SE436330B - Sett att minska mengden fri formaldehyd i karbamidhartsbundna spanskivor - Google Patents
Sett att minska mengden fri formaldehyd i karbamidhartsbundna spanskivorInfo
- Publication number
- SE436330B SE436330B SE7908455A SE7908455A SE436330B SE 436330 B SE436330 B SE 436330B SE 7908455 A SE7908455 A SE 7908455A SE 7908455 A SE7908455 A SE 7908455A SE 436330 B SE436330 B SE 436330B
- Authority
- SE
- Sweden
- Prior art keywords
- free formaldehyde
- ammonium
- ammonium compounds
- ammonia
- reduce
- Prior art date
Description
vsoanss-up 5 2
av en termiskt sönderdelbar ammoniumförening, varpå skivorna
staplas för mognadslagringm Skivorna i stapeln har härvid
normalt en temperatur av 40-70°C. Under mognadslagringen, som
vanligen försiggår 2 dygn, sönderdelas ammoniumföreningen och
avger ammoniakgas, vilken tränger in i skivorna. Efter mognads-
lagringen går skivorna som förut till formatsâgning och slip-
ning. Skivorna, som i övrigt är till sina egenskaper oför-
ändrade, innehåller nu avsevärt mindre mängd fri formaldehyd.
I enlighet med det ovan sagda har sättet enligt upp-
finningen de i krav 1 angivna kännetecknen.
Med hänsyn till den normala temperaturen under mognads-
lagringen används som ammoniumföreningar företrädesvis sådana
som vid 40-70°C avger ammoniak i väsentlig grad. Speciellt
föredragna föreningar är ammoniumvätekarbonat och ammonium-
karbonat, eventuellt i kombination med ammoniumacetat för
sänkning av pH. Den använda ammoniumföreningen får givetvis
ej vara explosiv och den får ej heller vid sin sönderdelning
ge oacceptabla restjoner eller föreningar.
Ammoniumföreningarna kan appliceras exempelvis i pulver-
form eller i form av en vattenlösning, vilken företrädesvis
är koncentrerad.
En klar sänkning av halten fri formaldehyd uppnås i all-
mänhet redan vid 5 g ammoniumsalt / m2. Företrädesvis an-
vänds minst 10 g / m2. I allmänhet uppnås endast marginella
ytterligare förbättringar genom ökning av halten över 40-Sö
g / m2. Samtliga mängder är härvid beräknade på 15 mm skivor.
Uppfinningen kommer i det följande att illustreras när-
mare av ett antal utföringsexempel, vilka samtliga är ut-
förda med spânskivor av storleken 500 x 500 mm.
- Exempel 1
Spânskivor med tjockleken 12 mm belades med finpulvri-
serad ammoniumkarbonat, 10 g / mg staplades och lagrades 48
timmar vid 60°C temperatur.
Exempel 2
Spânskivor med tjockleken 12 mm belades med finpulvri-
serad ammoniumkarbonat, 20 g / m2, staplades och lagrades
19084554»
48 timmar vid 60°C temperatur.
Exemgel 3
Spånskivor med tjockleken 16 mm belades med finpulvri-
serad ammoniumkarbonat, 15 g / m2, staplades och lagrades
48 timmar vid 40°C temperatur. _
Exemgel 4
Spânskivor med tjockleken 16 mm besprutades med vatten-
lösning av 20 g ammoniumkarbonat i 100 g lösning och belades
med 50 g lösning / m2, staplades och lagrades 48 timmar vid
60°C temperatur.
Exemgel 5
Spånskivor med tjockleken 16 mm besprutades med en vatten-
lösning av 20 g ammoniumkarbonat i 100 g vatten och belades
med 100 g lösning / m2, staplades och lagrades 48 timmar
vid 60°C temperatur.
Exemgel 6
Spånskivor med tjockleken 16 mm besprutades medken
vattenlösning av 16 g ammoniumkarbonat och 4 g ammonium-
acetat i 100 g lösning och belades med 100 g lösning / m2,
staplades och lagrades 48 timar vid 60°C temperatur.
Vid samtliga försök bestämdes efter konditionering halten
fri formaldehyd enligt FESYP-perforatormetod (British I
Standard 1811). På en del av proven mättes svällning, tvär-
draghållfasthet och böjhållfasthet enligt DIN 68761. Som
referensprov användes motsvarande enbart värmebehandlade och
konditionerade skivor. Varje försök utfördes med sex skivor.
Mätresultaten återges i nedanstående tabell.
7908115541
H
Tabell
Skiv- Lagr. ' Tvär- Böj- Fri
Exempel tjock- g salt temp. Svälln. drag- hållf. formal-
lek 2 o ' hâllf. dehyd
'mm / m C MPa Ma vikt-%
1 12 10 60 0,016
2 12 20 60 0,011
3 16 15 40 I 0,75 17,0 0,012
4 16 10 60 , 0,35 16,0 0,017
5 16 20 60 , 0,36 18,8 0,012
6 16 20_ '60 0,013
Ref 1 12 0 60 0,032
Ref 2 16 0 60 8,6 0,32 17.2 0,030
Claims (3)
1. sätt att minska mängden fri formaldehyd i karbamid- hartsbundna spånskivor, varvid skivorna belägqs med en lösning av ett ammoniakavspaltande ämne och de så behandlade skivorna staplas för mognadslagring, k ä n n e t e c k n a t a V att skivorna efter pressningen kyls till en för moqnadslagring i stapel konventionell temperatur, att som ammoniakavspaltande ämne används en eller flera ammoniumföreningar som vid 40-70°C avger ammoniak i väsentlig grad och att lösningen av ammonium- föreningarna appliceras på de kylda skivorna.
2. Sätt enligt krav 1, k ä n n e t e c k n a t a v att som ammoniumföreningar används ammoniumkarbonat och/eller ammoniumvätekarbonat.
3. Sätt enligt krav 1 eller 2, k ä n n e t e c k n a t a v att ammoniumföreningarna används i vattenlösning. _ véoaass-4 SAMNLÅNDiQAÉ I Ett sätt att minska mängden fri formaldehyd i karbamid- hartsbundna spânskivor genom behandling med ammoniakgas under bildning áv hexametylentetramin. Ammoniakgasen alstras in situ genom termisk sönderdelning av en eller flera ammonium- föreningar.