RU2012108879A - Оптическое волокно, содержащее многослойную систему покрытий - Google Patents
Оптическое волокно, содержащее многослойную систему покрытий Download PDFInfo
- Publication number
- RU2012108879A RU2012108879A RU2012108879/03A RU2012108879A RU2012108879A RU 2012108879 A RU2012108879 A RU 2012108879A RU 2012108879/03 A RU2012108879/03 A RU 2012108879/03A RU 2012108879 A RU2012108879 A RU 2012108879A RU 2012108879 A RU2012108879 A RU 2012108879A
- Authority
- RU
- Russia
- Prior art keywords
- coating
- optical fiber
- young
- modulus
- less
- Prior art date
Abstract
1. Оптическое волокно, включающее:стекловолокно; итри или более покрытия, которые герметизируют стекловолокно, причем эти три или более покрытия включают первичное покрытие в контакте с упомянутым стекловолокном, промежуточное покрытие, которое окружает первичное покрытие, и внешнее покрытие, которое окружает промежуточное покрытие;при этом первичное покрытие имеет модуль Юнга от примерно 0,025 до примерно 3 МПа и/или температуру стеклования (Т) от примерно -100°C до примерно -25°C, а промежуточное покрытие имеет одно или оба из модуля Юнга, который является по существу таким же как, или более низким, чем модуль Юнга первичного покрытия, и Т, которая является по существу такой же как, или более низкой, чем Тпервичного покрытия; ипри этом внешнее покрытие оптического волокна имеет диаметр, который составляет менее примерно 300 мкм.2. Оптическое волокно по п.1, при этом промежуточное покрытие имеет одно или оба из модуля Юнга, который составляет менее примерно 0,2 МПа, и Тот примерно -100°C до примерно -25°C.3. Оптическое волокно по п.1, при этом внешнее покрытие имеет одно или оба из модуля Юнга от примерно 0,5 до примерно 8,0 ГПа и Тот примерно 50°C до примерно 120°C.4. Оптическое волокно по п.1, при этом первичное покрытие имеет толщину менее примерно 15 мкм.5. Оптическое волокно по п.1, при этом промежуточное покрытие имеет толщину менее примерно 15 мкм.6. Оптическое волокно по п.1, при этом внешнее покрытие имеет толщину менее примерно 40 мкм.7. Оптическое волокно по п.1, при этом упомянутые три или более покрытия имеют толщину, которая составляет менее примерно 60 мкм.8. Оптическое волокно по п.1, при этомпервичное покрытие является продуктом полиме�
Claims (20)
1. Оптическое волокно, включающее:
стекловолокно; и
три или более покрытия, которые герметизируют стекловолокно, причем эти три или более покрытия включают первичное покрытие в контакте с упомянутым стекловолокном, промежуточное покрытие, которое окружает первичное покрытие, и внешнее покрытие, которое окружает промежуточное покрытие;
при этом первичное покрытие имеет модуль Юнга от примерно 0,025 до примерно 3 МПа и/или температуру стеклования (Тс) от примерно -100°C до примерно -25°C, а промежуточное покрытие имеет одно или оба из модуля Юнга, который является по существу таким же как, или более низким, чем модуль Юнга первичного покрытия, и Тс, которая является по существу такой же как, или более низкой, чем Тс первичного покрытия; и
при этом внешнее покрытие оптического волокна имеет диаметр, который составляет менее примерно 300 мкм.
2. Оптическое волокно по п.1, при этом промежуточное покрытие имеет одно или оба из модуля Юнга, который составляет менее примерно 0,2 МПа, и Тс от примерно -100°C до примерно -25°C.
3. Оптическое волокно по п.1, при этом внешнее покрытие имеет одно или оба из модуля Юнга от примерно 0,5 до примерно 8,0 ГПа и Тс от примерно 50°C до примерно 120°C.
4. Оптическое волокно по п.1, при этом первичное покрытие имеет толщину менее примерно 15 мкм.
5. Оптическое волокно по п.1, при этом промежуточное покрытие имеет толщину менее примерно 15 мкм.
6. Оптическое волокно по п.1, при этом внешнее покрытие имеет толщину менее примерно 40 мкм.
7. Оптическое волокно по п.1, при этом упомянутые три или более покрытия имеют толщину, которая составляет менее примерно 60 мкм.
8. Оптическое волокно по п.1, при этом
первичное покрытие является продуктом полимеризации композиции, включающей один или более сшиваемых агентов, инициатор полимеризации и усилитель адгезии; и
промежуточное покрытие является продуктом полимеризации композиции, которая является такой же, как и композиция, которая образует первичное покрытие, за исключением отсутствия усилителя адгезии.
9. Оптическое волокно, включающее:
стекловолокно; и
по меньшей мере четыре покрытия, которые герметизируют стекловолокно, причем эти по меньшей мере четыре покрытия включают первичное покрытие в контакте с упомянутым стекловолокном, первое промежуточное покрытие, которое окружает первичное покрытие, второе промежуточное покрытие, которое окружает первое промежуточное покрытие, и внешнее покрытие, которое окружает второе промежуточное покрытие;
при этом первое промежуточное покрытие имеет одно или оба из модуля Юнга, который выше, чем модуль Юнга первичного покрытия, и температуры стеклования (Тс), которая выше, чем Тс первичного покрытия;
при этом второе промежуточное покрытие имеет одно или оба из модуля Юнга, который ниже, чем модуль Юнга первого промежуточного покрытия, и Тс, которая ниже, чем Тс первого промежуточного покрытия;
при этом внешнее покрытие имеет одно или оба из модуля Юнга, который выше, чем модуль Юнга второго промежуточного покрытия, и Тс, которая выше, чем Тс второго промежуточного покрытия; и
при этом оптическое волокно имеет диаметр, который составляет менее примерно 300 мкм.
10. Оптическое волокно по п.9, при этом второе промежуточное покрытие имеет одно или оба из модуля Юнга, который является по существу таким же как, или более низким, чем модуль Юнга первичного покрытия, и Тс, которая является по существу такой же как, или более низкой, чем Тс первичного покрытия.
11. Оптическое волокно по п.9, при этом первичное покрытие имеет одно или оба из модуля Юнга от примерно 0,025 до примерно 3 МПа и Тс от примерно -100°C до примерно -25°C.
12. Оптическое волокно по п.11, при этом первое промежуточное покрытие имеет одно или оба из модуля Юнга от примерно 0,1 до примерно 2,0 ГПа и Тс от примерно 0°C до примерно 60°C.
13. Оптическое волокно по п.12, при этом второе промежуточное покрытие имеет одно или оба из модуля Юнга, который составляет менее примерно 0,2 МПа, и Тс от примерно - 100°C до примерно -30°C.
14. Оптическое волокно по п.13, при этом вторичное покрытие имеет одно или оба из модуля Юнга, который составляет от примерно 0,1 до примерно 2,0 ГПа, и Тс от примерно 50°C до примерно 120°C.
15. Оптическое волокно по п.9, при этом первичное покрытие имеет толщину менее примерно 15 мкм.
16. Оптическое волокно по п.9, при этом первое промежуточное покрытие имеет толщину менее примерно 15 мкм.
17. Оптическое волокно по п.9, при этом второе промежуточное покрытие имеет толщину менее примерно 40 мкм.
18. Оптическое волокно по п.9, при этом внешнее покрытие имеет толщину менее примерно 40 мкм.
19. Оптическое волокно по п.1, при этом упомянутые четыре или более покрытия имеют толщину, которая составляет менее примерно 60 мкм.
20. Оптическое волокно по п.1, при этом одно или оба из второго промежуточного покрытия и внешнего покрытия имеют толщину, которая в от примерно 2 до примерно 10 раз превышает толщину соответственно первичного покрытия и первого промежуточного покрытия.