RU99112113A - Стеклянные нити, пригодные для упрочнения органических и/или неорганических материалов - Google Patents
Стеклянные нити, пригодные для упрочнения органических и/или неорганических материаловInfo
- Publication number
- RU99112113A RU99112113A RU99112113/03A RU99112113A RU99112113A RU 99112113 A RU99112113 A RU 99112113A RU 99112113/03 A RU99112113/03 A RU 99112113/03A RU 99112113 A RU99112113 A RU 99112113A RU 99112113 A RU99112113 A RU 99112113A
- Authority
- RU
- Russia
- Prior art keywords
- less
- glass
- cao
- mgo
- composition
- Prior art date
Links
- 239000011521 glass Substances 0.000 title claims 15
- 229910010272 inorganic material Inorganic materials 0.000 title claims 2
- 239000011147 inorganic material Substances 0.000 title claims 2
- 239000011368 organic material Substances 0.000 title claims 2
- 238000005728 strengthening Methods 0.000 title claims 2
- ODINCKMPIJJUCX-UHFFFAOYSA-N calcium monoxide Chemical compound [Ca]=O ODINCKMPIJJUCX-UHFFFAOYSA-N 0.000 claims 18
- CPLXHLVBOLITMK-UHFFFAOYSA-N magnesium oxide Chemical compound [Mg]=O CPLXHLVBOLITMK-UHFFFAOYSA-N 0.000 claims 14
- 229910018068 Li 2 O Inorganic materials 0.000 claims 9
- 239000000203 mixture Substances 0.000 claims 9
- 239000002699 waste material Substances 0.000 claims 5
- 229910004298 SiO 2 Inorganic materials 0.000 claims 4
- 229910010413 TiO 2 Inorganic materials 0.000 claims 4
- 239000002994 raw material Substances 0.000 claims 3
- 229910018072 Al 2 O 3 Inorganic materials 0.000 claims 2
- 239000000835 fiber Substances 0.000 claims 2
- VASIZKWUTCETSD-UHFFFAOYSA-N manganese(II) oxide Inorganic materials [Mn]=O VASIZKWUTCETSD-UHFFFAOYSA-N 0.000 claims 2
- 239000006060 molten glass Substances 0.000 claims 2
- 239000002131 composite material Substances 0.000 claims 1
- 238000004519 manufacturing process Methods 0.000 claims 1
- 239000011159 matrix material Substances 0.000 claims 1
Claims (11)
1. Упрочняющая стеклянная нить, композиция которой включает следующие компоненты в пределах, определенных ниже, вес.%:
SiO2 - 58 - 62
А12O3 - 10 - 16
СаO - более 18
MgO - более 1,5
CaO + МgO - менее 28
Na2O + K2O + Li2O - менее 2
TiO2 - менее 1,5
Fe2O3 - менее 0,5
B2O3 - менее 2
F2 - менее 2
причем эта композиция содержит кроме того менее 1% другого (их) компонента (ов) и более 0,5% по меньшей мере одного из трех компонентов F2, B2O3 и Li2O.
SiO2 - 58 - 62
А12O3 - 10 - 16
СаO - более 18
MgO - более 1,5
CaO + МgO - менее 28
Na2O + K2O + Li2O - менее 2
TiO2 - менее 1,5
Fe2O3 - менее 0,5
B2O3 - менее 2
F2 - менее 2
причем эта композиция содержит кроме того менее 1% другого (их) компонента (ов) и более 0,5% по меньшей мере одного из трех компонентов F2, B2O3 и Li2O.
2. Стеклянная нить по п.1, отличающаяся тем, что стекло для получения нити имеет вязкость 102.5 пуаз при температуре 1200 - 1380°С и вязкость 103 пуаз при температуре 1110 - 1290°С.
3. Стеклянная нить по любому из пп.1 и 2, отличающаяся тем, что в ее композиции суммарное содержание СаO и МgO обычно составляет более 21 вес.%, причем содержания СаО и МgO не превышают 26 и 10%, соответственно.
4. Стеклянная нить по одному из пп.1-3, отличающаяся тем, что ее композиция включает следующие компоненты в определенных ниже пределах, вес.%:
SiO2 - 58,5 - 61
Аl2O3 - 11 - 14
СаO - 21 - 23
MgO - 2 - 3,5
Na2O + K2O + Li2O - 0,5 - 1,8
TiO2 - 0 - 1
Fe2O3 - 0 - 0,4
B2O3 - до 1,8
F2 - до 1,8
причем эта композиция содержит кроме того по меньшей мере 0,7% по меньшей мере одного из трех компонентов F2, B2O3, Li2O и менее 1% другого(их) компонента(ов) F2, B2O3 и Li2O.
SiO2 - 58,5 - 61
Аl2O3 - 11 - 14
СаO - 21 - 23
MgO - 2 - 3,5
Na2O + K2O + Li2O - 0,5 - 1,8
TiO2 - 0 - 1
Fe2O3 - 0 - 0,4
B2O3 - до 1,8
F2 - до 1,8
причем эта композиция содержит кроме того по меньшей мере 0,7% по меньшей мере одного из трех компонентов F2, B2O3, Li2O и менее 1% другого(их) компонента(ов) F2, B2O3 и Li2O.
5. Композит, полученный из стеклянных нитей и по меньшей мере из органических или неорганических материалов, отличающийся тем, что он содержит стеклянные нити по одному из пп.1-4.
6. Способ получения стеклянных нитей по одному из пп.1-4, в котором вытягивают множество струек расплавленного стекла, причем они вытекают из множества отверстий, расположенных в основании одной или нескольких матриц, в форме одного или нескольких пучков непрерывных волокон, а затем волокна соединяют в одну или несколько нитей, которые накапливают на подвижном суппорте.
7. Способ по п.6, отличающийся тем, что расплавленное стекло, подаваемое к отверстиям в матрице(ах), имеет следующую композицию, вес.%:
SiO2 - 58 - 62
А12O3 - 10 - 16
СаO - более 18
MgO - более 1,5
CaO + МnO - менее 28
Na2O + K2O + Li2O - менее 2
TiO2 - менее 1,5
Fe2O3 - менее 0,5
B2O3 - менее 2
F2 - менее 2
причем эта композиция содержит кроме того менее 1% другого(их) компонента(ов) и более 0,5% по меньшей мере одного из трех компонентов F2, B2O3 и Li2O.
SiO2 - 58 - 62
А12O3 - 10 - 16
СаO - более 18
MgO - более 1,5
CaO + МnO - менее 28
Na2O + K2O + Li2O - менее 2
TiO2 - менее 1,5
Fe2O3 - менее 0,5
B2O3 - менее 2
F2 - менее 2
причем эта композиция содержит кроме того менее 1% другого(их) компонента(ов) и более 0,5% по меньшей мере одного из трех компонентов F2, B2O3 и Li2O.
8. Способ по п.6 или 7, отличающийся тем, что расплавленное стекло получают из сырьевых материалов, смешанных в подходящих пропорциях с по меньшей мере несколькими из упомянутых сырьевых материалов, представляющих собой отходы стеклянных нитей.
9. Способ по п.8, отличающийся тем, что отходы представляют собой отходы нитей из Е-стекла и/или отходы стеклянных нитей, как определено по одному из пп.1-4.
10. Способ по п.8 или 9, отличающийся тем, что отходы составляют 0 - 35 вес.% от сырьевых материалов.
11. Стекольная композиция, предназначенная для получения стеклянных нитей, используемых для упрочнения, включающая следующие компоненты в пределах, определенных ниже, вес.%:
SiO2 - 58 - 62
Аl2O3 - 10 - 16
СаO - более 18
MgO - более 1,5
CaO + МnO - менее 28
Na2O + K2O + Li2O - менее 2
TiO2 - менее 1,5
Fe2O3 - менее 0,5
B2O3 - менее 2
F2 - менее 2
причем эта композиция содержит кроме того менее 1% другого(их) компонента(ов) и более 0,5% по меньшей мере одного из трех компонентов F2, B2O3 и Li2O.
SiO2 - 58 - 62
Аl2O3 - 10 - 16
СаO - более 18
MgO - более 1,5
CaO + МnO - менее 28
Na2O + K2O + Li2O - менее 2
TiO2 - менее 1,5
Fe2O3 - менее 0,5
B2O3 - менее 2
F2 - менее 2
причем эта композиция содержит кроме того менее 1% другого(их) компонента(ов) и более 0,5% по меньшей мере одного из трех компонентов F2, B2O3 и Li2O.