SE522845C2 - Sätt att tillverka ett skär sammansatt av olika hårdmetallsorter - Google Patents
Sätt att tillverka ett skär sammansatt av olika hårdmetallsorterInfo
- Publication number
- SE522845C2 SE522845C2 SE0004273A SE0004273A SE522845C2 SE 522845 C2 SE522845 C2 SE 522845C2 SE 0004273 A SE0004273 A SE 0004273A SE 0004273 A SE0004273 A SE 0004273A SE 522845 C2 SE522845 C2 SE 522845C2
- Authority
- SE
- Sweden
- Prior art keywords
- cemented carbide
- powder
- cavity
- ways
- different types
- Prior art date
Description
25 30 35 40 2522 845 Två eller flera sorter i samma skär beskrivs också i AT 269598 där en metod presenteras med ett antal pressteg med använd- ning av ramar av gummi eller andra elastiska material för att forma kaviteterna som behövs för att fylla de olika pulvren. AT 269598 beskriver sålunda skär bestående av två eller flera hårdme- tallsorter tillverkade genom förpressning av ett ämne av en sort försedd med spår, urtag och/eller fördjupningar. Dessa fylls med hårdmetallpulver av den andra sorten och pressas därefter till en grönkropp som slutligen sintras. Sådana kroppar betecknas häri som kompoundkroppar.
Men val av sorter, slutligt presstryck och sintringsbetingel- ser måste utföras med stor omsorg för att undvika att sprickor ut- vecklas i övergångsområdet mellan de två sorterna. Ett skäl här- till är att det är vanligen inte möjligt att erhålla optimalt presstryck för båda sorterna för att erhålla samma krympning. Van- ligen krymper den ena sorten mer än den andra vilket leder till en distorderad kropp efter sintring, se Fig l som visar ett tvärsnitt av ett RNGN skär och samma del av skäret från ovan. Det är därför AT 269598 beskriver en värmebehandling efter sintring för att minska spänningarna vid övergångarna. Även om inga sprickor ut- vecklas behöver kroppen omfattande slipning för att vara användbar som ett skärverktyg.
Det är därför ett syfte med föreliggande uppfinning att för- lägga ett sätt att tillverka hårdmetallskär innehållande två olika hårdmetallsorter som är mindre känsligt för att utveckla sprickor i övergångenszonen mellan sorterna.
Fig 1 visar ett kompoundskär enligt känd teknik.
Fig 2 a-e illustrerar sättet enligt föreliggande uppfinning.
Fig 3 a-d visar tvärsnitt och vy från ovan av RNGN skär en- ligt uppfinningen.
Fig 4 visar ett ljusoptiskt mikrofoto vid omkring 1000X av den diffusa gränsen mellan de två sorterna.
Det har nu överraskande visat sig att de ovannämnda problemen kan övervinnas med användning av ett speciellt formgivet pressverktyg för tillverkning av kompoundhårdmetallskär. Metoden illustreras i Fig 2 a-e. I Fig 2a fylls pulver Pl från en fyllsko, F, i huvudkaviteten, A, av dynan och pulver P2 i ytterligare en kavitet, B. peln, C, sänkts till ett läge där pulvret P2 kan introduceras I Fig 2b har fyllskon avlägsnats och den undre stäm- ovanpå pulvret Pl som visas i Fig 2c och 2d. Det resulterande skä- 10 522 845 3 ret efter pressning och sintring visas i Fig 3a och b. Alterna- tivt, väljs nivån något högre sà att pulvret P2 skjuter bort pulv- ret Pl under introduktion och därvid bildar en portion djupare på spånsidan. Det resulterande pressade och sintrade Skäret visas i Fig 3c och 3d. Relationen mellan ll och 12 i Fig. 2e skall inte överskrida l/2.
Den multiaxiella fyllproceduren tillåter de två pulvren att pressas samtidigt och en presskropp med mer optimal pressdensitet uppnås. Den sintrade kroppen kommer att behöva mycket liten slip- ning. Genom sättet kan ett skär tillverkas.
Claims (1)
1. 0 §22 845 Krav Sätt att tillverka ett hårdmetallskär av en första sort vari åtminstone en skärspets består av en hàrdmetall av en andra sort med annan sammansättning och/eller kornstorlek k ä n n e t e c k n a t att ett multiaxiellt pressverktyg omfattande en fyllsko (F), en dyna med en huvudkavitet (A) och ytterligare en kavitet (B) samt en undre stämpel (C) används (Pl) från fyllskon (F) fylls i huvudkaviteten (A) och pulver av en andra sort (P2) i kaviteten varvid ett pulver av en första sort (B), den undre stämpeln (C) sänks till ett läge där pulvret (P2) kan introduceras ovanpå pulvret (Pl) från kaviteten (B) så att efter pressning ll/l2 pressade pulvren, och slutligen sintras.