RU2014143382A - Композиция полипропилена, армированного волокнами с высокой текучестью - Google Patents
Композиция полипропилена, армированного волокнами с высокой текучестью Download PDFInfo
- Publication number
- RU2014143382A RU2014143382A RU2014143382A RU2014143382A RU2014143382A RU 2014143382 A RU2014143382 A RU 2014143382A RU 2014143382 A RU2014143382 A RU 2014143382A RU 2014143382 A RU2014143382 A RU 2014143382A RU 2014143382 A RU2014143382 A RU 2014143382A
- Authority
- RU
- Russia
- Prior art keywords
- propylene
- propylene copolymer
- composition
- fiber reinforced
- fibers
- Prior art date
Abstract
1. Композиция, армированная волокнами, содержащая(a) гетерофазный сополимер пропилена (НЕСО),(b) гомополимер пропилена (Н-РР1) и/или сополимер пропилена (С-РР1), и(c) волокна (F) со средним диаметром 12,0 µм или менее,где(i) сополимер пропилена (С-РР1) содержит не более чем 2,0 масс. % C-Cα-олефинов, иных чем пропилен,(ii) гомополимер пропилена (Н-РР1) и сополимер пропилена (С-РР1) имеют скорость течения расплава MFR(230°C), измеренную согласно ISO 1133, по меньшей мере 50 г/10 минут, и(iii) композиция, армированная волокнами имеет скорость течения расплава MFR(230°C), измеренную согласно ISO 1133, по меньшей мере 10 г/10 минут.2. Композиция, армированная волокнами, по п. 1, где гетерофазный сополимер пропилена (НЕСО) содержит полипропиленовую матрицу (М-РР), предпочтительно полипропиленовая матрица (М-РР) представляет гомополимер пропилена (Н-РР2), в котором диспергирован эластомерный сополимер (Е1), содержащий единицы, полученные из- пропилена и- этилена и/или C-Cα-олефина.3. Композиция, армированная волокнами, по п. 2, где полипропиленовая матрица (М-РР) имеет более низкую скорость течения расплава MFR(230°C), измеренную согласно ISO 1133, по сравнению с гомополимером пропилена (Н-РР1) или сополимером пропилена (С-РР1).4. Композиция, армированная волокнами, по любому из пп. 1-3, где композиция содержит:(a) от 10,0 до 50,0 масс. % гетерофазного сополимера пропилена (НЕСО),(b) от 20,0 до 70,0 масс. % гомополимера пропилена (Н-РР1), сополимера пропилена (С-РР1) или смеси гомополимера пропилена (Н-РР1) и сополимера пропилена (С-РР1), и(c) от 5,0 до 50,0 масс. % волокна (F)от общей массы композиции, армированной волокнами.5. Композиция, армированная волокнами, по любому из пп. 1-3, где гетерофазный сополимер пропилена (НЕСО) имеет(a) фракцию, растворимую в холодном ксилоле (XCS), измеренную согласно ISO 6427 (23°C), не более чем 35 масс. % и/или(b) скорость течения расп
Claims (10)
1. Композиция, армированная волокнами, содержащая
(a) гетерофазный сополимер пропилена (НЕСО),
(b) гомополимер пропилена (Н-РР1) и/или сополимер пропилена (С-РР1), и
(c) волокна (F) со средним диаметром 12,0 µм или менее,
где
(i) сополимер пропилена (С-РР1) содержит не более чем 2,0 масс. % C2-C10 α-олефинов, иных чем пропилен,
(ii) гомополимер пропилена (Н-РР1) и сополимер пропилена (С-РР1) имеют скорость течения расплава MFR2 (230°C), измеренную согласно ISO 1133, по меньшей мере 50 г/10 минут, и
(iii) композиция, армированная волокнами имеет скорость течения расплава MFR2 (230°C), измеренную согласно ISO 1133, по меньшей мере 10 г/10 минут.
2. Композиция, армированная волокнами, по п. 1, где гетерофазный сополимер пропилена (НЕСО) содержит полипропиленовую матрицу (М-РР), предпочтительно полипропиленовая матрица (М-РР) представляет гомополимер пропилена (Н-РР2), в котором диспергирован эластомерный сополимер (Е1), содержащий единицы, полученные из
- пропилена и
- этилена и/или C4-C20 α-олефина.
3. Композиция, армированная волокнами, по п. 2, где полипропиленовая матрица (М-РР) имеет более низкую скорость течения расплава MFR2 (230°C), измеренную согласно ISO 1133, по сравнению с гомополимером пропилена (Н-РР1) или сополимером пропилена (С-РР1).
4. Композиция, армированная волокнами, по любому из пп. 1-3, где композиция содержит:
(a) от 10,0 до 50,0 масс. % гетерофазного сополимера пропилена (НЕСО),
(b) от 20,0 до 70,0 масс. % гомополимера пропилена (Н-РР1), сополимера пропилена (С-РР1) или смеси гомополимера пропилена (Н-РР1) и сополимера пропилена (С-РР1), и
(c) от 5,0 до 50,0 масс. % волокна (F)
от общей массы композиции, армированной волокнами.
5. Композиция, армированная волокнами, по любому из пп. 1-3, где гетерофазный сополимер пропилена (НЕСО) имеет
(a) фракцию, растворимую в холодном ксилоле (XCS), измеренную согласно ISO 6427 (23°C), не более чем 35 масс. % и/или
(b) скорость течения расплава MFR2 (230°C), измеренную согласно ISO 1133, более чем 15 г/10 минут и/или
(c) общее содержание C2-С10 α-олефина, иного чем пропилен, от 10 до 30 масс. %.
6. Композиция, армированная волокнами по любому из пп. 1-3, где гомополимер пропилена (Н-РР1) имеет скорость течения расплава MFR2 (230°C), измеренную согласно ISO 1133, в пределах от 50 до 150 г/10 минут.
7. Композиция, армированная волокнами, по любому из пп. 1-3, где волокна (F) выбирают из группы, состоящей из стекловолокна, металлического волокна, керамического волокна и графитного волокна.
8. Изделие для автомобильной промышленности, содержащее композицию, армированную волокнами, по любому из предшествующих пп..
9. Вспененное изделие, содержащее композицию, армированную волокнами, по одному из пп. 1-8.
10. Способ получения композиции, армированной волокнами, по любому из пп. 1-7, включающий стадии добавления
(a) гетерофазного сополимера пропилена (НЕСО),
(b) гомополимера пропилена (Н-РР1), сополимера пропилена (С-РР1) или смеси гомополимера пропилена (Н-РР1) и сополимера пропилена (С-РР1) и
(c) волокна (F)
в экструдер и их экструдирование с получением указанной композиции, армированной волокнами.