US20100308262A1 - Composite getter for manufacturing photovoltaic panels - Google Patents

Composite getter for manufacturing photovoltaic panels Download PDF

Info

Publication number
US20100308262A1
US20100308262A1 US12/679,280 US67928008A US2010308262A1 US 20100308262 A1 US20100308262 A1 US 20100308262A1 US 67928008 A US67928008 A US 67928008A US 2010308262 A1 US2010308262 A1 US 2010308262A1
Authority
US
United States
Prior art keywords
composite getter
polymeric matrix
photovoltaic panel
composite
photovoltaic
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US12/679,280
Other languages
English (en)
Inventor
Sergio Rondena
Antonio Bonucci
Giorgio Longoni
Luca Toia
Marco Amiotti
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SAES Getters SpA
Original Assignee
SAES Getters SpA
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SAES Getters SpA filed Critical SAES Getters SpA
Assigned to SAES GETTERS S.P.A. reassignment SAES GETTERS S.P.A. ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: AMIOTTI, MARCO, BONUCCI, ANTONIO, LONGONI, GIORGIO, RONDENA, SERGIO, TOIA, LUCA
Publication of US20100308262A1 publication Critical patent/US20100308262A1/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • H—ELECTRICITY
    • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
    • H10F—INORGANIC SEMICONDUCTOR DEVICES SENSITIVE TO INFRARED RADIATION, LIGHT, ELECTROMAGNETIC RADIATION OF SHORTER WAVELENGTH OR CORPUSCULAR RADIATION
    • H10F19/00—Integrated devices, or assemblies of multiple devices, comprising at least one photovoltaic cell covered by group H10F10/00, e.g. photovoltaic modules
    • H10F19/80—Encapsulations or containers for integrated devices, or assemblies of multiple devices, having photovoltaic cells
    • H10F19/804—Materials of encapsulations
    • H—ELECTRICITY
    • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
    • H10F—INORGANIC SEMICONDUCTOR DEVICES SENSITIVE TO INFRARED RADIATION, LIGHT, ELECTROMAGNETIC RADIATION OF SHORTER WAVELENGTH OR CORPUSCULAR RADIATION
    • H10F19/00—Integrated devices, or assemblies of multiple devices, comprising at least one photovoltaic cell covered by group H10F10/00, e.g. photovoltaic modules
    • H10F19/80—Encapsulations or containers for integrated devices, or assemblies of multiple devices, having photovoltaic cells
    • H—ELECTRICITY
    • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
    • H10F—INORGANIC SEMICONDUCTOR DEVICES SENSITIVE TO INFRARED RADIATION, LIGHT, ELECTROMAGNETIC RADIATION OF SHORTER WAVELENGTH OR CORPUSCULAR RADIATION
    • H10F71/00—Manufacture or treatment of devices covered by this subclass
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
    • Y02E—REDUCTION OF GREENHOUSE GAS [GHG] EMISSIONS, RELATED TO ENERGY GENERATION, TRANSMISSION OR DISTRIBUTION
    • Y02E10/00—Energy generation through renewable energy sources
    • Y02E10/50—Photovoltaic [PV] energy

Definitions

  • the present invention refers to a composite getter for preventing the H 2 O ingress into photovoltaic (either silicon based or thin-film) panels made by means of a dispersion of an active element consisting essentially of one or more alkaline earth metal oxides in a polymeric matrix having low H 2 O transmission.
  • photovoltaic and solar indicate the same or equivalent type of devices (panel, cells) and are to be considered technically equivalent, even though in the following it will be preferably employed the term photovoltaic panel.
  • a photovoltaic panel is composed of one or more photovoltaic elements (so-called cells) for the conversion of solar energy into electric energy.
  • photovoltaic cell reference is made to a single active element, that is the element that converts the luminescent radiation into electric energy, while by photovoltaic panel reference is made to the final product, that is to the set of suitably interconnected solar cells, provided with electrical connections and finally encapsulated.
  • a photovoltaic panel may contain more than one photovoltaic cells (the number of solar cells can vary from 50 to 150). Typically in a thin-film panel the number of photovoltaic cells is about 80.
  • photovoltaic cells There are various types of photovoltaic cells. Among those recently developed, the thin-film photovoltaic cells are of particular interest, due to their conversion efficiency and industrial feasibility.
  • the active element is deposited in form of a film on a (vitreous, metallic or plastic) substrate and is not present in the form of expensive stripes or slices as in the case of mono- or polycrystalline silicon solar cells.
  • metallizations placed in contact with the active element, having the function of interconnecting the cells as such and transporting the current generated by them.
  • the final structure of the photovoltaic panel is rather standardized and independent on the specific type of photovoltaic cell and foresees the use of two, vitreous or plastic, supports to confine and enclose the photovoltaic element. These supports, one of which necessarily must be transparent to the light radiation, ensure also the mechanical stability and the protection from the atmospheric agents.
  • These supports are typically joined together by arranging an encapsulating polymer having good adhesive properties in the space between the two supports; in some cases there can also be spacing elements that fix the distance between the supports, while in other cases it is the thickness of the encapsulating polymer to determine the distance between the supports.
  • the composite getter being object of the present invention is used in both of the above-mentioned structures.
  • the photovoltaic element can be directly in contact with one of the inner surfaces of the supports of the photovoltaic module or can be completely encapsulated by a transparent polymeric material having a low transmission for H 2 O, that is a transmission lower than 10 m ⁇ 2 d ⁇ 1 mm (grams of H 2 O per square meter per day for each millimeter of thickness of the material) at 25° C. and 60% of relative humidity (RH).
  • a transparent polymeric material having a low transmission for H 2 O, that is a transmission lower than 10 m ⁇ 2 d ⁇ 1 mm (grams of H 2 O per square meter per day for each millimeter of thickness of the material) at 25° C. and 60% of relative humidity (RH).
  • the transmission of water by the polymer can also be characterized by means of the MVTR, standing for Moisture Vapour Transmission Rate; the two are strictly correlated, the permeability being the MVTR multiplied by the thickness of the polymeric material and divided by the pressure.
  • the polymeric material used for encapsulating the photovoltaic element is typically composed of EthylVinylAcetate (EVA); often used are also thermoplastic polyurethanes (TPU) and PolyVinylButyral (PVB).
  • EVA EthylVinylAcetate
  • TPU thermoplastic polyurethanes
  • PVB PolyVinylButyral
  • This polymeric material has essentially the aim to fill the inner volume of the photovoltaic panel giving to it at the same time also mechanical stability.
  • inner volume of the photovoltaic panel is intended the volume that is defined by the two supports and by the frame of the panel (typically formed of a polymer having good adhesive properties) that is not occupied by the photovoltaic element or by the other constructive elements of the photovoltaic panel (for example the electric contacts). If the photovoltaic element is in contact with one of the two supports (typically the lower one), it finds itself encapsulated on three sides by the encapsulating polymeric material.
  • thermosealing The manufacturing process of a photovoltaic panel foresees also a process of thermosealing.
  • two main types of processes are used: one foresees the use of a vacuum laminator, while the other foresees the use of an autoclave.
  • the thermosealing is usually carried out between 100 and 170° C. This process results in the melting of the encapsulating polymer.
  • the peripheral adhesion region between the upper support and the lower support, which also can be seen as the frame of the panel, represents a preferential region for the entry of water inside the device since the two supports, upper and lower one, are to be considered impermeable for H 2 O.
  • H 2 O inside the photovoltaic panel has been confronted according to three main approaches: introduction of a H 2 O sorbing material inside the panel; use of a barrier having low H 2 O transmission; use of a barrier having low H 2 O transmission and containing also a H 2 O sorbing element.
  • barriers having low H 2 O transmission comprising a H 2 O sorbing material, is described in the patent application EP 1617494 A2, where such barrier replaces the upper support of the photovoltaic panel.
  • the inventors have instead analyzed the problem on the basis of a different parameter and approach, that is the “lag time” that the water needs to reach the inside of the device; this parameter actually indicates when the constructive elements of the panel begin to deteriorate, whose progressive degeneration during the life results in the deterioration of the characteristics of the panel.
  • the inventors have identified a class of materials, the alkaline earth metals oxides, that when used for the manufacturing of composite getters allow to obtain lag times definitely superior (at the same H 2 O capacity) with respect to composite getters made according to the prior art, thus allowing to prolong the life of the photovoltaic panels.
  • Object of the present invention is thus to provide a composite getter material for the manufacturing of photovoltaic panels capable of increasing the lag time.
  • the invention consists in a composite getter for photovoltaic panels comprising a H 2 O sorber dispersed in a polymeric matrix having low H 2 O transmission, characterized in that said moisture sorber consists essentially of one or more alkaline earth metal oxide.
  • FIGS. 1A and 1B show a thin-film photovoltaic panel containing a composite getter according to the present invention, respectively before and after the process of thermosealing;
  • FIG. 2 shows a comparison between composite getters according to the present invention and a composite getter according to the known art
  • FIG. 3 shows a comparison between two composite getter according to the present invention, containing different moisture sorbers
  • FIG. 4 shows a comparison between composite getter according to the present invention realized with different polymeric matrixes
  • FIG. 5 shows tests results obtained on dummy panels with two preferred composite getters according to the present invention.
  • FIGS. 1A and 1B the dimensions and the dimensional relations between the various elements, particularly with reference to their thicknesses, are not correct, but have been distorted for the sake of better comprehensibility of the figures. Further some constitutive elements of a photovoltaic panel, as for example electrical feedthroughs and connections, have not been shown because they are not relevant for the description of the present invention.
  • the polymeric matrix is a welding polymeric matrix, meaning that its adhesive properties show or improve following a thermal treatment such as the thermosealing, i.e. the heating to a temperature between 100 and 170° C. This condition often implies that the polymeric matrix must have a melting temperature lower than 170° C.
  • Polymers useful for carrying out the invention are for example EthylVinylAcetate (EVA), polyethylene of low (LDPE), medium (MDPE) and high (HDPE) density, polyether block amides (PEBA), ionomeric resins such as SurlynTM commercialized by DuPont, ethylene-acrylic acid copolymers as for example Lucalen® commercialized by Basell, polyvinylidene fluoride (PVDF), PolyVinylButyral (PVB), polyvinylidene chloride (PVDC) such as SaranTM commercialized by DOW Chemicals, Ethylene-Propylene Rubbers (EPR), Ethylene Propylene Diene Monomer Rubbers (EPDM) and butyl rubbers.
  • EVA EthylVinylAcetate
  • PEBA polyether block amides
  • ionomeric resins such as SurlynTM commercialized by DuPont
  • ethylene-acrylic acid copolymers as for example Lucalen
  • these polymers must also have good adhesive characteristics for the supports of the photovoltaic panel.
  • These supports can be made from glass or, in the case it is desired to obtain flexible panels, can be made from plastic materials such as ethylene tetrafluoroethylene (ETFE).
  • ETFE ethylene tetrafluoroethylene
  • the adhesive properties of these polymers can be improved by adding suitable additives such as for example adhesive promoters based on silane or polyolefines functionalized by maleic anhydride grafting, in such a way to obtain panels that have a lap shear force resistance of 0.3-15 N mm ⁇ 2 . Further information on this characteristic may be found in the article by Jorgenson et al. “Testing of Packaging Materials for Improved PV Module Reliability” published in NREL/CP-520-37366.
  • the H 2 O transmission by a polymeric matrix is not linked univocally only to the type of polymer but is a function of various parameters, among which the composition is one of the most relevant ones; thus it is important not to choose the polymer on the basis of the class it belongs to but on the basis of its H 2 O transmission and melting temperature, information easily available to an expert in the field. For example as far as the transmission characteristics of EVA are concerned, this information is available in the article by Marais et al. “Permeation and Sorption of Water and Gases through EVA Copolymers Films” published in 2002 in Mat. Res. Innovation, Vol. 6, pp. 79-88.
  • the inventors have found that properties such as the H 2 O transmission of the polymeric matrix as well as the capacity of the material, defined as quantity of H 2 O sorbed per weight unit, are not the only ones that influence the lag time.
  • the inventors have found that the nature and type of absorber plays a key role.
  • the use of some specific sorbing materials, the alkaline earth metal oxides offers advantages with respect to the use of other types of H 2 O sorbers, such as for example zeolites, alumina and silica.
  • the composite getter is realized with alkaline metal oxides, the presence of other compounds at low levels may not be excluded, depending on the purity of the starting materials; in this regard it is important that the composite getter consists essentially of one or more alkaline metal oxide, meaning that at least 90% of the moisture sorber is an alkaline earth metal oxide.
  • composite getters comprising essentially only one type of alkaline earth metal oxide; in this regard preferred is the use of magnesium oxide, and even more preferred is the use of calcium oxide.
  • the composite getter system being object of the present invention contains a quantity of H 2 O sorber, between 10 wt % and 50 wt %: preferably this percentage is between 30% and 45%. It is important that the concentration in weight of this sorbing material must be not less than 10% to ensure a sufficient lag time. On the other side this concentration has an upper limit because excessively loaded composite getters show problems with respect to the adhesiveness for the substrates.
  • FIG. 1A shows in cross section a thin film panel 10 , containing a composite getter 15 of the present invention, before the operation of thermosealing of the supports.
  • the photovoltaic element 11 has been shown in contact with the lower support 12 .
  • This element is encapsulated by a polymeric material 14 that fills the inner volume of the photovoltaic panel delimited by the lower support 12 , by the upper support 13 and by the composite getter made according to the present invention.
  • FIG. 1B shows the photovoltaic panel 10 after the process of thermosealing: in this case it is possible that the thickness of the composite getter 15 ′ becomes smaller with respect to the starting thickness of the composite getter 15 as a consequence of the combined action of the weight of the upper support and the heating. Further it is possible that the composite getter 15 ′ slightly stands out, both towards the inside and towards the outside of the panel 10 , in this case the quantity of material that outflows from the panel is removed, such removal process is typically called trimming in the technical field.
  • the invention in a second aspect thereof relates to a thin-film photovoltaic panel containing a composite getter, in which said composite getter comprises a H 2 O sorber dispersed in a polymeric matrix having low H 2 O transmission, characterized in that said sorber consists essentially of one or more alkaline earth metal oxide.
  • the photovoltaic panels of the present invention provide for the positioning of the composite getter, typically in the form of a strip, close to the edge or the frame of the panel; in other words the composite getter forms the side interface of the panel to the outer atmosphere.
  • the upper and lower interfaces of the photovoltaic panel are instead formed by the upper and lower support.
  • the invention refers to a method for the manufacturing of photovoltaic panels, characterized in that the composite getter being object of the present invention is arranged close to the edge of one of the two supports, subsequently the other support is laid over and the panel undergoes the thermal process of thermosealing.
  • thermosealing Two main types of processes are used for thermosealing: one foresees the use of a vacuum laminator, while the other foresees the use of an autoclave. In both cases the thermosealing is usually carried out between 100 and 170° C. This process typically consists in a heating to a temperature between 100° C. and 170° C., for a time period variable between 3 and 40 minutes.
  • Different samples of composite getters are produced via extrusion of a blend of a polymerix matrix and a moisture sorber.
  • the extrusion process avoids exposure of the activated moisture sorbers to ambient air.
  • the prepared samples are listed in table 1 that reports the polymeric matrix, its permeability characteristics, the moisture sorber type and its loading content in terms of weight % into the polymeric matrix.
  • the lag time is not directly measurable on a photovoltaic panel since a complete test will require years to complete, whereby accelerated testing procedure have been internally developed, using as starting point the ASTM procedure ASTM E-96-00.
  • the sample is placed in a drier kept at 25° C., and the weight of the aluminum cup is measured over time.
  • the time at which the cup starts to lose weight represents the lag time, since it is the time required for moisture to leave the cup, passing through the composite getter placed on the cup.
  • the cup in this case simulates the ambient environment, whereas the drier atmosphere simulates the panel environment. The purpose of these tests is to provide a relative comparison for the lag times of the different samples.
  • the required width with sample 5 is not compatible with the available lateral space within a photovolatic panel, that typically is less than 20 mm.
  • a more efficient composite getter as the one object of the present invention allows for a prolonged panel lifetime if the same width is kept, otherwise minimizes the lost space thanks to the reduced width in order to guarantee the required lifetime.
  • sample 2 and sample 4 were also characterized with another experiment by means of 15 ⁇ 15 cm dummy panels mounting on the frame different widths of composite getters; in this case it is possible to directly observe the moisture penetration front thanks to a darker coloration in correspondence to the wetted areas of the frame. Also the tests on the dummy panel have been necessarily carried out in accelerated conditions, meaning that the panel have been tested at 85° C. and 85% RH.
  • FIG. 2 shows the comparison between the weight loss curve S 1 obtained for sample 1, shown as a dotted line, with the weight loss curve S 2 obtained for sample 2 and the weight loss curve S 5 , obtained with the comparative sample 5, shown as a thick line.
  • Such comparison shows that the lag time for sample 1, obtained with a composite getter according to the present invention, is about twice with respect to a composite getter obtained with zeolites.
  • Such a comparison is rather important since sample 1 has been loaded with a 20 wt % quantity of moisture sorber, while comparative sample 5 with 40 wt %.
  • the lag time is not a mere function of the moisture sorption capacity, since with these different loading levels samples 1 and 5 have an equivalent capacity, but a lag time that differs by a factor 2 when a composite getter according to the present invention is used. From FIG. 2 it is also possible to observe that the lag time, at a first and rough approximation, depends linearly from the loaded quantity of moisture sorber; being the lag time of sample 2 about twice the one for sample 1, and being sample 2 loaded with twice the amount of calcium oxide.
  • FIG. 3 shows the comparison between the weight loss curve S 2 obtained for sample 2, shown as a dotted line, with the weight loss curve S 3 , shown as thick line, obtained with sample 3. Also these data show that the moisture capacity is not the main parameter influencing the lag time, since sample 3 being loaded with MgO presents a higher moisture absorption capacity with respect to sample 2 that has been loaded with the same wt % of CaO, but has a lower lag time, almost a factor 2 with respect to sample 2.
  • FIG. 4 shows the comparison between the weight loss curve S 4 obtained for sample 4, shown as a thick line, with the weight loss curve S 3 , shown as dotted line, obtained with sample 3.
  • FIG. 5 is a direct comparison of the lag time obtained with different width on the dummy panels, where the thicker curve S′ 4 refers to the results obtained with sample 4, while curve S′ 2 shows the results obtained with sample 2.

Landscapes

  • Photovoltaic Devices (AREA)
  • Sealing Material Composition (AREA)
US12/679,280 2007-10-04 2008-09-24 Composite getter for manufacturing photovoltaic panels Abandoned US20100308262A1 (en)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
IT001902A ITMI20071902A1 (it) 2007-10-04 2007-10-04 Getter composito per la produzione di pannelli solari
ITMI2007A001902 2007-10-04
PCT/EP2008/062782 WO2009043776A1 (en) 2007-10-04 2008-09-24 Composite getter for manufacturing photovoltaic panels

Related Parent Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP2008/062782 A-371-Of-International WO2009043776A1 (en) 2007-10-04 2008-09-24 Composite getter for manufacturing photovoltaic panels

Related Child Applications (1)

Application Number Title Priority Date Filing Date
US14/446,278 Continuation US8906257B2 (en) 2007-10-04 2014-07-29 Composite getter for manufacturing photovoltaic panels

Publications (1)

Publication Number Publication Date
US20100308262A1 true US20100308262A1 (en) 2010-12-09

Family

ID=40092054

Family Applications (2)

Application Number Title Priority Date Filing Date
US12/679,280 Abandoned US20100308262A1 (en) 2007-10-04 2008-09-24 Composite getter for manufacturing photovoltaic panels
US14/446,278 Active US8906257B2 (en) 2007-10-04 2014-07-29 Composite getter for manufacturing photovoltaic panels

Family Applications After (1)

Application Number Title Priority Date Filing Date
US14/446,278 Active US8906257B2 (en) 2007-10-04 2014-07-29 Composite getter for manufacturing photovoltaic panels

Country Status (12)

Country Link
US (2) US20100308262A1 (enrdf_load_stackoverflow)
EP (1) EP2206161B1 (enrdf_load_stackoverflow)
JP (2) JP2010541262A (enrdf_load_stackoverflow)
KR (1) KR101559080B1 (enrdf_load_stackoverflow)
CN (2) CN101828269A (enrdf_load_stackoverflow)
BR (1) BRPI0817632A2 (enrdf_load_stackoverflow)
CA (1) CA2699619A1 (enrdf_load_stackoverflow)
IT (1) ITMI20071902A1 (enrdf_load_stackoverflow)
MY (1) MY153505A (enrdf_load_stackoverflow)
TW (1) TWI453241B (enrdf_load_stackoverflow)
WO (1) WO2009043776A1 (enrdf_load_stackoverflow)
ZA (1) ZA201002045B (enrdf_load_stackoverflow)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US9362435B2 (en) 2011-10-13 2016-06-07 Lg Innotek Co., Ltd. Solar cell apparatus and method of fabricating the same
CN113766971A (zh) * 2019-06-27 2021-12-07 庄信万丰股份有限公司 层状吸着剂结构

Families Citing this family (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
ITMI20071902A1 (it) 2007-10-04 2009-04-05 Getters Spa Getter composito per la produzione di pannelli solari
ITMI20081374A1 (it) 2008-07-25 2010-01-26 Getters Spa Assorbitore composito di h2o per dispositivi medicali sigillati
US20120216869A1 (en) * 2009-10-30 2012-08-30 Takehito Kato Organic photovoltaic cell and method for manufacturing the same
EP2422976B1 (de) * 2010-07-30 2017-03-08 Ems-Patent Ag Photovoltaikmodul-Mehrschichtrückfolie sowie deren Herstellung und Verwendung bei der Produktion photovoltaischer Module
CN101980370B (zh) * 2010-08-31 2012-09-26 深圳市创益科技发展有限公司 一种无边框的太阳能电池组件及封装方法
KR101531452B1 (ko) * 2010-10-12 2015-06-24 쌩-고벵 글래스 프랑스 복합 웨이퍼 구조를 갖는 박층 태양광 모듈
KR101220113B1 (ko) * 2011-07-08 2013-01-11 엘에스산전 주식회사 내습용 태양전지모듈 및 태양전지모듈의 제조방법
WO2016108506A1 (ko) * 2015-01-02 2016-07-07 주식회사 엘지화학 알칼리 금속이 도핑된 산화 마그네슘 입자를 포함하는 게터 조성물
JP6542631B2 (ja) * 2015-09-30 2019-07-10 宇部マテリアルズ株式会社 太陽電池モジュール及びその製造方法
CN105810768B (zh) 2016-04-14 2017-11-21 珠海格力电器股份有限公司 双玻组件

Citations (22)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3998680A (en) * 1975-10-28 1976-12-21 Flint Theodore R Method of fabricating insulating glass units
US4134927A (en) * 1975-10-17 1979-01-16 Mitsui Petrochemical Industries, Ltd. Production of thermoplastic olefin elastomers
US4382999A (en) * 1981-02-16 1983-05-10 Kuraray Isoprene Chemical Co. Ltd. Water-swellable composite caulking material for preventing water leakage
US4453997A (en) * 1979-01-31 1984-06-12 Nitto Electric Industrial Co., Ltd. Bonding method
US5304419A (en) * 1990-07-06 1994-04-19 Alpha Fry Ltd Moisture and particle getter for enclosures
US5401536A (en) * 1992-01-10 1995-03-28 Shores; A. Andrew Method of providing moisture-free enclosure for electronic device
US5548012A (en) * 1993-10-14 1996-08-20 Sumitomo Chemical Company, Ltd. Automotive weather strip
US5733382A (en) * 1995-12-18 1998-03-31 Hanoka; Jack I. Solar cell modules and method of making same
US5874804A (en) * 1997-03-03 1999-02-23 Motorola, Inc. Organic electroluminescent device hermetic encapsulation package and method of fabrication
US6187448B1 (en) * 1997-07-24 2001-02-13 Evergreen Solar, Inc. Encapsulant material for solar cell module and laminated glass applications
US6358580B1 (en) * 1998-01-09 2002-03-19 Thomas Mang Sealing material which swells when treated with water
US20020183431A1 (en) * 2000-05-17 2002-12-05 Yohei Kawaguchi Moisture absorbing formed article
US6534571B1 (en) * 2001-04-25 2003-03-18 Flow Polymers, Inc. Desiccant dispersion for rubber compounds
US20030079772A1 (en) * 2001-10-23 2003-05-01 Gittings Bruce E. Sealed photovoltaic modules
US20030222413A1 (en) * 2002-05-29 2003-12-04 Kabushiki Kaisha Toshiba Gasket for a disk apparatus, and cover, case and disk apparatus having the same
US6936131B2 (en) * 2002-01-31 2005-08-30 3M Innovative Properties Company Encapsulation of organic electronic devices using adsorbent loaded adhesives
US20050284516A1 (en) * 2004-06-23 2005-12-29 Bernhard Koll Solar laminates as laminated safety glass
US20060049396A1 (en) * 2004-09-09 2006-03-09 Karl Pichler Sealing of electronic device using absorbing layer for glue line
US7335422B2 (en) * 2002-04-25 2008-02-26 Sud-Chemie Inc. Absorbent polymeric material
US20080185701A1 (en) * 2005-06-10 2008-08-07 General Electric Company Hermetically Sealed Package and Methods of Making the Same
US7462651B2 (en) * 2005-04-04 2008-12-09 National Starch And Chemical Investment Holding Corporation Radiation-curable desiccant-filled adhesive/sealant
US7901991B2 (en) * 2007-10-04 2011-03-08 Saes Getters S.P.A. Method for manufacturing photovoltaic panels by the use of a polymeric tri-layer comprising a composite getter system

Family Cites Families (16)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2800528B2 (ja) 1992-02-26 1998-09-21 松下電器産業株式会社 ＣｄＳ／ＣｄＴｅ系太陽電池用ＣｄＳ膜の製造方法
JPH09116180A (ja) * 1995-10-20 1997-05-02 Kanegafuchi Chem Ind Co Ltd 半導体装置
JPH1081548A (ja) * 1996-09-05 1998-03-31 Nippon Sheet Glass Co Ltd 複層ガラス及びその製造方法
JP2001148496A (ja) * 1999-11-19 2001-05-29 Kanegafuchi Chem Ind Co Ltd 太陽電池モジュールおよびその製造方法
JP2006291224A (ja) * 2000-05-17 2006-10-26 Dynic Corp 吸湿性成形体
AU2002365087A1 (en) * 2001-10-23 2003-06-23 Bp Corporation North America Inc. Sealed thin film photovoltaic modules
AU2003220839A1 (en) * 2002-03-12 2003-09-22 Hitachi Chemical Co., Ltd. Strip member, sealing medium including the same, sheet sealing medium, sealing substrate, sealed structure, mount device and process for producing these
JP2004311385A (ja) * 2002-03-12 2004-11-04 Hitachi Chem Co Ltd 条部材、これを用いた封止材、シート状封止材、封止用基板、封止構成体、実装体及びこれらの製造方法
US7449629B2 (en) 2002-08-21 2008-11-11 Truseal Technologies, Inc. Solar panel including a low moisture vapor transmission rate adhesive composition
CA2517234C (en) * 2003-03-11 2012-08-28 H.B. Fuller Licensing & Financing, Inc. Low-temperature press process for making insulating glass assemblies
JP4768217B2 (ja) * 2003-07-07 2011-09-07 株式会社ブリヂストン 透明フィルム
JP5167639B2 (ja) * 2004-05-07 2013-03-21 旭硝子株式会社 単層シール型複層透明体
DE602005022805D1 (de) 2004-07-02 2010-09-23 Konarka Technologies Inc Organische photovoltaische Vorrichtung mit Verkapselung
EP1788037B1 (en) 2005-11-16 2013-01-02 Kyocera Mita Corporation Titanylphthalocyanin crystal, method for preparing the same, and electrophotographic photoreceptor
JP2007250082A (ja) * 2006-03-16 2007-09-27 Ricoh Co Ltd 光記録媒体形成用基板および光記録媒体の製造方法と装置
ITMI20071902A1 (it) 2007-10-04 2009-04-05 Getters Spa Getter composito per la produzione di pannelli solari

Patent Citations (23)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4134927A (en) * 1975-10-17 1979-01-16 Mitsui Petrochemical Industries, Ltd. Production of thermoplastic olefin elastomers
US3998680A (en) * 1975-10-28 1976-12-21 Flint Theodore R Method of fabricating insulating glass units
US4453997A (en) * 1979-01-31 1984-06-12 Nitto Electric Industrial Co., Ltd. Bonding method
US4382999A (en) * 1981-02-16 1983-05-10 Kuraray Isoprene Chemical Co. Ltd. Water-swellable composite caulking material for preventing water leakage
US5304419A (en) * 1990-07-06 1994-04-19 Alpha Fry Ltd Moisture and particle getter for enclosures
US5401536A (en) * 1992-01-10 1995-03-28 Shores; A. Andrew Method of providing moisture-free enclosure for electronic device
US5548012A (en) * 1993-10-14 1996-08-20 Sumitomo Chemical Company, Ltd. Automotive weather strip
US5733382A (en) * 1995-12-18 1998-03-31 Hanoka; Jack I. Solar cell modules and method of making same
US5874804A (en) * 1997-03-03 1999-02-23 Motorola, Inc. Organic electroluminescent device hermetic encapsulation package and method of fabrication
US6187448B1 (en) * 1997-07-24 2001-02-13 Evergreen Solar, Inc. Encapsulant material for solar cell module and laminated glass applications
US6358580B1 (en) * 1998-01-09 2002-03-19 Thomas Mang Sealing material which swells when treated with water
US20020183431A1 (en) * 2000-05-17 2002-12-05 Yohei Kawaguchi Moisture absorbing formed article
US6534571B1 (en) * 2001-04-25 2003-03-18 Flow Polymers, Inc. Desiccant dispersion for rubber compounds
US20030079772A1 (en) * 2001-10-23 2003-05-01 Gittings Bruce E. Sealed photovoltaic modules
US6936131B2 (en) * 2002-01-31 2005-08-30 3M Innovative Properties Company Encapsulation of organic electronic devices using adsorbent loaded adhesives
US7335422B2 (en) * 2002-04-25 2008-02-26 Sud-Chemie Inc. Absorbent polymeric material
US20030222413A1 (en) * 2002-05-29 2003-12-04 Kabushiki Kaisha Toshiba Gasket for a disk apparatus, and cover, case and disk apparatus having the same
US20050284516A1 (en) * 2004-06-23 2005-12-29 Bernhard Koll Solar laminates as laminated safety glass
US20060049396A1 (en) * 2004-09-09 2006-03-09 Karl Pichler Sealing of electronic device using absorbing layer for glue line
US7078726B2 (en) * 2004-09-09 2006-07-18 Osram Opto Semiconductors Gmbh Sealing of electronic device using absorbing layer for glue line
US7462651B2 (en) * 2005-04-04 2008-12-09 National Starch And Chemical Investment Holding Corporation Radiation-curable desiccant-filled adhesive/sealant
US20080185701A1 (en) * 2005-06-10 2008-08-07 General Electric Company Hermetically Sealed Package and Methods of Making the Same
US7901991B2 (en) * 2007-10-04 2011-03-08 Saes Getters S.P.A. Method for manufacturing photovoltaic panels by the use of a polymeric tri-layer comprising a composite getter system

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US9362435B2 (en) 2011-10-13 2016-06-07 Lg Innotek Co., Ltd. Solar cell apparatus and method of fabricating the same
CN113766971A (zh) * 2019-06-27 2021-12-07 庄信万丰股份有限公司 层状吸着剂结构

Also Published As

Publication number Publication date
CN104377262B (zh) 2016-06-22
US8906257B2 (en) 2014-12-09
EP2206161B1 (en) 2013-09-18
ITMI20071902A1 (it) 2009-04-05
WO2009043776A1 (en) 2009-04-09
KR20100088674A (ko) 2010-08-10
JP5767364B2 (ja) 2015-08-19
JP2010541262A (ja) 2010-12-24
TW200932809A (en) 2009-08-01
JP2014195095A (ja) 2014-10-09
BRPI0817632A2 (pt) 2015-03-24
TWI453241B (zh) 2014-09-21
ZA201002045B (en) 2010-11-24
KR101559080B1 (ko) 2015-10-08
EP2206161A1 (en) 2010-07-14
US20140332065A1 (en) 2014-11-13
MY153505A (en) 2015-02-27
CN101828269A (zh) 2010-09-08
CN104377262A (zh) 2015-02-25
CA2699619A1 (en) 2009-04-09

Similar Documents

Publication Publication Date Title
US8906257B2 (en) Composite getter for manufacturing photovoltaic panels
US9595626B2 (en) Method for manufacturing photovoltaic panels by the use of a polymeric tri-layer comprising a composite getter system
EP2417631B1 (en) Optoelectronic device
EP1921684A1 (en) Solar cell module and process for manufacture thereof
US10396225B2 (en) Photovoltaic module with improved moisture protection layer
JP2009188357A (ja) 太陽電池モジュール
US20130255745A1 (en) Thin layered solar module having a composite wafer structure
JP2006066761A (ja) 太陽電池モジュール
WO2023132135A1 (ja) 太陽電池

Legal Events

Date Code Title Description
AS Assignment

Owner name: SAES GETTERS S.P.A., ITALY

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:RONDENA, SERGIO;BONUCCI, ANTONIO;LONGONI, GIORGIO;AND OTHERS;REEL/FRAME:024667/0603

Effective date: 20100325

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION