JP3079506B2 - 紫外線吸収無色透明ガラス - Google Patents
紫外線吸収無色透明ガラスInfo
- Publication number
- JP3079506B2 JP3079506B2 JP09222964A JP22296497A JP3079506B2 JP 3079506 B2 JP3079506 B2 JP 3079506B2 JP 09222964 A JP09222964 A JP 09222964A JP 22296497 A JP22296497 A JP 22296497A JP 3079506 B2 JP3079506 B2 JP 3079506B2
- Authority
- JP
- Japan
- Prior art keywords
- glass
- oxide
- colorless
- transparent glass
- cerium oxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】
【発明の属する技術分野】本発明は、特にガラスびんと
して用いて好適な紫外線吸収無色透明ガラスに関する。
して用いて好適な紫外線吸収無色透明ガラスに関する。
【０００２】
【従来の技術】ガラスびんにおいては、内容物の変質を
防ぐために紫外線を吸収し、しかも、内容物の様子を正
確に確認することのできる無色透明性を有するものが望
まれている。従来、このような用途のガラスは、特公昭
４５−１７７９４号、特公平５−３５４号などて提案さ
れている。前者のものは、ソーダライムガラスにセリウ
ム酸化物を０．２〜０．５重量％、ネオジウム酸化物を
０．０５〜０．３重量％加えるというもので、セリウム
酸化物を加えることで紫外線を吸収し、それによって黄
色味をおびる色を消色剤であるネオジウム酸化物を加え
ることで無色に近くなるよに補正しようというものであ
る。後者のものは、容器の最大長を２５０ｍｍ以下と
し、重量％で０．０４〜０．１％の酸化セリウムと、
０．０６５％以下の酸化鉄を含有させたソーダライムガ
ラスのびんである。やはり、酸化セリウムを添加するこ
とで紫外線を吸収し、黄色味を助長させる酸化鉄の含有
量を抑えると共にびんの最大長さを制限することでガラ
スが黄色に見えることを極力抑えようというものであ
る。
防ぐために紫外線を吸収し、しかも、内容物の様子を正
確に確認することのできる無色透明性を有するものが望
まれている。従来、このような用途のガラスは、特公昭
４５−１７７９４号、特公平５−３５４号などて提案さ
れている。前者のものは、ソーダライムガラスにセリウ
ム酸化物を０．２〜０．５重量％、ネオジウム酸化物を
０．０５〜０．３重量％加えるというもので、セリウム
酸化物を加えることで紫外線を吸収し、それによって黄
色味をおびる色を消色剤であるネオジウム酸化物を加え
ることで無色に近くなるよに補正しようというものであ
る。後者のものは、容器の最大長を２５０ｍｍ以下と
し、重量％で０．０４〜０．１％の酸化セリウムと、
０．０６５％以下の酸化鉄を含有させたソーダライムガ
ラスのびんである。やはり、酸化セリウムを添加するこ
とで紫外線を吸収し、黄色味を助長させる酸化鉄の含有
量を抑えると共にびんの最大長さを制限することでガラ
スが黄色に見えることを極力抑えようというものであ
る。
【０００３】
【発明が解決しようとする課題】上記の従来技術の前者
のものは、青紫色を付けるネオジウム酸化物を加えるこ
とで、酸化セリウムの黄色若しくは黄緑色を消して無色
に近づけようとするものであるが、ネオジウム酸化物が
高価であるうえに、添加する分量が難しく、少なすぎる
とガラスは黄色ないしは黄緑色を呈し、多すぎると青色
を呈してしまうという課題がある。
のものは、青紫色を付けるネオジウム酸化物を加えるこ
とで、酸化セリウムの黄色若しくは黄緑色を消して無色
に近づけようとするものであるが、ネオジウム酸化物が
高価であるうえに、添加する分量が難しく、少なすぎる
とガラスは黄色ないしは黄緑色を呈し、多すぎると青色
を呈してしまうという課題がある。
【０００４】上記の従来技術の後者のものは、大型のび
んが作れない上に、セリウムの添加量が少ないから十分
な紫外線吸収効果を期待できず、また、セリウム酸化物
による黄色味を消すことができないから、結局ガラスの
色は無色とすることができず、黄色味をおびたガラスと
なってしまう。
んが作れない上に、セリウムの添加量が少ないから十分
な紫外線吸収効果を期待できず、また、セリウム酸化物
による黄色味を消すことができないから、結局ガラスの
色は無色とすることができず、黄色味をおびたガラスと
なってしまう。
【０００５】本発明は、このような課題を解決するもの
で、より安価で、より容易に、より無色に近い紫外線吸
収無色透明ガラスを得ることができるものである。
で、より安価で、より容易に、より無色に近い紫外線吸
収無色透明ガラスを得ることができるものである。
【０００６】
【課題を解決するための手段】本発明は、重量％で酸化
セリウム０．３〜０．６％、酸化鉄０．０５％以下を含
むソーダライムガラスで、消色剤として酸化エルビウム
０．０２〜０．０７％を添加したことを特徴とする紫外
線吸収無色透明ガラスである。
セリウム０．３〜０．６％、酸化鉄０．０５％以下を含
むソーダライムガラスで、消色剤として酸化エルビウム
０．０２〜０．０７％を添加したことを特徴とする紫外
線吸収無色透明ガラスである。
【０００７】本発明においては、酸化セリウムを加える
ことで紫外線吸収効果を得る。酸化セリウムの添加量
は、少なすぎては紫外線吸収作用が弱く、多すぎてはガ
ラスが強く発色し無色透明とすることができず、０．３
〜０．６％の量が双方の要素のバランスが良く、好適で
ある。表１に酸化セリウムの添加率と紫外線吸収率の関
係を示す。この表は、紫外線吸収率を該当波長範囲での
平均吸収率と定義し算出した。すなわち、１０ｎｍ毎の
透過率を１００から引いて、その平均値を求めている。
このように、酸化セリウムの添加量を増やすと、紫外線
吸収率が向上する。０．３〜０．６％とすれば、実用的
な紫外線吸収率を得ることができる。なお、表１におけ
るガラスの厚みは３ｍｍである。
ことで紫外線吸収効果を得る。酸化セリウムの添加量
は、少なすぎては紫外線吸収作用が弱く、多すぎてはガ
ラスが強く発色し無色透明とすることができず、０．３
〜０．６％の量が双方の要素のバランスが良く、好適で
ある。表１に酸化セリウムの添加率と紫外線吸収率の関
係を示す。この表は、紫外線吸収率を該当波長範囲での
平均吸収率と定義し算出した。すなわち、１０ｎｍ毎の
透過率を１００から引いて、その平均値を求めている。
このように、酸化セリウムの添加量を増やすと、紫外線
吸収率が向上する。０．３〜０．６％とすれば、実用的
な紫外線吸収率を得ることができる。なお、表１におけ
るガラスの厚みは３ｍｍである。
【表１】
【０００８】酸化セリウムを加えることで、ガラス中に
不純物として存在している鉄を酸化する。そのため、２
価の鉄イオンの緑色着色が少なくなり、３価の鉄イオン
の黄色が多くなる。これにより、明度Ｙが大きくなり、
主波長λｄは長波長側へシフトし、ガラスの色が黄色味
がかる。不純物である酸化鉄の含有量を０．０５％以下
に抑えることで、ガラスの黄色ないし黄緑色の発色を最
小限に抑制する。なお、酸化鉄の含有量を０．０５％以
下に抑えることは、当業者にとって容易になし得ること
である。
不純物として存在している鉄を酸化する。そのため、２
価の鉄イオンの緑色着色が少なくなり、３価の鉄イオン
の黄色が多くなる。これにより、明度Ｙが大きくなり、
主波長λｄは長波長側へシフトし、ガラスの色が黄色味
がかる。不純物である酸化鉄の含有量を０．０５％以下
に抑えることで、ガラスの黄色ないし黄緑色の発色を最
小限に抑制する。なお、酸化鉄の含有量を０．０５％以
下に抑えることは、当業者にとって容易になし得ること
である。
【０００９】酸化鉄の含有量を抑えるだけではガラスを
無色にすることはできない。そこで、本発明において
は、消色剤として酸化エルビウム０．０２〜０．０７％
を添加する。酸化セリウムで黄色味がかった色は酸化エ
ルビウムの淡いピンク色で補正されて無色に近くなる。
酸化エルビウムの発色はきわめて安定していて、雰囲気
の変化や酸化セリウムのような酸化剤の影響を受けにく
く、所望の効果を容易に得ることができる。
無色にすることはできない。そこで、本発明において
は、消色剤として酸化エルビウム０．０２〜０．０７％
を添加する。酸化セリウムで黄色味がかった色は酸化エ
ルビウムの淡いピンク色で補正されて無色に近くなる。
酸化エルビウムの発色はきわめて安定していて、雰囲気
の変化や酸化セリウムのような酸化剤の影響を受けにく
く、所望の効果を容易に得ることができる。
【００１０】
【実施例】本発明の実施例を表２に示す。酸化セリウム
を０．３％、０．４％又は０．６％添加し、それぞれに
ついて消色剤を添加したもの（実施例）と添加しないも
の（比較例）を試料として作成し、三刺激値を測定し
た。いずれの試料においてもガラスの厚みは１０ｍｍ、
酸化鉄の含有量は０．０３８％である。三刺激値は、明
度Ｙが８５％以上、主波長λｄが５６５〜５７５ｎｍ、
刺激純度Ｐｅが１．５％以下の範囲の値となれば、ほぼ
良好な無色透明性を有すると判断できるが、主波長につ
いては５６８〜５７２ｎｍの範囲となることが最も好ま
しい。消色剤として酸化エルビウムを添加した実施例
は、いずれも三刺激値がこの最も好ましい範囲にあり、
良好な無色透明性を有すると判断できる。また、視覚検
査においても、いずれの実施例も比較例に対して無色透
明性が向上しており、良好な無色透明ガラスとなってい
ることが確認された。
を０．３％、０．４％又は０．６％添加し、それぞれに
ついて消色剤を添加したもの（実施例）と添加しないも
の（比較例）を試料として作成し、三刺激値を測定し
た。いずれの試料においてもガラスの厚みは１０ｍｍ、
酸化鉄の含有量は０．０３８％である。三刺激値は、明
度Ｙが８５％以上、主波長λｄが５６５〜５７５ｎｍ、
刺激純度Ｐｅが１．５％以下の範囲の値となれば、ほぼ
良好な無色透明性を有すると判断できるが、主波長につ
いては５６８〜５７２ｎｍの範囲となることが最も好ま
しい。消色剤として酸化エルビウムを添加した実施例
は、いずれも三刺激値がこの最も好ましい範囲にあり、
良好な無色透明性を有すると判断できる。また、視覚検
査においても、いずれの実施例も比較例に対して無色透
明性が向上しており、良好な無色透明ガラスとなってい
ることが確認された。
【表２】
【００１１】
【発明の効果】本発明は、酸化セリウムを添加すること
で紫外線を吸収し、消色剤として酸化エルビウムを用い
たので、安価かつ容易に無色透明性の高いガラスを得る
ことができる。
で紫外線を吸収し、消色剤として酸化エルビウムを用い
たので、安価かつ容易に無色透明性の高いガラスを得る
ことができる。
Claims (1)
- 【請求項１】 重量％で酸化セリウム０．３〜０．６
％、酸化鉄０．０５％以下を含むソーダライムガラス
で、消色剤として酸化エルビウム０．０２〜０．０７％
を添加したことを特徴とする紫外線吸収無色透明ガラス