TW201300507A - 紋理蝕刻液組成物及結晶矽晶圓紋理蝕刻方法 - Google Patents
紋理蝕刻液組成物及結晶矽晶圓紋理蝕刻方法 Download PDFInfo
- Publication number
- TW201300507A TW201300507A TW101120947A TW101120947A TW201300507A TW 201300507 A TW201300507 A TW 201300507A TW 101120947 A TW101120947 A TW 101120947A TW 101120947 A TW101120947 A TW 101120947A TW 201300507 A TW201300507 A TW 201300507A
- Authority
- TW
- Taiwan
- Prior art keywords
- composition
- compound
- group
- texture etching
- texture
- Prior art date
Abstract
揭露的是一種用於結晶矽晶圓的紋理蝕刻溶液組成物以及使用該紋理蝕刻溶液組成物的紋理蝕刻方法。用於結晶矽晶圓的紋理蝕刻溶液組成物包括鹼性化合物;環狀化合物;多醣;以及作為剩餘部分的水,以藉由改進該結晶矽晶圓表面上區域內的紋理均勻性而最大化陽光吸收的量,同時大大地降低光反射率,藉此高度增加光吸收功效。此外,該具創造性的紋理蝕刻溶液組成物可增加單位使用量將處理的晶圓片數,因此提升品質以及生產力,同時達到關於成本的經濟優勢。
Description
此申請案主張來自於2011年6月28日在韓國智慧財產局申請的韓國專利申請案編號10-2011-0062735的優先權,其全部揭露內容併入於本文中以作為參考。
本發明有關一種用於結晶矽晶圓的紋理蝕刻溶液組成物,能夠在該矽晶圓表面上的區域內最小化紋理品質偏差,以改進光吸收功效,以及一種紋理蝕刻方法。
本發明有關一種用於結晶矽晶圓的紋理蝕刻溶液組成物,能夠在該矽晶圓表面上的區域內最小化紋理品質偏差,以改進光吸收功效,以及一種紋理蝕刻方法。
近年來,太陽能電池已快速普及,且熟知為下個世代的能源以及直接轉換乾淨能量的電子裝置,也就是,將陽光轉成電。這種太陽能電池原則上具有包含矽以及硼加至其中的P型矽半導體,且包含PN接面半導體基板,其中原則上包含具有矽以及硼加至其中的P型矽半導體,以及藉由將磷(P)擴散入該P型矽半導體的表面而形成N型矽半導體層。
當光,例如陽光,照射具有由PN接面提供的電場的基板時,半導體中的電子(-)以及電洞(+)被激發,且這種激發的電子(-)以及電洞(+)可自由且隨機地在該半導體內移動。在此情況中,由該PN接面形成的電場內的電子(-)可移動至該N型半導體中,而該電洞(+)移動至該P型半導體。如果在該P型半導體以及該N型半導體的表面上都提供電極以將電子朝向外部電路流動,即產生電流。基於這種原理,陽光被轉換成電能。因此,為了改進陽光轉換效率,PN接面半導體基板的每單位區域的電輸出應被盡可能地增加,為了這種目的,在最大化光吸收度的同時必須減少反射率。考慮前述情況,構成PN接面半導體基板的用於太陽能電池的矽晶圓應具有形成在其表面上的微金字塔結構,且可提供有抗反射的薄膜。已被紋理化成微金字塔結構的矽晶圓表面可減少具有廣範圍波長的入射光的反射率,隨之增加吸收光的量。因此,太陽能電池的效能,也就是該太陽能電池的效率可被提高。
用於將矽晶圓表面紋理化成微金字塔結構的方法已被揭露,例如,美國專利編號4,137,123描述了一種矽紋理蝕刻溶液,其中將0.5至10重量%的矽溶解於非等向性蝕刻(常為「乾蝕刻」)溶液中,該等向性蝕刻溶液包含0至75體積%的乙二醇、0.05至50重量%的氫氧化鉀以及剩餘部分為水。然而,這種蝕刻溶液導致金字塔形成的失敗,因此增加了光反射率,並造成光吸收功效的降低。
此外,歐洲專利編號0477424提出了一種將氧進料至紋理蝕刻溶液的紋理蝕刻方法,也就是執行通氣過程達數分鐘,該紋理蝕刻溶液包括溶解於乙二醇、氫氧化鉀以及該剩餘部分為水的混合物中的矽。然而,上述蝕刻方法造成金字塔形成的失敗,隨之增加光反射率,同時降低光吸收功效,且此外,具有進一步需要替代性的通氣裝置的缺點。
此外,韓國專利註冊編號0180621揭露了一種紋理蝕刻溶液,該紋理蝕刻溶液包含0.5至5%的氫氧化鉀溶液、3至20體積%的異丙醇以及75至96.5體積%的去離子水的混合物;美國專利編號6,451,218揭露了一種包括鹼土金屬化合物、異丙醇、水性鹼性乙二醇以及水的紋理蝕刻溶液。然而,由於每種上述蝕刻溶液包括具有相對低沸點的異丙醇,且此材料必須在紋理化期間被額外導入,可能造成關於生產力與成本上的經濟不利。此外,該額外導入的異丙醇導致該蝕刻溶液的溫度梯度,因此在矽晶圓表面上的區域內增加了紋理品質的偏差,且最終降低均勻性。
當光,例如陽光,照射具有由PN接面提供的電場的基板時,半導體中的電子(-)以及電洞(+)被激發,且這種激發的電子(-)以及電洞(+)可自由且隨機地在該半導體內移動。在此情況中,由該PN接面形成的電場內的電子(-)可移動至該N型半導體中,而該電洞(+)移動至該P型半導體。如果在該P型半導體以及該N型半導體的表面上都提供電極以將電子朝向外部電路流動,即產生電流。基於這種原理,陽光被轉換成電能。因此,為了改進陽光轉換效率,PN接面半導體基板的每單位區域的電輸出應被盡可能地增加,為了這種目的,在最大化光吸收度的同時必須減少反射率。考慮前述情況,構成PN接面半導體基板的用於太陽能電池的矽晶圓應具有形成在其表面上的微金字塔結構,且可提供有抗反射的薄膜。已被紋理化成微金字塔結構的矽晶圓表面可減少具有廣範圍波長的入射光的反射率,隨之增加吸收光的量。因此,太陽能電池的效能,也就是該太陽能電池的效率可被提高。
用於將矽晶圓表面紋理化成微金字塔結構的方法已被揭露,例如,美國專利編號4,137,123描述了一種矽紋理蝕刻溶液,其中將0.5至10重量%的矽溶解於非等向性蝕刻(常為「乾蝕刻」)溶液中,該等向性蝕刻溶液包含0至75體積%的乙二醇、0.05至50重量%的氫氧化鉀以及剩餘部分為水。然而,這種蝕刻溶液導致金字塔形成的失敗,因此增加了光反射率,並造成光吸收功效的降低。
此外,歐洲專利編號0477424提出了一種將氧進料至紋理蝕刻溶液的紋理蝕刻方法,也就是執行通氣過程達數分鐘,該紋理蝕刻溶液包括溶解於乙二醇、氫氧化鉀以及該剩餘部分為水的混合物中的矽。然而,上述蝕刻方法造成金字塔形成的失敗,隨之增加光反射率,同時降低光吸收功效,且此外,具有進一步需要替代性的通氣裝置的缺點。
此外,韓國專利註冊編號0180621揭露了一種紋理蝕刻溶液,該紋理蝕刻溶液包含0.5至5%的氫氧化鉀溶液、3至20體積%的異丙醇以及75至96.5體積%的去離子水的混合物;美國專利編號6,451,218揭露了一種包括鹼土金屬化合物、異丙醇、水性鹼性乙二醇以及水的紋理蝕刻溶液。然而,由於每種上述蝕刻溶液包括具有相對低沸點的異丙醇,且此材料必須在紋理化期間被額外導入,可能造成關於生產力與成本上的經濟不利。此外,該額外導入的異丙醇導致該蝕刻溶液的溫度梯度,因此在矽晶圓表面上的區域內增加了紋理品質的偏差,且最終降低均勻性。
因此,本發明的目的是提供一種用於結晶矽晶圓的紋理蝕刻溶液組成物,能夠在區域內最小化紋理品質的偏差,以改進光吸收功效,同時增加對於單位使用量將處理的晶圓片數的數量。
本發明的另一個目的是提供一種用於結晶矽晶圓的紋理蝕刻溶液組成物,而不需應用通氣過程以及在紋理化期間導入額外的蝕刻溶液成分。
此外,本發明的更另一個目的是提供一種使用用於結晶矽晶圓的前述紋理蝕刻溶液組成物的紋理蝕刻方法。
為了完成上述目的,本發明提供下述。
(1)一種用於結晶矽晶圓的紋理蝕刻溶液組成物,包含:0.1至20重量%的鹼性化合物;0.1至50重量%的環狀化合物;10-9至0.5重量%的多醣;;以及作為剩餘部分的水。
(2)根據上述第(1)項所述的組成物,該鹼性化合物選自氫氧化鉀、氫氧化鈉、氫氧化銨、四羥甲基銨以及四羥乙基銨所組成的群組中的至少其中之一。
(3)根據上述第(1)項所述的組成物,該環狀化合物具有100℃或更高的沸點。
(4)根據上述第(3)項所述的組成物,該環狀化合物具有6 至15的Hansen溶解度參數(HSP)。
(5)根據上述第(1)項所述的組成物,該多醣選自聚葡萄糖化合物、聚果糖化合物、聚甘露糖化合物、聚半乳糖化合物以及其金屬鹽類所組成的群組中的至少其中之一。
(6)根據上述第(5)項所述的組成物,該多醣為至少一聚葡萄糖化合物,該聚葡萄糖化合物選自纖維素、二甲基胺基乙基纖維素、二乙基胺基乙基纖維素、乙基羥乙基纖維素、甲基羥乙基纖維素、4-胺基苄基纖維素、三乙基胺基乙基纖維素、氰基乙基纖維素、乙基纖維素、甲基纖維素、羧甲基纖維素、羧乙基纖維素、羥乙基纖維素、羥丙基纖維素、藻酸、直鏈澱粉、支鏈澱粉、果膠、澱粉、糊精、α-環糊精、β-環糊精、γ-環糊精、羥丙基-β-環糊精、甲基-β-環糊精、類糊精、類糊精硫酸鈉、皂素、肝糖、酵母聚糖、香菇多糖、裂褶菌多糖以及其金屬鹽類所組成的群組。
(7)根據上述第(5)項所述的組成物,該多醣具有5,000至1,000,000的中數分子量。
(8)根據上述第(1)項所述的組成物,該組成物更包含水溶性極性溶劑。
(9)根據上述第(8)項所述的組成物,該水溶性極性溶劑為選自乙二醇單甲醚、二乙二醇單甲醚、三乙二醇單甲醚、聚乙二醇單甲醚、乙二醇單乙醚、二乙二醇單乙醚、乙二醇單丁醚、二乙二醇單丁醚、三乙二醇單丁醚、聚丙二醇單甲醚、二聚丙二醇單甲醚、丙醇、丁醇、異丙醇、四氫呋喃甲醇、乙二醇、丙二醇、N-甲基甲醯胺、N,N-二甲基甲醯胺、二甲基亞碸、環丁碸、磷酸三乙酯以及磷酸三丁酯所組成的群組中的至少其中之一。
(10)根據上述第(8)項所述的組成物,相對於總100重量%的環狀化合物,該水溶性極性溶劑包括於0.1至30重量%的量。
(11)根據上述第(1)項所述的組成物,該組成物更包含選自脂肪酸以及其金屬鹽類所組成的群組中的至少其中之一。
(12)根據上述第(1)項所述的組成物,該組成物更包含至少一界面活性劑,該界面活性劑選自聚氧乙烯(POE)化合物、聚氧丙烯(POP)化合物以及其共聚物所組成的群組。
(13)根據上述第(1)項所述的組成物,該組成物更包含至少一二氧化矽化合物,該二氧化矽化合物選自:超細二氧化矽粉末;以Na2O穩定的矽溶膠溶液;以K2O穩定的矽溶膠溶液;以酸性溶液穩定的矽溶膠溶液;以NH3穩定的矽溶膠溶液;以至少一有機溶劑穩定的矽溶膠溶液,該有機溶劑選自乙醇、丙醇、乙二醇、丁酮以及甲基異丁酮所組成的群組;液體矽酸鈉;液體矽酸鉀;以及液體矽酸鋰所組成的群組。
(14)一種結晶矽晶圓的紋理蝕刻方法,包含:將該結晶矽晶圓浸沒於根據上述第(1)至(13)項任一項所述的紋理蝕刻溶液組成物中,噴灑該組成物,或將該組成物噴灑於該晶圓上時將該結晶矽晶圓浸沒於該組成物中。
(15)根據上述第(14)項所述的方法,該浸沒、噴灑或浸沒與噴灑是在50至100℃下進行30秒至60分鐘。
根據本發明用於結晶矽晶圓的紋理蝕刻溶液組成物以及紋理蝕刻方法,可最小化在該結晶矽晶圓表面上區域內的紋理品質偏差,以因此改進紋理均勻性。經由此,可最大化陽光吸收量,同時大大地減少光反射率,藉此大大地提高光吸收功效。
此外,相較於傳統的紋理蝕刻溶液組成物,本發明可增加單位使用量將處理的晶圓片數,且既不需要導入額外的蝕刻溶液成分,也不需在紋理化期間應用通氣設備,因此增強品質以及生產力,同時達成關於成本的經濟優勢。
本發明的另一個目的是提供一種用於結晶矽晶圓的紋理蝕刻溶液組成物,而不需應用通氣過程以及在紋理化期間導入額外的蝕刻溶液成分。
此外,本發明的更另一個目的是提供一種使用用於結晶矽晶圓的前述紋理蝕刻溶液組成物的紋理蝕刻方法。
為了完成上述目的,本發明提供下述。
(1)一種用於結晶矽晶圓的紋理蝕刻溶液組成物,包含:0.1至20重量%的鹼性化合物;0.1至50重量%的環狀化合物;10-9至0.5重量%的多醣;;以及作為剩餘部分的水。
(2)根據上述第(1)項所述的組成物,該鹼性化合物選自氫氧化鉀、氫氧化鈉、氫氧化銨、四羥甲基銨以及四羥乙基銨所組成的群組中的至少其中之一。
(3)根據上述第(1)項所述的組成物,該環狀化合物具有100℃或更高的沸點。
(4)根據上述第(3)項所述的組成物,該環狀化合物具有6 至15的Hansen溶解度參數(HSP)。
(5)根據上述第(1)項所述的組成物,該多醣選自聚葡萄糖化合物、聚果糖化合物、聚甘露糖化合物、聚半乳糖化合物以及其金屬鹽類所組成的群組中的至少其中之一。
(6)根據上述第(5)項所述的組成物,該多醣為至少一聚葡萄糖化合物,該聚葡萄糖化合物選自纖維素、二甲基胺基乙基纖維素、二乙基胺基乙基纖維素、乙基羥乙基纖維素、甲基羥乙基纖維素、4-胺基苄基纖維素、三乙基胺基乙基纖維素、氰基乙基纖維素、乙基纖維素、甲基纖維素、羧甲基纖維素、羧乙基纖維素、羥乙基纖維素、羥丙基纖維素、藻酸、直鏈澱粉、支鏈澱粉、果膠、澱粉、糊精、α-環糊精、β-環糊精、γ-環糊精、羥丙基-β-環糊精、甲基-β-環糊精、類糊精、類糊精硫酸鈉、皂素、肝糖、酵母聚糖、香菇多糖、裂褶菌多糖以及其金屬鹽類所組成的群組。
(7)根據上述第(5)項所述的組成物,該多醣具有5,000至1,000,000的中數分子量。
(8)根據上述第(1)項所述的組成物,該組成物更包含水溶性極性溶劑。
(9)根據上述第(8)項所述的組成物,該水溶性極性溶劑為選自乙二醇單甲醚、二乙二醇單甲醚、三乙二醇單甲醚、聚乙二醇單甲醚、乙二醇單乙醚、二乙二醇單乙醚、乙二醇單丁醚、二乙二醇單丁醚、三乙二醇單丁醚、聚丙二醇單甲醚、二聚丙二醇單甲醚、丙醇、丁醇、異丙醇、四氫呋喃甲醇、乙二醇、丙二醇、N-甲基甲醯胺、N,N-二甲基甲醯胺、二甲基亞碸、環丁碸、磷酸三乙酯以及磷酸三丁酯所組成的群組中的至少其中之一。
(10)根據上述第(8)項所述的組成物,相對於總100重量%的環狀化合物,該水溶性極性溶劑包括於0.1至30重量%的量。
(11)根據上述第(1)項所述的組成物,該組成物更包含選自脂肪酸以及其金屬鹽類所組成的群組中的至少其中之一。
(12)根據上述第(1)項所述的組成物,該組成物更包含至少一界面活性劑,該界面活性劑選自聚氧乙烯(POE)化合物、聚氧丙烯(POP)化合物以及其共聚物所組成的群組。
(13)根據上述第(1)項所述的組成物,該組成物更包含至少一二氧化矽化合物,該二氧化矽化合物選自:超細二氧化矽粉末;以Na2O穩定的矽溶膠溶液;以K2O穩定的矽溶膠溶液;以酸性溶液穩定的矽溶膠溶液;以NH3穩定的矽溶膠溶液;以至少一有機溶劑穩定的矽溶膠溶液,該有機溶劑選自乙醇、丙醇、乙二醇、丁酮以及甲基異丁酮所組成的群組;液體矽酸鈉;液體矽酸鉀;以及液體矽酸鋰所組成的群組。
(14)一種結晶矽晶圓的紋理蝕刻方法,包含:將該結晶矽晶圓浸沒於根據上述第(1)至(13)項任一項所述的紋理蝕刻溶液組成物中,噴灑該組成物,或將該組成物噴灑於該晶圓上時將該結晶矽晶圓浸沒於該組成物中。
(15)根據上述第(14)項所述的方法,該浸沒、噴灑或浸沒與噴灑是在50至100℃下進行30秒至60分鐘。
根據本發明用於結晶矽晶圓的紋理蝕刻溶液組成物以及紋理蝕刻方法,可最小化在該結晶矽晶圓表面上區域內的紋理品質偏差,以因此改進紋理均勻性。經由此,可最大化陽光吸收量,同時大大地減少光反射率,藉此大大地提高光吸收功效。
此外,相較於傳統的紋理蝕刻溶液組成物,本發明可增加單位使用量將處理的晶圓片數,且既不需要導入額外的蝕刻溶液成分,也不需在紋理化期間應用通氣設備,因此增強品質以及生產力,同時達成關於成本的經濟優勢。
本發明提供一種用於結晶矽晶圓的紋理蝕刻溶液組成物,以及此外,一種使用該紋理蝕刻溶液組成物的結晶矽晶圓紋理蝕刻方法。
在下文中,將給出下述描述以更具體地解釋本發明。
根據本發明用於結晶矽晶圓的紋理蝕刻溶液組成物可包含:具有最理想含量的鹼性化合物;環狀化合物;多醣;以及作為剩餘部分的水。
更特別的是,前述組成物包括0.1至20重量%的鹼性化合物;0.1至50重量%的環狀化合物;10-9至0.5重量%的多醣;以及作為剩餘部分的水。
該鹼性化合物是蝕刻結晶矽晶圓表面的成分,且該成分的種類不特別受限制。例如,使用了氫氧化鉀、氫氧化鈉、氫氧化銨、四羥甲基銨、四羥乙基銨,等等,且在這些之中,較佳使用氫氧化鉀或氫氧化鈉。這些化合物被單獨或以其二或更多個的組合而使用。
相對於總100重量%的用於結晶矽晶圓的理蝕刻溶液化合物,鹼性化合物可包括於0.1至20重量%的量,較佳為1至5重量%。當該鹼性化合物的含量在前述範圍內時,可進行蝕刻該矽晶圓的表面。
環狀化合物意指包括下述的化合物:具有4至10個碳原子的環狀碳氫化合物;及/或具有4至10個碳原子的雜環碳氫化合物,其含有至少一選自N、O或S的雜原子。該化合物可改進結晶矽晶圓表面的濕潤性,以預防被鹼性化合物過度蝕刻,因此最小化紋理品質的偏差,且同時快速地減少氫氣泡的量,隨之預防氣泡沾黏的發生。
同樣的,由於高沸點,相較於傳統使用的異丙醇,可使用相對小量的該化合物,且可增加以使用相同量化合物來處理的片數。
環狀化合物可具有100℃或更高的高沸點,更佳地,範圍為150至400℃。同時,較佳的是,在與蝕刻溶液組成物中所包括的其他成分具有相容性的方面,該環狀化合物具有6至15的Hansen溶解度參數(HSP)。
如果環狀化合物滿足前述沸點以及Hansen溶解度參數的範圍,該環狀化合物的種類不特別受限制,但可包括例如哌嗪、嗎啉、吡啶、哌啶、哌啶酮、吡咯啶、吡咯烷酮、咪唑啉酮、呋喃、苯胺、甲苯胺、胺、内酯、碳酸酯以及咔唑化合物。其特定的範例可包括哌嗪、N-甲基哌嗪、N-乙基哌嗪、N-乙烯基哌嗪、N-乙烯基甲基哌嗪、N-乙烯基乙基哌嗪、N-乙烯基-N’-甲基哌嗪、N-丙烯醯基哌嗪、N-丙烯醯基-N’-甲基哌嗪、羥基乙基哌嗪、N-(2-胺基乙基)哌嗪、N,N’-二甲基哌嗪、嗎啉、N-甲基嗎啉、N-乙基嗎啉、N-苯基嗎啉、N-乙烯基嗎啉、N-乙烯基甲基嗎啉、N- 丙烯醯基嗎啉、N-椰油基-嗎啉、N-(2-胺基乙基)嗎啉、N-(2-氰基乙基)嗎啉、N-(2-羥基乙基)嗎啉、N-(2-羥基丙基)嗎啉、N-乙醯基嗎啉、N-甲醯基嗎啉、N-甲基嗎啉-N-氧化物;甲基吡啶;N-甲基哌啶、3,5-二甲基哌啶、N-乙基哌啶、N-(2-羥基乙基)哌啶;N-乙烯基-哌啶酮、N-乙烯基甲基哌啶酮、N-乙烯基乙基哌啶酮、N-丙烯醯基哌啶酮、N-甲基-4-哌啶酮、N-乙烯基-2-哌啶酮;N-甲基吡咯啶、N-乙烯基吡咯啶、N-乙烯基甲基吡咯烷酮、N-乙烯基乙基-2-吡咯烷酮、N- 丙烯醯基吡咯烷酮、N-甲基吡咯烷酮、N-乙基-2-吡咯烷酮、N-異丙基-2-吡咯烷酮、N-丁基-2-吡咯烷酮、N-叔丁基-2-吡咯烷酮、N-己基-2-吡咯烷酮、N-辛基-2-吡咯烷酮、N-苄基-2-吡咯烷酮、N-環己基-2-吡咯烷酮、N-乙烯基-2-吡咯烷酮、N-(2-羥基乙基)-2-吡咯烷酮、N-(2-甲氧基乙基)-2-吡咯烷酮、N-(2-甲氧基丙基)-2-吡咯烷酮、N-(2-乙氧基乙基)-2-吡咯烷酮、己內醯胺;N-甲基咪唑啉酮、二甲基咪唑啉酮、N-(2-羥基乙基)-2-咪唑啉酮;四氫呋喃、四氫-2-呋喃甲醇;N-甲基苯胺、N-乙基苯胺、N,N-二甲基苯胺、N-(2-羥基乙基)苯胺、N,N-雙-(2-羥基乙基)苯胺、N-乙基-N-(2-羥基乙基)苯胺;N,N-二乙基-鄰-甲苯胺、N-乙基-N-(2-羥基乙基)-間-甲苯胺;二甲基苄基胺;γ-丁内酯、己内酯;碳酸乙烯酯、丙烯碳酸酯、N-乙烯基咔唑、N-丙烯醯基咔唑或諸如此類,其被單獨或與其二或更多個組合使用。
相對於總100重量%的用於結晶矽晶圓的紋理蝕刻溶液組成物,環狀化合物可包括於0.1至50重量%的量,較佳為,1至10重量%。如果該環狀化合物的含量在前述範圍內,可有效地改進該矽晶圓表面的濕潤性,以最小化紋理品質的偏差,並因此增強該紋理的均勻性。
環狀化合物可為與水溶性極性溶劑混合的化合物。
如果水溶性極性溶劑與用於結晶矽晶圓的蝕刻溶液組成物中所包括的其他成分以及水具有相容性,該水溶性極性溶劑的種類不特別受到限制,但可包括質子性極性溶劑或非質子性極性溶劑。
質子性極性溶劑可包括醚類化合物,例如乙二醇單甲醚、二乙二醇單甲醚、三乙二醇單甲醚、聚乙二醇單甲醚、乙二醇單乙醚、二乙二醇單乙醚、乙二醇單丁基乙醚、二乙二醇單丁基乙醚、三乙二醇單丁基乙醚、丙二醇單甲醚、二丙二醇單甲醚;醇類化合物,例如丙醇、丁醇、異丙醇、四氫呋喃甲醇、乙二醇、丙二醇。非質子性極性溶劑可包括醯胺化合物,例如 N-甲基甲醯胺、N,N-二甲基甲醯胺;亞碸化合物,例如二甲基亞碸、環丁碸;磷酸酯化合物,例如磷酸三乙酯以及磷酸三丁酯。這些化合物被單獨或與其二或更多個組合使用。
相對於總100重量%的環狀化合物,水溶性極性溶劑可包括於0.1至30重量%的量。
根據本發明用於結晶矽晶圓的紋理蝕刻溶液組成物可進一步包括具有理想含量的多醣。
多醣是包含二個或更多個單糖的糖類,以經由糖苷鍵結而形成大尺寸分子,防止過度蝕刻,並藉由使用鹼性化合物有效地控制蝕刻加速,以製備一致的微金字塔,同時快速地減少由蝕刻掉矽晶圓表面而產生的氫氣泡,藉此預防氣泡沾黏的發生。
多醣的範例可包括;聚葡萄糖化合物、聚果糖化合物、聚甘露糖化合物、聚半乳糖化合物以及其金屬鹽類。在這些之中,較佳使用聚葡萄糖化合物以及其金屬鹽類(例如,鹼性金屬鹽類)。可單獨或與其二個或更多個組合而使用前述物質。
聚葡萄糖化合物可包括,例如;纖維素、二甲基胺基乙基纖維素、二乙基胺基乙基纖維素、乙基羥乙基纖維素、甲基羥乙基纖維素、4-胺基苄基纖維素、三乙基胺基乙基纖維素、氰基乙基纖維素、乙基纖維素、甲基纖維素、羧甲基纖維素、羧乙基纖維素、羥乙基纖維素、羥丙基纖維素、藻酸、直鏈澱粉、支鏈澱粉、果膠、澱粉、糊精、α-環糊精、β-環糊精、γ-環糊精、羥丙基-β-環糊精、甲基-β-環糊精、類糊精、類糊精硫酸鈉、皂素、肝糖、酵母聚糖、香菇多糖、裂褶菌多糖以及其金屬鹽類。
多醣可具有5,000至1,000,000,以及較佳為50,000至200,000的分子量。
相對於100重量%的用於結晶矽晶圓的紋理蝕刻溶液組成物,多醣可包括於10-9至0.5重量%,以及較佳為10-6至0.1重量%的含量中。如果該多醣的含量在前述範圍內,可防止過度蝕刻,並可有效地控制蝕刻加速。當該含量超過0.5重量%時,當使用鹼性化合物時,蝕刻率可能會突然降低,導致形成想要微金字塔的困難。
根據本發明用於結晶矽晶圓的紋理蝕刻溶液組成物可進一步包括至少一添加物,該添加物選自脂肪酸以及其金屬鹽類所組成的群組;為聚氧乙烯(POE)化合物、聚氧丙烯(POP)化合物以及其共聚物其中之一的界面活性劑;以及二氧化矽化合物。
脂肪酸以及其金屬鹽類是與多醣一起使用的成分,以防止被鹼性化合物過度蝕刻,以製備一致的微金字塔,同時快速地減少由蝕刻掉矽晶圓表面而產生的氫氣泡,藉此防止氣泡沾黏的發生。
脂肪酸可為具有羧基的碳氫鏈的羧酸,具體而言可包括醋酸、丙酸、丁酸、戊酸、庚酸、辛酸、壬酸、癸酸、月桂酸、肉豆蔻酸、棕櫚酸、硬脂酸、花生酸、山萮酸、二十四酸、蠟酸、二十碳五烯酸、二十二碳六烯酸、亞麻油酸、α-亞麻油、γ-亞麻油、雙同-γ-亞麻油、花生油酸、油酸、反油酸、芥酸、二十四烯酸,或諸如此類。此外,該脂肪酸的金屬鹽類可包括酯類反應物,例如前述的酸以及NaOH或KOH。可單獨或與其二個或更多個組合使用前述物質。
相對於100重量%的用於結晶矽晶圓的紋理蝕刻溶液組成物,脂肪酸以及其金屬鹽類可包括於10-9至10重量%以及,較佳為10-6至1重量%的含量中。如果多醣的含量在前述範圍內,可有效地防止過度蝕刻。
具有羥基,例如聚氧乙烯(POE)化合物、聚氧丙烯(POP)化合物以及其共聚物,的界面活性劑可控制紋理蝕刻溶液組成物中氫氧根離子〔OH-〕的活性,以減少往以及Si111方向的蝕刻率差異,因此改進結晶矽晶圓表面的濕潤性,藉此快速地減少由蝕刻產生的氫氣泡量,以防止氣泡沾黏的發生。
聚氧乙烯(POE)界面活性劑可包括,例如,聚氧乙二醇、聚氧乙二醇甲醚、聚氧乙烯單烯丙基醚、聚氧乙烯新戊基醚、聚乙二醇單(三苯乙烯基苯基)醚、聚氧乙烯十六烷基醚、聚氧乙烯月桂醚、聚氧乙烯油烯基醚、聚氧乙烯硬脂醯基醚、聚氧乙烯十三烷基醚、聚氧乙烯癸基醚、聚氧乙烯辛基乙醚、聚氧乙烯雙酚-A乙醚、聚氧乙烯甘油醚、聚氧乙烯壬基苯基醚、聚氧乙烯苄基醚、聚氧乙烯苯基醚、聚氧乙烯辛基苯基醚、聚氧乙烯酚醚、提供有具有6至30個碳原子的烷基的聚氧乙烯烷基環己基醚、聚氧乙烯β-萘基醚、聚氧乙烯蓖麻油醚、聚氧乙烯氫化蓖麻油醚;聚氧乙烯月桂酯、聚氧乙烯硬脂醯基酯、聚氧乙烯油烯基酯;聚氧乙烯月桂基胺、聚氧乙烯硬脂醯基胺、聚氧乙烯牛脂胺,等等。此外,聚氧丙烯(POP)界面活性劑可為聚丙二醇。同樣地,可使用聚氧乙烯(POE)化合物以及聚氧丙烯(POP)化合物的共聚物,且包括,例如,聚氧乙烯-聚氧丙烯共聚物、聚氧乙烯-聚氧丙烯癸基醚共聚物、聚氧乙烯-聚氧丙烯十一烷基醚共聚物、聚氧乙烯-聚氧丙烯十二烷基醚共聚物、聚氧乙烯-聚氧丙烯十四烷基醚共聚物、聚氧乙烯-聚氧丙烯2-乙基己基醚共聚物、聚氧乙烯-聚氧丙烯月桂醚共聚物、聚氧乙烯-聚氧丙烯硬脂醯基醚共聚物、添加甘油的聚氧乙烯-聚氧丙烯共聚物、添加乙二胺的聚氧乙烯-聚氧丙烯共聚物或諸如此類。可單獨或以與其二個或更多個組合來使用這些材料。
相對於總100重量%的用於結晶矽晶圓的紋理蝕刻溶液組成物,選自聚氧乙烯(POE)化合物、聚氧丙烯(POP)化合物以及其共聚物所組成的群組的至少一界面活性劑可包括於10-9至10重量%,較佳為0.00001至0.1重量%,以及更佳為 10-6至1重量%的量中。如果該量在前述範圍內,可減少在紋理期間該矽晶圓表面上區域內的紋理品質偏差。
二氧化矽化合物可被物理上地吸附至結晶矽晶圓表面,並作為遮罩,因此使該矽晶圓表面能為微金字塔形式。
二氧化矽化合物可包括粉末狀的、膠體狀的溶液或液體金屬矽酸鹽化合物。更特別的是,超細二氧化矽粉末;以Na2O穩定的矽溶膠溶液;以K2O穩定的矽溶膠溶液;以酸性溶液穩定的矽溶膠溶液;以NH3穩定的矽溶膠溶液;以至少一有機溶劑穩定的矽溶膠溶液,該有機溶劑選自乙醇、丙醇、乙二醇、丁酮以及甲基異丁酮所組成的群組;液體矽酸鈉;液體矽酸鉀;液體矽酸鋰等等。可單獨或以其二個或更多個的組合而使用前述材料。
相對於總100重量%的用於結晶矽晶圓的紋理蝕刻溶液組成物,來包括二氧化矽化合物可包括於10-9至10重量%以及,較佳為,10-6至1重量%的量。如果該量在前述範圍內,可在該結晶矽晶圓表面上輕易地形成微金字塔。
用於結晶矽晶圓的紋理蝕刻溶液組成物可進一步包括組成物的總100重量%的作為剩餘部分的水。
水的類型不受特別的限制,然而,較佳為去離子水以及,更佳為,用於半導體製程、具有18MΩ /cm或更高特定電阻的去離子水。
除了環狀化合物之外,包含前述成分的根據本發明用於結晶矽晶圓的紋理蝕刻溶液組成物可包括理想含量的多醣,藉此在該結晶矽晶圓表面上的區域內最小化紋理品質偏差,並提升該紋理的均勻性。因此,陽光的吸收量被最大化,且光反射率被減少,因此增加了光吸收功效。此外,該具創造性的紋理蝕刻溶液組成物可增加單位使用量將處理的晶圓片數,且既不需導入額外的蝕刻溶液成分,也不需在紋理化期間應用通氣設備,因此達到極佳的生產力以及關於成本的經濟優勢。
根據本發明用於結晶矽晶圓的紋理蝕刻溶液組成物可被適當地使用在常用的蝕刻過程中,例如浸漬、噴灑、嵌入類型的蝕刻,等等。
本發明提供一種結晶矽晶圓的紋理蝕刻方法,使用上述用於結晶矽晶圓的紋理蝕刻溶液組成物。
結晶矽晶圓的紋理蝕刻方法可包括將該結晶矽晶圓浸沒於用於結晶矽晶圓的蝕刻溶液組成物中,噴灑該組成物,或將該結晶矽晶圓浸沒於其中時同時噴灑。
可不特別限制浸沒及/或噴灑的次數,在該浸沒以及噴灑同時執行的例子中,也可不限制其操作順序。
浸沒、噴灑或浸沒以及噴灑可在50至100℃進行30秒至60分鐘。
如上所述,根據本發明的結晶矽晶圓紋理蝕刻方法不需導入額外的通氣設備以供應氧氣,因此,在關於開始生產以及處理成本方面為經濟的,且即使藉由簡單的過程也能夠形成一致的微金字塔結構。
在下文中,將描述較佳的具體實施例,參照範例以及比較性範例而更具體地了解本發明。然而,對於本領域的技術人員而言,將顯而易見的是,這種具體實施例是提供用於說明的目的,且不悖離本發明的範圍以及精神的各種修飾以及改變是可能的,且如附帶申請專利範圍所定義的,這種修飾以及改變充分地包括在本發明中。
範例
範例1
藉由混合2重量%的氫氧化鉀(KOH)、4重量%的N-甲基嗎啉(NMM)、0.001重量%的藻酸以及作為剩餘部分的去離子水而製備用於結晶矽晶圓的紋理蝕刻溶液組成物。
範例2至25以及比較性範例1至4
除了使用列於下述表1中的基本成分以及其含量之外,執行與範例1中所描述的相同程序。這裡,該含量意指重量%。
在下文中,將給出下述描述以更具體地解釋本發明。
根據本發明用於結晶矽晶圓的紋理蝕刻溶液組成物可包含:具有最理想含量的鹼性化合物;環狀化合物;多醣;以及作為剩餘部分的水。
更特別的是,前述組成物包括0.1至20重量%的鹼性化合物;0.1至50重量%的環狀化合物;10-9至0.5重量%的多醣;以及作為剩餘部分的水。
該鹼性化合物是蝕刻結晶矽晶圓表面的成分,且該成分的種類不特別受限制。例如,使用了氫氧化鉀、氫氧化鈉、氫氧化銨、四羥甲基銨、四羥乙基銨,等等,且在這些之中,較佳使用氫氧化鉀或氫氧化鈉。這些化合物被單獨或以其二或更多個的組合而使用。
相對於總100重量%的用於結晶矽晶圓的理蝕刻溶液化合物,鹼性化合物可包括於0.1至20重量%的量,較佳為1至5重量%。當該鹼性化合物的含量在前述範圍內時,可進行蝕刻該矽晶圓的表面。
環狀化合物意指包括下述的化合物:具有4至10個碳原子的環狀碳氫化合物;及/或具有4至10個碳原子的雜環碳氫化合物,其含有至少一選自N、O或S的雜原子。該化合物可改進結晶矽晶圓表面的濕潤性,以預防被鹼性化合物過度蝕刻,因此最小化紋理品質的偏差,且同時快速地減少氫氣泡的量,隨之預防氣泡沾黏的發生。
同樣的,由於高沸點,相較於傳統使用的異丙醇,可使用相對小量的該化合物,且可增加以使用相同量化合物來處理的片數。
環狀化合物可具有100℃或更高的高沸點,更佳地,範圍為150至400℃。同時,較佳的是,在與蝕刻溶液組成物中所包括的其他成分具有相容性的方面,該環狀化合物具有6至15的Hansen溶解度參數(HSP)。
如果環狀化合物滿足前述沸點以及Hansen溶解度參數的範圍,該環狀化合物的種類不特別受限制,但可包括例如哌嗪、嗎啉、吡啶、哌啶、哌啶酮、吡咯啶、吡咯烷酮、咪唑啉酮、呋喃、苯胺、甲苯胺、胺、内酯、碳酸酯以及咔唑化合物。其特定的範例可包括哌嗪、N-甲基哌嗪、N-乙基哌嗪、N-乙烯基哌嗪、N-乙烯基甲基哌嗪、N-乙烯基乙基哌嗪、N-乙烯基-N’-甲基哌嗪、N-丙烯醯基哌嗪、N-丙烯醯基-N’-甲基哌嗪、羥基乙基哌嗪、N-(2-胺基乙基)哌嗪、N,N’-二甲基哌嗪、嗎啉、N-甲基嗎啉、N-乙基嗎啉、N-苯基嗎啉、N-乙烯基嗎啉、N-乙烯基甲基嗎啉、N- 丙烯醯基嗎啉、N-椰油基-嗎啉、N-(2-胺基乙基)嗎啉、N-(2-氰基乙基)嗎啉、N-(2-羥基乙基)嗎啉、N-(2-羥基丙基)嗎啉、N-乙醯基嗎啉、N-甲醯基嗎啉、N-甲基嗎啉-N-氧化物;甲基吡啶;N-甲基哌啶、3,5-二甲基哌啶、N-乙基哌啶、N-(2-羥基乙基)哌啶;N-乙烯基-哌啶酮、N-乙烯基甲基哌啶酮、N-乙烯基乙基哌啶酮、N-丙烯醯基哌啶酮、N-甲基-4-哌啶酮、N-乙烯基-2-哌啶酮;N-甲基吡咯啶、N-乙烯基吡咯啶、N-乙烯基甲基吡咯烷酮、N-乙烯基乙基-2-吡咯烷酮、N- 丙烯醯基吡咯烷酮、N-甲基吡咯烷酮、N-乙基-2-吡咯烷酮、N-異丙基-2-吡咯烷酮、N-丁基-2-吡咯烷酮、N-叔丁基-2-吡咯烷酮、N-己基-2-吡咯烷酮、N-辛基-2-吡咯烷酮、N-苄基-2-吡咯烷酮、N-環己基-2-吡咯烷酮、N-乙烯基-2-吡咯烷酮、N-(2-羥基乙基)-2-吡咯烷酮、N-(2-甲氧基乙基)-2-吡咯烷酮、N-(2-甲氧基丙基)-2-吡咯烷酮、N-(2-乙氧基乙基)-2-吡咯烷酮、己內醯胺;N-甲基咪唑啉酮、二甲基咪唑啉酮、N-(2-羥基乙基)-2-咪唑啉酮;四氫呋喃、四氫-2-呋喃甲醇;N-甲基苯胺、N-乙基苯胺、N,N-二甲基苯胺、N-(2-羥基乙基)苯胺、N,N-雙-(2-羥基乙基)苯胺、N-乙基-N-(2-羥基乙基)苯胺;N,N-二乙基-鄰-甲苯胺、N-乙基-N-(2-羥基乙基)-間-甲苯胺;二甲基苄基胺;γ-丁内酯、己内酯;碳酸乙烯酯、丙烯碳酸酯、N-乙烯基咔唑、N-丙烯醯基咔唑或諸如此類,其被單獨或與其二或更多個組合使用。
相對於總100重量%的用於結晶矽晶圓的紋理蝕刻溶液組成物,環狀化合物可包括於0.1至50重量%的量,較佳為,1至10重量%。如果該環狀化合物的含量在前述範圍內,可有效地改進該矽晶圓表面的濕潤性,以最小化紋理品質的偏差,並因此增強該紋理的均勻性。
環狀化合物可為與水溶性極性溶劑混合的化合物。
如果水溶性極性溶劑與用於結晶矽晶圓的蝕刻溶液組成物中所包括的其他成分以及水具有相容性,該水溶性極性溶劑的種類不特別受到限制,但可包括質子性極性溶劑或非質子性極性溶劑。
質子性極性溶劑可包括醚類化合物,例如乙二醇單甲醚、二乙二醇單甲醚、三乙二醇單甲醚、聚乙二醇單甲醚、乙二醇單乙醚、二乙二醇單乙醚、乙二醇單丁基乙醚、二乙二醇單丁基乙醚、三乙二醇單丁基乙醚、丙二醇單甲醚、二丙二醇單甲醚;醇類化合物,例如丙醇、丁醇、異丙醇、四氫呋喃甲醇、乙二醇、丙二醇。非質子性極性溶劑可包括醯胺化合物,例如 N-甲基甲醯胺、N,N-二甲基甲醯胺;亞碸化合物,例如二甲基亞碸、環丁碸;磷酸酯化合物,例如磷酸三乙酯以及磷酸三丁酯。這些化合物被單獨或與其二或更多個組合使用。
相對於總100重量%的環狀化合物,水溶性極性溶劑可包括於0.1至30重量%的量。
根據本發明用於結晶矽晶圓的紋理蝕刻溶液組成物可進一步包括具有理想含量的多醣。
多醣是包含二個或更多個單糖的糖類,以經由糖苷鍵結而形成大尺寸分子,防止過度蝕刻,並藉由使用鹼性化合物有效地控制蝕刻加速,以製備一致的微金字塔,同時快速地減少由蝕刻掉矽晶圓表面而產生的氫氣泡,藉此預防氣泡沾黏的發生。
多醣的範例可包括;聚葡萄糖化合物、聚果糖化合物、聚甘露糖化合物、聚半乳糖化合物以及其金屬鹽類。在這些之中,較佳使用聚葡萄糖化合物以及其金屬鹽類(例如,鹼性金屬鹽類)。可單獨或與其二個或更多個組合而使用前述物質。
聚葡萄糖化合物可包括,例如;纖維素、二甲基胺基乙基纖維素、二乙基胺基乙基纖維素、乙基羥乙基纖維素、甲基羥乙基纖維素、4-胺基苄基纖維素、三乙基胺基乙基纖維素、氰基乙基纖維素、乙基纖維素、甲基纖維素、羧甲基纖維素、羧乙基纖維素、羥乙基纖維素、羥丙基纖維素、藻酸、直鏈澱粉、支鏈澱粉、果膠、澱粉、糊精、α-環糊精、β-環糊精、γ-環糊精、羥丙基-β-環糊精、甲基-β-環糊精、類糊精、類糊精硫酸鈉、皂素、肝糖、酵母聚糖、香菇多糖、裂褶菌多糖以及其金屬鹽類。
多醣可具有5,000至1,000,000,以及較佳為50,000至200,000的分子量。
相對於100重量%的用於結晶矽晶圓的紋理蝕刻溶液組成物,多醣可包括於10-9至0.5重量%,以及較佳為10-6至0.1重量%的含量中。如果該多醣的含量在前述範圍內,可防止過度蝕刻,並可有效地控制蝕刻加速。當該含量超過0.5重量%時,當使用鹼性化合物時,蝕刻率可能會突然降低,導致形成想要微金字塔的困難。
根據本發明用於結晶矽晶圓的紋理蝕刻溶液組成物可進一步包括至少一添加物,該添加物選自脂肪酸以及其金屬鹽類所組成的群組;為聚氧乙烯(POE)化合物、聚氧丙烯(POP)化合物以及其共聚物其中之一的界面活性劑;以及二氧化矽化合物。
脂肪酸以及其金屬鹽類是與多醣一起使用的成分,以防止被鹼性化合物過度蝕刻,以製備一致的微金字塔,同時快速地減少由蝕刻掉矽晶圓表面而產生的氫氣泡,藉此防止氣泡沾黏的發生。
脂肪酸可為具有羧基的碳氫鏈的羧酸,具體而言可包括醋酸、丙酸、丁酸、戊酸、庚酸、辛酸、壬酸、癸酸、月桂酸、肉豆蔻酸、棕櫚酸、硬脂酸、花生酸、山萮酸、二十四酸、蠟酸、二十碳五烯酸、二十二碳六烯酸、亞麻油酸、α-亞麻油、γ-亞麻油、雙同-γ-亞麻油、花生油酸、油酸、反油酸、芥酸、二十四烯酸,或諸如此類。此外,該脂肪酸的金屬鹽類可包括酯類反應物,例如前述的酸以及NaOH或KOH。可單獨或與其二個或更多個組合使用前述物質。
相對於100重量%的用於結晶矽晶圓的紋理蝕刻溶液組成物,脂肪酸以及其金屬鹽類可包括於10-9至10重量%以及,較佳為10-6至1重量%的含量中。如果多醣的含量在前述範圍內,可有效地防止過度蝕刻。
具有羥基,例如聚氧乙烯(POE)化合物、聚氧丙烯(POP)化合物以及其共聚物,的界面活性劑可控制紋理蝕刻溶液組成物中氫氧根離子〔OH-〕的活性,以減少往以及Si111方向的蝕刻率差異,因此改進結晶矽晶圓表面的濕潤性,藉此快速地減少由蝕刻產生的氫氣泡量,以防止氣泡沾黏的發生。
聚氧乙烯(POE)界面活性劑可包括,例如,聚氧乙二醇、聚氧乙二醇甲醚、聚氧乙烯單烯丙基醚、聚氧乙烯新戊基醚、聚乙二醇單(三苯乙烯基苯基)醚、聚氧乙烯十六烷基醚、聚氧乙烯月桂醚、聚氧乙烯油烯基醚、聚氧乙烯硬脂醯基醚、聚氧乙烯十三烷基醚、聚氧乙烯癸基醚、聚氧乙烯辛基乙醚、聚氧乙烯雙酚-A乙醚、聚氧乙烯甘油醚、聚氧乙烯壬基苯基醚、聚氧乙烯苄基醚、聚氧乙烯苯基醚、聚氧乙烯辛基苯基醚、聚氧乙烯酚醚、提供有具有6至30個碳原子的烷基的聚氧乙烯烷基環己基醚、聚氧乙烯β-萘基醚、聚氧乙烯蓖麻油醚、聚氧乙烯氫化蓖麻油醚;聚氧乙烯月桂酯、聚氧乙烯硬脂醯基酯、聚氧乙烯油烯基酯;聚氧乙烯月桂基胺、聚氧乙烯硬脂醯基胺、聚氧乙烯牛脂胺,等等。此外,聚氧丙烯(POP)界面活性劑可為聚丙二醇。同樣地,可使用聚氧乙烯(POE)化合物以及聚氧丙烯(POP)化合物的共聚物,且包括,例如,聚氧乙烯-聚氧丙烯共聚物、聚氧乙烯-聚氧丙烯癸基醚共聚物、聚氧乙烯-聚氧丙烯十一烷基醚共聚物、聚氧乙烯-聚氧丙烯十二烷基醚共聚物、聚氧乙烯-聚氧丙烯十四烷基醚共聚物、聚氧乙烯-聚氧丙烯2-乙基己基醚共聚物、聚氧乙烯-聚氧丙烯月桂醚共聚物、聚氧乙烯-聚氧丙烯硬脂醯基醚共聚物、添加甘油的聚氧乙烯-聚氧丙烯共聚物、添加乙二胺的聚氧乙烯-聚氧丙烯共聚物或諸如此類。可單獨或以與其二個或更多個組合來使用這些材料。
相對於總100重量%的用於結晶矽晶圓的紋理蝕刻溶液組成物,選自聚氧乙烯(POE)化合物、聚氧丙烯(POP)化合物以及其共聚物所組成的群組的至少一界面活性劑可包括於10-9至10重量%,較佳為0.00001至0.1重量%,以及更佳為 10-6至1重量%的量中。如果該量在前述範圍內,可減少在紋理期間該矽晶圓表面上區域內的紋理品質偏差。
二氧化矽化合物可被物理上地吸附至結晶矽晶圓表面,並作為遮罩,因此使該矽晶圓表面能為微金字塔形式。
二氧化矽化合物可包括粉末狀的、膠體狀的溶液或液體金屬矽酸鹽化合物。更特別的是,超細二氧化矽粉末;以Na2O穩定的矽溶膠溶液;以K2O穩定的矽溶膠溶液;以酸性溶液穩定的矽溶膠溶液;以NH3穩定的矽溶膠溶液;以至少一有機溶劑穩定的矽溶膠溶液,該有機溶劑選自乙醇、丙醇、乙二醇、丁酮以及甲基異丁酮所組成的群組;液體矽酸鈉;液體矽酸鉀;液體矽酸鋰等等。可單獨或以其二個或更多個的組合而使用前述材料。
相對於總100重量%的用於結晶矽晶圓的紋理蝕刻溶液組成物,來包括二氧化矽化合物可包括於10-9至10重量%以及,較佳為,10-6至1重量%的量。如果該量在前述範圍內,可在該結晶矽晶圓表面上輕易地形成微金字塔。
用於結晶矽晶圓的紋理蝕刻溶液組成物可進一步包括組成物的總100重量%的作為剩餘部分的水。
水的類型不受特別的限制,然而,較佳為去離子水以及,更佳為,用於半導體製程、具有18MΩ /cm或更高特定電阻的去離子水。
除了環狀化合物之外,包含前述成分的根據本發明用於結晶矽晶圓的紋理蝕刻溶液組成物可包括理想含量的多醣,藉此在該結晶矽晶圓表面上的區域內最小化紋理品質偏差,並提升該紋理的均勻性。因此,陽光的吸收量被最大化,且光反射率被減少,因此增加了光吸收功效。此外,該具創造性的紋理蝕刻溶液組成物可增加單位使用量將處理的晶圓片數,且既不需導入額外的蝕刻溶液成分,也不需在紋理化期間應用通氣設備,因此達到極佳的生產力以及關於成本的經濟優勢。
根據本發明用於結晶矽晶圓的紋理蝕刻溶液組成物可被適當地使用在常用的蝕刻過程中,例如浸漬、噴灑、嵌入類型的蝕刻,等等。
本發明提供一種結晶矽晶圓的紋理蝕刻方法,使用上述用於結晶矽晶圓的紋理蝕刻溶液組成物。
結晶矽晶圓的紋理蝕刻方法可包括將該結晶矽晶圓浸沒於用於結晶矽晶圓的蝕刻溶液組成物中,噴灑該組成物,或將該結晶矽晶圓浸沒於其中時同時噴灑。
可不特別限制浸沒及/或噴灑的次數,在該浸沒以及噴灑同時執行的例子中,也可不限制其操作順序。
浸沒、噴灑或浸沒以及噴灑可在50至100℃進行30秒至60分鐘。
如上所述,根據本發明的結晶矽晶圓紋理蝕刻方法不需導入額外的通氣設備以供應氧氣,因此,在關於開始生產以及處理成本方面為經濟的,且即使藉由簡單的過程也能夠形成一致的微金字塔結構。
在下文中,將描述較佳的具體實施例,參照範例以及比較性範例而更具體地了解本發明。然而,對於本領域的技術人員而言,將顯而易見的是,這種具體實施例是提供用於說明的目的,且不悖離本發明的範圍以及精神的各種修飾以及改變是可能的,且如附帶申請專利範圍所定義的,這種修飾以及改變充分地包括在本發明中。
範例
範例1
藉由混合2重量%的氫氧化鉀(KOH)、4重量%的N-甲基嗎啉(NMM)、0.001重量%的藻酸以及作為剩餘部分的去離子水而製備用於結晶矽晶圓的紋理蝕刻溶液組成物。
範例2至25以及比較性範例1至4
除了使用列於下述表1中的基本成分以及其含量之外,執行與範例1中所描述的相同程序。這裡,該含量意指重量%。
比較性範例5
藉由混合1.5重量%的氫氧化鉀(KOH)、5重量%的異丙醇(IPA)以及作為剩餘部分的去離子水而製備用於結晶矽晶圓的紋理蝕刻溶液組成物。
比較性範例6
除了以乙二醇(EG)取代異丙醇(IPA)之外,已執行如比較性範例5中所描述的相同程序。
比較性範例7
除了以甲基二甘醇(MDG)取代異丙醇(IPA)之外,已執行如比較性範例5中所描述的相同程序。
比較性範例8
除了以單乙胺(MEA)取代異丙醇(IPA)之外,已執行如比較性範例5中所描述的相同程序。
示範性範例
藉由下述程序,將根據上述範例以及比較性範例的用於結晶矽晶圓的每個製備的紋理蝕刻溶液組成物進行紋理蝕刻效果的評估,其結果顯示於表2中:
將單晶矽晶圓基板於80℃下浸沒在用於單晶矽晶圓的製備紋理蝕刻溶液組成物達20分鐘。
(1)紋理均勻性
經由數位相機、3D光學顯微鏡以及掃瞄電子顯微鏡(SEM)來視覺觀察在紋理蝕刻之後獲得的單晶矽晶圓基板表面上形成的紋理偏差,也就是,均勻性,並根據下述標準來評估。
<評估標準>
◎–金字塔形成在整個晶圓基板。
○–金字塔不形成在部分的晶圓基板上(沒有金字塔的部分少於5%)。
△–金字塔不形成在部分的晶圓基板上(沒有金字塔的部分範圍為5至50%)。
× –金字塔不形成在大體上大部分的晶圓基板上(沒有金字塔的部分為90%或更多)。
(2)平均金字塔大小(μm)
使用掃瞄電子顯微鏡(SEM)測量在紋理蝕刻之後獲得的單晶矽晶圓基板表面上形成的每個微金字塔的大小。這裡,在測量單位面積上形成的每個微金字塔的大小之後,計算所測量大小的平均。
(3)平均反射率(%)
在具有波長範圍為400至800 nm的光射照在紋理蝕刻之後獲得的單晶矽晶圓基板表面上的例子中,使用UV光譜儀測量平均反射率。
[表2]
如表2中所示,在使用根據本發明範例1至33中製備的所任一紋理蝕刻溶液組成物進行紋理蝕刻的例子中,該紋理蝕刻溶液組成物包括鹼性化合物;環狀化合物;多醣;以及具有理想含量的作為剩餘部分的水,展示出單晶矽晶圓表面上微金字塔區域內的品質偏差被減少,因此確保極佳的均勻性,並減少光反射率,隨之改進光吸收功效。
第1圖是3D光學顯微鏡影像,顯示了在使用範例15中所製備的紋理蝕刻溶液組成物來紋理蝕刻之後獲得的結晶矽晶圓表面;以及第2圖是SEM照片,顯示如上述在紋理蝕刻之後獲得的結晶矽晶圓表面。從這些圖片,可確認微金字塔已被形成在整個晶圓表面,藉由增強紋理均勻性,同時減少品質上的偏差。
另一方面,當使用比較性範例1中所製備不含多醣的紋理蝕刻溶液組成物時,晶圓基板的外觀不佳,且有一部分沒有形成金字塔;以及發現到的是,在過量含有多醣的比較性範例2中的產物顯示了大大減少的蝕刻率,隨之增加了光反射率。此外,當使用比較性範例3中所製備不具環狀化合物的紋理蝕刻溶液組成物時,類似於比較性範例1,展現了呈現一部分不形成金字塔;以及發現由於難以控制蝕刻率,比較性範例4中過量含有環狀化合物的產物顯示了增加的光反射率。此外,關於比較性範例5中所製備的紋理蝕刻溶液組成物,由於該蝕刻溶液組成物中包括的異丙醇(IPA)的低沸點,在紋理化期間連續導入該組成物造成的溫度梯度已導致紋理失敗以及增加的成本。相較於範例,比較性範例6中的紋理蝕刻溶液組成物展現了關於紋理均勻性以及光反射率的相當惡化的特徵。比較性範例7以及8中的紋理蝕刻溶液組成物顯示了隨時間的自我改變,且溫度提升至紋理處理溫度。
雖然已參照較佳的具體實施例描述了本發明,相關技術領域的技術人員將了解的是,其中可做出各種修飾以及變化,而不悖離如附帶申請專利範圍所定義的本發明範圍。
無。
從下述詳細的描述結合伴隨的圖式,本發明的上述以及其他目標、特徵以及其他優勢將更清楚地被了解,其中:
第1圖是說明單晶矽晶圓表面的3D光學顯微鏡影像,該單晶矽晶圓藉由使用本發明範例11中所製備用於結晶矽晶圓的紋理蝕刻溶液組成物而紋理蝕刻;以及
第2圖是說明單晶矽晶圓表面的掃瞄電子顯微鏡(SEM)照片,該單晶矽晶圓藉由使用本發明範例11中所製備用於結晶矽晶圓的紋理蝕刻溶液組成物而紋理蝕刻。
第1圖是說明單晶矽晶圓表面的3D光學顯微鏡影像,該單晶矽晶圓藉由使用本發明範例11中所製備用於結晶矽晶圓的紋理蝕刻溶液組成物而紋理蝕刻;以及
第2圖是說明單晶矽晶圓表面的掃瞄電子顯微鏡(SEM)照片,該單晶矽晶圓藉由使用本發明範例11中所製備用於結晶矽晶圓的紋理蝕刻溶液組成物而紋理蝕刻。
無。
Claims (15)
- 一種用於一結晶矽晶圓的紋理蝕刻溶液組成物,包含:0.1至20重量%的一鹼性化合物;0.1至50重量%的一環狀化合物;10-9至0.5重量%的一多醣;以及作為剩餘部分的水。
- 如申請專利範圍第1項所述的組成物,其中該鹼性化合物是選自氫氧化鉀、氫氧化鈉、氫氧化銨、四羥甲基銨以及四羥乙基銨所組成的群組的至少其中之一。
- 如申請專利範圍第1項所述的組成物,其中該環狀化合物具有100℃或更高的一沸點。
- 如申請專利範圍第3項所述的組成物,其中該環狀化合物具有6至15的一Hansen溶解度參數(HSP)。
- 如申請專利範圍第1項所述的組成物,其中該多醣是選自一聚葡萄糖化合物、一聚果糖化合物、一聚甘露糖化合物、一聚半乳糖化合物以及其金屬鹽類所組成的群組的至少其中之一。
- 如申請專利範圍第5項所述的組成物,其中該多醣是至少一聚葡萄糖化合物,該聚葡萄糖化合物選自纖維素、二甲基胺基乙基纖維素、二乙基胺基乙基纖維素、乙基羥乙基纖維素、甲基羥乙基纖維素、4-胺基苄基纖維素、三乙基胺基乙基纖維素、氰基乙基纖維素、乙基纖維素、甲基纖維素、羧甲基纖維素、羧乙基纖維素、羥乙基纖維素、羥丙基纖維素、藻酸、直鏈澱粉、支鏈澱粉、果膠、澱粉、糊精、α-環糊精、β-環糊精、γ-環糊精、羥丙基-β-環糊精、甲基-β-環糊精、類糊精、類糊精硫酸鈉、皂素、肝糖、酵母聚糖、香菇多糖、裂褶菌多糖以及其金屬鹽類所組成的群組。
- 如申請專利範圍第5項所述的組成物,其中該多醣具有5,000至1,000,000的一中數分子量。
- 如申請專利範圍第1項所述的組成物,該組成物更包含一水溶性極性溶劑。
- 如申請專利範圍第8項所述的組成物,該水溶性極性溶劑為選自乙二醇單甲醚、二乙二醇單甲醚、三乙二醇單甲醚、聚乙二醇單甲醚、乙二醇單乙醚、二乙二醇單乙醚、乙二醇單丁醚、二乙二醇單丁醚、三乙二醇單丁醚、聚丙二醇單甲醚、二聚丙二醇單甲醚、丙醇、丁醇、異丙醇、四氫呋喃甲醇、乙二醇、丙二醇、N-甲基甲醯胺、N,N-二甲基甲醯胺、二甲基亞碸、環丁碸、磷酸三乙酯以及磷酸三丁酯所組成的群組中的至少其中之一。
- 如申請專利範圍第8項所述的組成物,相對於總100重量%的該環狀化合物,該水溶性極性溶劑包括於0.1至30重量%的量。
- 如申請專利範圍第1項所述的組成物,其中該組成物更包含選自脂肪酸以及其金屬鹽類所組成的群組的至少其中之一。
- 如申請專利範圍第1項所述的組成物,其中該組成物更包含至少一界面活性劑,該界面活性劑選自一聚氧乙烯(POE)化合物、一聚氧丙烯(POP)化合物以及其共聚物所組成的群組。
- 如申請專利範圍第1項所述的組成物,其中該組成物更包含至少一二氧化矽化合物,該二氧化矽化合物選自:超細二氧化矽粉末;以Na2O穩定的一矽溶膠溶液;以K2O穩定的一矽溶膠溶液;以一酸性溶液穩定的一矽溶膠溶液;以NH3穩定的一矽溶膠溶液;以至少一有機溶劑穩定的一矽溶膠溶液,該有機溶劑選自乙醇、丙醇、乙二醇、丁酮以及甲基異丁酮所組成的群組;液體矽酸鈉;液體矽酸鉀;以及液體矽酸鋰所組成的群組。
- 一種一結晶矽晶圓的紋理蝕刻方法,包含:將該結晶矽晶圓浸沒於如申請專利範圍第1至13項任一所述的紋理蝕刻溶液組成物中,噴灑該組成物,或將該結晶矽晶圓浸沒於該組成物中同時將該組成物噴灑在該晶圓上。
- 如申請專利範圍第14項所述的方法,其中該浸沒、噴灑、或浸沒以及噴灑是在50至100℃下進行30秒至60分鐘。