RU2008118082A - Керамический порошок, керамический слой и многослойная система с пирохлорной фазой и оксидами - Google Patents
Керамический порошок, керамический слой и многослойная система с пирохлорной фазой и оксидами Download PDFInfo
- Publication number
- RU2008118082A RU2008118082A RU2008118082/02A RU2008118082A RU2008118082A RU 2008118082 A RU2008118082 A RU 2008118082A RU 2008118082/02 A RU2008118082/02 A RU 2008118082/02A RU 2008118082 A RU2008118082 A RU 2008118082A RU 2008118082 A RU2008118082 A RU 2008118082A
- Authority
- RU
- Russia
- Prior art keywords
- powder according
- layer
- oxide
- ceramic
- inner layer
- Prior art date
Abstract
1. Керамический порошок, содержащий пирохлорную фазу общей формулы А2В2О7 с х, у 2, z 7 и вторичный оксид CrOs r, s>0, в частности, с содержанием 0,5-10 мас.%, в частности состоящий, по меньшей мере, из одной пирохлорной фазы и, по меньшей мере, одного вторичного оксида. ! 2. Порошок по п.1, в котором А - гадолиний (Gd). ! 3. Порошок по п.1 или 2, в котором В - гафний (Hf). ! 4. Порошок по пп.1, 2 или 3, в котором В - цирконий (Zr). ! 5. Порошок по пп.1, 2, 3 или 4, в котором С - В. ! 6. Порошок по пп.1, 2, 3 или 4, в котором С - В. ! 7. Порошок по пп.1, 2, 3, 4, 5 или 6, в котором С - гафний (Hf). ! 8. Порошок по пп.1, 2, 3, 4, 5 или 6, в котором С - цирконий (Zr). ! 9. Порошок по пп.1, 5, 6, 7 или 8, содержащий максимум 3 мас.%, в частности максимум 2 мас.%, особенно в частности 1,5-2,5 мас.% вторичного оксида. ! 10. Порошок по пп.1, 5, 6, 7 или 8, содержащий максимум 8 мас.%, в частности максимум 6 мас.%, особенно в частности 5-7 мас.% вторичного оксида. ! 11. Порошок по пп.1, 7 или 9, в котором вторичный оксид представляет собой оксид гафния (HfO2). ! 12. Порошок по пп.1, 8 или 10, в котором вторичный оксид представляет собой оксид циркония (ZrO2). ! 13. Порошок по одному или нескольким пп.1-12, содержащий в качестве способствующих спеканию добавок ! до 0,05 мас.% оксида кремния; ! до 0,1 мас.% оксида кальция; ! до 0,1 мас.% оксида магния; ! до 0,1 мас.% оксида железа; ! до 0,1 мас.% оксида алюминия; ! до 0,08 мас.% оксида титана. ! 14. Порошок по пп.1, 2, 3 или 4, содержащий, по меньшей мере, 92 мас.%, в частности, по меньшей мере, 94 мас.% пирохлорной фазы. ! 15. Порошок по одному или нескольким предыдущим пунктам, содержащий только одну пирохлорную фазу. ! 16. Порошок по одному или нескольким пп.1-14, содержащий только две пирохлорные фазы. ! 17. Порошок по одному или нескольким предыдущим пунктам, сод
Claims (43)
1. Керамический порошок, содержащий пирохлорную фазу общей формулы А2В2О7 с х, у 2, z 7 и вторичный оксид CrOs r, s>0, в частности, с содержанием 0,5-10 мас.%, в частности состоящий, по меньшей мере, из одной пирохлорной фазы и, по меньшей мере, одного вторичного оксида.
2. Порошок по п.1, в котором А - гадолиний (Gd).
3. Порошок по п.1 или 2, в котором В - гафний (Hf).
4. Порошок по пп.1, 2 или 3, в котором В - цирконий (Zr).
5. Порошок по пп.1, 2, 3 или 4, в котором С - В.
6. Порошок по пп.1, 2, 3 или 4, в котором С - В.
7. Порошок по пп.1, 2, 3, 4, 5 или 6, в котором С - гафний (Hf).
8. Порошок по пп.1, 2, 3, 4, 5 или 6, в котором С - цирконий (Zr).
9. Порошок по пп.1, 5, 6, 7 или 8, содержащий максимум 3 мас.%, в частности максимум 2 мас.%, особенно в частности 1,5-2,5 мас.% вторичного оксида.
10. Порошок по пп.1, 5, 6, 7 или 8, содержащий максимум 8 мас.%, в частности максимум 6 мас.%, особенно в частности 5-7 мас.% вторичного оксида.
11. Порошок по пп.1, 7 или 9, в котором вторичный оксид представляет собой оксид гафния (HfO2).
12. Порошок по пп.1, 8 или 10, в котором вторичный оксид представляет собой оксид циркония (ZrO2).
13. Порошок по одному или нескольким пп.1-12, содержащий в качестве способствующих спеканию добавок
до 0,05 мас.% оксида кремния;
до 0,1 мас.% оксида кальция;
до 0,1 мас.% оксида магния;
до 0,1 мас.% оксида железа;
до 0,1 мас.% оксида алюминия;
до 0,08 мас.% оксида титана.
14. Порошок по пп.1, 2, 3 или 4, содержащий, по меньшей мере, 92 мас.%, в частности, по меньшей мере, 94 мас.% пирохлорной фазы.
15. Порошок по одному или нескольким предыдущим пунктам, содержащий только одну пирохлорную фазу.
16. Порошок по одному или нескольким пп.1-14, содержащий только две пирохлорные фазы.
17. Порошок по одному или нескольким предыдущим пунктам, содержащий смешанный кристалл в качестве пирохлорной фазы.
18. Порошок по одному или нескольким предыдущим пунктам, содержащий только один вторичный оксид CrOs.
19. Порошок по одному или нескольким предыдущим пунктам, содержащий только два вторичных оксида CrOs и С'r'Os'.
20. Порошок по одному или нескольким предыдущим пунктам, в котором вторичный оксид или вторичные оксиды присутствуют только в виде оксида.
21. Порошок по одному или нескольким пп.1-19, в котором вторичный оксид или вторичные оксиды присутствуют полностью в виде смешанного кристалла.
22. Порошок по одному или нескольким пп.1-19, в котором вторичный оксид или вторичные оксиды присутствуют как в виде оксида, так и в виде смешанного кристалла.
23. Порошок по одному или нескольким пп.1-22, состоящий из пирохлорных фаз А2В2О7, оксидов, в частности вторичных оксидов CrOs, и способствующих спеканию добавок.
24. Порошок по одному или нескольким пп.1-22, состоящий из пирохлорных фаз, вторичных оксидов CrOs и не содержащий способствующих спеканию добавок по п.13.
25. Керамический слой (13), полученный из керамического порошка по одному или нескольким пп.1-24, в частности полученный исключительной из керамического порошка по одному или нескольким пп.1-24.
26. Многослойная система, содержащая основу (4) и керамический слой (13) по п.25, представляющий собой, в частности, внешний слой (13).
27. Система по п.26, содержащая металлический адгезионный слой (7), содержащий, в частности, сплав NiCoCrAlX, в частности состоящий из него.
28. Система по п.26 или 27, содержащая внутренний керамический слой (10), в частности, на металлическом адгезионном слое (7), в частности стабилизированный слой оксида циркония, в частности стабилизированный иттрием слой оксида циркония, причем на внутреннем керамическом слое (10) расположен керамический слой (13).
29. Система по п.28, в которой внутренний слой (10) имеет толщину 10-50%, в частности 10-40% от общей толщины внутреннего слоя (10) и внешнего слоя (13).
30. Система по п.28, в которой внутренний слой (10) имеет толщину 10-30% от общей толщины внутреннего слоя (10) и внешнего слоя (13).
31. Система по п.28, в которой внутренний слой (10) имеет толщину 20-40% от общей толщины внутреннего слоя (10) и внешнего слоя (13).
32. Система по п.28, в которой внутренний слой (10) имеет толщину 50-90%, в частности 60-90% от общей толщины внутреннего слоя (10) и внешнего слоя (13).
33. Система по п.28, в которой внутренний слой (10) имеет толщину 70-90% от общей толщины внутреннего слоя (10) и внешнего слоя (13).
34. Система по п.28, в которой внутренний слой (10) имеет толщину 60-80% от общей толщины внутреннего слоя (10) и внешнего слоя (13).
35. Система по одному или нескольким пп.28-34, в которой внутренний слой (10) имеет толщину, в частности 1±10%.
36. Система по п.27, в которой металлический адгезионный слой (7) имеет следующий состав, мас.%: 11-13 кобальта, 20-22 хрома, 10,5-11,5 алюминия, 0,3-0,5 иттрия, 1,5-2,5 рения, остальное никель, в частности состоит из них.
37. Система по п.27, в которой металлический адгезионный слой (7) имеет следующий состав, мас.%: 24-26 кобальта, 16-18 хрома, 9,5-11 алюминия, 0,3-0,5 иттрия, 1-1,8 рения, остальное никель, в частности состоит из них.
38. Система по п.28, в которой стабилизированный иттрием слой оксида циркония содержит 6-8 мас.% иттрия.
39. Система по одному или нескольким пп.28-35, в которой общая толщина внутреннего слоя (10) и внешнего слоя (13) составляет, по меньшей мере, 300 мкм.
40. Система по одному или нескольким пп.28-35, в которой общая толщина внутреннего слоя (10) и внешнего слоя (13) составляет, по меньшей мере, 450 мкм, в частности 45 мкм.
41. Система по одному или нескольким пп.28-35, в которой общая толщина слоев составляет максимум 600 мкм, в частности максимум 800 мкм.
42. Система по одному или нескольким предыдущим пунктам, состоящая из основы (4), металлического слоя (7), внутреннего керамического слоя (10) и внешнего керамического слоя (13).
43. Система по одному или нескольким предыдущим пунктам, состоящая из основы (4), металлического слоя (7), оксидного слоя на металлическом слое (7), внутреннего керамического слоя (10) и внешнего керамического слоя (13).