Classifications

• • C—CHEMISTRY; METALLURGY
  • C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
  • C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
  • C25D13/00—Electrophoretic coating characterised by the process
  • C25D13/20—Pretreatment
• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61L—METHODS OR APPARATUS FOR STERILISING MATERIALS OR OBJECTS IN GENERAL; DISINFECTION, STERILISATION OR DEODORISATION OF AIR; CHEMICAL ASPECTS OF BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES; MATERIALS FOR BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES
  • A61L27/00—Materials for grafts or prostheses or for coating grafts or prostheses
  • A61L27/28—Materials for coating prostheses
  • A61L27/30—Inorganic materials
• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61L—METHODS OR APPARATUS FOR STERILISING MATERIALS OR OBJECTS IN GENERAL; DISINFECTION, STERILISATION OR DEODORISATION OF AIR; CHEMICAL ASPECTS OF BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES; MATERIALS FOR BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES
  • A61L31/00—Materials for other surgical articles, e.g. stents, stent-grafts, shunts, surgical drapes, guide wires, materials for adhesion prevention, occluding devices, surgical gloves, tissue fixation devices
  • A61L31/08—Materials for coatings
  • A61L31/082—Inorganic materials
• • C—CHEMISTRY; METALLURGY
  • C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
  • C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
  • C25D13/00—Electrophoretic coating characterised by the process
  • C25D13/02—Electrophoretic coating characterised by the process with inorganic material
• • C—CHEMISTRY; METALLURGY
  • C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
  • C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
  • C25D15/00—Electrolytic or electrophoretic production of coatings containing embedded materials, e.g. particles, whiskers, wires
• • C—CHEMISTRY; METALLURGY
  • C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
  • C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
  • C25D5/00—Electroplating characterised by the process; Pretreatment or after-treatment of workpieces
  • C25D5/54—Electroplating of non-metallic surfaces
  • C25D5/56—Electroplating of non-metallic surfaces of plastics

Definitions

• the present invention relates to obtaining a ceramic, metal or composite coating on a non-conductive substrate, such as a plastic or ceramic substrate. More specifically the invention relates to a new process for obtaining a ceramic, metal or composite coating which comprises generating, from a colloidal polypyrrole dispersion, a conductive layer on the non-conductive material and then carrying out an electrochemical process.
• the metallization of a non-conductive material can be performed by means of different processes.
• the most used conventional process comprises the following stages for generating a conductive layer on the surface of the insulating material: (i) mordanting or conditioning; (ii) neutralization (iii) activation or channeling and (iv) chemical deposition.
• a thin layer of the metal which in most cases does not reach one micron, is formed on the surface of the part, which becomes conductive.
• highly toxic Cr(VI) is used.
• This process generally has the serious drawback that very low thickness of this metal film are obtained, which makes it necessary to reinforce it by electrolytically applying a second layer in order for it to have a suitable metal section for the passage of the current in the points of contact with the frame.
• the second layer is obtained, for example, by applying a flash of electrolytic nickel and, thereafter, the successive metal layers of copper-nickel-chromium are applied.
• the non-conductive surface is reacted with an alkaline permanganate solution to form a manganese dioxide chemically fixed by adsorption; the surface is then contacted with an aqueous acid solution containing 0.1 to 200 g/l of pyrrole or the derivative oligomers thereof, an electrically conductive layer being formed; and finally an electric current suitable for depositing the metal is applied.
• an oxidizer solution is applied to activate the non-conductive surface, followed by a treatment in a solution containing a heterocyclic monomer such as pyrrole, thiophene, furan or the derivatives thereof for example.
• the surface is then metallized by means of a galvanostatic technique.
• WO 0104072 describes a process which comprises impregnating a ceramic surface with a solution containing metal particles, such as a paint applied by spraying. The conductive surface obtained thus allows the electrodeposition of a metal coating.
• U.S. Pat. No. 4,289,829 describes a (“moly-manganese”) process for metallizing a ceramic substrate which comprises applying a thin layer of paint containing molybdenum on the ceramic surface and sintering the part under a reduced atmosphere.
• U.S. Pat. No. 3,998,602 describes a process for metallizing a non-conductive material which uses polymerizable monomers in the presence of small amounts of silver ions.
• JP493970 describes a process for depositing ceramic particles which consists of formulating the conductive polymer in the presence of ceramic particles and thus forming a conductive layer thereon.
• WO 200711010 describes obtaining metal and ceramic parts in a varied manner by electrophoretic deposition. In this process, a metal or ceramic powder suspension is injected into the substrate through a hollow needle. The deposition of material occurs by applying a voltage between the suspension and the substrate.
• the state-of-the-art processes in which electrophoretic deposition is used are always performed on the metal substrates and, furthermore, they later need a machining process.
• Application US 2007029199 describes the formation of ceramic substrates for dental applications by means of electrophoretic deposition.
• Metal or ceramic substrates are used to which a layer of silver paint and a hygroscopic layer have been applied to prevent bubble formation.
• the state-of-the-art electrophoretic deposition processes are generally applied on metal substrates and may need an additional machining stage.
• the inventors of the present invention have discovered a new process by means of which it is possible to obtain a ceramic, metal or composite coating on an insulating substrate, based on the generation of a conductive layer from a colloidal polypyrrole dispersion on the surface of the insulating substrate, and the use of said conductive layer in obtaining one of said coatings electrochemically.
• the invention relates to a process for obtaining a ceramic, metal or composite coating on an insulating substrate which comprises the following stages:
• process of the invention can be applied on any type of non-conductive substrate of a different nature, such as for example plastic, ceramic, wood, among others.
• the aqueous base paint useful to put the invention into practice can be a commercial outdoor acrylic water-based paint, and the acid type water-soluble pure resin can be a acrylic resin in an aqueous base with a pH comprised between 2 and 5.
• Stage A) of the process of the invention comprises obtaining in the first place a polypyrrole dispersion in aqueous medium by pyrrole polymerization at room temperature.
• the resulting dispersion is taken to dryness either by lyophilization or in a rotary evaporator for the complete evaporation of water.
• the dry material obtained is redispersed in a commercial aqueous base paint or in an acid type water-soluble pure resin, maintaining the stirring.
• the concentration of this dispersion is comprised between 0.05 and 2.5 gram of polypyrrole/g of paint or resin.
• a particular embodiment of the process of the invention starts from the monomer pyrrole, at a concentration comprised between 1 ⁇ 10 ⁇ 4 and 1 ⁇ 10 ⁇ 1 g/ml in aqueous medium, and an anionic dispersant of the type of polystyrene sulfonate, poly(vinyl sulfonate), etc. with a molecular weight comprised between 10,000 and 1,000,000 g/mol.
• This mixture is submerged in a bath at a temperature below 0° C. and stirred by ultrasound.
• the oxidizer previously dissolved in water, of the type of ammonium persulfate, iron trichloride, etc., is added, following a process well known in the state of the art.
• the polymerization reaction is usually carried out at room temperature with mechanical stirring at 300 r.p.m, for a time usually comprised between half an hour and 7 hours. Once the reaction has ended, the stirring is stopped and the polypyrrole dispersion is removed from the bath.
• the polypyrrole dispersion in paint or resin is then diluted with an alcohol in a factor of 1.5 until achieving a homogenous polypyrrole dispersion, ready to be used.
• the alcohol is isopropanol.
• the final steps of drying, redispersing and diluting are necessary for the final paint or resin to not coagulate, be perfectly homogenous, have a lower viscosity, and not be as diluted as if the aqueous paint and the polypyrrole dispersion were directly mixed without having been previously taken to dryness.
• the electrical conductivity of the conductive polymer can be optionally determined by means of any conventional method.
• Stage C) of the process of the invention refers to the application of the dispersion of the conductive polymer which is performed by the immersion of the part to be coated, painting or spraying.
• the application is performed by the immersion of the part in the paint containing the colloidal polypyrrole and subsequent drying in a temperature range comprised between 10 and 80° C., preferably room temperature.
• the part is washed with distilled water.
• Stage D) of the process consists of obtaining the final coating on the surface to which the conductive polymer has been applied.
• the various processes for obtaining each type of coating are described below:
• D-1) Obtaining a metal coating by means of an electrolytic process: It is necessary to have a simple cell containing the electrolyte and the counter electrodes (anode and cathode) to obtain coatings of this type. Any conventional electrolyte or electrodeposition bath (silver, copper, nickel, gold, etc.) which is commonly used in conventional industrialized processes can be used to perform this galvanic process.
• the current used in the electrodeposition process can be direct current or by means of current pulses (depending on the properties to be obtained in the final coating).
• the electrolyte comprises at least one metal salt and at least one ceramic particle.
• metal salts are salts of metals such as silver, copper, nickel, gold, among others.
• the ceramic particles can be of SiC, Al 2 O 3 , SiO 2 , ZrO 2 , etc.
• the current used in the electrodeposition process can be direct current or by means of current pulses (depending on the properties to be obtained in the final coating).
• Ceramic particles Preparing the suspension of ceramic particles in an aqueous medium to which the ceramic particles are added, at a concentration comprised between 1-60% by weight, preferably between 4-30% by weight with respect to the total weight of the suspension.
• the types of ceramic particles that can be used in the present invention are, among others, oxides such as SiO 2 , ZrO 2 , Al 2 O 3 , TiO 2 ; carbides, such as SiC, nitrides, such as NTi; and dental ceramic particles such as Base Dentine, Enamel, Dentine 3M-2, Effect Peral, Effect Croma, which can be commercially acquired, for example, of the VITA Zahnfabrik trademark, as well as other ceramics which are conventionally used for generating esthetic layers on dental ceramic substrates.
• a series of dispersant, binder and/or plasticizer additives are then added, always in a percentage which can vary between 0.1-2% by weight with respect to the total weight of the suspension, for the purpose of stabilizing the suspension.
• the additives used are: amines, polymethacrylates, pyrophosphates, citric acid, hydrochloric acid, methyl cellulose, etc. To homogenize and generate an electric charge density in the surface of the ceramic particles, they are stirred by means of ultrasound for a time ranging between 1 to 60 minutes.
• the ceramic coating is obtained by means of an electrophoretic deposition, for which a simple cell containing the previously prepared suspension and the counter electrodes (anode and cathode) is used. Potentials varying between 20 and 400 V are applied for a time ranging between 1 and 40 minutes for the formation of the ceramic coating.
• the latter is subjected to a sintering process, applying temperatures comprised between 400° C. and 1500° C., preferably at temperatures above 800° C.
• the process of the present invention has a number of advantages in comparison with the processes of the art. It should be emphasized that the use of metal particles such as silver, of baths based on strong oxidizers such as Cr(VI), substances which are highly toxic for the environment, is eliminated. Furthermore, the number of stages necessary for generating a conductive layer on an insulating surface is reduced, with respect to conventional processes for metallizing plastic, to the application of the conductive polymer in an aqueous base and to the drying thereof. Therefore, the process of the invention achieves, in a single stage, transforming an insulating surface into a conductive surface using a colloidal polypyrrole dispersion in an aqueous paint or resin, which furthermore considerably reduces the cost and time of the process.
• the process of the invention has the additional advantage that it allows obtaining the final ceramic layers in a few minutes, using to that end an electrophoretic deposition process.
• This process can be automated, further simplifying the process.
• the process of the invention therefore allows, in a particular embodiment, obtaining biodegradable and ceramic dental prostheses quickly and with a high volumetric accuracy.
• the process is performed on final ceramic teeth; the time of application of these decorative layers of ceramic is reduced from one day to a few minutes.
• the global process is therefore simplified and the manufacturing time of the prostheses is significantly reduced.
• Aqueous polypyrrole dispersion was prepared in the first place. To that end, a volume of pyrrole of 0.5-10 ml was added to an aqueous solution containing 1-5% polystyrene in water. The resulting mixture was submerged in a bath at a temperature equal to 0° C. and stirred by ultrasound. Once cooled, ammonium persulfate previously dissolved at a concentration of 6.84 g in 50 ml of water was added. After two hours of reaction, the stirring was stopped and the polypyrrole dispersion was removed from the bath. The resulting dispersion was lyophilized.
• the part was then submerged in a simple cell containing the suspension of ceramic particles.
• the part with the conductive polymer on its surface was connected to one of the electrodes, and closing the electric circuit, a metal counter electrode of stainless steel was used.
• a potential of 100 V was applied for a time equal to 10 minutes for the formation of the ceramic coating.
• the part was subjected to a sintering process which comprised subjecting the part to a pre-drying temperature of 500° C. for 6 minutes, applying a heating gradient of 55° C/min until reaching the cooking temperature of 910° C. and maintaining this temperature for 1 minute.
• An aqueous polypyrrole dispersion was prepared in the first place as in Example 1. The dispersion was applied by means of immersion to the ABS part.
• the resulting part was subsequently introduced in a simple cell containing the counter electrodes (anode and cathode) and a conventional electrolyte of acid copper as an electrolyte or electrodeposition bath.
• the current used in the electrodeposition process was 3 A/dm 2 .

Landscapes

• Chemical & Material Sciences (AREA)
• Health & Medical Sciences (AREA)
• Organic Chemistry (AREA)
• Metallurgy (AREA)
• Materials Engineering (AREA)
• Electrochemistry (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Engineering & Computer Science (AREA)
• Inorganic Chemistry (AREA)
• Veterinary Medicine (AREA)
• Life Sciences & Earth Sciences (AREA)
• Public Health (AREA)
• Animal Behavior & Ethology (AREA)
• General Health & Medical Sciences (AREA)
• Epidemiology (AREA)
• Heart & Thoracic Surgery (AREA)
• Vascular Medicine (AREA)
• Surgery (AREA)
• Transplantation (AREA)
• Oral & Maxillofacial Surgery (AREA)
• Medicinal Chemistry (AREA)
• Dermatology (AREA)
• Application Of Or Painting With Fluid Materials (AREA)
• Paints Or Removers (AREA)

Applications Claiming Priority (1)

Publications (1)

Family

ID=41433724

Family Applications (1)

Country Status (3)

Cited By (3)

Citations (4)

Family Cites Families (13)

• 2008
  • 2008-06-19 US US12/999,723 patent/US20110266158A1/en not_active Abandoned
  • 2008-06-19 EP EP08787617A patent/EP2302104A4/de not_active Withdrawn
  • 2008-06-19 WO PCT/ES2008/000436 patent/WO2009153361A1/es active Application Filing

Patent Citations (4)

Non-Patent Citations (3)

Also Published As

Similar Documents

Legal Events