US20050143477A1 - Macroporous cross-linked polymer particles - Google Patents
Macroporous cross-linked polymer particles Download PDFInfo
- Publication number
- US20050143477A1 US20050143477A1 US10/514,857 US51485704A US2005143477A1 US 20050143477 A1 US20050143477 A1 US 20050143477A1 US 51485704 A US51485704 A US 51485704A US 2005143477 A1 US2005143477 A1 US 2005143477A1
- Authority
- US
- United States
- Prior art keywords
- vinyl
- groups
- solvent
- ether monomers
- polymer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Links
Images
Classifications
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01D—SEPARATION
- B01D15/00—Separating processes involving the treatment of liquids with solid sorbents; Apparatus therefor
- B01D15/08—Selective adsorption, e.g. chromatography
- B01D15/26—Selective adsorption, e.g. chromatography characterised by the separation mechanism
- B01D15/32—Bonded phase chromatography
- B01D15/325—Reversed phase
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J20/00—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof
- B01J20/22—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof comprising organic material
- B01J20/26—Synthetic macromolecular compounds
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J20/00—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof
- B01J20/22—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof comprising organic material
- B01J20/26—Synthetic macromolecular compounds
- B01J20/261—Synthetic macromolecular compounds obtained by reactions only involving carbon to carbon unsaturated bonds
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J20/00—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof
- B01J20/22—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof comprising organic material
- B01J20/26—Synthetic macromolecular compounds
- B01J20/265—Synthetic macromolecular compounds modified or post-treated polymers
- B01J20/267—Cross-linked polymers
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J20/00—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof
- B01J20/281—Sorbents specially adapted for preparative, analytical or investigative chromatography
- B01J20/282—Porous sorbents
- B01J20/285—Porous sorbents based on polymers
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J20/00—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof
- B01J20/281—Sorbents specially adapted for preparative, analytical or investigative chromatography
- B01J20/286—Phases chemically bonded to a substrate, e.g. to silica or to polymers
- B01J20/287—Non-polar phases; Reversed phases
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J20/00—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof
- B01J20/30—Processes for preparing, regenerating, or reactivating
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
- C08F283/00—Macromolecular compounds obtained by polymerising monomers on to polymers provided for in subclass C08G
- C08F283/06—Macromolecular compounds obtained by polymerising monomers on to polymers provided for in subclass C08G on to polyethers, polyoxymethylenes or polyacetals
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J2220/00—Aspects relating to sorbent materials
- B01J2220/50—Aspects relating to the use of sorbent or filter aid materials
- B01J2220/54—Sorbents specially adapted for analytical or investigative chromatography
Definitions
- the present invention relates to the production of macroporous cross-linked polymeric particles useful as packings or carrier of ligands in chromatographic methods as well as to macroporous cross-linked polymeric particles as such.
- chromatography There are numerous methods of chromatography available today, such as ion exchange chromatography (IEX), hydrophobic interaction chromatography (HIC), reversed phase chromatography (RPC), affinity chromatography, gel filtration etc.
- IEX ion exchange chromatography
- HIC hydrophobic interaction chromatography
- RPC reversed phase chromatography
- affinity chromatography gel filtration etc.
- the feature that distinguishes chromatography from most other physical and chemical methods of separation is that two mutually immiscible phases are brought into contact wherein one phase is stationary and the other mobile.
- the sample mixture introduced into the mobile phase, undergoes a series of interactions i.e. partitions many times between the stationary and mobile phases as it is being carried through the system by the mobile phase. Interactions exploit differences in the physical or chemical properties of the components in the sample. These differences govern the rate of migration of the individual components under the influence of a mobile phase moving through the stationary phase.
- Separated components emerge in a certain order, depending on their interaction with the stationary phase.
- the least retained component elutes first, the most strongly retained material elutes last. Separation is obtained when one component is retarded sufficiently to prevent overlap with the zone of an adjacent solute as sample components elute from the column.
- Chromatographic separation methods are useful e.g. for recovery of biomolecules, such as nucleic acids and proteins, and small organic molecules from liquids.
- chromatographic separation methods can also be used for recovery of liquids, in which case impurities such as organic or inorganic molecules are removed to result in a liquid of higher purity.
- the matrix used in chromatography is composed of a carrier material, which is usually in the form of particles, monolithic matrices or the like.
- a carrier material which is usually in the form of particles, monolithic matrices or the like.
- the surface of the carrier itself will provide the interaction with the target molecules.
- the carrier has been provided with ligands that comprise charged groups or affinity groups for interaction with target molecules.
- the carrier materials used can be classified as inorganic materials, such as silica, and organic material, including the groups of synthetic polymers, such as poly(divinylbenzene) (DVB) and poly(divinylbenzene/styrene), and native polymers, such as agarose.
- silica has been used for several years as chromatography beads.
- a general problem with silica is that it is susceptible to hydrolysis in basic conditions, and accordingly the conventional cleaning in place (cip) procedure using sodium hydroxide is not suitable in this case.
- silica matrices cannot be operated in chromatography under high pH conditions, which severely limits their use in a wide range of applications.
- alkyl-bonded silica particles have been suggested for reversed phase liquid chromatography.
- alkyl-bonded silica contains residual silanol groups or impurities, which in some cases results in peak tailing and a poor chromatographic performance in general.
- Matrices based on native organic polymers such as polysaccharides and especially agarose, are used for many chromatographic applications, especially in a derivatised form since the hydroxyl groups available on their surfaces render them easy to derivatise.
- Agarose particles can be cross-linked by addition of a chemical cross-linker, and they will become porous as a result of the gelling procedure. The nature of such particles is what is generally denoted gelporous, and such gelporous particles are in general less advantageous in procedures where high pressures are used.
- Matrices based on synthetic organic polymers such as divinylbenzene (DVB) and styrene
- DVB divinylbenzene
- styrene styrene
- a disadvantage of DVB based matrices is that they often exhibit a large proportion of undesired micropores, which results in impaired mass transfer properties in chromatography. It has been hypothesised that these micropores, which are especially disadvantageous in RPC, are produced as a result of the rapid polymerisation of DVB monomers in suspension polymerisation.
- styrene based matrices Another disadvantage of styrene based matrices appears in cases where it is desired to derivatise the surface of the particle to change its properties, since this kind of matrices exhibit a chemical inertness that in most cases necessitates several surface modification steps before the desired change can be achieved.
- organic polymer-based polymers such as styrene and DVB is that they are somewhat compressible at the high-pressure conditions that are used in high-performance separation methods.
- Ericsson et al have disclosed a separation method, wherein hydrophilic vinyl ether polymers attached to a support are used as a matrix. More specifically, the polymers suggested therein comprise a poly(vinyl ether) chain comprising identical or different vinyl subunits, and the support is illustrated with agarose particles. The polymers are synthesised using cationic polymerisation.
- Hirayama et al (Chromatographia Vol. 33, No 1/2, January 1992, 19-24) suggest suspension copolymerisation of an alkylvinyl ether with triethylene glycol divinyl ether.
- the organic phase was comprised of two different kinds of reactive vinyl ether monomers, the mutual ratio of which was used to set a specific hydrophobicity of the resulting product.
- U.S. Pat. No. 5,334,310 discloses a liquid chromatographic column that contains a separation medium in the form of a macroporous polymer plug, also known as a monolith.
- the polymerisation mixture from which the plug is prepared contains at least one polyvinyl monomer, a free radical generating initiator and a porogen.
- the so prepared plug contains small pores of diameters less than about 200 nm as well as large pores of diameters greater than about 600 nm. Such a large pore diameter range is advantageous for monoliths to allow a high flow rate, but clearly above the useful pore diameter ranges in polymer particles intended for chromatography.
- EP 1 179 732 presents a solution as regards how to produce a polymer adsorbent that exhibits selected porosity and permeability characteristics. This has been achieved by a method, preferably a suspension polymerisation method, wherein selected mixed porogens in selected proportions relative to the monomer are used. The thereby produced adsorbent is due to its rigidity especially suitable for use as an RPC stationary phase at high-pressure conditions.
- each separation principle can be viewed as one tool useful in a toolbox, where there is a constant need of new tools. Accordingly, despite the known matrix materials discussed above, there is still a need of novel methods to use as supplement, i.e. as further tools in a tool box.
- one object of the present invention is to provide a novel material useful as a matrix in chromatographic separation methods, which exhibits properties that differ from known materials. This is achieved by providing macroporous cross-linked polymer particles, which have been polymerised from divinyl ether monomers in an inert solvent that comprises ether and/or polyether groups.
- Another object of the invention is to provide such polymer particles, which result in novel selectivity patterns when used as a matrix in chromatography, such as RPC for protein separation.
- Yet another object of the invention is to provide polymer particles as described above, the surfaces of which are easily derivatised e.g. with functional groups for ion exchange or affinity chromatography, with hydrophobic groups for hydrophobic interaction chromatography (HIC) or any other groups that change the properties of the particle surface in a desired way.
- This is achieved by providing macroporous cross-linked polymer particles that exhibit a sufficient number of vinyl groups available for reaction on their surfaces.
- Another object of the invention is to provide polymer particles essentially devoid of micropores with a narrow pore size distribution.
- Another object of the invention is to provide polymer particles wherein the average pore size has been carefully controlled. This is achieved by using polyethers with different molecular weights as the inert solvent in the method according to the invention.
- One more object of the invention is to provide polymer particles as described above, that fulfil one or more of the criteria above and at the same time exhibit an advantageous mechanical stability and consequently withstand high pressures when packed in chromatographic columns.
- One more object of the present invention is to provide a method of producing a novel material as mentioned above, in which method the average pore size of the final product is carefully controlled. This is achieved by radical polymerisation of divinyl ether monomers in an inert solvent that comprises ether and/or polyether groups of suitable molecular weights, where the solvent also acts as a porogen.
- An additional object of the present invention is to provide a method of producing macroporous cross-linked polymer particles, wherein the polymerisation rate is slower than for prior art polymerisations of divinyl benzene and styrene. This can be desired for various reasons, one of which is that it appears to result in a macroporous structure with less micropores.
- FIG. 1 shows separation of 4 different peptides on an underivatised macroporous polymer particle and a macroporous polymer made more hydrophobic by chemical modification with octadecyl vinyl ether.
- FIG. 2 shows the separation of 6 proteins and illustrates the difference in selectivity between divinyl ether particles according to the invention and prior art DVB/Styrene particles.
- FIG. 3A -C show the pore size distributions of three macoporous polymer particles of the present invention.
- chromatography is used herein to include dynamic as well as batch procedures.
- matrix is used herein to denote a material that is useful as a stationary phase in chromatography. Accordingly, e.g. an RPC matrix will normally be comprised of one material throughout each bead, while an ion exchange matrix will denote a carrier provided with ligands that comprise functional groups for binding target molecules.
- macroporous particles means particles that are porous both in a dry or wet state, as compared to gelporous particles that are porous only in the wet state.
- particle means herein a chromatographic carrier of essentially spherical shape.
- divininyl ether means herein a bifunctional vinyl ether, wherein the two functions are two vinyl groups.
- bifunctional refers to the function of an unsaturated carbon-carbon bond.
- porogen refers to an inert solvent (low molecular weight or polymeric) present during the polymerisation reaction that gives rise to the formation of a macroporous polymer at some stage during the polymerisation.
- inert means being unreactive, i.e. not capable of participating in a chemical reaction such as polymerisation.
- polyether refers to a polymer comprising one or more ether groups with the general formula (I) X—(O—R—O—) n —Y (I) where X and Y may, or may not be identical end groups, for instance alkyl, aryl or hydrogen groups, for example hydrogen, methyl, ethyl, tert-butyl or phenyl groups.
- R is an alkyl or aryl group, linear or branched, which may contain other functional groups, (e.g. carboxylic acid groups, hydroxyl groups or amines, etc) and n is an integer between 2 and 10000, such as between 3 and 5000, or preferably between 5 and 100.
- a first aspect of the present invention is a method of producing one or more macroporous cross-linked polymer particles, which comprises polymerisation and cross-linking of divinyl ether monomers in an inert solvent that comprises ether groups, in which method the polymerisation is free radical initiated.
- the solvent can comprise ethers as well as polyethers, for example as mixtures.
- the solvent comprises polyether groups.
- the solvent is a mixture of ether and/or polyether groups and an alcoholic solvent, preferably comprised to a substantial proportion of ether and/or polyether groups.
- the macroporous cross-linked polymer particles according to the invention polymers can for example be prepared according to the basic principles of conventional suspension polymerisation (see e.g. J. R. Benson and D. J. Woo, J. Chromatographic Sci., 1984, 22, 386).
- an organic solution comprising the desired divinyl ether monomers is mixed with an ether solvent (also denoted porogen in this context) and a thermal initiator and contacted with an aqueous phase containing water, an emulsifying agent and optionally other additives.
- the organic phase and the aqueous phase will form a suspension that is stirred, preferably mechanically, until the desired droplet size is obtained.
- the suspension is then heated to an elevated temperature, typically 65° C., which will lead to thermal decomposition of the initiator and thereby to initiation of the polymerisation.
- the suspension will be kept at an elevated temperature until the polymerisation is considered to be complete, which may typically occur after about 24 hours.
- the resulting macroporous particles can easily be separated from the aqueous phase e.g. on a sintered glass filter, and subsequently be washed with water and/or organic solvents to remove the emulsifier and the porogen, respectively.
- the divinyl ether monomers will act as monomers during the polymerisation as well as as cross-linkers.
- a deliberate choice of a solvent of a small or large molecular weight will result in a correspondingly small or large average pore size.
- the present invention also provides a different solution to the problem addressed e.g. by the above discussed EP 1 179 732.
- the polymerisation is free radical initiated.
- the free radical initiator can be any suitable commercially available initiator, based e.g. on diacetyl peroxide, dibenzoyl peroxide, dilauroyl peroxide, t-butyl peroxypivalate, t-butyl peroctoate, t-amyl peroxypivalate, t-butyl peroxy-2-ethylhexanoate, di-(4-t-butylcyclohexyl)peroxydicarbonate, 2,2′-azobis(isobutyronitrile), 2,2′-azo-bis(2,4-dimethylvaleronitrile), or 1,1′-azo-bis(cyanocyclohexane), and mixtures thereof.
- radical initiator is within the range of 1-10 mole % (per monomer), such as 1-2 mole %.
- the present invention describes for the first time a method of producing cross-linked macroporous polymer particles by polymerisation of divinyl ethers in an inert solvent comprising one or more ethers.
- divinyl ethers have been polymerised for other purposes, such as in surface coatings application, their advantages as cross-linkers in methods to provide macroporous polymer particles have not been fully appreciated before.
- Vinyl ethers can successfully be polymerised by a cationic mechanism to yield high molecular weight polymers.
- vinyl ethers polymerise poorly by a free radical mechanism in traditional low-molecular weight solvents. For this reason, vinyl ethers have not to this point been considered for the synthesis of macroporous polymer particles by suspension polymerisation.
- suspension polymerisation has not been considered to be a suitable polymerisation technique for cationic polymerisations, since it is carried out in the presence of water, and cationic polymerisations are known to be very sensitive to moisture.
- the present inventor has shown that by using divinyl ethers as cross-linkers in a method which is initiated by free radical chemistry and wherein a polyether solvent is used; such particles can successfully be prepared. Furthermore, the particles produced according to the invention have been shown to exhibit a novel kind of selectivity pattern when used as matrices in chromatographic separation methods, as will be illustrated in the experimental part below.
- the use of an inert ether solvent in suspension polymerisation of divinyl ethers has not been suggested before the present invention.
- the solvent is not capable of actively participating in the polymerisation process other than by dissolving the reactive monomers.
- the inert solvent used in the present method does not comprise any vinyl groups, i.e. it does not comprise any polymerisable carbon-carbon double bonds. Accordingly, the present invention clearly differs from the above-discussed Hirayana et al, wherein two reactive monomers but no solvent are used.
- solvents such as toluene, heptane, hexanol and other low molecule weight compounds have been used.
- solvents such as toluene, heptane, hexanol and other low molecule weight compounds have been used.
- the mixtures so obtained have been composed to a substantial extent of small molecular weight components.
- These low molecule weight compounds or mixtures have been a convenient tool to obtain a desired pore size.
- the present invention shows for the first time that use of a relatively high molecule weight solvent comprising ether groups can advantageously be used to produce macroporous cross-linked polymer particles from divinyl ethers.
- the present method uses a polymeric solvent, wherein the average molecular weight of the polymer is above at least 60 g/mole, e.g. above about 100 g/mole, or at least above about 1000 g/mole.
- the polyether solvent is selected from the group that consists of poly(ethylene glycol) (PEG), polypropylene glycol (PPG) and poly (tetrahydrofuran). All these solvents are obtainable from commercial sources, such as Aldrich.
- the present method uses polypropylene glycol (PPG) as a solvent.
- PPG polypropylene glycol
- the divinyl ether monomers used for the present polymerisation are one or more linear, branched or cyclic alkyl, aryl or polymeric divinyl ether monomers.
- the divinyl ethers used according to the present invention can be characterised by the chemical formula (II) C ⁇ C—O—R—O—C ⁇ C (II) wherein R can be any group that does not interfere chemically or sterically with the polymerisation.
- R groups are a linear, branched or cyclic alkyl or aryl chain or polymer, such as ethyl, butyl, hexyl or polyethylene glycol, polypropylene glycol or polytetrahydrofuran.
- the divinyl ether monomers are selected from the group that consists of cyclohexanedimethanol divinyl ether, butanediol divinyl ether or diethyleneglycol divinyl ether.
- the choice of divinyl ether monomers will affect the nature of the polymer particle. Accordingly, if a hydrophobic particle is desired, such as for RPC, then cyclohexanedimethanol divinyl ether is selected, while if a more hydrophilic particle is desired, then diethyleneglycol divinyl ether is preferably used.
- divinyl ether monomers that are useful in the present polymerisation are commercially available, e.g. cyclohexanedimethanol divinyl ether, butanediol divinyl ether or diethyleneglycol divinyl ether (all available from Aldrich).
- the divinyl ether monomers used as starting material can be obtained by synthesis according to well-known methods, see e.g. WO 95/13861.
- the present method is based on the polymerisation and cross-linking of one or more divinyl ethers.
- the monomer mixture used as starting material in the present polymerisation can also comprise other monomers, such as monofunctional monomers comprising one vinyl group and/or bifunctional monomers comprising two such vinyl groups.
- the starting material comprises, in addition to one or more divinyl ether monomers, a monomer that comprises one vinyl group which will be able to participate in polymerisation by reacting said vinyl group and one other functional group, which is not a vinyl group.
- a non-vinyl functional group can e.g.
- the present polymerisation is performed in the presence of another monomer in addition to the divinyl ethers, which comprises one vinyl group and no other functionality.
- Such other monomer can for example comprise a long hydrophobic aliphatic chain or aromatic group, and including such a monomer will result in a more hydrophobic surface of the particle.
- the present invention provides a very versatile method, that can be designed depending on the intended use of the particles produced thereby.
- the present method also comprises a step of modification of the surface of the macroporous particles produced as described above.
- the surface is modified with a compound that comprises a group which is a readily derivatised functionality, such as a hydroxyl group, which is suitable if a hydrophilic particle is desired.
- the hydroxyl may be derivatised e.g. with glycidol.
- Plural molecules of glycidol may be polymerically attached to the hydroxyl by addition of boron trifluoride etherate to produce a covalent coating comprising polymer chains including plural hydroxyls.
- hydroxyls may be oxidised to produce plural carboxylic acid groups.
- the hydroxyl may be reacted with a compound such as an epihalohydrin, such as epibromohydrin, to produce a terminal halide on the covalent coating, which may be reacted with an amine to produce a quaternary amine.
- a compound such as an epihalohydrin, such as epibromohydrin
- An alternative advantageous method of modifying the surface is by grafting, see e.g. International patent application PCT/SE02/02159.
- graffing of a polymer surface with a hydrophobic group, namely octadecyl vinyl ether, is described in Example 1 below.
- modification of the surface of a macroporous particle according to the invention is easily performed by the skilled person in this field according to any well-known method.
- a second aspect of the present invention is a macroporous cross-linked polymer particle, which is comprised of cross-linked divinyl ether polymers.
- the present particles are comprised of polymers of one or more further subunits than divinyl ethers.
- the particles according to the invention can exhibit an average particle size diameter within the interval of about 2-600 ⁇ m, such as about 2-150 ⁇ m, more preferably about 3-100 ⁇ m and most preferably in the interval of about 5-30 ⁇ m.
- the macroporous cross-linked polymer particle according to the invention has been produced as described above. Thus, more details regarding this embodiment are found above.
- a third aspect of the present invention is a reversed phase chromatographic (RPC) method wherein one or more macroporous polymer particles comprised of cross-linked divinyl ethers are used to separate e.g. a protein, peptide, oligonucleotide or smaller organic molecule from a liquid.
- RPC reversed phase chromatographic
- a fourth aspect of the present invention is chemical derivatisation of macroporous polymer particles comprised of cross-linked divinyl ethers with hydrophobic or hydrophilic monofunctional vinyl compounds e.g. monofunctional vinyl ethers or styrene.
- a fifth aspect of the present invention is the use of divinyl ether monomers in a suspension polymerisation initiated by radical reactions.
- the suspension polymerisation is performed in an inert solvent that comprises ether or polyether groups, as discussed in detail above.
- FIG. 1 shows separation of 4 different peptides on macroporous cyclohexane dimetanol divinyl ether particles (Polymer 2) according to the invention (upper), which has been made more hydrophobic by chemical modification with octadecyl vinyl ether, and on the same macroporous polymer particle (Polymer 2) without derivatization (lower).
- Polymer 2 according to the invention was prepared as described in example 1 below.
- FIG. 2 shows the separation of 6 proteins as described in example 3 and illustrates the difference in selectivity between cyclohexane dimetanol divinyl ether particles (Polymer 2) according to the invention (lower) and prior art DVB/styrene particles (SourceTM 15 RPC, available from Amersham Biosciences AB, Uppsala, Sweden) (upper). It should 25 be noted that the particle size of polymer 2 is larger (average diameter 25 ⁇ m) than SourceTM 15 RPC (average diameter 15 ⁇ m), which results in somewhat broader peaks.
- the upper chromatogram shows ribonuclease (19.45); insulin (22.22); lysozyme (25.16); bovine serum albumin (BSA) and ⁇ -chymotrypsin (27.66); and ovalbumin (33.18), while the lower chromatogram shows ribonuclease (14.06); insulin (18.18); lysozyme (20.43); bovine serum albumin (BSA) (22.56); ⁇ -chymotrrpsin (23.75); and ovalbumin (28.36).
- the retention times are generally shorter for polymer 2 compared to Source 15TM RPC. This is a positive feature, since less organic solvent is required for the separation. This improves the process economy, which is especially important for large-scale separations.
- the separation pattern is clearly different between polymer 2 and SourceTM 15 RPC.
- Ovalbumin is better separated from a-chymotrypsin with SourceTM 15 RPC than with Polymer 2.
- FIG. 3A -C show the pore size distributions of three macroporous polymer particles (Polymer 1, Polymer 2 and Polymer 3, respectively) of the present invention as described in example 4.
- the effect on the average pore size of the average molecular weight of the polypropylene glycol can clearly be seen.
- a higher molecular weight polypropylene glycol results in a larger average pore size.
- aqueous phase was prepared in a 250 mL three-necked round-bottom flask equipped with a condenser, a mechanical stirrer and a nitrogen inlet by combining the following ingredients:
- the reaction mixture (combined organic and aqueous phases) was stirred at 540 rpm for 30 minutes under a nitrogen atmosphere. This resulted in organic droplets with an average diameter of approximately 20 ⁇ m.
- the round-bottom flask was then heated to 65° C. over a period of 20 minutes.
- the reaction mixture was kept at 65° C. for 24 h to polymerise the reactants.
- the reaction mixture was allowed to cool to ambient temperature under a nitrogen atmosphere.
- the suspension was transferred to a sintered-glass funnel and the aqueous phase was filtered from the polymer.
- the polymer was washed with 500 mL distilled water, 500 mL ethanol and 500 mL acetone and finally 100 mL 23% ethanol in water (v/v).
- This example describes surface modification of the macroporous polymer particles of the present invention.
- reaction mixture was allowed to cool to ambient temperature and it was subsequently transferred to a sintered-glass funnel and washed with 500 mL of methanol and 500 mL of ethanol.
- This example describes the chromatographic evaluation of the macroporous polymer particles of the present invention for the separation of peptides and proteins.
- Polymer samples of about 2.5 mL volume were packed into analytical steel columns (4.6 mm internal diameter and 15 cm length) and evaluated by performing two separations in aqueous solution, of four peptides and six proteins, respectively.
- a solution of four peptides, angiotensin I, angiotensin III, Val 4 -angiotensin III and Ile 7 -angiotensin III (all available from Sigma-Aldrich, except for angiotensin III which was purchased from ICN) at a concentration of 0.125 mg/mL was prepared.
- the aqueous buffer (here denoted buffer A) was 10 mM potassium phosphate buffer (adjusted to pH 3.0 with potassium hydroxide).
- the organic modifier (buffer B) was 100% acetonitrile, HPLC grade. The linear velocity was 361 cm/h.
- All protein solutions are prepared as stock-solutions (10 mg/ml) that are kept in the freezer.
- the proteins are dissolved one by one in MilliQ-water, except for Insulin that needs acidic conditions to be dissolved (10 mM phosphate buffer pH 2.0).
- the aqueous phase (here denoted buffer A) consisted of 0.1% (v/v) trifluoroacetic acid (TFA) in deionized water.
- the organic modifier (buffer B) was 100% acetonitrile, HPLC grade.
- the injection solutions are prepared by diluting known volumes of stock solution with buffer A to a final protein concentration of 0.5 mg/ml.
- the linear velocity was 361 cm/h.
Landscapes
- Chemical & Material Sciences (AREA)
- Analytical Chemistry (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Organic Chemistry (AREA)
- Polymers & Plastics (AREA)
- Medicinal Chemistry (AREA)
- Health & Medical Sciences (AREA)
- Addition Polymer Or Copolymer, Post-Treatments, Or Chemical Modifications (AREA)
- Graft Or Block Polymers (AREA)
- Solid-Sorbent Or Filter-Aiding Compositions (AREA)
- Macromonomer-Based Addition Polymer (AREA)
- Processes Of Treating Macromolecular Substances (AREA)
- Polymerisation Methods In General (AREA)
Applications Claiming Priority (3)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
SE0201623A SE0201623D0 (sv) | 2002-05-30 | 2002-05-30 | Macroporous cross-linked polymer particles |
SE0201623-6 | 2002-05-30 | ||
PCT/SE2003/000868 WO2003102040A1 (fr) | 2002-05-30 | 2003-05-27 | Particules polymères macroporeuses réticulées |
Publications (1)
Publication Number | Publication Date |
---|---|
US20050143477A1 true US20050143477A1 (en) | 2005-06-30 |
Family
ID=20288009
Family Applications (2)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US10/514,857 Abandoned US20050143477A1 (en) | 2002-05-30 | 2003-05-27 | Macroporous cross-linked polymer particles |
US10/915,290 Expired - Lifetime US7148264B2 (en) | 2002-05-30 | 2004-08-09 | Method of producing macroporous cross-linked polymer particles |
Family Applications After (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US10/915,290 Expired - Lifetime US7148264B2 (en) | 2002-05-30 | 2004-08-09 | Method of producing macroporous cross-linked polymer particles |
Country Status (8)
Country | Link |
---|---|
US (2) | US20050143477A1 (fr) |
EP (1) | EP1507808B1 (fr) |
JP (1) | JP4523408B2 (fr) |
AT (1) | ATE463519T1 (fr) |
AU (1) | AU2003232713A1 (fr) |
DE (1) | DE60332013D1 (fr) |
SE (1) | SE0201623D0 (fr) |
WO (1) | WO2003102040A1 (fr) |
Cited By (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20140309314A1 (en) * | 2011-11-21 | 2014-10-16 | 3M Innovative Properties Company | Polymeric particles for storage and delivery of active agents |
Families Citing this family (9)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
SE0201623D0 (sv) | 2002-05-30 | 2002-05-30 | Amersham Biosciences Ab | Macroporous cross-linked polymer particles |
US7842767B2 (en) | 2003-08-04 | 2010-11-30 | Matrix Innovation Inc. | Polyether based monomers and highly cross-linked amphiphile resins |
JP4741823B2 (ja) * | 2004-09-10 | 2011-08-10 | 新日鐵化学株式会社 | マイクロリアクターを用いたカルボニル化合物の製造法 |
WO2009040826A2 (fr) * | 2007-09-24 | 2009-04-02 | Secretary, Department Of Atomic Energy | Résine sous forme de petits solides, poreuse, non-ionique, avec un éther couronne chimiquement lié |
US20140224738A1 (en) * | 2009-12-22 | 2014-08-14 | Ge Healthcare Bio-Sciences Ab | Packing of chromatography columns |
JP5835724B2 (ja) * | 2011-04-28 | 2015-12-24 | 国立大学法人福井大学 | ジビニルエーテルホモポリマー、その製造方法およびその用途 |
CN103566781B (zh) * | 2013-11-19 | 2016-01-06 | 天津工业大学 | 一种具有星形网状结构的聚氧化乙烯co2优先渗透分离膜 |
JP6848177B2 (ja) * | 2016-01-15 | 2021-03-24 | 昭和電工マテリアルズ株式会社 | 分離材及びカラム |
JP6862679B2 (ja) * | 2016-05-13 | 2021-04-21 | 昭和電工マテリアルズ株式会社 | 多孔質ポリマ粒子の製造方法 |
Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4568706A (en) * | 1983-05-28 | 1986-02-04 | Hoechst Aktiengesellschaft | Macroporous bead polymers, a process for their preparation and their use |
US5135740A (en) * | 1988-04-22 | 1992-08-04 | Advanced Polymer Systems, Inc. | Porous particles in preparations involving immiscible phases |
US5334310A (en) * | 1991-10-21 | 1994-08-02 | Cornell Research Foundation, Inc. | Column with macroporous polymer media |
US5728457A (en) * | 1994-09-30 | 1998-03-17 | Cornell Research Foundation, Inc. | Porous polymeric material with gradients |
US6616825B1 (en) * | 2000-08-23 | 2003-09-09 | The Regents Of The University Of California | Electrochromatographic device for use in enantioselective separation, and enantioselective separation medium for use therein |
Family Cites Families (10)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPS5823137B2 (ja) * | 1979-05-01 | 1983-05-13 | 工業技術院長 | 金属イオン捕捉剤 |
JPS6466219A (en) * | 1987-09-07 | 1989-03-13 | Hitachi Chemical Co Ltd | Production of porous particle of crosslinked copolymer |
JPH01260360A (ja) * | 1988-04-12 | 1989-10-17 | Nippon Oil & Fats Co Ltd | 逆相クロマトグラフィー用充填剤 |
SE9303790D0 (sv) | 1993-11-17 | 1993-11-17 | Pharmacia Lkb Biotech | A method for separation and synthetic polymers that can be used as separation media in the method |
JP4109418B2 (ja) * | 1998-02-27 | 2008-07-02 | ビーアイエー セパレイションズ ディーオーオー | 新規なクロマトグラフィー装置 |
EP1179732B2 (fr) * | 2000-08-11 | 2012-02-29 | Rohm And Haas Company | Absorbants polymère et méthode de préparation |
DK1352003T3 (da) * | 2000-11-20 | 2006-05-29 | Matrix Innovation Inc | Fremgangsmåde til fremstilling af amfifil fast understötning til peptidsyntese, bioorganisk og organisk kemi |
JP2002308925A (ja) * | 2001-04-12 | 2002-10-23 | Univ Nihon | ポリカルボン酸又はポリアルコール球状樹脂 |
US7060187B2 (en) | 2001-11-26 | 2006-06-13 | Ge Healthcare Bio-Sciences Ab | Post-modification of a porous support |
SE0201623D0 (sv) | 2002-05-30 | 2002-05-30 | Amersham Biosciences Ab | Macroporous cross-linked polymer particles |
-
2002
- 2002-05-30 SE SE0201623A patent/SE0201623D0/xx unknown
-
2003
- 2003-05-27 US US10/514,857 patent/US20050143477A1/en not_active Abandoned
- 2003-05-27 AT AT03756138T patent/ATE463519T1/de not_active IP Right Cessation
- 2003-05-27 WO PCT/SE2003/000868 patent/WO2003102040A1/fr active Application Filing
- 2003-05-27 DE DE60332013T patent/DE60332013D1/de not_active Expired - Lifetime
- 2003-05-27 AU AU2003232713A patent/AU2003232713A1/en not_active Abandoned
- 2003-05-27 EP EP03756138A patent/EP1507808B1/fr not_active Expired - Lifetime
- 2003-05-27 JP JP2004509728A patent/JP4523408B2/ja not_active Expired - Lifetime
-
2004
- 2004-08-09 US US10/915,290 patent/US7148264B2/en not_active Expired - Lifetime
Patent Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4568706A (en) * | 1983-05-28 | 1986-02-04 | Hoechst Aktiengesellschaft | Macroporous bead polymers, a process for their preparation and their use |
US5135740A (en) * | 1988-04-22 | 1992-08-04 | Advanced Polymer Systems, Inc. | Porous particles in preparations involving immiscible phases |
US5334310A (en) * | 1991-10-21 | 1994-08-02 | Cornell Research Foundation, Inc. | Column with macroporous polymer media |
US5728457A (en) * | 1994-09-30 | 1998-03-17 | Cornell Research Foundation, Inc. | Porous polymeric material with gradients |
US6616825B1 (en) * | 2000-08-23 | 2003-09-09 | The Regents Of The University Of California | Electrochromatographic device for use in enantioselective separation, and enantioselective separation medium for use therein |
Cited By (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20140309314A1 (en) * | 2011-11-21 | 2014-10-16 | 3M Innovative Properties Company | Polymeric particles for storage and delivery of active agents |
US9827318B2 (en) * | 2011-11-21 | 2017-11-28 | 3M Innovative Properties Company | Polymeric particles for storage and delivery of active agents |
Also Published As
Publication number | Publication date |
---|---|
US20050035061A1 (en) | 2005-02-17 |
EP1507808B1 (fr) | 2010-04-07 |
SE0201623D0 (sv) | 2002-05-30 |
ATE463519T1 (de) | 2010-04-15 |
WO2003102040A1 (fr) | 2003-12-11 |
JP4523408B2 (ja) | 2010-08-11 |
AU2003232713A1 (en) | 2003-12-19 |
US7148264B2 (en) | 2006-12-12 |
DE60332013D1 (de) | 2010-05-20 |
JP2005531651A (ja) | 2005-10-20 |
EP1507808A1 (fr) | 2005-02-23 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
Benes̆ et al. | Methacrylate‐based chromatographic media | |
Legido‐Quigley et al. | Advances in capillary electrochromatography and micro‐high performance liquid chromatography monolithic columns for separation science | |
CA2737404C (fr) | Particules de polymeres reagissant a la chaleur en vue de la separation de proteine | |
Hosoya et al. | Influence of the seed polymer on the chromatographic properties of size monodisperse polymeric separation media prepared by a multi‐step swelling and polymerization method | |
Buchmeiser | New synthetic ways for the preparation of high-performance liquid chromatography supports | |
Svec et al. | Molded rigid monolithic porous polymers: an inexpensive, efficient, and versatile alternative to beads for the design of materials for numerous applications | |
Tennikova et al. | High-performance membrane chromatography of proteins, a novel method of protein separation | |
US5453185A (en) | Column with macroporous polymer media | |
Smith et al. | Developments in the use and fabrication of organic monolithic phases for use with high-performance liquid chromatography and capillary electrochromatography | |
JP4440474B2 (ja) | クロマトグラフィー分離法および選択吸着体 | |
CN103959057A (zh) | 用于蛋白质纯化的基于烯丙胺及其衍生物的新型色谱介质 | |
JP2015515633A (ja) | 分離方法及び分離マトリックス | |
EP1448638B8 (fr) | Post-modification d'un support poreux | |
EP1507808B1 (fr) | Particules polymeres macroporeuses reticulees | |
EP1281436A1 (fr) | Nouveau materiau utilise pour la separation et procede de separation | |
US20100047904A1 (en) | Materials, methods and systems for purification and/or separation | |
AU5381700A (en) | Process for making fluorinated polymer adsorbent particles | |
JP2005510593A5 (fr) | ||
CN110267740B (zh) | 体积排阻色谱用填充剂和其制造方法 | |
Blondeau et al. | Methacrylic copolymers prepared by the ultrasound method: chiral HPLC and GC applications | |
JPH0351460B2 (fr) | ||
Svec | Organic Polymer Support Materials | |
Svec | University of California at Berkeley Berkeley, California | |
WO1996025992A9 (fr) | Supports polymeres poreux passives et procedes de preparation et d'utilisation de ces derniers | |
Lloyd et al. | Polymers and their Application in Liquid Chromatography |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AS | Assignment |
Owner name: AMERSHAM BIOSCIENCES AB, SWEDEN Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:SODERMAN, TOBIAS;REEL/FRAME:015403/0061 Effective date: 20041108 |
|
AS | Assignment |
Owner name: GE HEALTHCARE BIO-SCIENCES AB,SWEDEN Free format text: CHANGE OF NAME;ASSIGNORS:PHARMACIA FINE CHEMICALS AB;PHARMACIA LKB BIOTECHNOLOGY AB;PHARMACIA BIOTECH AB;AND OTHERS;SIGNING DATES FROM 19670125 TO 20011017;REEL/FRAME:017186/0644 Owner name: GE HEALTHCARE BIO-SCIENCES AB, SWEDEN Free format text: CHANGE OF NAME;ASSIGNORS:PHARMACIA FINE CHEMICALS AB;PHARMACIA LKB BIOTECHNOLOGY AB;PHARMACIA BIOTECH AB;AND OTHERS;SIGNING DATES FROM 19670125 TO 20011017;REEL/FRAME:017186/0644 Owner name: GE HEALTHCARE BIO-SCIENCES AB, SWEDEN Free format text: CHANGE OF NAME;ASSIGNORS:PHARMACIA FINE CHEMICALS AB;PHARMACIA LKB BIOTECHNOLOGY AB;PHARMACIA BIOTECH AB;AND OTHERS;REEL/FRAME:017186/0644;SIGNING DATES FROM 19670125 TO 20011017 |
|
STCB | Information on status: application discontinuation |
Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION |