 2016-12-16 | 2018-06-21 | Renolit Se | Self-fusing antifouling tape |
US20200024462A1 (en) * | 2017-01-17 | 2020-01-23 | Akzo Nobel Coatings International B.V. | Foul release coating composition |
US11603475B2 (en) | 2017-03-29 | 2023-03-14 | I-Tech Ab | Antifouling article |
WO2018182499A1 (en) | 2017-03-29 | 2018-10-04 | I-Tech Ab | Antifouling article |
WO2018235092A1 (en) * | 2017-06-21 | 2018-12-27 | Garware-Wall Ropes Limited | FABRIC REDUCING TRAINING AND BIOLOGICAL ENCRASION FOR AQUACULTURE |
US10519327B2 (en) * | 2018-04-20 | 2019-12-31 | Redjak, L.L.C. | Methods and coatings for protecting surfaces from bio-fouling species |
WO2023187731A1 (en) * | 2022-03-31 | 2023-10-05 | Asian Paints Limited | Coating composition and a process for its preparation |
Also Published As
Publication number | Publication date |
---|---|
MX2013015164A (es) | 2014-03-31 |
CN103608411A (zh) | 2014-02-26 |
EP2723821A1 (en) | 2014-04-30 |
KR20140038520A (ko) | 2014-03-28 |
WO2012175459A1 (en) | 2012-12-27 |
KR101980220B1 (ko) | 2019-05-20 |
BR112013032015A2 (pt) | 2016-12-20 |
SA112330621B1 (ar) | 2016-01-14 |
JP5993451B2 (ja) | 2016-09-14 |
TW201305289A (zh) | 2013-02-01 |
AU2012271948B2 (en) | 2015-10-15 |
MY163188A (en) | 2017-08-15 |
TWI575038B (zh) | 2017-03-21 |
JP2014519978A (ja) | 2014-08-21 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
AU2012271948B2 (en) | Biocidal foul release coating systems | |
AU2012271948A1 (en) | Biocidal foul release coating systems | |
EP3571251B1 (en) | Foul release coating composition, substrate coated with such coating composition, and use of such coating composition | |
AU2018383882B2 (en) | Foul release coating composition, substrate coated with such coating composition, and use of such coating composition | |
DK3077468T3 (en) | PROCEDURE FOR COATING AN OLD COATING LAYER ON A SUBSTRATE AND COATING COMPOSITION SUITABLE FOR USE IN THIS PROCEDURE |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AS | Assignment |
Owner name: AKZO NOBEL COATINGS INTERNATIONAL B.V., NETHERLAND Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:JONES, PHILLIP KEITH;HAWKINS, IAN MICHAEL;CURRY, ANDREW;AND OTHERS;SIGNING DATES FROM 20131003 TO 20131115;REEL/FRAME:031781/0095 |
|
STCB | Information on status: application discontinuation |
Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION |