TW202241693A - 複合材料結構 - Google Patents

複合材料結構 Download PDF

Info

Publication number
TW202241693A
TW202241693A TW111108435A TW111108435A TW202241693A TW 202241693 A TW202241693 A TW 202241693A TW 111108435 A TW111108435 A TW 111108435A TW 111108435 A TW111108435 A TW 111108435A TW 202241693 A TW202241693 A TW 202241693A
Authority
TW
Taiwan
Prior art keywords
fiber
fiber layer
fibers
composite material
structure according
Prior art date
Application number
TW111108435A
Other languages
English (en)
Inventor
黃寒青
吳榮欽
凌國南
李盛宏
Original Assignee
仁寶電腦工業股份有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 仁寶電腦工業股份有限公司 filed Critical 仁寶電腦工業股份有限公司
Publication of TW202241693A publication Critical patent/TW202241693A/zh

Abstract

一種複合材料結構，包括第一纖維層、第二纖維層以及第三纖維層。第一纖維層由第一長纖維與第一樹脂材料所組成。第二纖維層由第二長纖維與第二樹脂材料所組成。第三纖維層設置於第一纖維層與第二纖維層之間。第三纖維層由短纖維與第三樹脂材料所組成。第一長纖維的長度與第二長纖維的長度皆大於短纖維的長度，且短纖維的長度小於等於25毫米。

Description

複合材料結構
本發明是有關於一種複合結構，且特別是有關於一種複合材料結構。
隨著消費者的生活與工作型態的改變，智慧型手機、平板電腦、電子書閱讀器以及筆記型電腦等電子裝置已成為當前的市場主流。進一步而言，該些電子裝置的機殼須具有足夠的結構強度以提供充分地保護，因此開發出可以使電子裝置的機殼具有足夠的結構強度的材料始終為相關廠商的重要課題。
本發明提供一種複合材料結構，其所製成的電子裝置的機殼可以具有足夠的結構強度。
本發明的一種複合材料結構，包括第一纖維層、第二纖維層以及第三纖維層。第一纖維層由第一長纖維與第一樹脂材料所組成。第二纖維層由第二長纖維與第二樹脂材料所組成。第三纖維層設置於第一纖維層與第二纖維層之間。第三纖維層由短纖維與第三樹脂材料所組成。第一長纖維的長度與第二長纖維的長度皆大於短纖維的長度，且短纖維的長度小於等於25毫米(millimeter, mm)。
在本發明的一實施例中，上述的短纖維的長度大於等於5毫米。
在本發明的一實施例中，上述的短纖維的材料包括碳纖維(carbon fiber)、玻璃纖維(glass fiber)、植物纖維(plant fiber)或其組合。
在本發明的一實施例中，上述的碳纖維包括聚丙烯腈系(PAN系)碳纖維與瀝青系(Pitch系)碳纖維。
在本發明的一實施例中，上述的聚丙烯腈系碳纖維佔短纖維的比例與瀝青系碳纖維佔短纖維的比例皆介於20wt%至80wt%之間。
在本發明的一實施例中，上述的瀝青系碳纖維佔短纖維的比例大於聚丙烯腈系碳纖維佔短纖維的比例。
在本發明的一實施例中，上述的第三纖維層為單層結構。
在本發明的一實施例中，上述的第三纖維層為多層結構。
在本發明的一實施例中，上述的多層結構包括第一部分、第二部分以及第三部分，且第一部分與第一纖維層相鄰、第二部分與第二纖維層相鄰，第三部分位於第一部分與第二部分之間。
在本發明的一實施例中，上述的第一部分的密度等於第二部分的密度且大於第三部分的密度。
在本發明的一實施例中，上述的第一部分的密度與第三部分的密度的比值介於1至1.3之間。
在本發明的一實施例中，上述的第一部分的彎曲彈性模數等於第二部分的彎曲彈性模數且大於第三部分的彎曲彈性模數。
在本發明的一實施例中，上述的第一部              分的彎曲彈性模數與第三部分的彎曲彈性模數的比值介於1至3之間。
在本發明的一實施例中，上述的第三部分為多層結構。
在本發明的一實施例中，上述的第一部分與第二部分以第三部分對稱設置。
在本發明的一實施例中，上述的第一樹脂材料、第二樹脂材料與第三樹脂材料包括熱塑性樹脂、熱固性樹脂或其組合。
在本發明的一實施例中，上述的熱塑性樹脂包括聚碳酸酯(polycarbonate, PC)、聚對苯二甲酸乙二醇酯(polyethylene terephthalate, PET)、聚甲基丙烯酸甲酯(poly(methyl methacrylate), PMMA)、聚乙烯(polyethylene, PE)、丙烯-丁二烯-苯乙烯樹脂(acrylonitrile butadiene styrene, ABS)、聚丙烯(polypropylene, PP)、聚苯乙烯(polystyrene, PS)、聚醯胺(polyamide, PA)或其組合，而熱固性樹脂包括環氧樹脂(epoxy)、酚酫樹脂(phenolic)或其組合。
在本發明的一實施例中，上述的第一長纖維的材料與第二長纖維的材料包括碳纖維、玻璃纖維、植物纖維或其組合。
在本發明的一實施例中，上述的第三纖維層的基重(fiber area weight, FAW)介於每米平方重量10克至300克之間。
基於上述，本發明的複合材料結構包括不同纖維長度的第一纖維層、第二纖維層與第三纖維層，且具有第一纖維層與第二纖維層包括長纖維，第三纖維層包括短纖維的設計，利用不同纖維層在性能上的協同效應提升材料剛性，因此藉由前述複合材料結構所製成的電子裝置的機殼可以具有足夠的結構強度。
為讓本發明的上述特徵和優點能更明顯易懂，下文特舉實施例，並配合所附圖式作詳細說明如下。
下文將會附加標號以對本發明較佳實施例進行詳細描述，並以圖式說明。在可能的情況下，圖式為清楚表達會省略不必要的構件。此外，所繪圖式中的元件尺寸係為說明方便而繪製，並非代表其實際之元件尺寸比例。
本文所使用之方向用語(例如，上、下、右、左、前、後、頂部、底部)僅作為參看所繪圖式使用且不意欲暗示絕對定向。
應當理解，儘管術語”第一”、”第二”、”第三”等在本文中可以用於描述各種元件、部件、區域、層及/或部分，但是這些元件、部件、區域、及/或部分不應受這些術語的限制。這些術語僅用於將一個元件、部件、區域、層或部分與另一個元件、部件、區域、層或部分區分開。
圖1A是依據本發明一實施例的複合材料結構的分解示意圖。圖1B是依據本發明一實施例的複合材料結構的剖面示意圖。請參考圖1A、圖1B，在本實施例中，複合材料結構100包括第一纖維層110、第二纖維層120以及第三纖維層130，其中第三纖維層130設置於第一纖維層110與第二纖維層120之間。進一步而言，第一纖維層110由第一長纖維與第一樹脂材料所組成；第二纖維層120由第二長纖維與第二樹脂材料所組成；第三纖維層130由短纖維與第三樹脂材料所組成。此外，第一長纖維的長度與第二長纖維的長度皆大於短纖維的長度，且短纖維的長度小於等於25毫米。據此，本實施例的複合材料結構100包括不同纖維長度的第一纖維層110、第二纖維層120與第三纖維層130，且具有第一纖維層110與第二纖維層120包括長纖維，第三纖維層130包括短纖維的設計，利用不同纖維層在性能上的協同效應提升材料剛性，因此藉由複合材料結構100所製成的電子裝置的機殼可以具有足夠的結構強度。
在一實施例中，前述第一纖維層110與第二纖維層120可以是依照產品(如智慧型手機或筆記型電腦等)的需求，對應產品的長邊或短邊，使用沒有經過裁切的長纖維所形成的連續纖維層，而第三纖維層130可以是藉由將長纖維裁切成多段的短纖維(長度皆小於等於25毫米)再經由重製所形成的不連續纖維層(可以稱為不織布毡，non-woven mat)，但本發明不限於此。
應說明的是，本發明不限制裁切成多段的短纖維的長度，可以使用相同或不同的長度重製成第三纖維層130，只要每段長度皆小於等於25毫米即屬於本發明的保護範圍。此外，也不限制單一種類、密度或重量的短纖維，亦可以使用多種種類、密度或重量的短纖維重製成第三纖維層130。
進一步而言，第三纖維層130的製作過程中可以藉由控制纖維之順向程度(對應重製製程中的水流方向)，使得縱向方向(machine direction, MD)與橫向方向(transverse direction, TD)具備不同之模數，且縱向方向與橫向方向上的模數比值(MD/TD)可以是大於2以上，舉例而言，在一實施例中，縱向方向上的模數為19.9GPa，而橫向方向上的模數為9.6GPa，但本發明不限於此，在實際產品運用上可視結構需求具有不同的方向配置。在此，縱向方向與橫向方向可以是相互垂直。
在一實施例中，根據所應用的產品，第一纖維層110使用的第一長纖維的長度與第二纖維層120使用的第二長纖維的長度大於第三纖維層130所使用的短纖維長度，而第三纖維層130所使用的短纖維的長度可以是大於等於5毫米(因此第三纖維層130所使用的短纖維的長度可以是5毫米至25毫米之間的任一數值，如10毫米、15毫米、20毫米等)，但本發明不限於此，前述纖維長度皆可以視實際產品(如手持裝置或其他IOT產品)應用進行調整。
在一實施例中，短纖維的材料包括碳纖維、玻璃纖維、植物纖維或其組合，舉例而言，短纖維的材料可以是碳纖維，且碳纖維可以包括聚丙烯腈系碳纖維與瀝青系碳纖維，以利用不同種類的碳纖維在性能上的協同效應，進一步提升複合材料結構100的整體剛性。進一步而言，詳如表1所示，瀝青系碳纖維相較於聚丙烯腈系碳纖維而言具有較高的抗拉模數(tensile modulus)與較低的抗拉強度(tensile strength)及延展性，進而全部使用聚丙烯腈系碳纖維所製成的纖維層會具有抗拉模數較低的問題，而全部使用瀝青系碳纖維所製成的纖維層，會因瀝青系碳纖維低的抗拉強度及延展性造成材料易斷裂的問題，因此藉由不同配比的聚丙烯腈系碳纖維與瀝青系碳纖維的設計，可以使第三纖維層130在具有較佳的抗拉模數的同時改善材料易斷裂的問題。在此，前述配比例如是聚丙烯腈系碳纖維佔短纖維的比例與瀝青系碳纖維佔短纖維的比例皆介於20wt%至80wt%之間(例如是20wt%、40wt%、50wt%、60wt%、70wt%、80wt%或上述20wt%至80wt%內的任一數值)，但本發明不限於此。
表1
　 聚丙烯腈系碳纖維 瀝青系碳纖維
抗拉強度(MPa) 4900 2600
抗拉模數(GPa) 230 640
延展率(%) 2.1 0.3
此外，當全部使用聚丙烯腈系碳纖維所製成的纖維層的抗拉模數為14.1GPa；當聚丙烯腈系碳纖維佔短纖維的比例為50%與瀝青系碳纖維佔短纖維的比例為50%所製成的纖維層的抗拉模數為28.2GPa；而當聚丙烯腈系碳纖維的佔短纖維的比例為20%與瀝青系碳纖維的佔短纖維的比例為80%所製成的纖維層的抗拉模數為36.6GPa，因此在使用的碳纖維中瀝青系碳纖維的比例大於聚丙烯腈系碳纖維的比例可以達到較優異的性能，但本發明不限於此，聚丙烯腈系碳纖維與瀝青系碳纖維可以依照實際設計上的需求進行調整。
在一實施例中，第三纖維層130的基重介於每米平方重量10克至300克之間(例如是10克、30克、50克、80克、100克、200克、300克或上述10克至300克內的任一數值)，因此可以使本實施例的複合材料結構100具有輕量化的優勢，但本發明不限於此。
在一實施例中，第一纖維層110的第一長纖維的材料與第二纖維層120的第二長纖維的材料例如是包括碳纖維、玻璃纖維、植物纖維或其組合，且第一長纖維的材料與第二長纖維的材料可以相同或不同，舉例而言，第一長纖維的材料與第二長纖維的材料可以皆是碳纖維，但本發明不限於此。
在一實施例中，前述第一樹脂材料、第二樹脂材料與第三樹脂材料包括熱塑性樹脂、熱固性樹脂或其組合，其中熱塑性樹脂包括聚碳酸酯、聚對苯二甲酸乙二醇酯、聚甲基丙烯酸甲酯、聚乙烯、丙烯-丁二烯-苯乙烯樹脂、聚丙烯、聚苯乙烯、聚醯胺或其組合，而熱固性樹脂包括環氧樹脂、酚酫樹脂或其組合，但本發明不限於此。
在一實施例中，第一纖維層110、第二纖維層120以及第三纖維層130之間可以經由壓力與溫度壓進行接著，但本發明不限於此。
在一實施例中，第三纖維層130為單層結構，但本發明不限於此，在其他實施例中，第三纖維層可以具有其他不同的態樣。
在此必須說明的是，以下實施例沿用上述實施例的元件標號與部分內容，其中採用相同或近似的標號來表示相同或近似的元件，並且省略了相同技術內容的說明，關於省略部分的說明可參考前述實施例，下述實施例不再重複贅述。
圖2是依據本發明另一實施例的複合材料結構的剖面示意圖。請參考圖2，相較於圖1B的複合材料結構100而言，本實施例的複合材料結構200的第三纖維層230為多層結構，且多層結構包括第一部分230a、第二部分230b以及第三部分230c，其中第一部分230a與第一纖維層110相鄰、第二部分230b與第二纖維層120相鄰，第三部分230c位於第一部分230a與第二部分230b之間。
在本實施例中，第一部分230a的密度等於第二部分230b的密度且大於第三部分230c的密度，舉例而言，第一部分230a的密度與第三部分230c的密度的比值可以介於1至1.3之間(例如是1.05、1.1、1.15、1.2、1.25或上述1至1.3內的任一數值)。此外，第一部分230a的彎曲彈性模數等於第二部分230b的彎曲彈性模數且大於第三部分230c的彎曲彈性模數，舉例而言，第一部分230a的彎曲彈性模數與第三部分230c的彎曲彈性模數的比值可以介於1至3之間(例如是1.5、2、2.5或上述1至3內的任一數值)。
另一方面，第一部分230a與第二部分230b以第三部分230c對稱設置，亦即第一部分230a可以與第二部分230b為相同組成。此外，在未繪示的實施例中，第三部分230c可以為多層結構，因此第三部分亦可以具有多個部分，但本發明不限於此。
在本實施例中，當第三纖維層230使用的短纖維的材料是碳纖維，且碳纖維包括聚丙烯腈系碳纖維與瀝青系碳纖維時，第一部分230a與第二部分230b的瀝青系碳纖維佔短纖維的比例可以高於第三部分230c的瀝青系碳纖維佔短纖維的比例，但本發明不限於此。
綜上所述，本發明的複合材料結構包括不同長度纖維的第一纖維層、第二纖維層與第三纖維層，且具有第一纖維層與第二纖維層包括長纖維，第三纖維層包括短纖維的設計，利用不同纖維層在性能上的協同效應提升材料剛性，因此藉由前述複合材料結構所製成的電子裝置的機殼可以具有足夠的結構強度。此外，短纖維的材料可以是碳纖維，且碳纖維可以包括聚丙烯腈系碳纖維與瀝青系碳纖維，以利用不同種類的碳纖維在性能上的協同效應，進一步提升複合材料結構的整體剛性。
雖然本發明已以實施例揭露如上，然其並非用以限定本發明，任何所屬技術領域中具有通常知識者，在不脫離本發明的精神和範圍內，當可作些許的更動與潤飾，故本發明的保護範圍當視後附的申請專利範圍所界定者為準。
100、200:複合材料結構 110:第一纖維層 120:第二纖維層 130、230:第三纖維層 230a:第一部分 230b:第二部分 230c:第三部分
圖1A是依據本發明一實施例的複合材料結構的分解示意圖。 圖1B是依據本發明一實施例的複合材料結構的剖面示意圖。 圖2是依據本發明另一實施例的複合材料結構的剖面示意圖。
100:複合材料結構
110:第一纖維層
120:第二纖維層
130:第三纖維層

Claims (19)

  1. 一種複合材料結構，包括： 第一纖維層，其中所述第一纖維層由第一長纖維與第一樹脂材料所組成； 第二纖維層，其中所述第二纖維層由第二長纖維與第二樹脂材料所組成；以及 第三纖維層，設置於所述第一纖維層與所述第二纖維層之間，其中所述第三纖維層由短纖維與第三樹脂材料所組成，所述第一長纖維的長度與所述第二長纖維的長度皆大於所述短纖維的長度，且所述短纖維的所述長度小於等於25毫米。
  2. 如請求項1所述的複合材料結構，其中所述短纖維的所述長度大於等於5毫米。
  3. 如請求項1所述的複合材料結構，其中所述短纖維的材料包括碳纖維、玻璃纖維、植物纖維或其組合。
  4. 如請求項3所述的複合材料結構，其中所述碳纖維包括聚丙烯腈系碳纖維與瀝青系碳纖維。
  5. 如請求項4所述的複合材料結構，其中所述聚丙烯腈系碳纖維佔所述短纖維的比例與所述瀝青系碳纖維佔所述短纖維的比例皆介於20wt%至80wt%之間。
  6. 如請求項5所述的複合材料結構，其中所述瀝青系碳纖維佔所述短纖維的所述比例大於所述聚丙烯腈系碳纖維佔所述短纖維的所述比例。
  7. 如請求項1所述的複合材料結構，其中所述第三纖維層為單層結構。
  8. 如請求項1所述的複合材料結構，其中所述第三纖維層為多層結構。
  9. 如請求項8所述的複合材料結構，其中所述多層結構包括第一部分、第二部分以及第三部分，且所述第一部分與所述第一纖維層相鄰、所述第二部分與所述第二纖維層相鄰，所述第三部分位於所述第一部分與所述第二部分之間。
  10. 如請求項9所述的複合材料結構，其中所述第一部分的密度等於所述第二部分的密度且大於所述第三部分的密度。
  11. 如請求項10所述的複合材料結構，其中所述第一部分的所述密度與所述第三部分的所述密度的比值介於1至1.3之間。
  12. 如請求項9所述的複合材料結構，其中所述第一部分的彎曲彈性模數等於所述第二部分的彎曲彈性模數且大於所述第三部分的彎曲彈性模數。
  13. 如請求項12所述的複合材料結構，其中所述第一部分的所述彎曲彈性模數與所述第三部分的所述彎曲彈性模數的比值介於1至3之間。
  14. 如請求項9所述的複合材料結構，其中所述第三部分為多層結構。
  15. 如請求項9所述的複合材料結構，其中所述第一部分與所述第二部分以所述第三部分對稱設置。
  16. 如請求項1所述的複合材料結構，其中第一樹脂材料、所述第二樹脂材料與所述第三樹脂材料包括熱塑性樹脂、熱固性樹脂或其組合。
  17. 如請求項16所述的複合材料結構，其中所述熱塑性樹脂包括聚碳酸酯、聚對苯二甲酸乙二醇酯、聚甲基丙烯酸甲酯、聚乙烯、丙烯-丁二烯-苯乙烯樹脂、聚丙烯、聚苯乙烯、聚醯胺或其組合，而所述熱固性樹脂包括環氧樹脂、酚酫樹脂或其組合。
  18. 如請求項1所述的複合材料結構，其中所述第一長纖維的材料與所述第二長纖維的材料包括碳纖維、玻璃纖維、植物纖維或其組合。
  19. 如請求項1所述的複合材料結構，其中所述第三纖維層的基重介於每米平方重量10克至300克之間。
TW111108435A 2021-04-19 2022-03-08 複合材料結構 TW202241693A (zh)