Classifications

• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F8/00—Chemical modification by after-treatment
  • C08F8/02—Alkylation
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
  • C08G65/00—Macromolecular compounds obtained by reactions forming an ether link in the main chain of the macromolecule
  • C08G65/02—Macromolecular compounds obtained by reactions forming an ether link in the main chain of the macromolecule from cyclic ethers by opening of the heterocyclic ring
  • C08G65/26—Macromolecular compounds obtained by reactions forming an ether link in the main chain of the macromolecule from cyclic ethers by opening of the heterocyclic ring from cyclic ethers and other compounds
  • C08G65/2696—Macromolecular compounds obtained by reactions forming an ether link in the main chain of the macromolecule from cyclic ethers by opening of the heterocyclic ring from cyclic ethers and other compounds characterised by the process or apparatus used
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
  • C08G2/00—Addition polymers of aldehydes or cyclic oligomers thereof or of ketones; Addition copolymers thereof with less than 50 molar percent of other substances
  • C08G2/30—Chemical modification by after-treatment
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
  • C08G65/00—Macromolecular compounds obtained by reactions forming an ether link in the main chain of the macromolecule
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
  • C08G65/00—Macromolecular compounds obtained by reactions forming an ether link in the main chain of the macromolecule
  • C08G65/02—Macromolecular compounds obtained by reactions forming an ether link in the main chain of the macromolecule from cyclic ethers by opening of the heterocyclic ring
  • C08G65/26—Macromolecular compounds obtained by reactions forming an ether link in the main chain of the macromolecule from cyclic ethers by opening of the heterocyclic ring from cyclic ethers and other compounds
  • C08G65/2642—Macromolecular compounds obtained by reactions forming an ether link in the main chain of the macromolecule from cyclic ethers by opening of the heterocyclic ring from cyclic ethers and other compounds characterised by the catalyst used
  • C08G65/2645—Metals or compounds thereof, e.g. salts
  • C08G65/2663—Metal cyanide catalysts, i.e. DMC's
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J27/00—Catalysts comprising the elements or compounds of halogens, sulfur, selenium, tellurium, phosphorus or nitrogen; Catalysts comprising carbon compounds
  • B01J27/24—Nitrogen compounds
  • B01J27/26—Cyanides

Definitions

• the present invention relates in general to catalysis, and more specifically, to the acidification of starter feed stream(s) in a continuous addition of starter (CAOS) polyether polyol production process to improve double metal cyanide (“DMC”) catalyst activity.
• CAOS starter polyether polyol production process
• DMC double metal cyanide
• Base-catalyzed oxyalkylation has been used to prepare polyoxyalkylene polyols for many years.
• a suitably hydric low molecular weight starter molecule such as propylene glycol or glycerine
• one or more alkylene oxides such as ethylene oxide or propylene oxide
• the build ratio (polyol weight/starter weight) is relatively high, and thus the process effectively utilizes reactor capacity.
• Strongly basic catalysts such as sodium hydroxide or potassium hydroxide are typically used in such oxyalkylations.
• polyoxyalkylene polyols useful in synthesis of polyurethane polymers contain substantial amounts of oxypropylene moieties.
• a competing rearrangement of propylene oxide to allyl alcohol generates monofunctional species which also become oxyalkylated, producing a wide range of polyoxyalkylene monols with molecular weights ranging from that of allyl alcohol itself or its low molecular weight oxyalkylated oligomers to polyether monols of very high molecular weight.
• the continuous generation of monols lowers the product functionality.
• a polyoxypropylene diol or triol of 2,000 Da equivalent weight may contain from 30 to 40 mole percent monol.
• the monol content lowers the functionality of the polyoxypropylene diols produced from their “nominal” or “theoretical” functionality of 2.0 to “actual” functionalities in the range of 1.6 to 1.7.
• the functionality may range from 2.2 to 2.4.
• the oxypropylation proceeds further, the functionality continues to decrease, and the molecular weight growth rate slows.
• the upper practical limit for base-catalyzed polyoxypropylene polyol equivalent weight is just above 2,000 Da. Even at those modest equivalent weights, the products are characterized by low actual functionality and broad molecular weight distribution.
• the monol content of polyoxyalkylene polyols is generally determined by measuring the unsaturation, for example by ASTM D-2849-69, “Testing of Urethane Foam Polyol Raw Materials”, as each monol molecule contains allylic termination. Levels of unsaturation of about 0.060 meq/g to in excess of 0.10 meq/g for based-catalyzed polyols such as those described above are generally obtained. Numerous attempts have been made to lower unsaturation, and hence monol content, but few have been successful.
• DMC double metal cyanide
• DMC catalysts were developed with far greater activity than was theretofore possible.
• Those catalysts described for example in U.S. Pat. Nos. 5,470,813 and 5,482,908, allowed commercialization of DMC-catalyzed polyether polyols by ARCO Chemical Company under the ACCLAIM tradename.
• these ultra-low unsaturation polyols often demonstrated dramatic improvements in polymer properties, although formulations were often different from the formulations useful with conventional polyols.
• These polyols typically have unsaturation in the range of 0.002 to 0.008 meq/g.
• DMC-catalyzed oxyalkylation is the difficulty of using low molecular weight starters in polyether synthesis.
• Polyoxyalkylation of low molecular weight starters is generally sluggish, and often accompanied by catalyst deactivation.
• oligomeric starters are prepared in a separate process by base-catalyzed oxypropylation of a low molecular weight starter to equivalent weights in the range of 200 Da to 700 Da or higher. Further oxyalkylation to the target molecular weight takes place in the presence of DMC catalysts.
• strong bases deactivate DMC catalysts.
• the basic catalyst used in oligomeric starter preparation must be removed by methods such as neutralization, adsorption, ion exchange, and the like.
• Several such methods require prolonged filtration of viscous polyol.
• the additional steps associated with catalyst removal from the oligomeric starter can add significant process time, and thus cost, to the overall process.
• the higher molecular weight of the starter lowers the build ratio of the process significantly, thereby decreasing reactor utilization.
• DMC-catalyzed polyol product molecules are contained in a relatively narrow molecular weight band, and thus DMC-catalyzed polyols exhibit very low polydispersities, generally 1.20 or less.
• a very small fraction of molecules i.e., less than 1,000 ppm, have molecular weights in excess of 100,000 Da.
• This very small, but very high molecular weight, fraction is thought to be responsible for some of the anomalous properties observed with ultra-low unsaturation, high functionality polyols.
• These ultra high molecular weight molecules do not significantly alter the polydispersity, however, due to the extremely small amounts present.
• U.S. Pat. Nos. 5,777,177 and 5,689,012 disclose that the high molecular weight “tail” in polyoxypropylene polyols may be minimized by continuous addition of starter (“CAOS”) during oxyalkylation.
• CAOS starter
• low molecular weight starter e.g., propylene glycol or dipropylene glycol
• the continued presence of low molecular weight species has been found to lower the amount of high molecular weight tail produced, while also increasing the build ratio, because a large proportion of the final polyol product is derived from low molecular weight starter itself.
• glycerine a widely used trifunctional starter
• the DMC catalyst gradually deactivates, and often a polyether of the desired molecular weight cannot be obtained, or when obtained, product characteristics such as amount of high molecular weight tail, polydispersity, etc., are less than optimal.
• product characteristics such as amount of high molecular weight tail, polydispersity, etc.
• glycerin and other low molecular weight starters can act as inhibitors and stress the catalyst. Any other effects may be more evident under these stressed conditions.
• glycerine is derived from plant or animal matter by base-dependent processes, it contains one or more basic contaminants which may cause a loss of DMC catalyst activity. McDaniel et al., recognize this and teach in U.S. Pat. No. 6,077,978, the addition of very small amounts (i.e., up to about 100 ppm) of acid to the glycerine initiator prior to its introduction into the reactor as continuously added starter to neutralize the basic contaminants. Synthetic glycerin may have trace residues of base from the manufacturing process.
• Methods said to be useful other than the addition of acid include adsorption by acid adsorbents, and ion-exchange to either neutralize the impurities or to exchange them for acidic moieties.
• the addition of acid is the preferred method of McDaniel et al. for increasing the DMC catalyst's ability to resist deactivation during CAOS feeds at high CAOS/oxide ratios.
• the '978 patent states at col. 6, lines 55-58, that, “ . . . less than 100 ppm acid based on total low molecular weight starter need be added, preferably about 5 ppm to 50 ppm, and most preferably about 10 ppm to 30 ppm” should be used.
• McDaniel et al. fail to provide any teaching or suggestion to add greater amounts of acid than that needed to neutralize basic contaminants of the glycerine.
• the present invention provides a process for the manufacture of lower molecular weight DMC-catalyzed polyols than was heretofore possible using non-acidified continuous addition of starter (CAOS) feeds.
• An excess of acid over that required for neutralization of the basicity of a low molecular weight starter is added to a CAOS feed stream.
• the inventive process may permit the use of less catalyst for a given process than was heretofore required.
• the polyether polyols provided by the process of the present invention may allow for the production of improved polyurethane products, such as coatings, adhesives, elastomers, sealants, foams and the like.
• the present invention adds an excess of acid to a continuous addition of starter (CAOS) feed stream over that required for neutralization of the basicity of a low molecular weight starter. It had heretofore been thought that the addition of excess acid would have, at best no effect, and at worst a negative effect, as experiments in which DMC catalyst is exposed to phosphoric acid in glycerine during storage showed a marked decrease in catalyst activity over time.
• the inventive process unexpectedly allows manufacture of lower molecular weight DMC-catalyzed polyols (250 Da to 2,500 Da) than is possible using non-acidified CAOS feeds.
• the present invention may also permit the use of less catalyst for a given process than heretofore required. Glycerin and other low molecular weight starters can act as inhibitors and stress the catalyst.
• the acid addition has a positive effect allowing the reaction to proceed to completion. This positive effect is unexpectedly observed even with starters having little or no basicity.
• the present invention therefore, provides a process for the polyoxyalkylation of a low molecular weight starter involving establishing oxyalkylation conditions in an oxyalkylation reactor in the presence of a double metal cyanide catalyst, continuously introducing into the reactor at least one alkylene oxide and a low molecular weight starter acidified with at least one of an inorganic protic mineral acid and an organic acid, wherein the acid is in an amount in excess of 100 ppm, based on the weight of the low molecular weight starter and recovering an oxyalkylated low molecular weight starter polyether product.
• the process may be conducted as a semi-batch process or as a continuous addition process. In either case, the low molecular weight starter feed stream, is acidified over and above the level of basic impurities found in the starter.
• the present invention is also directed to the polyol made by the inventive process and polyurethane products incorporating those polyols.
• continuous means a mode of addition of a relevant reactant in such a manner so as to maintain an effective concentration of the reactant substantially continuously.
• Continuous starter addition for example, may be truly continuous, or may be in relatively closely spaced increments. It would not detract from the present process to incrementally add a reactant in such a manner that the added material's concentration decreases to essentially zero for some time prior to the next incremental addition. However, it is preferred that the amount of catalyst be maintained at substantially the same level, although the concentration will change as the alkylene oxide and starter are charged to the reactor, during the course of the continuous reaction. Incremental addition of reactant which does not substantially affect the nature of the product is still “continuous” as that term is used herein.
• polyoxyalkylene polyols are prepared by the oxyalkylation of a low molecular weight starter, in the presence of a double metal cyanide complex catalyst.
• a double metal cyanide complex catalyst In conventional batch processes employing DMC catalysts, the entire initiator (starter) is added initially to the reactor, DMC catalyst is added, and a small percentage of the alkylene oxide feed is added. A significant pressure drop indicates that the catalyst has been activated.
• a preactivated master batch of catalyst mixed with initiator may be used.
• the reactor temperature is maintained at between 70° C. and 150° C., and the remainder of propylene oxide added at relatively low pressure, i.e., less than 10 psig.
• oligomeric starters having an equivalent weight in the range of 200-700 Da or higher are generally used.
• the preparation of a 3,000 Da molecular weight polyoxypropylated glycerine triol may be achieved through oxypropylation of a 1,500 Da molecular weight oligomeric oxypropylated glycerine starter until a molecular weight of 3,000 Da is achieved.
• the build ratio is 3,000 Da/1,500 Da or 2.0. This low build ratio cannot efficiently take advantage of reactor capacity, as some 40 percent of the total reactor capacity is used for starter alone.
• the product will have a small, but significant amount of a very high molecular weight (>100,000 Da) fraction. This high molecular weight fraction (“tail”) is believed to contribute to foam collapse in some polyurethane systems.
• CAOS continuous addition of starter
• polyoxyalkylation is accomplished by addition of a smaller amount of oligomeric starter together with catalyst and initial alkylene oxide for activation as in the conventional process.
• low molecular weight starter is added in addition to alkylene oxide, preferably as a mixed reactor feed stream.
• the amount may be 1.8 weight percent based on the weight of the combined low molecular weight starter/alkylene oxide stream, as a non-limiting example.
• a glycerine polyol of 3,000 Da molecular weight may be prepared at higher build ratios, for example, a build ratio of 5.
• the process efficiency is increased by approximately 100 percent based on propylene oxide usage.
• the product also exhibits less high molecular weight tail.
• the typical CAOS process described above works well when making high molecular weight polyols (e.g. greater than 2500 Da), however, when making lower molecular weight polyols (in the range of 250 to 2500 Da), the catalyst often partially or fully deactivates, particularly where glycerine a common trihydric starter is used in the CAOS process. This is shown by an increase in propylene oxide pressure in the reactor. The reaction slows or substantially ceases, and the product may not reach the desired molecular weight. Products are found to have broad polydispersities and a relatively higher amount of high molecular weight tail.
• Low molecular weight starters useful in the inventive process include those having molecular weights below 400 Da, more preferably below 300 Da, which contain basic, DMC catalyst-deactivating impurities.
• Non-limiting examples of such low molecular weight starter molecules include glycerine, diglycerol, and polyglycerol, all of which are generally prepared through the use of strong bases.
• Glycerine is generally obtained by the hydrolysis, or “saponification” of triglycerides, while diglycerol and polyglycerol may be obtained by base-catalyzed condensation of glycerine.
• suitable low molecular weight starter molecules include various methylolated phenols and similar products prepared by the base-catalyzed reaction of formaldehyde with urea, phenol, cresol, and the like.
• the beneficial effects of the invention unexpectedly extend as well to starter molecules which do not contain basicity, e.g., ethylene glycol, propylene glycol, dipropylene glycol, trimethylolpropane, pentaerythritol, sorbitol, sucrose, and the like.
• the low molecular weight starter may be mixed with other starters as well, e.g., ethylene glycol, propylene glycol, dipropylene glycol, trimethylolpropane, pentaerythritol, sorbitol, sucrose, and the like, to produce co-initiated polyether polyols.
• Reactions where another starter or a lower oligomer are added all at once to the reactor is not a “continuous addition of starter” process.
• a final portion of oxyalkylation may, if desired, be conducted without addition of low molecular weight starter.
• This “finishing” step allows for reduction of moderate molecular weight oligomers by providing sufficient reaction time for the last added low molecular weight starter to be oxyalkylated to a high molecular weight, thus minimizing polydispersity.
• useful acids include, but are not limited to, the mineral acids and the organic carboxylic acids, phosphonic acids, sulfonic acids, and other acids.
• Phosphoric acid is preferred as a mineral acid
• citric acid and 1,3,5-benzene tricarboxylic acids may be useful as organic acids.
• Acid derivatives which are reactive with bases, such as acid chlorides and acid anhydrides and the like, are also useful.
• Organic acids such as phosphonic acids, sulfonic acids, e.g., p-toluene-sulfonic acid, and the like, may also be used.
• mineral acids which are suitable include hydrochloric acid, hydrobromic acid, and sulfuric acid, among others, while useful carboxylic acids or their acidifying derivatives include formic acid, oxalic acid, citric acid, acetic acid, maleic acid, maleic anhydride, succinic acid, succinic anhydride, adipic acid, adipoyl chloride, adipic anhydride, and the like.
• Inorganic acid precursors such as thionyl chloride, phosphorous trichloride, carbonyl chloride, sulfur trioxide, thionyl chloride phosphorus pentoxide, phosphorous oxytrichloride, and the like are considered as mineral acids herein.
• the amount of acid added in the inventive process is in excess of that needed for the mere neutralization of the glycerine, i.e., greater than 100 ppm, more preferably the amount of acid ranges from greater than 100 ppm to 2,000 ppm, and most preferably 200 ppm to 300 ppm.
• the acid may be added in the process of the present invention in an amount ranging between any combination of the above-recited values, inclusive of the recited values.
• the reaction may be initiated by use of an oligomeric starter, but once begun is continuously initiated by further oligomeric starter, preferably by recycle of an oligomer or polymer from a later stage of the reaction.
• Alkylene oxide together with starter or low molecular weight oxyalkylation product is added at various points along the reactor which may, for example, be a tubular reactor (“multi-point addition”).
• a continuous stirred tank reactor (CSTR) or a back-mixed reactor may also be used.
• alkylene oxides useful in the inventive process include, but are not limited to, ethylene oxide, propylene oxide, oxetane, 1,2- and 2,3-butylene oxide, isobutylene oxide, epichlorohydrin, cyclohexene oxide, styrene oxide, and the higher alkylene oxides such as the C 5 -C 30 ⁇ -alkylene oxides.
• Propylene oxide alone or mixtures of propylene oxide with ethylene oxide or another alkylene oxide are preferred.
• Other polymerizable monomers may be used as well, e.g., anhydrides and other monomers as disclosed in U.S. Pat. Nos. 3,404,109, 3,538,043 and 5,145,883, the contents of which are herein incorporated in their entireties by reference thereto.
• the process of the present invention may employ any double metal cyanide (DMC) catalyst.
• Double metal cyanide complex catalysts are non-stoichiometric complexes of a low molecular weight organic complexing agent and optionally other complexing agents with a double metal cyanide salt, e.g. zinc hexacyanocobaltate.
• Suitable DMC catalysts are known to those skilled in the art.
• Exemplary DMC catalysts include those suitable for preparation of low unsaturation polyoxyalkylene polyether polyols, such as disclosed in U.S. Pat. Nos.
• the DMC catalysts more preferred in the process of the present invention are those capable of preparing “ultra-low” unsaturation polyether polyols. Such catalysts are disclosed in U.S. Pat. Nos. 5,470,813 and 5,482,908, 5,545,601, 6,689,710 and U.S. Published Patent Application No. 2004-0044240-A1, the contents of which are herein incorporated in their entireties by reference thereto. Particularly preferred in the inventive process are those zinc hexacyanocobaltate catalysts prepared by the methods described in U.S. Pat. No. 5,482,908.
• the DMC catalyst concentration is chosen so as to ensure good control of the polyoxyalkylation reaction under the given reaction conditions.
• the catalyst concentration is preferably in the range from 0.0005 wt. % to 1 wt. %, more preferably in the range from 0.001 wt. % to 0.1 wt. %, most preferably in the range from 0.001 to 0.01 wt. %, based on the amount of polyether polyol to be produced.
• the DMC catalyst may be present in the process of the present invention in an amount ranging between any combination of these values, inclusive of the recited values.
• the present invention is further illustrated, but is not to be limited, by the following examples.
• inventive process is described below using glycerine as the starter, it is equally applicable to other low molecular weight starters which are synthesized, treated, or stored such that basic impurities which can cause DMC catalyst deactivation are present in the polyol, preferably starters having molecular weights below 300 Da, more preferably below 200 Da.
• starters having molecular weights below 300 Da, more preferably below 200 Da.
• the present invention can also be extended to those starters which do not contain basic impurities.
• Comparative and excess acidified oxypropylations employing continuous addition of starter (CAOS) were performed in a 20 kg reactor.
• CAOS continuous addition of starter
• an amount of 700 Da molecular weight propoxylated glycerin starter sufficient to provide a build ratio of 8 was introduced to the reactor together with an amount of zinc hexacyanocobaltate complex DMC catalyst sufficient to provide a final catalyst concentration of 30 ppm in the final product.
• Commercial glycerin and propylene glycol were utilized.
• the reactor was stripped with a nitrogen sparge at a pressure of 5 to 30 mm Hg for 30 to 40 minutes and a reactor temperature of 130° C.
• Propylene oxide was introduced in an amount equivalent to 4 to 6 weight percent of the starter charge and the reactor pressure monitored to ensure catalyst activation had occurred.
• the “red hot” build ratio is defined as the ratio of the amount of propylene oxide added plus the initial starter weight to the initial starter weight.
• the “red hot” build ratio is necessary to ensure the catalyst is fully activated before the glycerin or propylene glycol is introduced.
• the first “red hot” build ratio refers to the build ratio when the propylene glycol is started. The propylene glycol fed at a weight ratio of 2.3 weight percent to the propylene oxide feed.
• the second “red hot build ratio refers to the start of the glycerin feed, at which point the glycerin was fed at a weight ratio of 17.1 percent to the propylene oxide.
• the co-feed of glycerin, propylene glycol and propylene oxide continued until the reactor contents reached 60 percent of the final batch weight (a 40% non-CAOS cap for propylene glycol).
• Example 2 the glycerin was acidified with 60 ppm of phosphoric acid.
• the reactor pressure was 45 psia when the reactor contents reached 89 percent of the final batch weight, and the reactant feeds were shut down.
• 60 ppm of acid is more than enough to neutralize the basic contaminants measured in the glycerin
• the peak pressure during this batch was 43% higher than was observed during the batch in which the glycerin was acidified to 240 ppm phosphoric acid (Example 2).
• the batch of Example 2 completed normally, reaching a maximum pressure of 32 psia. The presence of a significant excess of acid in Example 2 appears to have had a significant beneficial effect on catalyst activity.
• oxyalkylation conditions in an oxyalkylation reactor is believed to be self-explanatory. Such conditions are established when the reactor temperature, alkylene oxide pressure, catalyst level, degree of catalyst activation, presence of oxyalkylatable compounds within the reactor, etc., are such that upon addition of unreacted alkylene oxide to the reactor, oxyalkylation takes place.
• oxyalkylation conditions are initially established by following the procedures detailed in the preceding examples.
• continuous introducing with respect to addition of alkylene oxide and glycerine starter is meant truly continuous, or an incremental addition which provides substantially the same results as continuous addition of these components.
• oxyalkylated low molecular weight starter polyether is meant a polyoxyalkylene polyether prepared by oxyalkylating the glycerine starter.
• the oxyalkylated glycerine starter polyether will be a polyoxypropylated, glycerine-initiated triol.
• starter and initiator as used herein are the same unless otherwise indicated.
• polyether polyols produced by the process of the present invention may be reacted with one or more isocyanates to provide improved polyurethane products including, but not limited to, coatings, adhesives, sealants, elastomers, foams and the like.

Landscapes

• Chemical & Material Sciences (AREA)
• Health & Medical Sciences (AREA)
• Organic Chemistry (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Medicinal Chemistry (AREA)
• Polymers & Plastics (AREA)
• Toxicology (AREA)
• General Chemical & Material Sciences (AREA)
• Polyethers (AREA)
• Polyurethanes Or Polyureas (AREA)
• Sealing Material Composition (AREA)
• Heterocyclic Carbon Compounds Containing A Hetero Ring Having Oxygen Or Sulfur (AREA)
• Low-Molecular Organic Synthesis Reactions Using Catalysts (AREA)

Priority Applications (17)

Applications Claiming Priority (1)

Related Child Applications (1)

Publications (1)

Family

ID=34838948

Family Applications (2)

Family Applications After (1)

Country Status (15)

Cited By (17)

Families Citing this family (32)

Citations (21)

Family Cites Families (7)

• 2004
  • 2004-03-19 US US10/804,894 patent/US20050209438A1/en not_active Abandoned
• 2005
  • 2005-03-15 CA CA2500905A patent/CA2500905C/fr not_active Expired - Fee Related
  • 2005-03-16 PL PL05005699T patent/PL1577334T3/pl unknown
  • 2005-03-16 AT AT05005699T patent/ATE386766T1/de not_active IP Right Cessation
  • 2005-03-16 EP EP05005699A patent/EP1577334B1/fr active Active
  • 2005-03-16 ES ES05005699T patent/ES2300889T3/es active Active
  • 2005-03-16 PT PT05005699T patent/PT1577334E/pt unknown
  • 2005-03-16 DE DE602005004821T patent/DE602005004821T2/de active Active
  • 2005-03-17 BR BRPI0500969-3A patent/BRPI0500969B1/pt not_active IP Right Cessation
  • 2005-03-17 SG SG200501617A patent/SG115771A1/en unknown
  • 2005-03-17 MX MXPA05003008A patent/MXPA05003008A/es active IP Right Grant
  • 2005-03-18 RU RU2005107562/04A patent/RU2005107562A/ru not_active Application Discontinuation
  • 2005-03-18 JP JP2005078816A patent/JP4912602B2/ja not_active Expired - Fee Related
  • 2005-03-18 KR KR1020050022718A patent/KR101156415B1/ko active IP Right Grant
  • 2005-03-21 CN CN201010004910A patent/CN101851329A/zh active Pending
  • 2005-03-21 CN CNA2005100560038A patent/CN1670007A/zh active Pending
• 2010
  • 2010-05-25 US US12/786,628 patent/US7919575B2/en not_active Expired - Lifetime

Patent Citations (21)

Also Published As

Similar Documents

Legal Events