US20050100494A1 - Ferrierite compositions for reducing NOx emissions during fluid catalytic cracking - Google Patents

Ferrierite compositions for reducing NOx emissions during fluid catalytic cracking Download PDF

Info

Publication number
US20050100494A1
US20050100494A1 US10/909,706 US90970604A US2005100494A1 US 20050100494 A1 US20050100494 A1 US 20050100494A1 US 90970604 A US90970604 A US 90970604A US 2005100494 A1 US2005100494 A1 US 2005100494A1
Authority
US
United States
Prior art keywords
metal
catalyst
composition
zeolite
reduction
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US10/909,706
Other languages
English (en)
Inventor
George Yaluris
Michael Ziebarth
Xinjin Zhao
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from US10/702,240 external-priority patent/US20050100493A1/en
Application filed by Individual filed Critical Individual
Priority to US10/909,706 priority Critical patent/US20050100494A1/en
Priority to AU2004288928A priority patent/AU2004288928B2/en
Priority to BRPI0416147-5A priority patent/BRPI0416147B1/pt
Priority to SG200900862-4A priority patent/SG150502A1/en
Priority to PCT/US2004/036642 priority patent/WO2005047429A1/en
Priority to CN2004800327499A priority patent/CN1878855B/zh
Priority to RU2006119619/04A priority patent/RU2365615C2/ru
Priority to JP2006538463A priority patent/JP4977469B2/ja
Priority to CN200910126434.5A priority patent/CN101503632B/zh
Priority to CA2544918A priority patent/CA2544918C/en
Priority to AT04810274T priority patent/ATE550408T1/de
Priority to KR1020067008710A priority patent/KR101133833B1/ko
Priority to EP04810274A priority patent/EP1680484B1/en
Publication of US20050100494A1 publication Critical patent/US20050100494A1/en
Priority to TW94125998A priority patent/TWI395614B/zh
Priority to ARP050103203 priority patent/AR051556A1/es
Priority to IL174876A priority patent/IL174876A/en
Priority to NO20062598A priority patent/NO20062598L/no
Priority to US12/833,336 priority patent/US9931595B2/en
Priority to IL213527A priority patent/IL213527A0/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01D—SEPARATION
    • B01D53/00—Separation of gases or vapours; Recovering vapours of volatile solvents from gases; Chemical or biological purification of waste gases, e.g. engine exhaust gases, smoke, fumes, flue gases, aerosols
    • B01D53/34—Chemical or biological purification of waste gases
    • B01D53/74—General processes for purification of waste gases; Apparatus or devices specially adapted therefor
    • B01D53/86—Catalytic processes
    • B01D53/8621—Removing nitrogen compounds
    • B01D53/8625—Nitrogen oxides
    • B01D53/8628—Processes characterised by a specific catalyst
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J21/00—Catalysts comprising the elements, oxides, or hydroxides of magnesium, boron, aluminium, carbon, silicon, titanium, zirconium, or hafnium
    • B01J21/14—Silica and magnesia
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J23/00—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00
    • B01J23/38—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of noble metals
    • B01J23/40—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of noble metals of the platinum group metals
    • B01J23/42—Platinum
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J23/00—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00
    • B01J23/70—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of the iron group metals or copper
    • B01J23/76—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of the iron group metals or copper combined with metals, oxides or hydroxides provided for in groups B01J23/02 - B01J23/36
    • B01J23/83—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of the iron group metals or copper combined with metals, oxides or hydroxides provided for in groups B01J23/02 - B01J23/36 with rare earths or actinides
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J29/00—Catalysts comprising molecular sieves
    • B01J29/04—Catalysts comprising molecular sieves having base-exchange properties, e.g. crystalline zeolites
    • B01J29/06—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof
    • B01J29/65—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof of the ferrierite type, e.g. types ZSM-21, ZSM-35 or ZSM-38, as exemplified by patent documents US4046859, US4016245 and US4046859, respectively
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J29/00—Catalysts comprising molecular sieves
    • B01J29/04—Catalysts comprising molecular sieves having base-exchange properties, e.g. crystalline zeolites
    • B01J29/06—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof
    • B01J29/80—Mixtures of different zeolites
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J35/00—Catalysts, in general, characterised by their form or physical properties
    • B01J35/19—Catalysts containing parts with different compositions
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J35/00—Catalysts, in general, characterised by their form or physical properties
    • B01J35/30—Catalysts, in general, characterised by their form or physical properties characterised by their physical properties
    • B01J35/34—Mechanical properties
    • B01J35/38—Abrasion or attrition resistance
    • C—CHEMISTRY; METALLURGY
    • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
    • C10G—CRACKING HYDROCARBON OILS; PRODUCTION OF LIQUID HYDROCARBON MIXTURES, e.g. BY DESTRUCTIVE HYDROGENATION, OLIGOMERISATION, POLYMERISATION; RECOVERY OF HYDROCARBON OILS FROM OIL-SHALE, OIL-SAND, OR GASES; REFINING MIXTURES MAINLY CONSISTING OF HYDROCARBONS; REFORMING OF NAPHTHA; MINERAL WAXES
    • C10G11/00—Catalytic cracking, in the absence of hydrogen, of hydrocarbon oils
    • C10G11/14—Catalytic cracking, in the absence of hydrogen, of hydrocarbon oils with preheated moving solid catalysts
    • C10G11/18—Catalytic cracking, in the absence of hydrogen, of hydrocarbon oils with preheated moving solid catalysts according to the "fluidised-bed" technique
    • C—CHEMISTRY; METALLURGY
    • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
    • C10G—CRACKING HYDROCARBON OILS; PRODUCTION OF LIQUID HYDROCARBON MIXTURES, e.g. BY DESTRUCTIVE HYDROGENATION, OLIGOMERISATION, POLYMERISATION; RECOVERY OF HYDROCARBON OILS FROM OIL-SHALE, OIL-SAND, OR GASES; REFINING MIXTURES MAINLY CONSISTING OF HYDROCARBONS; REFORMING OF NAPHTHA; MINERAL WAXES
    • C10G11/00—Catalytic cracking, in the absence of hydrogen, of hydrocarbon oils
    • C10G11/14—Catalytic cracking, in the absence of hydrogen, of hydrocarbon oils with preheated moving solid catalysts
    • C10G11/18—Catalytic cracking, in the absence of hydrogen, of hydrocarbon oils with preheated moving solid catalysts according to the "fluidised-bed" technique
    • C10G11/182—Regeneration
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01D—SEPARATION
    • B01D2255/00—Catalysts
    • B01D2255/50—Zeolites
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01D—SEPARATION
    • B01D2258/00—Sources of waste gases
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J2229/00—Aspects of molecular sieve catalysts not covered by B01J29/00
    • B01J2229/10—After treatment, characterised by the effect to be obtained
    • B01J2229/18—After treatment, characterised by the effect to be obtained to introduce other elements into or onto the molecular sieve itself
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J2229/00—Aspects of molecular sieve catalysts not covered by B01J29/00
    • B01J2229/30—After treatment, characterised by the means used
    • B01J2229/42—Addition of matrix or binder particles
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J29/00—Catalysts comprising molecular sieves
    • B01J29/04—Catalysts comprising molecular sieves having base-exchange properties, e.g. crystalline zeolites
    • B01J29/06—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof
    • B01J29/08—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof of the faujasite type, e.g. type X or Y
    • B01J29/084—Y-type faujasite
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J35/00—Catalysts, in general, characterised by their form or physical properties
    • B01J35/30—Catalysts, in general, characterised by their form or physical properties characterised by their physical properties
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J37/00—Processes, in general, for preparing catalysts; Processes, in general, for activation of catalysts
    • B01J37/0009—Use of binding agents; Moulding; Pressing; Powdering; Granulating; Addition of materials ameliorating the mechanical properties of the product catalyst
    • B01J37/0027—Powdering
    • B01J37/0045—Drying a slurry, e.g. spray drying
    • C—CHEMISTRY; METALLURGY
    • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
    • C10G—CRACKING HYDROCARBON OILS; PRODUCTION OF LIQUID HYDROCARBON MIXTURES, e.g. BY DESTRUCTIVE HYDROGENATION, OLIGOMERISATION, POLYMERISATION; RECOVERY OF HYDROCARBON OILS FROM OIL-SHALE, OIL-SAND, OR GASES; REFINING MIXTURES MAINLY CONSISTING OF HYDROCARBONS; REFORMING OF NAPHTHA; MINERAL WAXES
    • C10G2300/00—Aspects relating to hydrocarbon processing covered by groups C10G1/00 - C10G99/00
    • C10G2300/40—Characteristics of the process deviating from typical ways of processing
    • C10G2300/405—Limiting CO, NOx or SOx emissions

Definitions

  • the present invention relates to NO x reduction compositions and the method of use thereof to reduce NO x emissions in refinery processes, and specifically in fluid catalytic cracking (FCC) processes. More particularly, the present invention relates to NO x reduction compositions and their method of use to reduce the content of NO x off gases released from a fluid catalytic cracking unit (FCCU) regenerator during the FCC process without a substantial change in hydrocarbon conversion or the yield of valuable cracked products.
  • FCCU fluid catalytic cracking unit
  • FCCU Fluid catalytic cracking units
  • catalyst particles are continuously circulated between a catalytic cracking zone and a catalyst regeneration zone.
  • coke deposited on the cracking catalyst particles in the cracking zone is removed at elevated temperatures by oxidation with oxygen containing gases such as air.
  • oxygen containing gases such as air.
  • the removal of coke deposits restores the activity of the catalyst particles to the point where they can be reused in the cracking reaction.
  • the regenerator flue gas when coke is burned with a deficiency of oxygen, the regenerator flue gas has a high CO/CO 2 ratio and a low level of NO x , but when burned with excess oxygen, the flue gas has a high level of NO x and a reduced CO content.
  • CO and NO x , or mixtures of these pollutants are emitted with the flue gas in varying quantities, depending on such factors as unit feed rate, nitrogen content of the feed, regenerator design, mode of operation of the regenerator, and composition of the catalyst inventory.
  • Additives have also been used in attempts to deal with NO x emissions.
  • U.S. Pat. Nos. 6,379,536, 6,280,607, 6,129,834 and 6,143,167 disclose the use of NO x removal compositions for reducing NO x emissions from the FCCU regenerator.
  • U.S. Pat. Nos. 6,358,881 and 6,165,933 also disclose a NO x reduction composition, which promotes CO combustion during the FCC catalyst regeneration process step while simultaneously reducing the level of NO x emitted during the regeneration step.
  • NO x reduction compositions disclosed by these patents may be used as an additive which is circulated along with the FCC catalyst inventory, or incorporated as an integral component of the FCC catalyst.
  • U.S. Pat. Nos. 4,973,399 and 4,980,052 disclose reducing emissions of NO x from the regenerator of the FCCU by incorporating into the circulating inventory of cracking catalyst separate additive particles containing a copper-loaded zeolite.
  • the FCCU may have insufficient air capacity to burn the extra coke and may result in a lower feed throughput in the unit. If the additive increases the production of low value dry gas, the production of more valuable products may decrease. An increase in dry gas may exceed the ability of the unit to handle it, thus forcing a reduction of the amount of feed processed. While an additive that increases light olefins production may be desirable if the refinery values these products and the unit has the equipment necessary to process the extra light hydrocarbons, the additive may, however, reduce profitability if the refinery's goal is to maximize gasoline production. Light olefins are typically made in the FCCU at the expense of gasoline production. Even an additive which increases unit conversion may be undesirable if it affects product yields, causes the unit to reach an equipment limitation, and/or decreases the amount of feed that can be processed.
  • FCCU fluid catalytic cracking unit
  • FCC fluid catalytic cracking
  • the NO x reduction compositions comprise a particulate composition containing particles of ferrierite zeolite.
  • the ferrierite zeolite may be added as a separate additive particle to a circulating inventory of the cracking catalyst or incorporated directly into the Y-type zeolite containing cracking catalyst as an integral component of the catalyst.
  • the ferrierite zeolite are separate additive particles bound with an inorganic binder.
  • the binder preferably comprises silica, alumina or silica alumina.
  • the ferrierite zeolite is exchanged with hydrogen, ammonium, alkali metal and combinations thereof.
  • the preferred alkali metal is sodium, potassium and combinations thereof.
  • novel ferrierite zeolite-containing NO x reduction compositions are provided which are added to a circulating inventory of the catalytic cracking catalyst as a separate admixture of particles to reduce NO x emissions released from the FCCU regenerator during the FCC process.
  • novel NO x reduction compositions which comprise ferrierite zeolite incorporated as an integral component of the FCC catalyst, preferably containing a Y-type zeolite active component.
  • novel NO x reduction compositions are provided which compositions reduce NO x emissions from the FCCU regenerator during the FCC process while substantially maintaining hydrocarbon conversion and the yield of cracked petroleum products and minimizing an increase in the production of coke.
  • Another aspect of the invention is to provide improved FCC processes for the reduction of the content of NO x in the off gases of the FCCU regenerator without substantially affecting hydrocarbon conversion or the yield of petroleum products produced during the FCC process.
  • the FIGURE is a graphic representation of the effectiveness of Additive A and Additive B, prepared in EXAMPLES 1 and 2, respectively, to reduce NO x emissions from a DCR regenerator versus time on stream, when the additives are blended with a commercially available cracking catalyst (SUPERNOVA®-DMR+, obtained from Grace Davison, Columbia, Md.), which contains 0.25 weight percent of a platinum promoter, CP-3® (obtained from Grace Davison, Columbia, Md.) and which was deactivated using the Cyclic Propylene Steaming procedure as described in EXAMPLE 3.
  • SUPERNOVA®-DMR+ obtained from Grace Davison, Columbia, Md.
  • CP-3® obtained from Grace Davison, Columbia, Md.
  • NO x will be used herein to represent nitric oxide, nitrogen dioxide (the principal noxious oxides of nitrogen) as well as N 2 O 4 , N 2 O 5 and mixtures thereof.
  • the present invention encompasses the discovery that the use of ferrierite zeolite containing NO x reduction compositions in combination with a fluid catalytic cracking (FCC) catalyst, preferably a catalyst comprising an active Y-type zeolite, is very effective for the reduction of NO x emissions released from the FCCU regenerator under FCC process conditions without a substantial change in hydrocarbon feed conversion or the yield of cracked products.
  • the NO x reduction compositions typically comprise a particulate composition containing particles of ferrierite zeolite.
  • the ferrierite particles are bound with an inorganic binder.
  • the novel ferrierite zeolite-containing NO x reduction compositions may be added to the circulating inventory of the catalytic cracking catalyst as a separate particle additive or incorporated as an integral component into the cracking catalyst.
  • the phrase “a substantial change in hydrocarbon feed conversion or the yield of cracked products” is defined herein to mean in the alternative, (i) less than a 50% relative change, preferably less than a 30% relative change and most preferably less than a 15% relative change in the yield of LPG (liquefied petroleum gas) as compared to the baseline yield of the same or substantially the game product; or (ii) less than a 30% relative change, preferably less than a 20% relative change and most preferably less than a 10% relative change in the yield of LCO (light cycle oils), bottoms and gasoline in combination with LPG as compared to the baseline yield of the same or substantially the same products; or (iii) less than a 10% relative change, preferably less than a 6.5% relative change and most preferably less than a 5% relative change in the hydrocarbon feed conversion as compared to the baseline conversion.
  • the conversion is defined as 100% times (1—bottoms yield—LCO yield).
  • the baseline is the mean conversion or yield of a product in the FCCU, operating with the same or substantially the same feed and under the same or substantially the same reaction and unit conditions, but before the additive of the present invention is added to the catalyst inventory.
  • a significant change in the hydrocarbon conversion or yield of cracked products is determined using a baseline defined as the mean conversion or yield of a product in the same or substantially the same FCCU operating with the same or substantially the same feed, under the same or substantially the same reaction and unit conditions, and with a cracking catalyst inventory comprising the same or substantially the same cracking catalyst composition as that containing the NO x reduction composition, except that the NO x reduction composition is replaced in the cracking catalyst with a matrix component such as kaolin or other filler.
  • the percent changes specified above are derived from statistical analysis of DCR operating data.
  • any ferrierite zeolite is useful to prepare the NO x reduction compositions of the invention.
  • the ferrierite zeolite has a surface area of at least 100 m 2 /g, more preferably at least 200 m 2 /g and most preferably at least 300 m 2 /g and a SiO 2 to Al 2 O 3 molar ratio of less than 500, preferably less than 250, most preferably, less than 100.
  • the ferrierite zeolite is exchanged with a material selected from the group consisting of hydrogen, ammonium, alkali metal and combinations thereof, prior to incorporation into the binder or FCC catalyst.
  • the preferred alkali metal is one selected from the group consisting of sodium, potassium and mixtures thereof.
  • the ferrierite zeolite may contain stabilizing amounts, e.g., up to about 25 weight percent, of a stabilizing metal (or metal ion), preferably incorporated into the pores of the zeolite.
  • a stabilizing metal or metal ion
  • Suitable stabilizing metals include, but are not limited to, metals selected from the group consisting of Groups IIA, IIIB, IVB, VB, VIB, VIIB, VIII, IIB, IIIA, IVA, VA, the Lanthanide Series of The Periodic Table, Ag and mixtures thereof.
  • the stabilizing metals are selected from the group consisting of Groups IIIB, IIA, IIB, IIIA and the Lanthanide Series of the Periodic Table, and mixtures thereof.
  • the stabilizing metals are selected from the group consisting of lanthanum, aluminum, magnesium, zinc, and mixtures thereof.
  • the metal may be incorporated into the pores of the ferrierite zeolite by any method known in the art, e.g., ion exchange, impregnation or the like.
  • the Periodic Table referenced herein above is the Periodic Table as published by the American Chemical Society.
  • the amount of ferrierite zeolite used in the NO x reduction compositions of the invention will vary depending upon several factors, including but not limited to, the mode of combining the ferrierite zeolite with the catalytic cracking catalyst and the type of cracking catalyst used.
  • the NO x reduction compositions of the invention are separate catalyst/additive compositions and comprise a particulate composition formed by binding particles of a ferrierite zeolite with a suitable inorganic binder.
  • the amount of ferrierite zeolite present in the particulate NO x reduction compositions is at least 10, preferably at least 30, most preferably at least 40 and even more preferably at least 50, weight percent based on the total weight of the composition.
  • the particulate catalyst/additive composition of the invention contains from about 10 to about 85, preferably from about 30 to about 80, most preferably, from about 40 to about 75, weight percent of ferrierite zeolite based on the total weight of the catalyst/additive composition.
  • Binder materials useful to prepare the particulate compositions of the invention include any inorganic binder which is capable of binding ferrierite zeolite powder to form particles having properties suitable for use in the FCCU under FCC process conditions.
  • Typical inorganic binder materials useful to prepare compositions in accordance with the present invention include, but are not limited to, alumina, silica, silica alumina, aluminum phosphate and the like, and mixtures thereof.
  • the binder is selected from the group consisting of alumina, silica, silica alumina. More preferably, the binder comprises alumina. Even more preferably, the binder comprises an acid or base peptized alumina.
  • the binder comprises an alumina sol, e.g., aluminum chlorohydrol.
  • the amount of binder material present in the particular NO x reduction compositions comprises from about 5 to about 50 weight percent, preferably from about 10 to about 30 weight percent, most preferably from about 15 to about 25 weight percent, of the NO x reduction composition of the invention.
  • Additional materials optionally present in the compositions of the present invention include, but are not limited to, fillers (e.g., kaolin clay) or matrix materials (e.g., alumina, silica, silica alumina, yttria, lanthana, ceria, neodymia, samaria, europia, gadolinia, titania, zirconia, praseodymia and mixtures thereof).
  • the additional materials are used in an amount which does not significantly adversely affect the performance of the compositions to reduce NO x emissions released from the FCCU regenerator under FCC conditions, the hydrocarbon feed conversion or the product yield of the cracking catalyst.
  • the additional materials will comprise no more than about 70 weight percent of the compositions. It is preferred, however, that the compositions of the invention consist essentially of ferrierite and an inorganic binder.
  • Particulate NO x reduction compositions of the invention should have a particle size sufficient to permit the composition to be circulated throughout the FCCU simultaneously with the inventory of cracking catalyst during the FCC process.
  • the composition of the invention will have a mean particle size of greater than 45 ⁇ m.
  • the mean particle size is from about 50 to about 200 ⁇ m, most preferably from about 55 to about 150 ⁇ m, even more preferred from about 60 to about 120 ⁇ m.
  • the compositions of the invention typically have a Davison attrition index (DI) value of less than about 50, preferably less than about 20, most preferably less than about 15.
  • DI Davison attrition index
  • the particulate NO x reduction compositions of the invention are prepared by forming an aqueous slurry containing the ferrierite zeolite, optional zeolite components, the inorganic binder and optional matrix materials, in an amount sufficient to provide at least 10.0 weight percent of ferrierite zeolite and at least 5.0 weight percent of binder material in the final NO x reduction composition and, thereafter, spray drying the aqueous slurry to form particles.
  • the spray-dried particles are optionally dried at a sufficient temperature for a sufficient time to remove volatiles, e.g., at about 90° C. to about 320° C. for about 0.5 to about 24 hours.
  • the ferrierite zeolite containing aqueous slurry is milled prior to spray-drying to reduce the mean particle size of materials contained in the slurry to 10 ⁇ m or less, preferably 5 ⁇ m or less, most preferably 3 ⁇ m or less.
  • the aqueous slurry containing ferrierite zeolite may be milled prior to or after incorporation of the binder and/or matrix materials as desired.
  • the spray-dried composition may be calcined at a temperature and for a time sufficient to remove volatiles and provide sufficient hardness to the binder for use in the FCCU under FCC process conditions, preferably from about 320° C. to about 900° C. from about 0.5 to about 6 hours.
  • the dried or calcined composition is washed or exchanged with an aqueous solution of ammonia or ammonium salt (e.g., ammonium sulfate, nitrate, chloride, carbonate, phosphate and the like), or an inorganic or organic acid (e.g., sulfuric, nitric, phosphoric, hydrochloric, acetic, formic and the like) to reduce the amount of alkaline metals, e.g. sodium or potassium, in the finished product.
  • ammonia or ammonium salt e.g., ammonium sulfate, nitrate, chloride, carbonate, phosphate and the like
  • an inorganic or organic acid e.g., sulfuric, nitric, phosphoric, hydrochloric, acetic, formic and the like
  • Particulate NO x reduction compositions of the invention are circulated in the form of separate particle additives along with the main cracking catalyst throughout the FCCU.
  • the catalyst/additive composition is used in an amount of at least 0.1 weight percent of the FCC catalyst inventory.
  • the amount of the catalyst/additive composition used ranges from about 0.1 to about 75 weight percent, most preferably from about 1 to about 50 weight percent of the FCC catalyst inventory.
  • Separate particle catalyst/additive compositions of the invention may be added to the FCCU in the conventional manner, e.g., with make-up catalyst to the regenerator or by any other convenient method.
  • the ferrierite zeolite is integrated or incorporated into the cracking catalyst particles themselves to provide an integral NO x reduction catalyst system.
  • the ferrierite zeolite may be added to the catalyst at any stage during catalyst manufacturing prior to spray drying the cracking catalyst slurry to obtain the fluid cracking catalyst, regardless of any additional optional or required processing steps needed to finish the cracking catalyst preparation.
  • the ferrierite zeolite, any additional zeolites, the cracking catalyst zeolite, usually USY or REUSY-type, and any matrix materials are slurried in water.
  • the slurry is milled to reduce the mean particle size of solids in the slurry to less than 10 ⁇ m, preferably to less than 5 ⁇ m, most preferably less than 3 ⁇ m.
  • the milled slurry is combined with a suitable inorganic binder, i.e., a silica sol binder, and an optional matrix material, e.g. clay.
  • the resulting slurry is mixed and spray-dried to provide a catalyst material.
  • the spray-dried catalyst is optionally washed using an aqueous solution of ammonium hydroxide, an ammonium salt, an inorganic or organic acid, and water to remove the undesirable salts.
  • the washed catalyst may be exchanged with a water soluble rare-earth salt, e.g., rare-earth chlorides, nitrates and the like.
  • the ferrierite zeolite, optional additional zeolites, the cracking catalyst zeolite, any matrix materials, a rare-earth water soluble salt, clay and alumina sol binder are slurried in water and blended.
  • the slurry is milled and spray-dried.
  • the spray-dried catalyst is calcined at about 250° C. to about 900° C.
  • the spray-dried catalyst may then optionally be washed using an aqueous solution of ammonium hydroxide, an ammonium salt, an inorganic or organic acid, and water to remove the undesirable salts.
  • the catalyst may be exchanged with a water-soluble rare-earth salt after it has been washed, by any of the methods known in the art.
  • the ferrierite zeolite compound When integrated into the FCC catalyst particles, the ferrierite zeolite compound typically represents at least about 0.1 weight percent of the FCC catalyst particle. Preferably, the amount of the ferrierite zeolite used ranges from about 0.1 to about 60 weight percent, most preferably from about 1 to about 40 weight percent, of the FCC catalyst particles.
  • the integrated FCC catalyst will typically comprise the ferrierite zeolite along with the cracking catalyst zeolite, inorganic binder materials and optionally, matrix, fillers, and other additive components such as metals traps (for example, traps for Ni and V) to make up the cracking catalyst.
  • the cracking catalyst zeolite usually a Y. USY or REUSY-type, provides the majority of the cracking activity and is typically present in a range from about 10 to about 75, preferably from about 15 to about 60 and most preferably from about 20 to about 50 weight percent based on the total weight of the composition.
  • Inorganic binder materials useful to prepare integrated catalyst compositions in accordance with the present invention include, any inorganic material capable of binding the components of the integrated catalyst to form particles having properties suitable for use in the FCCU under FCC process conditions.
  • the inorganic binder materials include, but are not limited to, alumina, silica, silica alumina, aluminum phosphate and the like, and mixtures thereof.
  • the binder is selected from the group consisting of alumina, silica, silica alumina.
  • the amount of binder material present in the integrated catalyst composition is less than 50 weight percent, based on the total weight of the catalyst composition.
  • the, amount of binder material present in the integrated catalyst composition ranges from about 5 to about 45 weight percent, most preferably from about 10 to about 30 weight percent and even more preferably from about 15 to about 25 weight percent, based on the total weight of the composition.
  • the matrix materials optionally present in the integrated catalyst compositions of the present invention include, but are not limited to alumina, silica alumina, rare earth oxides such as lanthana, transition metal oxides such as titania, zirconia, and manganese oxide, Group IIA oxides such as magnesium and barium oxides, clays such as kaolin, and mixtures thereof.
  • the matrix or fillers may be present in the integral catalyst in the amount of less than 50 weight percent based on the total weight of the composition.
  • the matrix and fillers, if any, are present in an amount ranging from about 1 to about 45 weight present based on the total weight of the catalyst composition.
  • the particle size and attrition properties of the integral catalyst affect fluidization properties in the unit and determine how well the catalyst is retained in the commercial FCC unit.
  • the integral catalyst composition of the invention typically has a mean particle size of about 45 to about 200 ⁇ m, more preferably from about 50 ⁇ m to about 150 ⁇ m.
  • the attrition properties of the integral catalyst as measured by the Davison Attrition Index (DI), have a DI value of less than 50, more preferably less than 20 and most preferably less than 15.
  • the FCC cracking catalyst contains a Y-type zeolite.
  • the ferrierite zeolite may be added as a separate additive particle to a circulating inventory of the cracking catalyst or incorporated directly into the Y-type zeolite containing cracking catalyst as an integral component of the catalyst. In either case, it is preferred that ferrierite zeolite is present in the final composition in an amount sufficient to provide in the total catalyst inventory a ratio of ferrierite zeolite to Y-type zeolite of less than 2, preferably less than 1.
  • additional zeolite components in the ferrierite zeolite containing NO x reduction compositions of the invention.
  • the additional zeolite component may be any zeolite which does not adversely affect the NO x reduction performance or cause a substantial change in hydrocarbon conversion or cracked product yields during the FCC process.
  • the additional zeolite component is a zeolite having a pore size ranging from about 3 to about 7.2 Angstroms with a SiO 2 to Al 2 O 3 molar ratio of less than about 500, preferably less than 250.
  • the additional zeolite component is a zeolite selected from the group consisting of ZSM-5, ZSM-11, beta, MCM-49, mordenite, MCM-56, Zeolite-L, zeolite Rho, errionite, chabazite, clinoptilolite, MCM-22, MCM-35, MCM-61, Offretite, A, ZSM-12, ZSM-23, ZSM-18, ZSM-22, ZSM-35, ZSM-57, ZSM-61, ZK-5, NaJ, Nu-87, Cit-1, SSZ-35, SSZ-48, SSZ-44, SSZ-23, Dachiardite, Merlinoite, Lovdarite, Levyne, Laumontite, Epistilbite, Gmelonite, Gismondine, Cancrinite, Brewsterite, Stilbite, Paulingite, goosecreekite, Natrolite or mixtures thereof.
  • the additional zeolite component is selected from the group consisting of ZSM-5, ZSM-11, beta, MCM-49, mordenite, MCM-56, Zeolite-L, zeolite Rho, errionite, chabazite, clinoptilolite, MCM-22, MCM-35, Offretite, A, ZSM-12 and mixtures thereof.
  • the additional zeolite component is used in any amount that does not significantly adversely affect the performance of the NO x reduction compositions to reduce NO x emissions and substantially maintain the hydrocarbon conversion or the product yields of the cracking catalyst relative to the use of the cracking catalyst without the catalyst/additive composition.
  • the additional zeolite component is used in an amount ranging from about 1 to about 80, preferably from about 10 to about 70, weight percent of the catalyst/additive composition.
  • the additional zeolite component is preferably used in an amount ranging from about 0.1 to about 60, most preferably from about 1 to about 40, weight percent of the catalyst composition.
  • the FCC process involves the cracking of heavy hydrocarbon feedstocks to lighter products by contact of the feedstock in a cyclic catalyst recirculation cracking process with a circulating fluidizable cracking catalyst inventory consisting of particles having a mean size ranging from about 50 to about 150 ⁇ m, preferably from about 60 to about 120 ⁇ m.
  • the catalytic cracking of these relatively high molecular weight hydrocarbon feedstocks results in the production of a hydrocarbon product of lower molecular weight.
  • the significant steps in the cyclic FCC process are:
  • FCC catalysts include, for example, zeolite based catalysts with a faujasite cracking component as described in the seminal review by Venuto and Habib, Fluid Catalytic Cracking with Zeolite Catalysts, Marcel Dekker, New York 1979, ISBN 0-8247-6870-1, as well as in numerous other sources such as Sadeghbeigi, Fluid Catalytic Cracking Handbook, Gulf Publ. Co. Houston, 1995, ISBN 0-88415-290-1.
  • the FCC catalyst is a catalyst comprising a Y-type zeolite active cracking component.
  • the FCC catalysts consist of a binder, usually silica, alumina, or silica alumina, a Y-type zeolite active component, one or more matrix aluminas and/or silica aluminas, and fillers such as kaolin clay.
  • the Y-type zeolite may be present in one or more forms and may have been ultra stabilized and/or treated with stabilizing cations such as any of the rare-earths.
  • Typical FCC processes are conducted at reaction temperatures of 480° C. to 600° C. with catalyst regeneration temperatures of 600° C. to 800° C.
  • the catalyst regeneration zone may consist of a single or multiple reactor vessels.
  • the compositions of the invention may be used in FCC processing of any typical hydrocarbon feedstock. Suitable feedstocks include petroleum distillates or residuals of crude oils, which when catalytically cracked, provide either a gasoline or a gas oil product. Synthetic feeds having boiling points of about 204° C. to about 816° C., such as oil from coal, tar sands or shale oil, can also be included.
  • oxygen or air is added to the regeneration zone. This is performed by a suitable sparging device in the bottom of the regeneration zone, or if desired, additional oxygen is added to the dilute or dense phase of the regeneration zone.
  • NO x reduction compositions in accordance with the invention dramatically reduce, i.e., by at least 10%, preferably at least 20%, the emissions of NO x in the FCCU regenerator effluent during the catalyst regeneration, while substantially maintaining the hydrocarbon feed conversion or the yield of cracked products, e.g., gasoline and light olefins, obtained from the cracking catalyst.
  • NO x reduction of 90% or greater is readily achievable using the compositions and method of the invention without significantly affecting the cracked products yields or feed conversion.
  • the extent of NO x reduction will depend on such factors as, for example, the composition and amount of the additive utilized; the design and the manner in which the catalytic cracking unit is operated, including but not limited to oxygen level and distribution of air in the regenerator, catalyst bed depth in the regenerator, stripper operation and regenerator temperature, the properties of the hydrocarbon feedstock cracked, and the presence of other catalytic additives that may affect the chemistry and operation of the regenerator.
  • the effectiveness of the process of the invention may be expected to vary from unit to unit.
  • NO x reduction compositions of the invention also prevent a significant increase in the production of coke during the FCC process.
  • NO x reduction compositions of the invention may be used alone or in combination with one or more additional NO x reduction component to achieve NO x reduction more efficiently than the use of either of the compositions alone.
  • the additional NO x reduction component is a non-zeolitic material, that is, a material that contains no or substantially no (i.e., less than 5 weight percent, preferably less than I weight percent) zeolite.
  • non-zeolitic materials suitable for use in combination with the NO x reduction compositions of the invention include noble metal containing NO x reduction compositions such as disclosed and described in U.S. Pat. No. 6,660,683 the entire disclosure of which is herein incorporated by reference.
  • compositions in this class will typically comprise a particulate mixture of (1) an acidic metal oxide containing substantially no zeolite (preferably containing silica and alumina, most preferably containing at least 1 weight percent alumina); (2) an alkali metal (at least 0.5 weight percent, preferably about 1 to about 15 weight percent), an alkaline earth metal (at least 0.5 weight percent, preferably about 0.5 to about 50 weight percent) and mixtures thereof; (3) at least 0.1 weight percent of an oxygen storage metal oxide component (preferably ceria); and (4) at least 0.1 ppm of a noble metal component (preferably Pt, Pd, Rh, Ir, Os, Ru, Re and mixtures thereof).
  • a noble metal component preferably Pt, Pd, Rh, Ir, Os, Ru, Re and mixtures thereof.
  • compositions in this class of materials comprise (1) an acidic oxide containing at least 50 weight percent alumina and substantially no zeolite; (2) at least 0.5 weight percent of an alkali metal and/or an alkaline earth metal or mixtures thereof; (3) about 1 to about 25 weight percent of an oxygen storage capable transition metal oxide or a rare-earth (preferably, ceria); and (4) at least 0.1 ppm of a noble metal selected from the group consisting of Pt, Rh, Ir, and a combination thereof, all percentages being based on the total weight of the oxidative catalyst/additive composition.
  • non-zeolitic materials suitable for use in combination with the NO x reduction compositions of the invention include a low NO x , CO combustion promoter as disclosed and described in U.S. Pat. Nos. 6,165,933 and 6,358,881, the entire disclosure of these patents being herein incorporated by reference.
  • the low NO x CO combustion promoter compositions comprise (1) an acidic oxide support; (2) an alkali metal and/or alkaline earth metal or mixtures thereof; (3) a transition metal oxide having oxygen storage capability; and (4) palladium.
  • the acidic oxide support preferably contains silica alumina. Ceria is the preferred oxygen storage oxide.
  • the NO x reduction composition comprises (1) an acidic metal oxide support containing at least 50 weight percent alumina; (2) about 1-10 parts by weight, measured as metal oxide, of at least one alkali metal, alkaline earth metal or mixtures thereof; (3) at least 1 part by weight of CeO 2 ; and (4) about 0.01-5.0 parts by weight of Pd, all of said parts by weight of components (2)-(4) being per 100 parts by weight of said acidic metal oxide support material.
  • non-zeolitic materials suitable for use in combination with the NO x reduction compositions of the invention include NO x reduction compositions as disclosed and described in U.S. Pat. Nos. 6,280,607 B1, 6,143,167, 6,379,536 and 6,129,834, the entire disclosure of these patents being herein incorporated by reference.
  • the NO x reduction compositions comprise (1) an acidic oxide support; (2) an alkali metal and/or alkaline earth metal or mixtures thereof; (3) a transition metal oxide having oxygen storage capability; and (4) a transition metal selected from Groups IB and IIB of the Periodic Table.
  • the acidic oxide support contains at least 50 weight percent alumina and preferably contains silica alumina.
  • the NO x reduction compositions comprise (1) an acidic oxide support containing at least 50 weight percent alumina; (2) 1-10 weight percent, measured as the metal oxide, of an alkali metal, an alkaline earth metal or mixtures thereof; (3) at least 1 weight percent CeO 2 ; and (4) 0.01-5.0 parts weight percent of a transition metal, measured as metal oxide, of Cu or Ag, all parts by weight of components (2)-(4) being per 100 parts by weight of said acidic oxide support.
  • non-zeolitic NO x reduction materials suitable for use in combination with the NO x reduction compositions of the invention include magnesium-aluminum spinel based additives heretofore being useful for the removal of sulfur oxides from a FCC regenerator.
  • Exemplary patents which disclose and describe this type of materials include U.S. Pat. Nos.
  • compositions in this class comprise at least one metal-containing spinel which includes a first metal and a second metal having a valence higher than the valence of said first metal, at least one component of a third metal other than said first and second metals and at least one component of a fourth metal other than said first, second and third metals, wherein said third metal is selected from the group consisting of Group IB metals, Group IIB metals, Group VIA metals, the rare-earth metals, the Platinum Group metals and mixtures thereof, and said fourth metal is selected from the group consisting of iron, nickel, titanium, chromium, manganese, cobalt, germanium, tin, bismuth, molybdenum, antimony, vanadium and mixtures thereof.
  • the metal containing spinel comprises magnesium as said first metal and aluminum as said second metal, and the atomic ratio of magnesium to aluminum in said spinel is at least about 0.17.
  • the third metal in the spinel preferably comprises a metal selected from the group consisting of the Platinum Group metals, the rare-earth metals and mixtures thereof.
  • the third metal component is preferably present in an amount in the range of about 0.001 to about 20 weight percent, calculated as elemental third metal, and said fourth metal component is present in an amount in the range of about 0.001 to about 10 weight percent, calculated as elemental fourth metal.
  • non-zeolitic materials useful in combination with the NO x reduction additives of the invention include, but are not limited to, zinc based catalysts such as disclosed and described in U.S. Pat. No. 5,002,654; antimony based NO x reduction additives such as described and disclosed in U.S. Pat. No. 4,988,432; perovskite-spinel NO x reduction additives such as described and disclosed in U.S. Pat. Nos. 5,364,517 and 5,565,181; hydrotalcite catalyst and additive compositions such as described and disclosed, for example, in U.S. Pat. Nos.
  • Such NO x removal composition generally comprises (i) an acidic oxide support, (ii) cerium oxide, (iii) a lanthanide oxide other than ceria and (iv) optionally, at least one oxide of a transition metal selected from Groups IB and IIB of the Periodic Table, noble metals, and mixtures thereof.
  • the additional non-zeolitic NO x reduction compositions are used in an amount sufficient to provide increased NO x reduction when compared to the use of the ferrierite NO x reduction compositions alone.
  • the additional non-zeolitic compositions are used in an amount up to about 50 weight percent of the FCC catalyst inventory.
  • the non-zeolitic composition is used in an amount up to about 30 weight percent, most preferably up to about 10 weight percent of the FCC catalyst inventory.
  • the additional NO x reduction composition may be blended with the FCC catalyst inventory as a separate particle additive.
  • the additional NO x reduction composition may be incorporated into the FCC catalyst as an integral component of the catalyst.
  • NO x reduction compositions in accordance with the present invention may be used in combination with other additives conventionally used in the FCC process, e.g., SO x reduction additives, gasoline-sulfur reduction additives, CO combustion promoters, additives for the production of light olefins, and the like.
  • SO x reduction additives e.g., SO x reduction additives, gasoline-sulfur reduction additives, CO combustion promoters, additives for the production of light olefins, and the like.
  • any range of numbers recited in the specification or claims, such as that representing a particular set of properties, units of measure, conditions, physical states or percentages, is intended to literally incorporate expressly herein by reference or otherwise, any number falling within such range, including any subset of numbers within any range so recited.
  • a composition comprising 75% ferrierite and 25% alumina sol (Additive B) was prepared as follows.
  • the slurry was milled in a Drais mill to an average particle size of less than 2.5 ⁇ m and then spray-dried in a Bowen spray dryer.
  • the spray-dried product was calcined for 90 minutes at 1100° F.
  • Table 1 The properties of the catalyst are shown in Table 1 below.
  • Additives A and B were evaluated for their ability to reduce NO x emissions from a FCCU using the Davison Circulating Riser (DCR).
  • the description of the DCR has been published in the following papers: G. W. Young, G. D. Weatherbee, and S. W. Davey, “Simulating Commercial FCCU Yields With The Davison Circulating Riser (DCR) Pilot Plant Unit,” National Petroleum Refiners_Association (NPRA) Paper AM88-52; G. W. Young, “Realistic Assessment of FCC Catalyst Performance in the Laboratory,” in Fluid Catalytic Cracking: Science and Technology, J. S. Magee and M. M. Mitchell, Jr. Eds. Studies in Surface Science and Catalysis Volume 76, p. 257, Elsevier Science Publishers B.V., Amsterdam 1993, ISBN 0-444-89037-8.
  • the DCR was operated with 1% excess O 2 in the regenerator, and with the regenerator operating at 705° C. After the unit stabilized the baseline NO x emissions data were collected using an on-line Lear-Siegler SO 2 /NO x Analyzer (SM8100A). Subsequently, 100 g of catalyst were injected into the DCR consisting of 4.75 g of a commercial sample of a Pt-based combustion promoter, CP-3® (obtained from Grace Davison), which had been deactivated for 20 hours at 788° C. without any added Ni or V using the Cyclic Propylene Steaming method (CPS) and 95.25 grams of hydrothermally deactivated SUPERNOVA®-DMR+. The description of the CPS method has been published in L.
  • CP-3® obtained from Grace Davison
  • Table 4 shows the conversion and product yields with and without the composition of this invention.
  • the means of conversion and cracked product yields were calculated using a sample of 7 baseline DCR tests.
  • both Additives A and B are especially effective in decreasing NO x emissions without significantly affecting the cracked products yields.
  • both overall conversion and gasoline yield do not change substantially, even though the FCC feedstock used in these experiments is a high nitrogen feed.
  • a particulate NO x reduction composition (Additive D) was prepared as follows: A slurry was prepared from an aqueous slurry having 20% solids of a peptizable alumina (Versal 700 alumina powder obtained from La Roche Industries Inc., 99% Al 2 O 3 , 30% moisture). The alumina slurry was prepared using 31.6 lbs of the alumina. To the alumina slurry 3.87 lbs of an aqueous sodium hydroxide solution (50% NaOH) was added. Next, 10.4 lbs of cerium carbonate crystals (obtained from Rhone Poulenc, Inc., 96% CeO 2 , 4% La2O 3 , 50% moisture) was added to the slurry.
  • the slurry was diluted with a sufficient amount of water to bring the solids concentration of the slurry to 12%. Finally, 3.38 lbs of ion exchanged silica sol of Nalco 1140 (obtained from Nalco Chemicals Co.) was added to the slurry. The mixture was agitated to assure good mixing and then milled in a stirred media mill to reduce agglomerates to substantially less than 10 ⁇ m. The milled mixture was then spray-dried to form approximately 70 ⁇ m microspheres and thereafter calcined at approximately 650° C. to remove volatiles.
  • the resulting material was impregnated with an aqueous solution of a Cu containing salt (e.g., CuSO 4 ) to achieve about 2% Cu on the final product, and was flash dried.
  • a Cu containing salt e.g., CuSO 4
  • the final product had the following analysis (dry basis): 7.8% SiO 2 , 7.1% Na 2 O, 18.5% CeO 2 , 60.2% Al 2 O 3 , 1.9% Cu and BET surface area of 111 m 2 /g.
  • Additive C and a blend of Additives C and D consisting of 75% Additive C and 25% Additive D where tested in the DCR with a feedstock having the properties shown in Table 6.
  • the unit was loaded with 1995 g of an equilibrium cracking catalyst (ECAT) having the properties as shown in Table 7 below, and 5 g of the commercially available CO combustion promoter CP-3®, which had been deactivated for 20 hours at 788° C. without any added Ni or V using the CPS method. After the unit was stabilized, the baseline NO x emissions data were collected. Subsequently, 42 g of Additive C or the blend of Additive C and D were injected into the unit along with 0.25 g of the combustion promoter, and 157.75 g of the equilibrium catalyst.
  • ECAT equilibrium cracking catalyst

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Organic Chemistry (AREA)
  • Materials Engineering (AREA)
  • Oil, Petroleum & Natural Gas (AREA)
  • General Chemical & Material Sciences (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Environmental & Geological Engineering (AREA)
  • Health & Medical Sciences (AREA)
  • Biomedical Technology (AREA)
  • Analytical Chemistry (AREA)
  • Catalysts (AREA)
  • Production Of Liquid Hydrocarbon Mixture For Refining Petroleum (AREA)
US10/909,706 2003-11-06 2004-08-02 Ferrierite compositions for reducing NOx emissions during fluid catalytic cracking Abandoned US20050100494A1 (en)

Priority Applications (19)

Application Number Priority Date Filing Date Title
US10/909,706 US20050100494A1 (en) 2003-11-06 2004-08-02 Ferrierite compositions for reducing NOx emissions during fluid catalytic cracking
EP04810274A EP1680484B1 (en) 2003-11-06 2004-11-04 FERRIERITE COMPOSITIONS FOR REDUCING NOx EMISSIONS DURING FLUID CATALYTIC CRACKING
CN200910126434.5A CN101503632B (zh) 2003-11-06 2004-11-04 流化裂化催化剂及降低流化裂化期间NOx排放量的方法
AT04810274T ATE550408T1 (de) 2003-11-06 2004-11-04 Ferrieritzusammensetzungen zur reduktion von nox- emissionen beim katalytischen cracken in der wirbelschicht
SG200900862-4A SG150502A1 (en) 2003-11-06 2004-11-04 Ferrierite compositions for reducing nox emissions during fluid catalytic cracking
PCT/US2004/036642 WO2005047429A1 (en) 2003-11-06 2004-11-04 FERRIERITE COMPOSITIONS FOR REDUCING NOx EMISSIONS DURING FLUID CATALYTIC CRACKING
CN2004800327499A CN1878855B (zh) 2003-11-06 2004-11-04 用于降低流化催化裂化期间NOx排放量的镁钠针沸石组合物
RU2006119619/04A RU2365615C2 (ru) 2003-11-06 2004-11-04 Ферриеритные композиции для снижения выбросов noх в процессе крекинга с флюидизированным катализатором
JP2006538463A JP4977469B2 (ja) 2003-11-06 2004-11-04 流動式接触分解中のＮＯｘ排気を減少させるフェリエライト組成物
AU2004288928A AU2004288928B2 (en) 2003-11-06 2004-11-04 Ferrierite compositions for reducing NOx emissions during fluid catalytic cracking
CA2544918A CA2544918C (en) 2003-11-06 2004-11-04 Ferrierite compositions for reducing nox emissions during fluid catalytic cracking
BRPI0416147-5A BRPI0416147B1 (pt) 2003-11-06 2004-11-04 COMPOSIÇÕES DE FERRIERITA PARA A REDUÇÃO DE EMISSÕES DE NOx DURANTE O CRAQUEAMENTO CATALÍTICO DE FLUIDO
KR1020067008710A KR101133833B1 (ko) 2003-11-06 2004-11-04 유체 촉매적 분해 동안 질소 산화물의 방출을 감소시키는페리어라이트 조성물
ARP050103203 AR051556A1 (es) 2004-08-02 2005-08-01 Composiciones de ferrierita para reducir las emisiones de nox durante el craqueo catalitico fluido
TW94125998A TWI395614B (zh) 2004-08-02 2005-08-01 用於減低流體觸媒裂解期間之ＮＯｘ排放之鎂鹼沸石
IL174876A IL174876A (en) 2003-11-06 2006-04-09 FERRIERITE COMPOSITIONS FOR REDUCING NOx EMISSIONS DURING FLUID CATALYTIC CRACKING
NO20062598A NO20062598L (no) 2003-11-06 2006-06-06 Ferriertittsammensetninger for a redusere NOx-utslipp under fluidkatalytisk krakking
US12/833,336 US9931595B2 (en) 2003-11-06 2010-07-09 Ferrierite composition for reducing NOx emissions during fluid catalytic cracking
IL213527A IL213527A0 (en) 2003-11-06 2011-06-13 FERRIERITE COMPOSITIONS FOR REDUCING NOx EMISSIONS DURING FLUID CATALYTIC CRACKING

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US10/702,240 US20050100493A1 (en) 2003-11-06 2003-11-06 Ferrierite compositions for reducing NOx emissions during fluid catalytic cracking
US10/909,706 US20050100494A1 (en) 2003-11-06 2004-08-02 Ferrierite compositions for reducing NOx emissions during fluid catalytic cracking

Related Parent Applications (2)

Application Number Title Priority Date Filing Date
US10/702,240 Continuation-In-Part US20050100493A1 (en) 2003-11-06 2003-11-06 Ferrierite compositions for reducing NOx emissions during fluid catalytic cracking
US10/909,709 Continuation US20050232839A1 (en) 2004-04-15 2004-08-02 Compositions and processes for reducing NOx emissions during fluid catalytic cracking

Related Child Applications (2)

Application Number Title Priority Date Filing Date
US11/918,086 Continuation US7918991B2 (en) 2005-04-27 2006-03-24 Compositions and processes for reducing NOx emissions during fluid catalytic cracking
US12/833,336 Division US9931595B2 (en) 2003-11-06 2010-07-09 Ferrierite composition for reducing NOx emissions during fluid catalytic cracking

Publications (1)

Publication Number Publication Date
US20050100494A1 true US20050100494A1 (en) 2005-05-12

Family

ID=34595355

Family Applications (2)

Application Number Title Priority Date Filing Date
US10/909,706 Abandoned US20050100494A1 (en) 2003-11-06 2004-08-02 Ferrierite compositions for reducing NOx emissions during fluid catalytic cracking
US12/833,336 Expired - Lifetime US9931595B2 (en) 2003-11-06 2010-07-09 Ferrierite composition for reducing NOx emissions during fluid catalytic cracking

Family Applications After (1)

Application Number Title Priority Date Filing Date
US12/833,336 Expired - Lifetime US9931595B2 (en) 2003-11-06 2010-07-09 Ferrierite composition for reducing NOx emissions during fluid catalytic cracking

Country Status (14)

Country Link
US (2) US20050100494A1 (zh)
EP (1) EP1680484B1 (zh)
JP (1) JP4977469B2 (zh)
KR (1) KR101133833B1 (zh)
CN (1) CN1878855B (zh)
AT (1) ATE550408T1 (zh)
AU (1) AU2004288928B2 (zh)
BR (1) BRPI0416147B1 (zh)
CA (1) CA2544918C (zh)
IL (1) IL174876A (zh)
NO (1) NO20062598L (zh)
RU (1) RU2365615C2 (zh)
SG (1) SG150502A1 (zh)
WO (1) WO2005047429A1 (zh)

Cited By (16)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
FR2887467A1 (fr) * 2005-06-22 2006-12-29 Air Liquide Procede de traitement des fumees issues du regenerateur catalytique d'une unite de craquage catalytique
US20080213150A1 (en) * 2005-03-24 2008-09-04 George Yaluris Method for Controlling Nox Emissions in the Fccu
US20090057199A1 (en) * 2005-04-27 2009-03-05 Michael Scott Ziebarth Compositions and Processes for Reducing NOx Emissions During Fluid Catalytic Cracking
US20090107885A1 (en) * 2007-10-29 2009-04-30 Petroleo Brasileiro S.A.- Petrobras Catalytic system and additive for maximisation of light olefins in fluid catalytic cracking units in operations of low severity
US7976697B2 (en) 2005-04-29 2011-07-12 W. R. Grace & Co.-Conn. NOX reduction compositions for use in partial burn FCC processes
US20130005565A1 (en) * 2010-03-18 2013-01-03 W. R. Grace & Co.-Conn. Process for making improved zeolite catalysts from peptized aluminas
EP2729553A4 (en) * 2011-07-06 2015-04-29 Reliance Ind Ltd METHOD AND COMPOSITION FOR CATALYST / ADDITIVE TO REDUCE GAS LEAKAGE IN FLUID CATALYTIC CRACKING (FCC) PROCESS
US9416322B2 (en) 2010-03-18 2016-08-16 W. R. Grace & Co.-Conn. Process for making improved catalysts from clay-derived zeolites
WO2017216617A1 (en) * 2016-06-15 2017-12-21 Hindustan Petroleum Corporation Limited A fluid catalytic cracking process for obtaining cracked run naphtha from vacuum gas oil
WO2018071905A1 (en) * 2016-10-14 2018-04-19 Gevo, Inc. Conversion of mixtures of c2-c8 olefins to jet fuel and/or diesel fuel in high yield from bio-based alcohols
WO2018225036A1 (en) * 2017-06-09 2018-12-13 Basf Corporation Catalytic washcoat with controlled porosity for nox abatement
EP3504297A4 (en) * 2016-08-23 2020-06-17 Quanta Technologies, LLC IMPROVING THE EFFICIENCY OF FCCU REFINERY ADDITIVES
WO2020156801A1 (en) * 2019-02-01 2020-08-06 Casale Sa Process for removing nitrogen oxides from a gas
US11298656B2 (en) 2016-06-08 2022-04-12 Basf Corporation Copper-promoted GMElinite and use thereof in the selective catalytic reduction of NOX
CN115025777A (zh) * 2014-08-29 2022-09-09 中国石油化工股份有限公司 用于降低FCC再生烟气CO和NOx排放的组合物及其制备方法
RU2809651C2 (ru) * 2019-02-01 2023-12-14 Касале Са Способ удаления оксидов азота из газа

Families Citing this family (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20050232839A1 (en) * 2004-04-15 2005-10-20 George Yaluris Compositions and processes for reducing NOx emissions during fluid catalytic cracking
KR100958362B1 (ko) * 2005-03-11 2010-05-17 유오피 엘엘씨 나프타 접촉 분해 촉매 및 방법
US7678735B2 (en) 2005-11-28 2010-03-16 Engelhard Corporation FCC additive for partial and full burn NOx control
CN101314725B (zh) * 2007-05-31 2012-01-25 中国石油化工股份有限公司 一种降低FCC再生烟气中NOx排放的组合物
CN102371165B (zh) * 2010-08-26 2013-06-05 中国石油化工股份有限公司 用于降低FCC再生烟气CO和NOx排放的低堆比组合物
JP5660674B2 (ja) * 2011-02-18 2015-01-28 コスモ石油株式会社 炭化水素油の接触分解触媒及びその製造方法
JP5972694B2 (ja) * 2012-07-18 2016-08-17 ユニゼオ株式会社 Ｆｅ（ＩＩ）置換ＭＥＬ型ゼオライト、それを含むガス吸着剤及びその製造方法、並びに一酸化窒素及びハイドロカーボンの除去方法
EP2877281B1 (en) * 2012-07-24 2021-08-18 Indian Oil Corporation Ltd Catalyst composition for fluid catalytic cracking, process for preparing the same and use thereof
KR101598578B1 (ko) * 2013-08-05 2016-02-29 (주)후산 접촉분해경유에 포함된 질소 성분 제거 방법
WO2022072544A1 (en) * 2020-10-01 2022-04-07 W.R. Grace & Co.-Conn. Catalyst composition for fluid catalytic cracking, and preparation methods thereof

Citations (98)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US2892801A (en) * 1955-12-13 1959-06-30 Gen Electric Catalysts
US3036973A (en) * 1958-11-21 1962-05-29 Hoffmann La Roche Racemization catalyst and process for the manufacture thereof
US3129252A (en) * 1960-12-29 1964-04-14 Gen Aniline & Fihn Corp Purification of butynediol
US3184417A (en) * 1960-12-29 1965-05-18 Gen Aniline & Film Corp Method of preparing a copper modified nickel catalyst composition
US3634140A (en) * 1968-09-20 1972-01-11 Asea Ab Fuel cell device utilizing air as oxidant
US4199435A (en) * 1978-12-04 1980-04-22 Chevron Research Company NOx Control in cracking catalyst regeneration
US4309279A (en) * 1979-06-21 1982-01-05 Mobil Oil Corporation Octane and total yield improvement in catalytic cracking
US4368057A (en) * 1980-10-14 1983-01-11 Matthews Ronald D Method for reducing ammonia concentration in pre-combusted fuel gas using nitric oxide
US4377502A (en) * 1979-12-26 1983-03-22 Standard Oil Company (Indiana) Synthesis of crystalline aluminosilicate molecular sieves
US4427536A (en) * 1982-02-02 1984-01-24 Chevron Research Company Promoter for the oxidation of SO2 in an FCC process
US4428827A (en) * 1983-01-24 1984-01-31 Uop Inc. FCC Sulfur oxide acceptor
US4434147A (en) * 1981-10-05 1984-02-28 Chevron Research Company Simultaneous sulfur oxide and nitrogen oxide control in FCC units using cracking catalyst fines with ammonia injection
US4495304A (en) * 1980-07-29 1985-01-22 Atlantic Richfield Company Catalyst for conversion of hydrocarbons
US4495305A (en) * 1980-07-29 1985-01-22 Atlantic Richfield Company Catalyst for conversion of hydrocarbons
US4513091A (en) * 1983-02-14 1985-04-23 Mobil Oil Corporation Hydrothermal zeolite activation
US4521298A (en) * 1980-07-18 1985-06-04 Mobil Oil Corporation Promotion of cracking catalyst octane yield performance
US4522937A (en) * 1982-11-29 1985-06-11 Atlantic Richfield Company Preparative process for alkaline earth metal, aluminum-containing spinels
US4582815A (en) * 1984-07-06 1986-04-15 Mobil Oil Corporation Extrusion of silica-rich solids
US4642178A (en) * 1980-07-29 1987-02-10 Katalistiks, Inc. Process for conversion of hydrocarbons
US4654318A (en) * 1984-02-28 1987-03-31 Toa Nenryo Kogyo Kabushiki Kaisha Process for preparing catalyst component for polymerization of olefins
US4728635A (en) * 1986-04-07 1988-03-01 Katalistiks International Inc. Alkaline earth metal spinels and processes for making
US4735927A (en) * 1985-10-22 1988-04-05 Norton Company Catalyst for the reduction of oxides of nitrogen
US4744962A (en) * 1987-07-22 1988-05-17 Shell Oil Company Process for the reduction of ammonia in regeneration zone off gas by select addition of NOx to the regeneration zone or to the regeneration zone off gas
US4747935A (en) * 1986-03-26 1988-05-31 Union Oil Company Of California Process for the catalytic cracking of feedstocks containing nitrogen
US4797266A (en) * 1986-08-07 1989-01-10 Shell Oil Company Method of preparation of a combined ZSM-5-ferrierite aluminosilicate
US4798813A (en) * 1986-07-04 1989-01-17 Babcock-Hitachi Kabushiki Kaisha Catalyst for removing nitrogen oxide and process for producing the catalyst
US4810369A (en) * 1987-05-07 1989-03-07 Union Oil Company Of California Process for the catalytic cracking of feedstocks containing high levels of nitrogen
US4812431A (en) * 1987-08-12 1989-03-14 Mobil Oil Corporation NOx control in fluidized bed combustion
US4812430A (en) * 1987-08-12 1989-03-14 Mobil Oil Corporation NOx control during multistage combustion
US4818509A (en) * 1984-03-23 1989-04-04 Mobil Oil Corporation Continuous process for manufacturing crystalline zeolites in continuously stirred backmixed crystallizers
US4826799A (en) * 1988-04-14 1989-05-02 W. R. Grace & Co.-Conn. Shaped catalyst and process for making it
US4830840A (en) * 1987-03-13 1989-05-16 Uop Process for removing sulfur oxide and nitrogen oxide
US4839026A (en) * 1978-09-11 1989-06-13 Atlantic Richfield Company Catalytic cracking with reduced emissions of sulfur oxides
US4895994A (en) * 1988-04-14 1990-01-23 W. R. Grace & Co.-Conn. Shaped catalysts and processes
US4898846A (en) * 1986-03-21 1990-02-06 W. R. Grace & Co.-Conn. Cracking catalysts with octane enhancement
US4904627A (en) * 1987-03-13 1990-02-27 Uop Alkaline earth metal spinel/kaolin clays and processes for making
US4923842A (en) * 1988-10-11 1990-05-08 Allied-Signal Inc. Lanthanum containing catalyst for treating automotive exhaust
US4986897A (en) * 1989-12-28 1991-01-22 Mobil Oil Corporation Catalytic conversion of NOx with NH3
US4988654A (en) * 1989-12-29 1991-01-29 Chevron Research Company Dual component cracking catalyst with vanadium passivation and improved sulfur tolerance
US4988432A (en) * 1989-12-28 1991-01-29 Mobil Oil Corporation Reducing NOx emissions with antimony additive
US5002653A (en) * 1989-12-29 1991-03-26 Chevron Research Company Catalytic cracking process with vanadium passivation and improved
US5002654A (en) * 1989-12-28 1991-03-26 Mobil Oil Corporation Reducing NOx emissions with zinc catalyst
US5015362A (en) * 1989-12-28 1991-05-14 Mobil Oil Corporation Catalytic conversion of NOx over carbonaceous particles
US5017538A (en) * 1988-04-18 1991-05-21 Toyota Jidosha Kabushiki Kaisha Catalyst for purifying exhaust gas and a method of producing the same
US5021144A (en) * 1989-02-28 1991-06-04 Shell Oil Company Process for the reduction of NOX in an FCC regeneration system by select control of CO oxidation promoter in the regeneration zone
US5102530A (en) * 1986-03-21 1992-04-07 W. R. Grace & Co.-Conn. Cracking catalysts with octane enhancement
US5114691A (en) * 1990-01-18 1992-05-19 Board Of Trustees Operating Michigan State University Process using sorbents for the removal of SOx from flue gas
US5114898A (en) * 1990-01-18 1992-05-19 Board Of Trustees Operating Michigan State University Layered double hydroxide sorbents for the removal of SOx from flue gas and other gas streams
US5190736A (en) * 1991-10-18 1993-03-02 Mobil Oil Corporation Synthesis of crystalline ZSM-35
US5206196A (en) * 1990-12-18 1993-04-27 Tosoh Corporation Catalyst for purifying exhaust gas
US5208198A (en) * 1990-12-18 1993-05-04 Tosoh Corporation Catalyst for purifying exhaust gas
US5286693A (en) * 1991-11-06 1994-02-15 Nippon Oil Co., Ltd. Method of producing catalyst for converting hydrocarbons
US5294332A (en) * 1992-11-23 1994-03-15 Amoco Corporation FCC catalyst and process
US5317055A (en) * 1989-06-02 1994-05-31 Exxon Chemical Patents Inc. Internal resin-tackified acrylic polymers
US5320822A (en) * 1991-11-20 1994-06-14 The Dow Chemical Company Process of growing crystalline microporous solids in a fluoride-containing, substantially non-aqueous growth medium
US5379536A (en) * 1993-11-15 1995-01-10 Lorenzana; Moises B. Ironing board attachment including basket
US5382352A (en) * 1992-10-20 1995-01-17 Mobil Oil Corporation Conversion of NOx in FCC bubbling bed regenerator
US5413977A (en) * 1992-02-27 1995-05-09 Union Oil Company Of California Catalyst containing zeolite beta and a layered magnesium silicate
US5413699A (en) * 1993-10-14 1995-05-09 Mobil Oil Corporation FCC process with fines tolerant SCR reactor
US5422333A (en) * 1992-08-25 1995-06-06 Idemitsu Kosan Company Limited Exhaust gas purifying catalyst
US5503818A (en) * 1993-11-01 1996-04-02 Csir Aluminosilicate catalyst, a process for the manufacture thereof and a process for the skeletal isomerization of linear olefins
US5510306A (en) * 1993-12-29 1996-04-23 Shell Oil Company Process for isomerizing linear olefins to isoolefins
US5591418A (en) * 1994-06-01 1997-01-07 Amoco Corporation Process for removing sulfur oxides or nitrogen oxides from a gaseous mixture
US5599520A (en) * 1994-11-03 1997-02-04 Garces; Juan M. Synthesis of crystalline porous solids in ammonia
US5614453A (en) * 1991-09-11 1997-03-25 Uop Catalyst containing zeolite beta and a pillared clay
US5627125A (en) * 1994-07-01 1997-05-06 Monsanto Company Process for preparing carboxylic acid salts and methods for making such catalysts and catalysts useful in such process
US5705053A (en) * 1995-08-30 1998-01-06 Mobil Oil Corporation FCC regenerator NOx reduction by homogeneous and catalytic conversion
US5716514A (en) * 1995-08-30 1998-02-10 Mobil Oil Corporation FCC NOx reduction by turbulent/laminar thermal conversion
US5741468A (en) * 1994-12-28 1998-04-21 Kabushiki Kaisha Riken Exhaust gas cleaner and method for cleaning exhaust gas
US5744686A (en) * 1995-09-20 1998-04-28 Uop Process for the removal of nitrogen compounds from an aromatic hydrocarbon stream
US5744113A (en) * 1993-05-27 1998-04-28 Siemens Aktiengesellschaft Process and catalyst for decomposing oxides of nitrogen
US5879645A (en) * 1994-11-03 1999-03-09 Korea Research Institute Of Chemical Technology Method for removing nitrogen oxides in exhaust gas by selective catalytic reduction and catalyst for reduction of nitrogen oxides
US6017508A (en) * 1995-10-24 2000-01-25 The Dow Chemical Company Process of modifying the porosity of aluminosilicates and silicas, and mesoporous compositions derived therefrom
US6027696A (en) * 1997-04-11 2000-02-22 Indian Oil Corporation Ltd. Fluidized catalytic cracking apparatus
US6033641A (en) * 1996-04-18 2000-03-07 University Of Pittsburgh Of The Comonwealth System Of Higher Education Catalyst for purifying the exhaust gas from the combustion in an engine or gas turbines and method of making and using the same
US6040259A (en) * 1996-05-29 2000-03-21 Exxon Chemical Patents Inc. Metal-containing zeolite catalyst, preparation thereof and use for hydrocarbon conversion
US6190538B1 (en) * 1998-08-03 2001-02-20 Shell Oil Company Process for the preparation of a catalyst composition
US6214211B1 (en) * 1998-04-21 2001-04-10 Idemitsu Kosan Co., Ltd Catalytic cracking catalyst
US20010002426A1 (en) * 1994-11-23 2001-05-31 Mohr Gary David Hydrocarbon conversion process using a zeolite bound zeolite catalyst
US20020013228A1 (en) * 2000-06-20 2002-01-31 Takeshi Matsumoto Exhaust gas purifying catalyst and method for purifying exhaust gas
US20020016259A1 (en) * 2000-06-28 2002-02-07 Tatsuya Yoshikawa Exhaust gas purifying catalyst
US20020022574A1 (en) * 2000-07-17 2002-02-21 Hiroshi Tanada Exhaust gas purifying catalyst
US20020022573A1 (en) * 2000-06-22 2002-02-21 Hiroshi Tanada Exhaust gas purifying catalyst
US6358881B1 (en) * 1995-05-05 2002-03-19 W. R. Grace & Co.-Conn. Reduced NOx combustion promoter for use in FCC processes
US20020038051A1 (en) * 2000-02-18 2002-03-28 Degussa-Huls Ag Raney copper
US20020037808A1 (en) * 1999-07-31 2002-03-28 Degussa-Huels Aktiengesellschaft Fixed bed catalysts
US20020039550A1 (en) * 2000-04-22 2002-04-04 Adolf Schafer-Sindlinger Process and catalyst for reducing nitrogen oxides
US6376708B1 (en) * 2000-04-11 2002-04-23 Monsanto Technology Llc Process and catalyst for dehydrogenating primary alcohols to make carboxylic acid salts
US20020049132A1 (en) * 1998-11-03 2002-04-25 Deng-Yang Jan Process for preparing attrition resistant zeolitic layered catalyst composition
US6380119B1 (en) * 1997-06-06 2002-04-30 Basf Aktiengesellschaft Method for regenerating a zeolitic catalyst
US6395403B2 (en) * 1999-05-06 2002-05-28 W. R. Grace & Co. Conn Promoted porous catalyst
US20030019794A1 (en) * 2001-04-13 2003-01-30 Schmidt Stephen Raymond Process for sulfur removal from hydrocarbon liquids
US6514470B1 (en) * 1999-10-28 2003-02-04 The Regents Of The University Of California Catalysts for lean burn engine exhaust abatement
US20030040425A1 (en) * 2001-08-21 2003-02-27 Sud-Chemie Prototech Inc. Method for washcoating a catalytic material onto a monolithic structure
US6528031B1 (en) * 1998-12-31 2003-03-04 Korea Research Institute Of Chemical Technology Method for preparing noble metal-supported zeolite catalyst for catalytic reduction of nitrogen oxide
US6538169B1 (en) * 2000-11-13 2003-03-25 Uop Llc FCC process with improved yield of light olefins
US20030073566A1 (en) * 2001-10-11 2003-04-17 Marshall Christopher L. Novel catalyst for selective NOx reduction using hydrocarbons
US20040086442A1 (en) * 2002-08-13 2004-05-06 Intercat, Inc. Flue gas treatments to reduce NOx and CO emissions

Family Cites Families (110)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3617488A (en) 1969-12-19 1971-11-02 Sigmund M Csicsery Hydrotreating catalyst comprising clay-type aluminosilicate component and a crystalline zeolitic molecular sieve component, and process using said catalyst
US4473658A (en) 1973-09-20 1984-09-25 Mobil Oil Corporation Moving bed catalytic cracking process with platinum group metal or rhenium supported directly on the cracking catalyst
US3894940A (en) 1973-11-15 1975-07-15 Grace W R & Co Hydrocarbon cracking catalysts with promoter mixtures
US4086187A (en) * 1976-06-17 1978-04-25 Filtrol Corporation Attrition resistant zeolitic catalyst
US4064511A (en) 1976-09-24 1977-12-20 Raytheon Company Clutter subtraction system
US4138326A (en) * 1977-08-12 1979-02-06 Gulf Research & Development Hydrotreating process and catalyst
US6042797A (en) 1997-07-02 2000-03-28 Tosoh Corporation Adsorbent for ethylene, method for adsorbing and removing ethylene and method for purifying an exhaust gas
US4170571A (en) 1977-12-27 1979-10-09 Union Carbide Corporation Novel combustion catalyst
US4290878A (en) 1978-12-08 1981-09-22 Chevron Research Company NOx control in platinum-promoted complete combustion cracking catalyst regeneration
JPS5761085A (en) 1980-07-29 1982-04-13 Atlantic Richfield Co Conversion of hydrocarbon
US4758418A (en) 1980-07-29 1988-07-19 Union Carbide Corporation Process for combusting solid sulfur-containing material
US4472267A (en) 1980-07-29 1984-09-18 Atlantic Richfield Company Catalyst and process for conversion of hydrocarbons
US4957892A (en) 1980-07-29 1990-09-18 Uop Process for combusting solid sulfur containing material
US4458023A (en) * 1981-08-10 1984-07-03 W. R. Grace & Co. Catalyst manufacture
US4471070A (en) 1982-11-29 1984-09-11 Atlantic Richfield Company Preparative process for alkaline earth metal, aluminum-containing spinels
US4476245A (en) 1982-11-29 1984-10-09 Atlantic Richfield Company Preparative process for alkaline earth metal, aluminum-containing spinels
US4472532A (en) 1982-11-29 1984-09-18 Atlantic Richfield Company Preparative process for alkaline earth metal, aluminum-containing spinels
US4608355A (en) 1983-08-10 1986-08-26 Mobil Oil Corporation Hydrocarbon conversion catalyst
JPS6123689A (ja) * 1984-07-13 1986-02-01 Toa Nenryo Kogyo Kk 低流動点ｌｃｇｏ用接触分解触媒組成物及びそれを用いた低流動点ｌｃｇｏの製造方法
GB8420205D0 (en) 1984-08-09 1984-09-12 British Petroleum Co Plc Selective dealumination of zeolites
US4778664A (en) 1986-03-10 1988-10-18 The Dow Chemical Company Process for the removal of NO from fluid streams using a water soluble polymeric chelate of a polyvalent metal
US4708786A (en) 1986-03-26 1987-11-24 Union Oil Company Of California Process for the catalytic cracking of nitrogen-containing feedstocks
US4790982A (en) 1986-04-07 1988-12-13 Katalistiks International, Inc. Metal-containing spinel composition and process of using same
CA1295598C (en) 1986-07-29 1992-02-11 Makoto Imanari Process for removing nitrogen oxides from exhaust gases
US4778665A (en) 1986-09-09 1988-10-18 Mobil Oil Corporation Abatement of NOx in exhaust gases
FR2607128B1 (fr) 1986-11-21 1989-04-28 Inst Francais Du Petrole Nouvelles ferrierites, leur procede de preparation et leur utilisation
US4866019A (en) 1987-01-13 1989-09-12 Akzo N.V. Catalyst composition and absorbent which contain an anionic clay
US4880521A (en) 1987-05-07 1989-11-14 Union Oil Company Of California Process for the cracking of feedstocks containing high levels of nitrogen
US4755282A (en) 1987-07-22 1988-07-05 Shell Oil Company Process for the reduction of NH3 in regeneration zone off gas by select recycle of certain-sized NH3 decomposition catalysts
US4957718A (en) 1987-11-24 1990-09-18 Uop Process for reducing emissions of sulfur oxides and composition useful in same
US5057205A (en) 1988-06-10 1991-10-15 Mobil Oil Corporation Additive for vanadium and sulfur oxide capture in catalytic cracking
GB8904409D0 (en) 1989-02-27 1989-04-12 Shell Int Research Process for the conversion of a hydrocarbonaceous feedstock
US5371055A (en) 1988-07-07 1994-12-06 W. R. Grace & Co.-Conn. Increasing metal-tolerance of FCC catalyst by sulfur oxide removal
NL8802081A (nl) * 1988-08-23 1990-03-16 Nagron Precision Tooling Werkwijze voor het vervaardigen van een drager met optisch leesbare, digitale informatie.
GB8820358D0 (en) * 1988-08-26 1988-09-28 Shell Int Research Process for catalytic cracking of hydrocarbon feedstock
US4980052A (en) 1988-12-05 1990-12-25 Mobil Oil Corporation Catalytic cracking of hydrocarbons
US4889615A (en) 1988-12-06 1989-12-26 Mobil Oil Corporation Additive for vanadium capture in catalytic cracking
US5145815A (en) 1989-08-10 1992-09-08 Uop Regeneration of zeolitic molecular sieves with sulfur oxide absorption on soda-lime bed
CA2024154C (en) 1989-08-31 1995-02-14 Senshi Kasahara Catalyst for reducing nitrogen oxides from exhaust gas
US4973399A (en) 1989-11-03 1990-11-27 Mobil Oil Corporation Catalytic cracking of hydrocarbons
JPH07106300B2 (ja) 1989-12-08 1995-11-15 財団法人産業創造研究所 燃焼排ガス中の窒素酸化物除去法
CA2032799C (en) 1989-12-21 1996-01-30 Akinori Eshita Catalyst for and method of purifying oxygen-excess exhaust gas
US5260240A (en) 1989-12-29 1993-11-09 Chevron Research And Technology Company Process for the demetallization of FCC catalyst
US5037538A (en) 1990-02-26 1991-08-06 Mobil Oil Corporation Catalytic cracking process with isolated catalyst for conversion of NO.sub.x
CA2044893C (en) 1990-06-20 1998-11-03 Senshi Kasahara Transition metal-containing zeolite having high hydrothermal stability, production method thereof and method of using same
JP2973524B2 (ja) 1990-12-18 1999-11-08 東ソー株式会社 排ガス浄化触媒
US5130012A (en) 1991-01-24 1992-07-14 Mobil Oil Corporation Process and apparatus for reducing NOx emissions from high-efficiency FFC regenerators
US5173278A (en) 1991-03-15 1992-12-22 Mobil Oil Corporation Denitrification of flue gas from catalytic cracking
US5260043A (en) 1991-08-01 1993-11-09 Air Products And Chemicals, Inc. Catalytic reduction of NOx and carbon monoxide using methane in the presence of oxygen
JP3086015B2 (ja) 1991-08-07 2000-09-11 トヨタ自動車株式会社 排気ガス浄化用触媒
US5174980A (en) 1991-10-04 1992-12-29 Mobil Oil Corp. Synthesis of crystalline ZSM-35
US5171553A (en) 1991-11-08 1992-12-15 Air Products And Chemicals, Inc. Catalytic decomposition of N2 O
US5785947A (en) 1991-12-18 1998-07-28 Chevron U.S.A. Inc. Preparation of zeolites using organic template and amine
US5547648A (en) 1992-04-15 1996-08-20 Mobil Oil Corporation Removing SOx, NOX and CO from flue gases
US5240690A (en) 1992-04-24 1993-08-31 Shell Oil Company Method of removing NH3 and HCN from and FCC regenerator off gas
US5268089A (en) 1992-06-24 1993-12-07 Mobil Oil Corporation FCC of nitrogen containing hydrocarbons and catalyst regeneration
US5316661A (en) 1992-07-08 1994-05-31 Mobil Oil Corporation Processes for converting feedstock organic compounds
US5364517A (en) * 1993-02-19 1994-11-15 Chevron Research And Technology Company Perovskite-spinel FCC NOx reduction additive
US5372706A (en) 1993-03-01 1994-12-13 Mobil Oil Corporation FCC regeneration process with low NOx CO boiler
JP3185448B2 (ja) 1993-03-11 2001-07-09 日産自動車株式会社 排気ガス浄化用触媒
DE69401036T2 (de) 1993-06-25 1997-04-10 Tosoh Corp Verfahren zur Entfernung von Stickstoffoxiden
US5407652A (en) 1993-08-27 1995-04-18 Engelhard Corporation Method for decomposing N20 utilizing catalysts comprising calcined anionic clay minerals
DE69519243T2 (de) 1994-02-15 2001-03-08 Tokyo Gas Co. Ltd., Tokio/Tokyo Verfahren und Katalysator zur Reinigung von NOx-enthaltenden Abgasen
US6114265A (en) 1994-03-15 2000-09-05 Exxon Research And Engineering Company Combustion control in a fluid catalytic cracking regenerator
US5589147A (en) 1994-07-07 1996-12-31 Mobil Oil Corporation Catalytic system for the reducton of nitrogen oxides
US5552129A (en) 1994-07-07 1996-09-03 Mobil Oil Corporation Catalytic system for the reduction of nitrogen oxides
CA2156464C (en) 1994-09-30 1999-07-20 Raghu K. Menon Reduction of emissions from fcc regenerators
US20020120169A1 (en) 1995-01-13 2002-08-29 Michel Spagnol Process facilitating the regeneration of a catalyst based on a zeolite used in an acylation reaction, catalyst and use
DE19505579A1 (de) 1995-02-18 1996-08-22 Sued Chemie Ag Adsorbens zur Behandlung von Ölen und/oder Fetten
US6129834A (en) 1995-05-05 2000-10-10 W. R. Grace & Co. -Conn. NOx reduction compositions for use in FCC processes
AU718321B2 (en) 1995-05-05 2000-04-13 W.R. Grace & Co.-Conn. Compositions for reduced NOx and combustion promotion in FCC processes
US5968466A (en) 1995-06-07 1999-10-19 Asec Manufacturing Copper-silver zeolite catalysts in exhaust gas treatment
US6471924B1 (en) 1995-07-12 2002-10-29 Engelhard Corporation Method and apparatus for NOx abatement in lean gaseous streams
US5830346A (en) 1995-08-30 1998-11-03 Mobil Oil Corporation FCC regenerator in partial CO burn with downstream air addition
ATE246032T1 (de) 1995-10-06 2003-08-15 Enitecnologie Spa Katalysator und verfahren zur entfernung von stickstoffoxiden in abgas
US5827793A (en) 1996-04-11 1998-10-27 Exxon Research And Engineering Company Controlled FCC catalyst regeneration using a distributed air system
JP3889467B2 (ja) 1996-09-25 2007-03-07 日本特殊陶業株式会社 窒素酸化物除去用触媒材料及び該材料を用いた窒素酸化物処理装置並びに窒素酸化物除去方法
US5958818A (en) 1997-04-14 1999-09-28 Bulldog Technologies U.S.A., Inc. Alkaline phosphate-activated clay/zeolite catalysts
US6103949A (en) 1997-04-14 2000-08-15 Bulldog Technologies U.S.A., Inc. Alkaline phosphate-activated clay/zeolite catalysts
US6090271A (en) 1997-06-10 2000-07-18 Exxon Chemical Patents Inc. Enhanced olefin yields in a catalytic process with diolefins
US6028023A (en) 1997-10-20 2000-02-22 Bulldog Technologies U.S.A., Inc. Process for making, and use of, anionic clay materials
CN1290193A (zh) 1997-12-03 2001-04-04 埃克森化学专利公司 包含局部涂有第二沸石的沸石的催化剂及其用于烃类转化的用途
US6143261A (en) 1997-12-15 2000-11-07 Exxon Research And Engineering Company Catalytic reduction of nitrogen oxide emissions with MCM-49 and MCM-56
US6106697A (en) 1998-05-05 2000-08-22 Exxon Research And Engineering Company Two stage fluid catalytic cracking process for selectively producing b. C.su2 to C4 olefins
US6908604B2 (en) 1999-05-17 2005-06-21 Exxonmobil Chemical Patents Inc. Macrostructures of porous inorganic material and process for their preparation
US6143681A (en) 1998-07-10 2000-11-07 Northwestern University NOx reduction catalyst
US6037307A (en) 1998-07-10 2000-03-14 Goal Line Environmental Technologies Llc Catalyst/sorber for treating sulfur compound containing effluent
US6110258A (en) 1998-10-06 2000-08-29 Matheson Tri-Gas, Inc. Methods for removal of water from gases using superheated zeolites
DE19854502A1 (de) * 1998-11-25 2000-05-31 Siemens Ag Katalysatorkörper und Verfahren zum Abbau von Stickoxiden
US20020003103A1 (en) 1998-12-30 2002-01-10 B. Erik Henry Fluid cat cracking with high olefins prouduction
DE19936135A1 (de) 1999-07-31 2001-02-15 Degussa Festbettkatalysatoren
KR20020061011A (ko) * 1999-12-28 2002-07-19 코닝 인코포레이티드 제올라이트/알루미나 촉매 지지체 조성물 및 이의 제조방법
US6555492B2 (en) 1999-12-29 2003-04-29 Corning Incorporated Zeolite/alumina catalyst support compositions and method of making the same
US6358169B1 (en) * 2000-05-02 2002-03-19 Borgwarner Inc. Chain tensioner system having a pivoting tensioner arm
US6585952B1 (en) 2000-05-25 2003-07-01 Board Of Trustees Operating Michigan State University Ultrastable hexagonal, cubic and wormhole aluminosilicate mesostructures
CN1156555C (zh) 2000-08-10 2004-07-07 中国石油化工集团公司 一种催化裂化助剂及其制备方法
US7081431B2 (en) 2000-09-08 2006-07-25 Toyota Jidosha Kabushiki Kaisha NOx absorbent and absorption reduction-type NOx purifying catalyst
US6492297B1 (en) 2000-09-15 2002-12-10 Engelhard Corporation Catalyst composition for purifying exhaust gas
US20020094314A1 (en) 2000-11-27 2002-07-18 National Institute Of Advanced Industrial Science And Technology Method for the reduction and removal of nitrogen oxides
JP2002253967A (ja) 2001-02-28 2002-09-10 Showa Denko Kk 亜酸化窒素分解触媒、その製造方法および亜酸化窒素の分解方法
US6632768B2 (en) 2001-03-12 2003-10-14 University Of Missouri-Columbia Adsorbent for HC in exhaust gas, and process for producing the same
JP3981915B2 (ja) 2001-04-03 2007-09-26 日産自動車株式会社 排気ガス浄化システム
DE10132890A1 (de) 2001-07-06 2003-01-16 Daimler Chrysler Ag Feststoff und Verfahren zur Adsorption und Desorption von Stickoxiden in Abgasen von Verbrennungskraftmaschinen
US6800586B2 (en) 2001-11-23 2004-10-05 Engelhard Corporation NOx reduction composition for use in FCC processes
AU2002361338A1 (en) * 2001-11-26 2003-06-10 Atofina Research Composition based on a ferrierite and its use in a gas treatment method for reducing nitrogen oxide emissions
US6912847B2 (en) 2001-12-21 2005-07-05 Engelhard Corporation Diesel engine system comprising a soot filter and low temperature NOx trap
US6709572B2 (en) * 2002-03-05 2004-03-23 Exxonmobil Research And Engineering Company Catalytic cracking process
ATE370917T1 (de) 2002-06-25 2007-09-15 Albemarle Netherlands Bv Verwendung von kationischen schichtmaterialien, zusammensetzungen dieser materialien und die herstellung von kationischen schichtmaterialien
US7045056B2 (en) 2002-10-10 2006-05-16 Engelhard Corporation CO oxidation promoters for use in FCC processes
US20040262197A1 (en) 2003-06-24 2004-12-30 Mcgregor Duane R. Reduction of NOx in low CO partial-burn operation using full burn regenerator additives

Patent Citations (99)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US2892801A (en) * 1955-12-13 1959-06-30 Gen Electric Catalysts
US3036973A (en) * 1958-11-21 1962-05-29 Hoffmann La Roche Racemization catalyst and process for the manufacture thereof
US3129252A (en) * 1960-12-29 1964-04-14 Gen Aniline & Fihn Corp Purification of butynediol
US3184417A (en) * 1960-12-29 1965-05-18 Gen Aniline & Film Corp Method of preparing a copper modified nickel catalyst composition
US3634140A (en) * 1968-09-20 1972-01-11 Asea Ab Fuel cell device utilizing air as oxidant
US4839026A (en) * 1978-09-11 1989-06-13 Atlantic Richfield Company Catalytic cracking with reduced emissions of sulfur oxides
US4199435A (en) * 1978-12-04 1980-04-22 Chevron Research Company NOx Control in cracking catalyst regeneration
US4309279A (en) * 1979-06-21 1982-01-05 Mobil Oil Corporation Octane and total yield improvement in catalytic cracking
US4377502A (en) * 1979-12-26 1983-03-22 Standard Oil Company (Indiana) Synthesis of crystalline aluminosilicate molecular sieves
US4521298A (en) * 1980-07-18 1985-06-04 Mobil Oil Corporation Promotion of cracking catalyst octane yield performance
US4495304A (en) * 1980-07-29 1985-01-22 Atlantic Richfield Company Catalyst for conversion of hydrocarbons
US4495305A (en) * 1980-07-29 1985-01-22 Atlantic Richfield Company Catalyst for conversion of hydrocarbons
US4642178A (en) * 1980-07-29 1987-02-10 Katalistiks, Inc. Process for conversion of hydrocarbons
US4368057A (en) * 1980-10-14 1983-01-11 Matthews Ronald D Method for reducing ammonia concentration in pre-combusted fuel gas using nitric oxide
US4434147A (en) * 1981-10-05 1984-02-28 Chevron Research Company Simultaneous sulfur oxide and nitrogen oxide control in FCC units using cracking catalyst fines with ammonia injection
US4427536A (en) * 1982-02-02 1984-01-24 Chevron Research Company Promoter for the oxidation of SO2 in an FCC process
US4522937A (en) * 1982-11-29 1985-06-11 Atlantic Richfield Company Preparative process for alkaline earth metal, aluminum-containing spinels
US4428827A (en) * 1983-01-24 1984-01-31 Uop Inc. FCC Sulfur oxide acceptor
US4513091A (en) * 1983-02-14 1985-04-23 Mobil Oil Corporation Hydrothermal zeolite activation
US4654318A (en) * 1984-02-28 1987-03-31 Toa Nenryo Kogyo Kabushiki Kaisha Process for preparing catalyst component for polymerization of olefins
US4818509A (en) * 1984-03-23 1989-04-04 Mobil Oil Corporation Continuous process for manufacturing crystalline zeolites in continuously stirred backmixed crystallizers
US4582815A (en) * 1984-07-06 1986-04-15 Mobil Oil Corporation Extrusion of silica-rich solids
US4735927A (en) * 1985-10-22 1988-04-05 Norton Company Catalyst for the reduction of oxides of nitrogen
US5102530A (en) * 1986-03-21 1992-04-07 W. R. Grace & Co.-Conn. Cracking catalysts with octane enhancement
US4898846A (en) * 1986-03-21 1990-02-06 W. R. Grace & Co.-Conn. Cracking catalysts with octane enhancement
US4747935A (en) * 1986-03-26 1988-05-31 Union Oil Company Of California Process for the catalytic cracking of feedstocks containing nitrogen
US4728635A (en) * 1986-04-07 1988-03-01 Katalistiks International Inc. Alkaline earth metal spinels and processes for making
US4798813A (en) * 1986-07-04 1989-01-17 Babcock-Hitachi Kabushiki Kaisha Catalyst for removing nitrogen oxide and process for producing the catalyst
US4797266A (en) * 1986-08-07 1989-01-10 Shell Oil Company Method of preparation of a combined ZSM-5-ferrierite aluminosilicate
US4830840A (en) * 1987-03-13 1989-05-16 Uop Process for removing sulfur oxide and nitrogen oxide
US4904627A (en) * 1987-03-13 1990-02-27 Uop Alkaline earth metal spinel/kaolin clays and processes for making
US4810369A (en) * 1987-05-07 1989-03-07 Union Oil Company Of California Process for the catalytic cracking of feedstocks containing high levels of nitrogen
US4744962A (en) * 1987-07-22 1988-05-17 Shell Oil Company Process for the reduction of ammonia in regeneration zone off gas by select addition of NOx to the regeneration zone or to the regeneration zone off gas
US4812431A (en) * 1987-08-12 1989-03-14 Mobil Oil Corporation NOx control in fluidized bed combustion
US4812430A (en) * 1987-08-12 1989-03-14 Mobil Oil Corporation NOx control during multistage combustion
US4826799A (en) * 1988-04-14 1989-05-02 W. R. Grace & Co.-Conn. Shaped catalyst and process for making it
US4895994A (en) * 1988-04-14 1990-01-23 W. R. Grace & Co.-Conn. Shaped catalysts and processes
US5017538A (en) * 1988-04-18 1991-05-21 Toyota Jidosha Kabushiki Kaisha Catalyst for purifying exhaust gas and a method of producing the same
US4923842A (en) * 1988-10-11 1990-05-08 Allied-Signal Inc. Lanthanum containing catalyst for treating automotive exhaust
US5021144A (en) * 1989-02-28 1991-06-04 Shell Oil Company Process for the reduction of NOX in an FCC regeneration system by select control of CO oxidation promoter in the regeneration zone
US5317055A (en) * 1989-06-02 1994-05-31 Exxon Chemical Patents Inc. Internal resin-tackified acrylic polymers
US5002654A (en) * 1989-12-28 1991-03-26 Mobil Oil Corporation Reducing NOx emissions with zinc catalyst
US5015362A (en) * 1989-12-28 1991-05-14 Mobil Oil Corporation Catalytic conversion of NOx over carbonaceous particles
US4988432A (en) * 1989-12-28 1991-01-29 Mobil Oil Corporation Reducing NOx emissions with antimony additive
US4986897A (en) * 1989-12-28 1991-01-22 Mobil Oil Corporation Catalytic conversion of NOx with NH3
US5002653A (en) * 1989-12-29 1991-03-26 Chevron Research Company Catalytic cracking process with vanadium passivation and improved
US4988654A (en) * 1989-12-29 1991-01-29 Chevron Research Company Dual component cracking catalyst with vanadium passivation and improved sulfur tolerance
US5114691A (en) * 1990-01-18 1992-05-19 Board Of Trustees Operating Michigan State University Process using sorbents for the removal of SOx from flue gas
US5114898A (en) * 1990-01-18 1992-05-19 Board Of Trustees Operating Michigan State University Layered double hydroxide sorbents for the removal of SOx from flue gas and other gas streams
US5206196A (en) * 1990-12-18 1993-04-27 Tosoh Corporation Catalyst for purifying exhaust gas
US5208198A (en) * 1990-12-18 1993-05-04 Tosoh Corporation Catalyst for purifying exhaust gas
US5614453A (en) * 1991-09-11 1997-03-25 Uop Catalyst containing zeolite beta and a pillared clay
US5190736A (en) * 1991-10-18 1993-03-02 Mobil Oil Corporation Synthesis of crystalline ZSM-35
US5286693A (en) * 1991-11-06 1994-02-15 Nippon Oil Co., Ltd. Method of producing catalyst for converting hydrocarbons
US5320822A (en) * 1991-11-20 1994-06-14 The Dow Chemical Company Process of growing crystalline microporous solids in a fluoride-containing, substantially non-aqueous growth medium
US5413977A (en) * 1992-02-27 1995-05-09 Union Oil Company Of California Catalyst containing zeolite beta and a layered magnesium silicate
US5422333A (en) * 1992-08-25 1995-06-06 Idemitsu Kosan Company Limited Exhaust gas purifying catalyst
US5382352A (en) * 1992-10-20 1995-01-17 Mobil Oil Corporation Conversion of NOx in FCC bubbling bed regenerator
US5294332A (en) * 1992-11-23 1994-03-15 Amoco Corporation FCC catalyst and process
US5744113A (en) * 1993-05-27 1998-04-28 Siemens Aktiengesellschaft Process and catalyst for decomposing oxides of nitrogen
US5413699A (en) * 1993-10-14 1995-05-09 Mobil Oil Corporation FCC process with fines tolerant SCR reactor
US5503818A (en) * 1993-11-01 1996-04-02 Csir Aluminosilicate catalyst, a process for the manufacture thereof and a process for the skeletal isomerization of linear olefins
US5379536A (en) * 1993-11-15 1995-01-10 Lorenzana; Moises B. Ironing board attachment including basket
US5510306A (en) * 1993-12-29 1996-04-23 Shell Oil Company Process for isomerizing linear olefins to isoolefins
US5591418A (en) * 1994-06-01 1997-01-07 Amoco Corporation Process for removing sulfur oxides or nitrogen oxides from a gaseous mixture
US5627125A (en) * 1994-07-01 1997-05-06 Monsanto Company Process for preparing carboxylic acid salts and methods for making such catalysts and catalysts useful in such process
US5599520A (en) * 1994-11-03 1997-02-04 Garces; Juan M. Synthesis of crystalline porous solids in ammonia
US5879645A (en) * 1994-11-03 1999-03-09 Korea Research Institute Of Chemical Technology Method for removing nitrogen oxides in exhaust gas by selective catalytic reduction and catalyst for reduction of nitrogen oxides
US20010002426A1 (en) * 1994-11-23 2001-05-31 Mohr Gary David Hydrocarbon conversion process using a zeolite bound zeolite catalyst
US5741468A (en) * 1994-12-28 1998-04-21 Kabushiki Kaisha Riken Exhaust gas cleaner and method for cleaning exhaust gas
US6358881B1 (en) * 1995-05-05 2002-03-19 W. R. Grace & Co.-Conn. Reduced NOx combustion promoter for use in FCC processes
US5705053A (en) * 1995-08-30 1998-01-06 Mobil Oil Corporation FCC regenerator NOx reduction by homogeneous and catalytic conversion
US5716514A (en) * 1995-08-30 1998-02-10 Mobil Oil Corporation FCC NOx reduction by turbulent/laminar thermal conversion
US5744686A (en) * 1995-09-20 1998-04-28 Uop Process for the removal of nitrogen compounds from an aromatic hydrocarbon stream
US6017508A (en) * 1995-10-24 2000-01-25 The Dow Chemical Company Process of modifying the porosity of aluminosilicates and silicas, and mesoporous compositions derived therefrom
US6033641A (en) * 1996-04-18 2000-03-07 University Of Pittsburgh Of The Comonwealth System Of Higher Education Catalyst for purifying the exhaust gas from the combustion in an engine or gas turbines and method of making and using the same
US6040259A (en) * 1996-05-29 2000-03-21 Exxon Chemical Patents Inc. Metal-containing zeolite catalyst, preparation thereof and use for hydrocarbon conversion
US6027696A (en) * 1997-04-11 2000-02-22 Indian Oil Corporation Ltd. Fluidized catalytic cracking apparatus
US6380119B1 (en) * 1997-06-06 2002-04-30 Basf Aktiengesellschaft Method for regenerating a zeolitic catalyst
US6214211B1 (en) * 1998-04-21 2001-04-10 Idemitsu Kosan Co., Ltd Catalytic cracking catalyst
US6190538B1 (en) * 1998-08-03 2001-02-20 Shell Oil Company Process for the preparation of a catalyst composition
US20020049132A1 (en) * 1998-11-03 2002-04-25 Deng-Yang Jan Process for preparing attrition resistant zeolitic layered catalyst composition
US6528031B1 (en) * 1998-12-31 2003-03-04 Korea Research Institute Of Chemical Technology Method for preparing noble metal-supported zeolite catalyst for catalytic reduction of nitrogen oxide
US6395403B2 (en) * 1999-05-06 2002-05-28 W. R. Grace & Co. Conn Promoted porous catalyst
US20020037808A1 (en) * 1999-07-31 2002-03-28 Degussa-Huels Aktiengesellschaft Fixed bed catalysts
US6514470B1 (en) * 1999-10-28 2003-02-04 The Regents Of The University Of California Catalysts for lean burn engine exhaust abatement
US20020038051A1 (en) * 2000-02-18 2002-03-28 Degussa-Huls Ag Raney copper
US6376708B1 (en) * 2000-04-11 2002-04-23 Monsanto Technology Llc Process and catalyst for dehydrogenating primary alcohols to make carboxylic acid salts
US20020039550A1 (en) * 2000-04-22 2002-04-04 Adolf Schafer-Sindlinger Process and catalyst for reducing nitrogen oxides
US20020013228A1 (en) * 2000-06-20 2002-01-31 Takeshi Matsumoto Exhaust gas purifying catalyst and method for purifying exhaust gas
US20020022573A1 (en) * 2000-06-22 2002-02-21 Hiroshi Tanada Exhaust gas purifying catalyst
US20020016259A1 (en) * 2000-06-28 2002-02-07 Tatsuya Yoshikawa Exhaust gas purifying catalyst
US20020022574A1 (en) * 2000-07-17 2002-02-21 Hiroshi Tanada Exhaust gas purifying catalyst
US6538169B1 (en) * 2000-11-13 2003-03-25 Uop Llc FCC process with improved yield of light olefins
US20030019794A1 (en) * 2001-04-13 2003-01-30 Schmidt Stephen Raymond Process for sulfur removal from hydrocarbon liquids
US6558533B2 (en) * 2001-04-13 2003-05-06 W.R. Grace & Co.-Conn Process for sulfur removal from hydrocarbon liquids
US20030040425A1 (en) * 2001-08-21 2003-02-27 Sud-Chemie Prototech Inc. Method for washcoating a catalytic material onto a monolithic structure
US20030073566A1 (en) * 2001-10-11 2003-04-17 Marshall Christopher L. Novel catalyst for selective NOx reduction using hydrocarbons
US20040086442A1 (en) * 2002-08-13 2004-05-06 Intercat, Inc. Flue gas treatments to reduce NOx and CO emissions

Cited By (21)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20080213150A1 (en) * 2005-03-24 2008-09-04 George Yaluris Method for Controlling Nox Emissions in the Fccu
US7780935B2 (en) 2005-03-24 2010-08-24 W. R. Grace & Co.-Conn. Method for controlling NOx emissions in the FCCU
US20090057199A1 (en) * 2005-04-27 2009-03-05 Michael Scott Ziebarth Compositions and Processes for Reducing NOx Emissions During Fluid Catalytic Cracking
US7918991B2 (en) 2005-04-27 2011-04-05 W. R. Grace & Co.-Conn. Compositions and processes for reducing NOx emissions during fluid catalytic cracking
US7976697B2 (en) 2005-04-29 2011-07-12 W. R. Grace & Co.-Conn. NOX reduction compositions for use in partial burn FCC processes
FR2887467A1 (fr) * 2005-06-22 2006-12-29 Air Liquide Procede de traitement des fumees issues du regenerateur catalytique d'une unite de craquage catalytique
US20090107885A1 (en) * 2007-10-29 2009-04-30 Petroleo Brasileiro S.A.- Petrobras Catalytic system and additive for maximisation of light olefins in fluid catalytic cracking units in operations of low severity
US9617480B2 (en) * 2010-03-18 2017-04-11 W. R. Grace & Co.-Conn. Process for making improved zeolite catalysts from peptized aluminas
US9416322B2 (en) 2010-03-18 2016-08-16 W. R. Grace & Co.-Conn. Process for making improved catalysts from clay-derived zeolites
US20130005565A1 (en) * 2010-03-18 2013-01-03 W. R. Grace & Co.-Conn. Process for making improved zeolite catalysts from peptized aluminas
EP2729553A4 (en) * 2011-07-06 2015-04-29 Reliance Ind Ltd METHOD AND COMPOSITION FOR CATALYST / ADDITIVE TO REDUCE GAS LEAKAGE IN FLUID CATALYTIC CRACKING (FCC) PROCESS
CN115025777A (zh) * 2014-08-29 2022-09-09 中国石油化工股份有限公司 用于降低FCC再生烟气CO和NOx排放的组合物及其制备方法
US11298656B2 (en) 2016-06-08 2022-04-12 Basf Corporation Copper-promoted GMElinite and use thereof in the selective catalytic reduction of NOX
WO2017216617A1 (en) * 2016-06-15 2017-12-21 Hindustan Petroleum Corporation Limited A fluid catalytic cracking process for obtaining cracked run naphtha from vacuum gas oil
EP3504297A4 (en) * 2016-08-23 2020-06-17 Quanta Technologies, LLC IMPROVING THE EFFICIENCY OF FCCU REFINERY ADDITIVES
US11078433B2 (en) 2016-10-14 2021-08-03 Gevo, Inc. Conversion of mixtures of C2—C8 olefins to jet fuel and/or diesel fuel in high yield from bio-based alcohols
WO2018071905A1 (en) * 2016-10-14 2018-04-19 Gevo, Inc. Conversion of mixtures of c2-c8 olefins to jet fuel and/or diesel fuel in high yield from bio-based alcohols
WO2018225036A1 (en) * 2017-06-09 2018-12-13 Basf Corporation Catalytic washcoat with controlled porosity for nox abatement
US11717814B2 (en) 2017-06-09 2023-08-08 Basf Corporation Catalytic washcoat with controlled porosity for NOx abatement
WO2020156801A1 (en) * 2019-02-01 2020-08-06 Casale Sa Process for removing nitrogen oxides from a gas
RU2809651C2 (ru) * 2019-02-01 2023-12-14 Касале Са Способ удаления оксидов азота из газа

Also Published As

Publication number Publication date
WO2005047429A1 (en) 2005-05-26
US20100276337A1 (en) 2010-11-04
CN1878855A (zh) 2006-12-13
US9931595B2 (en) 2018-04-03
SG150502A1 (en) 2009-03-30
KR20060113916A (ko) 2006-11-03
ATE550408T1 (de) 2012-04-15
EP1680484B1 (en) 2012-03-21
EP1680484A1 (en) 2006-07-19
JP4977469B2 (ja) 2012-07-18
CA2544918C (en) 2014-07-29
RU2006119619A (ru) 2007-12-27
BRPI0416147B1 (pt) 2014-11-18
KR101133833B1 (ko) 2012-04-06
IL174876A0 (en) 2006-08-20
IL174876A (en) 2011-07-31
CA2544918A1 (en) 2005-05-26
CN1878855B (zh) 2010-12-01
AU2004288928A1 (en) 2005-05-26
JP2007510782A (ja) 2007-04-26
RU2365615C2 (ru) 2009-08-27
BRPI0416147A (pt) 2007-01-09
AU2004288928B2 (en) 2011-03-10
NO20062598L (no) 2006-08-07

Similar Documents

Publication Publication Date Title
US9931595B2 (en) Ferrierite composition for reducing NOx emissions during fluid catalytic cracking
US7641787B2 (en) Compositions and processes for reducing NOx emissions during fluid catalytic cracking
CA2606513C (en) Nox reduction compositions for use in partial burn fcc processes
CA2606249C (en) Compositions and processes for reducing nox emissions during fluid catalytic cracking
ZA200608953B (en) Compositions and processes for reducing NOx emissions during catalytic cracking
ZA200604345B (en) Ferrierite compositions for reducing NOx emissions during fluid catalytic cracking
TWI395614B (zh) 用於減低流體觸媒裂解期間之ＮＯｘ排放之鎂鹼沸石
MXPA06005000A (en) FERRIERITE COMPOSITIONS FOR REDUCING NOx

Legal Events

Date Code Title Description
STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION