TW201905181A - 一種液晶組合物及其應用 - Google Patents

一種液晶組合物及其應用

Info

Publication number
TW201905181A
TW201905181A TW107122186A TW107122186A TW201905181A TW 201905181 A TW201905181 A TW 201905181A TW 107122186 A TW107122186 A TW 107122186A TW 107122186 A TW107122186 A TW 107122186A TW 201905181 A TW201905181 A TW 201905181A
Authority
TW
Taiwan
Prior art keywords
liquid crystal
crystal composition
compound
group
general formula
Prior art date
Application number
TW107122186A
Other languages
English (en)
Other versions
TWI670363B (zh
Inventor
朱貝貝
徐海彬
李鵬飛
賀笛
徐爽
Original Assignee
大陸商江蘇和成顯示科技有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 大陸商江蘇和成顯示科技有限公司 filed Critical 大陸商江蘇和成顯示科技有限公司
Publication of TW201905181A publication Critical patent/TW201905181A/zh
Application granted granted Critical
Publication of TWI670363B publication Critical patent/TWI670363B/zh

Abstract

本發明公開了一種液晶組合物及其應用，所述液晶組合物包含至少一種通式Ⅰ的化合物，以及至少一種選自由通式Ⅱ-1、通式Ⅱ-2及其組合組成的組的化合物。本發明提供的液晶組合物具有適合的光學各向異性、高的清亮點以及高的彈性常數K11和K33，還具有相對低的介電各向異性，所述液晶組合物應用於液晶顯示器中時，可以具有較好的耐候性及較高的對比度。

Description

一種液晶組合物及其應用
本發明涉及液晶材料領域，具體涉及一種液晶組合物及其應用。
液晶顯示器（Liquid Crystal Display，LCD）因其體積小、重量輕、功耗低且顯示品質優異而獲得了飛速發展，特別在可擕式電子資訊產品中獲得廣泛的應用。隨著用於可擕式電腦、辦公應用、視頻應用的液晶螢幕尺寸的增加，液晶顯示器能夠用於大螢幕顯示並最終替代了陰極射線管的顯示器（Cathode Ray Tube，CRT）。
根據顯示模式的類型分為PC（phase change，相變）、TN（twist nematic，扭曲向列）、STN（super twisted nematic，超扭曲向列）、ECB（electrically controlled birefringence，電控雙折射）、OCB（optically compensated bend，光學補償彎曲）、IPS（in-plane switching，共面轉變）、VA（vertical alignment，垂直配向）等類型。
液晶材料必須具有良好的低溫互溶性和熱穩定性。此外，液晶材料應當具有低粘度和短回應時間，低閾值電壓和高對比。為了獲得具有良好特性的液晶顯示元件，而提高液晶組合物的各項性能指標。根據市售的液晶顯示元件來進一步說明組合物的各項性能指標。向列相的溫度範圍與元件的工作溫度範圍相關聯。向列相的上限溫度較好的是大於等於70℃，並且向列相的下限溫度較好的是小於等於-10℃。組合物的粘度與元件的回應時間相關聯。為了在元件中顯示動畫，較好的是元件的回應時間短。因此，較好的是組合物的粘度小，而更好的是溫度低時組合物的粘度小。
含有光學各向異性適當的液晶組合物的液晶顯示元件能夠增大對比度。
含有介電各向異性的絕對值大的液晶組合物的液晶顯示元件能夠降低基礎電壓值、降低驅動電壓，並能進一步降低消耗電功率。
陡度因數γ對器件參數是一個大的影響因素，U10 、U50 、U90 分別對應於TN-LCD透過率變化量為10%、50%、90%時的電壓。
按自由能密度的方法計算得到平衡態下的U50 、U90 ，得出如下關係式：
當1時，γ最陡。該條件與漏光最小條件大體一致，所以該條件可得到對比度大的顯示，在該條件下顯示器件漏光最小、陡度最好，其中，λ為入射波長。
因此，γ與液晶材料的K33 /K11 也有關，在TN盒的K33 /K11 愈小，其γ愈小。但在TFT顯示中，γ愈大，灰階顯示愈好，因此在TFT顯示中，K33 /K11 相對較大會更好。
單一的液晶化合物通常難以發揮其特性，通常將其與其他多種液晶化合物混合配製成組合物。在現有液晶組合物中，能夠得到較優的特性，但是該種類組合物清亮點較低、粘度較高、光學各向異性不夠大、介電各向異性的絕對值較低、電壓保持率低，對混合成具有較大光學各向異性、適宜介電各向異性的絕對值、較好穩定性以及較好對比度的組合物説明不大，直接導致對比度低、回應速度慢、器件顯示效果差等不良後果，例如國外專利文獻WO9202597、WO9116398、WO9302153、WO9116399，中國專利文獻CN1157005A等，不同程度上具有上述缺點。
因此，需要一種液晶組合物，其具有大的光學各向異性、高的介電各向異性的絕對值、高的清亮點、低的閾值電壓、較好的可靠性、良好的陡度、良好灰階顯示效果等特性。
發明目的： 針對現有技術的缺陷，本發明的目的在於提供一種光學各向異性大、介電各向異性的絕對值大、具有寬的向列相、低溫存儲穩定性高並且對比度高的液晶組合物，以及包含所述液晶組合物的液晶顯示元件。
本發明的技術方案： 本發明的一個方面提供一種液晶組合物，包含： 至少一種通式Ⅰ的化合物Ⅰ；以及 至少一種選自由通式Ⅱ-1、通式Ⅱ-2及其組合組成的組的化合物Ⅱ-1；Ⅱ-2， 其中， R1 、R2 、R3 、R4 、R3 ’和R4 ’各自獨立的表示-H、-F、含有1-12個碳原子的烷基或烷氧基、含有2-12個碳原子的烯基或烯氧基、-OR5 OR6 、、或，其中所述烷基或烷氧基和所述烯基或烯氧基中的一個或多個H可以被F取代，且R1 和R2 中至少一個為-OR5 OR6 ； R5 和R6 各自獨立的表示含有1-12個碳原子的烷基或含有2-12個碳原子的烯基； Z1 、Z2 和Z3 各自獨立的表示單鍵、-COO-、-OCO-、-CH2 O-、-OCH2 -或-CH2 CH2 -； L1 和L2 各自獨立的表示-F、-Cl、-CN或-NCS； 環和環各自獨立的表示或，其中，中一個或多個-CH2 -可被-O-替代，中一個或多個H可以被鹵素取代； 環、環、環、環和環各自獨立的表示、、或； n1和n2各自獨立的表示0、1、2或3，且當n1為2或3時，環可以相同或不同，Z1 可以相同或不同；當n2為2或3時，環可以相同或不同，Z2 可以相同或不同； m表示1或2，且當m為2時，環可以相同或不同，Z3 可以相同或不同。
優選的，所述通式Ⅰ的化合物選自如下化合物組成的組：Ⅰ-1；以及Ⅰ-2， 其中， 環表示或，且當n1為1時，環表示，當n1為2或3時，至少一個環表示； L6 、L7 、L8 和L9 各自獨立的表示-H或-F； o表示1或2； p和q各自獨立的表示0或1。
進一步優選的，所述通式Ⅰ-1的化合物選自如下化合物組成的組：Ⅰ-1-1；Ⅰ-1-2；Ⅰ-1-3；Ⅰ-1-4；Ⅰ-1-5；Ⅰ-1-6；Ⅰ-1-7；Ⅰ-1-8；Ⅰ-1-9；Ⅰ-1-10；Ⅰ-1-11；以及Ⅰ-1-12， 所述通式Ⅰ-2的化合物選自如下化合物組成的組：Ⅰ-2-1；Ⅰ-2-2；Ⅰ-2-3；Ⅰ-2-4；以及Ⅰ-2-5； 其中， R11 和R21 各自獨立的表示-H、-F、含有1-7個碳原子的烷基或烷氧基、含有2-7個碳原子的烯基或烯氧基、-OR51 OR61 、、或，其中所述烷基或烷氧基和所述烯基或烯氧基中的一個或多個H可以被F取代，且R11 和R21 中至少一個為-OR51 OR61 ； R51 和R61 各自獨立的表示含有1-10個碳原子的烷基或含有2-10個碳原子的烯基。
再進一步的，所述Ⅰ-1-1的化合物選自如下化合物組成的組 所述Ⅰ-1-2的化合物選自如下化合物組成的組： 所述Ⅰ-1-3的化合物選自如下化合物組成的組 所述Ⅰ-1-4的化合物選自如下化合物組成的組： 所述Ⅰ-1-5的化合物選自如下化合物組成的組 所述Ⅰ-1-6的化合物選自如下化合物組成的組： 所述Ⅰ-1-7的化合物選自如下化合物組成的組 所述Ⅰ-1-8的化合物選自如下化合物組成的組： 所述Ⅰ-1-9的化合物選自如下化合物組成的組 所述Ⅰ-1-10的化合物選自如下化合物組成的組：Ⅰ-1-10-1；Ⅰ-1-10-2；Ⅰ-1-10-3；Ⅰ-1-10-4；Ⅰ-1-10-5；Ⅰ-1-10-6；Ⅰ-1-10-7；Ⅰ-1-10-8；Ⅰ-1-10-9；Ⅰ-1-10-10；Ⅰ-1-10-11；以及Ⅰ-1-10-12， 所述Ⅰ-1-11的化合物選自如下化合物組成的組：Ⅰ-1-11-1；Ⅰ-1-11-2；Ⅰ-1-11-3；Ⅰ-1-11-4；Ⅰ-1-11-5；Ⅰ-1-11-6；Ⅰ-1-11-7；Ⅰ-1-11-8；Ⅰ-1-11-9；Ⅰ-1-11-10；Ⅰ-1-11-11；以及Ⅰ-1-11-12， 所述Ⅰ-1-12的化合物選自如下化合物組成的組：Ⅰ-1-12-1；Ⅰ-1-12-2；Ⅰ-1-12-3；Ⅰ-1-12-4；Ⅰ-1-12-5；Ⅰ-1-12-6；Ⅰ-1-12-7；Ⅰ-1-12-8；Ⅰ-1-12-9；Ⅰ-1-12-10；Ⅰ-1-12-11；以及Ⅰ-1-12-12， 所述Ⅰ-2-1的化合物選自如下化合物組成的組 所述Ⅰ-2-2的化合物選自如下化合物組成的組： 所述Ⅰ-2-3的化合物選自如下化合物組成的組 所述Ⅰ-2-4的化合物選自如下化合物組成的組： 所述Ⅰ-2-5的化合物選自如下化合物組成的組
優選的，所述通式Ⅱ-1的化合物選自如下化合物組成的組：Ⅱ-1-1；Ⅱ-1-2；Ⅱ-1-3；Ⅱ-1-4， 所述通式Ⅱ-2的化合物選自如下化合物組成的組：Ⅱ-2-1；Ⅱ-2-2；Ⅱ-2-3；Ⅱ-2-4；Ⅱ-2-5；Ⅱ-2-6；Ⅱ-2-7；Ⅱ-2-8；Ⅱ-2-9；以及Ⅱ-2-10， 其中， R31 、R41 、R31 ’和R41 ’各自獨立的表示H、含有1-7個碳原子的烷基或烷氧基、含有2-7個碳原子的烯基或烯氧基。
進一步優選的，所述通式Ⅱ-1的化合物選自如下化合物組成的組：Ⅱ-1-1；Ⅱ-1-2；以及Ⅱ-1-3； 所述通式Ⅱ-2的化合物選自如下化合物組成的組：Ⅱ-2-1；以及Ⅱ-2-2。
優選的，所述液晶組合物至少包含2wt%以上的通式Ⅱ-2的化合物。
優選的，所述R5 為-C3 H6 -或-C4 H8 -。
在本發明的一些實施方案中，優選的，所述通式Ⅱ-1-1的化合物選自由如下化合物組成的組 所述通式Ⅱ-1-2的化合物選自由如下化合物組成的組： 所述通式Ⅱ-1-3的化合物選自由如下化合物組成的組 所述通式Ⅱ-1-4的化合物選自由如下化合物組成的組： 所述通式Ⅱ-2-1的化合物選自由如下化合物組成的組： 所述通式Ⅱ-2-2的化合物選自由如下化合物組成的組 所述通式Ⅱ-2-3的化合物選自由如下化合物組成的組： 所述通式Ⅱ-2-4的化合物選自由如下化合物組成的組 所述通式Ⅱ-2-5的化合物選自由如下化合物組成的組：Ⅱ-2-5-1；Ⅱ-2-5-2；Ⅱ-2-5-3；Ⅱ-2-5-4；Ⅱ-2-5-5；Ⅱ-2-5-6；Ⅱ-2-5-7；Ⅱ-2-5-8；Ⅱ-2-5-9；以及Ⅱ-2-5-10， 所述通式Ⅱ-2-6的化合物選自由如下化合物組成的組：Ⅱ-2-6-1；Ⅱ-2-6-2；Ⅱ-2-6-3；Ⅱ-2-6-4；Ⅱ-2-6-5；Ⅱ-2-6-6；Ⅱ-2-6-7；Ⅱ-2-6-8；Ⅱ-2-6-9；Ⅱ-2-6-10；Ⅱ-2-6-11；Ⅱ-2-6-12；Ⅱ-2-6-13；Ⅱ-2-6-14；Ⅱ-2-6-15；以及Ⅱ-2-6-16， 所述通式Ⅱ-2-7的化合物選自由如下化合物組成的組：Ⅱ-2-7-1；Ⅱ-2-7-2；Ⅱ-2-7-3；Ⅱ-2-7-4；Ⅱ-2-7-5；Ⅱ-2-7-6；Ⅱ-2-7-7；Ⅱ-2-7-8；Ⅱ-2-7-9；Ⅱ-2-7-10；Ⅱ-2-7-11；Ⅱ-2-7-12；Ⅱ-2-7-13；Ⅱ-2-7-14；Ⅱ-2-7-15；以及Ⅱ-2-7-16， 所述通式Ⅱ-2-8的化合物選自由如下化合物組成的組：Ⅱ-2-8-1；Ⅱ-2-8-2；Ⅱ-2-8-3；Ⅱ-2-8-4；Ⅱ-2-8-5；Ⅱ-2-8-6；Ⅱ-2-8-7；Ⅱ-2-8-8；Ⅱ-2-8-9；Ⅱ-2-8-10；Ⅱ-2-8-11；Ⅱ-2-8-12；Ⅱ-2-8-13；Ⅱ-2-8-14；Ⅱ-2-8-15；以及Ⅱ-2-8-16， 所述通式Ⅱ-2-9的化合物選自由如下化合物組成的組：Ⅱ-2-9-1；Ⅱ-2-9-2；Ⅱ-2-9-3；Ⅱ-2-9-4；Ⅱ-2-9-5；Ⅱ-2-9-6；Ⅱ-2-9-7；Ⅱ-2-9-8；Ⅱ-2-9-9；Ⅱ-2-9-10；Ⅱ-2-9-11；Ⅱ-2-9-12；Ⅱ-2-9-13；Ⅱ-2-9-14；Ⅱ-2-9-15；以及Ⅱ-2-9-16， 所述通式Ⅱ-2-10的化合物選自由如下化合物組成的組：Ⅱ-2-10-1；Ⅱ-2-10-2；Ⅱ-2-10-3；Ⅱ-2-10-4；Ⅱ-2-10-5；Ⅱ-2-10-6；Ⅱ-2-10-7；Ⅱ-2-10-8；Ⅱ-2-10-9；Ⅱ-2-10-10；Ⅱ-2-10-11；Ⅱ-2-10-12；Ⅱ-2-10-13；Ⅱ-2-10-14；Ⅱ-2-10-15；以及Ⅱ-2-10-16。
所述液晶組合物還包含至少一種通式Ⅲ的化合物Ⅲ， 其中， R7 和R8 各自獨立的表示-H、-F、含有1-12個碳原子的烷基或烷氧基、含有2-12個碳原子的烯基或烯氧基、、或，其中所述烷基或烷氧基和所述烯基或烯氧基中的一個或多個H可以被F取代； Z4 和Z5 各自獨立的表示單鍵、-COO-、-OCO-、-CH2 O-、-OCH2 -或-CH2 CH2 -； 環和環各自獨立的表示或，其中，中一個或多個-CH2 -可被-O-替代，中一個或多個H可以被鹵素取代； k1和k2各自獨立的表示0、1、2或3，且當k1為2或3時，環可以相同或不同，Z4 可以相同或不同；當k2為2或3時，環可以相同或不同，Z5 可以相同或不同。
優選的，所述通式Ⅲ的化合物選自由如下化合物組成的組：Ⅲ-1；Ⅲ-2；Ⅲ-3；Ⅲ-4；Ⅲ-5；Ⅲ-6；Ⅲ-7；Ⅲ-8；Ⅲ-9；Ⅲ-10；Ⅲ-11；Ⅲ-12；Ⅲ-13；Ⅲ-14；Ⅲ-15；Ⅲ-16；以及Ⅲ-17， 其中， R71 和R81 各自獨立的表示-H、-F、含有1-7個碳原子的烷基或烷氧基、含有2-7個碳原子的烯基或烯氧基、、或，其中所述烷基或烷氧基和所述烯基或烯氧基中的一個或多個H可以被F取代。
在本發明的一些實施方案中，所述通式Ⅰ的化合物占所述液晶組合物總重量的1%~60%，所述通式Ⅱ的化合物占所述液晶組合物總重量的1%~55%，所述通式Ⅲ的化合物占所述液晶組合物總重量的0%~60%。
進一步的，在本發明的一些實施方案中,所述通式Ⅰ的化合物占所述液晶組合物總重量的1%~50%，所述通式Ⅱ的化合物占所述液晶組合物總重量的1%~55%，所述通式Ⅲ的化合物占所述液晶組合物總重量的0%~55%。
更進一步的，在本發明的一些實施方案中，所述通式Ⅰ的化合物占所述液晶組合物總重量的1%~50%，所述通式Ⅱ的化合物占所述液晶組合物總重量的1%~50%，所述通式Ⅲ的化合物占所述液晶組合物總重量的1%~50%。
本發明另一方面提供一種液晶組合物，還包含本領域技術人員已知和文獻中描述的一種或多種添加劑。例如，可以加入占所述液晶組合物總重量的0-15%的多色染料和/或手性摻雜劑。
如下顯示優選加入到根據本發明的混合物中的可能摻雜劑。；；；；；；；；；；；；以及。
在本發明的實施方案中，優選所述摻雜劑占所述液晶組合物總重量的0-5%；更優地，所述摻雜劑占所述液晶組合物總重量的0-1%。
如下提及例如可以加入到根據本發明的混合物中的穩定劑
優選地，所述穩定劑選自如下所示的穩定劑。
在本發明的實施方案中，優選所述穩定劑占所述液晶組合物總重量的0-5%；更優地，所述穩定劑占所述液晶組合物總重量的0-1%；作為特別優選方案，所述穩定劑占所述液晶組合物總重量的0-0.1%。
本發明另一方面還提供一種包含上述液晶組合物的液晶顯示器件。
有益效果：
本發明提供的液晶組合物具有適合的光學各向異性、高的清亮點以及彈性常數K11 和K33 ，還具有相對低的介電各向異性，所述液晶組合物應用於液晶顯示器中時，可以具有較好的耐候性及較高的對比度。
以下將結合具體實施方案來說明本發明。需要說明的是，下面的實施例為本發明的示例，僅用來說明本發明，而不用來限制本發明。在不偏離本發明主旨或範圍的情況下，可進行本發明構思內的其他組合和各種改良。
為便於表達，以下各實施例中，液晶組合物的基團結構用表1所列的代碼表示： 表1 液晶化合物的基團結構代碼
以如下結構式的化合物為例：該結構式如用表1所列代碼表示，則可表達為：nCCGF，代碼中的n表示左端烷基的C原子數，例如n為“3”，即表示該烷基為-C3 H7 ；代碼中的C代表環己烷基，G代表2-氟-1,4-亞苯基，F代表氟。
以下實施例中測試專案的簡寫代號如下： Cp（℃） 清亮點（向列-各向同性相轉變溫度） Δn 光學各向異性（589 nm，25℃） Δε 介電各向異性（1 KHz，25℃） K11 展曲彈性常數 K33 彎曲彈性常數 其中， 光學各向異性使用阿貝折光儀在鈉光燈（589 nm）光源下、25℃測試得到； Δε=ε‖ -ε⊥ ，其中，ε‖ 為平行于分子軸的介電常數，ε⊥ 為垂直于分子軸的介電常數，測試條件：25℃、1KHz、測試盒為TN90型，盒厚7 μm。 K11 、K33 是使用LCR儀和反平行摩擦盒，測試液晶的C-V曲線計算所得，測試條件：7μm反平行摩擦盒，V=0.1~20V。 在以下的實施例中所採用的各成分，均可以通過公知的方法進行合成，或者通過商業途徑獲得。這些合成技術是常規的，所得到各液晶化合物經測試符合電子類化合物標準。
按照以下實施例規定的各液晶組合物的配比，製備液晶組合物。所述液晶組合物的製備是按照本領域的常規方法進行的，如採取加熱、超聲波、懸浮等方式按照規定比例混合制得。
製備並研究下列實施例中給出的液晶組合物。下面顯示了各液晶組合物的組成和其性能參數測試結果。
對比例 1
按表2中所列的各化合物及重量百分數配製成對比例1的液晶組合物，其填充於液晶顯示器兩基板之間進行性能測試，測試資料如下表所示： 表2 液晶組合物配方及其測試性能
實施例 1
按表3中所列的各化合物及重量百分數配製成實施例1的液晶組合物，其填充於液晶顯示器兩基板之間進行性能測試，測試資料如下表所示： 表3 液晶組合物配方及其測試性能
實施例 2
按表4中所列的各化合物及重量百分數配製成實施例2的液晶組合物，其填充於液晶顯示器兩基板之間進行性能測試，測試資料如下表所示： 表4 液晶組合物配方及其測試性能
實施例 3
按表5中所列的各化合物及重量百分數配製成實施例3的液晶組合物，其填充於液晶顯示器兩基板之間進行性能測試，測試資料如下表所示： 表5 液晶組合物配方及其測試性能
實施例 4
按表6中所列的各化合物及重量百分數配製成實施例4的液晶組合物，其填充於液晶顯示器兩基板之間進行性能測試，測試資料如下表所示： 表6 液晶組合物配方及其測試性能
實施例 5
按表7中所列的各化合物及重量百分數配製成實施例5的液晶組合物，其填充於液晶顯示器兩基板之間進行性能測試，測試資料如下表所示： 表7 液晶組合物配方及其測試性能
實施例 6
按表8中所列的各化合物及重量百分數配製成實施例6的液晶組合物，其填充於液晶顯示器兩基板之間進行性能測試，測試資料如下表所示： 表8 液晶組合物配方及其測試性能
實施例 7
按表9中所列的各化合物及重量百分數配製成實施例7的液晶組合物，其填充於液晶顯示器兩基板之間進行性能測試，測試資料如下表所示： 表9 液晶組合物配方及其測試性能
為了突出本發明的液晶組合物的有益效果，發明人選取和本發明實施例體系相近的對比例。通過以上對比例1、實施例1-7可以看出，包含本發明通式Ⅰ的液晶組合物可以顯著的提高低溫存儲性能，再匹配以通式Ⅱ-1和/或通式Ⅱ-2的中性組分時，可以顯著增大彈性常數K11 和K33 ，能夠提升對比度。綜上，本發明提供的液晶組合物具有適合的光學各向異性以及高的彈性常數K11 和K33 ，還具有相對高的清亮點和相對低的介電各向異性，所述液晶組合物應用於液晶顯示器中時，可以具有較好的耐候性及較高的對比度。
以上實施方式只為說明本發明的技術構思及特點，其目的在於讓熟悉此項技術的人瞭解本發明內容並加以實施，並不能以此限制本發明的保護範圍，凡根據本發明精神實質所做的等效變化或修飾，都應涵蓋在本發明的保護範圍內。

Claims (10)

  1. 一種液晶組合物，其包含： 至少一種通式Ⅰ的化合物Ⅰ；以及 至少一種選自由通式Ⅱ-1、通式Ⅱ-2及其組合組成的組的化合物Ⅱ-1；Ⅱ-2， 其中， R1 、R2 、R3 、R4 、R3 ’和R4 ’各自獨立的表示-H、-F、含有1-12個碳原子的烷基或烷氧基、含有2-12個碳原子的烯基或烯氧基、-OR5 OR6 、、或，其中該烷基或烷氧基和該烯基或烯氧基中的一個或多個H可以被F取代，且R1 和R2 中至少一個為-OR5 OR6 ； R5 和R6 各自獨立的表示含有1-12個碳原子的烷基或含有2-12個碳原子的烯基； Z1 、Z2 和Z3 各自獨立的表示單鍵、-COO-、-OCO-、-CH2 O-、-OCH2 -或-CH2 CH2 -； L1 和L2 各自獨立的表示-F、-Cl、-CN或-NCS； 環和環各自獨立的表示或，其中，中一個或多個-CH2 -可被-O-替代，中一個或多個H可以被鹵素取代； 環、環、環、環和環各自獨立的表示、、或； n1和n2各自獨立的表示0、1、2或3，且當n1為2或3時，環可以相同或不同，Z1 可以相同或不同；當n2為2或3時，環可以相同或不同，Z2 可以相同或不同； m表示1或2，且當m為2時，環可以相同或不同，Z3 可以相同或不同。
  2. 如申請專利範圍第1項所述之液晶組合物，其中，該通式Ⅰ的化合物選自如下化合物組成的組：Ⅰ-1；以及Ⅰ-2， 其中， 環表示或，且當n1為1時，環表示，當n1為2或3時，至少一個環表示； L6 、L7 、L8 和L9 各自獨立的表示-H或-F； o表示1或2； p和q各自獨立的表示0或1。
  3. 如申請專利範圍第2項所述之液晶組合物，其中，根據權利要求2所述的液晶組合物，其特徵在於，該通式Ⅰ-1的化合物選自如下化合物組成的組：Ⅰ-1-1；Ⅰ-1-2；Ⅰ-1-3；Ⅰ-1-4；Ⅰ-1-5；Ⅰ-1-6；Ⅰ-1-7；Ⅰ-1-8；Ⅰ-1-9；Ⅰ-1-10；Ⅰ-1-11；以及Ⅰ-1-12， 該通式Ⅰ-2的化合物選自如下化合物組成的組：Ⅰ-2-1；Ⅰ-2-2；Ⅰ-2-3；Ⅰ-2-4；以及Ⅰ-2-5； 其中， R11 和R21 各自獨立的表示-H、-F、含有1-7個碳原子的烷基或烷氧基、含有2-7個碳原子的烯基或烯氧基、-OR51 OR61 、、或，其中該烷基或烷氧基和該烯基或烯氧基中的一個或多個H可以被F取代，且R11 和R21 中至少一個為-OR51 OR61 ； R51 和R61 各自獨立的表示含有1-10個碳原子的烷基或含有2-10個碳原子的烯基。
  4. 如申請專利範圍第1項所述之液晶組合物，其中，該通式Ⅱ-1的化合物選自如下化合物組成的組：Ⅱ-1-1；Ⅱ-1-2；Ⅱ-1-3；以及Ⅱ-1-4； 該通式Ⅱ-2的化合物選自如下化合物組成的組：Ⅱ-2-1；Ⅱ-2-2；Ⅱ-2-3；Ⅱ-2-4；Ⅱ-2-5；Ⅱ-2-6；Ⅱ-2-7；Ⅱ-2-8；Ⅱ-2-9；以及Ⅱ-2-10， 其中， R31 、R41 、R31 ’和R41 ’各自獨立的表示H、含有1-7個碳原子的烷基或烷氧基、含有2-7個碳原子的烯基或烯氧基。
  5. 如申請專利範圍第1項所述之液晶組合物，其中，該液晶組合物至少包含2wt%以上的通式Ⅱ-2的化合物。
  6. 如申請專利範圍第1項所述之液晶組合物，其中，R5 為-C3 H6 -或-C4 H8 -。
  7. 如申請專利範圍第1項所述之液晶組合物，其中，該液晶組合物還包含至少一種通式Ⅲ的化合物Ⅲ， 其中， R7 和R8 各自獨立的表示-H、-F、含有1-12個碳原子的烷基或烷氧基、含有2-12個碳原子的烯基或烯氧基、、或，其中該烷基或烷氧基和該烯基或烯氧基中的一個或多個H可以被F取代； Z4 和Z5 各自獨立的表示單鍵、-COO-、-OCO-、-CH2 O-、-OCH2 -或-CH2 CH2 -； 環和環各自獨立的表示或，其中，中一個或多個-CH2 -可被-O-替代，中一個或多個H可以被鹵素取代； k1和k2各自獨立的表示0、1、2或3，且當k1為2或3時，環可以相同或不同，Z4 可以相同或不同；當k2為2或3時，環可以相同或不同，Z5 可以相同或不同。
  8. 如申請專利範圍第7項所述之液晶組合物，其中，該通式Ⅰ的化合物占該液晶組合物總重量的1%~60%，該通式Ⅱ的化合物占該液晶組合物總重量的1%~55%，該通式Ⅲ的化合物占該液晶組合物總重量的0%~60%。
  9. 如申請專利範圍第8項所述之液晶組合物，其中，該通式Ⅰ的化合物占該液晶組合物總重量的1%~50%，該通式Ⅱ的化合物占該液晶組合物總重量的1%~55%，該通式Ⅲ的化合物占該液晶組合物總重量的0%~55%。
  10. 一種包含如申請專利範圍第1~9項中任一項所述之液晶組合物的液晶顯示器件。
TW107122186A 2017-06-30 2018-06-27 一種液晶組合物及其應用 TWI670363B (zh)