RU2415827C1 - Glase mixture - Google Patents
Glase mixture Download PDFInfo
- Publication number
- RU2415827C1 RU2415827C1 RU2009146318/03A RU2009146318A RU2415827C1 RU 2415827 C1 RU2415827 C1 RU 2415827C1 RU 2009146318/03 A RU2009146318/03 A RU 2009146318/03A RU 2009146318 A RU2009146318 A RU 2009146318A RU 2415827 C1 RU2415827 C1 RU 2415827C1
- Authority
- RU
- Russia
- Prior art keywords
- glase
- dolomite
- borax
- pegmatite
- boric acid
- Prior art date
Abstract
Description
Изобретение относится к технологии силикатов и касается шихтовых составов глазурей для нанесения на керамическую плитку, изразцы.The invention relates to the technology of silicates and for charge compositions of glazes for application on ceramic tiles, tiles.
Известен также шихтовый состав глазури, включающий, мас.%: пегматит 26-30; кварцевый песок 20-21; бура 5-33; карбонат стронция 3-15; доломит 2-5; сода кальцинированная 3-6; борная кислота 5-26 [1].The charge composition of the glaze is also known, including, wt.%: Pegmatite 26-30; silica sand 20-21; borax 5-33; strontium carbonate 3-15; dolomite 2-5; soda ash 3-6; boric acid 5-26 [1].
Задача изобретения состоит в повышении термостойкости глазури.The objective of the invention is to increase the heat resistance of the glaze.
Технический результат достигается тем, что в шихтовом составе глазури, включающем пегматит, кварцевый песок, буру, карбонат стронция, доломит, соду кальцинированную, борную кислоту, компоненты находятся при следующем соотношении, мас.%: пегматит 35-36; кварцевый песок 24-26; бура 18-20; карбонат стронция 8-10; доломит 6-7; сода кальцинированная 1-2; борная кислота 3-4.The technical result is achieved by the fact that in the charge composition of the glaze, including pegmatite, quartz sand, borax, strontium carbonate, dolomite, soda ash, boric acid, the components are in the following ratio, wt.%: Pegmatite 35-36; silica sand 24-26; borax 18-20; strontium carbonate 8-10; dolomite 6-7; soda ash 1-2; boric acid 3-4.
В таблице приведены варианты шихтового состава глазури.The table shows the options for the charge composition of the glaze.
Компоненты дозируют в требуемых количествах, измельчают, смешивают и при температуре 1400°С варят фритту. Расплав гранулируют в воду. Фритту размалывают до полного прохождения через сетку №008 и подготавливают суспензию влажностью 45-47%. Готовую глазурную суспензию наносят (напылением, поливом, окунанием) на поверхность керамических изделий, сушат на воздухе и обжигают при температуре 950°С в течение 30-45 мин.The components are dosed in the required quantities, crushed, mixed and the frit is cooked at a temperature of 1400 ° C. The melt is granulated into water. The frit is ground until it passes through mesh No. 008 and a suspension is prepared with a moisture content of 45-47%. The finished glaze suspension is applied (by spraying, watering, dipping) on the surface of ceramic products, dried in air and burned at a temperature of 950 ° C for 30-45 minutes.
Термостойкость глазури (нагрев до 100°С - охлаждение до 20°С и воде) составит 8-10 теплосмен.The temperature resistance of the glaze (heating to 100 ° C - cooling to 20 ° C and water) will be 8-10 heat changes.
Источники информацииInformation sources
1. А.с. №872515 СССР, 1981.1. A.S. No. 872515 USSR, 1981.
Claims (1)