US20090301683A1 - Method and apparatus for removal of cooling water from ingots by means of water jets - Google Patents

Method and apparatus for removal of cooling water from ingots by means of water jets Download PDF

Info

Publication number
US20090301683A1
US20090301683A1 US12/455,274 US45527409A US2009301683A1 US 20090301683 A1 US20090301683 A1 US 20090301683A1 US 45527409 A US45527409 A US 45527409A US 2009301683 A1 US2009301683 A1 US 2009301683A1
Authority
US
United States
Prior art keywords
ingot
water
sprays
cooling water
nozzles
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US12/455,274
Other languages
English (en)
Inventor
Eric W. Reeves
Randy Womack
Wayne J. Fenton
Jeff McDermott
Jim Boorman
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Novelis Inc Canada
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to US12/455,274 priority Critical patent/US20090301683A1/en
Assigned to NOVELIS INC. reassignment NOVELIS INC. ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: FENTON, WAYNE J., REEVES, ERIC W., BOORMAN, JIM, MCDERMOTT, JEFF, WOMACK, RANDY
Assigned to UBS AG, STAMFORD BRANCH reassignment UBS AG, STAMFORD BRANCH SECURITY AGREEMENT Assignors: NOVELIS INC.
Assigned to BANK OF AMERICA, N.A. reassignment BANK OF AMERICA, N.A. SECURITY AGREEMENT Assignors: NOVELIS INC.
Publication of US20090301683A1 publication Critical patent/US20090301683A1/en
Assigned to NOVELIS INC. reassignment NOVELIS INC. SUPPLEMENTAL US INTELLECTUAL PROPERTY SECURITY RELEASE AGREEMENT (CANADIAN GRANTORS) Assignors: UBS AG, STAMFORD BRANCH
Assigned to NOVELIS INC. reassignment NOVELIS INC. SUPPLEMENTAL US INTELLECTUAL PROPERTY SECURITY RELEASE AGREEMENT (CANADIAN GRANTORS) Assignors: BANK OF AMERICA, N.A.
Assigned to BANK OF AMERICA, N.A. reassignment BANK OF AMERICA, N.A. TERM LOAN PATENT SECURITY AGREEMENT (NOVELIS INC. AND U.S. GRANTOR) Assignors: NOVELIS CORPORATION, NOVELIS INC.
Assigned to BANK OF AMERICA, N.A. reassignment BANK OF AMERICA, N.A. ABL PATENT SECURITY AGREEMENT (NOVELIS INC. AND U.S. GRANTOR) Assignors: NOVELIS CORPORATION, NOVELIS INC.
Abandoned legal-status Critical Current

Links

Images

Classifications

    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22D—CASTING OF METALS; CASTING OF OTHER SUBSTANCES BY THE SAME PROCESSES OR DEVICES
    • B22D7/00—Casting ingots, e.g. from ferrous metals
    • B22D7/12—Appurtenances, e.g. for sintering, for preventing splashing
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22D—CASTING OF METALS; CASTING OF OTHER SUBSTANCES BY THE SAME PROCESSES OR DEVICES
    • B22D11/00—Continuous casting of metals, i.e. casting in indefinite lengths
    • B22D11/12—Accessories for subsequent treating or working cast stock in situ
    • B22D11/124—Accessories for subsequent treating or working cast stock in situ for cooling
    • B22D11/1248—Means for removing cooling agent from the surface of the cast stock
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22D—CASTING OF METALS; CASTING OF OTHER SUBSTANCES BY THE SAME PROCESSES OR DEVICES
    • B22D30/00—Cooling castings, not restricted to casting processes covered by a single main group
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22D—CASTING OF METALS; CASTING OF OTHER SUBSTANCES BY THE SAME PROCESSES OR DEVICES
    • B22D9/00—Machines or plants for casting ingots

Definitions

  • This invention relates to casting of metal ingots. More particularly, the invention relates to the cooling of such ingots as they emerge from a casting apparatus by the application and removal of cooling water to the outer surfaces of the ingots.
  • DC direct chill
  • EMC electromagnetic casting
  • billets extrusion ingots
  • HDC horizontal direct chill casting
  • cooling water is directed onto the outer surface of the ingot around the bottom of the mold and the cooling water flows down the sides of the ingot.
  • the cooling water may be removed by means of physical wipers or squeegee-like devices that contact the metal surface, but the surface of the ingot is still hot and wiper devices may quickly become degraded, especially if there is an instance of molten metal bleed-out that brings molten metal into contact with the elastomeric material of the wiper or the metal of the supporting structure.
  • Wipers which mechanically engage the ingot cannot be engaged prior to final curl, so again the first 10 to 14 inches of the ingot is substantially cooled prior to any water being removed. After wiper engagement, the dissimilar temperatures between the butt portion and run portion generates varied metallurgical structures and stresses which can result in further processing problems or the formation of scrap while casting, preheating and rolling.
  • An exemplary embodiment of the invention provides a method of removing cooling water from a surface of a metal ingot, wherein the cooling water streams over the surface in a casting direction.
  • the method involves directing one or more water sprays onto the surface of the ingot at an angle and rate of flow effective to cause the cooling water streaming over the surface to separate from the surface as the cooling water encounters the sprays.
  • enough of the cooling water is removed to allow natural film boiling to occur, thereby removing all of the cooling water within a short distance of the water sprays.
  • Another exemplary embodiment provides an apparatus for removing cooling water from a surface of a metal ingot, wherein the cooling water streams over the surface in a casting direction.
  • the apparatus includes one or more nozzles adapted to direct water sprays onto the surface, the nozzles being positioned and angled such that the water sprays are effective in use to cause the cooling water streaming over the surface to separate from the surface as the cooling water encounters the sprays.
  • the apparatus also includes one or more conduits for supplying water to the nozzles, and pressurizing apparatus for pressurizing water supplied to the nozzles.
  • water jets or sprays are used to remove cooling water from the surface of an ingot as it is being cast.
  • the apparatus for producing the water jets is economical to provide and operate given that the removal medium is water (which may be taken from the same source as the water used for cooling the ingot).
  • the apparatus and method may be used early during casting operations and close to the outlet of the casting mold as the jets are not affected by molten metal bleed out and they follow any variations in the profile of the ingot as it is being produced.
  • FIG. 1 is a vertical cross-section of a known direct chill casting mold provided with a mechanical wiper for removal of cooling water;
  • FIG. 2 is a horizontal cross-section of an ingot being cast by DC casting showing an exemplary embodiment of apparatus for removing cooling water;
  • FIG. 3 is an enlargement of part of the apparatus of FIG. 2 , showing water jets in action;
  • FIG. 4 is a vertical section of part of the apparatus of FIG. 2 prior to activation of the water jets;
  • FIG. 5 is the same view as FIG. 4 but showing the apparatus following activation of the water jets
  • FIG. 6 is a vertical cross-section similar to that of FIG. 5 but showing an exemplary embodiment that makes use of a scupper to remove cooling water;
  • FIG. 7 is a horizontal cross-section of an alternative exemplary embodiment that makes use of a corrugated shield wall to form channels for cooling water stripped from the ingot surface.
  • FIGS. 8 to 10 illustrate alternative embodiments making use of narrow cylindrical water jets to remove cooling water from an ingot
  • FIG. 11 is a cross-section illustrating an exemplary embodiment applied to horizontal DC casting.
  • the exemplary embodiments of the present invention may be used with apparatus of many kinds that employ streams of water to cool a newly-formed metal ingot, e.g. an ingot of a non-ferrous or light metal, such as an ingot of an aluminum, magnesium or copper alloy.
  • a newly-formed metal ingot e.g. an ingot of a non-ferrous or light metal, such as an ingot of an aluminum, magnesium or copper alloy.
  • the exemplary embodiments are especially suitable for use with DC casting apparatus and one form of such apparatus is shown in FIG. 1 and is briefly described below so that the preferred and exemplary embodiments may be better understood, although it is to be noted that the present invention is not limited to equipment of this kind.
  • FIG. 1 is a vertical cross-section of a direct chill casting mold producing a metal ingot and showing a known arrangement for removing cooling water from the outer surface of the ingot.
  • This apparatus is disclosed in U.S. patent publication no. 2007/0102136 to Wagstaff et al., published on May 10, 2007 (the disclosure of which is specifically incorporated herein by this reference).
  • the mold is indicated generally at 10 and it is provided with an open upper entrance 11 and an open lower exit 12 .
  • Molten metal is introduced into the entrance of the mold as indicated by arrow 13 .
  • the mold includes a primary cooling channel 14 filled with recirculating cooling water 15 that cools the inner wall of the mold. The molten metal cools adjacent to the mold wall and forms an embryonic ingot 16 that emerges from the mold.
  • the embryonic ingot has a molten metal sump 17 surrounded by a solid metal shell 18 which increases in thickness as the ingot descends until full solidification occurs at a point remote from the exit 12 of the mold to form a fully solid ingot 19 .
  • Streams or jets of cooling water 20 are poured onto the surface of the ingot from the channel 14 adjacent to the lower exit 12 of the mold to help to form 5 and maintain the solid outer shell 18 around the molten metal sump.
  • the water streams down along the sides of the embryonic ingot, but is removed by a mechanical wiper 21 positioned at a distance X from the exit of the mold.
  • the cooling water 20 removed in this way forms streams 22 spaced from the ingot 19 that have no further cooling effect.
  • the wiper is in the form of an annulus made of a soft flexible or elastomeric material that physically contacts the outer surface of the ingot to wipe away the cooling water.
  • the wiper is held in a rigid holder (not shown) made of metal or the like.
  • distance X is made such as to allow the ingot to “self homogenize”.
  • the exemplary embodiments are not limited to this one purpose.
  • a mechanical wiper of the kind shown at 21 may be replaced by a series of water jets that remove the cooling water from the surface of the ingot.
  • FIG. 2 shows a horizontal cross-section of an ingot at a distance below a direct chill casting mold where cooling water is to be removed.
  • the ingot 19 (or embryonic ingot 16 ) having a downwardly streaming surface layer of cooling water 20 is completely surrounded at a narrow horizontal spacing by a short solid vertical wall 25 (made, for example, of a metal such as aluminum or stainless steel) that extends downwardly from a bottom wall 26 of a direct chill casting mold 10 (see FIGS. 4 and 5 ).
  • the wall 25 is not essential, but acts as a shield to prevent water from spraying onto any other ingots that may be cast at the same time in adjacent areas.
  • the wall 25 is penetrated by a number of holes or slots 27 all positioned at the same vertical height in the illustrated embodiment.
  • An elongated nozzle 28 extends through each slot from outside the wall and terminates a short distance from the outer surface 29 of the ingot.
  • the nozzles 28 on each side of the ingot 19 are connected to a manifold 30 that supplies water under pressure to the nozzles, and the manifolds are connected together in series by high pressure flexible hoses 31 , 32 and 33 .
  • the first manifold in the series is connected by a flexible high pressure hose 34 to an apparatus 35 , e.g. a pump, for supplying water under pressure.
  • an apparatus 35 e.g. a pump
  • the nozzles each spray a jet 36 ( FIG. 3 ) of water towards the surface 29 of the ingot.
  • each of the nozzles forms a jet 36 having the shape of a flat fan of water.
  • the jets 36 are generally flat in vertical side view but expand outwardly in plan view, so that they extend vertically by a much smaller distance than they extend horizontally.
  • the fan shaped jets 36 are preferably partially overlapping, as shown. The angle at the apex of the water jets (as shown in the plan view of FIG.
  • the nozzles are preferably spaced from each other (and/or from the ingot) by distances effective to provide an overlap of the water jets of 1-2 inches at the ingot surface 29 . While this arrangement is particularly preferred, it will be noted from later embodiments that nozzles producing water jets of other shapes may alternatively be employed, e.g. cylindrical jets, and that overlap of the jets may not always be necessary.
  • the manifolds 30 may be of any size and shape, but are preferably square in cross-section (e.g. of 11 ⁇ 4 inches per side) and the nozzles 28 are preferably arranged at intervals of up to about 5 inches from each other, although this may be varied to suit particular molds and spacing arrangements.
  • the manifolds 30 may be, for example, 1720 mm long (long side of ingot) and 560 mm long (short side of ingot).
  • the pressure of the water supplied to the nozzles 28 should be adequate for the removal of most or all of the coolant water from the surface of the ingot and is preferably at least 80 psi up to about 150 psi, and more preferably is in the range of 100-120 psi, to give a rate of flow at each nozzle of at least 0.4 gallons per minute per linear inch of distance around the mold circumference (gpm/in) up to about 1.5 gpm/in, (ideally in the range of 0.6-1.0 gpm/in).
  • the mold discharge flow rate (flow rate relating to the overall water discharge from the mold in advance of the wipers) is preferably at least 0.6 gpm/in up to about 1.5 gpm/in, and is preferably in the range of 0.7-1.0 gpm/in.
  • the high pressure hoses 31 , 32 , 33 and 34 are preferably attached to the manifolds by quick release fittings so that they may be easily disconnected and re-connected to allow the replacement of one or more of the manifolds if they become blocked or otherwise require attention.
  • the manifolds 30 are preferably supported on equipment (not shown) that allows them to be moved closer to or further away from the ingot 19 , and/or closer to or further away from the casting mold. Also, it is desirable to make the nozzles rotatable about a horizontal axis to make it possible to adjust the angle of spray relative to the ingot surface, as circumstances dictate.
  • FIGS. 4 and 5 are detailed vertical sectional views in the region of the bottom wall 26 of the casting mold 10 .
  • the manifolds 30 have been omitted from these drawings for the sake of simplicity but are positioned immediately outside the walls 25 .
  • FIG. 4 shows the situation before the jets are started.
  • Nozzles 28 extend through the vertical wall 25 and face the surface 29 of the ingot 19 emerging from an exit 12 of the casting mold.
  • Cooling water 20 is streamed onto the surface 29 from apertures in the bottom of channel 14 of the mold and the water streams in a continuous layer downwardly along the outer surface of the ingot (as represented by arrow A).
  • the cooling water streams down the ingot in this way until it reaches the bottom of the ingot or a water collection pool.
  • the nozzles 28 are supplied with water under pressure to create flat fan-shaped jets 36 of water that contact the surface 29 of the ingot.
  • the jets When the jets have sufficient momentum (volume of water and rate of flow), and a suitable angle ⁇ relative to the surface 29 (preferably in the range of 65 to 75°, and more preferably 68 to 72°) with a component of movement countercurrent to the direction of flow of the cooling water 20 , they strip the cooling water 20 from the ingot surface and force it to adopt an upward flow 40 (as indicated by arrow B) after leaving the ingot surface 29 .
  • the nozzles 28 are preferably angled upwardly from the horizontal (when the streams 20 flow downwardly) at an angle of 15 to 25°, and more preferably 19 to 22°, although the most effective angle may be determined in particular situations by trial and experimentation.
  • the overlap of the jets further helps to remove the streaming water from the ingot because the momentum created by the water in the overlap region helps to cause the streaming water to spray away from the ingot with an “interactive fountain” effect. Ideally, sufficient cooling water is removed in this way to leave just a thin residual film that quickly dries off due to the high temperature of the ingot.
  • the upward flow 40 of cooling water is caused to bounce off the bottom wall 26 of the casting mold without impacting the junction between the ingot and the mold and entering the mold cavity, and is then caused to run down the inside surface 42 of the vertical wall 25 (as indicated by arrow C) so that there is no further contact between the cooling water and the surface 29 of the ingot beyond distance X.
  • the cooling water is thus stripped from the surface without any direct contact from mechanical parts of the apparatus.
  • cooling water should be stripped from the surface 29 to achieve a desired reduction of cooling of the ingot beyond distance X. Ideally, all or substantially all of the cooling water is removed in this way, but this is not always essential (or perhaps possible) because small amounts of cooling water remain beyond distance X. However, these residual amounts normally disappear quickly or even instantly due to evaporation caused by the heat of the ingot. Also, according to the cooling effect desired in any particular case, a small amount of residual cooling water may be acceptable, even if it does not disperse immediately by evaporation.
  • At least 90% of the volume of the cooling water above point X is removed by the water jets themselves to leave just a sub-film that is quickly or even substantially instantly removed by evaporation.
  • the spacing of the nozzles from the ingot is preferably optimized according to the following considerations.
  • the distance X at which the water jets are applied to the ingot surface depends on the reason for the desired water stripping operation.
  • the water stripping may be required for “in-situ homogenization”, in which case the distance X is one that allows the temperature of the ingot to rise to the homogenization range following water stripping. Cooling water removal may alternatively be carried out for stress relief within the ingot. In the case of more conventional wiping used with hard alloys, a greater distance X is employed and a flash boiling effect of any residual cooling water may not be so important.
  • the distance X may, in some cases, be chosen to differ on different sides of the ingot.
  • the short sides of the ingot (ingot ends) may have a jet contact point that is higher (closer to the mold) than that required for the long faces of the ingot (rolling faces).
  • thinner ingots may have water contact points that are higher than those required for thicker ingots.
  • the rate of flow and pressure of the water jets would normally be the same on all sides of the ingot, unless the streaming water is acted upon by a different force on different sides of the ingot (e.g. gravity in the case of horizontal direct chill casting). In such a case, the flow rate and/or pressure would be varied on different sides of the ingot to achieve the desired degree of water stripping from each ingot face.
  • the ideal angle of the nozzles to produce the cooling water stripping effect can be determined by manually adjusting the angle of the jets (e.g. by rotating the manifolds 30 ) and observing the results. This may be done in a preliminary run of the casting apparatus and then maintained at the same angle for all subsequent casting runs of the same characteristics.
  • exemplary embodiments of the present invention may be especially effective when used with the means of cooling water application disclosed in U.S. Pat. No. 5,685,359 to Wagstaff mentioned above.
  • This means of cooling employs a split jet/dual jet arrangement for ingot cooling purposes at the exit of the casting mold.
  • hoses and manifolds through which the water passes will need filters, shut off valves and other conventional equipment.
  • a 50 mesh filter may be provided to protect the nozzles from blockage.
  • Such a filter may be provided on the supply side of the apparatus 35 for supplying the water under pressure in order to minimize loss of performance of the apparatus.
  • the apparatus 35 may be a pump capable of generating for example 150 psi or more of water pressure and a rate of water flow of 115 gallons per minute or more. Suitable pumps may be obtained, for example, from Pioneer Pump Inc., of 310 South Sequoia Parkway, Canby, Oreg. 97013, U.S.A. (e.g. model SC32C10).
  • the same water that is used for cooling may be employed for the nozzles, or it may be supplied from a different source.
  • the water may be substantially pure, but may contain various additives, such as ethylene glycol. When the water contains such additives, it must of course be supplied from a source different from the cooling water.
  • the water may also contain unintentional additives, particularly if recycled cooling stream water is used.
  • the water is generally at ambient temperature when fed to the nozzles.
  • the nozzles 28 are preferably capable of delivering about 0.8 to 1.0 (or even 1.5 or more) gallons of water per minute over an arc of at least 65° (preferably 72°) at a pressure of 120 psi.
  • Such nozzles may be obtained, for example, from Spraying Systems Co. of P.O. Box 7900, Wheaton, Ill. 60189-7900, U.S.A.
  • the nozzles are preferably used with extenders to allow them to project sufficiently through the shield wall 25 to avoid interruption by contact with the reverse flow of cooling water streaming along the inner surface of the wall.
  • FIG. 6 An alternative embodiment is shown in FIG. 6 .
  • the underside 26 of the mold 10 is provided with a scupper 50 to collect the cooling water 20 stripped from the ingot 19 before it descends down wall 25 to the level of the nozzles 28 .
  • a scupper 50 to collect the cooling water 20 stripped from the ingot 19 before it descends down wall 25 to the level of the nozzles 28 .
  • Water collected in the scupper 50 flows to the ends of the mold and is allowed to pour away from the ingot or is removed through suitable channels (not shown).
  • FIG. 7 Another alternative arrangement is shown in FIG. 7 which makes use of a shield wall 25 having a corrugated shape in plan view.
  • the nozzles 28 project through the wall 25 at positions where the wall is closest to the surface 29 of the ingot 19 .
  • cooling water 20 stripped from the mold by the jets 36 tends to stream into the vertical channels 52 formed between the points of the wall 25 closest to the ingot. This directs the cooling water away from the nozzles 28 and water jets 36 , thereby minimizing any likelihood of interference with the jets.
  • FIGS. 8 to 10 show embodiments where narrow cylindrical water jets are used instead of the fan shaped jets of the above embodiments.
  • the jets 36 (which are upwardly angled as in previous embodiments) penetrate the layer of cooling water 20 to the surface 29 of the ingot 19 and then spread out to separate the cooling water from the ingot surface.
  • the jets 36 spread sufficiently to contact each other and form a combined “interactive fountain” 54 between the positions of the nozzles. This effect is created by adjusting the pressure and flow rates of the nozzles sufficiently. The cooling water layer becomes completely separated from the ingot.
  • FIG. 11 shows an exemplary embodiment of the invention applied to horizontal DC casting.
  • the positions of the nozzles may have to be adjusted to allow the water wiping jets to contact the top surface of the ingot at a different distance from the casting mold relative to the bottom surface of the ingot.
  • a scupper 50 is used at the upper side of the ingot to collect and remove cooling water 20 stripped from the ingot. Without such a means of collecting and removing the stripped cooling water, it would fall back on the ingot and adversely affect the cooling characteristics of the ingot.
  • cooling water 20 may fall naturally from the ingot 19 as shown, or alternatively a series of water jets may also be applied to remove the cooling water at a distinct distance from the mold.
  • a scupper such as the one 50 used at the upper side of the mold, will not be needed at the lower side of the mold because cooling water stripped from the ingot will anyway stream away from the ingot under the action of gravity.
  • the scupper 50 removes the collected cooling water to the ends of the mold and disposes of it without allowing it to come into contact with the ingot or the nozzles.
  • the exemplary embodiments may be employed with various kinds of casting apparatus, not just the DC casting apparatus of FIG. 1 .
  • the invention is suitable for use with metals of various kinds, particularly alloys of aluminum, magnesium and copper. Use with the casting of aluminum alloys is particularly preferred.

Landscapes

  • Engineering & Computer Science (AREA)
  • Mechanical Engineering (AREA)
  • Continuous Casting (AREA)
US12/455,274 2008-06-06 2009-05-28 Method and apparatus for removal of cooling water from ingots by means of water jets Abandoned US20090301683A1 (en)

Priority Applications (1)

Application Number Priority Date Filing Date Title
US12/455,274 US20090301683A1 (en) 2008-06-06 2009-05-28 Method and apparatus for removal of cooling water from ingots by means of water jets

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US13128308P 2008-06-06 2008-06-06
US12/455,274 US20090301683A1 (en) 2008-06-06 2009-05-28 Method and apparatus for removal of cooling water from ingots by means of water jets

Publications (1)

Publication Number Publication Date
US20090301683A1 true US20090301683A1 (en) 2009-12-10

Family

ID=41397664

Family Applications (1)

Application Number Title Priority Date Filing Date
US12/455,274 Abandoned US20090301683A1 (en) 2008-06-06 2009-05-28 Method and apparatus for removal of cooling water from ingots by means of water jets

Country Status (7)

Country Link
US (1) US20090301683A1 (enExample)
EP (1) EP2293892A1 (enExample)
JP (1) JP2011526205A (enExample)
KR (1) KR20110022659A (enExample)
CN (1) CN102083569A (enExample)
CA (1) CA2725614A1 (enExample)
WO (1) WO2009146527A1 (enExample)

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2013138924A1 (en) 2012-03-23 2013-09-26 Novelis Inc. In-situ homogenization of dc cast metals with additional quench
CN104399913A (zh) * 2014-12-10 2015-03-11 西南铝业（集团）有限责任公司 一种铸造用刮水装置及其刮水器升降机
WO2022020248A1 (en) * 2020-07-22 2022-01-27 Novelis Inc. Direct chill casting mold system
RU2830598C1 (ru) * 2020-07-22 2024-11-22 Новелис Инк. Система литейной формы для литья в кристаллизатор

Families Citing this family (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN104368771A (zh) * 2014-12-08 2015-02-25 西南铝业（集团）有限责任公司 一种硬质合金铸造用刮水装置
JP6560838B1 (ja) * 2019-02-12 2019-08-14 株式会社神戸製鋼所 連続鋳造用鋳型および連続鋳造装置並びに連続鋳造方法
CN115867399A (zh) * 2020-07-23 2023-03-28 诺维尔里斯公司 用于监控锭块从底块脱离的系统和方法
CN113441689A (zh) * 2021-06-08 2021-09-28 江苏神铸智能科技有限公司 一种合金铸锭自动化生产设备
FR3151230A1 (fr) 2023-07-21 2025-01-24 Constellium Issoire Dispositif de coulée semi-continue verticale et procédé de fabrication d’alliages d’aluminium

Citations (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US1874959A (en) * 1929-04-20 1932-08-30 Bethlehem Steel Corp Rod cooling and water eliminating apparatus
US2705353A (en) * 1952-04-04 1955-04-05 Kaiser Aluminium Chem Corp Method of continuous casting
US4237961A (en) * 1978-11-13 1980-12-09 Kaiser Aluminum & Chemical Corporation Direct chill casting method with coolant removal
US4474225A (en) * 1982-05-24 1984-10-02 Aluminum Company Of America Method of direct chill casting
US5431214A (en) * 1992-05-12 1995-07-11 Yoshida Kogyo K.K. Apparatus for continuous casting
US5685359A (en) * 1994-02-25 1997-11-11 Wagstaff, Inc. Direct cooled annular mold
US6508298B2 (en) * 2000-01-13 2003-01-21 Sms Demag Ag Method and apparatus for preventing undesirable cooling of the strip edge areas of a cast strand
US20040255987A1 (en) * 2001-09-05 2004-12-23 Heinz-Dietrich Schneider Method and device for draining waste water in the inner bend of a beam blank casting machine
US7007739B2 (en) * 2004-02-28 2006-03-07 Wagstaff, Inc. Direct chilled metal casting system
US20070102136A1 (en) * 2005-10-28 2007-05-10 Wagstaff Robert B Homogenization and heat-treatment of cast metals

Family Cites Families (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB2077643A (en) * 1980-06-13 1981-12-23 British Aluminium Wiping cooling water from a continuous casting
JP3607503B2 (ja) * 1998-06-23 2005-01-05 古河スカイ株式会社 アルミニウム合金鋳塊割れ防止装置とｄｃ鋳造方法
JP2008100253A (ja) * 2006-10-19 2008-05-01 Jfe Steel Kk 連続鋳造機における鋳片水切り装置

Patent Citations (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US1874959A (en) * 1929-04-20 1932-08-30 Bethlehem Steel Corp Rod cooling and water eliminating apparatus
US2705353A (en) * 1952-04-04 1955-04-05 Kaiser Aluminium Chem Corp Method of continuous casting
US4237961A (en) * 1978-11-13 1980-12-09 Kaiser Aluminum & Chemical Corporation Direct chill casting method with coolant removal
US4474225A (en) * 1982-05-24 1984-10-02 Aluminum Company Of America Method of direct chill casting
US5431214A (en) * 1992-05-12 1995-07-11 Yoshida Kogyo K.K. Apparatus for continuous casting
US5685359A (en) * 1994-02-25 1997-11-11 Wagstaff, Inc. Direct cooled annular mold
US6508298B2 (en) * 2000-01-13 2003-01-21 Sms Demag Ag Method and apparatus for preventing undesirable cooling of the strip edge areas of a cast strand
US20040255987A1 (en) * 2001-09-05 2004-12-23 Heinz-Dietrich Schneider Method and device for draining waste water in the inner bend of a beam blank casting machine
US7007739B2 (en) * 2004-02-28 2006-03-07 Wagstaff, Inc. Direct chilled metal casting system
US20070102136A1 (en) * 2005-10-28 2007-05-10 Wagstaff Robert B Homogenization and heat-treatment of cast metals

Cited By (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2013138924A1 (en) 2012-03-23 2013-09-26 Novelis Inc. In-situ homogenization of dc cast metals with additional quench
US8813827B2 (en) 2012-03-23 2014-08-26 Novelis Inc. In-situ homogenization of DC cast metals with additional quench
RU2561538C1 (ru) * 2012-03-23 2015-08-27 Новелис Инк. Гомогенизация in-situ металлов, получаемых литьем с прямым охлаждением и дополнительной закалкой
US9415439B2 (en) 2012-03-23 2016-08-16 Novelis Inc. In-situ homogenization of DC cast metals with additional quench
DE202013012631U1 (de) 2012-03-23 2018-01-15 Novelis, Inc. In-Situ-Homogenisierung von DC-Gussmetallen mit zusätzlichem Abschrecken
RU2641935C2 (ru) * 2012-03-23 2018-01-23 Новелис Инк. Устройство для литья металлических слитков
EP3290131A1 (en) 2012-03-23 2018-03-07 Novelis, Inc. In-situ homogenization of dc cast metals with additional quench
CN104399913A (zh) * 2014-12-10 2015-03-11 西南铝业（集团）有限责任公司 一种铸造用刮水装置及其刮水器升降机
WO2022020248A1 (en) * 2020-07-22 2022-01-27 Novelis Inc. Direct chill casting mold system
CN115697585A (zh) * 2020-07-22 2023-02-03 诺维尔里斯公司 直接激冷铸造模具系统
RU2830598C1 (ru) * 2020-07-22 2024-11-22 Новелис Инк. Система литейной формы для литья в кристаллизатор

Also Published As

Publication number Publication date
CA2725614A1 (en) 2009-12-10
JP2011526205A (ja) 2011-10-06
CN102083569A (zh) 2011-06-01
WO2009146527A1 (en) 2009-12-10
EP2293892A1 (en) 2011-03-16
KR20110022659A (ko) 2011-03-07

Similar Documents

Publication Publication Date Title
US20090301683A1 (en) Method and apparatus for removal of cooling water from ingots by means of water jets
CN101437638B (zh) 用于冷却阳极的方法和设备
US9415439B2 (en) In-situ homogenization of DC cast metals with additional quench
CN106216622A (zh) 一种钢水连铸过程中快速更换中间包的方法
RU2559071C2 (ru) Система управления охлаждающим средством и протиром для кристаллизатора машины непрерывного литья металла
JP2010253529A (ja) 連続鋳造における二次冷却方法
JP2011526205A5 (enExample)
WO2014167895A1 (ja) 高圧鋳造における離型剤塗布方法および装置
JP4437046B2 (ja) 連続鋳造における鋳片のデスケーリング方法
JP4325992B2 (ja) ビームブランク鋳造機の内側湾曲部内の排水を導出するための方法及び装置
JP4882406B2 (ja) 連続鋳造機用クーリンググリッド設備及び連続鋳造鋳片の製造方法
CA1083774A (en) Spray apparatus for continuous casting machine
JP6148447B2 (ja) 連続鋳造の二次冷却方法
JP2007245213A (ja) 連続鋳造時のブレークアウトで流出する溶鋼の粉砕方法およびその装置
KR101243119B1 (ko) 열간 압연기의 와이퍼 탄화 방지 장치
US20250381596A1 (en) Systems and methods for steam condensation in aluminum direct chill casting pit
JP5333296B2 (ja) 連続鋳造用冷却装置及び連続鋳造方法
WO2024006604A1 (en) Systems and methods for steam condensation in aluminum direct chill casting pit
JP2003290880A (ja) 非鉄金属の鋳造用鋳型
JPH01262056A (ja) 連続鋳造装置
JP2009082937A (ja) 水切り装置、及びエアノズルの異常検知方法
KR20120020439A (ko) 연주설비의 수명연장용 냉각장치
JP2008238201A (ja) 連続鋳造機用クーリンググリッド装置および連続鋳造鋳片の製造方法
JPH0611921U (ja) 金属鋳造物の切削片除去装置

Legal Events

Date Code Title Description
AS Assignment

Owner name: NOVELIS INC., CANADA

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:REEVES, ERIC W.;WOMACK, RANDY;FENTON, WAYNE J.;AND OTHERS;REEL/FRAME:022984/0841;SIGNING DATES FROM 20090701 TO 20090706

AS Assignment

Owner name: UBS AG, STAMFORD BRANCH, CONNECTICUT

Free format text: SECURITY AGREEMENT;ASSIGNOR:NOVELIS INC.;REEL/FRAME:023192/0098

Effective date: 20090707

Owner name: BANK OF AMERICA, N.A., ILLINOIS

Free format text: SECURITY AGREEMENT;ASSIGNOR:NOVELIS INC.;REEL/FRAME:023192/0160

Effective date: 20090707

AS Assignment

Owner name: NOVELIS INC., GEORGIA

Free format text: SUPPLEMENTAL US INTELLECTUAL PROPERTY SECURITY RELEASE AGREEMENT (CANADIAN GRANTORS);ASSIGNOR:BANK OF AMERICA, N.A.;REEL/FRAME:025581/0727

Effective date: 20101217

Owner name: NOVELIS INC., GEORGIA

Free format text: SUPPLEMENTAL US INTELLECTUAL PROPERTY SECURITY RELEASE AGREEMENT (CANADIAN GRANTORS);ASSIGNOR:UBS AG, STAMFORD BRANCH;REEL/FRAME:025581/0707

Effective date: 20101217

AS Assignment

Owner name: BANK OF AMERICA, N.A., ILLINOIS

Free format text: ABL PATENT SECURITY AGREEMENT (NOVELIS INC. AND U.S. GRANTOR);ASSIGNORS:NOVELIS INC.;NOVELIS CORPORATION;REEL/FRAME:025671/0507

Effective date: 20101217

Owner name: BANK OF AMERICA, N.A., CALIFORNIA

Free format text: TERM LOAN PATENT SECURITY AGREEMENT (NOVELIS INC. AND U.S. GRANTOR);ASSIGNORS:NOVELIS INC.;NOVELIS CORPORATION;REEL/FRAME:025671/0445

Effective date: 20101217

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION