US20120220697A2 - Sustainable compositions, related methods, and members formed therefrom - Google Patents
Sustainable compositions, related methods, and members formed therefrom Download PDFInfo
- Publication number
- US20120220697A2 US20120220697A2 US13/049,222 US201113049222A US2012220697A2 US 20120220697 A2 US20120220697 A2 US 20120220697A2 US 201113049222 A US201113049222 A US 201113049222A US 2012220697 A2 US2012220697 A2 US 2012220697A2
- Authority
- US
- United States
- Prior art keywords
- extrusion
- profile extrusion
- polylactic acid
- window
- door
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Links
Images
Classifications
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
- C08L97/00—Compositions of lignin-containing materials
- C08L97/02—Lignocellulosic material, e.g. wood, straw or bagasse
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
- B29C48/00—Extrusion moulding, i.e. expressing the moulding material through a die or nozzle which imparts the desired form; Apparatus therefor
- B29C48/022—Extrusion moulding, i.e. expressing the moulding material through a die or nozzle which imparts the desired form; Apparatus therefor characterised by the choice of material
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
- B29C48/00—Extrusion moulding, i.e. expressing the moulding material through a die or nozzle which imparts the desired form; Apparatus therefor
- B29C48/03—Extrusion moulding, i.e. expressing the moulding material through a die or nozzle which imparts the desired form; Apparatus therefor characterised by the shape of the extruded material at extrusion
- B29C48/05—Filamentary, e.g. strands
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
- B29C48/00—Extrusion moulding, i.e. expressing the moulding material through a die or nozzle which imparts the desired form; Apparatus therefor
- B29C48/03—Extrusion moulding, i.e. expressing the moulding material through a die or nozzle which imparts the desired form; Apparatus therefor characterised by the shape of the extruded material at extrusion
- B29C48/07—Flat, e.g. panels
- B29C48/08—Flat, e.g. panels flexible, e.g. films
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
- B29C48/00—Extrusion moulding, i.e. expressing the moulding material through a die or nozzle which imparts the desired form; Apparatus therefor
- B29C48/03—Extrusion moulding, i.e. expressing the moulding material through a die or nozzle which imparts the desired form; Apparatus therefor characterised by the shape of the extruded material at extrusion
- B29C48/09—Articles with cross-sections having partially or fully enclosed cavities, e.g. pipes or channels
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
- B29C48/00—Extrusion moulding, i.e. expressing the moulding material through a die or nozzle which imparts the desired form; Apparatus therefor
- B29C48/16—Articles comprising two or more components, e.g. co-extruded layers
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
- B29C48/00—Extrusion moulding, i.e. expressing the moulding material through a die or nozzle which imparts the desired form; Apparatus therefor
- B29C48/25—Component parts, details or accessories; Auxiliary operations
- B29C48/78—Thermal treatment of the extrusion moulding material or of preformed parts or layers, e.g. by heating or cooling
- B29C48/80—Thermal treatment of the extrusion moulding material or of preformed parts or layers, e.g. by heating or cooling at the plasticising zone, e.g. by heating cylinders
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
- B29C48/00—Extrusion moulding, i.e. expressing the moulding material through a die or nozzle which imparts the desired form; Apparatus therefor
- B29C48/25—Component parts, details or accessories; Auxiliary operations
- B29C48/78—Thermal treatment of the extrusion moulding material or of preformed parts or layers, e.g. by heating or cooling
- B29C48/86—Thermal treatment of the extrusion moulding material or of preformed parts or layers, e.g. by heating or cooling at the nozzle zone
- B29C48/865—Heating
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
- B29C48/00—Extrusion moulding, i.e. expressing the moulding material through a die or nozzle which imparts the desired form; Apparatus therefor
- B29C48/25—Component parts, details or accessories; Auxiliary operations
- B29C48/78—Thermal treatment of the extrusion moulding material or of preformed parts or layers, e.g. by heating or cooling
- B29C48/875—Thermal treatment of the extrusion moulding material or of preformed parts or layers, e.g. by heating or cooling for achieving a non-uniform temperature distribution, e.g. using barrels having both cooling and heating zones
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
- B29C48/00—Extrusion moulding, i.e. expressing the moulding material through a die or nozzle which imparts the desired form; Apparatus therefor
- B29C48/25—Component parts, details or accessories; Auxiliary operations
- B29C48/88—Thermal treatment of the stream of extruded material, e.g. cooling
- B29C48/911—Cooling
- B29C48/9115—Cooling of hollow articles
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
- B29C48/00—Extrusion moulding, i.e. expressing the moulding material through a die or nozzle which imparts the desired form; Apparatus therefor
- B29C48/25—Component parts, details or accessories; Auxiliary operations
- B29C48/88—Thermal treatment of the stream of extruded material, e.g. cooling
- B29C48/919—Thermal treatment of the stream of extruded material, e.g. cooling using a bath, e.g. extruding into an open bath to coagulate or cool the material
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
- B29C48/00—Extrusion moulding, i.e. expressing the moulding material through a die or nozzle which imparts the desired form; Apparatus therefor
- B29C48/25—Component parts, details or accessories; Auxiliary operations
- B29C48/92—Measuring, controlling or regulating
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
- C08J3/00—Processes of treating or compounding macromolecular substances
- C08J3/20—Compounding polymers with additives, e.g. colouring
- C08J3/203—Solid polymers with solid and/or liquid additives
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
- C08J5/00—Manufacture of articles or shaped materials containing macromolecular substances
- C08J5/04—Reinforcing macromolecular compounds with loose or coherent fibrous material
- C08J5/045—Reinforcing macromolecular compounds with loose or coherent fibrous material with vegetable or animal fibrous material
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
- C08J5/00—Manufacture of articles or shaped materials containing macromolecular substances
- C08J5/04—Reinforcing macromolecular compounds with loose or coherent fibrous material
- C08J5/10—Reinforcing macromolecular compounds with loose or coherent fibrous material characterised by the additives used in the polymer mixture
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
- C08L67/00—Compositions of polyesters obtained by reactions forming a carboxylic ester link in the main chain; Compositions of derivatives of such polymers
- C08L67/04—Polyesters derived from hydroxycarboxylic acids, e.g. lactones
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
- B29C2948/00—Indexing scheme relating to extrusion moulding
- B29C2948/92—Measuring, controlling or regulating
- B29C2948/92504—Controlled parameter
- B29C2948/92704—Temperature
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
- B29C2948/00—Indexing scheme relating to extrusion moulding
- B29C2948/92—Measuring, controlling or regulating
- B29C2948/92819—Location or phase of control
- B29C2948/92857—Extrusion unit
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
- B29K2067/00—Use of polyesters or derivatives thereof, as moulding material
- B29K2067/04—Polyesters derived from hydroxycarboxylic acids
- B29K2067/046—PLA, i.e. polylactic acid or polylactide
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
- B29K2105/00—Condition, form or state of moulded material or of the material to be shaped
- B29K2105/0005—Condition, form or state of moulded material or of the material to be shaped containing compounding ingredients
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
- B29K2105/00—Condition, form or state of moulded material or of the material to be shaped
- B29K2105/06—Condition, form or state of moulded material or of the material to be shaped containing reinforcements, fillers or inserts
- B29K2105/16—Fillers
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
- B29K2509/00—Use of inorganic materials not provided for in groups B29K2503/00 - B29K2507/00, as filler
- B29K2509/08—Glass
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
- B29K2511/00—Use of natural products or their composites, not provided for in groups B29K2401/00 - B29K2509/00, as filler
- B29K2511/14—Wood, e.g. woodboard or fibreboard
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
- B29K2995/00—Properties of moulding materials, reinforcements, fillers, preformed parts or moulds
- B29K2995/0037—Other properties
- B29K2995/0059—Degradable
- B29K2995/006—Bio-degradable, e.g. bioabsorbable, bioresorbable or bioerodible
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29L—INDEXING SCHEME ASSOCIATED WITH SUBCLASS B29C, RELATING TO PARTICULAR ARTICLES
- B29L2031/00—Other particular articles
- B29L2031/001—Profiled members, e.g. beams, sections
- B29L2031/003—Profiled members, e.g. beams, sections having a profiled transverse cross-section
- B29L2031/005—Profiled members, e.g. beams, sections having a profiled transverse cross-section for making window frames
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
- C08J2367/00—Characterised by the use of polyesters obtained by reactions forming a carboxylic ester link in the main chain; Derivatives of such polymers
- C08J2367/04—Polyesters derived from hydroxy carboxylic acids, e.g. lactones
Definitions
- compositions and methods relate generally to compositions and methods and more specifically to structural or decorative members such as window and door components, for example, that are made with biopolymers such as polylactic acid (PLA).
- biopolymers such as polylactic acid (PLA).
- compositions and members made therefrom as well as methods of compounding the compositions, methods of enhancing properties of the compositions, and methods of processing the compositions into structural or decorative members.
- Structural and decorative members made by extrusion of polymeric materials are well known in the building industry. For example, many parts of windows, doors, railings, decking, siding, flooring, fencing, trim, and the like are produced by extrusion of polymers such as polyvinyl chloride (PVC) or composites made of PVC and fillers such as wood fiber, other organic and inorganic fillers, binders, and/or reinforcing materials.
- PVC polyvinyl chloride
- Other thermoplastic polymers such as polyethylene, polypropylene, and acrylonitrile butadiene styrene (ABS), along with a variety of thermoset polymers, have also been found useful.
- a common reinforcing material is wood particulate, in the form of sawdust, though other filler or reinforcing materials may also be used.
- a common filler material is wood fiber, though other fillers or reinforcing materials may also be used.
- the extruded members may comprise more than one layer, such as a coextruded outer layer or capping layer that covers an inner base extrusion. Such capping layers may serve to improve weatherability or appearance of the base extrusion or provide an outer surface of a desired texture or character. Capping material may, for example, impart a particular color to some or all of portions of extruded members. It is also common practice to provide capping layers on only part of an extruded member, or to provide two or more different capping layers to different parts of an extruded member.
- PVC polyvinyl styrene resin
- PLA polystyrene resin
- PLA can be produced by fermentation of corn or other renewable resources, and degrades to relatively harmless substances after its useful life when deposited in a landfill or other waste location.
- PLA may also be depolymerized into lactic acid and repolymerized after appropriate processing to allow more economically viable recycling into a wide variety of useful products, thereby reducing the disposal burden.
- PLA is thus recyclable as well as being renewable. It will be understood that while this disclosure is couched primarily in terms of PLA, PLA composites, and compounding and extrusion methodologies, the term biopolymer should be construed to include and encompass all polymers derived from renewable resources, including PLA.
- PLA has proven useful for certain products such as the manufacture of textiles, cups, snack chip bags, and the like, it has been found to suffer significant performance limitations for use in other applications.
- PLA's sensitivity to high temperatures, and particularly its relatively low heat distortion temperature (HDT) has made PLA and PLA composites unsuitable for use in most building construction and other components that may be exposed to the elements.
- HDT heat distortion temperature
- PLA is prone to degradation by hydrolysis, especially at elevated temperatures and humidity levels.
- This inherent aspect of PLA makes it prone to deterioration over time and has further limited its use as a component of structural or decorative members that will be exposed to the elements.
- adhesion of other polymers or coatings to the surface of PLA may be difficult to achieve.
- PLA can be crystallized, and that increased crystallinity can raise the heat distortion temperature of the material. It is also known, however, that the speed of crystallization of PLA is relatively low, which may limit its value in situations where high throughput, coupled with high crystallinity, that is to say rapid crystallization, is needed. This combination of requirements can occur, for example, where structural and decorative members are to be produced by extrusion, and the required crystallization rate is therefore dictated by the line speed of the extrusion process. Such line speeds typically have been far too fast to allow PLA to crystallize before cooling. An additional problem can arise due to the fact that PLA has a rather sharply defined melting point. This can place strict requirements on temperature control and die design in an extruder, and it may be difficult to produce an extruded member from PLA that retains its shape well during cooling.
- Such structural and decorative members may include, for instance, components for windows and doors, railings, decking, siding, flooring, fencing, trim, and other building products.
- fenestration components such as window and door components such as jambs, sills, frames, rails, stiles, extenders, grilles, trim, mull posts, panels and other accessories or components to be made with PLA or other biopolymers that retain sufficient strength at elevated temperatures and that resist hydrolysis and other deterioration for extended periods of time.
- reference to a “member” or any one or more of the specific members mentioned above as well as the terms “structural members” or “decorative members” includes and encompasses all of the above applications.
- PLA compositions and other biopolymer compositions
- production techniques that enable viable members for the applications specified herein. It is to the provision of PLA compositions, methods of enhancing their properties, methods of compounding them, and methods of extruding and capping them that meet the above and other needs that the present disclosure is primarily directed.
- biopolymer-based compositions compounding methods, extrusion methods, capping methods and members extruded or otherwise formed therefrom are disclosed.
- methodologies for significantly enhancing properties such as heat distortion temperature and hydrolysis resistance of such compositions and members so that they are suitable for exposure to the elements for extended periods of time are disclosed.
- a process for extruding an improved formulation of a composition, including a composite containing PLA and wood fiber is disclosed. Additives, treatments, and extrusion conditions have been discovered for increasing crystallization during extrusion, and thus greatly increasing the heat distortion temperature of the resulting extruded members.
- the process involves, among other things, controlling the conditions and temperature of the composition at various stages of the extrusion process to match time-temperature profiles that the inventors have discovered promote rapid nucleation of PLA crystals and promotes further crystallization of the PLA.
- a filler such as wood fiber in the composition has been found to help the extruded member retain its shape after exiting from the extrusion die, thereby simplifying temperature control downstream of the extruder.
- Resulting extruded members having heat distortion temperatures in excess of 100° Celsius (212° Fahrenheit) have been obtained.
- Field experience with window and door products has shown that components having such heat distortion temperatures may perform significantly better in warmer environments than petroleum-based polymers currently in use.
- the present disclosure includes improved formulations for significantly enhancing the resistance of resulting extrusions to hydrolysis and the deterioration that it causes, thereby rendering such extrusions suitable for use in members such as window and door components to be exposed to the environment.
- Formulations for capping material methods to apply the capping material to underlying base extrusions made of the disclosed PLA compositions and for overcoming the inherent difficulty of bonding such capping material to a PLA composition are also disclosed.
- the inventors have discovered that coextruding a capping material over a base extrusion comprising PLA with a filler such as wood fiber can improve various properties of resulting extruded PLA-filler composite members. It has been found for instance that the presence of the capping material has a surprisingly significant effect on such properties as flexural modulus and heat shrink tolerance of extruded members formed of the composite.
- a method of extruding members from PLA-filler composites that results in a member useful for members such as window and door components is disclosed.
- the term neat PLA formulation will refer to a PLA polymer that does not contain fillers, but may or may not contain additives, such as heat or UV stabilizers, colorants, nucleating agents, process aids and hydrolysis inhibitors.
- the term process aid will include any additives for improving the processing of the formulation. Such additives may include metal release agents, lubricants, viscosity modifiers, additives for improving melt strength in extrusion, as well as other additives.
- Process aids can function in a variety of ways, sometimes modifying the polymer, and sometimes depositing onto various surfaces that the polymer contacts during processing, or both. In some cases, process aids may function in more than one way, for example as a lubricant and as a metal release agent. Examples of process aids include waxes, stearates, such as calcium stearate, and polymeric materials. It is contemplated that there may be examples wherein satisfactory results may be obtained without one or more of the disclosed additives.
- compositions of matter with PLA and various fillers and additives suitable for making such members are disclosed, as are a variety of members extruded from the compositions.
- compositions of matter including, for example, the following combinations or compositions, extruded into or for extrusion into a structural or decorative member for use, for example, in the construction industry.
- composition (f) Composition (a) and further including 10% to 90% of a capstock material
- composition comprising a combination of one or more of:
- Thermoplastic polymers for use in the formation of members are disclosed, as are various categories of biopolymers such as plant-oil based biopolymers, protein based biopolymers, fermentation based biopolymers, polyesters derived from renewable resources, and PLA.
- biopolymers such as plant-oil based biopolymers, protein based biopolymers, fermentation based biopolymers, polyesters derived from renewable resources, and PLA.
- a mixture of biopolymer and petroleum based polymers materials is considered less commercially desirable, formulations containing, for example, 75% or more biopolymer mixed with a petroleum based polymers such as acrylic, a family of synthetic or man-made plastic materials containing one or more derivatives of acrylic acid, are possible and within the scope of the invention.
- Members made with PLA containing no fillers, having a ratio of PLA to filler of 100/0, are also disclosed. However, it has been found that a preferred ratio of weight percent PLA to weight percent filler such as wood fiber is between about
- lignocellulose fibers such as wood fiber
- Wood fiber can be sourced from hardwoods and/or softwoods.
- Other biomaterials or other organic materials may also be used as fillers.
- biomaterial will refer to materials of biological origin, such as wood fiber, hemp, kenaf, bamboo, rice hulls, and nutshells. More generally, other lignocellulose materials resulting from agricultural crops and their residues may also be used as fillers.
- Other biomaterials, including proteinaceous materials such as poultry feathers may also find application in some instances.
- Other organic materials such as carbon black, carbon fiber, and the like may also be used as fillers.
- polymeric materials such as thermosetting materials or composites thereof in particulate form may also find application.
- inorganic particulate materials such as metal oxide particles or spheres, glass particles, short glass fibers, or other like materials may be used.
- These fillers may be used either alone or in combination with other organic or inorganic fillers.
- the fillers may be treated in various ways to improve adhesion to the polymeric materials, reduce moisture effects, or provide other useful properties.
- window and door components such as jambs, sills, frames, rails, stiles, extenders, grilles, trim, mull posts and panels; siding components such as siding, trim, soffit, fascia and shakes; decking components such as decking, posts, trim, rails and balusters and other building components are within the scope of the invention.
- capping of extrusions can provide many advantages, including improved crystallinity and, in some cases, improved hydrolysis resistance. It is contemplated that the improvements in capping provided for PLA-filler composites will also apply, to some degree, to neat PLA formulations.
- Disclosed capping materials may comprise PVC, acrylic and other polymers. These capping materials have been found to provide varying levels of resistance to moisture transmission. When co-extruded over the PLA compositions the capping material can act as a moisture barrier that in turn increases the base PLA composition's resistance to hydrolysis. Uncapped structures made of the disclosed compositions also may be appropriate in certain situations, such as interior components of a window or door.
- the inventive techniques raise the heat distortion temperature of members formed from PLA compositions to 100° Celsius (212° Fahrenheit) or greater, which is suitable for use as members for window and door applications.
- the target heat distortion temperature of the composition may be less, such as between 80° Celsius (176° Fahrenheit) and 100° Celsius (212° Fahrenheit) or even less than 80° Celsius (176° Fahrenheit).
- the inventors have developed techniques and formulations for increasing the hydrolysis resistance of members made of PLA compositions to 18 times or more that of a PLA composition that does not contain a hydrolysis inhibitor. It is believed that such enhancement of hydrolysis resistance may be sufficient to permit resulting members to withstand exposure to the elements for extended periods of time.
- FIG. 1 is a schematic illustration of an extruder arrangement used to compound and pelletize a PLA-wood composite for use in a subsequent extrusion process.
- FIG. 2 is a schematic illustration of the primary and co-extruder arrangement used to produce the extruded members tested according to the disclosure.
- FIG. 3 is a cross-sectional view illustrating a generic simplified hollow profile of a member extruded according to the disclosure.
- FIG. 4 is a cross-sectional view illustrating a capped hollow profile of a member extruded with different capping materials on different surfaces according to the disclosure.
- FIG. 5 is a graph illustrating results of testing and showing the relationship between flexural modulus and density for a variety of sample profiles.
- FIG. 6 is a graph illustrating results of testing and showing the relationship between tensile modulus and density for a variety of sample profiles.
- FIG. 7 is a graph illustrating results of testing and showing the relationship between heat shrink and density for a variety of sample profiles.
- FIG. 8 is a graph illustrating results of testing and showing the relationship between density and extruder motor current draw for a variety of sample profiles.
- FIG. 9 is a graph illustrating results of testing and showing the relationship between density and extruder motor current draw for a variety of sample profiles.
- FIG. 10 is a graph of flexural modulus versus capping thickness for a variety of capped sample profiles.
- FIG. 11 is a graph of tensile modulus versus capping thickness for a variety of capped sample profiles.
- FIG. 12 is a graph of heat shrink versus capping thickness for a variety of capped sample profiles.
- FIG. 13 is a graph of density versus capping thickness for a variety of capped sample profiles.
- FIG. 14 is a simplified diagrammatic illustration of a device used by the inventors to measure heat distortion temperature of samples.
- FIG. 15 is a cross-sectional view illustrating a capped hollow profile of a member formed according to the disclosure.
- FIG. 16 is a graph of flexural strength versus complex viscosity for an extruded uncapped sample.
- FIG. 17 is a graph of flexural strength versus complex viscosity for an extruded capped sample.
- FIG. 18 is a graph of complex viscosity versus hours of exposure to 82° Celsius (180° F.), 90% relative humidity for an extruded neat PLA formulation sample with a 1% hydrolysis inhibitor additive.
- FIG. 19 is a graph of complex viscosity versus hours of exposure to 82° Celsius (180° F.), 90% relative humidity for an extruded PLA-wood composite sample with a 1% hydrolysis inhibitor additive.
- FIG. 20 is a graph of complex viscosity versus hours of exposure to 82° Celsius (180° F.), 90% relative humidity for an extruded neat PLA formulation sample with a 2.5% hydrolysis inhibitor additive.
- FIG. 21 is a graph of complex viscosity versus hours of exposure to 82° Celsius (180° F.), 90% relative humidity for an extruded PLA-wood composite sample with a 2.5% hydrolysis inhibitor additive.
- FIG. 22 is a graph of complex viscosity versus hours of exposure to 82° Celsius (180° F.), 90% relative humidity for an extruded neat PLA formulation sample with a 5% hydrolysis inhibitor additive.
- FIG. 23 is a graph of complex viscosity versus hours of exposure to 82° Celsius (180° F.), 90% relative humidity for an extruded PLA-wood composite sample with a 5% hydrolysis inhibitor additive.
- FIG. 24 is a graph showing hours to 50% complex viscosity at 88° Celsius (190° F.) and 90% relative humidity as a function of percent of a hydrolysis inhibitor additive for neat PLA formulation samples.
- FIG. 25 is a graph showing hours to 50% complex viscosity at 88° Celsius (190° F.) and 90% relative humidity as a function of percent of a hydrolysis inhibitor additive for PLA-wood composite samples.
- FIG. 26 is a graph of complex viscosity versus hours of exposure to 60° Celsius (140° F.) and 90% relative humidity for a PLA-wood composite sample with a 2.5% hydrolysis inhibitor additive.
- FIG. 27 is a graph of complex viscosity versus hours of exposure to 60° Celsius (140° F.) and 90% relative humidity for a PLA-wood composite sample with a 5% hydrolysis inhibitor additive.
- Tests as detailed below show the effects of co-extruding a capping material onto the surface of extruded members made of PLA-wood composites as well as neat PLA formulations.
- the tests were designed to investigate the effects of capping on density, flexural modulus, tensile modulus, heat shrink, crystallization, heat distortion temperature, hydrolysis resistance and adhesion of various capping materials to PLA-wood composites as well as neat PLA formulations. The conditions and results of these tests are described below.
- a composite comprising PLA and wood fiber for use as a base extrusion was prepared in pellet form according to the procedures set forth in detail below.
- the pellets were fed into a profile extruder, as detailed below, which produced the simple square extruded members shown in FIGS. 3 and 4 .
- Extrusions were made with and without capping material co-extruded onto the surface of the PLA-wood composite base extrusions, and with capping materials of different compositions, as described in Sample Profiles 2-8 below.
- two extrusion runs were made with PLA, wood fiber, and a process aid fed directly into the extruder as described in Sample Profile 2, without going through a separate compounding and pelletizing step to test the viability of direct extrusion for PLA-wood composites.
- Density of the specimens was measured using an AccuPycTM 1330 gas displacement pycnometer, available from Micromeritics Instrument Corporation, 4356 Communications Drive, Norcross, Ga., 30093-2901. The gas used was nitrogen. Specimens were obtained by cutting the side of the extruded rectangular sample profiles into strips 1′′ wide ⁇ 1′′ tall. The specimen was weighed and then placed into the pycnometer for density measurement.
- Specimens were prepared by cutting 0.5′′ ⁇ 3′′ ⁇ 0.09′′ strips from the sides of the extruded rectangular sample profiles. Flexural modulus was tested according to ASTM D790-03 with simple beam supports spaced at a distance of 1.53 inches and the contact points having a radius of 0.043 inches. Force was applied using an Instron 5500R tensile tester. Flexural strength was calculated using the maximum value on the force versus displacement curve generated as outlined in ASTM D790-03.
- Specimens were prepared by cutting 0.5′′ ⁇ 6′′ ⁇ 0.09′′ strips from the sides of the extruded rectangular sample profiles. The specimens were conditioned at standard ASTM conditions (21° Celsius (70° F.)/50% RH). Tensile modulus was tested using an Instron 5500R tensile tester, using a gauge length of 4.00 inches and a cross head speed of 0.200 inches per minute. The data was processed using Instron Series IX Automated Materials Testing System Version 5.25 software with Testing Module Rev. 1.16.
- Specimens were prepared by cutting 12.0 inch long sections from the extruded rectangular sample profiles. The specimens were kept at room temperature for a sufficient time to assure equilibration. A first scribe mark and a second scribe mark were then made using a scribing tool having scribing styli spaced from each other at a fixed distance of 10.0 inches. The specimens were then placed on a flat surface in a forced air oven that had been preheated to 82.0° Celsius and that could maintain that temperature to within ⁇ 3.0° Celsius. The specimens were left in the oven for 60 minutes. The specimens were then removed from the oven and allowed to cool to room temperature.
- One of the scribe styli was placed at the first original scribe mark, and a third scribe mark was made at the fixed distance of 10.0 inches. The distance between the original second scribe mark and the newly applied third scribe mark after heat treatment was measured. The distance, in inches, between the two scribe marks was divided by 10 to obtain the fractional shrinkage. The fractional shrinkage was multiplied by 100 to obtain percent shrink as a result of the heat exposure.
- Capping adhesion was measured according to ASTM D5179-02, wherein an aluminum stud or button having the dimensions prescribed therein was adhered to the capping material extruded onto the surface of PLA-wood composite base extrusions. After curing of the adhesive, the button was pulled from the extruded members using an Instron Model 4505 tensile tester equipped with a 1124 pound load cell. This instrument measured the force at the time of fracture between the capping material and the PLA-wood composite base extrusion on which it was applied. Resulting data indicate the force required to remove the capping material from the underlying extruded PLA-wood composite using a 3 ⁇ 4′′ diameter button.
- the nature of the break between the capping material and the underlying base extrusion was also noted.
- the break was reported as either adhesive or cohesive failure, depending upon whether the fracture interface occurred between the surface of the PLA-wood composite base extrusion and the capping material (adhesive failure) or whether portions of the PLA-wood composite base extrusion or the capping material fractured at locations other than at the interface between them (cohesive failure). In the latter case, portions of either the capping material or the PLA-wood composite adhered to the other surface after failure.
- wood fiber for incorporation into a polymer composite is described in some detail in U.S. Pat. No. 6,280,667 owned by the assignee of the present disclosure. This patent is hereby incorporated by reference in its entirety.
- wood fiber was classified first through a US Standard 30 mesh screen and then an 80 mesh screen, with the wood fiber that passed the 30 mesh screen but was retained in the 80 mesh screen being used in preparing the PLA-wood composite.
- the wood fiber so obtained was fed into barrel section B 1 of a ZSK 25 mm extruder running at 300 rpm and was heated to approximately 1500 Celsius as it passed into section B 2 , where water vapor was allowed to escape through vent V 1 .
- the heated and dried wood fiber was further heated and further dried in barrel sections B 3 and B 4 .
- the wood fiber then passed into section B 5 , where NatureWorks PLA pellets obtained from NatureWorks LLC of Minnetonka, Minn., were added, using a gravimetric metering side feeder.
- the PLA pellets were added in an amount sufficient to produce the desired composite of PLA and wood fiber.
- the term compounding will refer to the process of combining a polymeric material with at least one other ingredient, either polymeric or non-polymeric, at a temperature sufficiently elevated to allow the ingredients to be mixed into a molten mass.
- the composite was then heated in barrel sections B 6 and B 7 to about 1600 Celsius and devolatilized through vacuum vent V 2 in section B 8 , resulting in a molten composite.
- the composite was further compounded at 170° Celsius in barrel sections B 9 -B 11 , from which it dropped into a second single screw extruder E 2 .
- Extruder E 2 was equipped with vacuum vent V 3 for further devolatization of the composite, and was operated with a barrel temperature of 170-175° Celsius and a screw speed of 38 rpm.
- the pelletizing die produced small cylindrical pellets of PLA-wood composite having a density of about 1.29 gm/cc. These pellets, in turn, were fed to a production scale profile extruder as described below to extrude the various sample profiles from which specimens were taken for testing.
- Extruder 200 is a production scale Davis Standard GC8 61 mm conical twin screw extruder with gravimetric feeders 202 and 204 for feeding both primary materials and additive and/or capping materials to the extruder.
- the extruder was further equipped with a vacuum port or vent 206 for controlled devolatilization of (removal of moisture from) the molten material. Heating and other temperature adjustments and controls conventional to extrusion equipment were also components of the extruder.
- the PLA-wood composite pellets were fed into the extruder in a gravimetrically metered manner through one of the feeders 202 , a technique known as metered feeding.
- Extruder temperature also known as melt temperature, was adjusted by removing the vacuum connection from the devolatilization port and visually monitoring the rheology of the molten material as it passed the port.
- extrusion die 210 was made up of primary die body 212 and capping plate or coextrusion die 214 , which could be used to coextrude an outer or capping layer onto the PLA-wood composite base extrusion.
- Coextrusion die 214 was fed by extruders 222 and 224 , each of which applied capping material to two adjacent sides of the PLA-wood composite base extrusion.
- the coextruded capping material applied by extruders 222 and 224 can be the same or different. For example, in FIG. 4 adjacent sides 43 and 44 can be capped with a first material, and adjacent sides 41 and 42 can be capped with a second material.
- the extrusion apparatus further comprised a conventional calibration die 230 for applying vacuum to size and maintain the desired final shape of the extruded member as the member began to cool.
- the extruded member passed through cooling tank 240 , aided by Greiner Cat Pul puller 250 , which was a pair of sectioned belts of conventional design.
- the continuous extruded member was cut into 4 foot lengths by traveling cut-off saw 260 , also of conventional design, wherein the saw traveled with the extrusion while sawing, to allow continuous operation of the extruder during sawing. Specimens from the resulting sample profiles were subjected to the various tests described above.
- the actual measured density, shown in Table 7, is about 1.3761 gm/cc. This indicates that the composite in Sample Profile 1 was well compressed by the extruder and relatively free of voids. It will also be noted from Table 5 that the current drawn by the extruder motor was relatively high while extruding Sample Profile 1 compared to other sample profiles. This too may be an indicator of good compression of the molten material since the motor current draw indicates a high motor torque required to compress and move the molten material through the extruder.
- the addition of the XL-623 reduced the chattering effect at primary die body 212 to an insignificant level, while also reducing the current drawn by the extruder motor to 12.5 amperes for Sample Profile 2, a significant reduction from the draw of 74.0 amperes seen for Sample Profile 1.
- the addition of the XL-623 also resulted in a reduction in the density of the Sample Profile 2 to 1.1361 gm/cc, which is well below the theoretical density of a well compressed 60% PLA and 40% wood fiber composite.
- Sample Profiles 4-7 were extruded in the same general manner as in Sample Profile 2 using the PLA-wood composite pellets produced as described, but with varying extrusion conditions and coextruded capping materials as shown in Table 5 and in Tables 1-4. Extrusion of Sample Profiles 4-7 illustrate, among other things, that a range of properties can be obtained by (1) using different capping materials; (2) using the same capping materials on all four sides of an extruded member; (3) using different capping materials on different sides of the extruded member; and (4) using a capping material on only two adjacent sides.
- Adhesion of Capping Material B for Sample Profile 5 was tested according to ASTM D5179 and found to be low and variable, with the minimum adhesion being less than half of the average of samples taken along the 48′′ length of the extruded-sample profile. Failure occurred at the adhesive interface, not in the PLA-wood composite base extrusion or in the capping layer. Adhesion for Capping Material D of Sample Profile 7 was quite high, with failure occurring in the PLA-wood composite base extrusion, rather than at the adhesive interface between the base extrusion and the capping layer. Adhesion of Capping Material A of Sample Profile 9 was found to be better than that of Capping Material B of Sample Profile 5, but failed at the adhesive interface and not in the PLA-wood composite base extrusion or capping layer.
- Sample Profile 8 PLA 4060D pellets from NatureWorks LLC were mixed with Confluence brand firewood pellets in a ratio of about 60 wt % PLA to about 40 wt % wood, and fed into extruder 200 . Capping material A was coextruded onto the PLA-wood composite base extrusion. The mechanical properties of the resulting Sample Profile 8 are seen to be relatively poor compared to the other extruded sample profiles, as shown by the results in Table 7.
- PLA 4060D pellets were mixed with wood fiber in a ratio of about 60 wt % PLA to about 40 wt % wood fiber to form a blend and fed directly, without prior compounding and pelletization, into the extruder 200 . Although these materials were mixed prior to being fed in to the extruder, they could also be fed individually and mixed within the extruder. Process aid XL-623 was also blended into the mixture in an amount of about 0.6 wt % of the final composite. The PLA-wood composite base extrusion was capped with coextruded capping material A on all sides. The gravimetric metering devices on extruder 200 were not used.
- the mix was allowed to feed at a rate determined by the extruder screws, a feed technique known as flood feeding.
- a feed technique known as flood feeding.
- Sample Profile 9 which had relatively good mechanical properties compared to Sample Profiles 1-8. This may indicate that direct extrusion of the components of a PLA-wood composite so that they are mixed and compounded in the primary extruder itself is viable as well as when the components are compounded and pelletized in a separate process.
- Sample Profile 10 the extrusion approach and PLA-wood composite formulation of Sample Profile 9 was used, but without coextruding any capping material onto the base extrusion. As seen in Table 7, the improved properties of the capped Sample Profile 9 over the uncapped Sample Profile 10 tends to indicate that the capping material produces improvements in mechanical properties, increased density, and reduced heat shrink.
- the extruded members illustrated in FIGS. 3 and 4 may be used, for example, as vertical members, or balusters, in stair and porch railings, as well as in picket fences and the like. In such applications, similar to the needs of window and door components, lateral or bending loads are the primary loads borne by the profiles during use. As a result, flexural modulus is an important mechanical property for the sample profiles above. Table 7 shows test results of flexural modulus, density, and other measurements performed on the various sample profiles extruded as described above.
- FIG. 5 is a graph of the flexural modulus results taken from Table 7, plotted against density, also taken from Table 7. Reference numbers on the graph refer to the sample profile numbers from Tables 5, 6 and 7.
- FIG. 5 illustrates that capping tends to increase the density of an extruded sample profile.
- Sample Profiles 3 and 10 with no capping applied have the lowest density
- Sample Profile 4 which is capped on only two adjacent sides, has a slightly higher density, though not as high as the fully capped Sample Profiles 1 and 9.
- An exception to this may be Sample Profile 1, which tends to show that the absence of the XL-623 process aid appears to increase density without a commensurate increase in flexural modulus.
- Capping of a PLA-wood composite base extrusion did not affect tensile modulus.
- FIG. 6 which graphs tensile modulus against density, capping appears to increase tensile modulus for Sample Profiles 2 and 3, but not for Sample Profiles 9 and 10.
- Sample Profiles 4-7 is shown that the particular choice of capping material has little or no effect on tensile modulus, even though it is shown to have some effect on density.
- coextruding a capping material onto a PLA-wood composite base extrusion provides no particular advantage where the resulting profile is to be exposed primarily to tensile forces.
- FIG. 7 which graphs percent heat shrink versus density, it is shown, in comparing Sample Profile 2 with Sample Profile 3, and Sample Profile 9 with Sample Profile 10, that capping tends to reduce heat shrink. Moreover, it is shown that by increasing density heat shrink is reduced, although the scatter in the data in FIG. 7 would indicate that other factors also may contribute to heat shrink. It is concluded that applying a capping material to a PLA-wood composite base extrusion reduces heat shrink of the extrusion when exposed to relatively high temperatures.
- Increased density of an extruded sample improves mechanical properties and decreases heat shrink of the sample profile. Accordingly, factors contributing to or indicating increased density are presented.
- One such factor is the current drawn by the motor driving the extruder screws during extrusion. This, in turn, is a measure of the torque that the extruder screw requires, and indicates the level of compression the extruder applies to the molten material.
- FIG. 8 which graphs density against extruder motor current, density generally increases with increased motor current for sample profiles extruded using metered flow of pellets to the extruder.
- Sample Profiles 9 and 10 which were extruded using unmetered or flood feeding, do not fit this pattern, since capping produces an increase in density without an increase in motor current. However, it should also be noted that the motor current for Sample Profiles 9 and 10 is higher than the previous samples where profiles were extruded using metered flow of composite pellets.
- FIG. 9 shows the data of FIG. 8 , with the density scale expanded.
- the inherent heat distortion temperature (HDT) of PLA is generally too low for use in hot environments or in direct sunlight. These are, of course, the very environments within which window and door components and other building product members must perform.
- the inventors conducted testing in an effort to determine whether the HDT of a PLA composition can be raised to a value that makes the corresponding member viable for use when exposed to the environment for long periods of time. Such testing and results thereof are discussed below.
- samples were extruded with a laboratory extruder with various run conditions and compositions.
- Various formulations of a PLA-wood composite shown as Samples 1-5 in Table 8 below, were compounded and pelletized as described above and extruded to form substantially flat samples using a Brabender laboratory extruder.
- the formulation shown as Sample 6 in Table 8 was extruded in a production scale twin screw extruder into a rectangular sample profile. Specimens were taken from the resulting samples and subjected to testing to determine their heat distortion temperatures.
- the experimental formulations were prepared by mixing the PLA, wood fiber, and various additives in the compounding extruder and pelletizing the resulting blends as detailed above for extrusion in the subsequent profile extrusion operation.
- PLA 4032D is a substantially homopolymeric polylactic acid obtained from NatureWorks LLC, of Minnetonka, Minn. It is preferred that the PLA be substantially homopolymeric so as to promote crystallization. It will be appreciated that since lactic acid is a chiral compound, PLA can exist either as PLA-L or PLA-D. As used herein, the term homopolymeric PLA will refer to either PLA-L or PLA-D, wherein the monomeric units making up each polymer are all of substantially the same chirality, either L or D.
- PLA-L and PLA-D will, when combined, co-crystallize to form stereoisomers, provided that the PLA-L and PLA-D are each substantially homopolymeric, and that, as used herein, PLA containing such stereoisomers is also to be considered homopolymeric.
- nucleating agents can play a significant role in improving the speed and degree of polymer crystallization.
- Nucleating agents can be either organic or inorganic, and specific nucleating agents are more suitable than others for particular polymers.
- Talc in the form of a finely ground powder, has been found to be a particularly suitable inorganic nucleating agent for PLA.
- Suitable organic nucleating agents for polyesters include metal salts of aromatic sulphonates, as disclosed in published U.S. Patent application 2007/0270535A1, incorporated herein by reference.
- One particularly useful salt of an aromatic sulphonate is LAK-301, which is commercially available from Takemoto Oil and Fat Co, LTD, of Japan. It is believed that there may be advantages to using a combination of organic and inorganic nucleating agents to achieve optimal crystallization.
- XL-623 is a process aid that acts as a metal release agent and possible stabilizer.
- Calcium stearate is a process aid that acts as a lubricant and is used in the processing of polymeric materials.
- Wood fiber was prepared as described above and mixed with PLA. Depending on the formulation being prepared, talc, LAK 301, and the other ingredients were added to the mixture in the amounts shown in Table 8. The combined blend was then compounded and pelletized in the manner detailed above to produce pellets for use in extruding samples for testing.
- the PLA-wood composite pellets for each sample were fed into a Brabender single screw extruder using a die that produced a generally flat extruded member having a thickness of 0.090 inches to 0.100 inches and a width of about 1.0 inch.
- the extruded member was deposited onto a moving belt with a speed adjusted to match the extrusion speed and cooled as the belt carried the material away from the extruder.
- Three different cooling rates of the extruded member on the belt were used, along with different initial melt temperatures within the extruder.
- Cooling temperature profiles were determined by extruding a neat PLA formulation and embedding a thermocouple in the extruded member as it exited the die. The thermocouple traveled with the extruded member to the end of the cooling belt while sending temperature data to a data logger, thereby producing time-temperature profiles for each cooling rate.
- Initial melt temperatures were measured using a thermocouple located in the die.
- the different cooling rates produced samples with surprisingly different material properties, including different heat distortion temperatures. This was due at least in part, it is believed, to differences in the amount of crystallization occurring during the cooling process. Early onset of nucleation of PLA crystals influenced by lower melt temperatures also is a contributing factor. Because crystallization of the PLA is a significant factor in determining the HDT of each extruded sample, and because the temperature range of 100° Celsius to 120° Celsius is a particularly significant range in the crystallization behavior of PLA, each of the time-temperature profiles corresponding to the cooling rates was characterized by the time the extruded sample spent in that temperature range. The three cooling rates, and the resulting times within the critical range were:
- Slow cooling rate heat lamps were placed over the belt allowing the sample's time spent in the temperature range of 100° Celsius to 120° Celsius to be in the range of 50 seconds to 275 seconds as measured by the thermocouple.
- Fast cooling rate either compressed air was blown on the sample immediately upon exiting the die or the sample was immersed in water at a temperature of about 10° Celsius (50° Fahrenheit) in the cooling tank. In either case the cooling method allowed the sample's time spent in the range of 100° Celsius to 120° Celsius to be in the range of less than 15 seconds as measured by the thermocouple.
- cold crystallization refers to taking a member that has fully cooled, reheating it and holding it at a somewhat elevated temperature, that is below its melt temperature, for a longer period of time than might be available in other processes, such as extrusion.
- the temperature and time can be selected to achieve the desired level of crystallization.
- a cold crystallization temperature range that has been found useful for PLA-wood composites is 100° C. to 120° C., however temperatures above or below this range can also increase crystallinity depending on composition of the member.
- Specimens for heat distortion testing were obtained by cutting the resulting samples into pieces having a length of approximately 6 inches and a width of about 0.52 inches. The specimens were extracted from approximately the center of the extruded sheet to avoid any irregularities at the edges.
- Heat distortion temperature was measured using the test fixture shown in FIG. 14 .
- Specimens were placed edgewise in the test fixture, with the 0.52 inch dimension extending in the vertical direction. More specifically, each specimen 20 was placed on cylindrical supports 22 and 24 , which were located a distance L apart. L was chosen to be 4.0 inches for the tests disclosed herein and the specimens 20 were held in an edgewise vertical orientation by pairs of vertical shafts 23 and 25 . The shafts in each pair were spaced at a distance slightly greater than the thickness of the sample to hold specimen 20 in a stable vertical position without gripping it in a way that would cause measurement errors.
- a deflection force of 500 grams was applied to each specimen 20 at a point midway between cylindrical supports 22 and 24 .
- the deflection force was applied by a BEI 9600 spring loaded position sensor 26 having a position sensing shaft 271 . Movement of shaft 271 in the vertical direction, in or out of sensor 26 , induces a change in resistance that is measured and calibrated to indicate distance moved. Shaft 271 pressed against a second shaft 272 held in place by bracket 29 . Shaft 272 then contacted specimen 20 , thereby applying a deflection force to the specimen.
- the 500 gram force was therefore the sum of the spring force from sensor 26 and the weight of shaft 272 .
- Calibration of the apparatus to produce a precise value of 500 grams was achieved by replacing specimen 20 with a balance to measure precisely 500 grams and adjusting the position of sensor 26 relative to bracket 28 until a force of 500 grams was obtained.
- the test fixture, along with specimens 20 was placed in oven 200 and gradually heated until the specimens 20 softened sufficiently to deflect 0.1 inches, as measured by sensor 26 , under the 500 gram load applied by sensor 26 and shaft 272 .
- the oven temperature was measured using a thermocouple embedded in a second specimen having substantially the same dimensions as specimen 20 and placed proximate to each specimen 20 in oven 200 . Heating of oven 200 to the heat deflection temperature of the specimens generally occurred over a period of about one hour.
- the oven temperature was limited to 130° Celsius.
- the heat deflection temperature was found to be somewhat greater than 130° Celsius.
- projected values of heat distortion temperature were calculated by linear extrapolation of deflection as a function of oven temperature in the region just below an oven temperature of 130° C.
- Table 9 Sample Compositions and Extrusion Conditions and Heat Distortion Temperature Measurements Laboratory Extruder MELT COOLING LAK-301 TALC SAMPLE TEMP, ° C. MODE % % HDT ° C.
- samples in the table were formulated with various combinations of nucleating agents, in particular LAK-301 and talc, extruded at various melt temperatures, and cooled either with air cooling (medium cooling rate) or water cooling (fast cooling rate).
- the slow cooling rate using heat lamps was also used, but it was felt that this cooling method might have limited value in a manufacturing setting, and for this reason samples using the slow cooling rate were not tested for heat distortion temperature.
- Melt temperature was measured in the extrusion die of the Brabender laboratory extruder by a thermocouple. It is noteworthy that the range in measured heat distortion temperature (HDT) of 53° Celsius to 146° Celsius is surprisingly large, considering the relatively small changes in extrusion and cooling conditions and in the nucleating agents used.
- HDT measured heat distortion temperature
- Crystallization proceeds first by a nucleation phase (referred to herein as “nucleation” or “nucleation of PLA crystals”), which can only begin when the temperature reaches a certain relatively higher range, followed by a crystal growth stage (referred to herein as “crystallization” or “further crystallization”) that occurs at a relatively lower temperature range.
- nucleation or “nucleation of PLA crystals”
- crystal growth stage referred to herein as “crystallization” or “further crystallization”
- the material in Sample 21 spent less than 15 seconds in the temperature range of 100° Celsius to 120° Celsius (the range in which most crystal growth takes place), yet exhibited a HDT value of 142° C., a value that would be expected in a well crystallized polymer undergoing a longer period of crystal growth.
- Sample 6 in Table 8 The formulation of Sample 6 in Table 8 was selected based upon the results from Samples 1-5 (extruded in the laboratory extruder).
- the formulation was pelletized as described above and extruded using the production scale Davis Standard GC8 61 mm conical twin screw extruder to investigate the scaling of the HDT phenomena noted from the laboratory extruder tests of Samples 1-5. Rectangular extrusion members were produced using various calibration die cooling techniques and various final cooling techniques. PLA-wood composite pellets were fed into the extruder in a gravimetrically metered manner. Extruder temperature was adjusted by removing the vacuum connection from the devolatilization port and visually monitoring the molten material as it passed the port. The melt temperature was adjusted until the pellets were not completely fused at the devolatilization port, but rather appeared to have a somewhat lumpy texture.
- FIG. 15 depicts a capped hollow extruded member 400 which includes a hollow space 401 defined by base extrusion layer 402 , wherein all four sides were capped with the same capping material 404 . Uncapped extrusions were extruded by turning off coextruders 222 and 224 ( FIG. 2 ).
- the extruder included a calibration die 230 for providing the final shape to the extruded member by applying a vacuum to the outside of the moving extrusion.
- the body of the calibration die had internal cooling channels through which water was circulated for primary cooling of the calibration die itself.
- secondary cooling could be provided by cooling water circulating over and around the extruded member as it moved through the calibration die.
- a final cooling tank 240 which could be filled with water for faster cooling (water cooling) or not filled for slower cooling (air cooling), was disposed downstream of the calibration die. After exiting the calibration die, the extruded member passed through the final cooling tank 240 . If the final cooling tank was filled with water, the final cooling stage was designated as water cooling, while if the final cooling tank was not filled with water, the final cooling stage was designated as air cooling.
- An additional mode was also used for some of the extruded members wherein the extruded member moved first through a shortened water cooling phase followed by an air cooling phase. This mode was designated as water and air cooling.
- a self-contained temperature logging device was inserted into the hollow of a capped extruded member and located at various locations downstream of calibration die 230 .
- the logging device was maintained in position by a magnet on the outside of the moving extruded member and was allowed to travel downstream with the extruded member for about two minutes, during which time the temperature of the interior of the extruded member was continuously measured and logged.
- the logged temperature data showed that the total time during which the extrusion temperature was above 100° Celsius but below 120° Celsius (the crystallization temperature range) was approximately 20 seconds. Temperature measurements were not taken for the water or for the water and air cooling modes.
- the HDT test results indicate that the highest HDT of 135° Celsius is obtained with no secondary cooling in the calibration stage and air cooling in the final cooling stage, especially when a capping layer is applied. This is consistent with the observation that early initiation of nucleation of the PLA crystals as the material is extruded followed by longer times in the crystallization temperature range as it is cooled increases the completeness of crystallization within the polymer, thus increasing HDT.
- Compositions with HDT values above about 80° Celsius, and particularly above about 100° Celsius are believed to be commercially viable for use as members such as window and door components that are to be exposed to the elements for extended periods of time
- Hydrolysis is a chemical reaction in which water reacts with a chemical compound to produce other chemical compounds. It typically involves the splitting of a bond within the chemical compound and the addition to the chemical compound of the hydrogen cation and the hydroxide anion from the water.
- Polyester polymers in general, and polyesters made from renewable sources including PLA in particular are susceptible to hydrolysis, which breaks down chemical bonds in the polymer chains resulting in the progressive degradation of the polymer and of members made therefrom when exposed to moisture. While this degradability is desirable for items that are intended to be biodegradable after a short period of use, it is completely unacceptable for members used for window and door components and other building products. Such members must withstand exposure to the elements for extended periods of time without degrading. Accordingly, if PLA or other biopolymers are to be used to fabricate such members, their natural tendency to degrade through hydrolysis must be inhibited. The inventors have discovered that this can be accomplished as described in the following discussion.
- hydrolytic stability of a polymeric material refers to the degree to which the material retains its mechanical properties under hydrolytic conditions.
- Hydrolytic conditions refers to exposure to elevated temperature and humidity for an extended period of time.
- a mechanical property that is of particular interest for structural members, particularly for use as window and door components, is flexural strength which is related to flex modulus. This is because many of the loads encountered by various structural components of windows and doors are flexural in nature.
- Another set of properties of interest are those obtained by dynamic mechanical rheometry, namely storage modulus, loss modulus, and complex viscosity.
- Hydrolysis can result in the loss of molecular weight of a polymer, along with accumulation of monomers and other lower molecular weight species. These changes can affect both the dynamic storage modulus and loss modulus of a member formed of the polymer. It has been found that the complex viscosity, which combines the effects of both dynamic storage modulus and loss modulus, is a particularly useful property for evaluating the effects of hydrolysis on a polymer. It has also been found that the complex viscosity correlates positively with flexural strength of a sample, while at the same time indicating the occurrence of hydrolysis prior to measurable loss in flexural strength. Thus, tracking complex viscosity versus a variety of other parameters can be a good indicator of the resistance of a polymer to the detrimental effects of hydrolysis.
- PLA is particularly susceptible to hydrolysis, especially when exposed to conditions of elevated temperature and humidity; conditions commonly encountered by window and door components and other building products. It is further known that the rate of hydrolysis can be reduced by blending carbodiimide-containing chemical compounds with the PLA. It has been discovered by the inventors, however, that composites containing PLA and wood fiber suitable for forming members exhibit a higher rate of hydrolysis than PLA alone. Further, when wood fiber is present, carbodiimide-containing chemical compounds are less effective in reducing the rate of hydrolysis. It has further been discovered that the addition of higher amounts of carbodiimide-containing chemical compounds can, to a significant degree, overcome the detrimental effects of the wood fiber on hydrolytic stability.
- Mechanical properties that are particularly sensitive to hydrolysis are the viscoelastic properties measured by dynamic mechanical testing. These properties include G′, or storage modulus, G′′, or loss modulus, and ⁇ *, or complex viscosity. It has been found that changes in these properties due to hydrolysis can occur and be detectable before deterioration in other mechanical properties, such as flexural strength, become detectable. Accordingly, in order to investigate hydrolysis induced degradation of mechanical properties in members formed of PLA, dynamic testing of specimens was conducted by the inventors using a Rheometrics RDA II Dynamic Analyzer, which is a parallel plate rheometer available from Rheometrics, Inc., Piscataway, N.J.
- This instrument controls the temperature of a specimen being tested while subjecting it to an oscillating stress over a range of frequencies. Specimens can be tested at different temperatures and the temperature data shifted, according to the principle of time-temperature superposition, to form a master curve that can be used to predict sample properties at other temperatures. This process is described, among other places, in standard textbooks on the rheology of polymers (See e.g. Rosen, Steven L., Fundamental Properties Of Polymeric Materials , Wiley Interscience, LC TA 455.P58R63, ISBN 0-471-08704-1, pp. 256-263 and pp 272-276, which is hereby incorporated by reference).
- a single test temperature can be chosen as the standard temperature, and data produced for different specimens tested at that temperature can be compared.
- testing over a range of frequencies of oscillation applied to a specimen can provide a great deal of useful information.
- comparing test results from specimens at a single testing frequency can also provide useful information, especially when comparisons of properties of different samples tested at that frequency can be made.
- Tables 12-14 tabulate information referred to below in describing the testing methodology employed by and discoveries made by the inventors when investigating hydrolysis in compositions containing PLA.
- Table 12 shows the base formulation of a PLA-wood composite used for the testing described below. It will be noted that this formulation is based upon the formulation used in Samples 19-22 above that demonstrated good HDT performance when extruded under favorable conditions.
- This formulation was varied by including or excluding wood fiber and by adding various weight percentages of hydrolysis inhibitors, and the resulting variants were subjected to the testing and analysis detailed below.
- Table 13 tabulates testing results for a number of variants of the basic formulation, including formulations without any wood fiber or other fillers, and Table 14 shows two PLA-wood composite formulations made to test the impact of including different quantities of a hydrolysis inhibitor containing a carbodiimide, in this case Stabaxol I which is a monomeric carbodiimide made by Rhein Chemie of Chardon, Ohio, to the formulation.
- carbodiimide containing compounds may also be useful, such as Stabaxol I LF, which is a monomeric compound containing carbodiimide groups, and Stabaxol P, which is a polymeric material containing carbodiimide groups, both also made by Rhein Chemie.
- Stabaxol I LF which is a monomeric compound containing carbodiimide groups
- Stabaxol P which is a polymeric material containing carbodiimide groups
- Other compounds that contain carbodiimide groups and that are known to have stabilizing effects on polyesters are disclosed in U.S. Pat. No. 5,210,170 and U.S. Pat. No. 5,614,483, both incorporated herein by reference.
- U.S. published patent application 2010/0093888A1 which discloses carbodiimide compounds particularly suited for stabilization of PLA, is also incorporated herein by reference.
- Sample 31 a member having a rectangular profile was extruded from the PLA-wood composite of Table 12 using the production scale Davis Standard twin screw extruder described above. Sample 31 did not have a capping layer. The extruded member was cooled using about 10° to 16° Celsius (50° to 60° Fahrenheit) water.
- Sample 32 a member having a rectangular profile was extruded from the PLA-wood composite of Table 12 using the production scale Davis Standard twin screw extruder described above. Sample 32 included the capping material described in Table 10 co-extruded over the PLA-wood composite base extrusion.
- Disk-shaped control specimens were cut from the sides of the resulting extruded member of both Samples 31 and 32 prior to exposure to any elevated temperatures or humidities. These specimens were tested using the RDA II Dynamic Analyzer at temperatures ranging from about 140° Celsius to about 240° Celsius. The temperature data was shifted using shift factors that produced a continuous master curve of ⁇ * as a function of frequency, as prescribed by the Boltzman principle of time-temperature superposition. The value of ⁇ * at 10 Hertz was selected as the standard for comparison among samples. The results from this testing provided control data that the various test conditions described below were compared against.
- Strips of material were also cut from the sides of the extruded members and exposed to the same combinations of temperature and humidity conditions for the same times as used for the disk-shaped specimens. These strip-shaped specimens were tested for flexural strength according to ASTM D 790-03. Tests for flexural strength, which produced flexural modulus data, were run for each specimen until the specimen failed, and the stress in the most highly stressed element of the specimen at failure was calculated using Instron Series IX software. The unexposed control specimens were also tested for flexural strength in the same manner. The results and discoveries resulting from the testing are discussed below.
- FIG. 16 is a graph showing flexural strength plotted against complex viscosity ⁇ * for samples without capping extruded from the formulation of Table 12 and exposed to the 18 permutations of temperature, humidity, and exposure time conditions described above. More specifically, the measured flexural moduli for the various levels of exposure to temperature and humidity are plotted against the corresponding values of ⁇ *. As can be seen in FIG. 16 , for values of ⁇ * above 3000 Pa-sec (Pascal-seconds), relatively large changes in ⁇ * can occur with a relatively small effect on flexural strength. The higher values of ⁇ * correspond to shorter exposure times, lower relative humidity, and lower temperatures.
- Samples 33 to 38 were prepared by adding the ingredients specified in Table 13 at the corresponding weight percents to a Brabender fusion bowl.
- the molten material from the fusion bowl was transferred to a Wabash press, where it was compressed into a sheet having a thickness of about 0.1 inches.
- specimens in the form of disks having a diameter of about 1.0 inches were cut from the sheet, using a standard hole punch. These disks were used for dynamic mechanical analysis, to determine ⁇ * for the samples.
- appropriately dimensioned strips were also cut from the pressed sheet. This method of specimen preparation was used for all samples that used the Brabender fusion bowl.
- Sample 33 Even though significant hydrolysis occurs within only a few hours, it is seen that after about 75 hours, Sample 33 still retains about 50% of its original value, as represented by ⁇ * for the control specimen plotted at zero hours in FIG. 18 . Beyond 75 hours, Sample 33 still exhibits significant values of ⁇ * for up to 100 hours or more, and ⁇ * does not reach zero until about 300 hours of exposure.
- Sample 34 which includes 40 wt % wood fiber, was prepared in the Brabender fusion bowl as described. Specimens were exposed to 88° Celsius (190° Fahrenheit) and 90% relative humidity in the same manner as were the specimens of Sample 33, which did not contain wood fiber. Specimens were removed from the test chamber after specified periods of exposure and tested to determine ⁇ *. As seen from the resulting data presented in FIG. 19 , ⁇ * declined to 50% of its original value after only about 30 hours of exposure, and fell to almost zero, indicating complete hydrolysis, after only about 70 hours. It therefore became clear to the inventors that the presence of wood fiber has a detrimental effect on the hydrolytic stability of PLA.
- Sample 35 is a neat PLA formulation with the additives indicated in Table 13, including 2.5 wt % Stabaxol I. Testing of specimens exposed to 82° C. (180° F.) and 90% humidity produced the results shown in FIG. 20 .
- the increased Stabaxol I percentage increased the time for ⁇ * to drop to 50% of its original value to 160 hours, as well as increasing the time until complete hydrolysis to about 380 hours. Accordingly, increasing the percentage of Stabaxol I in a neat PLA formulation increases the resistance of PLA to hydrolysis and the consequent deterioration of the PLA.
- Sample 36 is a PLA-wood composite with the additives indicated in Table 13, including 2.5 wt % Stabaxol I. Sample 36 was tested as described and the resulting data is shown in FIG. 21 . Again, it is seen that the addition of the wood fiber has a detrimental effect on hydrolytic stability, since the value of ⁇ * drops to 50% of its original value in only about 35 hours, and the sample undergoes complete hydrolysis in only 70 hours.
- FIG. 24 plots the hours of exposure of the neat PLA formulations of Samples 33, 35, and 37 to 88° Celsius (190° Fahrenheit) and 90% relative humidity needed for ⁇ * to reach 50% of its original value as a function of the amount of the wt % Stabaxol I in the formulation.
- This data indicates that the addition of Stabaxol I improves hydrolytic stability up to a certain wt %, but rapidly exhibits diminishing improvement thereafter.
- the slope of the curve decreases with increasing Stabaxol I content in FIG. 24 .
- the point of diminishing improvement appears to be between 2 and 3 wt %, and more specifically around 2.5 wt % Stabaxol I.
- FIG. 25 plots the hours of exposure of the PLA-wood composites of Samples 34, 36, and 38 to 88° Celsius (190° Fahrenheit) and 90% relative humidity needed for ⁇ * to decrease to 50% of its original value is plotted as a function of the amount of Stabaxol I present in the formulation.
- the data indicate that, surprisingly, the positive effect of the Stabaxol I actually increases significantly after about 2.5 wt % with increasing amounts of Stabaxol I added. This is indicated by the increasing slope of a curve through the data points of FIG. 25 . This effect is the opposite of that seen in FIG. 24 , wherein wood fiber was not present in the sample.
- the increasing effect could be consistent with a chemical model in which the Stabaxol I not only reacts with the PLA to inhibit hydrolysis, but also reacts with or attaches to the wood fiber, thereby reducing the amount of the Stabaxol I available to protect the PLA from hydrolysis.
- the Stabaxol I does not attach to all of the potential hydrolysis sites of the PLA molecules even at 5 wt % because much of the Stabaxol I is absorbed by the wood fibers. The addition of more Stabaxol I therefore continues to improve the hydrolysis resistance of the composite.
- Samples 39 and 40 samples of a PLA-wood composite with 2.5% and 5% respectively of Stabaxol I in addition to the other ingredients indicated in Table 14 were exposed to less severe temperature and humidity conditions. More specifically, specimens from these samples were exposed in an environmental chamber to temperatures of about 60° Celsius (140° Fahrenheit) at about 90% relative humidity for various preselected periods of time and then tested as described above. The results for each sample are shown in FIGS. 26 and 27 respectively. Referring to FIG. 26 , it can be seen that with the addition of Stabaxol I to the formulation in an amount of about 2.5 wt %, the value of ⁇ * reaches 50% of its initial value after about 624 hours.
- a PLA composition can be formulated that will exhibit a level of hydrolysis resistance sufficient to allow the composition to be used in members to be exposed to the environment for extended periods of time.
- Biopolymers can also be blended with other polymers, including those that are petroleum based polymers.
- One example would be blending PLA with an acrylic.
- Such polymer blends can also be further blended with fillers such as wood fiber to form useful composites, as illustrated by Samples 41 and 42 in Table 15.
- PLA 4032D was blended with Solarkote H300 acrylic polymer, available from Arkema, Inc., 2000 Market Street, Philadelphia, Pa., to form Samples 41 and 42.
- Compounding was done in the Brabender fusion bowl, and the compounded material pressed into a sheet, according to the method described hereinabove for Samples 33-38. Heat distortion temperature was measured by cutting strips from the pressed sheet and subjecting these strip-shaped specimens to the heat distortion test also described hereinabove.
- an additional cold crystallization process can be used to further increase the crystallinity of a previously processed member.
- Samples 43 and 44 demonstrate the impact of an additional cold crystallization process on the compositions described above. In addition, these samples demonstrate the impact of a capping layer on the hydrolysis resistance of the PLA-wood composite base extrusion.
- Sample 44 the profile shown in FIG. 4 was extruded using the PLA-wood composite specified in Table 12 using the fast cooling rate.
- a capping material, shown in Table 10 was co-extruded over the PLA-wood composite base extrusion.
- both ends of the sample were plugged with about 1 inch of closed-cell foam that was sealed to the member with a polyurethane adhesive to prevent air flow to the hollow region of the sample.
- the plugged sample was then exposed to 78° Celsius (172° F.), and 79% RH for up to 96 hours, with specimens being removed at various intervals for testing using dynamic mechanical analysis. It was found that the value of complex viscosity ( ⁇ *) declined to 50% of its original value after approximately 40 hours of exposure to the 78° Celsius (172° F.), 79% RH. Comparing this result with Sample 43, it was apparent that the capping layer increased the hydrolytic stability by a factor of 2. It is believed that at least some of this improvement was due at least in part to the reduction in moisture transport through the capping layer to the PLA-wood composite.
- a preferred ratio of weight percent PLA to weight percent filler such as wood fiber is between about 50/40 and 60/40 depending upon the weight percentages of the other additives used, the ratio of PLA to filler can be varied to achieve a wide variety of properties. Samples 45 to 48 demonstrate the wide range of properties that can be achieved.
- Sample 45 is a PLA-wood composite containing only 40% NatureWorks 4032D polylactic acid and 60% wood fiber prepared as described hereinabove using the fusion bowl and pressing method. Specimens from Sample 45 were tested for heat distortion temperature and flexural strength, with the results shown in Table 16.
- Sample 46 is a PLA-wood composite containing only 25% NatureWorks 4032D polylactic acid and 75% wood fiber prepared as described hereinabove using the fusion bowl and pressing method. Specimens from Sample 46 were tested for heat distortion temperature and flexural strength, with the results shown in Table 16.
- Sample 47 is a PLA-wood composite having the composition shown in Table 12 prepared as described hereinabove using the fusion bowl and pressing method, as in Samples 45 and 46. Specimens from Sample 47 were tested for heat distortion temperature and flexural strength with the results shown in Table 16.
Landscapes
- Engineering & Computer Science (AREA)
- Chemical & Material Sciences (AREA)
- Mechanical Engineering (AREA)
- Organic Chemistry (AREA)
- Health & Medical Sciences (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Medicinal Chemistry (AREA)
- Polymers & Plastics (AREA)
- Physics & Mathematics (AREA)
- Thermal Sciences (AREA)
- Materials Engineering (AREA)
- Manufacturing & Machinery (AREA)
- Life Sciences & Earth Sciences (AREA)
- Wood Science & Technology (AREA)
- Extrusion Moulding Of Plastics Or The Like (AREA)
- Compositions Of Macromolecular Compounds (AREA)
Priority Applications (5)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
CA2793489A CA2793489A1 (fr) | 2010-03-16 | 2011-03-16 | Compositions durables, procedes apparentes, et elements ainsi obtenus |
US13/049,222 US20120220697A2 (en) | 2010-03-16 | 2011-03-16 | Sustainable compositions, related methods, and members formed therefrom |
PCT/US2011/028709 WO2011116122A1 (fr) | 2010-03-16 | 2011-03-16 | Compositions durables, procédés apparentés, et éléments ainsi obtenus |
EP11712096A EP2547505A1 (fr) | 2010-03-16 | 2011-03-16 | Compositions durables, procédés apparentés, et éléments ainsi obtenus |
US14/971,419 US20160108243A1 (en) | 2010-03-16 | 2015-12-16 | Sustainable compositions, related methods, and members formed therefrom |
Applications Claiming Priority (4)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US31435610P | 2010-03-16 | 2010-03-16 | |
US32356110P | 2010-04-13 | 2010-04-13 | |
US41302910P | 2010-11-12 | 2010-11-12 | |
US13/049,222 US20120220697A2 (en) | 2010-03-16 | 2011-03-16 | Sustainable compositions, related methods, and members formed therefrom |
Related Child Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US14/971,419 Division US20160108243A1 (en) | 2010-03-16 | 2015-12-16 | Sustainable compositions, related methods, and members formed therefrom |
Publications (2)
Publication Number | Publication Date |
---|---|
US20110230599A1 US20110230599A1 (en) | 2011-09-22 |
US20120220697A2 true US20120220697A2 (en) | 2012-08-30 |
Family
ID=44647729
Family Applications (2)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US13/049,222 Abandoned US20120220697A2 (en) | 2010-03-16 | 2011-03-16 | Sustainable compositions, related methods, and members formed therefrom |
US14/971,419 Abandoned US20160108243A1 (en) | 2010-03-16 | 2015-12-16 | Sustainable compositions, related methods, and members formed therefrom |
Family Applications After (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US14/971,419 Abandoned US20160108243A1 (en) | 2010-03-16 | 2015-12-16 | Sustainable compositions, related methods, and members formed therefrom |
Country Status (4)
Country | Link |
---|---|
US (2) | US20120220697A2 (fr) |
EP (1) | EP2547505A1 (fr) |
CA (1) | CA2793489A1 (fr) |
WO (1) | WO2011116122A1 (fr) |
Cited By (13)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2013123364A1 (fr) | 2012-02-17 | 2013-08-22 | Andersen Corporation | Élément de construction contenant de l'acide polylactique |
WO2014052300A1 (fr) * | 2012-09-26 | 2014-04-03 | Earth Renewable Technologies | Composition extrudable issue de ressources renouvelables |
US10550257B2 (en) | 2016-02-23 | 2020-02-04 | Andersen Corporation | Composite extrusion with non-aligned fiber orientation |
WO2022155228A1 (fr) * | 2021-01-15 | 2022-07-21 | BiologiQ, Inc. | Films orientés biaxialement et monoaxialement, stratifiés et autres structures comprenant des matériaux polymères à base d'amidon |
US11674018B2 (en) | 2015-06-30 | 2023-06-13 | BiologiQ, Inc. | Polymer and carbohydrate-based polymeric material blends with particular particle size characteristics |
US11674014B2 (en) | 2015-06-30 | 2023-06-13 | BiologiQ, Inc. | Blending of small particle starch powder with synthetic polymers for increased strength and other properties |
US11680439B2 (en) | 2017-08-17 | 2023-06-20 | Andersen Corporation | Selective placement of advanced composites in extruded articles and building components |
US11807741B2 (en) | 2015-06-30 | 2023-11-07 | BiologiQ, Inc. | Articles formed with renewable green plastic materials and starch-based polymeric materials lending increased biodegradability |
US11813818B2 (en) | 2016-02-23 | 2023-11-14 | Andersen Corporation | Fiber-reinforced composite extrusion with enhanced properties |
US11840623B2 (en) | 2015-06-30 | 2023-12-12 | BiologiQ, Inc. | Methods for lending biodegradability to non-biodegradable polyolefin and nylon materials |
US11879058B2 (en) | 2015-06-30 | 2024-01-23 | Biologiq, Inc | Yarn materials and fibers including starch-based polymeric materials |
US11926929B2 (en) | 2015-06-30 | 2024-03-12 | Biologiq, Inc | Melt blown nonwoven materials and fibers including starch-based polymeric materials |
US11926940B2 (en) | 2015-06-30 | 2024-03-12 | BiologiQ, Inc. | Spunbond nonwoven materials and fibers including starch-based polymeric materials |
Families Citing this family (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CA2793489A1 (fr) * | 2010-03-16 | 2011-09-22 | Andersen Corporation | Compositions durables, procedes apparentes, et elements ainsi obtenus |
MX2015013451A (es) * | 2013-03-25 | 2016-01-14 | Teijin Ltd | Composicion de resina. |
EP3004222B1 (fr) * | 2013-05-31 | 2018-12-05 | University of Maine System Board of Trustees | Matériaux composites polymères et procédés pour les fabriquer |
FR3102389A1 (fr) * | 2019-10-29 | 2021-04-30 | Smart Wood | Système et procédé de fabrication d'un produit composite à base de particules cellulosiques à défibrer et d’un liant thermoplastique |
Citations (61)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
EP0476942A2 (fr) * | 1990-09-18 | 1992-03-25 | Rohm And Haas Company | Compositions de résine |
US5300576A (en) * | 1991-10-03 | 1994-04-05 | Camelot Technologies, Inc. | Higher heat degradable polymer alloys |
US5536807A (en) * | 1992-10-02 | 1996-07-16 | Cargill, Incorporated | Melt-stable semi-crystalline lactide polymer film and process for manufacture thereof |
US5594095A (en) * | 1993-07-30 | 1997-01-14 | Cargill, Incorporated | Viscosity-modified lactide polymer composition and process for manufacture thereof |
US5686540A (en) * | 1995-09-29 | 1997-11-11 | Dainippon Ink And Chemicals, Inc. | Process for the preparation of lactic acid-based polyester |
US5883199A (en) * | 1997-04-03 | 1999-03-16 | University Of Massachusetts | Polyactic acid-based blends |
US6037039A (en) * | 1994-01-31 | 2000-03-14 | Daiwa Seiko, Inc. | Biodegradable article |
US6124384A (en) * | 1997-08-19 | 2000-09-26 | Mitsui Chemicals, Inc. | Composite resin composition |
US6262184B1 (en) * | 1998-10-01 | 2001-07-17 | Shimadzu Corporation | Resin composition and molded article |
US20010008560A1 (en) * | 1998-10-26 | 2001-07-19 | Stonikas Paul R. | Deformable, multi-material hearing aid housing |
US6482341B1 (en) * | 1997-12-08 | 2002-11-19 | Rodenburg Biopolymers B.V. | Biodegradable mouldings |
US6509397B1 (en) * | 1998-11-11 | 2003-01-21 | Fraunhofer-Gesellschaft zur Förderung der angewandten Forschung e.V. | Plastic material made from a polymer blend |
US6579605B2 (en) * | 2000-07-31 | 2003-06-17 | Crane Plastics Company Llc | Multilayer synthetic wood component |
US20030154662A1 (en) * | 2000-10-30 | 2003-08-21 | Andersen Corporation | Hollow profile decking system comprising plank and anchor using anchor flange construction |
US20040068059A1 (en) * | 2000-11-30 | 2004-04-08 | Hiroshi Katayama | Aliphatic polyester copolymer and process for producing the same, biodegradable resin molding based on aliphatic polyester, and lactone-containing resin |
JP2004143438A (ja) * | 2002-10-03 | 2004-05-20 | Daicel Chem Ind Ltd | 複合生分解性成形品 |
US20040142157A1 (en) * | 2000-11-13 | 2004-07-22 | George Melkonian | Multi-component coextrusion |
US20040180990A1 (en) * | 2003-03-11 | 2004-09-16 | Fuji Photo Film Co., Ltd. | Resin molded article |
US20040224123A1 (en) * | 2003-05-08 | 2004-11-11 | Nishikawa Rubber Co., Ltd. | Biodegradable resin composition and biodegradable resin molded article |
US20050001358A1 (en) * | 2001-12-28 | 2005-01-06 | Kenji Nakazawa | Polylactic acid-based resin compositions, molded articles and process for producing the same |
US6869985B2 (en) * | 2002-05-10 | 2005-03-22 | Awi Licensing Company | Environmentally friendly polylactide-based composite formulations |
US20050112352A1 (en) * | 2003-11-26 | 2005-05-26 | Laney Thomas M. | Polylactic-acid-based sheet material and method of making |
US20060036062A1 (en) * | 2004-05-20 | 2006-02-16 | Ramakrishna Sonti V | Process for the production of polylactic acid (PLA) from renewable feedstocks |
JP2006193541A (ja) * | 2005-01-11 | 2006-07-27 | Kaneka Corp | ポリ乳酸系樹脂成形加工品 |
US7084192B2 (en) * | 2002-07-16 | 2006-08-01 | Kabushiki Kaisha Toyota Chuo Kankyusho | Polylactic acid composite material and molded body |
US20060247387A1 (en) * | 2005-04-29 | 2006-11-02 | Board Of Trustees Of Michigan State University | Hyperbranched polymer modified biopolymers, their biobased materials and process for the preparation thereof |
US7138439B2 (en) * | 2004-02-27 | 2006-11-21 | Biocorp North America, Inc. | Biodegradable compounds including poly(lactic acid) polymer compositions and products |
US7173080B2 (en) * | 2001-09-06 | 2007-02-06 | Unitika Ltd. | Biodegradable resin composition for molding and object molded or formed from the same |
JP2007161957A (ja) * | 2005-12-16 | 2007-06-28 | Unitika Ltd | 樹脂組成物およびそれからなる成形体 |
US20070154689A1 (en) * | 2006-01-04 | 2007-07-05 | Hughes Thomas B | Composite products contaning a transparent or translucent capstock |
US20070173629A1 (en) * | 2004-03-25 | 2007-07-26 | Kenji Shiga | Modifier for polyester resin and process for producing molded article with the same |
US20070173616A1 (en) * | 2005-07-19 | 2007-07-26 | Kinki University | Resin composition |
US7256223B2 (en) * | 2002-11-26 | 2007-08-14 | Michigan State University, Board Of Trustees | Environmentally friendly polylactide-based composite formulations |
US7261935B2 (en) * | 2002-12-19 | 2007-08-28 | E. I. Du Pont De Nemours And Company | Co-extrudable multi-layer polymer |
US7268190B2 (en) * | 2001-08-03 | 2007-09-11 | Toray Industries, Inc. | Resin composition comprising polylactic acid and polyacetal and a molded article, film, and fiber each comprising the same |
US20080145656A1 (en) * | 2006-12-13 | 2008-06-19 | Cheil Industries Inc. | Natural Fiber-Reinforced Polylactic Acid-based Resin Composition |
US7393590B2 (en) * | 2004-02-27 | 2008-07-01 | Cereplast, Inc. | Biodegradable poly(lactic acid) polymer composition and films, coatings and products comprising Biodegradable poly(lactic acid) polymer compositions |
US20080188629A1 (en) * | 2007-02-05 | 2008-08-07 | Nishikawa Rubber Co., Ltd. | Poly-l-lactic acid crystallization accelerator and production method thereof |
US7445835B2 (en) * | 2003-01-10 | 2008-11-04 | Nec Corporation | Kenaf-fiber-reinforced resin composition |
US20080281023A1 (en) * | 2005-12-23 | 2008-11-13 | Evonik Roehm Gmbh | Pmma Film Featuring Particularly Great Weather Resistance and Great Uv Protection |
US20090093575A1 (en) * | 2005-08-02 | 2009-04-09 | Yohei Kabashima | Resin compositions, method of producing the same and molded article obtained therefrom |
US20090155611A1 (en) * | 2007-12-17 | 2009-06-18 | Tedford Jr Richard A | Thermoformed article made from renewable polymer and heat-resistant polymer |
US20090162683A1 (en) * | 2007-11-29 | 2009-06-25 | Sukano Management + Services Ag | Biodegradable Polyester Compositions |
WO2009083479A1 (fr) * | 2007-12-27 | 2009-07-09 | Basf Se | Résines à base de polyester aliphatique contenant un alcoolate de métal divalent |
US20090178361A1 (en) * | 2006-12-08 | 2009-07-16 | Kuei Yung Chen | Method of fabricating frames for 'doors and the like from extruded compponents and reinforced frame of extruded components |
US7585910B2 (en) * | 2005-03-25 | 2009-09-08 | Kabushiki Kaisha Toyota Chuo Kenkyusho | Polylactic acid composition |
US20090239433A1 (en) * | 2005-11-25 | 2009-09-24 | Kuraray Co., Ltd | Polylactic acid composition |
US20090246544A1 (en) * | 2006-06-01 | 2009-10-01 | Tohcello Co., Ltd. | Moldings comprising a polylactic acid composition |
US20100040904A1 (en) * | 2008-08-15 | 2010-02-18 | Toray Plastics (America). Inc. | Biaxially oriented polylactic acid film with high barrier |
US7682548B2 (en) * | 2003-07-30 | 2010-03-23 | Mitsubishi Plastics, Inc. | Injection molded article, production method thereof and pellets used for injection molded article |
FR2936803A1 (fr) * | 2008-10-06 | 2010-04-09 | Arkema France | Copolymere a blocs issu de matieres renouvelables et procede de fabrication d'un tel copolymere a blocs. |
US7736560B2 (en) * | 2006-11-02 | 2010-06-15 | Diaserve, Inc. | Biological polymeric compositions and methods related thereto |
US7807773B2 (en) * | 2004-03-04 | 2010-10-05 | Unitika Ltd. | Biodegradable polyester resin composition, preparation method therefor, and foamed article and molded article produced therefrom |
US7825212B2 (en) * | 2003-12-25 | 2010-11-02 | Toyota Jidosha Kabushiki Kaisha | Polylactic acid resin and composition and molded article of the same |
US20110034607A1 (en) * | 2008-04-24 | 2011-02-10 | Polyone Corporation | Heat resistant polylactic acid compounds |
US8017678B2 (en) * | 2006-05-09 | 2011-09-13 | Adeka Corporation | Polyester resin composition |
US20110230599A1 (en) * | 2010-03-16 | 2011-09-22 | Michael James Deaner | Sustainable Compositions, Related Methods, and Members Formed Therefrom |
US8030382B2 (en) * | 2007-02-23 | 2011-10-04 | Teijin Limited | Polylactic acid composition |
US8231954B2 (en) * | 2009-12-08 | 2012-07-31 | International Paper Co. | Thermoformed articles made from reactive extrusion products of biobased materials |
US8460797B1 (en) * | 2006-12-29 | 2013-06-11 | Timbertech Limited | Capped component and method for forming |
US20130217815A1 (en) * | 2012-02-17 | 2013-08-22 | Andersen Corporation | Pla-containing material |
Family Cites Families (93)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPH0781204B2 (ja) * | 1987-04-21 | 1995-08-30 | 株式会社バイオマテリアルユニバ−ス | ポリ乳酸繊維 |
CA2031780C (fr) * | 1989-12-07 | 1995-10-17 | Thomas Joseph Saloom | Methode pour l'obtention d'un plastique colore et a motif par extrusion; le produit ainsi obtenu |
DE4018184A1 (de) | 1990-06-07 | 1991-12-12 | Bayer Ag | Verfahren zur stabilisierung von estergruppen enthaltenden kunststoffen |
US6495656B1 (en) * | 1990-11-30 | 2002-12-17 | Eastman Chemical Company | Copolyesters and fibrous materials formed therefrom |
US5665439A (en) * | 1992-08-11 | 1997-09-09 | E. Khashoggi Industries | Articles of manufacture fashioned from hydraulically settable sheets |
US6004668A (en) * | 1992-08-31 | 1999-12-21 | Andersen Corporation | Advanced polymer wood composite |
CA2100320C (fr) * | 1992-08-31 | 2011-02-08 | Michael J. Deaner | Composite perfectionne de polymere et de bois |
US5773138A (en) * | 1992-08-31 | 1998-06-30 | Andersen Corporation | Advanced compatible polymer wood fiber composite |
CA2100319C (fr) * | 1992-08-31 | 2003-10-07 | Michael J. Deaner | Element de structure perfectionne en composite polymere/bois |
US5406768A (en) * | 1992-09-01 | 1995-04-18 | Andersen Corporation | Advanced polymer and wood fiber composite structural component |
GB2271118B (en) * | 1992-09-30 | 1996-09-18 | Merck Patent Gmbh | Ferroelectric liquid-crystalline media, and their use in electro-optical devices |
JP3447289B2 (ja) * | 1992-10-02 | 2003-09-16 | カーギル, インコーポレイテッド | 溶融安定性ラクチドポリマー繊維及びその製造方法 |
US5405921A (en) * | 1993-02-03 | 1995-04-11 | E. I. Du Pont De Nemours And Company | Polyester compositions having improved optical properties and heat stability |
US5441801A (en) * | 1993-02-12 | 1995-08-15 | Andersen Corporation | Advanced polymer/wood composite pellet process |
FI99125C (fi) * | 1993-12-31 | 1997-10-10 | Neste Oy | Polylaktidikoostumus |
US5439749A (en) * | 1994-08-18 | 1995-08-08 | Andersen Corporation | Composite wood structure |
DE4435548A1 (de) | 1994-10-05 | 1996-04-11 | Rhein Chemie Rheinau Gmbh | Stabilisierte Schmierstoff-Grundsubstanz |
AU4904896A (en) * | 1995-01-27 | 1996-08-14 | Andersen Corporation | Vibratory welded window and door joints, method and apparatus for manufacturing the same |
US5746958A (en) * | 1995-03-30 | 1998-05-05 | Trex Company, L.L.C. | Method of producing a wood-thermoplastic composite material |
US6071984A (en) * | 1995-09-26 | 2000-06-06 | Bayer Aktiengesellschaft | Biodegradable plastics filled with reinforcing materials |
US5851469A (en) * | 1995-12-27 | 1998-12-22 | Trex Company, L.L.C. | Process for making a wood-thermoplastic composite |
US5948524A (en) * | 1996-01-08 | 1999-09-07 | Andersen Corporation | Advanced engineering resin and wood fiber composite |
US5882564A (en) * | 1996-06-24 | 1999-03-16 | Andersen Corporation | Resin and wood fiber composite profile extrusion method |
US6357197B1 (en) * | 1997-02-05 | 2002-03-19 | Andersen Corporation | Polymer covered advanced polymer/wood composite structural member |
US5948505A (en) * | 1997-03-28 | 1999-09-07 | Andersen Corporation | Thermoplastic resin and fiberglass fabric composite and method |
EP0977912B1 (fr) * | 1997-05-02 | 2004-09-22 | Cargill, Incorporated | Fibres polymeres degradables; preparation; produit; et procedes d'utilisation |
US6122877A (en) * | 1997-05-30 | 2000-09-26 | Andersen Corporation | Fiber-polymeric composite siding unit and method of manufacture |
US6054207A (en) * | 1998-01-21 | 2000-04-25 | Andersen Corporation | Foamed thermoplastic polymer and wood fiber profile and member |
WO1999046332A1 (fr) * | 1998-03-12 | 1999-09-16 | Daicel Chemical Industries, Ltd. | Composition de resine contenant de la lactone, objet moule dans cette composition, et film |
US6129873A (en) | 1998-04-08 | 2000-10-10 | Eastman Chemical Company | Process for removing moisture and volatiles from pellets in single screw extruders |
US20080010924A1 (en) * | 2006-07-12 | 2008-01-17 | Pietruczynik Christopher B | Exterior building material having a hollow thin wall profile and an embossed low gloss surface |
US6265037B1 (en) * | 1999-04-16 | 2001-07-24 | Andersen Corporation | Polyolefin wood fiber composite |
US6280667B1 (en) * | 1999-04-19 | 2001-08-28 | Andersen Corporation | Process for making thermoplastic-biofiber composite materials and articles including a poly(vinylchloride) component |
DE10015658A1 (de) | 2000-03-29 | 2001-10-04 | Rhein Chemie Rheinau Gmbh | Blockcopolymere auf Basis von Polycarbodiimiden, ein Verfahren zu ihrer Herstellung und ihre Verwendung als Hydrolysestabilisatoren |
US6682798B1 (en) * | 2000-08-02 | 2004-01-27 | Ccl Label, Inc. | Expanded content device pouch |
KR20030061675A (ko) * | 2002-01-11 | 2003-07-22 | 뉴 아이스 리미티드 | 생분해성 또는 부패성 컨테이너 |
WO2003082981A1 (fr) * | 2002-04-02 | 2003-10-09 | Mitsubishi Plastics, Inc. | Film d'acide polylactique thermoretractable |
US7670545B2 (en) * | 2002-08-19 | 2010-03-02 | Natureworks Llc | Method for producing semicrystalline polylactic acid articles |
CA2765185A1 (fr) * | 2002-09-09 | 2004-03-18 | Sony Corporation | Composition resineuse |
EP1591487A4 (fr) * | 2003-02-04 | 2006-04-05 | Sony Corp | Composition de resine et procede de production d' un moulage en resine |
CN1320044C (zh) * | 2003-04-25 | 2007-06-06 | 株式会社艾迪科 | 聚乳酸类树脂组合物、成型品及其制备方法 |
EP1624024B1 (fr) * | 2003-05-12 | 2007-07-04 | Unitika Ltd. | Composition de resine polyester biodegradable, procede de production de celle-ci et article en mousse et article moule mettant en oeuvre celle-ci |
KR20060061301A (ko) * | 2003-06-13 | 2006-06-07 | 아그리-폴리머릭스 엘엘씨 | 바이오폴리머 구조체 및 성분 |
JP4585749B2 (ja) * | 2003-08-07 | 2010-11-24 | 日清紡ホールディングス株式会社 | 黄変を抑えたカルボジイミド組成物、耐加水分解安定剤及び熱可塑性樹脂組成物 |
JP4358603B2 (ja) * | 2003-11-05 | 2009-11-04 | 株式会社豊田中央研究所 | ポリ乳酸樹脂組成物、その製造方法及び成形体 |
WO2005052056A1 (fr) * | 2003-11-25 | 2005-06-09 | Asahi Kasei Life & Living Corporation | Film mat |
US7645823B2 (en) * | 2003-12-02 | 2010-01-12 | Sony Corporation | Resin composition, molded product from resin composition and method for preparing resin composition |
CN100432123C (zh) * | 2003-12-12 | 2008-11-12 | 日本电气株式会社 | 能重新成型和形状恢复性优异的形状记忆树脂和由交联树脂组成的成型产品 |
US7368511B2 (en) * | 2003-12-22 | 2008-05-06 | Eastman Chemical Company | Polymer blends with improved rheology and improved unnotched impact strength |
EP1707598B1 (fr) | 2004-01-20 | 2008-07-09 | Takemoto Yushi Kabushiki Kaisha | Composition et moulage de resine polyester aliphatique, et procede de fabrication du moulage de resine polyester aliphatique |
US7157140B1 (en) * | 2004-03-03 | 2007-01-02 | Rtp Company | Malleable composites and methods of making and using the same |
JP4498783B2 (ja) * | 2004-03-17 | 2010-07-07 | トヨタ紡織株式会社 | 木質成形体の製造方法 |
EP1746136B1 (fr) * | 2004-05-11 | 2015-04-22 | Kao Corporation | Composition de résine biodégradable |
US20050266210A1 (en) * | 2004-06-01 | 2005-12-01 | Blair Dolinar | Imprinted wood-plastic composite, apparatus for manufacturing same, and related method of manufacture |
US7410687B2 (en) * | 2004-06-08 | 2008-08-12 | Trex Co Inc | Variegated composites and related methods of manufacture |
US20080108742A1 (en) * | 2004-09-16 | 2008-05-08 | Asahi Kasei Life & Living Corporation | Aliphatic Polyester Resin Composition Superior in Heat Resistance |
JP4446385B2 (ja) * | 2004-10-04 | 2010-04-07 | 株式会社ジェイエスピー | 熱成形用多層ポリ乳酸系樹脂発泡体 |
CA2594990A1 (fr) * | 2004-12-13 | 2006-06-22 | Michael J. Riebel | Biopolymere comprenant de la prolamine et procedes de fabrication associes |
JP4736523B2 (ja) * | 2005-04-28 | 2011-07-27 | ソニー株式会社 | 樹脂組成物、及びこれより作製された成形物 |
US20060076545A1 (en) * | 2005-06-17 | 2006-04-13 | Trex Company, Inc. | Railing assemblies and related methods and apparatuses |
DE602006009542D1 (de) * | 2005-11-30 | 2009-11-12 | Toray Industries | Mehrlagiges flächengebilde aus polymilchsäureharz und daraus hergestellter formkörper |
US20090137748A1 (en) * | 2006-02-07 | 2009-05-28 | Nec Corporation | Polylactic acid-modified polycarbodiimide compound and polylactic acid resin composition and molded article comprising the same |
US20070207940A1 (en) * | 2006-02-10 | 2007-09-06 | Gyorgyi Fenyvesi | Detergent compositions comprising renewably-based, biodegradable 1,3-propanediol |
US20070218275A1 (en) * | 2006-03-17 | 2007-09-20 | Parris James H | Multi-layered environmentally friendly sheet material and products made therefrom |
JP4749267B2 (ja) * | 2006-07-28 | 2011-08-17 | 株式会社吉野工業所 | 耐熱性ポリl−乳酸プリフォーム |
JP4940840B2 (ja) * | 2006-09-05 | 2012-05-30 | 凸版印刷株式会社 | 床材の製造方法および床材 |
JP5233105B2 (ja) * | 2006-09-27 | 2013-07-10 | 豊田合成株式会社 | ポリ乳酸系樹脂成形品 |
US8962791B2 (en) * | 2006-10-26 | 2015-02-24 | Natureworks Llc | Polylactic acid stereocomplex compositions and methods for making and using same |
US20100056656A1 (en) * | 2006-12-22 | 2010-03-04 | Fumio Matsuoka | Biodegradable polyester resin composition, and molded body, foamed body and molded container obtained from the biodegradable polyester resin composition |
CN101235192A (zh) * | 2007-02-02 | 2008-08-06 | 东丽纤维研究所(中国)有限公司 | 聚乳酸和植物纤维复合材料及其制备方法 |
CA2674884C (fr) * | 2007-02-02 | 2015-01-27 | Gregory F. Jacobs | Article multicouche ayant une apparence panachee |
US8117790B2 (en) * | 2007-02-06 | 2012-02-21 | Vtech Patents Llc | Overmolded fenestration building product and method of manufacture |
TW200909512A (en) * | 2007-03-30 | 2009-03-01 | Teijin Ltd | Polylactic acid composition and fiber composed of the same |
EP2138543A1 (fr) * | 2007-03-30 | 2009-12-30 | Teijin Limited | Composition d'acide polylactique et fibre contenant ladite composition |
JP5324127B2 (ja) * | 2007-05-15 | 2013-10-23 | サンアロマー株式会社 | 難燃剤及びそれを用いた難燃性組成物、その成形品、被覆を有する電線 |
US20090054602A1 (en) * | 2007-08-20 | 2009-02-26 | Julius Uradnisheck | Thermoformed articles and compositions of poly (hydroxyalkanoic acid) and polyoxymethylene |
JP2009062410A (ja) * | 2007-09-04 | 2009-03-26 | Sekisui Seikei Ltd | ポリ乳酸樹脂シートの製造方法及びそれに使用する製造装置 |
WO2009058426A1 (fr) * | 2007-10-29 | 2009-05-07 | Belmay, Inc. | Matériau composite en matière bioplastique, son procédé de fabrication et son procédé d'utilisation |
JP4710921B2 (ja) * | 2008-02-29 | 2011-06-29 | ソニー株式会社 | 樹脂組成物 |
US20110123809A1 (en) * | 2008-03-24 | 2011-05-26 | Biovation, Llc | Biolaminate composite assembly and related methods |
KR20110003503A (ko) * | 2008-03-24 | 2011-01-12 | 바이오베이션 엘엘씨 | 바이오라미네이트 복합 조립체 및 관련 방법 |
US9136036B2 (en) * | 2008-07-02 | 2015-09-15 | Miller Waster Mills | Injection moldable, thermoplastic composite materials |
JP5470761B2 (ja) * | 2008-07-07 | 2014-04-16 | パナソニック株式会社 | スピーカ用振動板およびこれを用いたスピーカならびにこのスピーカを用いた電子機器および装置と、前記スピーカ用振動板の製造方法 |
JP5290313B2 (ja) * | 2008-10-24 | 2013-09-18 | 花王株式会社 | 樹脂組成物の製造方法 |
US8545857B2 (en) * | 2008-10-31 | 2013-10-01 | The Invention Science Fund I, Llc | Compositions and methods for administering compartmentalized frozen particles |
US20100119417A1 (en) * | 2008-11-10 | 2010-05-13 | Biotix, Inc. | Degradable fluid handling devices |
ES2635187T3 (es) * | 2008-12-19 | 2017-10-02 | Fiber Composites, Llc | Materiales compuestos de madera y plástico que utilizan capas protectoras de ionómero y métodos para su fabricación |
WO2010078134A1 (fr) * | 2008-12-29 | 2010-07-08 | 3M Innovative Properties Company | Films ayant une surface structurée, et procédés pour leur réalisation |
JP5513604B2 (ja) * | 2009-03-27 | 2014-06-04 | トウレ プラスチックス (アメリカ) インコーポレイテッド | 高金属接着性および高バリアー性を有する二軸配向金属化ポリ乳酸フィルム |
WO2011031558A2 (fr) * | 2009-08-27 | 2011-03-17 | Metabolix, Inc. | Compositions durcies de polyhydroxyalcanoate |
JP2013515822A (ja) * | 2009-12-28 | 2013-05-09 | スリーエム イノベイティブ プロパティズ カンパニー | 可塑化ポリラクチド |
US20120013037A1 (en) * | 2010-07-14 | 2012-01-19 | Riebel Michael J | Viscoelastic Extrusion Processing Method and Compositions for Biopolymers |
CA2823569A1 (fr) * | 2011-01-14 | 2012-07-19 | Cerestech, Inc. | Compositions de resine d'acide polylactique |
-
2011
- 2011-03-16 CA CA2793489A patent/CA2793489A1/fr not_active Abandoned
- 2011-03-16 EP EP11712096A patent/EP2547505A1/fr not_active Withdrawn
- 2011-03-16 WO PCT/US2011/028709 patent/WO2011116122A1/fr active Application Filing
- 2011-03-16 US US13/049,222 patent/US20120220697A2/en not_active Abandoned
-
2015
- 2015-12-16 US US14/971,419 patent/US20160108243A1/en not_active Abandoned
Patent Citations (66)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
EP0476942A2 (fr) * | 1990-09-18 | 1992-03-25 | Rohm And Haas Company | Compositions de résine |
US5300576A (en) * | 1991-10-03 | 1994-04-05 | Camelot Technologies, Inc. | Higher heat degradable polymer alloys |
US5536807A (en) * | 1992-10-02 | 1996-07-16 | Cargill, Incorporated | Melt-stable semi-crystalline lactide polymer film and process for manufacture thereof |
US5594095A (en) * | 1993-07-30 | 1997-01-14 | Cargill, Incorporated | Viscosity-modified lactide polymer composition and process for manufacture thereof |
US6037039A (en) * | 1994-01-31 | 2000-03-14 | Daiwa Seiko, Inc. | Biodegradable article |
US5686540A (en) * | 1995-09-29 | 1997-11-11 | Dainippon Ink And Chemicals, Inc. | Process for the preparation of lactic acid-based polyester |
US5883199A (en) * | 1997-04-03 | 1999-03-16 | University Of Massachusetts | Polyactic acid-based blends |
US6124384A (en) * | 1997-08-19 | 2000-09-26 | Mitsui Chemicals, Inc. | Composite resin composition |
US6482341B1 (en) * | 1997-12-08 | 2002-11-19 | Rodenburg Biopolymers B.V. | Biodegradable mouldings |
US6262184B1 (en) * | 1998-10-01 | 2001-07-17 | Shimadzu Corporation | Resin composition and molded article |
US20010008560A1 (en) * | 1998-10-26 | 2001-07-19 | Stonikas Paul R. | Deformable, multi-material hearing aid housing |
US6509397B1 (en) * | 1998-11-11 | 2003-01-21 | Fraunhofer-Gesellschaft zur Förderung der angewandten Forschung e.V. | Plastic material made from a polymer blend |
US6579605B2 (en) * | 2000-07-31 | 2003-06-17 | Crane Plastics Company Llc | Multilayer synthetic wood component |
US20030154662A1 (en) * | 2000-10-30 | 2003-08-21 | Andersen Corporation | Hollow profile decking system comprising plank and anchor using anchor flange construction |
US20040142157A1 (en) * | 2000-11-13 | 2004-07-22 | George Melkonian | Multi-component coextrusion |
US20040068059A1 (en) * | 2000-11-30 | 2004-04-08 | Hiroshi Katayama | Aliphatic polyester copolymer and process for producing the same, biodegradable resin molding based on aliphatic polyester, and lactone-containing resin |
US7268190B2 (en) * | 2001-08-03 | 2007-09-11 | Toray Industries, Inc. | Resin composition comprising polylactic acid and polyacetal and a molded article, film, and fiber each comprising the same |
US7173080B2 (en) * | 2001-09-06 | 2007-02-06 | Unitika Ltd. | Biodegradable resin composition for molding and object molded or formed from the same |
US20050001358A1 (en) * | 2001-12-28 | 2005-01-06 | Kenji Nakazawa | Polylactic acid-based resin compositions, molded articles and process for producing the same |
US6869985B2 (en) * | 2002-05-10 | 2005-03-22 | Awi Licensing Company | Environmentally friendly polylactide-based composite formulations |
US7084192B2 (en) * | 2002-07-16 | 2006-08-01 | Kabushiki Kaisha Toyota Chuo Kankyusho | Polylactic acid composite material and molded body |
JP2004143438A (ja) * | 2002-10-03 | 2004-05-20 | Daicel Chem Ind Ltd | 複合生分解性成形品 |
US7354656B2 (en) * | 2002-11-26 | 2008-04-08 | Michigan State University, Board Of Trustees | Floor covering made from an environmentally friendly polylactide-based composite formulation |
US7256223B2 (en) * | 2002-11-26 | 2007-08-14 | Michigan State University, Board Of Trustees | Environmentally friendly polylactide-based composite formulations |
US7261935B2 (en) * | 2002-12-19 | 2007-08-28 | E. I. Du Pont De Nemours And Company | Co-extrudable multi-layer polymer |
US7445835B2 (en) * | 2003-01-10 | 2008-11-04 | Nec Corporation | Kenaf-fiber-reinforced resin composition |
US20040180990A1 (en) * | 2003-03-11 | 2004-09-16 | Fuji Photo Film Co., Ltd. | Resin molded article |
US20040224123A1 (en) * | 2003-05-08 | 2004-11-11 | Nishikawa Rubber Co., Ltd. | Biodegradable resin composition and biodegradable resin molded article |
US7682548B2 (en) * | 2003-07-30 | 2010-03-23 | Mitsubishi Plastics, Inc. | Injection molded article, production method thereof and pellets used for injection molded article |
US20050112352A1 (en) * | 2003-11-26 | 2005-05-26 | Laney Thomas M. | Polylactic-acid-based sheet material and method of making |
US7825212B2 (en) * | 2003-12-25 | 2010-11-02 | Toyota Jidosha Kabushiki Kaisha | Polylactic acid resin and composition and molded article of the same |
US7138439B2 (en) * | 2004-02-27 | 2006-11-21 | Biocorp North America, Inc. | Biodegradable compounds including poly(lactic acid) polymer compositions and products |
US7393590B2 (en) * | 2004-02-27 | 2008-07-01 | Cereplast, Inc. | Biodegradable poly(lactic acid) polymer composition and films, coatings and products comprising Biodegradable poly(lactic acid) polymer compositions |
US7807773B2 (en) * | 2004-03-04 | 2010-10-05 | Unitika Ltd. | Biodegradable polyester resin composition, preparation method therefor, and foamed article and molded article produced therefrom |
US20070173629A1 (en) * | 2004-03-25 | 2007-07-26 | Kenji Shiga | Modifier for polyester resin and process for producing molded article with the same |
US20060036062A1 (en) * | 2004-05-20 | 2006-02-16 | Ramakrishna Sonti V | Process for the production of polylactic acid (PLA) from renewable feedstocks |
JP2006193541A (ja) * | 2005-01-11 | 2006-07-27 | Kaneka Corp | ポリ乳酸系樹脂成形加工品 |
US7585910B2 (en) * | 2005-03-25 | 2009-09-08 | Kabushiki Kaisha Toyota Chuo Kenkyusho | Polylactic acid composition |
US20060247387A1 (en) * | 2005-04-29 | 2006-11-02 | Board Of Trustees Of Michigan State University | Hyperbranched polymer modified biopolymers, their biobased materials and process for the preparation thereof |
US20070173616A1 (en) * | 2005-07-19 | 2007-07-26 | Kinki University | Resin composition |
US20090093575A1 (en) * | 2005-08-02 | 2009-04-09 | Yohei Kabashima | Resin compositions, method of producing the same and molded article obtained therefrom |
US20090239433A1 (en) * | 2005-11-25 | 2009-09-24 | Kuraray Co., Ltd | Polylactic acid composition |
JP2007161957A (ja) * | 2005-12-16 | 2007-06-28 | Unitika Ltd | 樹脂組成物およびそれからなる成形体 |
US20080281023A1 (en) * | 2005-12-23 | 2008-11-13 | Evonik Roehm Gmbh | Pmma Film Featuring Particularly Great Weather Resistance and Great Uv Protection |
US20070154689A1 (en) * | 2006-01-04 | 2007-07-05 | Hughes Thomas B | Composite products contaning a transparent or translucent capstock |
US8017678B2 (en) * | 2006-05-09 | 2011-09-13 | Adeka Corporation | Polyester resin composition |
US20090246544A1 (en) * | 2006-06-01 | 2009-10-01 | Tohcello Co., Ltd. | Moldings comprising a polylactic acid composition |
US7867422B2 (en) * | 2006-11-02 | 2011-01-11 | Diaserve, Inc. | Biological polymeric compositions and methods related thereto |
US7736560B2 (en) * | 2006-11-02 | 2010-06-15 | Diaserve, Inc. | Biological polymeric compositions and methods related thereto |
US20090178361A1 (en) * | 2006-12-08 | 2009-07-16 | Kuei Yung Chen | Method of fabricating frames for 'doors and the like from extruded compponents and reinforced frame of extruded components |
US20080145656A1 (en) * | 2006-12-13 | 2008-06-19 | Cheil Industries Inc. | Natural Fiber-Reinforced Polylactic Acid-based Resin Composition |
US8460797B1 (en) * | 2006-12-29 | 2013-06-11 | Timbertech Limited | Capped component and method for forming |
US20080188629A1 (en) * | 2007-02-05 | 2008-08-07 | Nishikawa Rubber Co., Ltd. | Poly-l-lactic acid crystallization accelerator and production method thereof |
US8030382B2 (en) * | 2007-02-23 | 2011-10-04 | Teijin Limited | Polylactic acid composition |
US20090162683A1 (en) * | 2007-11-29 | 2009-06-25 | Sukano Management + Services Ag | Biodegradable Polyester Compositions |
US20090155611A1 (en) * | 2007-12-17 | 2009-06-18 | Tedford Jr Richard A | Thermoformed article made from renewable polymer and heat-resistant polymer |
WO2009083479A1 (fr) * | 2007-12-27 | 2009-07-09 | Basf Se | Résines à base de polyester aliphatique contenant un alcoolate de métal divalent |
US20110034607A1 (en) * | 2008-04-24 | 2011-02-10 | Polyone Corporation | Heat resistant polylactic acid compounds |
US20100040904A1 (en) * | 2008-08-15 | 2010-02-18 | Toray Plastics (America). Inc. | Biaxially oriented polylactic acid film with high barrier |
FR2936803A1 (fr) * | 2008-10-06 | 2010-04-09 | Arkema France | Copolymere a blocs issu de matieres renouvelables et procede de fabrication d'un tel copolymere a blocs. |
US8231954B2 (en) * | 2009-12-08 | 2012-07-31 | International Paper Co. | Thermoformed articles made from reactive extrusion products of biobased materials |
US20110230599A1 (en) * | 2010-03-16 | 2011-09-22 | Michael James Deaner | Sustainable Compositions, Related Methods, and Members Formed Therefrom |
US20160108243A1 (en) * | 2010-03-16 | 2016-04-21 | Andersen Corporation | Sustainable compositions, related methods, and members formed therefrom |
US20130217815A1 (en) * | 2012-02-17 | 2013-08-22 | Andersen Corporation | Pla-containing material |
US20160039997A9 (en) * | 2012-02-17 | 2016-02-11 | Andersen Corporation | Pla-containing material |
US9512303B2 (en) * | 2012-02-17 | 2016-12-06 | Andersen Corporation | PLA-containing material |
Cited By (20)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US9512303B2 (en) * | 2012-02-17 | 2016-12-06 | Andersen Corporation | PLA-containing material |
WO2013123364A1 (fr) | 2012-02-17 | 2013-08-22 | Andersen Corporation | Élément de construction contenant de l'acide polylactique |
US8829097B2 (en) * | 2012-02-17 | 2014-09-09 | Andersen Corporation | PLA-containing material |
US20160039997A9 (en) * | 2012-02-17 | 2016-02-11 | Andersen Corporation | Pla-containing material |
US20130217815A1 (en) * | 2012-02-17 | 2013-08-22 | Andersen Corporation | Pla-containing material |
US20170121497A1 (en) * | 2012-02-17 | 2017-05-04 | Andersen Corporation | Pla-containing material |
WO2014052300A1 (fr) * | 2012-09-26 | 2014-04-03 | Earth Renewable Technologies | Composition extrudable issue de ressources renouvelables |
CN104781330A (zh) * | 2012-09-26 | 2015-07-15 | 地球可再生科技 | 源自可再生源的可挤出组合物 |
US11926940B2 (en) | 2015-06-30 | 2024-03-12 | BiologiQ, Inc. | Spunbond nonwoven materials and fibers including starch-based polymeric materials |
US11926929B2 (en) | 2015-06-30 | 2024-03-12 | Biologiq, Inc | Melt blown nonwoven materials and fibers including starch-based polymeric materials |
US11879058B2 (en) | 2015-06-30 | 2024-01-23 | Biologiq, Inc | Yarn materials and fibers including starch-based polymeric materials |
US11674018B2 (en) | 2015-06-30 | 2023-06-13 | BiologiQ, Inc. | Polymer and carbohydrate-based polymeric material blends with particular particle size characteristics |
US11674014B2 (en) | 2015-06-30 | 2023-06-13 | BiologiQ, Inc. | Blending of small particle starch powder with synthetic polymers for increased strength and other properties |
US11840623B2 (en) | 2015-06-30 | 2023-12-12 | BiologiQ, Inc. | Methods for lending biodegradability to non-biodegradable polyolefin and nylon materials |
US11807741B2 (en) | 2015-06-30 | 2023-11-07 | BiologiQ, Inc. | Articles formed with renewable green plastic materials and starch-based polymeric materials lending increased biodegradability |
US11813818B2 (en) | 2016-02-23 | 2023-11-14 | Andersen Corporation | Fiber-reinforced composite extrusion with enhanced properties |
US11267963B2 (en) | 2016-02-23 | 2022-03-08 | Andersen Corporation | Composite extrusion with non-aligned fiber orientation |
US10550257B2 (en) | 2016-02-23 | 2020-02-04 | Andersen Corporation | Composite extrusion with non-aligned fiber orientation |
US11680439B2 (en) | 2017-08-17 | 2023-06-20 | Andersen Corporation | Selective placement of advanced composites in extruded articles and building components |
WO2022155228A1 (fr) * | 2021-01-15 | 2022-07-21 | BiologiQ, Inc. | Films orientés biaxialement et monoaxialement, stratifiés et autres structures comprenant des matériaux polymères à base d'amidon |
Also Published As
Publication number | Publication date |
---|---|
US20160108243A1 (en) | 2016-04-21 |
CA2793489A1 (fr) | 2011-09-22 |
WO2011116122A1 (fr) | 2011-09-22 |
US20110230599A1 (en) | 2011-09-22 |
EP2547505A1 (fr) | 2013-01-23 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US20160108243A1 (en) | Sustainable compositions, related methods, and members formed therefrom | |
US10781596B2 (en) | Polymeric composites, resulting panels, and method for producing the same | |
US11813818B2 (en) | Fiber-reinforced composite extrusion with enhanced properties | |
US20060267238A1 (en) | Polymer wood composite material and method of making same | |
EP2814879B1 (fr) | Élément de construction contenant de l'acide polylactique | |
US11267963B2 (en) | Composite extrusion with non-aligned fiber orientation | |
EP2346929B1 (fr) | Composites thermoplastiques contenant des matériaux lignocellulosiques et leurs procédés de fabrication | |
WO2013112726A1 (fr) | Objets multicouches très résistants | |
US9708457B2 (en) | Moisture scavenger composition | |
US20050031848A1 (en) | Recycled polymeric composite crossties and methods of manufacture | |
KR20130096857A (ko) | 생분해성 고분자 섬유의 제조방법 | |
US20120013037A1 (en) | Viscoelastic Extrusion Processing Method and Compositions for Biopolymers | |
JP2002264967A (ja) | ポリ乳酸系梱包バンド | |
Gumowska et al. | The quality of the wood bonding depending on the method of applying the selected thermoplastic biopolymers | |
KR101249407B1 (ko) | 열가소성 전분의 제조방법 | |
Afrifah | Fracture Mechanics and Statistical Modeling of Ternary Blends of Polylactide/Ethylene-acrylate Copolymer/Wood-flour Composites | |
KR20220103452A (ko) | 생분해성 폴리에스테르 수지 조성물 | |
EP2470602A1 (fr) | Composite de polymère thermoplastique |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AS | Assignment |
Owner name: ANDERSEN CORPORATION, MINNESOTA Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:DEANER, MICHAEL JAMES;EFFERTZ, KEITH JAMES;GRONLUND, PATRICK JEROME;AND OTHERS;REEL/FRAME:026258/0705 Effective date: 20110428 |
|
STCV | Information on status: appeal procedure |
Free format text: ON APPEAL -- AWAITING DECISION BY THE BOARD OF APPEALS |
|
STCV | Information on status: appeal procedure |
Free format text: BOARD OF APPEALS DECISION RENDERED |
|
STCB | Information on status: application discontinuation |
Free format text: ABANDONED -- AFTER EXAMINER'S ANSWER OR BOARD OF APPEALS DECISION |