TW200524986A - Multifunctional acrylate oligomers as pigment grinding vehicles for radiation-curable ink applications - Google Patents
Multifunctional acrylate oligomers as pigment grinding vehicles for radiation-curable ink applications Download PDFInfo
- Publication number
- TW200524986A TW200524986A TW93130996A TW93130996A TW200524986A TW 200524986 A TW200524986 A TW 200524986A TW 93130996 A TW93130996 A TW 93130996A TW 93130996 A TW93130996 A TW 93130996A TW 200524986 A TW200524986 A TW 200524986A
- Authority
- TW
- Taiwan
- Prior art keywords
- michael
- pigment
- resin
- patent application
- diacrylate
- Prior art date
Description
200524986 九、發明說明: 【發明所屬之技術領域】 [0001】本發明大體上係有關於紫外線固化油墨之顏料 分散體’本發明特別地有關於邁克爾加成之聚丙烯酸酯 樹脂,與製自這些樹脂之顏料分散體。 【先前技術】 【0002】對於環境考量之日益重視是於印刷與繪畫藝術 工業中敦促使用能量固化性油墨技術之推動力,能量固 化性油墨包括紫外光(紫外線固化性)與電子束輻射(電子 束固化性)油墨。達成良好性能之紫外線油墨,其與系統 之最終流變具有非常密切的關聯,流變係經由潤溼顏料 表面時’載劑所擁有之構像決定。顏料於油墨配方中穩 定的分散、印刷機上良好的油墨流動與移轉、與隨後之 顏色強度,皆取決於顏料之潤溼。 [0003】顏料之潤澄可敘述為一種黏結劑與顏料之間的 化學相互作用,其有助於防止絮凝程序,並可強化印刷 油墨之顏色。一個良好潤溼系統之流變優點為:良好的流 動特性、低的整體油墨黏度、高度的光澤、與適宜的顯 色。紫外線固化性寡聚物已有商品,但是以習知寡聚物 為基質之油墨,不利地需要大量的各種光引發劑以確保 可接受之光固化。傳統的光引發劑(如··二苯甲酮)可為含 毒性、價昂、有惡臭,並可能使薄膜具有顏色,此可限 制其應用性,通常會使其不適合用於白色與淺色的油墨。
[0004】藉使用敘述於專利仍5,945,489與US 200524986 6,025,410(皆屬於Ashland公司)中之丙烯酸酯寡聚物技 術,油墨配方中外在光引發劑之數量可大幅地減少。這 些專利揭示:經由石-二叛基化合物與多官能丙烯酸酯進 行邁克爾加成反應製得之未交聯樹脂。揭示於此之發明 顯示:單獨地使用這些未交聯樹脂,或使用藉與其他物料 反應與/或摻合之經修飾者,有利於不同顏色顏料之研 磨。這些其他的物料包括:各種丙烯酸單體與募聚物、一 級、二級、與三級胺、酸官能之物料、分散劑、顏料潤 溼助劑、與其他,藉以強化顏料之潤溼性能。獲得之顏 料分散體可與適合的基於相同邁克爾加成樹脂技術之寡 聚物稀釋,藉以獲得紫外線固化之網印、膠印、喷墨、 與石印油墨。 / 、 [0005】於此敘述之本發明包括一族用於輻射固化性印 刷油墨應用之顏料分散體,這些分散體之基質為多官能 丙烯酸醋樹脂,係由丙烯酸醋單體及寡聚物與下者進行 反應生成酮酯(如:乙醯乙酸酯)、二酮(如:2,4_戊二 (如:乙醯乙醯苯胺、乙酿乙酿胺)、與/或 ::二:f基:或可參與邁克爾加成反應之邁克爾”供 ㈣#ί/勿’併同各種有機與無機顏料。這些顏料分散 重要新穎性為:以其為基質之油墨可於標準 ===條件下固化,相較於需要添加大量光引發 劑商業配方’使用非常少的傳統光引發劑。 [:〇:”本發明中用作顏料研磨载=官能聚丙烯 酸酉日养聚物具有雙化學官炉 ’亦即:其同時具有丙烯酸 200524986 官能性與一不穩定的酮基團,其暴露於紫外線輻射下能 夠分解而使寡聚物引發自由基聚合反應。 [0007] 顏料潤溼與分散之性能可予修飾,經由各種方 法,包括:使用其他的或補充的丙烯酸酯物料、使用各種 石-二羰基邁克爾供予體化合物、或單純地藉改變組成寡 聚物之反應物之化學計量。以這些顏料分散體為基質之 油墨可經由化學方法、熱、或藉暴露於紫外線或電子束 輻射,予以固化。其他的物料,包括反應性(如:習知的聚 丙烯酸酯或丙烯酸化寡聚物)與非反應性(如:熱塑性聚丙 烯酸S旨,如:PMMA),亦可加至分散體配方中,以強化這 些樹脂之顏料潤溼特性,此類添加物包括,但非限制性: 各種丙烯酸單體與寡聚物、一級、二級、與三級胺、以 及酸官能之單體與寡聚物。 [0008】 包括傳統的單體與寡聚物之分散體系統,常具 有與某些前述添加物之相容性問題,給予配方化學家較 少的選擇。然而於此所述建構自新穎的光固化性邁克爾 加成樹脂之分散體,由於其合成中可能之化學/建構控 制,可添加近乎無限種類之添加物,因此,對於必須滿 足每種印刷應用特殊挑戰之配方人員,能有更多的選擇。 【發明内容】 [0009】本發明係藉提供一種用於顏料分散體之邁克爾 樹脂,以滿足這些經察覺之需求。此新穎的邁克爾分散 型樹脂包括許多共價結合之組份,每個組份,其可為一 單體的或寡聚的單元,供給至少一種特殊的官能,因此 200524986 可解決前述之難題,一個組份可供給多於一種官能。 【0010]本發明提供一種用於顏料分散體之邁克爾樹 脂,其包括一單體(或募聚物),其於樹脂合成中具有邁克 爾接受體之功能,此外,此組份提供侧邊的丙烯酸酯基 團,用以將樹脂交聯成熱固性。適合此功能之組份包括, 但非限制性:聚酯丙烯酸酯、環氧丙烯酸酯、胺基甲酸酯 丙稀酸酯、丙烯酸單體、與其混合物。 [0011】本發明提供一種用於顏料分散體之邁克爾樹 脂,其包括一單體(或寡聚物),其具有顏料潤溼之功能。 適合此功能之組份包括,但非限制性:聚酯丙烯酸酯、環 氧丙烯酸酯、胺基曱酸酯丙烯酸酯、丙烯酸單體、與其 混合物。 【0012】本發明提供一種用於顏料分散體之邁克爾樹 脂,其包括一單體(或寡聚物),其具有顏料分散體安定性 之功能。適合此功能之組份包括,但非限制性:烷氧化之 壬酴丙烯酸酯、聚酯丙烯酸酯、環氧丙烯酸酯、胺基甲 酸酯丙烯酸酯、丙烯酸單體、烷氧化之乙醯乙酸酯、與 其混合物。 [0013】本發明提供一種用於顏料分散體之邁克爾樹 脂,其包括一單體(或寡聚物),其具有黏度控制之功能。 適合此功能之組份包括’但非限制性:聚酯丙烯酸醋 '環 氧丙烯酸酯、胺基甲酸酯丙烯酸酯、丙烯酸單體、與其 混合物。此類組份特殊地包括:乙二醇二丙烯酸醋、丙二 醇二丙烯酸醋、二乙二醇二丙烯酸醋、二丙二醇二丙稀 200524986 酸酯(DPGDA)、三乙二醇二丙烯酸酯、三丙二醇二丙稀 酸酯、四乙二醇二丙烯酸酯、四丙二醇二丙烯酸酯、聚 乙二醇二丙浠酸酯、聚丙二醇二丙烯酸酯、乙氧化雙酴 A二丙烯酸酯、雙酚A二環氧丙醚二丙烯酸酯、間苯二 酚二環氧丙醚二丙烯酸酯、1,3-丙二醇二丙烯酸酯、1,4_ 丁二醇二丙烯酸酯、〖,5·戊二醇二丙烯酸酯、丨,^己二醇 二丙浠酸酯、新戊二醇二丙浠酸醋、環己燒二甲醇二丙 烯酸酯、乙氧化新戊二醇二丙烯酸酯、丙氧化新戊二醇 二丙烯酸酯、乙氧化環己烧二甲醇二丙稀酸酯、丙氧化 環己烧二曱醇二丙稀酸酯、芳基胺基甲酸酯二丙烯酸 酯、脂肪族胺基甲酸酯二丙烯酸酯、聚酯二丙烯酸酯、 丙三醇三丙烯酸酯、乙氧化三甲基醇丙烷三丙烯酸酯 (TMPEOTA)、丙氧化三甲基醇丙烷三丙烯酸酯、乙氧化 丙三醇三丙烯酸酯、丙氧化丙三醇三丙烯酸酯、季戊四 醇三丙烯酸酯、芳基胺基甲酸酯三丙烯酸酯、脂肪族胺 基甲酸酯三丙烯酸酯、蜜胺三丙烯酸酯、環氧酚醛清漆 三丙烯酸酯、脂肪族環氧三丙烯酸酯、聚酯三丙烯酸酯、 與其混合物、季戊四醇四丙烯酸酯、乙氧化季戊四醇四 丙烯酸酯、丙氧化季戊四醇四丙烯酸酯、二季戊四醇四 丙烯酸酯、乙氧化二季戊四醇四丙烯酸酯、丙氧化二季 戊四醇四丙烯酸酯、芳基胺基甲酸酯四丙烯酸酯、脂肪 族胺基曱酸酯四丙烯酸酯、蜜胺四丙烯酸酯、環氧酚醛 清漆四丙烯酸酯、聚酯四丙烯酸酯、與其混合物。 【0014】纟發明提供—種用於顏料分散體之邁克爾樹 .200524986 月曰,其包括一單體或寡聚物或組份,其具有對最終油黑 配方增強固化之功能。適合此功能之組份包括,但非ς 制性:胺·修飾之聚丙烯酸g旨,包括··胺·修錦之聚鱗、胺_ 修飾之聚酯、胺-修飾之環氧丙烯酸酯、與胺-修飾之胺基 甲酸酯丙烯酸酯、胺基丙稀酸酯、與其混合物。 =015】树明提供—種用於顏料分散體之邁克爾樹 脂,其包括-種組份’其具有邁克爾供予體之功能並提 供一種光不穩定發色團。適合此功能之組份包括,但非 限制性·•乙醯乙酸乙酯(EAA)、乙醯乙酸甲酯、2_乙基己 基乙醯乙酸g旨、乙醯乙酸月桂g旨、乙醢乙酸第三丁醋、 乙醯乙醯苯胺(AAA)、N·烧基乙酿乙醯苯胺、乙酿乙酿 胺、2-乙醯乙醯氧基乙基丙烯酸酯、2_乙醯乙醯氧基乙基 甲基丙烯酸酯、乙醯乙酸烯丙酯、 戊二明_)、2,4-己二明、3,5-庚二網、乙V二 丁酯、與2-甲氧基乙基乙醯乙酸酯(2_MEAA)、丨,4•丁二 醇二乙醯乙酸g旨、1,6·己二醇二乙醯乙酸酯、新戊二醇二 乙醢乙酸酯、環己烷二甲醇二乙醯乙酸酯、乙氧化雙酚 A二乙醯乙酸酯、三曱基醇丙烷三乙醯乙酸酯(ΤΜρτΑ)、 聚己内酯三乙醯乙酸酯、季戊四醇四乙醯乙酸酯、長鏈 烧氧化之乙酿乙酸醋、與其混合物。 [0016】本發明提供一種用於顏料分散體之邁克爾樹 脂,其包括至多約90重量份之一種具有顏料潤溼功能之 單體或寡聚物。 [0017】本發明提供一種用於顏料分散體之邁克爾樹 11 .200524986 脂,其包括至多約50重量份之一種具有顏料安定功能之 單體或寡聚物。 [0018] 本發明提供一種用於顏料分散體之邁克爾樹 脂,其包括至多約90重量份之一種具有黏度控制功能之 單體或寡聚物。 [0019】 本發明提供一種用於顏料分散體之邁克爾樹 脂,其包括至多約90重量份之一種具有對最終油墨配方 增強固化之功能之單體或寡聚物或組份。 [0020] 本發明提供一種用於顏料分散體之邁克爾樹 脂,其包括至多約40重量份之一組份,其具有邁克爾供 予體之功能並提供一種光不穩定發色團。 [0021] 本發明之一層面為提供一種邁克爾樹脂之顏料 分散體,其包括自約10重量份至約90重量份之一種邁 克爾分散型樹脂,與自約10重量份至約75重量份之一 種顏料。 [0022] 本發明之一層面為對樹脂設計提供控制,例如.· 一種具有極佳顏料潤溼性能之單一樹脂,其可作為研磨 不同顏色顏料之載劑。本發明之另一層面為對樹脂設計 提供控制,以使系統之流變可予特定,以適合個別的應 用。 [0023] 本發明之一層面為提供經修飾之樹脂,添加技 藝所習知之分子以賦予極佳的分散性能,藉以進一步輔 助顏料潤溼之特性。 [0024] 本發明之一層面為提供樹脂,其相較於習知之 12 200524986 分散載劑,容許大幅地減少分散顏料所需之時間。本發 明之另一層面為提供樹脂,其相較於習知以丙烯酸酯為 基質之顏料分散體載劑,可容許較高的顏料裝載量。 [0025] 前述以邁克爾加成樹脂為基質之顏料分散體, 可進一步配方以獲得油墨,其固化可使用所有典型地用 於交聯丙烯酸物料之方法。固化或交聯通常經由一自由 基鏈機制達成,其可能需要任何的數種自由基-產生之物 料,例如:過氧化物、氫過氧化物、氧化還原併合物等。 此類物料當加熱時分解生成基團,或在胺或過渡金屬促 進劑之存在下,於室溫下分解。紫外(UV)光或電子束(EB) 輻射為引發反應之其他方法,係藉分解一適當的光引發 劑使生成自由基。本發明中所敘述以新穎丙烯酸酯寡聚 物為基質之顏料分散體,較以傳統多官能丙烯酸單體與 寡聚物為基質之分散體具有顯著的優越性,因為以前者 為基質之油墨,可僅使用標準紫外線固化所需量之一部 份量,經暴露於紫外線輻射下予以固化。 【實施方式】 圖之簡述 [0026] 由下列之詳細敘述以瞭解本發明的最佳方法為 連同所附之圖示一同閱讀。需強調的是:依照慣例,圖示 之各種特性並未按照比例,相反地,將各種特性之尺寸 任意地放大或縮小以使清晰,圖示中包括下圖: [0027】 圖1為合成Ashland D-30R之圖示。 [0028] 然而需注意的是:附加的圖示僅具說明性,而不 13 - 200524986 限制本發明之範缚。 最佳與各種之方^ _9】選擇業界之標準顏料,用以比較本發明 線固化樹脂與習知之紫外線固化樹脂之分散力道。、 擇之白色顏料為二氧化鈦白色杜邦R_7〇6,所選=之 顏料為顏料黃色i 4 YE丨働DC(二芳基黃,j 彩公司)’所選擇之藍色顏料為顏料藍色15jb^幻巴 ,青藍,Magruder色彩公司),所選擇之紅色顏料= 、、工色57:1 LR-1392(上金偶氮紅’ Magruder色穿乂 γ 所^之各種顏料係依#界之標準,本發明不侷所 =的顏料’精於此業之人士可容易地決定其他適合: 【0030】纟發明不侷限於所列舉之顏色(白色 色、與紅色),本發㈣是可適合地使用色任行 賴’包括但不赌&職輕賴料、料^之^ 香胺、與-芳基橘、碳黑、酞花青綠(顏料綠色7盎36、口 上金偶氣紅、祕紅、‘丫_紅、氧化鋅、硫_36)、 =黃、芳基黃、笨並味销黃、有機之酜 無機顏料。 化月監、與 【刪]於標準模式之評鏗:將乾燥的顏料與樹 並於一 HaUSC_現合器中以每分鐘2500轉進行二 1分鐘,藉以潤渥顏料顆粒與團塊之表面丁 料,其最終的分散係於- Lehmann 2.5x5英时 規模3-輥研磨機上進行,分散體係以 200524986 備,將混合物以相同次數橫越通過研磨機,以確保達到 相同程度之研磨,殘餘的顏料團塊使用一 NPIRI研磨量 規使其顯現。顏料之裝載量,除白色顏料裝載70%外, 於所有的分散體中皆為3〇%,分散體之顯色經由著色力 與無色漂白试驗予以評鑑。 [0032】 NPIRI研磨:將少量的分散體(足以取至量規上) 置放於一玻璃或塑膠平板上,並加入等量的寡聚物,用 以分散顏料。在使用一小鏟予以妥善混合後,取1角硬籲 幣尺寸之數量施加至量規上二個研磨通道之上端,使用 刮擦器予以下拉,謹慎地將刮擦器平滑地移動並使用中 度的壓力(以使二研磨通道之間不留存顯見的油墨薄 膜),其於量規上開始刮擦與,,撒射,,時,依延著研磨通道 側邊作記之NPIRI讀數,加以記錄,NPIRI係測量”研磨 之細度”,可參見ASTM標準中之D1210,D1316,與 D333,將其中每一個之全文皆併入本文供參考。 [0033] 著色力試驗:將50份預製之白色紫外線固化油· 墨(55%杜邦R-706與45%樹脂6923-30,分散於3-輥研 磨機上)與0·500份之顏料分散體於一 Max 60容器中予以 併合。混合係使用一 Hauschild混合器,以每分鐘2500 轉持續2分鐘予以完成。於Leneta 3NT-3紙上所進行標 準品相對於樣品之下拉,係使用一寬油灰刀,需確認下 拉有足夠的厚度,而使黑棒無法由油墨薄膜透視。溼膜 被一片6密爾之乙酸酯所覆蓋,使用一乾淨的油灰刀將 分散體上的薄膜下拉,以防止乙酸酯之下方存有霧末, 15 200524986 使用一手持之Byk Gardner分光光度計測量色料強度。 [0034】無色漂白試驗:於一 Max 60容器中將5份分散體 與45份無色樹脂pp 3204R併合,添加少量的光引發劑 Viacure®DX(UCB化學公司之商標名)至混合物中,以確 保光固化無任何表面黏性。UCB® ViaCure® DX載劑為一 種光引發劑之混合物,將其最佳化以用於深色油墨之配 方。於一 Hauschild混合器上,以每分鐘2500轉持續1 分鐘與每分鐘3000轉持續30秒鐘使完成混合。使用一 手動的校樣器,將樣品相對於標準品之印刷物於Leneta 3NT-3紙上輾平,並藉暴露於單一的600瓦特熔焊,,Η”燈 泡下,使用約1000毫焦耳/平方公分之劑量,完成固化, 使用一手持的ByK Gardner分光光度計測量光澤與色值。 [0035】黏度:分散體之錐板式黏度係使用一 Brookfield CAP 2000L黏度計,於一特殊的轉速、溫度、與時間下 測量。 [0036] 依本發明邁克爾樹脂之合成,係依照敘述於美 國專利5,945,489與6,025,410中之程序,其皆歸屬 Ashland公司,本發明之受讓人,這些專利中每一個的所 有内容皆意味深長地併入本文,供作全面性參考。 [0037] 本發明之各種樹脂,每種皆合成自多個單體, 每個單體皆被選擇具有至少一種官能。 [0038】本發明提供一種用於顏料分散體之邁克爾樹 脂,其包括至多約90份之具有顏料潤溼功能之單體,例 如:TMPE0TA(乙氧化之三曱基醇丙烷三丙烯酸酯)。 200524986 TMPEOTA充作邁克爾接受體,並於一化學計量進行反 應,以使:在暴露於具光化性之光或其他自由基引發劑之 前,獲得之樹脂尚未被交聯並且包含侧邊丙烯酸酯基 團,TMPEOTA所賦予之侧邊丙烯酸酯基團,隨後經暴露 於自由基下方可進行交聯。 [0039] 邁克爾接受體、賦予側邊丙烯酸酯基團、與顏 料潤溼之功能可由其他的丙烯酸酯提供,其包括但非限 制性:聚酯丙烯酸酯、環氧丙烯酸酯、胺基甲酸酯丙烯酸 酯、與丙烯酸單體,由單官能(EOEOEA,PEA等)至多官 能(PETA,二-TMPTA等)。這些單體與寡聚物囊括所有 種類之此種市售丙烯酸酯物料,其包括:胺-修飾、烷氧 化、雙官能性(如:丙烯酸烯丙酯、丙稀酸石夕氧烧酯)與/或 物理性獨特者(如:結晶)。 [0040] 本發明提供一種用於顏料分散體之邁克爾樹 脂,其包括至多約90重量份之具有顏料分散體安定功能 之單體,例如:烧氧化之壬酴丙稀酸醋。 [0041] 烧氧化之壬盼丙烯酸酯,其邁克爾接受體、賦 予侧邊丙烯酸酯基團、與顏料分散體安定之功能,可由 其他的丙烯酸酯提供,其包括但非限制性:陳述於前文中 之類目與種類。 [0042] 本發明提供一種用於顏料分散體之邁克爾樹 脂,其包括至多約90重量份之具有黏度控制功能之單 體,例如:DPGDA。 [0043] DPGDA具有之邁克爾接受體、與賦予側邊丙烯 17 200524986 酸酯基團、與黏度控制之功能,可由其他的丙烯酸酯提 供’其包括但非限制性:乙二醇二丙烯酸g旨、丙二醇二丙 烯酸酯、二乙二醇二丙烯酸酯、二丙二醇二丙烯酸酯、 二乙一醇二丙烯酸酯、三丙二醇二丙埽酸酯、四乙二醇 一丙烯酸酯、四丙一醇二丙烯酸酯、聚乙二醇二丙稀酸 酯、聚丙二醇二丙烯酸酯、乙氧化雙酚A二丙烯酸酯、 雙酚A二環氧丙醚二丙烯酸酯、間苯二酚二環氧丙醚二 =烯酸酯、1,3-丙二醇二丙烯酸酯、Μ_τ二醇二丙烯酸 知1,5_戊一醇一丙烯酸酯、ι,6·己二醇二丙稀酸酯、新 戊二醇二丙烯酸酯、環己烷二甲醇二丙烯酸酯、乙氧化 新戊二醇二丙烯酸酯、丙氧化新戊二醇二丙烯酸酯、乙 氧化%己烧^一甲醇^一丙稀酸酯、丙氧化環己烧二甲醇二 =烯fee酯、芳基胺基曱酸酯二丙烯酸酯、脂肪族胺基曱 酸酯二丙烯酸酯、聚酯二丙烯酸酯、與其混合物、丙三 醇f丙烯酸酯、乙氧化三甲基醇丙烷三丙烯酸酯、丙氧 =三甲基醇丙烷三丙烯酸酯、乙氧化丙三醇三丙烯酸 ^丙氧化丙三醇三丙烯酸酯、季戊四醇三丙烯酸酯、 =基胺基曱酸酯三丙烯酸酯、脂肪族胺基甲酸酯三丙烯 酸酯、蜜胺三丙烯酸酯、環氧酚醛清漆三丙烯酸酯、脂 =族環氧三丙烯酸酯、聚酯三丙烯酸酯、與其混合物、 =戊四醇四丙烯酸酯、乙氧化季戊四醇四丙烯酸酯、丙 氧化季戊四醇四丙烯酸酯、二季戊四醇四丙烯酸酯、乙 _ = 一季戊四醇四丙烯酸酯、丙氧化二季戊四醇四丙烯 文酯、芳基胺基曱酸酯四丙烯酸酯、脂肪族胺基曱酸酯 200524986 四丙烯酸s旨、蜜胺四丙烯酸s旨、環氧㈣清漆四丙稀酸 酯、聚酯四丙稀酸酯、與其混合物。 [0044]本發明提供一種用於顏料分散體之邁克爾樹 月曰,其包括至多約90重量份之一種具有對最終油墨配方 增強固化之功能之單體、寡聚物、或其他組份。 [0045】能對最終油墨配方增強固化者所具有邁克爾接 X體、與賦予侧邊丙烯酸酯基團之功能,可由下列丙烯 酸酯提供,其包括但非限制性:胺_修飾之聚酯、聚酯、 環氧或胺基甲酸酯丙烯酸酯、胺基丙烯酸酯、與類同物。 【0046】本發明提供一種用於顏料分散體之邁克爾樹 脂,其包括至多約50莫耳%之一種組份,如:乙醯乙酸乙 酯(EAA),其具有邁克爾供予體之功能並提供一種光不穩 定發色團,以使暴露於具光化性之輻射時,引入促進固 化之自由基。EAA為一種/3-二羰基化合物,於邁克爾合 成反應中充作供予體。 【0047】EAA之二羰基供予體,與引入光不穩定發色 團之功能,可由其他化合物提供,其包括但非限制性:乙 醯乙酸曱酯、2-乙基己基乙醯乙酸酯、乙醯乙酸月桂酯(乙 醯乙酸十二烷基酯)、乙醯乙酸第三丁酯、乙醯乙醯苯 胺、N-烷基乙醯乙醯苯胺、乙醯乙醯胺、乙醯乙醯氧 基乙基丙烯酸酯、2-乙醯乙醯氧基乙基曱基丙烯酸酯、 乙酿乙酸稀丙醋、乙酿乙酸节醋、2,4-戊二酮、2 4-己-酮、3,5-庚二酮、乙醢乙酸異丁酯、2_甲氧基乙基乙醯乙 酸醋、1,4-丁 一醇二乙醯乙酸酯、己二醇二乙醯乙酸 200524986 酯、新戊二醇二乙醢乙酸酯、環己烷二甲醇二乙醯乙酸 酯、與乙氧化雙酚A二乙醯乙酸酯、丙三醇或三曱基醇 丙烷三乙醯乙酸酯、聚己内酯三乙醯乙酸酯、長鏈烷氧 化之乙醯乙酸酯、季戊四醇四乙醯乙酸酯。 [0048] 表I:標準模式分散性樹脂之定義 樹脂 組成物 莫耳比率 黏度(泊) Ashland D-30R TMPEOTA 1.0 12.20 DPGDA 1.0 聚酯丙烯酸酯 0.5 EAA 2.4 PP3204R HDDA 17.0 7.08 環氧丙烯酸酯 2.0 TMPTA 1.0 EAA 1.0 2,4-戊二酮(2,4-PD) 2.6 DEA 0.2
[0049] 實例1藍色顏料分散體之比較標準模式: [0050] 藍色顏料BL-1531係於一 Hauschild混合器中予 以預分散,隨後以30%裝載量於所有的樹脂中,使用一 3-輥研磨機進行研磨,研磨之配方明確說明於表II。 20 200524986 表π:藍色顏料分散體之一般配方 組份 敘述 份(重量/重量) 樹脂 分散性樹脂 42.0 BL-1531 藍色顏料 18.0 [0051】用於生成藍色顏料分散體之樹脂界定於表III。 UCB Viascreen®與Viaflex®載劑為一種單體與寡聚物之φ 混合物,其已被最佳化分別用於網印與膠印之油墨應用 (Viascreen與Viaflex皆為UCB化學公司之商標名)。
21 200524986 表III:實驗用寡聚物之定義
樹脂 敘述 黏度(泊) Ebecryl 3411 環氧丙烯酸酯 498.70 ViaFlex 165 UCB膠印研磨載劑 26.50 ViaScreen 515 UCB網印研磨載劑 7008-135 TMPEOTA/DPGDA/0.50 聚酯丙烯 10.46 Ashland D-3 OR 酸酯/EAA 2.4 7008-136 TMPEOTA/TRPGDA/0.50 聚酯丙 烯酸酯/EAA2.4 11.11 7008-137 TMPEOTA/HDDA/0.50 聚酯丙烯 酸酯/EAA 2.4 10.95 7008-138 TMPEOTA/DEGDA/0.50 聚酯丙烯 酸酯/EAA 2.4 11.71 7008-139 4 TMPEOTA 13 DPGDA/SR 259(E200二丙烯酸酯)10.50聚酯 丙烯酸酯1EAA2.4 12.35 7008-140 4 TMPEOTA 13 DPGDA/SR 344(E400二丙烯酸酯)10.50聚酯 丙烯酸酯1EAA2.4 11.50 7001-110 TMPEOTA/DPGDA/2-甲氧基乙基 乙醯乙酸酯2.6/0.20哌啶 11.65 7001-136 Genomer 3497聚醚丙稀酸醋 /4DPGD A/2-甲氧基乙基乙醯乙酸 酯 2.6/0.20 DEA 14.15 7001-106 3 TMPEOTA/7 DPGDA/2-甲氧基 乙基乙醢乙酸酯2.6/0.20哌啶 8.45 7001-191 3 TMPEOTA/5 DPGDA/0.70 SR 504烧氧化之壬盼丙烯酸酯/EAA 2.6/0.2 DEA 20.30 7069-01 3 TMPEOTA/4 DPGDA/SR 504 烷 氧化之壬酚丙烯酸酯/2聚酯丙烯 酸酯/EAA2.4 26.25~ 22 200524986 黏度(泊)係於25°C。係數代表莫耳比率。 【0052】實例2顏料分散體之比較評鑑 [0053] 表IV: NPIRI研磨量規之觀察
編 號 研磨樣品 樹脂 黏度(泊) 刮擦 撒射 1 UCB-b-081103-02 (標準) Ebecryl 3411 未測 7 甚多 2 UCB flex-b-081203-01 ViaFlex 165 81.0 0 輕度至 中度 3 UCB screen-b-08110305 ViaScreen 515 331.5* 4 無 4 135b-081103-02 Ashland D-30R 66.7 0 甚多 5 136-b-071603-02 7008-136 52.7 0 無 6 137-b-071603-03 7008-137 40.7 0 無 7 138-b-071603-04 7008-138 63.7 0 無 8 139_b_071603-05 7008-139 64.2 0 無 9 140-b-071603-06 7008-140 40.0 0 無 10 110-b-073103-01 7001-110 66.0 0 無 11 7001136-b-073103-02 7001-136 41.0 0 無 12 106-b-073103-02 7001-106 60.7 0 無 13 191-b-073103-03 7001-191 59.0 0 無 14 706901-081503-02 7069-001 68.5 0 甚微 黏度(泊)係於300 RPM或100 RPM測定(*) 23 200524986 [0054] 表5:於顏料分散逋中之顯色 編5虎 無色漂白試驗 著色試驗 L a b 光澤 (60°) L a b 1 57.21 -30.3 -40.29 83.5 74.79 -20.6 -21.94 2 56.76 -30.38 -40.17 84.3 77.96 -19.77 -21.15 3 61.06 -32.28 -36.92 87.1 78.07 -19.89 -21.16 4 58.28 -31.07 -39.23 83.4 76.44 -20.49 -22.24 5 57.12 -30.79 -40 84 76.78 -20.35 -21.78 6 59.45 -31.25 -38.27 83.7 76.59 -20.47 -21.78 7 58.9 -31.25 -38.71 82.9 76.65 -20.37 -21.84 8 55.23 -29.55 -41.15 83.4 76.68 -20.43 -21.88 9 56.46 -30.4 -40.43 85.3 78.18 -20 -21.09 10 54.72 •29.21 -41.67 83.5 78.2 -19.79 -20.96 11 60.91 -31.43 -37.13 80.6 78.05 -19.9 -21 12 55.8 -29.93 -40.91 84.1 78.01 -19.94 -21.7 13 55.09 -29.81 -41.05 86.2 78.03 -19.75 -21.06 14 50.21 -24.69 -43.48 84.9 77.12 -20.13 -22.15
[0055]表 V,XII,與 XVI 記錄色值為”L”,’’a”,與”b” 刻度值,於近代色彩理論中,這些標示三個座標軸:L為 淺至深,a為綠至紅,b為藍至黃,對精於塗覆與平面藝 術者,這些原理被充分地瞭解。 24 200524986 [0056] 相較於市售之載劑,本發明樹脂於30%顏料裝 載量得到遠為較低之分散體黏度,此顯示於此揭示之樹 脂載劑,較習知載劑有利地對顏料具有分散較高程度之 能力。相較於市售之配方,於相同的30%顏料裝載量, 本實驗載劑於3-輥研磨機上遭受遠為較低的剪力,因 此,顯色、光澤、與透明度皆比某些配方所發表標準模 式之標準些微地較低。於樣品編號10,12,13,與14 之案例中,雖然具有較低的顏料分散體黏度,其顏色與 0 光澤性能與所發表標準模式載劑者相似或較佳,此亦顯 示本發明樹脂較標準模式之樹脂載劑能夠具有較高的顏 料裝載量。 [0057] 實例3白色顏料分散體之比較標準模式: [0058] 一種白色顏料,二氧化鈦(杜邦R-706®),以70% 裝載量於所有的樹脂中,使用一 3-輥研磨機進行研磨, 其所使用之配方明確說明於表VI。 表VL·白色顏料分散體之一般配方 組份 敘述 份(重量/重量) 樹脂 樹脂載劑 18.0 R-706 白色顏料 42.0 25 200524986 表VII:樹脂之定義 樹脂載劑 敘述 黏度 Ebecryl 3411 環氧丙烯酸酯 498.70 Viaflex 165 UCB膠印研磨載劑 26.50 Viascreen 515 UCB網印研磨載劑 139.00 7008-135 TMPEOTA/DPGDA/0.50 聚酯丙 10.46 (Ashland D-3 OR) 烯酸酯/EAA2.4 7001-106 3 TMPEOTA/7 DPGDA/2-甲氧 8.45 基乙基乙醯乙酸酯2.6/0.20哌啶 7069-01 3 TMPEOTA/4 DPGDA/SR 504 26.25 烷氧化之壬酚丙烯酸酯/2聚酯 丙烯酸酯/EAA2.4 黏度(泊,於25°c) [0059】實例4顏料分散體之比較評鑑 26 200524986 【0060】袅VIII: NPIRI研磨量梘之觀皇 編號 研磨樣品之編號 樹脂載劑 黏度 NPERI 董 NPKI 量 (50 轉/ 壯之刮 壯之撒 練) 樹通過 射(通過10 08/20/03 10次後) 次衡 1 UCB-W-082803-01 Ebecryl 太黏稠, 0 0 (標準) 3411 不易研磨 2 UCBflex-W-082803-02 Viaflex 681 >0 0 輕度 165 3 UCBScreen-W-082803-03 Viascreen 太黏稠, 16 甚多 515 不易研磨 4 135-W-082803-04 Ashland 328泊 0 0 D-30R 5 106-W-082803-05 700M06 207泊 0 0 6 706901-W-082803-06 7069-01 538泊 4 些微
[0061] 相較於習知載劑,本發明樹脂載劑於70%之二 氧化鈇白色顏料裝載量,得到遠為較低之分散體黏度, 此顯示本發明樹脂,較習知載劑具有分散較高程度白色 顏料之能力,此為一可貴的優點。 [0062] 實例5黃色顏料分散體之比較標準模式: [〇〇63]黃色顏料YE_1400DC,以30%裝載量於所有的 樹脂中,使用一 3-輥研磨機進行研磨,研磨之配方明確 27 200524986 說明於表IX。 [0064] 表IX:黃色顏料分散體之一般配方 組份 敘述 數量 樹脂 樹脂載劑 42.0 YE-1400DC 黃色顏料 18.00 [0065] 表X:黃色分散體樹脂之定義 鲁 樹脂載劑 樹脂敘述 黏度於25°C(厘泊) Ebecryl 3411 環氧丙烯酸酯 49,870 Viaflex 165 UCB膠印研磨載劑 2650 Viascreen 515 UCB網印研磨載劑 13,900 7008-135 (Ashland D-30R) TMPEOTA/DPGDA/0.50 聚酯 丙豨酸酯/EAA2.4 1046 7001-106 3 TMPEOTA/7 DPGDA/2-甲氧 基乙基乙醯乙酸酯2.6/0.20哌 啶 845 7069-01 3 TMPEOTA/4 DPGDA/SR 504 烷氧化之壬酚丙烯酸酯/2聚 酯丙烯酸酯/EAA2.4 2625 [0066] 實例6顏料分散體之比較評鑑 28 200524986 [0067】表XI: NPIRI研磨量規之觀察 編號 研磨樣品之編號 樹脂載劑 黏度 (300 轉/ 分鏜) 08/20/03 NPIRI 量規上 之刮擦 (通過10 NPIRI 量規上 之撒射 (通過10 次後) 1 UCB-Y-082903-01 (標準) Ebecryl 3411 954泊 (50 #/ 分鐘) 0 甚多 2 UCBflex-Y-082903-02 Viaflex 165 72·5 泊 0 0 3 UCBScreen-Y-082903-03 Viascreen 515 483泊 (50 轉/ 分鐘) 0 0 4 135-Y-082903-04 Ashland D-3 OR 56.7 泊 0 0 5 106-Y-082903-05 700M06 80.7 泊 0 0 6 70690 l-Y-082903-06 7069-01 50.2 泊 0 0 29 200524986 [0001] 表χιι:於顏料分散體中之顯色 編號 無色漂白試驗 著色試驗 L a b 光澤 (60°) L a b 1 86.59 -6.62 79.58 85.7 93.7 -4.72 33.13 2 86.22 -6.15 81.87 86 93.79 -4.58 32.84 3 86.65 -7.1 80.57 89.7 93.91 -5.07 33.71 4 86.43 -6.31 80.45 86.7 93.85 -4.63 33.22 5 86.04 -5.53 84.71 89.3 93.9 -4.49 32.62 6 86.59 -6.62 79.58 85.7 93.7 -4.72 33.13 [0068] 相較於習知載劑,本發明樹脂載劑於30%之黃 色顏料裝載量,得到遠為較低之分散體黏度,此顯示本 發明載劑,較習知載劑具有分散較高程度黃色顏料之能 力,此為一可貴的優點。於現時的評鑑中,本發明樹脂 載劑,於30%顏料與較低的黏度下,相較於習知之配方, 於3-輥研磨機上不會遭受如其那麼多的剪力,然而顏色 與光澤之性能與習知載劑所具有者相似或較佳。此亦顯 示:本發明樹脂較標準模式之樹脂載劑能夠具有較高的 顏料裝載量。 [0069] 實例7紅色顏料分散體之比較標準模式: [0070] 紅色顏料LR-1392,以30%裝載量於所有的樹脂 中,使用一 3-輥研磨機進行研磨,研磨之配方明確說明 於表XIII。 200524986 [0071] 表XIII:紅色顏料分散體之一般配方 組份 敘述 數量 樹脂 樹脂載劑 42.0 LR-1392 紅色顏料 18.00 [0072】表XIV: 紅色油墨實驗用樹脂之組份 樹脂載劑 樹脂敘述 黏度於25°C (厘泊) Ebecryl 3411 環氧丙烯酸酯 49,870 Viaflex 165 UCB膠印研磨載劑 2650 Viascreen 515 UCB網印研磨載劑 13,900 7008-135 (Ashland D-30R) TMPEOTA/DPGDA/0.50 聚酯 丙烯酸酯/EAA2.4 1046 7001-106 3 TMPEOTA/7 DPGDA/2-甲氧 基乙基乙醯乙酸酯16/0.20哌 啶 845 7069-01 3 TMPEOTA/4 DPGDA/SR 504 烷氧化之壬酚丙烯酸酯/2聚 酯丙烯酸酯/EAA2.4 2625 [0073] 實例7顏料分散體之比較評鑑 [0074] 表XV: NPIRI研磨量規之觀察 31 200524986 編號 研磨樣品號 樹脂載劑 黏度 NPIRI NPmi (300轉/分 量壯 量壯 鐘) 之到擦 08/20/03 (通過10 (通過10 次後) 次後) 1 UCB-R-082503-01 Ebeciyl3411 961泊 6 甚多 (標準) (50 #/分鐘) 2 UCBflex-R-082503-02 Viaflex 165 46·2 泊 2 無 3 UCBScreen-R-082503-0 Mascreen 597泊 7 甚多 3 515 (50 #/分鐘) 4 135-R-082503-04 Ashland 73.0 泊 2 一些 D-30R 5 106-R-082503-05 7001-106 532泊 3 一些 6 706901-082503-06 7069-01 98.2 泊 3 -itb 32 200524986 [0075] 表XVI:於顏料分散體中之顯色 編5虎 無色漂白試驗 著色試驗 L a b 光澤 (60°) L a b 1 49.25 54.97 0.28 78.3 76.75 24 -1.9 2 46.88 55.78 4.37 86.45 75.38 25.27 -2.5 3 56.63 48.96 -6.86 84.3 79.79 20.99 -0.25 4 46.67 55.44 4.33 79.7 75.87 24.85 -2.51 5 46.17 55.52 5.63 84.7 76.12 24.48 -2.61 6 47.35 55.18 3.18 84.2 75.97 24.53 -3.68 [0076] 相較於習知載劑,由本發明樹脂生成之分散 體,當裝載30%紅色顏料時具有遠為較低之黏度,此顯 示本發明樹脂較習知載劑具有分散較高程度紅色顏料之 能力,此為一可貴的優點。此外,NPIRI研磨量規評鑑 顯示:相較於習知樹脂,本發明樹脂需要較少的通過次數 以研磨其中之顏料,此為另一操作的優點。於現時的評 鑑中,本發明載劑,於30%顏料與較低的黏度下,在3_ 輥研磨機上不會遭受如以市售樹脂為基質之配方般那麼 多的剪力,然而光澤性能與習知樹脂所具有者相似或較 佳。此亦顯示:本發明樹脂較標準模式之樹脂載劑能夠具 有較高的顏料裝載量。 [0077】相較於習知載劑,由本發明提供之樹脂,其具 33 200524986 有較佳的顏料潤溼特性與較佳的可研磨性。本發明樹 脂,於研磨階段,在一 3-輥研磨機上,可具有較高的顏 料裝載程度。本發明樹脂可裝載30至32%之紅色、藍色、 與黃色顏料,相較於市售載劑之最大可能裝载量為 25%。於白色顏料之案例中,本發明樹脂可裝載70 %之 顏料,相較於市售樹脂之60%裝載量。NPIRI研磨量規 評鑑顯示:相較於標準品,本發明樹脂需要較少的通過次 數以研磨其中所裝載之顏料,此為一難得的操作優點。_ 可獲得另一優點:因為本發明樹脂為自行光引發,故可大 幅地減少由這些分散體衍生之油墨配方中的光引發劑裝 載量。 於敘述本發明後,我們所申請之新穎,並且意欲藉 專利特許證獲得之專利申請範圍為如後。 【圖式簡單說明】 圖1為合成Ashland D-30R之圖式。 【主要元件符號說明】 n 無 34
Claims (1)
- 200524986 十、申請專利範圍: h相m種包 1 於顏料分散體之邁克爾樹脂,該邁克爾分散性 也=體或募聚物’其具有邁克爾接受體之功能,並提 供側邊的丙烯酸酯基團供交聯用 一種單體或募聚物,其具有顏料潤溼之功能 一種單體或寡聚物,其具有顏料安定性之 一種單體或寡聚物,其具有黏度控制之功能 -種組份’其具有對最終油墨配方增強固化之功能 一種組份,其具有邁克爾供予體之功能,並提供一種光 不穩定發色團。 2·根據申請專利範圍第丨項之邁克爾分散性樹脂,其中 該具有顏料潤溼功能之單體或寡聚物係選自群組包括: 聚酯丙烯酸酯、環氧丙烯酸酯、胺基曱酸酯丙烯酸酯、 丙烯酸單體、與其混合物。 3·根據申請專利範圍第丨項之邁克爾分散性樹脂,其中 該具有顏料分散體安定性功能之單體或寡聚物係選自 群組包括:聚酯丙烯酸酯、環氧丙婦酸酯、胺基甲酸醋丙 烯酸酯、與丙烯酸單體、與其混合物。 4·根據申請專利範圍第1項之邁克爾分散性樹脂,其中 該具有黏度控制功能之單體或寡聚物係選自群組包括: 聚酯丙稀酸酯、環氧丙稀酸酯、胺基甲酸醋丙婦酸酉旨、 丙烯酸單體、與其混合物。 5·根據申請專利範圍第1項之邁克爾分散性樹脂,其中 35 200524986 該具有對最終油墨配方增強固化功能之組份係選自群 組包括··胺-修飾之聚醚、聚酯、環氧或胺基甲酸酯丙稀 酸酯、與胺基丙烯酸酯、與其混合物。 6.根據申請專利範圍第1項之邁克爾分散性樹脂,其中 該具有邁克爾供予體之功能,並提供一種光不穩定發色 團之組份係選自群組包括:乙酿乙酸乙醋、乙醯乙酸甲 醋、2-乙基己基乙醢乙酸酯、乙醢乙酸月桂酯、乙醯乙 酸第三丁酯、乙醢乙醢苯胺、N-烷基乙醯乙醯苯胺、乙 醢乙醯胺、2-乙醯乙醯氧基乙基丙烯酸酯、2_乙醯乙醯 氧基乙基曱基丙烯酸酯、乙醯乙酸烯丙酯、乙醯乙酸节 酯、2,4-戊二酮、2,4-己二酮、3,5-庚二酮、乙醯乙酸異 丁酯、與2-甲氧基乙基乙醯乙酸酯、ι,4·丁二醇二乙醜 乙酸酯、1,6_己二醇二乙醯乙酸酯、新戊二醇二乙醯乙 酸酯、環己烷二甲醇二乙醯乙酸酯、乙氧化雙盼A二乙 酿乙酸酯、三甲基醇丙烷三乙醯乙酸酯、聚己内醋三乙 醯乙酸酯、長鏈烷氧化之乙醯乙酸酯、季戊四醇四乙醯 乙酸酯、與其混合物。 7·根據申請專利範圍第丨項之邁克爾分散性樹脂,其中 該具有顏料潤溼功能之單體或寡聚物,其存在量為自約 50份至約90份。 ' 8. 根據申請專利範圍第丨項之邁克爾分散性樹脂,其中 該具有顏料安定性功能之單體或寡聚物,其存在量^至 多約50份。 … 9. 根據申請專利範圍第丨項之邁克爾分散性樹脂,其中 36 200524986 該具有黏度控制功能之單體或寡聚物,其存在量為至多 約90份。 1〇·根據申請專利範圍第1項之邁克爾分散性樹脂,其中 該具有對最終油墨配方增強固化功能之單體、募聚物或 組份’其存在量為至多約90份。 Π·根據申請專利範圍第1項之邁克爾分散性樹脂,其中 該具有邁克爾供予體之功能,並提供一種光不穩定發色 團之組份,其存在量為自約5數量份至約50份。 12·根據申請專利範圍第2項之邁克爾分散性樹脂,其中 一種較佳的顏料潤溼單體係選自群組包括:丙氧化與乙 氧化之聚丙烯酸酯。 13·根據申請專利範圍第4項之邁克爾分散性樹脂,其中 一種較佳的黏度控制單體係選自群組包括:乙二醇二丙 婦酸酯、丙二醇二丙婦酸酯、二乙二醇二丙烯酸酯、二 丙二醇二丙烯酸酯(DPGDA)、三乙二醇二丙烯酸酯、三 丙二醇二丙烯酸酯、四乙二醇二丙烯酸酯、四丙二醇二 丙烯酸酯、聚乙二醇二丙烯酸酯、聚丙二醇二丙烯酸 酯、乙氧化雙酴A二丙稀酸酯、雙盼A二環氧丙_二 丙烯酸酯、間苯二酚二環氧丙醚二丙烯酸酯、丙二 醇二丙烯酸酯、1,4-丁二醇二丙烯酸酯、ι,5-戊二醇二丙 烯酸酯、1,6-己二醇二丙烯酸酯、新戊二醇二丙烯酸酯、 環己烧二曱醇二丙烯酸酯、乙氧化新戊二醇二丙烯酸 酯、丙氧化新戊二醇二丙烯酸酯、乙氧化環己烷二甲醇 二丙烯酸酯、丙氧化環己烷二曱醇二丙烯酸酯、芳基胺 37 200524986 基甲酸酯二丙稀酸酯、脂肪族胺基甲酸酯二丙烯酸酯、 聚酯二丙烯酸酯、與其合物、丙三醇三丙烯酸酯、乙氧 化三甲基醇丙烷三丙烯酸酯(TMPEOTA)、丙氧化三甲基 醇丙烷三丙烯酸酯、乙氧化丙三醇三丙烯酸酯、丙氧化 丙三醇三丙烯酸酯、季戊四醇三丙烯酸酯、芳基胺基甲 酸酯三丙烯酸酯、脂肪族胺基甲酸酯三丙烯酸酯、蜜胺 三丙烯酸酯、環氧酚醛清漆三丙烯酸酯、脂肪族環氧三 丙烯酸酯、聚酯三丙稀酸酯、季戊四醇四丙稀酸酯、乙籲 氧化季戊四醇四丙烯酸酯、丙氧化季戊四醇四丙烯酸 酯、二季戊四醇四丙烯酸酯、乙氧化二季戊四醇四丙烯 酸酯、丙氧化二季戊四醇四丙烯酸酯、芳基胺基曱酸酯 四丙稀酸酯、脂肪族胺基甲酸酯四丙稀酸g旨、蜜胺四丙 烯酸酯、環氧盼酸清漆四丙烯酸酯、聚酯四丙烯酸酯、 與其混合物。 14·根據申請專利範圍第5項之邁克爾分散性樹脂,其中 一種較佳的增強固化組份係選自群組包括:胺_修飾之聚 _或聚酯丙烯酸酯、與一元或二元胺,其能與丙烯酸酯 部份進行假邁克爾加成反應者、與其併合物。 15·根據申請專利範圍第6項之邁克爾分散性樹脂,其中 一種較佳的邁克爾供予體與光不穩定發色團組份係選 自群組包括:EAA、2-MEAA、與長鏈烷氧化之乙醯乙酸 m ° 16·根據申請專利範圍第12項之邁克爾分散性樹脂,其中 一種最佳的顏料潤溼單體為TMPEOTA。 38 200524986 17. 根據申請專利範圍第13項之邁克爾分散性樹脂,其中 一種最佳的黏度控制單體為DPGDA。 18. 根據申請專利範圍第4項之邁克爾分散性樹脂,其中 一種最佳的增強固化組份為二乙醇胺。 19. 根據申請專利範圍第2項之邁克爾分散性樹脂,其中 一種最佳的邁克爾供予體與提供光不穩定發色團組份 為2_甲氧基乙基乙醯乙酸酯。 20. —種邁克爾分散性樹脂,其包括: 約 37.7 重量%丁]\«^0丁入; 約 26.4 重量% DPGDA; 約 21.3 重量 % Ebecryl 81;與 約12重量% EAA。 21. —種邁克爾分散性樹脂,其包括: 約 34.2 重量% TMPEOTA; 約 45.2 重量% DPGDA; 約16.4重量% 2-MEAA;與 約1.7重量%哌啶。 22. —種邁克爾樹脂-顏料分散體,該顏料分散體包括: 自約10重量份至約90重量份之一種根據申請專利範圍 第1項之邁克爾分散性樹脂,與自約10重量份至約75 重量份之一種顏料。 23. 根據申請專利範圍第22項之邁克爾樹脂-顏料分散 體,其中該顏料係選自群組包括:白色顏料、黃色顏料、 紅色顏料、與藍色顏料。 39 200524986 24.根據中請專利範圍第23項之邁克爾樹脂__分散 體’其中該白色顏料係選自群組包括:二氧化鈦、氧化 鋅、與硫酸鋇。 25. 根據申請專利範圍第23項之邁克爾樹脂_顏料分散 體’其中該黃色顏料係選自群組包括:二芳基黃、芳基 黃、苯並咪唑酮黃、有機與無機顏料。 土 26. 根據申請專利範圍第23項之邁克爾樹脂_顏料分散 體’其中該藍色顏料係選自群組包括:敵花青藍與其他的 有機與無機藍色顏料。 仏根據申請專利範圍第23項之邁克爾樹脂_顏料分散 體’其中該紅色顏料係選自群组包括·上金偶氮紅、革齡 紅、與喳吖酮紅。 不 28· —種製造顏料分散體之方法,此方法包括: 提供一數量之一種顏料, 使用一種根據申請專利範圍帛Μ之邁克爾樹脂濁渔該 顏料,並將該顏料研磨於該樹脂中使生成一種分散體。 29·根據申請專利範圍第28項之製造一種顏料分散體之 方法,其中潤座該顏料包括··於一操作於高剪力下之混合 設備中,將顏料與樹脂相混合。 30·根據申請專利範圍第29項之製造一種顏料分散體之 方法,其中满溼該顏料包括:於一 Hauschild混合器、R〇ss 汁匕合器、或一空氣混合器中進行分散。 31·根據申請專利範圍第28項之製造一種顏料分散體之 方法,其中研磨該顏料包括··將該樹脂與該顏料通過一介 200524986 質研磨機,其係選自群組包括:3-輥研磨機與水平介質 研磨機。