RU2008125143A - Солнечный элемент с просветляющим покрытием с градиентным слоем, включающим смесь оксида титана и оксида кремния - Google Patents

Солнечный элемент с просветляющим покрытием с градиентным слоем, включающим смесь оксида титана и оксида кремния Download PDF

Info

Publication number
RU2008125143A
RU2008125143A RU2008125143/28A RU2008125143A RU2008125143A RU 2008125143 A RU2008125143 A RU 2008125143A RU 2008125143/28 A RU2008125143/28 A RU 2008125143/28A RU 2008125143 A RU2008125143 A RU 2008125143A RU 2008125143 A RU2008125143 A RU 2008125143A
Authority
RU
Russia
Prior art keywords
gradient layer
solar cell
glass substrate
silicon oxide
cell according
Prior art date
Application number
RU2008125143/28A
Other languages
English (en)
Other versions
RU2390074C2 (ru
Inventor
Натан П. МЕЛЛОТТ (US)
Натан П. МЕЛЛОТТ
Томас Дж. ТЕЙЛОР (US)
Томас Дж. ТЕЙЛОР
Original Assignee
Гардиан Индастриз Корп. (Us)
Гардиан Индастриз Корп.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Гардиан Индастриз Корп. (Us), Гардиан Индастриз Корп. filed Critical Гардиан Индастриз Корп. (Us)
Publication of RU2008125143A publication Critical patent/RU2008125143A/ru
Application granted granted Critical
Publication of RU2390074C2 publication Critical patent/RU2390074C2/ru

Abstract

1. Солнечный элемент, включающий в себя ! фотоэлектрический слой и по меньшей мере одну стеклянную подложку на той стороне фотоэлектрического слоя, на которую попадает свет; ! просветляющее покрытие, предусмотренное на стеклянной подложке, причем просветляющее покрытие расположено на той стороне стеклянной подложки, на которую падает свет; ! в котором просветляющее покрытие включает в себя градиентный слой, предусмотренный непосредственно на стеклянной подложке и контактирующий с ней, при этом градиентный слой содержит смесь оксида кремния и оксида титана, причем больше оксида титана предусмотрено в дальней части градиентного слоя, более удаленной от стеклянной подложки, чем в ближней части градиентного слоя, более близкой к стеклянной подложке; и ! в котором просветляющее покрытие также содержит слой, содержащий оксид кремния, расположенный поверх градиентного слоя. ! 2. Солнечный элемент по п.1, в котором ближняя часть градиентного слоя имеет меньшее значение показателя преломления, чем у дальней части градиентного слоя. ! 3. Солнечный элемент по п.1, в котором ближняя часть градиентного слоя выполнена преимущественно из оксида кремния. ! 4. Солнечный элемент по п.1, в котором ближняя часть градиентного слоя имеет значение показателя преломления от примерно 1,46 до 1,9. ! 5. Солнечный элемент по п.1, в котором ближняя часть градиентного слоя имеет значение показателя преломления от примерно 1,46 до 1,7, при этом оксид титана представляет собой TiO2, а оксид кремния - SiO2. ! 6. Солнечный элемент по п.1, в котором дальняя часть градиентного слоя имеет значение показателя преломления от примерно 2,0 до 2,55. ! 7. Солнечный элемент по п.1, �

Claims (20)

1. Солнечный элемент, включающий в себя
фотоэлектрический слой и по меньшей мере одну стеклянную подложку на той стороне фотоэлектрического слоя, на которую попадает свет;
просветляющее покрытие, предусмотренное на стеклянной подложке, причем просветляющее покрытие расположено на той стороне стеклянной подложки, на которую падает свет;
в котором просветляющее покрытие включает в себя градиентный слой, предусмотренный непосредственно на стеклянной подложке и контактирующий с ней, при этом градиентный слой содержит смесь оксида кремния и оксида титана, причем больше оксида титана предусмотрено в дальней части градиентного слоя, более удаленной от стеклянной подложки, чем в ближней части градиентного слоя, более близкой к стеклянной подложке; и
в котором просветляющее покрытие также содержит слой, содержащий оксид кремния, расположенный поверх градиентного слоя.
2. Солнечный элемент по п.1, в котором ближняя часть градиентного слоя имеет меньшее значение показателя преломления, чем у дальней части градиентного слоя.
3. Солнечный элемент по п.1, в котором ближняя часть градиентного слоя выполнена преимущественно из оксида кремния.
4. Солнечный элемент по п.1, в котором ближняя часть градиентного слоя имеет значение показателя преломления от примерно 1,46 до 1,9.
5. Солнечный элемент по п.1, в котором ближняя часть градиентного слоя имеет значение показателя преломления от примерно 1,46 до 1,7, при этом оксид титана представляет собой TiO2, а оксид кремния - SiO2.
6. Солнечный элемент по п.1, в котором дальняя часть градиентного слоя имеет значение показателя преломления от примерно 2,0 до 2,55.
7. Солнечный элемент по п.1, в котором дальняя часть градиентного слоя имеет значение показателя преломления от примерно 2,3 до 2,55.
8. Солнечный элемент по п.1, в котором дальняя часть градиентного слоя выполнена преимущественно из оксида титана.
9. Солнечный элемент по п.1, в котором слой, содержащий оксид кремния, имеет приблизительно четвертьволновую толщину.
10. Солнечный элемент по п.1, в котором слой, содержащий оксид кремния, составляет от примерно 80 до 140 нм, более предпочтительно - от примерно 110 до 130 нм.
11. Солнечный элемент по п.1, в котором ближняя часть градиентного слоя выполнена из от примерно 40-100% оксида кремния, а дальняя часть градиентного слоя выполнена из от примерно 50-100% оксида титана.
12. Солнечный элемент по п.1, в котором ближняя часть градиентного слоя выполнена из от примерно 70-100% оксида кремния, а дальняя часть градиентного слоя выполнена из от примерно 70-100% оксида титана.
13. Солнечный элемент, включающий в себя
фотоэлектрический слой и по меньшей мере одну стеклянную подложку на той стороне фотоэлектрического слоя, на которую попадает свет;
просветляющее покрытие, предусмотренное на стеклянной подложке, причем просветляющее покрытие расположено на той стороне стеклянной подложки, на которую падает свет;
в котором просветляющее покрытие включает в себя градиентный слой, содержащий смесь оксида кремния и оксида металла (М), причем больше оксида металла (М) предусмотрено в дальней части градиентного слоя, более удаленной от стеклянной подложки, чем в ближней части градиентного слоя, более близкой к стеклянной подложке, и при этом М представляет собой один или более из группы Ti, Zr и Al; и
в котором просветляющее покрытие также включает в себя слой, содержащий оксид кремния, расположенный поверх градиентного слоя.
14. Солнечный элемент по п.13, где ближняя часть градиентного слоя выполнена преимущественно из оксида кремния.
15. Солнечный элемент по п.13, в котором ближняя часть градиентного слоя имеет значение показателя преломления от примерно 1,46 до 1,7.
16. Солнечный элемент по п.13, в котором дальняя часть градиентного слоя имеет значение показателя преломления от примерно 2,0 до 2,55.
17. Солнечный элемент по п.13, в котором слой, содержащий оксид кремния, имеет приблизительно четвертьволновую толщину.
18. Солнечный элемент по п.13, в котором слой, содержащий оксид кремния, составляет от примерно 80 до 140 нм.
19. Солнечный элемент по п.1, в котором стеклянная подложка содержит:
ингредиент мас.% SiO2 67-75% Na2O 10-20% CaO 5-15% всего железа (выраженного как Fe2O3) от 0,001 до 0,06% оксид церия от 0 до 0,30%
при этом сама по себе стеклянная подложка имеет пропускание видимого излучения по меньшей мере 90%, цветовую координату а* на пропускание от -1,0 до +1,0 и цветовую координату b* на пропускание от 0 до +1,5.
20. Покрытое изделие, включающее в себя
стеклянную подложку и просветляющее покрытие на этой стеклянной подложке;
в котором просветляющее покрытие включает в себя градиентный слой, содержащий смесь оксида кремния и оксида титана, причем больше оксида титана предусмотрено в дальней части градиентного слоя, более удаленной от стеклянной подложки, чем в ближней части градиентного слоя, более близкой к стеклянной подложке; и
в котором просветляющее покрытие также содержит слой, содержащий оксид кремния, расположенный поверх градиентного слоя.
RU2008125143/28A 2005-11-22 2006-11-03 Солнечный элемент с просветляющим покрытием с градиентным слоем, включающим смесь оксида титана и оксида кремния RU2390074C2 (ru)