SE437683B - CREATE OR SHELL - MATERIAL AGAINST THE ROLL - BY EXV - Google Patents
CREATE OR SHELL - MATERIAL AGAINST THE ROLL - BY EXVInfo
- Publication number
- SE437683B SE437683B SE8205807A SE8205807A SE437683B SE 437683 B SE437683 B SE 437683B SE 8205807 A SE8205807 A SE 8205807A SE 8205807 A SE8205807 A SE 8205807A SE 437683 B SE437683 B SE 437683B
- Authority
- SE
- Sweden
- Prior art keywords
- coating
- scraper
- surface coating
- carrier material
- scraper according
- Prior art date
Description
skzosaov-A niskt svårgenomförbara, särskilt vid tunna schabermate- rial. Det har bl.a. också visat sig, att det tunna schabermaterialets ursprungliga och för ett gott avskrap- ningsresultat nödvändiga mekaniska egenskaper, exempel- vis materialets elasticitet härigenom avsevärt försämras. skzosaov-A nically difficult to implement, especially with thin scraper material. It has i.a. It has also been found that the original mechanical properties of the thin scraper material and necessary for a good scraping result, for example the material's elasticity, are thereby considerably deteriorated.
Väsentligt är nämligen, att schabrarna eller raklarna icke enbart uppvisar en avsevärt längre livslängd utan alltjämt också ger ett fullvärdigt resultat vid renskrap- ning eller kräppning.It is important that the scrapers or squeegees not only have a considerably longer service life but still also give a full-fledged result when scraping or creping.
Det har nu enligt uppfinningen överraskande visat sig möjligt att åstadkomma en schaber med mycket lång livs- längd och som uppfyller ovannämnda fordringar. Känne- tecknande för schabern är, att den består av ett flexi- belt stålblad, vars verksamma arbetsyta åtminstone vid nrbetsytnns íngångskant uppvisar en tunn ytbeläggning med högre nötningsbeständighet än stålbladet, och att ytbe- läggningen innefattar ett flertal tunna, på varandra lag- rade delskikt av keramiskt material, vart och ett uppvi- sande en tjocklek av 0,002 - 0,045 mm.According to the invention, it has now surprisingly been found possible to provide a doctor with a very long service life and which fulfills the above-mentioned requirements. Characteristic of the doctor blade is that it consists of a flexible steel blade, the effective working surface of which at least at the entrance edge of the working surface has a thin coating with higher abrasion resistance than the steel blade, and that the surface coating comprises a plurality of thin, layered sublayers. of ceramic material, each having a thickness of 0.002 - 0.045 mm.
'Enligt en lämplig utföringsform av uppfinningen utgöres bladets totala arbetsyta av nämnda ytbeläggning.According to a suitable embodiment of the invention, the total working surface of the blade is constituted by said surface coating.
Den enligt uppfinningen föreslagna rakeln eller schabern med den applicerade nötningsbeständiga beläggningen upp- visar i huvudsak samma mekaniska egenskaper, bl.a. elasti- citet som det icke belagda ursprungliga stålbladet, var- igenom ett fullgott avskrapningsresultat garanteras. Genom den föreslagna lämpliga stegvisa utbyggnaden av den mycket tunna ytbeläggningen uppnås en god flexibilitet och ringa skörhet i själva beläggningen. Med metallsprutning menas här s.k. termisk sprutning innebärande, att smält belägg- ningsmaterial sprutas mot den för beläggning avsedda ytan.The squeegee or doctor blade proposed according to the invention with the applied abrasion-resistant coating exhibits essentially the same mechanical properties, e.g. elasticity as the uncoated original steel blade, thereby guaranteeing a satisfactory scraping result. Due to the proposed suitable stepwise expansion of the very thin surface coating, a good flexibility and low fragility in the coating itself is achieved. By metal spraying is meant here so-called thermal spraying, which means that molten coating material is sprayed against the surface intended for coating.
Lämpligen användes i det föreliggande sammanhanget plasma- 820580741 eller flamsprutning. Vid exempelvis plasmasprutning, som i många fall är att föredraga, upphettas en gas så kraf- tigt av en ljusbåge, att gasen når plasmatillstånd. I detta plasmatillstånd sprutas gasen i form av en stråle ut ur ett munstycke och det för beläggning avsedda mate- rialet tillföres plasmastrâlen i pulverform medelst en bärgas, så att pulvret omedelbart smältes och av strålen i smält tillstånd slungas mot den för beläggning avsedda ytan. För att då inte värmemässigt skada det för belägg- ning oftast tunna stâlbladet uppbygges den i sig mycket tunna beläggningen lämpligen stegvis.Conveniently, plasma or flame spraying is used in the present context. In plasma spraying, for example, which in many cases is preferable, a gas is heated so strongly by an arc that the gas reaches a plasma state. In this plasma state, the gas in the form of a jet is sprayed out of a nozzle and the material to be coated is supplied in powder form by means of a carrier gas, so that the powder is immediately melted and thrown by the jet in the molten state against the surface to be coated. In order then not to damage the thermally thin steel blade, which is usually thin in terms of coating, the very thin coating itself is suitably built up step by step.
Såsom beläggningsmaterial användes enligt uppfinningen företrädesvis aluminiumoxid med ev. mindre titanoxid tillsats. övriga kännetecken hos uppfinningen framgår av de i bifogade krav angivna särdragen.As the coating material, according to the invention, alumina with ev. minor titanium oxide addition. Other features of the invention are apparent from the features set forth in the appended claims.
Fördelarna med uppfinningen är uppenbara. Genom att en förhållandevis tunn slitstark ytbeläggning appliceras endast på en ringa del av bärarmaterialet bibehâlles bärarmaterialets nödvändiga elastiska egenskaper och övriga ursprungsegenskaper. Genom den mycket tunna yt- beläggningen har risken för sprickor minimerats. Detta förhållande samt det ytterligare nämnda förhållandet, att den enligt uppfinningen föreslagna schabern har samma me- kaniska egenskaper t.ex. elasticitet, som en traditionell schaber gör att schabern direkt kan användas i konven- tionella schaberhållare för fasthållning och anpressning, som finns på befintliga anläggningar, Uppfinningen skall i det följande beskrivas närmare under hänvisning till bifogade ritningar, där fig. 1 - 6 visar några olika utföringsformer av enligt uppfinningen föreslagna schabrar och raklar._ A*" szdssov-ß De på ritningen visade raklarna eller schabrarna kunna exempelvis användas för renskrapning av tryck- eller färgvalsar, torkcylindrar för papper eller tyg och lik- nande eller också exempelvis som schabrar för kräppning av papper.The advantages of the invention are obvious. By applying a relatively thin durable surface coating to only a small part of the carrier material, the necessary elastic properties of the carrier material and other original properties are maintained. Due to the very thin surface coating, the risk of cracks has been minimized. This condition and the further mentioned condition, that the scraper proposed according to the invention has the same mechanical properties e.g. The invention will be described in more detail below with reference to the accompanying drawings, in which Figs. 1 - 6 show a few different elasticities, which a traditional doctor blade can use directly in conventional doctor blade holders and presses, which are present in existing plants. embodiments of the scrapers and squeegees proposed according to the invention. of paper.
Den i fig.1 visade övre delenav schabern.betecknasned"1.Scha- berns motstâende, i det visade utförandet parallella sidor har betecknats med 2 och 3 och schaberns arbetsyta el- ler fasyta med 4. Med 6 betecknas en schematiskt antydd vals, exempelvis en gravyrvals för djuptryck, som roterar i pilens 7 riktning. Den mot valsen 6 riktade delen av den plana schabersidan 2 har belagts med en tunn beläggning 5 av ett mera nötningsbeständigt material än schaberma- terialet l, vilket i detta exempel kan utgöras av ett 0,05 - 0,15 mm tjockt och T5 mm brett stålband. Belägg- ' ningens 5 sammansättning och uppbyggnad skall nedan när- mare definieras. Bladets l fasyta är således avsedd att anligga mot gravyrvalsens yta för att skrapa bort färg- överskottet. Beläggningen 5 är direkt applicerad på plan- ytan 2 av schabern l. Planytan 2 betecknas också såsom schaberns ingångssida och beläggningen 5 är anordnad i en beläggningszon Sa, vars bredd utmed ingångssidan 2 lämp- ligen är ringa i förhållande till schaberbredden och i detta fall uppgår till högst 5 mm.The upper part of the doctor blade shown in Fig. 1 is denoted "1. The opposite side of the doctor blade, in the embodiment shown, parallel sides have been denoted by 2 and 3 and the working surface or bevel surface of the doctor blade by 4. A 6 denotes a schematically indicated roller, e.g. an gravure engraving roller rotating in the direction of the arrow 7. The part of the flat doctor blade 2 facing the roller 6 is coated with a thin coating 5 of a more abrasion resistant material than the doctor blade material 1, which in this example may be a .05 - 0.15 mm thick and T5 mm wide steel strip. The composition and structure of the coating 5 will be defined in more detail below. The bearing surface 1 of the blade is thus intended to abut against the surface of the engraving roller to scrape off the excess paint. is directly applied to the flat surface 2 of the doctor blade. The flat surface 2 is also referred to as the entrance side of the doctor blade and the coating 5 is arranged in a coating zone Sa, the width of which along the entrance side 2 is suitably small in ill scraper width and in this case does not exceed 5 mm.
I fig. 2 visas en variant av en enligt uppfinningen fram- ställd schaber för användning till renskrapning av en färg- vals, vilken roterar i riktning mot schabern, varvid den nöt- ningsbeständiga beläggningen 5 utgående från schaberns 1 in- gångssida 2 anordnats på en avfasning 8 i bärarmaterialet.Fig. 2 shows a variant of a scraper made according to the invention for use in scraping a paint roller, which rotates in the direction of the scraper, the abrasion-resistant coating 5 starting from the inlet side 2 of the scraper 1 being arranged on a chamfer 8 in the carrier material.
I fig. 3 - 6 visas fyra ytterligare varianter av en en- ligt uppfinningen framställd schaber för kräppning av en pappersbana.Figures 3 to 6 show four further variants of a scraper made according to the invention for creping a paper web.
I fig. 3 och 4 användes en kant 10 av beläggningen 5 som schaberns arbetsyta. I fig. 4 har beläggningen bringats " -i-í-_jáfi'b'r7"""'f""' “".-r,--<_._.___ Wik-Å X: 'e/¿ .ncâïaänå t.) ,..,__,._.._ . , 8205807-4 att även omfatta bärarmaterialets översida 11 för att öka kan- tens 10 hållfasthet. En ytterligare förbättring av hållfast- heten kan uppnås genom att bärarmaterialet före beläggningen bibringats en fas 12 enligt fig. 4. Genom att belägga scha- berns båda sidor 2 och 3 âstadkommes två ekvivalenta kanter så att när den ena kanten förslitits kan schabern vändas så att den andra kanten kan bringas i verksam anliggning.In Figs. 3 and 4, an edge 10 of the coating 5 is used as the working surface of the scraper. In Fig. 4 the coating has been brought "-i-í-_já fi 'b'r7" ""' f "" '“".-R, - <_._.___ Wik-Å X:' e / ¿. ncâïaänå t.), .., __, ._.._., 8205807-4 to also comprise the upper side 11 of the carrier material to increase the strength of the edge 10. A further improvement of the strength can be achieved by imparting the carrier material before the coating. a phase 12 according to Fig. 4. By coating both sides 2 and 3 of the scraper, two equivalent edges are provided so that when one edge is worn, the scraper can be turned so that the other edge can be brought into effective contact.
I fig. 3 har vinkeln mellan schabern och valsytan betecknats med ófl.In Fig. 3, the angle between the doctor blade and the roll surface has been denoted by ó fl.
I fig. 3a och 4a visas en utföringsform där den verksamma ytan utgöres av en liten fas 13. För övrigt är utföringsfor- merna enligt fig. 3 och 4 ekvivalenta med de i fig. 3a och 4a visade utföringsformerna.Figs. 3a and 4a show an embodiment in which the active surface consists of a small phase 13. Otherwise, the embodiments according to Figs. 3 and 4 are equivalent to the embodiments shown in Figs. 3a and 4a.
Vid papperskräppning definieras den s.k. stötvinkeln som vinkeln mellan schaberklingans överkant och cylinderytan. I fig. 3a har överkanten betecknats med 11 och i fig. 3a stöt- vinkeln med çf.In the case of paper scrapping, the so-called the angle of impact as the angle between the upper edge of the doctor blade and the cylinder surface. In Fig. 3a the upper edge is denoted by 11 and in Fig. 3a the angle of impact with çf.
Utföringsformerna enligt fig. 5 och 6 är ekvivalenta med ut- föringsformerna enligt fig. 3a och fig. 4a med undantag av att stötvinkeln 5.1 de två senare fallen är mindre.The embodiments according to Figs. 5 and 6 are equivalent to the embodiments according to Fig. 3a and Fig. 4a, except that the angle of impact 5.1 in the latter two cases is smaller.
Bärarmaterialet till schabern enligt uppfinningen utgöres lämpligen av ett kallvalsat, seghärdat fjäderstålband med en tjocklek av 0,15 - 2,0 mm och i sällsynta fall ännu tunnare.The carrier material for the doctor blade according to the invention suitably consists of a cold-rolled, toughened spring steel strip with a thickness of 0.15 - 2.0 mm and in rare cases even thinner.
Den enligt uppfinningen föreslagna beläggningens maximala tjocklek är beroende av bärarmaterialets tjocklek men bör un- der alla förhâllanden ej överstiga 0,35 mm. Beläggningen är uppbyggd av ett flertal genom metallsprutning på varandra an- ordnade delskikt, varvid varje delskikt exempelvis har en tjocklek av 0,002 - 0,045 mm. Lämpligen är beläggningens to- tala tjocklek högst 50 % av bärarmaterialets tjocklek för scha- bermaterial i tjocklekar upp till 0,40 mm, 40 % vid bärarmate- rial, som är 0,40 mm - 0,90 mm, 30 % vid bärarmaterial, som är stan n-fq 'FNFT - I» ~ -- ~e---í------_»-- . f...'-š“" um- _ U fiâšåäaàl CEj&fL_I___. --\ saga... ....-. 8205807 'Ä ß 0,90 - 1,20 mm och 25 % vid bärarmaterial som är 1,20 ~ 2,0 mm.The maximum thickness of the coating proposed according to the invention depends on the thickness of the carrier material but should not exceed 0.35 mm under all conditions. The coating is built up of a plurality of sub-layers arranged on each other by metal spraying, each sub-layer having, for example, a thickness of 0.002 - 0.045 mm. Suitably the total thickness of the coating is at most 50% of the thickness of the carrier material for scrapers in thicknesses up to 0.40 mm, 40% for carrier materials which are 0.40 mm - 0.90 mm, 30% for carrier materials, som är stan n-fq 'FNFT - I »~ - ~ e --- í ------_» -. f ...'- š “" um- _ U fi âšåäaàl CEj & fL_I ___. - \ saga ... ....-. 8205807 'Ä ß 0,90 - 1,20 mm and 25% for carrier materials that are 1, 20 ~ 2.0 mm.
Det enligt uppfinningen använda nötningsbeständiga ma- materialet i beläggningen kan lämpligen utgöras av kera- mer, metalloxider eller metallkarbider. Det för varje ändamål lämpligaste beläggningsmaterialet kan dock ibland behöva väljas med hänsyn till det aktuella användningsom- râdet. Även om vissa beläggningsmaterial, såsom exempelvis kromoxid ger en god nötningsbeständighet har det kunnat konstateras, att en sådan beläggning kan ge vissa nackdelar för en del användningsändamål. överraskande har beläggningar huvudsakligen bestående av aluminiumoxid visat sig vara synnerligen lämpliga och särskilt goda resultat har kunnat uppnås med belägg- ningar av alumhüumoxid (Al203) med en mindre halt av en annan metalloxid t.ex. titanoxid (Ti02).The abrasion-resistant material used in the coating in the coating may suitably be ceramics, metal oxides or metal carbides. However, the most suitable coating material for each purpose may sometimes need to be selected with regard to the area of use in question. Although certain coating materials, such as chromium oxide, provide good abrasion resistance, it has been found that such a coating can present certain disadvantages for some applications. Surprisingly, coatings consisting mainly of alumina have proved to be particularly suitable and particularly good results have been obtained with coatings of alumina (Al 2 O 3) with a lower content of another metal oxide, e.g. titanium oxide (TiO2).
Nedanstående försök med enligt uppfinningen framställda raklar eller schabrar bestyrker den enligt uppfinningen uppnådda eftersträvade förbättringen av konventionella schabrar.The following experiments with squeegees or scrapers produced according to the invention certify the desired improvement of conventional scrapers achieved according to the invention.
Försök 1 En enligt uppfinningen framställd 0,150 mm tjock rakel med en 0,050 mm tjock nötningsbeständig ytbeläggning av aluminiumoxid och titanoxid användes vid avrakling av en för gravyrtryck använd djuptryckscylinder.Experiment 1 A 0.150 mm thick doctor blade produced according to the invention with a 0.050 mm thick abrasion-resistant surface coating of alumina and titanium oxide was used when stripping a gravure printing cylinder used for gravure printing.
Den enligt uppfinningen framställda rakeln som var utförd enligt vad som visas i figur l gav mer än tredubblad livslängd jämfört med konventionella djuptrycksraklar och ett fullt likvärdigt avraklingsresultat.The squeegee made according to the invention, which was made as shown in Figure 1, gave more than three times the service life compared to conventional gravure squeegee squeegees and a fully equivalent squeegee result.
Försök 2 Vid framställning av kräppad tissue på en s.k. yankee- 8205807-4 maskin användes en kräppschaber enligt utföringsformen enligt fig. 6 med en nötningsbeständig beläggning av aluminiumoxid.Experiment 2 In the production of creped tissue on a so-called yankee machine 8205807-4 machine a crepe scraper according to the embodiment of Fig. 6 with an abrasion resistant coating of alumina was used.
Schabern av fjäderstål var 1,2 mm tjock och hade en 10 mm bred beläggning med en beläggningstjocklek av 0,200 mm. Ban- bredden var 3 m och banhastigheten uppgick till 900 m/min.The spring steel scraper was 1.2 mm thick and had a 10 mm wide coating with a coating thickness of 0.200 mm. The track width was 3 m and the track speed was 900 m / min.
Schabern som insattes i pappersmaskinens schaberhållare gav ett fullgott kräppningsresultat under en tid av 10 timmar.The scraper inserted in the paper machine's scraper holder gave a satisfactory creping result for a period of 10 hours.
Vid kräppning med konventionell kräppningsscbaber av samma material och tjocklek men utan nötningsbeständig beläggning måste den konventionella schabern bytas ut efter mindre än en timma pâ grund av att fasytan slitits ned så mycket attt kräppningen blev grov och ojämn. Tiden för schaberbytet var tre minuter vid användning av den konventionella schabern, vilket leder till en produktionsförlust av 5 procent, vilken således nästan helt kan intjänas genom användning av scha- bern enligt uppfinningen. 5 % produktionsförlust motsvarar 800 ton papper/år eller cirka 2,5 miljoner svenska kronor/år.When creping with a conventional creping scraper of the same material and thickness but without abrasion-resistant coating, the conventional scraper must be replaced after less than an hour due to the bevel surface being worn down so much that the creping became rough and uneven. The time for the scraper change was three minutes when using the conventional scraper, which leads to a production loss of 5 percent, which can thus be almost completely earned by using the scrapers according to the invention. 5% production loss corresponds to 800 tonnes of paper / year or approximately 2.5 million Swedish kronor / year.
När det gäller ytbeläggningens uppbyggnad bör bärarmaterialet innan det första delskiktet av beläggningen appliceras på bärarmaterialet inom den för beläggning avsedda ytzonen under- kastas en lämplig förberedande ytbehandling, exempelvis en försiktig blästring med karborundum, lämpligen omedelbart före applicerandet av nämnda första delskikt. I vissa fall kan det vara lämpligt, att ett bindeskikt av exempelvis en nickellegering eller liknande anbringas mellan bärarmateria- lets förbehandlade yta och det första delskiktet.With regard to the structure of the coating, the carrier material should be subjected to a suitable preparatory surface treatment, for example a gentle blasting with carborundum, before the first sublayer of the coating is applied to the carrier material within the surface zone to be coated, preferably immediately before applying said first sublayer. In some cases it may be appropriate for a bonding layer of, for example, a nickel alloy or the like to be applied between the pretreated surface of the carrier material and the first sublayer.
De olika delskikten appliceras därefter på ett sådant sätt på varandra, att bärarmaterialets ursprungliga elasticitet och jämnhet icke nämnvärt påverkas.The various sublayers are then applied to each other in such a way that the original elasticity and smoothness of the carrier material are not appreciably affected.
Beläggningszonens bredd.5a skall maximalt uppgå till 20 mm och företrädesvis vara mindre än 10 mm. gm* .må I ..i._,The width of the coating zone 5a should not exceed 20 mm and preferably be less than 10 mm. gm * .må I ..i._,
Claims (10)