TW201734081A - 製造纖維複合材料之液體浸漬法用的潛伏性環氧樹脂調合物 - Google Patents
製造纖維複合材料之液體浸漬法用的潛伏性環氧樹脂調合物 Download PDFInfo
- Publication number
- TW201734081A TW201734081A TW105140474A TW105140474A TW201734081A TW 201734081 A TW201734081 A TW 201734081A TW 105140474 A TW105140474 A TW 105140474A TW 105140474 A TW105140474 A TW 105140474A TW 201734081 A TW201734081 A TW 201734081A
- Authority
- TW
- Taiwan
- Prior art keywords
- diamine
- epoxy
- polyamine
- weight
- epoxy resin
- Prior art date
Abstract
本發明提出環氧組成物,其由至少一種樹脂組份和至少一種硬化劑組份所組成,該組成物適合用作為熱固基質以供製造纖維基質產品半成品和硬化的纖維基質積層物。
Description
本發明提出環氧組成物,其由至少一種樹脂組份和至少一種硬化劑組份所組成,該組成物適合用作為熱固基質以供製造纖維基質產品半成品和硬化的纖維基質積層物,所謂的複合物件。
長久以來已經知道由至少一種環氧樹脂和至少一種硬化劑(例如胺、酐或二氰二醯胺)所組成之環氧組成物且其用於例如塗料、複合物件或地板材料之應用領域。此處,複合物件是指由纖維和聚合物基質所構成之複合材料。
在廣泛之各種不同的工業中,對於有效利用珍貴的資源之要求提高,質輕的建構方案越來越受到重視。一旦物體必須移動,纖維複合材料/複合物件就成為感興趣的選項,此因這些提供高的特定韌度和強度及低重
量之故。因此,複合物件已用於航空達數十年,且若沒有纖維複合材料技術,甚至無法得到例如用於風車之均勻的轉子葉片。因為彼等之極佳的性質,這些材料亦在汽車建構中倍受關注。在所提到之所有的3個市場區塊中,均須要高機械強度的組件,此可藉連續之纖維強化的聚合物材料達成。但是,對於這些組件的幾何形狀的要求日增(例如,持續提高風車的轉子葉片的長度以便能夠"收成"最大風量),且同時要求更高的產能。
此發明之上下文中,"複合物件"特別作為"複合組件"、"複合材料"、"纖維複合材料"、"複合模製品"、"纖維強化的塑料"或"纖維強化的組件"、"預浸物"、"纖維基質產品半成品"、"SMC"(片模塑料)、"SMC複合物件"(SMC纖維基質產品半成品)、"CFK"、"GFK"和"FVK"的同義詞。用於製造複合物件之方法可分成單階段方法,例如RTM(樹脂轉移模製)和VARTM(真空輔助樹脂轉移模製),及多階段方法,例如預浸技術和SMC(片模塑料)。
在多階段方法中之經由纖維產品半成品(例如以玻璃纖維或碳纖維為基礎並以預聚合物浸漬的織物纖維,預浸物)的路徑具有優點。特別地,在連續之纖維強化的結構體組件之領域中,預浸技術,因為被樹脂基質潤濕的纖維之品質極佳,使得組件的機械品質極高,所以多年前就已經在航空工業中建立了預浸技術作為製造複合組件之最重要的加工方法。但是,纖維產品半成品,因其本質,為二維片狀結構體,此的確限制了其於具有受限的幾
何複雜性之基本上二維或三維組件(例如翼或尾組合組件)之產製上的應用。預浸技術亦為製造風車的轉子葉片中之已有的程序。
相較之下,藉RTM方法製造具有高複雜度的三維幾何形狀之連續纖維強化的複合組件。此方法之特徵在於先自織物製得所謂近淨形預製件(near net shape preforms)。此含括將未經樹脂預浸的產品(如,所供應的梭織品、無緯紗布、非梭織品等)預製成近淨形形式的三維結構體且同時結合個別積層以固定,或將其縫合(在零件特別複雜的情況中)。此純纖維預製件之後引至腔中,在密封的腔(例如,受熱的鋼模具)中,以無溶劑的液態樹脂調合物浸漬且,在密封的腔中,立刻充分固化以提供最終階段(單階段方法)。流動幾何形狀之發生,其中的一些具有高複雜度,低黏度樹脂須具有長擱置壽命以便能夠有效地潤濕所有的纖絲。據此,用於此目的之樹脂系統具低反應性且於高溫所須的硬化時間長。硬化之後,終組件經脫膜和必要時經進一步加工,例如去毛邊。
但是,在製造具有極大尺寸的組件(例如風車的轉子葉片)中或在製造小數量物件的原型(鋼模具過重和/或成本過高)中,上述的單階段RTM方法在技術上不可能或無法經濟地實行。開放式模製變體中所用的各種液態浸漬方法(真空浸漬方法,最大壓力1bar)述於,例如,F.Henning/E.Moeller "Handbuch Leichtbau"[輕質物建構手冊],Carl-Hanser-verlag,p.641。模具僅由下半部組成且
可,如同金屬材料,亦製自複合材料;在這些方法中,由待浸漬的強化纖維和任何其他預製組件或芯材所構成的結構體的頂部以真空膜密封。施以減低的壓力製造不超過1bar的壓力差,此為浸漬法中所用的樹脂系統必須具有極低濃度和長加工時間的原因。基本上,因為壓力差小,所以在製造大型零件中之流動路徑長且流動速率低。
已經知道適用於此目的之低反應性之無溶劑的環氧樹脂組成物,例如具有來自Hexion的EPIKURETM Curing Agent MGSTM RIMH233,RIMH235-237之EPIKOTETM Resin MGSTM RIMR235樹脂系統。
文件DE 2640408、DE 2640409、DE 2540410、DE 2950067和DE 3328134描述2,2,6,6-四甲基-4-哌啶胺(三丙酮二胺或簡稱TAD)作為用於硬化環氧樹脂的潛伏性胺。文中所述之可能的應用是表面塗料,特別是粉末塗料,但亦可任意地為經纖維或其他物質強化的模製組成物。例子包括純TAD和環氧樹脂之組合。但是,這些系統排除在熱條件下硬化且無法用於70至80℃的硬化溫度,但這些條件為開放式模製方法中製造大型零件(例如,風車的轉子葉片)的標準條件。
不僅以選擇的樹脂基質和強化纖維的性質變化界定複合物件的性能,而是極特別地亦以纖維-基質複
合物件的品質界定。高複合物件品質要求樹脂基質無誤地潤濕所有的強化纖維。在製造非常大型的零件(例如風車的轉子葉片)中,樹脂調合物必須克服在真空浸漬方法中之在不超過1bar壓力下的長流徑。額外的因素在於待浸漬的結構體,由強化纖維、預製零件和芯材所構成,常亦具有高壁厚及其複雜性。這些層必須被液態樹脂調合物完全穿透和潤濕且無缺陷。
就製造更高比例的再生能量之要求觀之,風車的轉子葉片之尺寸變得更大。因此,以上指定之慣用的環氧樹脂調合物趨近其可加工性的限制,且對於"開放"期間更長,即,低黏度的時間長得多且於這些低黏度可自由流動,以便以所須品質潤濕所有纖維,的環氧樹脂調合物有需求存在,但因為產能因素,所以其循環時間不能有任何明顯的提高,且在灌注期間內不能在樹脂儲槽(樹脂原料)中發展出高放熱溫度峰。
訝異地,已發現根據本發明之環氧樹脂組成物可在寬範圍內調整,使其符合較長加工時間的要求;例如,能夠將樹脂原料達到臨界溫度的時間提高40%及將樹脂原料達到1000mPas的黏度限制的時間提高12%。於70℃硬化使得玻璃轉變溫度70℃,轉化率95%,此符合用於轉子葉片的要求,例如根據GL(Germanischer Lloyd)。
根據本發明之環氧樹脂組成物,用於製造三維組件之有效率的液體浸漬程序,具有以下有利的性質:-低黏度,-用於對應於所須流徑的時間長度之低黏度得以無誤地浸漬所有的纖維,-在選用的條件下,所有纖維在浸漬之後經充分硬化,以確保所須的產能,-未發展出放熱溫度峰,其會因為複合物件中的應力累積而導致樹脂系統開始破壞和/或裂開,-符合關於機械、熱和介質安定性的所有要求並具有良好的表面性質。
本發明提出一種環氧樹脂組成物,其包含:A)至少一種環氧化合物,和B)硬化劑組成物,其係由以下所組成:B1)5重量%至65重量%之至少一種以三丙酮二胺為基礎的多胺,和B2)35重量%至95重量%之至少一種其他的二胺和/或多胺,其中A)的環氧基與B)的官能基的活性氫原子數的化學計量比是由1:0.5至1:1.1,較佳地為1:0.6至1:1.05,
更佳地為1:0.95至1:1.05,C)任意的至少一種硬化加速劑,其中A)至C)的量總共為100重量%,D)任意的其他添加劑。
適當的組份A)是環氧化合物。適當的環氧化合物述於,例如,EP 675 185。
有用的化合物是許多種已知用於此目的且每個分子含有超過一個環氧基,較佳是兩個環氧基的化合物。這些環氧化合物可為飽和或不飽和且可為脂族、環脂族、芳族或雜環,且亦具有羥基。它們可以另含有不會在混合或反應條件下引發任何麻煩的副反應之取代基,例如烷基或芳基取代基、醚原子團等。它們較佳是自多羥基酚(特別是雙酚和清漆)衍生的環氧丙醚,且以環氧基數目ME計,其所具有的莫耳質量("環氧當量重","EV值")介於100和1500g/eq之間,但特別介於150和250g/eq之間。
多羥基酚的例子尤其包括:間苯二酚、氫醌、2,2-雙(4-羥基苯基)丙烷(雙酚A)、二羥基二苯基甲烷之異構物的混合物(雙酚F)、4,4’-二羥基二苯基環己烷、4,4’-二羥基-3,3’-二甲基二苯基丙烷、4,4’-二羥基聯苯、4,4’-二羥基二苯甲酮、雙(4-羥基苯基)-1,1-乙烷、雙(4-羥基苯基)-1,1-異丁烷、2,2-雙(4-羥基-三級丁基苯基)丙烷、
雙(2-羥基萘基)甲烷、1,5-二羥基萘、參(4-羥基苯基)甲烷、雙(4-羥基苯基)醚、雙(4-羥基苯基)碸、及前述化合物的氯化和溴化產物,例如四溴雙酚A。極特別佳的是使用以雙酚A和雙酚F為基礎之具有150至200g/eq的環氧當量之液態二環氧丙醚。
亦可能使用多元醇的多環氧丙醚,例如乙-1,2-二醇二環氧丙醚、丙-1,2-二醇二環氧丙醚、丙-1,3-二醇二環氧丙醚、丁二醇二環氧丙醚、戊二醇二環氧丙醚(包括異戊二醇二環氧丙醚)、己二醇二環氧丙醚、二乙二醇二環氧丙醚、二丙二醇二環氧丙醚、高碳聚氧烷二醇二環氧丙醚(例如高碳聚氧乙二醇二環氧丙醚和聚氧丙二醇二環氧丙醚)、共-聚環氧乙烷-丙二醇二環氧丙醚、聚氧丁二醇二環氧丙醚、甘油、己-1,2,6-三醇、三羥甲基丙烷、三羥甲基乙烷、季戊四醇或山梨糖醇的聚環氧丙醚、氧烷基化的多元醇(例如,尤其是甘油、三羥甲基丙烷、季戊四醇)的聚環氧丙醚、環己烷二甲醇、雙(4-羥基環己基)甲烷和2,2-雙(4-羥基環己基)丙烷的二環氧丙醚、蓖麻油的多環氧丙醚、參(2-羥基乙基)三聚異氰酸三環氧丙酯。
其他可用的組份A)包括:藉表氯醇和胺(例如苯胺、正丁胺、雙(4-胺基苯基)甲烷、間-伸苯二甲基二胺或雙(4-甲基胺基酚)甲烷)之反應產物的去氫鹵化可得的聚(N-環氧丙基)化合物。聚(N-環氧丙基)化合物尤其亦包括三聚異氰酸三環氧丙酯、三環氧丙基脲唑和其寡聚物、環伸烷基脲的N,N’-二環氧丙基衍生物及乙內醯胺的二環氧
丙基衍生物。
此外,也可以使用多元羧酸的多環氧丙酯,其可藉表氯醇或類似的環氧化合物與脂族、環脂族或芳族多元羧酸(例如草酸、丁二酸、己二酸、戊二酸、酞酸、對酞酸、四氫酞酸、六氫酞酸、萘-2,6-二羧酸)及高碳二羧酸二環氧丙酯(例如二聚合或三聚合的次亞麻油酸)之反應得到。例子為己二酸二環氧丙酯、酞酸二環氧丙酯和六氫酞酸二環氧丙酯。
另可提及的是不飽和羧酸的環氧丙酯以及不飽和醇或不飽和羧酸之環氧化的酯。除了聚環氧丙醚以外,可使用小量的單環氧化物(例如甲基環氧丙醚、丁基環氧丙醚、烯丙基環氧丙醚、乙基己基環氧丙醚)、長鏈脂族環氧丙醚(例如,鯨蠟基環氧丙醚和硬脂基環氧丙醚、高碳異構醇混合物之單環氧丙醚、C12至C13醇之混合物的環氧丙醚、苯基環氧丙醚、甲苯酚基環氧丙醚、對-三級丁基苯基環氧丙醚、對-辛基苯基環氧丙醚、對-苯基苯基環氧丙醚、烷氧化的月桂醇之環氧丙醚)、及單環氧化物(例如環氧化之單不飽和的烴(環氧丁烷、環氧己烷、苯乙烯化氧),以聚環氧丙醚質量計,其質量比率是至多30重量%,較佳是10重量%至20重量%。
適當之環氧化合物的詳細列舉可見於手冊"Epoxidverbindungen und Epoxidharze"[環氧化合物和環氧樹脂],M.Paquin,Springer Verlag,Berlin 1958,Chapter IV,及見於Lee Neville "Handbook of Epoxy Resins",1967,
Chapter 2。
有用的環氧化合物較佳地包括環氧丙醚和環氧丙酯、脂族環氧化物、以雙酚A和/或雙酚F為基礎的二環氧丙醚、及甲基丙烯酸環氧丙酯。此環氧化物的其他例子是三聚異氰酸三環氧丙酯(TGIC,商品名稱:ARALDIT 810,Huntsman)、對酞酸二環氧丙酯和苯偏三酸三環氧丙酯之混合物(商品名稱:ARALDIT PT 910和912,Huntsman)、新癸酸的環氧丙酯(商品名稱:CARDURA E10,Shell)、3’,4’-環氧基環己烷羧酸3,4-環氧基環己基甲酯(ECC)、乙基己基環氧丙醚、丁基環氧丙醚、季戊四醇基四環氧丙醚(商品名稱:POLYPOX R 16,UPPC AG)、及其他具有自由環氧基的Polypox產品。
也可以使用所提及之環氧化合物之混合物。
特別佳的環氧組份是以雙酚A二環氧丙醚、雙酚F二環氧丙醚、4,4’-伸甲基雙[N,N-雙(2,3-環氧基丙基)苯胺]、己二醇二環氧丙醚、丁二醇二環氧丙醚、三羥甲基丙烷三環氧丙醚、丙烷-1,2,3-三醇三環氧丙醚、季戊四醇四環氧丙醚和六氫酞酸二環氧丙酯為基礎的多元環氧化物。根據本發明,亦可較佳地使用這些環氧化合物之混合物作為組份A)。
組份A)的量係由組份B)之組成所主導並經計算使得A)的環氧基與B)的官能基的活性氫原子數的化學計量比是由1:0.5至1:1.1,較佳地為1:0.6至1:1.05,更佳地為1:0.95至1:1.05。此意謂每一個來自B)的胺基中
的氫原子與來自A)的一個環氧基反應。
以三丙酮二胺為基礎的多胺B1)為由文獻一般已知者。所用組份B1)較佳地為下列之以三丙酮二胺為基礎的多胺:2,2,6,6-四甲基-4-胺基哌啶(TAD)、伸己基雙(4-胺基-2,2,6,6-四甲基哌啶)、N-丁基-4-胺基-2,2,6,6-四甲基哌啶、N,N-二甲基胺基丙基-4-胺基-2,2,6,6-四甲基哌啶、N-丙基-4-胺基-2,2,6,6-四甲基哌啶、N-異丙基-4-胺基-2,2,6,6-四甲基哌啶、N-羥基乙基-4-胺基-2,2,6,6-四甲基哌啶、N-甲氧基乙基-4-胺基-2,2,6,6-四甲基哌啶、N-甲氧基乙基-4-胺基-2,2,6,6-四甲基哌啶、N’,N’-二甲基胺基乙基-4-胺基-2,2,6,6-四甲基哌啶、N-嗎啉基乙基-4-胺基-2,2,6,6-四甲基哌啶、N-哌基乙基-4-胺基-2,2,6,6-四甲基哌啶、4-嗎啉基-2,2,6,6-四甲基哌啶。
也可能使用以上之以三丙酮二胺為基礎的胺B1)之混合物。
較佳地,使用2,2,6,6-四甲基-4-胺基哌啶(TAD)和/或伸己基雙(4-胺基-2,2,6,6-四甲基哌啶)。
以B1)和B2)總量計,組份B1)的用量通常是
5重量%至65重量%,較佳地是25重量%至55重量%,更佳地是35重量%至45重量%。
適當的化合物B2)基本上是含有至少2個胺基的二胺和多胺。二胺和多胺亦可以與胺基醇或多硫醇混合使用。
二-或多胺B2)由文獻已知。這些可為單體、寡聚和/或聚合的化合物。單體和寡聚的化合物較佳地選自由二胺、三胺、四胺所組成之群組。二-或多胺B2)的胺基可連接至一級、二級或三級碳原子,較佳是連接至一級或二級碳原子。
所用組份B2)可為以下的胺,單獨或其混合物:‧脂族胺,例如聚伸烷基多胺,較佳選自伸乙基-1,2-二胺、伸丙基-1,2-二胺、伸丙基-1,3-二胺、伸丁基-1,2-二胺、伸丁基-1,3-二胺、伸丁基-1,4-二胺、2-(乙基胺基)乙胺、3-(甲基胺基)丙胺、二伸乙基三胺、三伸乙基四胺、五伸乙基六胺、三甲基己二胺、2,2,4-三甲基己二胺、2,4,4-三甲基己二胺、2-甲基戊二胺、己二胺、N-(2-胺基乙基)乙-1,2-二胺、N-(3-胺基丙基)丙-1,3-二胺、N,N”-1,2-乙二基雙(1,3-丙二胺)、二伸丙三胺、己二酸二醯聯胺(adipic dihydrazide)、聯胺;
‧氧伸烷基多胺,選自聚氧丙二胺和聚氧丙三胺(例如Jeffamine® D-230、Jeffamine® D-400、Jeffamine® T-403、Jeffamine® T-5000)、1,13-二胺基-4,7,10-三氧雜十三烷、4,7-二氧雜癸-1,10-二胺;‧環脂族胺,選自異佛爾酮二胺(3,5,5-三甲基-3-胺基甲基環己胺)、4,4’-二胺基二環己基甲烷、2,4’-二胺基二環己基甲烷和2,2’-二胺基二環己基甲烷,單獨或其異構物的混合物、3,3’-二甲基-4,4’-二胺基二環己基甲烷、N-環己基-1,3-丙二胺、1,2-二胺基環己烷、3-(環己基胺基)丙胺、哌、N-胺基乙基哌、TCD二胺(3(4),8(9)-雙(胺基甲基)三環[5.2.1.02,6]癸烷)、4-甲基環己烷-1,3-二胺;‧芳脂族胺,例如二甲苯二胺;‧芳族胺,選自苯二胺、苯-1,3-二胺、苯-1,4-二胺、4,4’-二胺基二苯基甲烷、2,4’-二胺基二苯基甲烷、2,2’-二胺基二苯基甲烷,單獨或異構物的混合物;‧加合物硬化劑,其為環氧化合物(特別是雙酚A和F的環氧丙醚)與過量的胺之反應產物;‧多醯胺基胺硬化劑,其藉單-和多羧酸與多胺之縮合反應得到,特別是藉脂肪酸二聚體與聚伸烷多胺之縮合反應得到;‧Mannich鹼硬化劑,其藉單-或多羥基酚與醛(特別是甲醛)和多胺之反應得到;
‧Mannich鹼,例如基於酚和/或甲酚、甲醛和間-二甲苯二胺,及N-胺基乙基哌及N-胺基乙基哌與壬基酚和/或苯甲醇之摻合物、苯基烷胺(其在Mannich反應中得自腰果酚、醛和胺)。
也可以使用以上的二-或多胺之混合物作為組份B2)。
較佳之用作為組份B2)的是二胺,選自異佛爾酮二胺(3,5,5-三甲基-3-胺基甲基環己胺,IPD)、4,4’-二胺基二環己基甲烷、2,4’-二胺基二環己基甲烷、2,2’-二胺基二環己基甲烷(亦以PACM表示),單獨或其異構物的混合物;氧伸烷基多胺,選自聚氧丙二胺和聚氧丙三胺的氧伸烷多胺;以環氧化合物和前述胺B2)或前述胺B2)之組合之反應產物為基礎之加合物硬化劑。也可使用這些化合物之混合物。
特別佳地,用作為B2)的是:異佛爾酮二胺(3,5,5-三甲基-3-胺基甲基環己胺,IPD),和/或異佛爾酮二胺和/或PACM(4,4’-、2,4’-和2,2’-二胺基二環己基甲烷之混合物)和聚氧丙二胺和/或聚氧丙三胺之組合,和/或以環氧化合物和前述胺B2)或前述胺B2)之組合之反應產物為基礎之加合物硬化劑。
極特別佳地,使用以下作為組份B2):a)異佛爾酮二胺(3,5,5-三甲基-3-胺基甲基環己胺,
IPD),b)和/或異佛爾酮二胺和聚氧丙二胺和/或聚氧丙三胺之組合,c)和/或以環氧化合物和前述胺B2)或前述胺B2)之組合之反應產物為基礎之加合物硬化劑。
b)中之組份的重量比,異佛爾酮二胺:聚氧丙二胺和/或聚氧丙三胺,通常是10:90至90:10,且較佳的重量比是20:80至40:60。
根據本發明,胺基醇可作為組份B2)中之混合物中的二胺和多胺以外的其他組份。胺基醇的例子包括單乙醇胺、3-胺基-1-丙醇、異丙醇胺、胺基乙氧基乙醇、N-(2-胺基乙基)乙醇胺、N-乙基乙醇胺、N-丁基乙醇胺、二乙醇胺、3-(羥基乙基胺基)-1-丙醇、異佛爾酮胺基醇和二異丙醇胺。胺基醇可以單獨或以二或更多種胺基醇與二-或多胺之混合物作為組份B2)。
根據本發明,多硫醇亦可作為組份B2)中之混合物中的二胺和多胺以外的其他組份。硫醇的例子包括乙硫醇、二硫蘇糖醇、二硫丁四醇、二硫甘醇酸甘油酯(glyceryl dithioglycolate)、二(巰基乙酸)乙二醇酯(glycol dimercaptoacetate)、三(羥基乙酸)三羥甲基丙烷酯(trimethylolpropane trimercaptoacetate)、四(羥基乙酸)季戊四醇酯、二(3-巰基丙酸)甘醇酯、三(3-巰基丙酸)三羥甲基丙烷酯、四(3-巰基丙酸)季戊四醇酯、六(3-巰基丙酸)二季戊四醇酯、乙氧化的三(3-巰基丙酸)三羥甲基丙烷
酯(產品名稱:Thiocure ETTMP 1300)、參[2-(3-巰基丙醯氧基)乙基]三聚異氰酸酯。其他硫醇述於,例如,EP394495A1、US4775733A1和WO2007096425A2。硫醇可以單獨或二或更多種硫醇一起與二-或多胺之混合物作為組份B2)。
除了所述二-和多胺以外,可使用二-和多胺和多酚一起作為組份B2)。這些的例子述於"Epoxy Resins-Chemistry and Technology;Curing Agents and Modifiers;p.481-482,2nd edition 1988"。多酚可以單獨或二或更多種多酚一起與二-或多胺之混合物作為組份B2)。
以B1)和B2)總量計,組份B2)的用量通常是35重量%至95重量%,較佳是45重量%至75重量%,更佳是55重量%至65重量%。
此外,可以任意地添加用於環氧基-胺反應之觸媒。適當的加速劑述於:H.Lee and K.Neville,Handbook of Epoxy Resins,McGraw-Hill,New York,1967。根據本發明,使用0.1重量%至10重量%,較佳是0.1重量%至5重量%,更佳是0.5重量%至2.0重量%的至少一種硬化加速劑。
適當的加速劑的例子是有機酸(例如水楊酸、二羥基苯甲酸、三羥基苯甲酸、甲基水楊酸、2-羥基-3-異丙基苯甲酸或羥基萘酸、乳酸和甘醇酸)、三級胺(如苄基
二甲胺(BDMA)、1,4-二氮雜雙環[2.2.2]辛烷(DABCO)、三乙胺、N,N’-二甲基哌或胺基乙基哌(AEP))、羥基胺(例如二甲基胺基甲酚、雙(二甲基胺基甲基)酚、2,4,6-參(二甲基胺基甲基)酚(Ancamine K54))、糖醛酸(例如3-(4-氯苯基)-1,1-二甲基脲(滅草隆(monuron))、3-(3,4-二氯苯基)-1,1-二甲基脲(敵草隆(diuron))、3-苯基-1,1-二甲基脲(非草隆(fenuron))、3-(3-氯-4-甲基苯基)-1,1-二甲基脲(綠麥隆(chlortoluron))、四烷基胍啶(例如N,N,N’,N’-四甲基胍啶(TMG))、咪唑和咪唑衍生物(例如1H-咪唑、1-甲基咪唑、2-甲基咪唑、1-苄基-2-甲基咪唑、2-乙基-4-甲基咪唑、2-苯基咪唑、2-苯基-4-甲基咪唑、1-乙烯基咪唑、1-(2-羥基乙基)咪唑、1,2-二甲基咪唑、1-氰基乙基咪唑和其適當的鹽、酚和酚衍生物(例如三級丁基酚、壬酚、雙酚A或雙酚F)、和有機或無機鹽及錯合物(例如溴化甲基三苯基鏻、硝酸鈣(Accelerator 3130)、或Mg、Ca、Zn和Sn的羧酸鹽、磺酸鹽、磷酸鹽、硫酸鹽、四氟硼酸鹽或硝酸鹽。特別佳的是三級胺。
本發明之組成物可任意地包含添加劑。瞭解添加劑是指通常添加用以使得環氧組成物的性質朝最終應用的所欲方向(例如符合黏度、潤濕特性、安定性、反應速率、起泡形成、儲存性或黏著性)及使用性質改變的物質。適當的添加劑述於,例如,WO 99/55772,p.15-25,
及述於"Plastics Additives,R.Gächter and H.Müller,Hanser Publishers 1983"。這些可加至組份A)或B)。例如,可添加光安定劑,例如立體受阻胺,或例如EP 669 353中所述的其他輔助劑,其添加總量為0.05重量%至5重量%。用於製造本發明之反應性組成物,另可添加添加劑,例如均化劑(例如聚矽氧)或黏著促進劑(例如以丙烯酸酯為基礎者)。此外,可以任意地再有其他組份存在。另外使用的輔助劑和添加劑可為鏈轉移劑、塑化劑、安定劑和/或抑制劑。此外,可添加染料、奈米尺寸填料、韌化劑(韌性改良劑)、脫模劑、阻燃劑、顏料、乾燥劑、潤濕劑、分散劑和均化輔助劑、黏著促進劑、UV安定劑、消泡劑和流變添加劑。
本發明亦提出環氧樹脂組成物於製造複合物件之用途,該組成物包含:A)至少一種環氧化合物,和B)硬化劑組成物,其係由下列所組成:B1)5重量%至65重量%之至少一種以三丙酮二胺為基礎的多胺,和B2)35重量%至95重量%之至少一種其他的二胺和/或多胺,其中A)的環氧基與B)的官能基的活性氫原子數的化學計量比是由1:0.5至1:1.1,較佳地為1:0.6至1:1.05,
更佳地為1:0.95至1:1.05,C)任意的至少一種硬化加速劑,其中A)至C)的量總共為100重量%,D)任意的其他添加劑。
本發明亦提出複合組件,其基本上係由下列所形成:1)至少一種纖維載體和任意的芯材,和2)一種環氧樹脂組成物,其包含:A)至少一種環氧化合物,和B)硬化劑組成物,其係由下列所組成:B1)5重量%至65重量%之至少一種以三丙酮二胺為基礎的多胺,和B2)35重量%至95重量%之至少一種其他的二胺和/或多胺,其中A)的環氧基與B)的官能基的活性氫原子數的化學計量比是由1:0.5至1:1.1,較佳地為1:0.6至1:1.05,更佳地為1:0.95至1:1.05,C)任意的至少一種硬化加速劑,其中A)至C)的量總共為100重量%,D)任意的其他添加劑。
根據本發明較佳使用之纖維載體材料之特徵在於纖維載體大部分由玻璃、碳、塑料(如聚醯胺(芳醯胺)或聚酯)、天然纖維、或礦物纖維材料(例如玄武纖維或陶瓷纖維),單獨或其混合物,或各種類型的多層層積物,所構成。
纖維載體為片狀織品結構體形式,其由非梭織品、針織品(包括迴圈形成的和迴圈牽引的針織品)、非針織結構(如梭織品、無緯紗布或交織品)、或長纖或短纖材料,單獨或各種類型的多層層積物形成。
詳細的執行方式如下:本發明中之纖維載體由纖維材料(通常亦稱為強化纖維)所組成。組成纖維的任何材料通常適用,但較佳是使用玻璃、碳、塑料(例如聚醯胺(芳醯胺)或聚酯)、天然纖維、或礦物纖維材料(例如玄武纖維)或陶瓷纖維(以氧化鋁和/或氧化矽為基礎的含氧纖維)製成。也可以使用纖維類型之混合物,例如梭織物與芳醯胺和玻璃纖維、或碳和玻璃纖維之組合。
主要是因為其相對低的成本,玻璃纖維是最常用的纖維類型。基本上,所有類型之以玻璃為基礎的強化纖維適用於此處(E玻璃、S玻璃、R玻璃、M玻璃、C玻璃、ECR玻璃、D玻璃、AR玻璃、或中空玻璃纖維)。
碳纖維通常用於高性能複合物件,另一重要的因素為相較於玻璃纖維之較低的密度及同時高強度。碳纖維是工業生產的纖維,其由含碳的起始物所構成,含碳
的起始物係藉熱解而被轉化成似石墨排列的碳。等向和各向異類型之間有差異:等向纖維僅具有低強度和較低的工業重要性;各向異纖維展現高強度和剛性且低的破裂拉長率。此處所謂的天然纖維是指自植物和動物材料(例如木纖維、纖維素纖維、棉纖維、大麻纖維、黃麻纖維、亞麻纖維、瓊麻纖維和竹纖維)得到的所有的織物纖維和纖維材料。類似於碳纖維,芳醯胺纖維展現負的熱膨脹係數,即在加熱時變短。其比強度和彈性模數顯著低於碳纖維所具有者。與正膨脹係數的基質樹脂合併,能製造高尺寸安定性的組件。相較於碳纖維強化的塑料,芳醯胺纖維複合物件的壓縮強度更低。芳醯胺纖維的已知品牌名稱有DuPont的Nomex®和Kevlar®,或Teijin的Teijinconex®、Twaron®和Technora®。特別適合和較佳的載體是由玻璃纖維、碳纖維、芳醯胺纖維或陶瓷纖維製造者。該纖維材料是片狀織品結構體。適當的材料是由非梭織品、針織品(包括形成的迴圈和迴圈牽引的針織品)、和非針織結構(如梭織品、無緯紗布或交織品)製成之片狀織品結構體。此外,作為載體的長纖和短纖材料之間有差異。根據本發明亦適用的是紗束和紗線。本發明的上下文中,所提及的所有材料適合作為纖維載體。強化纖維之回顧可見於“Composites Technologies“,Paolo Ermanni(Version 4),script for lecture at ETH Zürich,August 2007,Chapter 7。
適當的芯材是,例如,以經浸漬的紙、芳醯胺纖維或輕質金屬(例如鋁)為基礎的蜂巢構造、以輕質金屬或熱塑性或熱固性聚合物材料(例如聚胺甲酸酯、聚烯烴、聚苯乙烯、聚甲基丙烯醯亞胺(PMI)(例如Rohacell®)、酚系樹脂或氰酸酯樹脂)為基礎的發泡體、和木材(例如,巴沙木)。
本發明亦提出一種製造複合組件之方法,其係藉下列方法步驟:I.提供包含下列的組成物:A)至少一種環氧化合物,和B)硬化劑組成物,其係由下列所組成:B1)5重量%至65重量%之至少一種以三丙酮二胺為基礎的多胺,和B2)35重量%至95重量%之至少一種其他的二胺和/或多胺,其中A)的環氧基與B)的官能基的活性氫原子數的化學計量比是由1:0.5至1:1.1,較佳地為1:0.6至1:1.05,更佳地為1:0.95至1:1.05,C)任意的至少一種硬化加速劑,其中A)至C)的量總共為100重量%,D)任意的其他添加劑;II.將由纖維載體和任意的其他芯材所構成之結構體
以得自I.之組成物的形式浸漬,或藉液態樹脂浸漬法在模具中浸漬,或浸漬在心軸上的纖維載體和間隙,III.硬化此反應性組成物以提供複合組件,和IV.將最終組件自模具脫模。
本發明特別地亦提出根據本發明製得之複合物件的用途,其係用於造船和造艦、航空技術、汽車建構、雙輪載具(較佳是機車和自行車)、汽車、建築(例如管線)、船舶建造、醫藥技術和運動用品、電力和電子工業、及特別是能量產生設備(例如風車渦輪)。
更特別地,根據本發明之環氧組成物適用於製造風車的轉子葉片。
以下實例中所用的原料闡明於表1中。
以下實例中所用分析方法之描述
儀器:Rheotec Rheometer RC 30
測量系統:EWS30-CC25 DIN/FTK與MB30-CC25 DIN/FTK杯
用量:16g
溫度控制:Julabo F33-ME冷凍循環機
儀器:Yokogawa 4153 3-channel μP recorder
熱偶:NiCr-Ni -200℃至1370℃
用量:900g
溫度控制:Julabo F33-ME冷凍循環機
步驟:熱偶位於混合物中央與底部相距約1.5cm處。
以溫度-時間曲線記錄溫度。
儀器:Mettler DSC 1
參數:溫度-30至+250℃,加熱速率10K/min
玻璃轉變溫度(Tg)之測定:半高寬方法,midpoint DIN 51007
轉化率之測定:
在適當的攪拌槽中,製備由50g的Vestamin® IPD、100g的三丙酮二胺、100g的Jeffamine® D230、730g的D.E.R.351和80g的D.E.R.731所構成的混合物並以1200-1800rpm在Hauschild Speedmixer,型號DAC 600.1 VAC-P中充分混合。之後,以Rheotec RC30流變計於30℃等溫測定此環氧樹脂組成物的黏度之提高。此外,於23℃測定溫度之提高。此外,執行硬化篩選。就此目的,5g的環氧樹脂組成物稱入鋁盤(直徑50mm)中且此樣品在空氣循環乾燥箱中於70℃硬化6小時。之後,藉DSC(Mettler DSC 1 machine)測定轉化率和Tg。自-30至250℃的加熱速率是10K/min。所有結果示於表2。
以與實例1相同的方式,在適當的攪拌槽中,製備由75g的Vestamin® IPD、175g的Jeffamine® D230、718g的D.E.R.351和80g的D.E.R.731所構成之混合物並以1200-1800rpm在Hauschild Speedmixer,型號DAC 600.1 VAC-P中充分混合。此環氧樹脂組成物以與實例1相同的方式進行於30℃的黏度之提高和於23℃的溫度之提高的試驗,及硬化篩選。此調合物未展現Tg的良好演化,而是於30℃更快地達到1000mPas的黏
度並因此而具有較小的加工窗口。亦更迅速地到達儲槽中的臨界溫度,此將導致浸滲程序的過早中止。這些結果亦示於表2。
以與實例1相同的方式,在適當的攪拌槽中,製備由250g的三丙酮二胺、720g的D.E.R.351和80g的D.E.R.731所構成之混合物並以1200-1800rpm在Hauschild Speedmixer,型號DAC 600.1 VAC-P中充分混合。此環氧樹脂組成物以與實例1相同的方式進行於30℃的黏度之提高和於23℃的溫度之提高的試驗,及硬化篩選。此調合物未展現極寬的加工窗口(於30℃僅4小時之後就達到1000mPas),在樹脂儲槽中完全未發生相對高溫。但是,在於70℃硬化條件下的Tg演化完全無法令人滿意,因此,純粹以TAD為基礎的硬化劑組成物未能提供符合要求的成品組件。這些結果亦示於表2。
Claims (16)
- 一種環氧樹脂組成物,其包含:A)至少一種環氧化合物,和B)硬化劑組成物,其係由以下所組成:B1)5重量%至65重量%之至少一種以三丙酮二胺為基礎的多胺,和B2)35重量%至95重量%之至少一種其他的二胺和/或多胺,其中A)的環氧基與B)的官能基的活性氫原子數的化學計量比是由1:0.5至1:1.1,較佳地為1:0.6至1:1.05,更佳地為1:0.95至1:1.05,C)任意的至少一種硬化加速劑,其中A)至C)的量總共為100重量%,D)任意的其他添加劑。
- 如申請專利範圍第1項之環氧樹脂組成物,其中含有選自飽和、不飽和、脂族、環脂族、芳族和雜環狀環氧化合物之環氧化合物A),且這些環氧化合物亦具有羥基。
- 如申請專利範圍第2項之環氧樹脂組成物,其中含有選自下列的環氧化合物A):環氧丙醚、環氧丙酯、脂族環氧化物、以雙酚A和/或雙酚F為基礎之二環氧丙醚、甲基丙烯酸環氧丙酯。
- 如申請專利範圍第3項之環氧樹脂組成物,其中含有選自包含下列的群組之環氧化合物A):以雙酚A二環氧丙醚為基礎的環氧樹脂、以雙酚F二環氧丙醚為基礎的環氧樹脂、4,4’-伸甲基雙[N,N-雙(2,3-環氧基丙基)苯胺]、己二醇二環氧丙醚、丁二醇二環氧丙醚、三羥甲基丙烷三環氧丙醚、丙烷-1,2,3-三醇三環氧丙醚、季戊四醇四環氧丙醚、六氫酚酸二環氧丙酯、脂族或環脂族環氧樹脂類型。
- 如申請專利範圍第1項之環氧樹脂組成物,其中含有選自下列之以三丙酮二胺為基礎的多胺B1):2,2,6,6-四甲基-4-胺基哌啶(TAD)、伸己基雙(4-胺基-2,2,6,6-四甲基哌啶)、N-丁基-4-胺基-2,2,6,6-四甲基哌啶、N,N-二甲基胺基丙基-4-胺基-2,2,6,6-四甲基哌啶、N-丙基-4-胺基-2,2,6,6-四甲基哌啶、N-異丙基-4-胺基-2,2,6,6-四甲基哌啶、N-羥基乙基-4-胺基-2,2,6,6-四甲基哌啶、N-甲氧基乙基-4-胺基-2,2,6,6-四甲基哌啶、N-甲氧基乙基-4-胺基-2,2,6,6-四甲基哌啶、N’,N’-二甲基胺基乙基-4-胺基-2,2,6,6-四甲基哌啶、N-嗎啉基乙基-4-胺基-2,2,6,6-四甲基哌啶、N-哌基乙基-4-胺基-2,2,6,6-四甲基哌啶、4-嗎啉基-2,2,6,6-四甲基哌啶。
- 如申請專利範圍第1項之環氧樹脂組成物,其中含 有選自一級和/或二級二-和/或多胺之二-和/或多胺B2)。
- 如申請專利範圍第6項之環氧樹脂組成物,其中所用組份B2)包含以下的胺,單獨或其混合物:‧脂族胺,例如聚伸烷基多胺,較佳選自伸乙基-1,2-二胺、伸丙基-1,2-二胺、伸丙基-1,3-二胺、伸丁基-1,2-二胺、伸丁基-1,3-二胺、伸丁基-1,4-二胺、2-(乙基胺基)乙胺、3-(甲基胺基)丙胺、二伸乙基三胺、三伸乙基四胺、五伸乙基六胺、三甲基己二胺、2,2,4-三甲基己二胺、2,4,4-三甲基己二胺、2-甲基戊二胺、己二胺、N-(2-胺基乙基)乙-1,2-二胺、N-(3-胺基丙基)丙-1,3-二胺、N,N”-1,2-乙二基雙(1,3-丙二胺)、二伸丙三胺、己二酸二醯聯胺(adipic dihydrazide)、聯胺;‧氧伸烷基多胺,選自聚氧丙二胺和聚氧丙三胺(例如Jeffamine® D-230、Jeffamine® D-400、Jeffamine® T-403、Jeffamine® T-5000)、1,13-二胺基-4,7,10-三氧雜十三烷、4,7-二氧雜癸-1,10-二胺;‧環脂族胺,選自異佛爾酮二胺(3,5,5-三甲基-3-胺基甲基環己胺)、4,4’-二胺基二環己基甲烷、2,4’-二胺基二環己基甲烷和2,2’-二胺基二環己基甲烷,單獨或其異構物的混合物、3,3’-二甲基-4,4’-二胺基二環己基甲烷、N-環己基-1,3-丙二胺、1,2-二胺基環己烷、3-(環己基胺基)丙胺、哌、N-胺基乙 基哌、TCD二胺(3(4),8(9)-雙(胺基甲基)三環[5.2.1.02,6]癸烷)、4-甲基環己烷-1,3-二胺;‧芳脂族胺,例如二甲苯二胺;‧芳族胺,選自苯二胺、苯-1,3-二胺、苯-1,4-二胺、4,4’-二胺基二苯基甲烷、2,4’-二胺基二苯基甲烷、2,2’-二胺基二苯基甲烷,單獨或異構物的混合物;‧加合物硬化劑,其為環氧化合物(特別是雙酚A和F的環氧丙醚)與過量的胺之反應產物;‧多醯胺基胺硬化劑,其藉單-和多羧酸與多胺之縮合反應得到,特別是藉脂肪酸二聚體與聚伸烷多胺之縮合反應得到;‧Mannich鹼硬化劑,其藉單-或多羥基酚與醛(特別是甲醛)和多胺之反應得到;‧Mannich鹼,例如基於酚和/或甲酚、甲醛和間-二甲苯二胺,及N-胺基乙基哌及N-胺基乙基哌與壬基酚和/或苯甲醇之摻合物、苯基烷胺(其在Mannich反應中得自腰果酚、醛和胺)。
- 如申請專利範圍第7項之環氧樹脂組成物,其中含有選自下列的二-和/或多胺B2):異佛爾酮二胺、4,4’-二胺基二環己基甲烷、2,4’-二胺基二環己基甲烷、2,2’-二胺基二環己基甲烷(PACM),單獨或其異構物的混合物,選自聚氧丙二胺和/或聚氧丙三胺的氧伸烷多胺、以環氧化合物和前述胺B2)或前述胺B2)之組合之反應產物為基礎之加合物硬化劑。
- 如申請專利範圍第8項之環氧樹脂組成物,其中使用下列作為組份B2):異佛爾酮二胺(3,5,5-三甲基-3-胺基甲基環己胺,IPD)、和/或異佛爾酮二胺和/或PACM和聚氧丙二胺和/或聚氧丙三胺之組合和/或以環氧化合物和前述胺B2)或前述胺B2)之組合之反應產物為基礎之加合物硬化劑。
- 如申請專利範圍第9項之環氧樹脂組成物,其中使用以下作為組份B2):a)異佛爾酮二胺,b)和/或異佛爾酮二胺和聚氧丙二胺和/或聚氧丙三胺之組合,c)和/或以環氧化合物和前述胺B2)或前述胺B2)之組合之反應產物為基礎之加合物硬化劑。
- 如申請專利範圍第1項之環氧樹脂組成物,其中含有三級胺作為硬化加速劑C)。
- 一種如申請專利範圍第1至11項中任一項之環氧樹脂組成物於製造調合物之用途,該組成物包含:A)至少一種環氧化合物,和B)硬化劑組成物,其係由下列所組成:B1)5重量%至65重量%之至少一種以三丙酮二胺為基礎的多胺, 和B2)35重量%至95重量%之至少一種其他的二胺和/或多胺,其中A)的環氧基與B)的官能基的活性氫原子數的化學計量比是由1:0.5至1:1.1,較佳地為1:0.6至1:1.05,更佳地為1:0.95至1:1.05,C)任意的至少一種硬化加速劑,其中A)至C)的量總共為100重量%,D)任意的其他添加劑。
- 一種複合組件,其基本上係由下列所形成:1)至少一種纖維載體和任意的芯材,和2)如申請專利範圍第1至10項中任一項之環氧樹脂組成物,其包含:A)至少一種環氧化合物,和B)硬化劑組成物,其係由下列所組成:B1)5重量%至65重量%之至少一種以三丙酮二胺為基礎的多胺,和B2)35重量%至95重量%之至少一種其他的二胺和/或多胺,其中A)的環氧基與B)的官能基的活性氫原子數的化學計量比是由1:0.5至1:1.1,較佳地為1:0.6至1:1.05, 更佳地為1:0.95至1:1.05,C)任意的至少一種硬化加速劑,其中A)至C)的量總共為100重量%,D)任意的其他添加劑。
- 一種製造如申請專利範圍第13項之複合組件之方法,其係藉下列方法步驟:I.提供包含下列的組成物:A)至少一種環氧化合物,和B)硬化劑組成物,其係由下列所組成:B1)5重量%至65重量%之至少一種以三丙酮二胺為基礎的多胺,和B2)35重量%至95重量%之至少一種其他的二胺和/或多胺,其中A)的環氧基與B)的官能基的活性氫原子數的化學計量比是由1:0.5至1:1.1,較佳地為1:0.6至1:1.05,更佳地為1:0.95至1:1.05,C)任意的至少一種硬化加速劑,其中A)至C)的量總共為100重量%,D)任意的其他添加劑;II.將由纖維載體和任意的其他芯材所構成之結構體以得自I.之組成物的形式浸漬,或藉液態樹脂浸漬法在模具中浸漬,或浸漬在心軸上的纖維載 體和間隙,III.硬化此反應性組成物以提供複合組件,和IV.將最終組件自模具脫模。
- 如申請專利範圍第13或14項之複合組件的用途,其係用於造船和造艦、航空技術、汽車建構、雙輪載具(較佳是機車和自行車)、汽車、建築、醫藥技術和體育界、電力和電子工業、能量產生設備。
- 如申請專利範圍第13或14項之複合組件的用途,其係用於製造風車的轉子葉片。