US20110165011A1 - High strength, high toughness steel alloy - Google Patents
High strength, high toughness steel alloy Download PDFInfo
- Publication number
- US20110165011A1 US20110165011A1 US13/016,606 US201113016606A US2011165011A1 US 20110165011 A1 US20110165011 A1 US 20110165011A1 US 201113016606 A US201113016606 A US 201113016606A US 2011165011 A1 US2011165011 A1 US 2011165011A1
- Authority
- US
- United States
- Prior art keywords
- alloy
- strength
- max
- high strength
- toughness
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Links
Classifications
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
- C22C38/42—Ferrous alloys, e.g. steel alloys containing chromium with nickel with copper
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D6/00—Heat treatment of ferrous alloys
- C21D6/004—Heat treatment of ferrous alloys containing Cr and Ni
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D7/00—Modifying the physical properties of iron or steel by deformation
- C21D7/13—Modifying the physical properties of iron or steel by deformation by hot working
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/005—Modifying the physical properties by deformation combined with, or followed by, heat treatment of ferrous alloys
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
- C21D9/0068—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for particular articles not mentioned below
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/002—Ferrous alloys, e.g. steel alloys containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/34—Ferrous alloys, e.g. steel alloys containing chromium with more than 1.5% by weight of silicon
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
- C22C38/44—Ferrous alloys, e.g. steel alloys containing chromium with nickel with molybdenum or tungsten
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
- C22C38/46—Ferrous alloys, e.g. steel alloys containing chromium with nickel with vanadium
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
- C22C38/48—Ferrous alloys, e.g. steel alloys containing chromium with nickel with niobium or tantalum
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
- C21D1/26—Methods of annealing
- C21D1/32—Soft annealing, e.g. spheroidising
Definitions
- This invention relates to high strength, high toughness steel alloys, and in particular, to such an alloy that can be tempered at a significantly higher temperature without significant loss of tensile strength.
- the invention also relates to a high strength, high toughness, tempered steel article.
- Age-hardenable martensitic steels that provide a combination of very high strength and fracture toughness are known.
- the known steels are those described in U.S. Pat. No. 4,706,525 and U.S. Pat. No. 5,087,415.
- the former is known as AF1410 alloy and the latter is sold under the registered trademark AERMET.
- AERMET The combination of very high strength and toughness provided by those alloys is a result of their compositions which include significant amounts of nickel, cobalt, and molybdenum, elements that are typically among the most expensive alloying elements available. Consequently, those steels are sold at a significant premium compared to other alloys that do not contain such elements.
- the alloy described in the '019 patent is not a stainless steel and therefore, it must be plated to resist corrosion.
- Material specifications for aerospace applications of the alloy require that the alloy be heated at 375° F. for at least 23 hours after being plated in order to remove hydrogen adsorbed during the plating process. Hydrogen must be removed because it leads to embrittlement of the alloy and adversely affects the toughness provided by the alloy. Because this alloy is tempered at 400° F., the 23 hour 375° F. post-plating heat treatment results in over-tempering of parts made from the alloy such that a tensile strength of at least 280 ksi cannot be provided.
- Fe Balance Balance Balance Balance Balance Balance Included in the balance are the usual impurities found in commercial grades of steel alloys produced for similar use and properties. Among said impurities phosphorus is preferably restricted to not more than about 0.01% and sulfur is preferably restricted to not more than about 0.001%. Within the foregoing weight percent ranges, silicon, copper, and vanadium are balanced such that
- the foregoing tabulation is provided as a convenient summary and is not intended to restrict the lower and upper values of the ranges of the individual elements for use in combination with each other, or to restrict the ranges of the elements for use solely in combination with each other.
- one or more of the ranges can be used with one or more of the other ranges for the remaining elements.
- a minimum or maximum for an element of a broad or preferred composition can be used with the minimum or maximum for the same element in another preferred or intermediate composition.
- the alloy according to the present invention may comprise, consist essentially of, or consist of the constituent elements described above and throughout this application.
- percent or the symbol “%” means percent by weight or mass percent, unless otherwise specified.
- a hardened and tempered steel alloy article that has very high strength and fracture toughness.
- the article is formed from an alloy having the broad or preferred weight percent composition set forth above.
- the alloy article according to this aspect of the invention is further characterized by being tempered at a temperature of about 500° F. to 600° F.
- the alloy according to the present invention contains at least about 0.30% and preferably at least about 0.32% carbon. Carbon contributes to the high strength and hardness capability provided by the alloy. When higher strength and hardness are desired, the alloy preferably contains at least about 0.40% carbon (e.g., Preferred C). Carbon is also beneficial to the temper resistance of this alloy. Too much carbon adversely affects the toughness provided by the alloy. Therefore, carbon is restricted to not more than about 0.55%, better yet to not more than about 0.50%, and preferably to not more than about 0.47%.
- the inventor has found that when the alloy contains as little as 0.30% carbon, the upper limit for carbon can be restricted to not more than about 0.40% and the alloy can be balanced with respect to its constituents (e.g., Preferred B) to provide a tensile strength of at least 290 ksi.
- At least about 0.6%, better yet at least about 0.7%, and preferably at least about 0.8% manganese is present in this alloy primarily to deoxidize the alloy. It has been found that manganese also benefits the high strength provided by the alloy. Thus, when higher strength is desired, the alloy contains at least about 1.0% manganese. If too much manganese is present, then an undesirable amount of retained austenite may result during hardening and quenching such that the high strength provided by the alloy is adversely affected. Therefore, the alloy may contain up to about 1.3% manganese. Otherwise, the alloy contains not more than about 1.2% or not more than about 0.9% manganese.
- the alloy contains at least about 0.9% silicon and preferably, at least about 1.3% silicon. At least about 1.5% and preferably at least about 1.9% silicon is present in the alloy when higher hardness and strength are needed. Too much silicon adversely affects the hardness, strength, and ductility of the alloy. In order to avoid such adverse effects silicon is restricted to not more than about 2.5% and preferably to not more than about 2.2% or 2.1% in this alloy.
- the alloy contains at least about 0.75% chromium because chromium contributes to the good hardenability, high strength, and temper resistance provided by the alloy.
- the alloy contains at least about 1.0%, and better yet at least about 1.2% chromium. Higher strength can be provided when the alloy contains at least about 1.5% and preferably at least about 1.7% chromium. More than about 2.5% chromium in the alloy adversely affects the impact toughness and ductility provided by the alloy.
- chromium is preferably restricted to not more than about 1.9%. Otherwise, chromium is restricted to not more than about 1.5% in this alloy and better yet to not more than about 1.35%.
- Nickel is beneficial to the good toughness provided by the alloy according to this invention. Therefore, the alloy contains at least about 3.0% nickel and preferably at least about 3.1% nickel.
- a preferred embodiment of the alloy e.g., Preferred A
- the alloy is balanced to provide higher strength, it preferably contains at least about 4.0% and better yet at least about 4.6% nickel.
- the benefit provided by larger amounts of nickel adversely affects the cost of the alloy without providing a significant advantage.
- the amount of nickel is restricted to not more than about 7%.
- the alloy contains not more than about 4.5% nickel.
- Molybdenum is a carbide former that is beneficial to the temper resistance provided by this alloy.
- the presence of molybdenum boosts the tempering temperature of the alloy such that a secondary hardening effect is achieved at about 500° F.
- Molybdenum also contributes to the strength and fracture toughness provided by the alloy.
- the benefits provided by molybdenum are realized when the alloy contains at least about 0.4% molybdenum and preferably at least about 0.5% molybdenum. For higher strength, the alloy contains at least about 0.7% molybdenum.
- molybdenum does not provide an increasing advantage in properties relative to the significant cost increase of adding larger amounts of molybdenum.
- the alloy contains up to about 1.3% molybdenum, better yet not more than about 1.1% molybdenum, preferably not more than about 0.9% molybdenum in the higher strength forms of the alloy (Preferred B and Preferred C).
- Tungsten may be substituted for some or all of the molybdenum in this alloy. When present, tungsten is substituted for molybdenum on a 2:1 basis.
- This alloy preferably contains at least about 0.5% copper which contributes to the hardenability and impact toughness of the alloy. When higher strength is desired, the alloy contains at least about 0.7% copper. Too much copper can result in precipitation of an undesirable amount of free copper in the alloy matrix and adversely affect the fracture toughness of the alloy. Therefore, not more than about 0.9% and preferably not more than about 0.85% copper is present in this alloy. Copper can be limited to about 0.6% max. when very high strength is not needed.
- Vanadium contributes to the high strength and good hardenability provided by this alloy. Vanadium is also a carbide former and promotes the formation of carbides that help provide grain refinement in the alloy and that benefit the temper resistance and secondary hardening of the alloy.
- the alloy preferably contains at least about 0.10% and preferably at least about 0.14% vanadium. Too much vanadium adversely affects the strength of the alloy because of the formation of larger amounts of carbides in the alloy which depletes carbon from the alloy matrix material. Accordingly, the alloy may contain up to about 1.0% vanadium, but preferably contains not more than about 0.35% vanadium.
- vanadium is restricted to not more than about 0.25% and preferably to not more than about 0.22%.
- Niobium can be substituted for some or all of the vanadium in this alloy because like vanadium, niobium combines with carbon to form M 4 C 3 carbides that benefit the temper resistance and hardenability of the alloy. When present, niobium is substituted for vanadium on 1.8:1 basis.
- This alloy may also contain a small amount of calcium up to about 0.005% retained from additions during melting of the alloy to help remove sulfur and thereby benefit the fracture toughness provided by the alloy.
- Silicon, copper, vanadium, and when present, niobium are preferably balanced within their above-described weight percent ranges to benefit the novel combination of strength and toughness that characterize this alloy. More specifically, the ratio (% Si+% Cu)/(% V+(5/9)x % Nb) is about 2 to 34. The ratio is preferably about 6-12 for strength levels below about 290 ksi. For strength levels of 290 ksi and above, the alloy is balanced such that the ratio is about 14.5 up to about 34. It is believed that when the amounts of silicon, copper, and vanadium present in the alloy are balanced in accordance with the ratio, the grain boundaries of the alloy are strengthened by preventing brittle phases and tramp elements from forming on the grain boundaries.
- the balance of the alloy is essentially iron and the usual impurities found in commercial grades of similar alloys and steels.
- the alloy preferably contains not more than about 0.01%, better yet, not more than about 0.005% phosphorus and not more than about 0.001%, better yet not more than about 0.0005% sulfur.
- the alloy preferably contains not more than about 0.01% cobalt. Titanium may be present at a residual level of up to about 0.01% from deoxidation additions during melting and is preferably restricted to not more than about 0.005%. Up to about 0.015% aluminum may also be present in the alloy from deoxidation additions during melting.
- the alloys according to preferred compositions B and C is balanced to provide very high strength and toughness in the hardened and tempered condition.
- the Preferred B composition is balanced to provide a tensile strength of at least about 290 ksi in combination with good toughness as indicated by a K Ic fracture toughness of at least about 70 ksi ⁇ in.
- the Preferred C composition is balanced to provide a tensile strength of at least about 310 ksi in combination with a K Ic fracture toughness of at least about 50 ksi ⁇ in for applications that require higher strength and good toughness.
- the alloy is preferably vacuum induction melted (VIM) and, when desired as for critical applications, refined using vacuum arc remelting (VAR).
- VIM vacuum induction melted
- VAR vacuum arc remelting
- the alloy can also be arc melted in air (ARC) if desired. After ARC melting, the alloy may be refined by electroslag remelting (ESR) or VAR.
- the alloy of this invention is preferably hot worked from a temperature of up to about 2100° F., preferably at about 1800° F., to form various intermediate product forms such as billets and bars.
- the alloy is preferably heat treated by austenitizing at about 1585° F. to about 1735° F. for about 1-2 hours.
- the alloy is then air cooled or oil quenched from the austenitizing temperature.
- the alloy can be vacuum heat treated and gas quenched.
- the alloy is preferably deep chilled to either ⁇ 100° F. or ⁇ 320° F. for about 1-8 hours and then warmed in air.
- the alloy is preferably tempered at about 500° F. for about 2-3 hours and then air cooled.
- the alloy may be tempered at up to 600° F. when an optimum combination of strength and toughness is not required.
- the alloy of the present invention is useful in a wide range of applications.
- the very high strength and good fracture toughness of the alloy makes it useful for machine tool components and also in structural components for aircraft, including landing gear.
- the alloy of this invention is also useful for automotive components including, but not limited to, structural members, drive shafts, springs, and crankshafts. It is believed that the alloy also has utility in armor plate, sheet, and bars.
- each bar was further hot worked to a cross section of 11 ⁇ 2 inches ⁇ 45 ⁇ 8 inches.
- the hot working was carried out in steps with reheating of the intermediate forms as needed. After forging, the bars were allowed to cool to room temperature in air. The cooled bars were each then cut into two pieces at the junction between the two section sizes. The bar pieces were annealed at 1250° F. for 8 hours and then cooled in air.
- Standard tensile, Charpy V-notch, and fracture toughness, and hardness test specimens were prepared from the bar pieces with both longitudinal and transverse orientations.
- the test specimens were heat treated as follows for testing.
- the specimens of Heat 1 were austenitized in a vacuum furnace at 1685° F. for 1.5 hours and then gas quenched.
- the as-quenched specimens were deep chilled at ⁇ 100° F. for 8 hours and then warmed to room temperature in air.
- the specimens were tempered at 500° F. for 2 hours and then cooled in air from the tempering temperature.
- the specimens of Heat 2 were austenitized in a vacuum furnace at 1735° F. for 2 hours and then gas quenched.
- the as-quenched specimens were deep chilled at ⁇ 100° F. for 8 hours and then warmed to room temperature in air.
- the specimens were tempered at 500° F. for 2 hours and then cooled in air from the tempering temperature.
- Tables 2A and 2B The results of room temperature tensile, Charpy V-notch, and K Ic fracture toughness testing are shown in Tables 2A and 2B below including the 0.2% offset yield strength (Y.S) and ultimate tensile strength (U.T.S.) in ksi, the percent elongation (% El.) and percent reduction in area (% R.A.), the Charpy V-notch impact strength (CVN) in ft-lbs, the rising step load K 1 fracture toughness in ksi ⁇ in, and Rockwell C-scale hardness (HRC).
- the rising step load fracture toughness test was conducted in accordance with ASTM Standard Test Procedures E399, E812, and E1290. Table 2A shows the results for Heat 1 and Table 2B shows the results for Heat 2.
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Materials Engineering (AREA)
- Mechanical Engineering (AREA)
- Metallurgy (AREA)
- Organic Chemistry (AREA)
- Crystallography & Structural Chemistry (AREA)
- Physics & Mathematics (AREA)
- Thermal Sciences (AREA)
- Heat Treatment Of Steel (AREA)
- Heat Treatment Of Articles (AREA)
- Heat Treatment Of Sheet Steel (AREA)
- Heat Treatment Of Strip Materials And Filament Materials (AREA)
Priority Applications (16)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US13/016,606 US20110165011A1 (en) | 2008-07-24 | 2011-01-28 | High strength, high toughness steel alloy |
PCT/US2012/023088 WO2012103539A1 (en) | 2011-01-28 | 2012-01-30 | High strength, high toughness steel alloy |
CA2825146A CA2825146C (en) | 2011-01-28 | 2012-01-30 | High strength, high toughness steel alloy |
PL12703212T PL2668306T3 (pl) | 2011-01-28 | 2012-01-30 | Stop stali o wysokiej wytrzymałości i wysokiej ciągliwości |
KR1020137022668A KR101696967B1 (ko) | 2011-01-28 | 2012-01-30 | 고강도 고인성 강합금 |
ES12703212T ES2530503T3 (es) | 2011-01-28 | 2012-01-30 | Aleación de acero de tenacidad elevada y de resistencia elevada |
RU2013139664/02A RU2556173C2 (ru) | 2011-01-28 | 2012-01-30 | Высокопрочная высокопластичная легированная сталь |
ARP120100291A AR084951A1 (es) | 2011-01-28 | 2012-01-30 | Aleacion de acero de alta resistencia y alta tenacidad |
TW101102936A TWI449799B (zh) | 2011-01-28 | 2012-01-30 | 高強度、高韌度之鋼合金 |
BR112013019167-8A BR112013019167B1 (pt) | 2011-01-28 | 2012-01-30 | Liga de aço de alta resistência e alta dureza e artigo de liga temperado e revenido. |
JP2013551407A JP5933597B2 (ja) | 2011-01-28 | 2012-01-30 | 高強度・高靭性鋼合金 |
MX2013008680A MX344839B (es) | 2011-01-28 | 2012-01-30 | Aleacion de acero con alta resistencia, alta tenacidad. |
EP12703212.6A EP2668306B1 (en) | 2011-01-28 | 2012-01-30 | High strength, high toughness steel alloy |
CN201280006801.8A CN103502498B (zh) | 2011-01-28 | 2012-01-30 | 高强度、高韧性钢 |
US13/645,596 US9518313B2 (en) | 2008-07-24 | 2012-10-05 | High strength, high toughness steel alloy |
IL227570A IL227570A (en) | 2011-01-28 | 2013-07-21 | High strength, high toughness steel alloy |
Applications Claiming Priority (4)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US8324908P | 2008-07-24 | 2008-07-24 | |
US17209809P | 2009-04-23 | 2009-04-23 | |
US12/488,112 US20100018613A1 (en) | 2008-07-24 | 2009-06-19 | High Strength, High Toughness Steel Alloy |
US13/016,606 US20110165011A1 (en) | 2008-07-24 | 2011-01-28 | High strength, high toughness steel alloy |
Related Parent Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US12/488,112 Continuation-In-Part US20100018613A1 (en) | 2008-07-24 | 2009-06-19 | High Strength, High Toughness Steel Alloy |
Related Child Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US13/645,596 Continuation US9518313B2 (en) | 2008-07-24 | 2012-10-05 | High strength, high toughness steel alloy |
Publications (1)
Publication Number | Publication Date |
---|---|
US20110165011A1 true US20110165011A1 (en) | 2011-07-07 |
Family
ID=45569764
Family Applications (2)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US13/016,606 Abandoned US20110165011A1 (en) | 2008-07-24 | 2011-01-28 | High strength, high toughness steel alloy |
US13/645,596 Active 2030-05-27 US9518313B2 (en) | 2008-07-24 | 2012-10-05 | High strength, high toughness steel alloy |
Family Applications After (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US13/645,596 Active 2030-05-27 US9518313B2 (en) | 2008-07-24 | 2012-10-05 | High strength, high toughness steel alloy |
Country Status (15)
Country | Link |
---|---|
US (2) | US20110165011A1 (pt) |
EP (1) | EP2668306B1 (pt) |
JP (1) | JP5933597B2 (pt) |
KR (1) | KR101696967B1 (pt) |
CN (1) | CN103502498B (pt) |
AR (1) | AR084951A1 (pt) |
BR (1) | BR112013019167B1 (pt) |
CA (1) | CA2825146C (pt) |
ES (1) | ES2530503T3 (pt) |
IL (1) | IL227570A (pt) |
MX (1) | MX344839B (pt) |
PL (1) | PL2668306T3 (pt) |
RU (1) | RU2556173C2 (pt) |
TW (1) | TWI449799B (pt) |
WO (1) | WO2012103539A1 (pt) |
Cited By (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2014014540A2 (en) | 2012-04-27 | 2014-01-23 | Crs Holdings, Inc. | High strength, high toughness steel alloy |
Families Citing this family (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US9499890B1 (en) | 2012-04-10 | 2016-11-22 | The United States Of America As Represented By The Secretary Of The Navy | High-strength, high-toughness steel articles for ballistic and cryogenic applications, and method of making thereof |
CN104498834B (zh) * | 2014-12-15 | 2016-05-18 | 北京理工大学 | 一种高韧性超高强度钢的成分及其制备工艺 |
CN111996452B (zh) * | 2020-08-07 | 2022-07-12 | 上海大学 | 高合金无缝钢管穿孔顶头及其制备方法 |
CN111979487A (zh) * | 2020-08-14 | 2020-11-24 | 上海佩琛金属材料有限公司 | 一种高塑韧性低合金超高强度钢及制备方法 |
CN112593166B (zh) * | 2020-12-22 | 2022-05-03 | 河南中原特钢装备制造有限公司 | 超高强度高韧性合金结构钢及其冶炼工艺 |
Citations (12)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US3713905A (en) * | 1970-06-16 | 1973-01-30 | Carpenter Technology Corp | Deep air-hardened alloy steel article |
US4729872A (en) * | 1985-09-18 | 1988-03-08 | Hitachi Metals, Ltd. | Isotropic tool steel |
US5972129A (en) * | 1994-11-30 | 1999-10-26 | Creusot Loire Industrie | Process for smelting a titanium steel and steel obtained |
US6187261B1 (en) * | 1996-07-09 | 2001-02-13 | Modern Alloy Company L.L.C. | Si(Ge)(-) Cu(-)V Universal alloy steel |
US6254696B1 (en) * | 1998-01-14 | 2001-07-03 | Nippon Steel Corporation | Bainitic type rail excellent in surface fatigue damage resistance and wear resistance |
US6426040B1 (en) * | 1996-07-09 | 2002-07-30 | Modern Alloy Co., Llc | Si(Ge)-Cu-V steel alloy |
US20030026723A1 (en) * | 2001-07-12 | 2003-02-06 | Takemori Takayama | High-toughness wear-resistant steel |
US6699333B1 (en) * | 1998-06-29 | 2004-03-02 | Aubert & Duval | Case hardened steel with high tempering temperature, method for obtaining same and parts formed with said steel |
US7067019B1 (en) * | 2003-11-24 | 2006-06-27 | Malltech, L.L.C. | Alloy steel and article made therefrom |
US7537727B2 (en) * | 2003-01-24 | 2009-05-26 | Ellwood National Forge Company | Eglin steel—a low alloy high strength composition |
US20090277539A1 (en) * | 2005-11-21 | 2009-11-12 | Yuuji Kimura | Steel for Warm Working, Warm Working Method Using the Steel, and Steel Material and Steel Component Obtainable Therefrom |
US20090291014A1 (en) * | 2008-05-20 | 2009-11-26 | Gregory Vartanov | High strength military steel |
Family Cites Families (15)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4076525A (en) | 1976-07-29 | 1978-02-28 | General Dynamics Corporation | High strength fracture resistant weldable steels |
US5087415A (en) | 1989-03-27 | 1992-02-11 | Carpenter Technology Corporation | High strength, high fracture toughness structural alloy |
JPH04143253A (ja) * | 1990-10-04 | 1992-05-18 | Kobe Steel Ltd | 転動疲労特性に優れた軸受用鋼 |
JPH05148581A (ja) * | 1991-11-28 | 1993-06-15 | Kobe Steel Ltd | 高強度ばね用鋼および高強度ばねの製造方法 |
AU663023B2 (en) | 1993-02-26 | 1995-09-21 | Nippon Steel Corporation | Process for manufacturing high-strength bainitic steel rails with excellent rolling-contact fatigue resistance |
JPH08209289A (ja) * | 1995-02-06 | 1996-08-13 | Sumitomo Metal Ind Ltd | 耐遅れ破壊性に優れた機械構造用鋼 |
JPH10102185A (ja) * | 1996-10-02 | 1998-04-21 | Nippon Steel Corp | 高靭性高温耐摩耗部材およびその厚鋼板の製造方法 |
JP3457498B2 (ja) | 1997-04-17 | 2003-10-20 | 新日本製鐵株式会社 | 高強度pc鋼棒およびその製造方法 |
JPH11152519A (ja) * | 1997-11-19 | 1999-06-08 | Mitsubishi Seiko Muroran Tokushuko Kk | 塩化物による腐食に耐える懸架用ばねの製造方法 |
JP2001262274A (ja) * | 2000-03-22 | 2001-09-26 | Kobe Steel Ltd | 高強度鋼ベルトおよびその製法 |
JP2003105485A (ja) | 2001-09-26 | 2003-04-09 | Nippon Steel Corp | 耐水素疲労破壊特性に優れた高強度ばね用鋼およびその製造方法 |
RU2262539C1 (ru) * | 2003-12-26 | 2005-10-20 | Общество с ограниченной отвественностью "Интелмет НТ" | Сортовой прокат круглый из легированной стали для холодной объемной штамповки сложнопрофильных высокопрочных крепежных деталей |
JP2008138241A (ja) | 2006-11-30 | 2008-06-19 | Jfe Steel Kk | 耐疲労損傷性及び耐食性に優れたパーライト鋼レールおよびその製造方法 |
CN102165086B (zh) * | 2008-07-24 | 2017-02-08 | Crs 控股公司 | 高强度、高韧性钢合金 |
JP7065141B2 (ja) * | 2020-03-31 | 2022-05-11 | 本田技研工業株式会社 | 鞍乗り型車両 |
-
2011
- 2011-01-28 US US13/016,606 patent/US20110165011A1/en not_active Abandoned
-
2012
- 2012-01-30 MX MX2013008680A patent/MX344839B/es active IP Right Grant
- 2012-01-30 PL PL12703212T patent/PL2668306T3/pl unknown
- 2012-01-30 KR KR1020137022668A patent/KR101696967B1/ko active IP Right Grant
- 2012-01-30 AR ARP120100291A patent/AR084951A1/es not_active Application Discontinuation
- 2012-01-30 RU RU2013139664/02A patent/RU2556173C2/ru active
- 2012-01-30 WO PCT/US2012/023088 patent/WO2012103539A1/en active Application Filing
- 2012-01-30 JP JP2013551407A patent/JP5933597B2/ja active Active
- 2012-01-30 ES ES12703212T patent/ES2530503T3/es active Active
- 2012-01-30 BR BR112013019167-8A patent/BR112013019167B1/pt active IP Right Grant
- 2012-01-30 CA CA2825146A patent/CA2825146C/en active Active
- 2012-01-30 EP EP12703212.6A patent/EP2668306B1/en active Active
- 2012-01-30 TW TW101102936A patent/TWI449799B/zh active
- 2012-01-30 CN CN201280006801.8A patent/CN103502498B/zh active Active
- 2012-10-05 US US13/645,596 patent/US9518313B2/en active Active
-
2013
- 2013-07-21 IL IL227570A patent/IL227570A/en active IP Right Grant
Patent Citations (14)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US3713905A (en) * | 1970-06-16 | 1973-01-30 | Carpenter Technology Corp | Deep air-hardened alloy steel article |
US4729872A (en) * | 1985-09-18 | 1988-03-08 | Hitachi Metals, Ltd. | Isotropic tool steel |
US5972129A (en) * | 1994-11-30 | 1999-10-26 | Creusot Loire Industrie | Process for smelting a titanium steel and steel obtained |
US6426038B1 (en) * | 1996-07-09 | 2002-07-30 | Modern Alloy Co., Llc | Universal alloy steel |
US6426040B1 (en) * | 1996-07-09 | 2002-07-30 | Modern Alloy Co., Llc | Si(Ge)-Cu-V steel alloy |
US6187261B1 (en) * | 1996-07-09 | 2001-02-13 | Modern Alloy Company L.L.C. | Si(Ge)(-) Cu(-)V Universal alloy steel |
US6254696B1 (en) * | 1998-01-14 | 2001-07-03 | Nippon Steel Corporation | Bainitic type rail excellent in surface fatigue damage resistance and wear resistance |
US6699333B1 (en) * | 1998-06-29 | 2004-03-02 | Aubert & Duval | Case hardened steel with high tempering temperature, method for obtaining same and parts formed with said steel |
US20030026723A1 (en) * | 2001-07-12 | 2003-02-06 | Takemori Takayama | High-toughness wear-resistant steel |
US7537727B2 (en) * | 2003-01-24 | 2009-05-26 | Ellwood National Forge Company | Eglin steel—a low alloy high strength composition |
US7067019B1 (en) * | 2003-11-24 | 2006-06-27 | Malltech, L.L.C. | Alloy steel and article made therefrom |
US20090277539A1 (en) * | 2005-11-21 | 2009-11-12 | Yuuji Kimura | Steel for Warm Working, Warm Working Method Using the Steel, and Steel Material and Steel Component Obtainable Therefrom |
US20090291014A1 (en) * | 2008-05-20 | 2009-11-26 | Gregory Vartanov | High strength military steel |
US20090291013A1 (en) * | 2008-05-20 | 2009-11-26 | Fedchun Vladimir A | Method of designing a low cost, high strength, high toughness, martensitic steel and an article made thereof |
Cited By (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2014014540A2 (en) | 2012-04-27 | 2014-01-23 | Crs Holdings, Inc. | High strength, high toughness steel alloy |
WO2014014540A3 (en) * | 2012-04-27 | 2014-03-27 | Crs Holdings, Inc. | High strength, high toughness steel alloy |
Also Published As
Publication number | Publication date |
---|---|
JP2014509348A (ja) | 2014-04-17 |
CN103502498A (zh) | 2014-01-08 |
BR112013019167B1 (pt) | 2019-04-09 |
ES2530503T3 (es) | 2015-03-03 |
PL2668306T3 (pl) | 2015-06-30 |
US9518313B2 (en) | 2016-12-13 |
BR112013019167A2 (pt) | 2016-10-04 |
US20130037176A1 (en) | 2013-02-14 |
MX2013008680A (es) | 2013-10-30 |
KR101696967B1 (ko) | 2017-01-16 |
EP2668306B1 (en) | 2014-12-24 |
RU2556173C2 (ru) | 2015-07-10 |
MX344839B (es) | 2017-01-09 |
TWI449799B (zh) | 2014-08-21 |
KR20130114261A (ko) | 2013-10-16 |
CN103502498B (zh) | 2016-09-21 |
CA2825146A1 (en) | 2012-08-02 |
AR084951A1 (es) | 2013-07-10 |
CA2825146C (en) | 2017-05-09 |
TW201235483A (en) | 2012-09-01 |
JP5933597B2 (ja) | 2016-06-15 |
IL227570A0 (en) | 2013-09-30 |
IL227570A (en) | 2017-01-31 |
WO2012103539A1 (en) | 2012-08-02 |
EP2668306A1 (en) | 2013-12-04 |
RU2013139664A (ru) | 2015-03-10 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US10472706B2 (en) | High strength, high toughness steel alloy | |
US9957594B2 (en) | High strength, high toughness steel alloy | |
US10458007B2 (en) | Quench and temper corrosion resistant steel alloy | |
US9518313B2 (en) | High strength, high toughness steel alloy | |
US20070113931A1 (en) | Ultra-high strength martensitic alloy | |
US11634803B2 (en) | Quench and temper corrosion resistant steel alloy and method for producing the alloy |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AS | Assignment |
Owner name: CRS HOLDINGS, INC., DELAWARE Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:NOVOTNY, PAUL M.;REEL/FRAME:026003/0400 Effective date: 20110216 |
|
STCB | Information on status: application discontinuation |
Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION |