RU2018107241A - СПОСОБ ПОЛУЧЕНИЯ NOx АККУМУЛИРУЮЩИХ МАТЕРИАЛОВ - Google Patents
СПОСОБ ПОЛУЧЕНИЯ NOx АККУМУЛИРУЮЩИХ МАТЕРИАЛОВ Download PDFInfo
- Publication number
- RU2018107241A RU2018107241A RU2018107241A RU2018107241A RU2018107241A RU 2018107241 A RU2018107241 A RU 2018107241A RU 2018107241 A RU2018107241 A RU 2018107241A RU 2018107241 A RU2018107241 A RU 2018107241A RU 2018107241 A RU2018107241 A RU 2018107241A
- Authority
- RU
- Russia
- Prior art keywords
- mixture
- range
- temperature
- minutes
- dried
- Prior art date
Links
- 239000000463 material Substances 0.000 title claims 4
- 238000004519 manufacturing process Methods 0.000 title claims 2
- 239000000203 mixture Substances 0.000 claims 29
- 238000000034 method Methods 0.000 claims 20
- MWUXSHHQAYIFBG-UHFFFAOYSA-N Nitric oxide Chemical compound O=[N] MWUXSHHQAYIFBG-UHFFFAOYSA-N 0.000 claims 18
- 239000011363 dried mixture Substances 0.000 claims 8
- 238000001354 calcination Methods 0.000 claims 6
- 239000003054 catalyst Substances 0.000 claims 3
- 238000001035 drying Methods 0.000 claims 3
- 239000011232 storage material Substances 0.000 claims 3
- 238000000227 grinding Methods 0.000 claims 2
- 238000002156 mixing Methods 0.000 claims 2
- 101500015541 Aedes aegypti Trypsin-modulating oostatic factor Proteins 0.000 claims 1
- 229910052788 barium Inorganic materials 0.000 claims 1
- AYJRCSIUFZENHW-UHFFFAOYSA-L barium carbonate Chemical compound [Ba+2].[O-]C([O-])=O AYJRCSIUFZENHW-UHFFFAOYSA-L 0.000 claims 1
- 230000003197 catalytic effect Effects 0.000 claims 1
- CETPSERCERDGAM-UHFFFAOYSA-N ceric oxide Chemical compound O=[Ce]=O CETPSERCERDGAM-UHFFFAOYSA-N 0.000 claims 1
- 229910000422 cerium(IV) oxide Inorganic materials 0.000 claims 1
- 239000007789 gas Substances 0.000 claims 1
- 239000002245 particle Substances 0.000 claims 1
- 238000006467 substitution reaction Methods 0.000 claims 1
- 239000000758 substrate Substances 0.000 claims 1
Classifications
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J27/00—Catalysts comprising the elements or compounds of halogens, sulfur, selenium, tellurium, phosphorus or nitrogen; Catalysts comprising carbon compounds
- B01J27/20—Carbon compounds
- B01J27/232—Carbonates
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J37/00—Processes, in general, for preparing catalysts; Processes, in general, for activation of catalysts
- B01J37/0009—Use of binding agents; Moulding; Pressing; Powdering; Granulating; Addition of materials ameliorating the mechanical properties of the product catalyst
- B01J37/0018—Addition of a binding agent or of material, later completely removed among others as result of heat treatment, leaching or washing,(e.g. forming of pores; protective layer, desintegrating by heat)
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01D—SEPARATION
- B01D53/00—Separation of gases or vapours; Recovering vapours of volatile solvents from gases; Chemical or biological purification of waste gases, e.g. engine exhaust gases, smoke, fumes, flue gases, aerosols
- B01D53/34—Chemical or biological purification of waste gases
- B01D53/92—Chemical or biological purification of waste gases of engine exhaust gases
- B01D53/94—Chemical or biological purification of waste gases of engine exhaust gases by catalytic processes
- B01D53/9404—Removing only nitrogen compounds
- B01D53/9409—Nitrogen oxides
- B01D53/9413—Processes characterised by a specific catalyst
- B01D53/9422—Processes characterised by a specific catalyst for removing nitrogen oxides by NOx storage or reduction by cyclic switching between lean and rich exhaust gases (LNT, NSC, NSR)
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J23/00—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00
- B01J23/10—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of rare earths
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J23/00—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00
- B01J23/38—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of noble metals
- B01J23/54—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of noble metals combined with metals, oxides or hydroxides provided for in groups B01J23/02 - B01J23/36
- B01J23/56—Platinum group metals
- B01J23/63—Platinum group metals with rare earths or actinides
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J31/00—Catalysts comprising hydrides, coordination complexes or organic compounds
- B01J31/02—Catalysts comprising hydrides, coordination complexes or organic compounds containing organic compounds or metal hydrides
- B01J31/12—Catalysts comprising hydrides, coordination complexes or organic compounds containing organic compounds or metal hydrides containing organo-metallic compounds or metal hydrides
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J35/00—Catalysts, in general, characterised by their form or physical properties
- B01J35/30—Catalysts, in general, characterised by their form or physical properties characterised by their physical properties
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J35/00—Catalysts, in general, characterised by their form or physical properties
- B01J35/40—Catalysts, in general, characterised by their form or physical properties characterised by dimensions, e.g. grain size
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J35/00—Catalysts, in general, characterised by their form or physical properties
- B01J35/50—Catalysts, in general, characterised by their form or physical properties characterised by their shape or configuration
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J35/00—Catalysts, in general, characterised by their form or physical properties
- B01J35/50—Catalysts, in general, characterised by their form or physical properties characterised by their shape or configuration
- B01J35/56—Foraminous structures having flow-through passages or channels, e.g. grids or three-dimensional monoliths
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J35/00—Catalysts, in general, characterised by their form or physical properties
- B01J35/60—Catalysts, in general, characterised by their form or physical properties characterised by their surface properties or porosity
- B01J35/61—Surface area
- B01J35/613—10-100 m2/g
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J37/00—Processes, in general, for preparing catalysts; Processes, in general, for activation of catalysts
- B01J37/0009—Use of binding agents; Moulding; Pressing; Powdering; Granulating; Addition of materials ameliorating the mechanical properties of the product catalyst
- B01J37/0027—Powdering
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J37/00—Processes, in general, for preparing catalysts; Processes, in general, for activation of catalysts
- B01J37/0009—Use of binding agents; Moulding; Pressing; Powdering; Granulating; Addition of materials ameliorating the mechanical properties of the product catalyst
- B01J37/0027—Powdering
- B01J37/0036—Grinding
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J37/00—Processes, in general, for preparing catalysts; Processes, in general, for activation of catalysts
- B01J37/02—Impregnation, coating or precipitation
- B01J37/0201—Impregnation
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J37/00—Processes, in general, for preparing catalysts; Processes, in general, for activation of catalysts
- B01J37/02—Impregnation, coating or precipitation
- B01J37/0234—Impregnation and coating simultaneously
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J37/00—Processes, in general, for preparing catalysts; Processes, in general, for activation of catalysts
- B01J37/04—Mixing
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J37/00—Processes, in general, for preparing catalysts; Processes, in general, for activation of catalysts
- B01J37/08—Heat treatment
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01D—SEPARATION
- B01D2255/00—Catalysts
- B01D2255/10—Noble metals or compounds thereof
- B01D2255/102—Platinum group metals
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01D—SEPARATION
- B01D2255/00—Catalysts
- B01D2255/10—Noble metals or compounds thereof
- B01D2255/102—Platinum group metals
- B01D2255/1021—Platinum
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01D—SEPARATION
- B01D2255/00—Catalysts
- B01D2255/10—Noble metals or compounds thereof
- B01D2255/102—Platinum group metals
- B01D2255/1023—Palladium
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01D—SEPARATION
- B01D2255/00—Catalysts
- B01D2255/10—Noble metals or compounds thereof
- B01D2255/102—Platinum group metals
- B01D2255/1025—Rhodium
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01D—SEPARATION
- B01D2255/00—Catalysts
- B01D2255/20—Metals or compounds thereof
- B01D2255/204—Alkaline earth metals
- B01D2255/2042—Barium
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01D—SEPARATION
- B01D2255/00—Catalysts
- B01D2255/20—Metals or compounds thereof
- B01D2255/206—Rare earth metals
- B01D2255/2065—Cerium
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01D—SEPARATION
- B01D2255/00—Catalysts
- B01D2255/20—Metals or compounds thereof
- B01D2255/209—Other metals
- B01D2255/2092—Aluminium
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01D—SEPARATION
- B01D2255/00—Catalysts
- B01D2255/90—Physical characteristics of catalysts
- B01D2255/91—NOx-storage component incorporated in the catalyst
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01D—SEPARATION
- B01D2255/00—Catalysts
- B01D2255/90—Physical characteristics of catalysts
- B01D2255/915—Catalyst supported on particulate filters
- B01D2255/9155—Wall flow filters
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
- Y02T—CLIMATE CHANGE MITIGATION TECHNOLOGIES RELATED TO TRANSPORTATION
- Y02T10/00—Road transport of goods or passengers
- Y02T10/10—Internal combustion engine [ICE] based vehicles
- Y02T10/12—Improving ICE efficiencies
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Materials Engineering (AREA)
- Organic Chemistry (AREA)
- Environmental & Geological Engineering (AREA)
- Health & Medical Sciences (AREA)
- Biomedical Technology (AREA)
- Combustion & Propulsion (AREA)
- Analytical Chemistry (AREA)
- General Chemical & Material Sciences (AREA)
- Oil, Petroleum & Natural Gas (AREA)
- Physics & Mathematics (AREA)
- Thermal Sciences (AREA)
- Catalysts (AREA)
- Exhaust Gas Treatment By Means Of Catalyst (AREA)
- Solid-Sorbent Or Filter-Aiding Compositions (AREA)
Claims (35)
1. Способ получения карбоната бария (ВаСО3), нанесенного на подложку из диоксида церия (СеО2), включающий:
смешивание Ва(ОН)2 с CeCO2 и Н2О с обеспечением смеси;
сушку смеси при температуре в интервале от около 100°C до около 150°C с обеспечением высушенной смеси; и
кальцинирование высушенной смеси при температуре в интервале от около 40°C до около 700°C.
2. Способ по п. 1, где высушенную смесь кальцинируют в атмосфере воздуха при температуре в интервале от около 40°C до около 450°C.
3. Способ по п. 1, где высушенную смесь кальцинируют в атмосфере газообразного СО2.
4. Способ по п. 3, где высушенную смесь кальцинируют при температуре кальцинирования в интервале от около 400°C до около 700°C.
5. Способ по п. 4, где высушенную смесь кальцинируют в течение периода времени в интервале от около 30 минут до около 120 минут.
6. Способ по п. 5, где высушенную смесь кальцинируют в течение периода времени в интервале от около 45 минут до около 75 минут.
7. Способ по п. 5, где высушенную смесь нагревают от комнатной температуры до температуры кальцинирования за период времени от около 150 минут до около 210 минут.
8. Способ по п. 1, где количество Ва(ОН)2 в смеси Ва(ОН)2, СеО2 и Н2О находится в интервале от 2% до около 15 мас. %, и количество Н2О в смеси Ва(ОН)2, СеО2 и Н2О находится в интервале от 30% до около 50 мас. %, и смесь Ва(ОН)2, СеО2 и Н2О в общем составляет 100%.
9. Способ по п. 1, где количество Ва(ОН)2 в смеси Ва(ОН)2, СеО2 и Н2О находится в интервале от 10% до около 15 мас. %, и количество Н2О в смеси Ва(ОН)2, СеО2 и Н2О находится в интервале от 35% до около 45 мас. %, и смесь Ва(ОН)2, СеО2 и Н2О в общем составляет 100%.
10. Способ по п. 1, где смесь сушат при температуре в интервале от около 125°C до около 135°C в течение периода времени в интервале от около 8 часов до около 18 часов.
11. Способ по п. 1, где смесь сушат в течение периода времени в интервале от около 10 часов до около 14 часов.
12. Способ по любому из пп. 1-11, где смесь измельчают в шаровой мельнице в течение периода времени в интервале от около 30 минут до около 60 минут.
13. Способ получения аккумулирующих оксиды азота материалов, включающий:
получение смеси Ва(ОН)2, СеО2 и Н2О, где Ва(ОН)2 присутствует в количестве вплоть до максимальной растворимости Ва(ОН)2 в Н2О при температуре Н2О, и СеО2 присутствует в количестве от около 1,75 до около 2,0 раз превышающем количество Ва(ОН)2 по массе;
измельчение смеси в течение периода времени в интервале от около 30 минут до около 60 минут с обеспечением измельченной смеси;
сушку измельченной смеси при температуре в интервале от около 110°C до около 140°C в течение периода времени в интервале от около 8 часов до около 18 часов с обеспечением высушенной измельченной смеси; и
кальцинирование высушенной измельченной смеси при температуре в интервале от около 40°C до около 700°C в течение периода времени в интервале от около 30 минут до около 120 минут.
14. Способ по п. 13, где смесь измельчают в шаровой мельнице.
15. Способ по п. 12, где Н2О находится при температуре в интервале от около 10°C до около 80°C для получения смеси, и Ва(ОН)2 присутствует в количестве в интервале от около 25 г/л Н2О до около 1014 г/л Н2О, соответствующем растворимости при температуре Н2О.
16. Способ по п. 13, где высушенную измельченную смесь кальцинируют в атмосфере газообразного CO2.
17. Способ по п. 16, где по меньшей мере часть газа CO2 в атмосфере кальцинирования обеспечивают посредством замещения от около 3% до около 15 мас. % Ва(ОН)2 на Ва(ООСН3)2.
18. Способ по п. 16, где высушенную измельченную смесь кальцинируют в атмосфере газообразного CO2 при температуре в интервале от около 400°C до около 700°C.
19. Способ по любому из пп. 13-18, где высушенную измельченную смесь кальцинируют при температуре около 650°C.
20. Способ получения аккумулирующего оксиды азота материала, включающий:
смешивание Ва(ОН)2 с СеО2 и Н2О с обеспечением смеси, где Ва(ОН)2 присутствует в количестве вплоть до максимальной растворимости Ва(ОН)2 в Н2О при температуре Н2О, и СеО2 присутствует в количестве от около 1,75 до около 2,0 раз превышающем количество Ва(ОН)2 по массе;
измельчение смеси в течение периода времени в интервале от около 30 минут до около 60 минут в шаровой мельнице с обеспечением измельченной смеси;
сушку измельченной смеси при температуре в интервале от около 110°C до около 140°C в течение периода времени в интервале от около 8 часов до около 18 часов с обеспечением высушенной измельченной смеси; и
кальцинирование высушенной измельченной смеси при температуре в интервале от около 200°C до около 700°C в течение периода времени в интервале от около 60 минут до около 120 минут в атмосфере газообразного CO2.
21. Аккумулирующий оксиды азота материал, полученный способом по п. 20.
22. Аккумулирующий оксиды азота материал по п. 21, имеющий средний размер частиц в интервале от около 2 микрон до около 8 микрон, и удельную поверхность БЭТ более 40 м2/г.
23. Катализатор-ловушка оксидов азота в условиях обедненной смеси (LNT), содержащий аккумулирующий оксиды азота материал по п. 21 или 22.
24. LNT катализатор по п. 23, где катализатор содержит слой материала катализатора LNT на сотообразной подложке.