RU2013147171A - Флоат-стекло и способ его получения - Google Patents
Флоат-стекло и способ его получения Download PDFInfo
- Publication number
- RU2013147171A RU2013147171A RU2013147171/03A RU2013147171A RU2013147171A RU 2013147171 A RU2013147171 A RU 2013147171A RU 2013147171/03 A RU2013147171/03 A RU 2013147171/03A RU 2013147171 A RU2013147171 A RU 2013147171A RU 2013147171 A RU2013147171 A RU 2013147171A
- Authority
- RU
- Russia
- Prior art keywords
- bath
- molten
- float glass
- glass
- water
- Prior art date
Abstract
1. Флоат-стекло, полученное посредством принуждения расплавленного стекла, непрерывно подаваемого на расплавленное олово в ванне, течь на расплавленном олове по направлению к выходу из ванны,причем, когда расстояние от первой поверхности, которая представляет собой одну поверхность обеих основных поверхностей флоат-стекла и расположена на стороне расплавленного олова в ванне, до произвольного положения в направлении толщины листа в сторону второй поверхности, которая является другой поверхностью флоат-стекла, устанавливают равным x (мкм), функцию концентрации воды (част/млн по массе), имеющую x в виде переменной величины, устанавливают равной C(x), расстояние между обеими основными поверхностями флоат-стекла устанавливают равным D (мкм), расстояние от первой поверхности до положения, в котором концентрация воды является максимальной в направлении толщины листа между обеими основными поверхностями флоат-стекла, устанавливают равным Da (мкм), и концентрацию воды в положении Da устанавливают равной Ca (част/млн по массе),флоат-стекло удовлетворяет следующей ниже формуле (1):2. Флоат-стекло по п. 1, удовлетворяющее следующей ниже формуле (2):3. Способ получения флоат-стекла, включающий принуждение расплавленного стекла, непрерывно подаваемого на расплавленное олово в ванне, течь на расплавленном олове по направлению к выходу из ванны,причем количество воды, элюируемое из расплавленного стекла в расплавленное олово в ванне, устанавливают равным 0,5% или менее от количества воды в расплавленном стекле непосредственно перед втеканием в ванну.4. Способ получения флоат-стекла по п. 3, в котором температуру расплавленного олов
Claims (7)
1. Флоат-стекло, полученное посредством принуждения расплавленного стекла, непрерывно подаваемого на расплавленное олово в ванне, течь на расплавленном олове по направлению к выходу из ванны,
причем, когда расстояние от первой поверхности, которая представляет собой одну поверхность обеих основных поверхностей флоат-стекла и расположена на стороне расплавленного олова в ванне, до произвольного положения в направлении толщины листа в сторону второй поверхности, которая является другой поверхностью флоат-стекла, устанавливают равным x (мкм), функцию концентрации воды (част/млн по массе), имеющую x в виде переменной величины, устанавливают равной C(x), расстояние между обеими основными поверхностями флоат-стекла устанавливают равным D (мкм), расстояние от первой поверхности до положения, в котором концентрация воды является максимальной в направлении толщины листа между обеими основными поверхностями флоат-стекла, устанавливают равным Da (мкм), и концентрацию воды в положении Da устанавливают равной Ca (част/млн по массе),
флоат-стекло удовлетворяет следующей ниже формуле (1):
2. Флоат-стекло по п. 1, удовлетворяющее следующей ниже формуле (2):
3. Способ получения флоат-стекла, включающий принуждение расплавленного стекла, непрерывно подаваемого на расплавленное олово в ванне, течь на расплавленном олове по направлению к выходу из ванны,
причем количество воды, элюируемое из расплавленного стекла в расплавленное олово в ванне, устанавливают равным 0,5% или менее от количества воды в расплавленном стекле непосредственно перед втеканием в ванну.
4. Способ получения флоат-стекла по п. 3, в котором температуру расплавленного олова в ванне и/или температуру расплавленного стекла в ванне регулируют, чтобы количество воды, элюируемой из расплавленного стекла в расплавленное олово в ванне, стало 0,5% или менее от количества воды в расплавленном стекле непосредственно перед втеканием в ванну.
5. Способ получения флоат-стекла по п. 3 или 4, в котором концентрацию газообразного водорода в атмосфере внутри ванны регулируют, чтобы количество воды, элюируемой из расплавленного стекла в расплавленное олово в ванне, стало 0,5% или менее от количества воды в расплавленном стекле непосредственно перед втеканием в ванну.
6. Способ получения флоат-стекла по п. 3 или 4, в котором концентрация воды в расплавленном стекле непосредственно перед втеканием в ванну составляет 470 част/млн по массе или более.
7. Способ получения флоат-стекла по п. 5, в котором концентрация воды в расплавленном стекле непосредственно перед втеканием в ванну составляет 470 част/млн по массе или более.