RU2219191C2 - Способ получения привитого сополимера с регулируемой структурой - Google Patents
Способ получения привитого сополимера с регулируемой структурой Download PDFInfo
- Publication number
- RU2219191C2 RU2219191C2 RU98122995/04A RU98122995A RU2219191C2 RU 2219191 C2 RU2219191 C2 RU 2219191C2 RU 98122995/04 A RU98122995/04 A RU 98122995/04A RU 98122995 A RU98122995 A RU 98122995A RU 2219191 C2 RU2219191 C2 RU 2219191C2
- Authority
- RU
- Russia
- Prior art keywords
- copolymer
- ethylene
- propylene
- olefin
- group
- Prior art date
Abstract
Изобретение относится к способу привитой сополимеризации полипропиленовых материалов. Способ получения привитого сополимера с регулируемой структурой включает: (а) обработку полипропиленового материала инициатором свободнорадикальной полимеризации, (в) обработку полипропиленового материала, по крайней мере, одним прививающимся мономером, способным полимеризоваться за счет свободных радикалов в присутствии регулятора скорости полимеризации, способного функционировать в по существу неокислительной среде, для замедления полимеризации на поверхности частиц таким образом, что содержание полимеризованного мономера ниже на поверхности частиц, чем внутри частиц, и (с) удаление любого непрореагировавшего мономера, разложение любого непрореагировавшего инициатора и дезактивацию любых остаточных свободных радикалов в материале. Технической задачей является разработка способа привитой сополимеризации полипропиленовых материалов, при котором будет ингибироваться поверхностная полимеризация и, как следствие этого, будет улучшаться технологичность получаемых полимерных частиц. 5 з.п.ф-лы, 15 табл., 8 ил.
Description
Текст описания в факсимильном виде (см. графическую часть) Тк
Claims (6)
1. Способ получения привитого сополимера в по существу неокислительной среде, включающий: (а) обработку частиц полипропиленового материала органическим соединением, которое является инициатором свободнорадикальной полимеризации; (b) обработку полипропиленового материала в течение периода времени, который совпадает с (а) или следует за (а), с или без перекрытия, и использованием примерно 5-240 ч, по крайней мере, одного прививающегося мономера, способного полимеризоваться за счет свободных радикалов, на 100 ч полипропиленового материала в присутствии регулятора скорости полимеризации, способного функционировать в по существу неокислительной среде, для замедления полимеризации на поверхности частиц таким образом, что содержание полимеризованного мономера ниже на поверхности частиц, чем внутри частиц; и (с) удаление любого непрореагировавшего прививающегося мономера из получающегося привитого полипропиленового материала, разложение любого непрореагировавшего инициатора и дезактивацию любых остаточных свободных радикалов в материале.
2. Способ по п.1, отличающийся тем, что полипропиленовый материал выбирают из группы, состоящей из: (а) кристаллического гомополимера пропилена, имеющего показатель стереорегулярности более 80; (b) кристаллического статистического сополимера пропилена и олефина, выбранного из группы, состоящей из этилена и α-С4-10-олефинов, при условии, что когда олефином является этилен, максимальное содержание полимеризованного этилена составляет 10 маc.%, а когда олефином является α-С4-10-олефин, максимальное содержание полимеризованного α-олефина составляет 20 маc.%, причем сополимер имеет показатель стереорегулярности более 85; (c) кристаллического статистического терполимера пропилена и двух олефинов, выбранных из группы, состоящей из этилена и α-С4-8-олефинов, при условии, что максимальное содержание полимеризованного α-С4-8-олефина составляет 20 маc.%, а когда одним из олефином является этилен, максимальное содержание полимеризованного этилена составляет 5 маc.%, причем терполимер имеет показатель стереорегулярности более 85; (d) полиолефиновой композиции, содержащей: (i) примерно 10-60 мас.ч. кристаллического гомополимера пропилена, имеющего показатель стереорегулярности более 80, или кристаллического сополимера, выбранного из группы, состоящей из (а) сополимера пропилена и этилена, (b) сополимера пропилена, этилена и α-С4-8-олефина и (с) сополимера пропилена и α-С4-8-олефина, причем сополимер имеет содержание пропилена более 85 маc.% и показатель стереорегулярности более 85; (ii) примерно 3-25 мас.ч. сополимера этилена и пропилена или α-С4-8-олефина, который является нерастворимым в ксилоле при температуре окружающей среды; и (iii) примерно 30-70 мас.ч. эластомерного сополимера, выбранного из группы, состоящей из (а) сополимера этилена и пропилена, (b) сополимера этилена, пропилена и α-С4-8-олефина и (с) сополимера этилена и α-С4-8-олефина, причем сополимер необязательно содержит примерно 0,5-10 маc.% диена, содержит менее 70 маc.% этилена, является растворимым в ксилоле при температуре окружающей среды и имеет характеристическую вязкость примерно 1,5-4,0 дл/г; причем сумма (ii) и (iii) по отношению к общей массе полиолефиновой композиции составляет от примерно 50 до примерно 90%, а массовое соотношение (ii) : (iii) составляет менее 0,4, где композиция получается полимеризацией, по крайней мере, в две стадии и имеет модуль упругости при изгибе менее 150 МПа; и (е) термопластичного полиолефина, содержащего: (i) примерно 10-60% гомополимера пропилена, имеющего показатель стереорегулярности более 80, или кристаллического сополимера, выбранного из группы, состоящей из (а) сополимера этилена и пропилена, (b) сополимера этилена, пропилена и α-С4-8-олефина и (с) сополимера этилена и α-С4-8-олефина, причем сополимер имеет содержание пропилена более 85 маc.% и показатель стереорегулярности более 85; (ii) примерно 20-60% аморфного сополимера, выбранного из группы, состоящей из (а) сополимера этилена и пропилена, (b) сополимера этилена, пропилена и α-С4-8-олефина и (с) сополимера этилена и α-С4-8-олефина, причем сополимер необязательно содержит примерно 0,5-10% диена, содержит менее 70% этилена и является растворимым в ксилоле при температуре окружающей среды; и (iii) примерно 3-40% сополимера этилена и пропилена или α-С4-8-олефина, который является нерастворимым в ксилоле при температуре окружающей среды, где композиция имеет модуль упругости при изгибе более 150 МПа, но менее 1200 МПа.
3. Способ по п.2, отличающийся тем, что полипропиленовым материалом является гомополимер пропилена.
4. Способ по п.1, отличающийся тем, что прививающийся мономер выбирается из группы, состоящей из стирола, метилметакрилата, метилакрилата, метакриловой кислоты, малеинового ангидрида и акрилонитрила.
5. Способ по п.1, отличающийся тем, что регулятор полимеризации выбирается из группы, состоящей из (а) серы, (b) бензохинона и его производных и (с) гидроксиламина и его производных.
6. Способ по п.5, отличающийся тем, что регулятором полимеризации является N,N-диэтилгидроксиламин.